MX2016012490A - Producto plano de acero laminado en frio y procedimiento para su fabricacion. - Google Patents
Producto plano de acero laminado en frio y procedimiento para su fabricacion.Info
- Publication number
- MX2016012490A MX2016012490A MX2016012490A MX2016012490A MX2016012490A MX 2016012490 A MX2016012490 A MX 2016012490A MX 2016012490 A MX2016012490 A MX 2016012490A MX 2016012490 A MX2016012490 A MX 2016012490A MX 2016012490 A MX2016012490 A MX 2016012490A
- Authority
- MX
- Mexico
- Prior art keywords
- flat steel
- steel product
- rolled
- cold
- case
- Prior art date
Abstract
La invención se refiere a un producto plano de acero laminado en frío y a un procedimiento para su fabricación. El producto plano de acero posee un límite elástico Rp0, 2 de = 320 MPa, un alargamiento de rotura A80 de = 20 % y una estructura con (en % de superficie) el 62-82 % de ferrita, el 10-30 % de martensita, el 1,5-8 % de austenita residual y en suma = 10 % de otros componentes estructurales. Con ello, el producto plano de acero se compone de una aleación de acero, que contiene (en % en peso) C: 0,06-0,1 %, Si: 0,15-0,4 %, Mn: 1,5-2 %, Cr: 0,2-0,5 %, Al: = 0,1 %, siendo la suma de los contenidos de C, Si, Mn y Cr = 2,3 % y = 2,8 %, y la suma de los contenidos de Si y Al = 0,4 %, P: = 0,03 %, S: = 0,006 %, N: = 0,008 %, impurezas técnicamente inevitables, a las que pertenecen = 0,0006 % de B, = 0,02 % de V, así como = 0,01 % en cada caso de Nb, Ti, , así como = 0,1 % en cada caso de Mo, Ni y Cu, hierro residual. Para fabricar un producto plano de acero de este tipo se fabrica en primer lugar un producto plano de acero laminado en frío, que a continuación en la pasada continua se lleva a 760 - 860 °C y allí se mantiene durante una duración de recocido Gt, para la que, dependiendo del grosor D del producto plano de acero, se cumple que Gtu = Gt = Gto con Gtu [s] = 3,56*D2 [s/mm2] - 5,1*D[s/mm] + 9,8 s Gto [s] = -21,4*D2 [s/mm2] + 132,8*D [s/mm] + 47 s.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP14161607.8A EP2924141B1 (de) | 2014-03-25 | 2014-03-25 | Kaltgewalztes Stahlflachprodukt und Verfahren zu seiner Herstellung |
PCT/EP2015/055686 WO2015144530A1 (de) | 2014-03-25 | 2015-03-18 | Kaltgewalztes stahlflachprodukt und verfahren zu seiner herstellung |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2016012490A true MX2016012490A (es) | 2017-01-06 |
Family
ID=50382301
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2016012490A MX2016012490A (es) | 2014-03-25 | 2015-03-18 | Producto plano de acero laminado en frio y procedimiento para su fabricacion. |
Country Status (8)
Country | Link |
---|---|
US (1) | US10287649B2 (es) |
EP (1) | EP2924141B1 (es) |
JP (1) | JP6600641B2 (es) |
KR (1) | KR20170013211A (es) |
CN (1) | CN106133155A (es) |
CA (1) | CA2942738C (es) |
MX (1) | MX2016012490A (es) |
WO (1) | WO2015144530A1 (es) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN109252095A (zh) * | 2018-10-09 | 2019-01-22 | 敬业钢铁有限公司 | 一种防锈螺纹钢筋的生产工艺 |
Families Citing this family (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102017209982A1 (de) * | 2017-06-13 | 2018-12-13 | Thyssenkrupp Ag | Hochfestes Stahlblech mit verbesserter Umformbarkeit |
DE102017218704A1 (de) | 2017-10-19 | 2019-04-25 | Thyssenkrupp Ag | Verfahren zur Herstellung eines mit einem metallischen, vor Korrosion schützenden Überzug versehenen Stahlbauteils |
EP3807429A1 (de) * | 2018-06-12 | 2021-04-21 | ThyssenKrupp Steel Europe AG | Stahlflachprodukt und verfahren zu seiner herstellung |
KR102098483B1 (ko) * | 2018-07-27 | 2020-04-07 | 주식회사 포스코 | 성형성 및 피로특성이 우수한 저비중 클래드 강판 및 그 제조방법 |
EP4083236A1 (de) * | 2018-09-26 | 2022-11-02 | ThyssenKrupp Steel Europe AG | Verfahren zur herstellung eines beschichteten stahlflachprodukts und beschichtetes stahlflachprodukt |
EP4092142A1 (de) * | 2019-06-03 | 2022-11-23 | ThyssenKrupp Steel Europe AG | Verfahren zum herstellen eines blechbauteils aus einem mit einer korrosionsschutzbeschichtung versehenen stahlflachprodukt |
WO2020245627A1 (en) * | 2019-06-03 | 2020-12-10 | Arcelormittal | Cold rolled and coated steel sheet and a method of manufacturing thereof |
CN110629102B (zh) * | 2019-10-16 | 2021-04-27 | 宝武集团鄂城钢铁有限公司 | 一种580MPa级低应力腐蚀敏感性海洋工程用钢及其生产方法 |
CN112226597A (zh) * | 2020-10-16 | 2021-01-15 | 四川汇源钢建科技股份有限公司 | 一种冷轧带钢的冷轧退火方法 |
CN112974562B (zh) * | 2021-03-31 | 2023-04-07 | 甘肃酒钢集团宏兴钢铁股份有限公司 | 一种焊带用不锈钢热轧卷的生产方法 |
CN113414545A (zh) * | 2021-03-31 | 2021-09-21 | 常州鱼跃金属制品有限公司 | 一种精细光亮的扁钢加工方法 |
CN114774659A (zh) * | 2022-05-25 | 2022-07-22 | 新疆八一钢铁股份有限公司 | 一种石油天然气输送管线用微合金钢卷的制造方法 |
Family Cites Families (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3569307B2 (ja) | 1994-01-12 | 2004-09-22 | 新日本製鐵株式会社 | 加工性に優れた引張強さ45〜65kgf/mm2 の高強度複合組織冷延鋼板とその製造方法 |
JP4085583B2 (ja) * | 2001-02-27 | 2008-05-14 | Jfeスチール株式会社 | 高強度冷延溶融亜鉛メッキ鋼板およびその製造方法 |
JP4936300B2 (ja) * | 2001-04-17 | 2012-05-23 | 新日本製鐵株式会社 | プレス加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
CN1273633C (zh) * | 2003-06-24 | 2006-09-06 | 宝山钢铁股份有限公司 | 超细晶粒低碳低合金双相钢板及其制造方法 |
CN101130847B (zh) * | 2006-08-24 | 2010-07-28 | 鞍钢股份有限公司 | 中薄板坯连铸连轧双相钢板及其制造方法 |
PL1918406T3 (pl) * | 2006-10-30 | 2009-10-30 | Thyssenkrupp Steel Ag | Sposób wytwarzania płaskich produktów stalowych z wielofazowej stali mikrostopowej z borem |
DE602008006310D1 (de) | 2007-08-16 | 2011-06-01 | Fujifilm Corp | Endoskopischer Reprozessor |
JP4623233B2 (ja) | 2009-02-02 | 2011-02-02 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
CN102409222B (zh) * | 2010-09-21 | 2014-09-03 | 鞍钢股份有限公司 | 连续退火或热镀锌的冷轧相变诱导塑性钢板及其制备方法 |
JP2014019928A (ja) * | 2012-07-20 | 2014-02-03 | Jfe Steel Corp | 高強度冷延鋼板および高強度冷延鋼板の製造方法 |
-
2014
- 2014-03-25 EP EP14161607.8A patent/EP2924141B1/de active Active
-
2015
- 2015-03-18 CA CA2942738A patent/CA2942738C/en not_active Expired - Fee Related
- 2015-03-18 JP JP2016558768A patent/JP6600641B2/ja not_active Expired - Fee Related
- 2015-03-18 WO PCT/EP2015/055686 patent/WO2015144530A1/de active Application Filing
- 2015-03-18 MX MX2016012490A patent/MX2016012490A/es unknown
- 2015-03-18 US US15/127,987 patent/US10287649B2/en not_active Expired - Fee Related
- 2015-03-18 CN CN201580016439.6A patent/CN106133155A/zh active Pending
- 2015-03-18 KR KR1020167029350A patent/KR20170013211A/ko not_active Application Discontinuation
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN109252095A (zh) * | 2018-10-09 | 2019-01-22 | 敬业钢铁有限公司 | 一种防锈螺纹钢筋的生产工艺 |
Also Published As
Publication number | Publication date |
---|---|
US10287649B2 (en) | 2019-05-14 |
KR20170013211A (ko) | 2017-02-06 |
JP2017512904A (ja) | 2017-05-25 |
EP2924141B1 (de) | 2017-11-15 |
WO2015144530A1 (de) | 2015-10-01 |
CA2942738C (en) | 2018-09-04 |
JP6600641B2 (ja) | 2019-10-30 |
EP2924141A1 (de) | 2015-09-30 |
US20170218471A1 (en) | 2017-08-03 |
CA2942738A1 (en) | 2015-10-01 |
CN106133155A (zh) | 2016-11-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2016012490A (es) | Producto plano de acero laminado en frio y procedimiento para su fabricacion. | |
MX2016012491A (es) | Metodo para producir un producto plano de acero altamente resistente. | |
JP6685244B2 (ja) | 強度、延性および成形性が改善された高強度鋼板を製造する方法 | |
US10000833B2 (en) | Thick, tough, high tensile strength steel plate and production method therefor | |
UA117865C2 (uk) | Високоміцна багатофазна сталь, спосіб її одержання та застосування | |
MA44120B1 (fr) | Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité et une aptitude au formage améliorées et tôle d'acier ainsi obtenue | |
JP2021059787A (ja) | 高強度鋼板を製造する方法および得られた鋼板 | |
MX2018007649A (es) | Metodo para producir una lamina de acero recubierta de alta resistencia que tenga ductilidad y conformabilidad mejorada, y lamina de acero recubierta obtenida. | |
RU2017121061A (ru) | Высокопрочная горячекатаная сталь с высокой ударной прочностью и временным сопротивлением 800 мпа и способ ее производства | |
MX2018007645A (es) | Metodo para producir una hoja de acero de alta fuerza que tiene ductilidad y formabilidad mejoradas y hoja de acero obtenida. | |
WO2016001895A3 (en) | Method for producing a high strength coated steel sheet having improved strength, ductility and formability | |
MX2018007641A (es) | Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida. | |
MX2016017398A (es) | Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida. | |
CA2903916A1 (en) | High strength hot dip galvanised complex phase steel strip | |
WO2016001893A3 (en) | Method for producing a high strength steel sheet having improved strength and formability and obtained sheet | |
MX359260B (es) | Acero laminado que se endurece por medio de precipitación después de formación por calor y/o enfriamiento con una herramienta que tiene muy alta resistencia y ductilidad, y método para su fabricación. | |
RU2015155181A (ru) | Способ изготовления детали путем горячей деформации стальной заготовки | |
WO2016001890A3 (en) | Method for producing a ultra high strength coated or not coated steel sheet and obtained sheet | |
US20140261914A1 (en) | Method of producing hot rolled high strength dual phase steels using room temperature water quenching | |
WO2016001889A3 (en) | Method for manufacturing a high-strength steel sheet and sheet obtained by the method | |
UA118706C2 (uk) | Спосіб виробництва сталевого листа з покриттям, що має підвищену міцність, пластичність і деформованість | |
WO2016001887A3 (en) | Method for manufacturing a high strength steel sheet having improved formability and sheet obtained | |
MX2017000185A (es) | Metodo para la fabricacion de una hoja de acero de alta resistencia que tiene formabilidad y ductilidad mejoradas y hoja obtenida. | |
MX2018007648A (es) | Metodo para producir una hoja de acero que tiene resistencia, ductilidad y formabilidad mejoradas. | |
WO2016001897A3 (en) | Method for producing a high strength coated steel sheet having improved strength, formability and obtained sheet |