MX2016011987A - Metodo para producir un producto de acero plano laminado en frio con alto limite elastico y producto de acero plano laminado en frio. - Google Patents

Metodo para producir un producto de acero plano laminado en frio con alto limite elastico y producto de acero plano laminado en frio.

Info

Publication number
MX2016011987A
MX2016011987A MX2016011987A MX2016011987A MX2016011987A MX 2016011987 A MX2016011987 A MX 2016011987A MX 2016011987 A MX2016011987 A MX 2016011987A MX 2016011987 A MX2016011987 A MX 2016011987A MX 2016011987 A MX2016011987 A MX 2016011987A
Authority
MX
Mexico
Prior art keywords
less
cold
rolled
steel product
steel
Prior art date
Application number
MX2016011987A
Other languages
English (en)
Inventor
Heller Thomas
Hammer Brigitte
Kaneko Shinjiro
Hisker Frank
Dzafic Almir
G Thiessen Richard
Shiimori Fusae
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2016011987A publication Critical patent/MX2016011987A/es

Abstract

La invención proporciona un método para producir un tira de acero laminado en frío con una relación de elasticidad Re/Rm de por lo menos 0.7, el producto de acero laminado en frío consiste de un acero que comprende hierro, impurezas inevitables de producción y (% en peso) C: 0.05 - 0.20%, Si: 0.25 - 1.00%, Mn: 1.0 - 3.0%, Al: 0.02 - 1.5%, Cr: 0.1 - 1.5%, N: menos de 0.02%, P: menos de 0.03%, S: menos de 0.05% y opcionalmente uno o más elementos del grupo "Ti, Mo, Nb, V, B" propenso a Ti: siendo de hasta 0.15%, Mo: menos de 2%, Nb: menos de 0.1%, V: menos de 0.12%, y B: 0.0005 - 0.003%. De acuerdo con la invención el producto de acero plano laminado en frío proporcionado experimenta un tratamiento térmico adicional, durante el cual es recocido durante un tiempo de recocido de 4.5 - 24 horas a una temperatura de recocido de hasta 150 - 400°C. Sorprendentemente, se revela que como resultado de tal recocido de larga duración llevado a cabo a temperaturas comparativamente bajas ocurre un aumento dramático en el límite elástico Re y una mejora en la expansión del orificio. La invención también proporciona un producto de acero plano laminado en frío que consiste en el acero mencionado anteriormente y que tiene una estructura que comprende por lo menos dos fases, que (en % en vol.) contiene por lo menos 10% de martensita templada, menos de 10% de bainita, menos de 10% de austenita residual y ferrita como el resto, el acero que tiene una relación de elasticidad Re/Rm de por lo menos 0.7, una resistencia a la tensión R de más de 750 MPa y una expansión del orificio LA de por lo menos 18%.
MX2016011987A 2014-04-15 2015-04-14 Metodo para producir un producto de acero plano laminado en frio con alto limite elastico y producto de acero plano laminado en frio. MX2016011987A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102014105396 2014-04-15
PCT/EP2015/058101 WO2015158731A1 (en) 2014-04-15 2015-04-14 Method for producing a cold-rolled flat steel product with high yield strength and flat cold-rolled steel product

Publications (1)

Publication Number Publication Date
MX2016011987A true MX2016011987A (es) 2017-04-06

Family

ID=53002660

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2016011987A MX2016011987A (es) 2014-04-15 2015-04-14 Metodo para producir un producto de acero plano laminado en frio con alto limite elastico y producto de acero plano laminado en frio.

Country Status (8)

Country Link
US (1) US10435763B2 (es)
EP (1) EP3132063B1 (es)
JP (1) JP6533528B2 (es)
KR (1) KR102419630B1 (es)
CN (1) CN106232852B (es)
CA (1) CA2947382C (es)
MX (1) MX2016011987A (es)
WO (1) WO2015158731A1 (es)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116065103A (zh) * 2021-11-01 2023-05-05 上海梅山钢铁股份有限公司 一种低成本屈服强度550MPa级高扩孔热轧酸洗钢板

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107406938B (zh) 2015-03-03 2019-07-26 杰富意钢铁株式会社 高强度钢板及其制造方法
WO2017125773A1 (en) 2016-01-18 2017-07-27 Arcelormittal High strength steel sheet having excellent formability and a method of manufacturing the same
EP3610049A1 (de) * 2017-04-11 2020-02-19 ThyssenKrupp Steel Europe AG Kaltgewalztes, haubengeglühtes stahlflachprodukt und verfahren zu dessen herstellung
CN110944765B (zh) * 2017-07-25 2022-02-25 蒂森克虏伯钢铁欧洲股份公司 通过热成型扁钢产品生产的金属板构件及其生产方法
KR102075222B1 (ko) * 2017-12-26 2020-02-07 주식회사 포스코 재질편차가 적고, 신장플랜지성 및 실수율이 우수한 고강도 냉연강판 및 그 제조방법
KR20210127922A (ko) 2019-02-18 2021-10-25 타타 스틸 이즈무이덴 베.뷔. 기계적 특성이 개선된 고강도 강
CN110117755B (zh) * 2019-05-21 2020-11-03 安徽工业大学 一种980MPa级低屈强比冷轧中锰钢的制备方法
CN111187893B (zh) * 2020-02-24 2021-06-29 攀钢集团攀枝花钢铁研究院有限公司 增强780dp高扩孔冷轧双相钢均一性的方法
EP3872193A1 (de) 2020-02-26 2021-09-01 ThyssenKrupp Steel Europe AG Verfahren zur herstellung eines warmgewalzten stahlflachprodukts und stahlflachprodukt
EP3872206B1 (de) 2020-02-28 2023-06-21 ThyssenKrupp Steel Europe AG Verfahren zur herstellung eines nachbehandelten, kaltgewalzten stahlflachprodukts und nachbehandeltes, kaltgewalztes stahlflachprodukt
CN113737108A (zh) * 2020-05-27 2021-12-03 宝山钢铁股份有限公司 一种耐延迟开裂的电镀锌超强双相钢及其制造方法
CN114058941A (zh) * 2020-07-31 2022-02-18 宝山钢铁股份有限公司 一种冷轧钢板及制造方法和汽车用冲裁件
SE545210C2 (en) * 2020-12-23 2023-05-23 Voestalpine Stahl Gmbh Coiling temperature influenced cold rolled strip or steel
CN114763595B (zh) * 2021-01-15 2023-07-07 宝山钢铁股份有限公司 一种冷轧钢板以及冷轧钢板的制造方法

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101821419B (zh) * 2007-10-25 2015-03-18 杰富意钢铁株式会社 加工性优良的高强度热镀锌钢板及其制造方法
JP5365216B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
JP5365217B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5369663B2 (ja) * 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5376927B2 (ja) 2008-12-11 2013-12-25 日新製鋼株式会社 曲げ加工性に優れた高比例限鋼板の製造方法
JP2013515167A (ja) 2009-12-21 2013-05-02 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップ 高強度溶融亜鉛めっき鋼帯
JP5446886B2 (ja) 2010-01-06 2014-03-19 新日鐵住金株式会社 冷延鋼板の製造方法
WO2011118126A1 (ja) 2010-03-24 2011-09-29 Ｊｆｅスチール株式会社 超高強度部材の製造方法および使用方法
ES2455222T5 (es) 2010-07-02 2018-03-05 Thyssenkrupp Steel Europe Ag Acero de resistencia superior, conformable en frío y producto plano de acero compuesto de un acero de este tipo
EP2489748B1 (de) * 2011-02-18 2017-12-13 ThyssenKrupp Steel Europe AG Aus einem Komplexphasenstahl hergestelltes warmgewalztes Stahlflachprodukt und Verfahren zu dessen Herstellung
CN103890202B (zh) * 2011-10-24 2015-09-30 杰富意钢铁株式会社 加工性优良的高强度钢板的制造方法
MX371405B (es) 2011-11-28 2020-01-29 Arcelormittal Investig Y Desarrollo S L Aceros de fase doble que llevan alto contenido de silicio con ductilidad mejorada.
DE102012013113A1 (de) 2012-06-22 2013-12-24 Salzgitter Flachstahl Gmbh Hochfester Mehrphasenstahl und Verfahren zur Herstellung eines Bandes aus diesem Stahl mit einer Mindestzugfestigkleit von 580MPa
ES2614465T3 (es) * 2012-07-10 2017-05-31 Thyssenkrupp Steel Europe Ag Producto plano de acero laminado en frío y procedimiento para su fabricación
US10370737B2 (en) * 2015-01-15 2019-08-06 Jfe Steel Corporation High-strength galvanized steel sheet

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116065103A (zh) * 2021-11-01 2023-05-05 上海梅山钢铁股份有限公司 一种低成本屈服强度550MPa级高扩孔热轧酸洗钢板

Also Published As

Publication number Publication date
CN106232852A (zh) 2016-12-14
JP2017514989A (ja) 2017-06-08
JP6533528B2 (ja) 2019-06-19
CA2947382C (en) 2022-07-12
KR20160145656A (ko) 2016-12-20
KR102419630B1 (ko) 2022-07-11
EP3132063A1 (en) 2017-02-22
US20170029917A1 (en) 2017-02-02
CA2947382A1 (en) 2015-10-22
WO2015158731A1 (en) 2015-10-22
EP3132063B1 (en) 2021-01-13
US10435763B2 (en) 2019-10-08
CN106232852B (zh) 2018-12-11

Similar Documents

Publication Publication Date Title
MX2016011987A (es) Metodo para producir un producto de acero plano laminado en frio con alto limite elastico y producto de acero plano laminado en frio.
MX2016017400A (es) Metodo para fabricar una hoja de acero de alta resistencia y hoja obtenida.
WO2016001898A3 (en) Method for producing a high strength steel sheet having improved strength, ductility and formability
MX2017006303A (es) Metodo para fabricar un producto de acero de alta resistencia y un producto de acero obtenido por el mismo.
MX2019006862A (es) Producto de acero plano laminado en caliente y metodo para la produccion del mismo.
UA117865C2 (uk) Високоміцна багатофазна сталь, спосіб її одержання та застосування
RU2689573C2 (ru) Способ изготовления высокопрочного стального листа, обладающего улучшенными прочностью, формуемостью, и полученный лист
WO2016001895A3 (en) Method for producing a high strength coated steel sheet having improved strength, ductility and formability
MX2017000192A (es) Metodo para producir una chapa de acero revestida o no revestida de resistencia ultra alta y chapa obtenida.
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
MX2016017398A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida.
EP3656879A3 (en) Method for manufacturing a high-strength steel sheet and sheet obtained by the method
IN2014CN02685A (es)
JP2017514989A5 (es)
MX350226B (es) Hoja de acero laminado en frio de alta resistencia que tiene capacidad de embuticion profunda y capacidad de temple en horno excelentes y metodo para su fabricacion.
WO2016001887A3 (en) Method for manufacturing a high strength steel sheet having improved formability and sheet obtained
MX356324B (es) Método para la fabricación de acero martensítico con límite de elasticidad muy alto y placa o pieza obtenida por tal método.
MX2017001745A (es) Metodo para producir una hoja de acero recubierta que tiene resistencia, ductilidad y conformabilidad mejoradas.
MX2017000185A (es) Metodo para la fabricacion de una hoja de acero de alta resistencia que tiene formabilidad y ductilidad mejoradas y hoja obtenida.
MX2021015145A (es) Metodo de produccion de lamina de acero revestida de alta resistencia con resistencia y conformabilidad mejoradas.
MX2022000631A (es) Metodo para producir una pieza de acero y una pieza de acero.
TH1601006097A (th) วิธีการสำหรับการผลิตผลิตภัณฑ์เหล็กกล้าแบนรีดเย็นที่มีความแข็งแรงครากสูง และผลิตภัณฑ์เหล็กกล้ารีดเย็นชนิดแบน
MY196420A (en) Steel Sheet for Cans and Method for Manufacturing the same
PL225825B1 (pl) Sposób obróbki cieplnej wyrobów z ultrawytrzymałej stali średniostopowej