MX2017010788A - Lamina de acero recubierta de alta resistencia a la traccion posteriormente recocida que tiene mejor limite elastico y ensanchamiento de orificios. - Google Patents

Lamina de acero recubierta de alta resistencia a la traccion posteriormente recocida que tiene mejor limite elastico y ensanchamiento de orificios.

Info

Publication number
MX2017010788A
MX2017010788A MX2017010788A MX2017010788A MX2017010788A MX 2017010788 A MX2017010788 A MX 2017010788A MX 2017010788 A MX2017010788 A MX 2017010788A MX 2017010788 A MX2017010788 A MX 2017010788A MX 2017010788 A MX2017010788 A MX 2017010788A
Authority
MX
Mexico
Prior art keywords
steel sheet
coated
hole expansion
coated steel
high tensile
Prior art date
Application number
MX2017010788A
Other languages
English (en)
Inventor
JUN Hyun
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2017010788A publication Critical patent/MX2017010788A/es

Abstract

Una lámina de acero laminada en frío recubierta y posteriormente recocida. La lámina de acero laminada en frío puede comprender (en % en peso): C - 0.1 - 0.3%; Mn - 1 - 3%; Si - 0.5 - 3.5%; Al - 0.05 - 1.5%; Mo + Cr está entre 0 - 1.0%; y Mo + Cr está entre 0.2 - 0.5%. La lámina de acero puede recubrirse con un recubrimiento de zinc o aleación de zinc. La lámina de acero recubierta puede formarse mediante laminación en frío, recubrimiento de zinc de la lámina laminada en frío y recocido de dicha lámina de acero después de la aplicación de dicho recubrimiento de zinc. El recocido se lleva a cabo a una temperatura y durante un tiempo suficiente para aumentar significativamente el límite elástico y el ensanchamiento de orificios de la lámina de acero laminada en frío recubierta recocida en comparación con la lámina recubierta.
MX2017010788A 2015-02-25 2016-02-24 Lamina de acero recubierta de alta resistencia a la traccion posteriormente recocida que tiene mejor limite elastico y ensanchamiento de orificios. MX2017010788A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201562120426P 2015-02-25 2015-02-25
PCT/US2016/019428 WO2016138185A1 (en) 2015-02-25 2016-02-24 Post annealed high tensile strength coated steel sheet having improved yield strength and hole expansion

Publications (1)

Publication Number Publication Date
MX2017010788A true MX2017010788A (es) 2018-04-30

Family

ID=55527652

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2017010788A MX2017010788A (es) 2015-02-25 2016-02-24 Lamina de acero recubierta de alta resistencia a la traccion posteriormente recocida que tiene mejor limite elastico y ensanchamiento de orificios.

Country Status (11)

Country Link
US (3) US20180044750A1 (es)
EP (1) EP3262205A1 (es)
JP (2) JP2018510263A (es)
KR (2) KR20190134842A (es)
CN (1) CN107429376B (es)
BR (1) BR112017016683A2 (es)
CA (1) CA2975149C (es)
MX (1) MX2017010788A (es)
RU (1) RU2705741C2 (es)
UA (1) UA120199C2 (es)
WO (1) WO2016138185A1 (es)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114107796A (zh) * 2020-08-31 2022-03-01 宝山钢铁股份有限公司 一种1180MPa级高塑性高扩孔钢及其制造方法
SE545209C2 (en) * 2020-12-23 2023-05-23 Voestalpine Stahl Gmbh Coiling temperature influenced cold rolled strip or steel

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4235030B2 (ja) * 2003-05-21 2009-03-04 新日本製鐵株式会社 局部成形性に優れ溶接部の硬さ上昇を抑制した引張強さが７８０ＭＰａ以上の高強度冷延鋼板および高強度表面処理鋼板
JP4473587B2 (ja) * 2004-01-14 2010-06-02 新日本製鐵株式会社 めっき密着性および穴拡げ性に優れた溶融亜鉛めっき高強度鋼板とその製造方法
EP1975266B1 (en) 2005-12-28 2012-07-11 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Ultrahigh-strength steel sheet
JP5434960B2 (ja) 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP5765092B2 (ja) * 2010-07-15 2015-08-19 Ｊｆｅスチール株式会社 延性と穴広げ性に優れた高降伏比高強度溶融亜鉛めっき鋼板およびその製造方法
JP5298114B2 (ja) * 2010-12-27 2013-09-25 株式会社神戸製鋼所 塗膜密着性と加工性に優れた高強度冷延鋼板、及びその製造方法
WO2012153009A1 (fr) 2011-05-12 2012-11-15 Arcelormittal Investigación Y Desarrollo Sl Procede de fabrication d'acier martensitique a tres haute resistance et tole ainsi obtenue
JP5299591B2 (ja) * 2011-07-29 2013-09-25 新日鐵住金株式会社 形状凍結性に優れた高強度鋼板、高強度亜鉛めっき鋼板およびそれらの製造方法
US20130076187A1 (en) 2011-09-16 2013-03-28 Adam Daniel Flaster 5-phase alternating current induction motor and inverter system
JP2013237877A (ja) * 2012-05-11 2013-11-28 Jfe Steel Corp 高降伏比型高強度鋼板、高降伏比型高強度冷延鋼板、高降伏比型高強度亜鉛めっき鋼板、高降伏比型高強度溶融亜鉛めっき鋼板、高降伏比型高強度合金化溶融亜鉛めっき鋼板、高降伏比型高強度冷延鋼板の製造方法、高降伏比型高強度溶融亜鉛めっき鋼板の製造方法、および高降伏比型高強度合金化溶融亜鉛めっき鋼板の製造方法
JP2013241636A (ja) * 2012-05-18 2013-12-05 Jfe Steel Corp 低降伏比型高強度溶融亜鉛めっき鋼板、低降伏比型高強度合金化溶融亜鉛めっき鋼板、低降伏比型高強度溶融亜鉛めっき鋼板の製造方法、および低降伏比型高強度合金化溶融亜鉛めっき鋼板の製造方法
WO2015015239A1 (en) * 2013-08-02 2015-02-05 ArcelorMittal Investigación y Desarrollo, S.L. Cold rolled, coated and post tempered steel sheet and method of manufacturing thereof

Also Published As

Publication number Publication date
RU2017133036A3 (es) 2019-03-25
CA2975149A1 (en) 2016-09-01
US12110570B2 (en) 2024-10-08
RU2705741C2 (ru) 2019-11-11
KR20190134842A (ko) 2019-12-04
JP2018510263A (ja) 2018-04-12
CA2975149C (en) 2019-04-30
WO2016138185A1 (en) 2016-09-01
US11661637B2 (en) 2023-05-30
RU2017133036A (ru) 2019-03-25
CN107429376B (zh) 2020-10-09
CN107429376A (zh) 2017-12-01
UA120199C2 (uk) 2019-10-25
US20230257846A1 (en) 2023-08-17
US20210123114A1 (en) 2021-04-29
EP3262205A1 (en) 2018-01-03
BR112017016683A2 (pt) 2018-04-10
JP2020153016A (ja) 2020-09-24
KR20170110650A (ko) 2017-10-11
US20180044750A1 (en) 2018-02-15

Similar Documents

Publication Publication Date Title
MX2016007570A (es) Acero martensitico con resistencia a fractura retardada y metodo de fabricacion.
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
MX2017000192A (es) Metodo para producir una chapa de acero revestida o no revestida de resistencia ultra alta y chapa obtenida.
MX2017003993A (es) Lamina de acero laminado en frio de alta resistencia y alta formabilidad o banda de acero y metodo para fabricar la misma.
MX2011008114A (es) Proceso de fabricacion de partes estampadas revestidas y partes preparadas a partir de las mismas.
RU2013146540A (ru) Стальной лист для горячештампованного изделия и способ его получения
WO2015099402A8 (ko) 스트립의 연속소둔 장치 및 그 연속소둔 방법
MX2018006419A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero laminada en caliente para laminas de acero galvanizadas de alta resistencia, metodo para la fabricacion de lamina de acero laminada en frio para laminas de acero galvanizadas de alta resistencia, y lamina de acero galvanizada de alta resistencia.
EP3656879A3 (en) Method for manufacturing a high-strength steel sheet and sheet obtained by the method
WO2014119268A8 (ja) 溶融Al－Zn系めっき鋼板とその製造方法
MX2016015550A (es) Hoja de acero provista con un revestimiento que proporciona proteccion catodica sacrificial que contiene lantano.
MX2016002696A (es) Procedimiento de fabricacion de un componente de acero provisto de un revestimiento metalico de proteccion contra la corrosion.
MX2016010667A (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma.
MX2015015890A (es) Metodo para la fabricacion de una lamina de acero recocida despues de galvanizada de alta resistencia.
MX2020005026A (es) Un metodo para la fabricacion de hoja de acero recubierta con zinc resistente a la fragilizacion por metal liquido.
MX2018008103A (es) Metodo para producir una hoja de acero galvano-recocido de ultra alta resistencia y hoja de acero galvano-recocido obtenida.
PH12015502714B1 (en) Steel sheet for can and method for manufacturing the same
NZ706336A (en) Method of producing metal-coated steel strip
MX2017010788A (es) Lamina de acero recubierta de alta resistencia a la traccion posteriormente recocida que tiene mejor limite elastico y ensanchamiento de orificios.
IN2015DN02512A (es)
MX2017002410A (es) Acero de baja aleacion de alta resistencia laminado en frio.
FI20135775L (fi) Menetelmä valmistaa galvannealed-käsitelty teräsnauhatuote kuumapuristusmuovaukseen, menetelmä valmistaa kuumapuristettu teräskomponentti, ja galvannealed-käsitelty teräsnauhatuote
MX370774B (es) Lámina de acero galvanizada de alta resistencia.
MX2021009093A (es) Metodo para producir una lamina o tira a partir de una aleacion de aluminio y una lamina, tira o parte formada producida de esta manera.
MX2018008714A (es) Enrollado caliente de aceros que contienen austenita metaestable.