MX2022000631A - Metodo para producir una pieza de acero y una pieza de acero. - Google Patents

Metodo para producir una pieza de acero y una pieza de acero.

Info

Publication number
MX2022000631A
MX2022000631A MX2022000631A MX2022000631A MX2022000631A MX 2022000631 A MX2022000631 A MX 2022000631A MX 2022000631 A MX2022000631 A MX 2022000631A MX 2022000631 A MX2022000631 A MX 2022000631A MX 2022000631 A MX2022000631 A MX 2022000631A
Authority
MX
Mexico
Prior art keywords
temperature
steel
steel part
product
semi
Prior art date
Application number
MX2022000631A
Other languages
English (en)
Inventor
Bernard Resiak
Marion Frotey
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2022000631A publication Critical patent/MX2022000631A/es

Abstract

Método para producir una pieza de acero que comprende: - proporcionar un producto semiacabado de un acero que comprenda, en peso 0.35% = C = 0.60% 0.15% = Si = 0.5%. 0.8% = Mn = 2.0%. 0.0003% = B = 0.01% 0.003% = Mo = 1.0%. 1.0% = Cr = 2.0% 0.01% = Ti = 0.04% 0.003% = N = 0.01% S = 0.015% P = 0.015% 0.01% = Ni = 1.0%. 0.01% = Nb = 0.1% opcionalmente 0 = Al = 0.1%. 0 = V = 0.5% el resto consiste en hierro e impurezas inevitables, - recocer este producto semiacabado a una temperatura estrictamente inferior a la temperatura Ac1 del acero; - conformar en frío el producto semiacabado en un producto conformado en frío; - someter el producto conformado en frío a un tratamiento térmico que comprende: - calentar el producto conformado en frío hasta una temperatura mayor o igual a la temperatura Ac3 del acero; y - mantener el producto a una temperatura de mantenimiento comprendida entre 300°C y 400°C durante un tiempo comprendido entre 15 minutos y 2 horas.
MX2022000631A 2019-07-16 2020-07-16 Metodo para producir una pieza de acero y una pieza de acero. MX2022000631A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2019/056061 WO2021009543A1 (en) 2019-07-16 2019-07-16 Method for producing a steel part and steel part
PCT/IB2020/056695 WO2021009705A1 (en) 2019-07-16 2020-07-16 Method for producing a steel part and steel part

Publications (1)

Publication Number Publication Date
MX2022000631A true MX2022000631A (es) 2022-03-11

Family

ID=67515035

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2022000631A MX2022000631A (es) 2019-07-16 2020-07-16 Metodo para producir una pieza de acero y una pieza de acero.

Country Status (13)

Country Link
US (1) US20220259693A1 (es)
EP (1) EP3999667B1 (es)
JP (1) JP7422854B2 (es)
CN (1) CN114096693B (es)
BR (1) BR112022000640A2 (es)
CA (1) CA3147223A1 (es)
FI (1) FI3999667T3 (es)
HU (1) HUE064880T2 (es)
MA (1) MA57970B1 (es)
MX (1) MX2022000631A (es)
PL (1) PL3999667T3 (es)
WO (2) WO2021009543A1 (es)
ZA (1) ZA202200328B (es)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9998914B2 (en) 2014-04-16 2018-06-12 Jamf Software, Llc Using a mobile device to restrict focus and perform operations at another mobile device
EP4355920A1 (en) * 2021-06-16 2024-04-24 ArcelorMittal Method for producing a steel part and steel part
EP4190934A1 (de) 2021-12-02 2023-06-07 KAMAX Holding GmbH & Co. KG Bauteil aus b-zr-legiertem stahl

Family Cites Families (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000054075A (ja) * 1998-07-31 2000-02-22 Nippon Steel Corp 電気伝導性および耐ころがり疲労損傷性に優れたベイナイト系レール
JP2001011575A (ja) * 1999-06-30 2001-01-16 Nippon Steel Corp 冷間加工性に優れた機械構造用棒鋼・鋼線及びその製造方法
JP3989138B2 (ja) * 1999-07-23 2007-10-10 Ｊｆｅ条鋼株式会社 機械加工性に優れた低歪み型浸炭焼入れ歯車用鋼材およびその鋼材による歯車の製造方法
JP4435954B2 (ja) * 1999-12-24 2010-03-24 新日本製鐵株式会社 冷間鍛造用棒線材とその製造方法
CN100436628C (zh) * 2003-01-17 2008-11-26 杰富意钢铁株式会社 高频淬火用钢材、采用该高频淬火用钢材的高频淬火构件及它们的制造方法
EP1767659A1 (fr) * 2005-09-21 2007-03-28 ARCELOR France Procédé de fabrication d'une pièce en acier de microstructure multi-phasée
FR2914929B1 (fr) * 2007-04-12 2010-10-29 Mittal Steel Gandrange Acier a bonne tenue a l'hydrogene pour le formage de pieces mecaniques a tres hautes caracteristiques.
DE102008022399A1 (de) * 2008-05-06 2009-11-19 Thyssenkrupp Steel Ag Verfahren zum Herstellen eines Stahlformteils mit einem überwiegend ferritisch-bainitischen Gefüge
DE102008022401B4 (de) * 2008-05-06 2012-12-06 Thyssenkrupp Steel Europe Ag Verfahren zum Herstellen eines Stahlformteils mit einem überwiegend bainitischen Gefüge
JP5245997B2 (ja) * 2009-04-06 2013-07-24 新日鐵住金株式会社 靭性に優れた高強度熱間鍛造非調質鋼及びその製造方法
CN101654728A (zh) * 2009-09-25 2010-02-24 清华大学 一种锰系淬火贝氏体钢的制备方法
CA2850195C (en) * 2011-09-30 2016-10-25 Nippon Steel & Sumitomo Metal Corporation High-strength hot-dip galvanized steel sheet excellent in impact resistance property and manufacturing method thereof, and high-strength alloyed hot-dip galvanized steel sheet and manufacturing method thereof
CZ2011612A3 (cs) * 2011-09-30 2013-07-10 Západoceská Univerzita V Plzni Zpusob dosazení TRIP struktury ocelí s vyuzitím deformacního tepla
JP5516680B2 (ja) * 2012-09-24 2014-06-11 Ｊｆｅスチール株式会社 電縫溶接部の耐ｈｉｃ性および低温靭性に優れた電縫鋼管およびその製造方法
US20140283960A1 (en) * 2013-03-22 2014-09-25 Caterpillar Inc. Air-hardenable bainitic steel with enhanced material characteristics
KR20140121229A (ko) * 2013-04-05 2014-10-15 태양금속공업주식회사 인장강도가 우수한 고강도 볼트의 제조방법
KR101773729B1 (ko) * 2013-08-26 2017-08-31 신닛테츠스미킨 카부시키카이샤 스티어링 랙 바용 압연 환강재 및 스티어링 랙 바
FR3022259A1 (fr) * 2014-06-16 2015-12-18 Asco Ind Acier pour pieces mecaniques a hautes caracteristiques traitees superficiellement, et pieces mecaniques en cet acier et leur procede de fabrication
WO2016016676A1 (fr) * 2014-07-30 2016-02-04 ArcelorMittal Investigación y Desarrollo, S.L. Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé
WO2016079565A1 (en) * 2014-11-18 2016-05-26 Arcelormittal Method for manufacturing a high strength steel product and steel product thereby obtained
AU2015361346B2 (en) * 2014-12-12 2019-02-28 Nippon Steel Corporation Low-alloy steel for oil well pipe and method for manufacturing low-alloy steel oil well pipe
CN104561829B (zh) * 2014-12-30 2017-05-24 中车戚墅堰机车车辆工艺研究所有限公司 一种铁路辙叉用高耐磨钢及其制造方法
CN104831189B (zh) * 2015-04-16 2016-08-24 河北钢铁股份有限公司 Hb600级非调质耐磨钢板及其制造方法
DK3168312T3 (da) * 2015-11-16 2019-07-01 Deutsche Edelstahlwerke Specialty Steel Gmbh & Co Kg Konstruktionsædelstål med bainitisk struktur, smedeemne fremstillet deraf og fremgangsmåde til fremstilling af et smedeemne
EP3486346B1 (en) * 2016-09-28 2020-08-12 JFE Steel Corporation Steel sheet and method of producing the same
CN108396220A (zh) * 2017-02-05 2018-08-14 鞍钢股份有限公司 一种高强高韧性镀锌钢板及其制造方法
JP6849536B2 (ja) * 2017-05-31 2021-03-24 株式会社神戸製鋼所 高強度鋼板およびその製造方法

Also Published As

Publication number Publication date
KR20220024526A (ko) 2022-03-03
JP2022540899A (ja) 2022-09-20
EP3999667B1 (en) 2023-12-20
EP3999667A1 (en) 2022-05-25
MA57970B1 (fr) 2024-03-29
BR112022000640A2 (pt) 2022-03-03
WO2021009705A1 (en) 2021-01-21
CN114096693A (zh) 2022-02-25
PL3999667T3 (pl) 2024-04-02
WO2021009543A1 (en) 2021-01-21
HUE064880T2 (hu) 2024-04-28
FI3999667T3 (fi) 2024-01-31
CN114096693B (zh) 2023-05-16
JP7422854B2 (ja) 2024-01-26
US20220259693A1 (en) 2022-08-18
ZA202200328B (en) 2022-07-27
CA3147223A1 (en) 2021-01-21

Similar Documents

Publication Publication Date Title
MX2017006303A (es) Metodo para fabricar un producto de acero de alta resistencia y un producto de acero obtenido por el mismo.
MX2022000631A (es) Metodo para producir una pieza de acero y una pieza de acero.
MX2016017400A (es) Metodo para fabricar una hoja de acero de alta resistencia y hoja obtenida.
MX371103B (es) Metodo para producir material de acero de alta resistencia, excelente en resistencia a agrietamiento por tension de sulfuro.
JP2020501017A5 (es)
MX2009009769A (es) Acero para formacion en caliente o enfriamiento en una herramienta, que tiene ductilidad mejorada.
MX2017000177A (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia, ductilidad y capacidad de formacion mejoradas.
MX2016011987A (es) Metodo para producir un producto de acero plano laminado en frio con alto limite elastico y producto de acero plano laminado en frio.
IN2014CN02685A (es)
RU2014101779A (ru) Способ изготовления высокопрочной конструкционной стали и изделие из высокопрочной конструкционной стали
MX2019014873A (es) Alambre laminado para acero de resorte.
RU2016110765A (ru) Высокотвердая горячекатаная стальная продукция и способ ее производства
CA2702427A1 (en) Method of production of 780 mpa class high strength steel plate excellent in low temperature toughness
MX2018012841A (es) Metodo para fabricar una parte de acero inoxidable martensitico a partir de lamina.
MX2016017398A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida.
WO2016001895A3 (en) Method for producing a high strength coated steel sheet having improved strength, ductility and formability
FI20195799A1 (fi) Hienojakoisen austeniittisen ruostumattoman teräksen valmistusmenetelmä
MX2017000201A (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia y capacidad de formacion mejoradas y hoja obtenida.
MX2021007215A (es) Hoja de acero laminada en frio y tratada termicamente y metodo de fabricacion de la misma.
MX2013005011A (es) Hoja de acero laminado de frio de alta resistencia que tiene capacidad de embuticion profunda y capacidad de temple en horno excelentes y metodo para su fabricacion.
MX2017000192A (es) Metodo para producir una chapa de acero revestida o no revestida de resistencia ultra alta y chapa obtenida.
MX2021014042A (es) Acero, barra de acero y metodo de fabricacion de los mismos.
UA118706C2 (uk) Спосіб виробництва сталевого листа з покриттям, що має підвищену міцність, пластичність і деформованість
MX2017016905A (es) Acero resistente a la corrosion, metodo para producir dicho acero y uso del mismo.
MX2018011206A (es) Hoja de acero inoxidable ferritico que contiene nb y metodo de fabricacion de la misma.