MA57970B1 - Procédé de production d'une pièce en acier, et pièce en acier - Google Patents

Procédé de production d'une pièce en acier, et pièce en acier

Info

Publication number
MA57970B1
MA57970B1 MA57970A MA57970A MA57970B1 MA 57970 B1 MA57970 B1 MA 57970B1 MA 57970 A MA57970 A MA 57970A MA 57970 A MA57970 A MA 57970A MA 57970 B1 MA57970 B1 MA 57970B1
Authority
MA
Morocco
Prior art keywords
temperature
steel
cold
steel part
product
Prior art date
Application number
MA57970A
Other languages
English (en)
Inventor
Bernard Resiak
Marion Frotey
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MA57970B1 publication Critical patent/MA57970B1/fr

Abstract

L'invention concerne un procédé de production d'une pièce en acier consistant : à fournir un produit semi-fini constitué d'un acier comprenant, en poids : 0,35 % = c = 0,60 %, 0,15 % = si = 0,5 %, 0,8 % = mn = 2,0 %, 0,0003 % = b = 0,01 %, 0,003 % = mo = 1,0 %, 1,0 % = cr = 2,0 %, 0,01 % = ti = 0,04 %, 0,003 % = n = 0,01 %, s = 0,015 %, p = 0,015 %, 0,01 % = ni = 1,0 %, 0,01 % = nb = 0,1 %, éventuellement 0 = al = 0,1 %, 0 = v = 0,5 %, le reste étant constitué de fer et d'impuretés inévitables ; à recuire ce produit semi-fini à une température strictement inférieure à la température ac1 de l'acier ; à former à froid le produit semi-fini pour obtenir un produit formé à froid ; à soumettre le produit formé à froid à un traitement thermique consistant : à chauffer le produit formé à froid à une température supérieure ou égale à la température ac3 de l'acier ; et à maintenir le produit à une température de maintien comprise entre 300 °c et 400 °c pendant une durée comprise entre 15 minutes et 2 heures.
MA57970A 2019-07-16 2020-07-16 Procédé de production d'une pièce en acier, et pièce en acier MA57970B1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2019/056061 WO2021009543A1 (fr) 2019-07-16 2019-07-16 Procédé de production de pièce en acier et pièce en acier
PCT/IB2020/056695 WO2021009705A1 (fr) 2019-07-16 2020-07-16 Procédé de production d'une pièce en acier, et pièce en acier

Publications (1)

Publication Number Publication Date
MA57970B1 true MA57970B1 (fr) 2024-03-29

Family

ID=67515035

Family Applications (1)

Application Number Title Priority Date Filing Date
MA57970A MA57970B1 (fr) 2019-07-16 2020-07-16 Procédé de production d'une pièce en acier, et pièce en acier

Country Status (14)

Country Link
US (1) US20220259693A1 (fr)
EP (1) EP3999667B1 (fr)
JP (1) JP7422854B2 (fr)
KR (1) KR102668389B1 (fr)
CN (1) CN114096693B (fr)
CA (1) CA3147223A1 (fr)
ES (1) ES2971131T3 (fr)
FI (1) FI3999667T3 (fr)
HU (1) HUE064880T2 (fr)
MA (1) MA57970B1 (fr)
MX (1) MX2022000631A (fr)
PL (1) PL3999667T3 (fr)
WO (2) WO2021009543A1 (fr)
ZA (1) ZA202200328B (fr)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9998914B2 (en) 2014-04-16 2018-06-12 Jamf Software, Llc Using a mobile device to restrict focus and perform operations at another mobile device
MX2023014918A (es) * 2021-06-16 2024-02-14 Arcelormittal Metodo para producir una pieza de acero y la pieza de acero.
EP4190934A1 (fr) 2021-12-02 2023-06-07 KAMAX Holding GmbH & Co. KG Composant en acier allié b-zr

Family Cites Families (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000054075A (ja) * 1998-07-31 2000-02-22 Nippon Steel Corp 電気伝導性および耐ころがり疲労損傷性に優れたベイナイト系レール
JP2001011575A (ja) 1999-06-30 2001-01-16 Nippon Steel Corp 冷間加工性に優れた機械構造用棒鋼・鋼線及びその製造方法
JP3989138B2 (ja) * 1999-07-23 2007-10-10 Ｊｆｅ条鋼株式会社 機械加工性に優れた低歪み型浸炭焼入れ歯車用鋼材およびその鋼材による歯車の製造方法
JP4435954B2 (ja) * 1999-12-24 2010-03-24 新日本製鐵株式会社 冷間鍛造用棒線材とその製造方法
CN100436628C (zh) * 2003-01-17 2008-11-26 杰富意钢铁株式会社 高频淬火用钢材、采用该高频淬火用钢材的高频淬火构件及它们的制造方法
EP1767659A1 (fr) * 2005-09-21 2007-03-28 ARCELOR France Procédé de fabrication d'une pièce en acier de microstructure multi-phasée
FR2914929B1 (fr) * 2007-04-12 2010-10-29 Mittal Steel Gandrange Acier a bonne tenue a l'hydrogene pour le formage de pieces mecaniques a tres hautes caracteristiques.
DE102008022399A1 (de) * 2008-05-06 2009-11-19 Thyssenkrupp Steel Ag Verfahren zum Herstellen eines Stahlformteils mit einem überwiegend ferritisch-bainitischen Gefüge
DE102008022401B4 (de) * 2008-05-06 2012-12-06 Thyssenkrupp Steel Europe Ag Verfahren zum Herstellen eines Stahlformteils mit einem überwiegend bainitischen Gefüge
JP2009293106A (ja) * 2008-06-09 2009-12-17 Nisshin Steel Co Ltd 高温導電性酸化物皮膜および通電材料
JP5484103B2 (ja) * 2009-02-17 2014-05-07 日新製鋼株式会社 高強度機械部品用素材鋼板およびその製造方法並びに高強度機械部品製造方法
JP5245997B2 (ja) 2009-04-06 2013-07-24 新日鐵住金株式会社 靭性に優れた高強度熱間鍛造非調質鋼及びその製造方法
CN101654728A (zh) * 2009-09-25 2010-02-24 清华大学 一种锰系淬火贝氏体钢的制备方法
US8932729B2 (en) * 2011-09-30 2015-01-13 Nippon Steel & Sumitomo Metal Corporation High-strength hot-dip galvanized steel sheet excellent in impact resistance property and high-strength alloyed hot-dip galvanized steel sheet
CZ2011612A3 (cs) 2011-09-30 2013-07-10 Západoceská Univerzita V Plzni Zpusob dosazení TRIP struktury ocelí s vyuzitím deformacního tepla
JP5516680B2 (ja) * 2012-09-24 2014-06-11 Ｊｆｅスチール株式会社 電縫溶接部の耐ｈｉｃ性および低温靭性に優れた電縫鋼管およびその製造方法
US20140283960A1 (en) * 2013-03-22 2014-09-25 Caterpillar Inc. Air-hardenable bainitic steel with enhanced material characteristics
KR20140121229A (ko) * 2013-04-05 2014-10-15 태양금속공업주식회사 인장강도가 우수한 고강도 볼트의 제조방법
PL3040435T3 (pl) * 2013-08-26 2018-04-30 Nippon Steel & Sumitomo Metal Corporation Walcowany okrągły materiał stalowy do pręta zębatki kierowniczej oraz pręt zębatki kierowniczej
FR3022259A1 (fr) * 2014-06-16 2015-12-18 Asco Ind Acier pour pieces mecaniques a hautes caracteristiques traitees superficiellement, et pieces mecaniques en cet acier et leur procede de fabrication
WO2016016676A1 (fr) * 2014-07-30 2016-02-04 ArcelorMittal Investigación y Desarrollo, S.L. Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé
WO2016079565A1 (fr) * 2014-11-18 2016-05-26 Arcelormittal Procédé de fabrication d'un produit en acier haute résistance et produit en acier ainsi obtenu
AU2015361346B2 (en) * 2014-12-12 2019-02-28 Nippon Steel Corporation Low-alloy steel for oil well pipe and method for manufacturing low-alloy steel oil well pipe
CN104561829B (zh) * 2014-12-30 2017-05-24 中车戚墅堰机车车辆工艺研究所有限公司 一种铁路辙叉用高耐磨钢及其制造方法
CN104831189B (zh) * 2015-04-16 2016-08-24 河北钢铁股份有限公司 Hb600级非调质耐磨钢板及其制造方法
DK3168312T3 (da) * 2015-11-16 2019-07-01 Deutsche Edelstahlwerke Specialty Steel Gmbh & Co Kg Konstruktionsædelstål med bainitisk struktur, smedeemne fremstillet deraf og fremgangsmåde til fremstilling af et smedeemne
MX2019002324A (es) * 2016-09-28 2019-07-04 Jfe Steel Corp Lamina de acero y metodo para producir la misma.
CN108396220A (zh) * 2017-02-05 2018-08-14 鞍钢股份有限公司 一种高强高韧性镀锌钢板及其制造方法
JP6849536B2 (ja) 2017-05-31 2021-03-24 株式会社神戸製鋼所 高強度鋼板およびその製造方法
WO2019122964A1 (fr) * 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication

Also Published As

Publication number Publication date
WO2021009705A1 (fr) 2021-01-21
CN114096693B (zh) 2023-05-16
HUE064880T2 (hu) 2024-04-28
JP2022540899A (ja) 2022-09-20
BR112022000640A2 (pt) 2022-03-03
MX2022000631A (es) 2022-03-11
EP3999667A1 (fr) 2022-05-25
WO2021009543A1 (fr) 2021-01-21
EP3999667B1 (fr) 2023-12-20
CN114096693A (zh) 2022-02-25
ZA202200328B (en) 2022-07-27
PL3999667T3 (pl) 2024-04-02
JP7422854B2 (ja) 2024-01-26
US20220259693A1 (en) 2022-08-18
KR20220024526A (ko) 2022-03-03
KR102668389B1 (ko) 2024-05-22
CA3147223A1 (fr) 2021-01-21
FI3999667T3 (fi) 2024-01-31
ES2971131T3 (es) 2024-06-03

Similar Documents

Publication Publication Date Title
JP7068434B2 (ja) 高強度鋼板を製造する方法
MA57970B1 (fr) Procédé de production d'une pièce en acier, et pièce en acier
JP6475861B2 (ja) ホットスタンピングに使用される鋼板、ホットスタンピングプロセスおよびホットスタンピングコンポーネント
MA44120B1 (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité et une aptitude au formage améliorées et tôle d'acier ainsi obtenue
US9194017B2 (en) Hot-rolled steel sheet having excellent cold formability and hardenability and method for manufacturing the same
US12054816B2 (en) Automotive steel and a method for the fabrication of the same
MA49159B1 (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle d'acier à haute résistance ainsi obtenue
MA44107B1 (fr) Procédé de fabrication d'une tôle d'acier à haute résistance présentant une ductilité et une formabilité améliorées et tôle d'acier obtenue par ce procédé
CN106133177B (zh) 奥氏体不锈钢
RU2017117067A (ru) Способ изготовления высокопрочного стального изделия и стальное изделие, полученное таким образом
MX2019006862A (es) Producto de acero plano laminado en caliente y metodo para la produccion del mismo.
MA47181A (fr) Procédé de fabrication d'une tôle d'acier à ultra-haute résistance revêtue et tôle obtenue
RU2016110765A (ru) Высокотвердая горячекатаная стальная продукция и способ ее производства
KR101674750B1 (ko) 표면 경화 열처리성이 우수한 중탄소강 비조질 선재 및 이의 제조방법
KR20050083912A (ko) 내마모성 강판 제조 방법 및 제조된 강판
RU2014135395A (ru) Многофазная сталь максимальной прочности с улучшенными свойствами в процессе изготовления и переработки
CN105008570A (zh) 厚壁高韧性高张力钢板及其制造方法
FI3164520T4 (fi) Menetelmä parannellun lujuuden, sitkeyden ja muokattavuuden omaavan korkealujuusteräslevyn tuottamiseksi
US20140338797A1 (en) High Strength Steel Exhibiting Good Ductility and Method of Production via In-Line Heat Treatment Downstream of Molten Zinc Bath
MA49777B1 (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle ainsi obtenue
KR102298180B1 (ko) 망간 함유 평탄 강으로 이루어지는 평탄 강 제품을 제조하는 방법 및 이러한 평탄 강 제품
WO2012164579A4 (fr) Acier bainitique à haute résistance et fort
MA43505B1 (fr) Procédé destiné à la production d'une tôle d'acier recuite après galvanisation à très haute résistance et tôle d'acier recuite après galvanisation obtenue
MA44134B1 (fr) Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
KR20210044260A (ko) 구멍 확장비가 높은 열간 압연된 강 시트 및 이의 제조 방법