MX2023009752A - Lamina de acero y lamina de acero enchapada. - Google Patents

Lamina de acero y lamina de acero enchapada.

Info

Publication number
MX2023009752A
MX2023009752A MX2023009752A MX2023009752A MX2023009752A MX 2023009752 A MX2023009752 A MX 2023009752A MX 2023009752 A MX2023009752 A MX 2023009752A MX 2023009752 A MX2023009752 A MX 2023009752A MX 2023009752 A MX2023009752 A MX 2023009752A
Authority
MX
Mexico
Prior art keywords
steel sheet
oxide
sup
layer
plated
Prior art date
Application number
MX2023009752A
Other languages
English (en)
Inventor
Jun Maki
Hiroshi Takebayashi
Masaaki Uranaka
Takuya Mitsunobu
Keitaro Matsuda
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of MX2023009752A publication Critical patent/MX2023009752A/es

Abstract

La presente invención se refiere a una lámina de acero de alta resistencia y lámina de acero enchapada que tiene alta capacidad de chapado, resistencia a LME, y resistencia a la fragilización de hidrógeno, es decir, lámina de acero que contiene C: 0.05 a 0.40%, Si: 0.2 a 3.0%, Mn: 0.1 a 5.0%, y Al sol.: 0.4 a 1.50%, que tiene una capa de oxidación interna que incluye óxidos granulares finos, óxidos granulares gruesos, y óxidos de límite de grano en una capa de superficie de la lámina de acero, una densidad numérica de óxidos granulares finos en la capa de oxidación interna siendo 4.0/µm2 o más, una densidad numérica de óxidos granulares gruesos en la capa de oxidación interna siendo 4.0/25 µm2 o más, que tiene una Relación A de la longitud de los óxidos de límite de grano proyectados sobre la superficie de la lámina de acero a la longitud de la superficie de la lámina de acero cuando se examina una sección transversal de la capa de superficie de la lámina de acero siendo 50% o más y 100% o menos, y que incluye una capa empobrecida en la superficie con una composición de acero que no incluye oxides que satisfacen, por % en masa, Si = 0.6% y Al = 0.05% a una profundidad de 1/2 de la profundidad promedio de la capa de oxidación interna calculada de la sección transversal a la imagen de SEM de la lámina de acero, y una lámina de acero enchapada usando la misma.
MX2023009752A 2021-04-27 2022-03-14 Lamina de acero y lamina de acero enchapada. MX2023009752A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021075057 2021-04-27
PCT/JP2022/011394 WO2022230400A1 (ja) 2021-04-27 2022-03-14 鋼板及びめっき鋼板

Publications (1)

Publication Number Publication Date
MX2023009752A true MX2023009752A (es) 2023-08-30

Family

ID=83847392

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2023009752A MX2023009752A (es) 2021-04-27 2022-03-14 Lamina de acero y lamina de acero enchapada.

Country Status (7)

Country Link
US (1) US20230399727A1 (es)
EP (1) EP4332262A1 (es)
JP (1) JPWO2022230400A1 (es)
KR (1) KR20230146082A (es)
CN (1) CN116897214A (es)
MX (1) MX2023009752A (es)
WO (1) WO2022230400A1 (es)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115679223B (zh) * 2022-11-07 2023-08-18 鞍钢股份有限公司 一种高屈强比冷轧dh980钢及其制备方法
CN115710673B (zh) * 2022-11-07 2023-07-14 鞍钢股份有限公司 一种高扩孔冷轧dh1180钢及其制备方法

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5672743B2 (ja) * 2009-03-31 2015-02-18 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5521520B2 (ja) * 2009-12-03 2014-06-18 新日鐵住金株式会社 合金化溶融亜鉛めっき鋼板およびその製造方法
JP5982906B2 (ja) * 2012-03-19 2016-08-31 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
JP2018193614A (ja) 2013-07-12 2018-12-06 株式会社神戸製鋼所 めっき性、加工性、および耐遅れ破壊特性に優れた高強度めっき鋼板、並びにその製造方法
WO2016111273A1 (ja) * 2015-01-09 2016-07-14 株式会社神戸製鋼所 高強度めっき鋼板、並びにその製造方法
MX2017009017A (es) 2015-01-09 2018-04-13 Kobe Steel Ltd Lamina de acero chapada de alta resistencia y metodo para su produccion.
US11274356B2 (en) * 2017-12-15 2022-03-15 Nippon Steel Corporation Steel sheet, hot-dip galvanized steel sheet and galvannealed steel sheet
EP3715493A4 (en) * 2017-12-27 2020-11-25 JFE Steel Corporation HIGH STRENGTH STEEL SHEET AND METHOD OF MANUFACTURING ITEM
KR102200175B1 (ko) * 2018-12-19 2021-01-08 주식회사 포스코 점 용접성이 우수한 아연도금강판 및 그 제조방법
EP4163404A1 (en) * 2020-06-08 2023-04-12 Nippon Steel Corporation Steel sheet and manufacturing method therefor

Also Published As

Publication number Publication date
WO2022230400A1 (ja) 2022-11-03
CN116897214A (zh) 2023-10-17
US20230399727A1 (en) 2023-12-14
EP4332262A1 (en) 2024-03-06
JPWO2022230400A1 (es) 2022-11-03
KR20230146082A (ko) 2023-10-18

Similar Documents

Publication Publication Date Title
MX2023009752A (es) Lamina de acero y lamina de acero enchapada.
TW200712223A (en) High strength steel sheet and method for manufacturing the same
JP2013139065A (ja) 高速断続切削加工で硬質被覆層がすぐれた耐チッピング性を発揮する表面被覆切削工具
EP3597718B1 (en) Sintered friction material for brake
EP2965857A1 (en) Welded metal and welded structure provided with same
JP2016098393A (ja) 超硬合金
JP2009024214A (ja) 超硬合金およびその製造方法
KR20180008733A (ko) 철기 분말 야금용 혼합 분말 및 그것을 이용하여 제작한 소결체
JP2009248217A (ja) 硬質被覆層が高速重切削加工ですぐれた耐チッピング性、耐摩耗性を発揮する表面被覆切削工具
MX2023009875A (es) Lamina de acero y lamina de acero enchapada.
MX2023011171A (es) Lamina de acero y lamina de acero enchapada.
WO2011135289A2 (en) Composite metal
JP5477767B2 (ja) 硬質被覆層がすぐれた耐チッピング性を発揮する表面被覆切削工具
US9656371B2 (en) High-hardness atomized powder, powder for projecting material for shot peening, and shot peening method using same
AU2017101636A4 (en) A new wear resistant powder with a much finer particle size (0.07 to 0.15mm) for hard facing
CN113061795A (zh) 一种铝合金表面激光合金化材料、耐磨涂层及其制备方法和应用
JPS626736B2 (es)
JP2011230279A (ja) ショットピーニング用高硬度投射材
WO2019111852A1 (ja) 熱伝導性組成物
WO2018101249A1 (ja) 導電性支持部材及びその製造方法
MX2023012001A (es) Lamina de acero galvanizada por inmersion en caliente con aleacion.
Guang-yao et al. Effect of rare earth on the microstructure and tribological properties of laser cladding Ni-based coatings on 6063 Al
Pötschke et al. Manufacturing and properties of polycrystalline WC-Co based cemented carbides
JP5892335B2 (ja) 硬質被覆層がすぐれた耐チッピング性を備える表面被覆切削工具
JP2006218546A (ja) 硬質被覆層が高速断続切削加工ですぐれた耐チッピング性を発揮する表面被覆サーメット製切削工具