MX2023011171A - Lamina de acero y lamina de acero enchapada. - Google Patents
Lamina de acero y lamina de acero enchapada.Info
- Publication number
- MX2023011171A MX2023011171A MX2023011171A MX2023011171A MX2023011171A MX 2023011171 A MX2023011171 A MX 2023011171A MX 2023011171 A MX2023011171 A MX 2023011171A MX 2023011171 A MX2023011171 A MX 2023011171A MX 2023011171 A MX2023011171 A MX 2023011171A
- Authority
- MX
- Mexico
- Prior art keywords
- steel sheet
- sup
- oxide
- î1⁄4m
- pieces
- Prior art date
Abstract
La presente invención se refiere a una lámina de acero de alta resistencia y lámina de acero enchapada que tiene alta capacidad de chapado, resistencia a LME, y resistencia a la fragilización de hidrógeno, es decir, lámina de acero que contiene C: 0.05 a 0.40%, Si: 0.2 a 3.0%, Mn: 0.1 a 5.0%, y Al sol.: 0.4 a 1.50%, que tiene una capa de oxidación interna que incluye óxidos granulares finos y óxidos granulares gruesos en una capa de superficie de la lámina de acero, una densidad numérica de óxidos granulares finos en la capa de oxidación interna siendo 4.0/µm2 o más, una densidad numérica de óxidos granulares gruesos en la capa de oxidación interna siendo 4.0/25 µm2 o más, u 30.0/25 µm2 o menos, y que incluye una capa empobrecida en la superficie con una composición de acero que no incluye oxides que satisfacen, por % en masa, Si = 0.6% y Al = 0.05% a una profundidad de 1/2 de la profundidad promedio de la capa de oxidación interna calculada de la sección transversal a la imagen de SEM de la lámina de acero, y una lámina de acero enchapada usando la misma.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021075169 | 2021-04-27 | ||
PCT/JP2022/011400 WO2022230401A1 (ja) | 2021-04-27 | 2022-03-14 | 鋼板及びめっき鋼板 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2023011171A true MX2023011171A (es) | 2023-09-29 |
Family
ID=83847394
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2023011171A MX2023011171A (es) | 2021-04-27 | 2022-03-14 | Lamina de acero y lamina de acero enchapada. |
Country Status (7)
Country | Link |
---|---|
US (1) | US20240117475A1 (es) |
EP (1) | EP4332263A1 (es) |
JP (1) | JPWO2022230401A1 (es) |
KR (1) | KR20230159559A (es) |
CN (1) | CN116940704A (es) |
MX (1) | MX2023011171A (es) |
WO (1) | WO2022230401A1 (es) |
Family Cites Families (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5672743B2 (ja) * | 2009-03-31 | 2015-02-18 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5521520B2 (ja) * | 2009-12-03 | 2014-06-18 | 新日鐵住金株式会社 | 合金化溶融亜鉛めっき鋼板およびその製造方法 |
JP5982906B2 (ja) * | 2012-03-19 | 2016-08-31 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
JP2018193614A (ja) | 2013-07-12 | 2018-12-06 | 株式会社神戸製鋼所 | めっき性、加工性、および耐遅れ破壊特性に優れた高強度めっき鋼板、並びにその製造方法 |
WO2016111273A1 (ja) * | 2015-01-09 | 2016-07-14 | 株式会社神戸製鋼所 | 高強度めっき鋼板、並びにその製造方法 |
MX2017009017A (es) | 2015-01-09 | 2018-04-13 | Kobe Steel Ltd | Lamina de acero chapada de alta resistencia y metodo para su produccion. |
BR112020008427A2 (pt) * | 2017-12-15 | 2020-11-17 | Nippon Steel Corporation | chapa de aço, chapa de aço galvanizado por imersão a quente e chapa de aço galvanizado e recozido |
WO2019130713A1 (ja) * | 2017-12-27 | 2019-07-04 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
KR102200175B1 (ko) * | 2018-12-19 | 2021-01-08 | 주식회사 포스코 | 점 용접성이 우수한 아연도금강판 및 그 제조방법 |
US20230183833A1 (en) * | 2020-06-08 | 2023-06-15 | Nippon Steel Corporation | Steel sheet and method for producing same |
-
2022
- 2022-03-14 JP JP2023517130A patent/JPWO2022230401A1/ja active Pending
- 2022-03-14 US US18/274,960 patent/US20240117475A1/en active Pending
- 2022-03-14 KR KR1020237036058A patent/KR20230159559A/ko unknown
- 2022-03-14 CN CN202280017870.2A patent/CN116940704A/zh active Pending
- 2022-03-14 WO PCT/JP2022/011400 patent/WO2022230401A1/ja active Application Filing
- 2022-03-14 MX MX2023011171A patent/MX2023011171A/es unknown
- 2022-03-14 EP EP22795324.7A patent/EP4332263A1/en active Pending
Also Published As
Publication number | Publication date |
---|---|
KR20230159559A (ko) | 2023-11-21 |
US20240117475A1 (en) | 2024-04-11 |
JPWO2022230401A1 (es) | 2022-11-03 |
EP4332263A1 (en) | 2024-03-06 |
WO2022230401A1 (ja) | 2022-11-03 |
CN116940704A (zh) | 2023-10-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2023009752A (es) | Lamina de acero y lamina de acero enchapada. | |
Li et al. | Effects of peak current density on the mechanical properties of nanocrystalline Ni–Co alloys produced by pulse electrodeposition | |
Yan et al. | Surface modification of SKD 61 during EDM with metal powder in the dielectric | |
MX357963B (es) | Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, con excelentes caracteristicas mecanicas de corte, lamina de acero galvanizado por inmersion en caliente, aleada, de alta resistencia y metodo para producir dichas laminas. | |
TW200613054A (en) | Robust spray-dried ziegler-natta procatalyst and polymerization process employing same | |
Prabhakar et al. | Producing Al5083-CNT composites by friction stir processing: influence of grain refinement and CNT on mechanical and corrosion properties | |
MX2023011171A (es) | Lamina de acero y lamina de acero enchapada. | |
CN106270840A (zh) | 一种放电表面处理用固液两相混合工作介质 | |
MX2021007922A (es) | Miembro de acero revestido, lamina de acero revestida, y metodos para producir los mismos. | |
JP2009024214A (ja) | 超硬合金およびその製造方法 | |
MX2023009875A (es) | Lamina de acero y lamina de acero enchapada. | |
Yanhai et al. | Effect of PTFE addition on the properties of electroless Ni-Cu-P-PTFE deposits | |
Tan et al. | High‐Cycle Fatigue Properties of Ultrafine‐Scale Cu/Ni Laminated Composites | |
MX2023012001A (es) | Lamina de acero galvanizada por inmersion en caliente con aleacion. | |
CN109576542A (zh) | 一种耐磨电源外壳铝型材 | |
Yue et al. | Laser cladding of Cu0. 5NiAlCoCrFeSi high entropy alloy on AZ91D magnesium substrates for improving wear and corrosion resistance | |
JP2010095794A (ja) | Co−Fe−Ni系合金スパッタリングターゲット材の製造方法 | |
CN104264097A (zh) | 一种CBN-TiO2涂层及其制备方法 | |
MX2022012141A (es) | Chapa de acero, miembro, y metodo para producirlos. | |
JP2009056561A (ja) | 表面被覆切削工具 | |
JP2011230279A (ja) | ショットピーニング用高硬度投射材 | |
Liu et al. | Metallic glass-strengthened thermoplastic elastomer composites | |
Allahkaram et al. | EVALUATION OF ELECTROLESS NI-P AND NI-P NANO-COMPOSITE COATINGS'PROPERTIES | |
JPS626736B2 (es) | ||
Guang-yao et al. | Effect of rare earth on the microstructure and tribological properties of laser cladding Ni-based coatings on 6063 Al |