MX2008013906A - Hormigon con bajo contenido de cemento. - Google Patents

Hormigon con bajo contenido de cemento.

Info

Publication number
MX2008013906A
MX2008013906A MX2008013906A MX2008013906A MX2008013906A MX 2008013906 A MX2008013906 A MX 2008013906A MX 2008013906 A MX2008013906 A MX 2008013906A MX 2008013906 A MX2008013906 A MX 2008013906A MX 2008013906 A MX2008013906 A MX 2008013906A
Authority
MX
Mexico
Prior art keywords
mum
grain size
particles whose
constituted
size materials
Prior art date
Application number
MX2008013906A
Other languages
English (en)
Inventor
Emmanuel Garcia
Original Assignee
Lafarge Sa
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lafarge Sa filed Critical Lafarge Sa
Publication of MX2008013906A publication Critical patent/MX2008013906A/es

Abstract

La invención proporciona una mezcla que comprende, en proporciones de masas: - de 0.4 a 4%, preferiblemente de 0.8 a 1.7%, de materiales en el intervalo ultrafino de tamaño de partícula, que comprende partículas con una D90 menor a 1 iim y/o con un área de superficie específica BET mayor a 6 m2/g; - de 1 a 6%, preferiblemente de 2 a 5%, de cemento Portland; - de 8 a 25%, preferiblemente de 12 a 21%, de materiales en el intervalo fino de tamaño de partícula, que comprende partículas en donde la 010 y la 090 son de 1 pm y 100 pm y con un área de superficie específica BET menor a 5 m2Ig, diferente al cemento; - de 25 a 50%, de partículas en donde la DIO y la 090 son de 100 pm y5 mm; y - de 25 a 55%, preferiblemente de 35 a 47%, de materiales en el intervalo más grande de tamaño de partícula, que comprende partículas en donde la DIO es mayor a 5 mm. La invención también proporciona notablemente premezclas, composiciones de hormigón y objetos asociados de hormigón fraguado, así como sus procesos de preparación.
MX2008013906A 2006-05-17 2007-05-16 Hormigon con bajo contenido de cemento. MX2008013906A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
FR0604398A FR2901268B1 (fr) 2006-05-17 2006-05-17 Beton a faible teneur en ciment
PCT/FR2007/000834 WO2007132098A1 (fr) 2006-05-17 2007-05-16 Beton a faible teneur en ciment

Publications (1)

Publication Number Publication Date
MX2008013906A true MX2008013906A (es) 2009-01-21

Family

ID=37560773

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2008013906A MX2008013906A (es) 2006-05-17 2007-05-16 Hormigon con bajo contenido de cemento.

Country Status (14)

Country Link
US (1) US8043425B2 (es)
EP (1) EP2029498A1 (es)
JP (1) JP5412279B2 (es)
KR (1) KR101382751B1 (es)
CN (1) CN101448757B (es)
BR (1) BRPI0711469A2 (es)
CA (1) CA2652276C (es)
EG (1) EG25870A (es)
FR (1) FR2901268B1 (es)
MX (1) MX2008013906A (es)
MY (1) MY147473A (es)
RU (1) RU2434822C2 (es)
UA (1) UA96448C2 (es)
WO (1) WO2007132098A1 (es)

Families Citing this family (59)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5107660B2 (ja) * 2007-03-28 2012-12-26 太平洋セメント株式会社 セメント添加材及びセメント組成物
FR2921358B1 (fr) * 2007-09-25 2010-10-01 Lafarge Sa Beton a faible teneur en clinker
EP2145868A1 (en) * 2008-07-18 2010-01-20 Lafarge Aqueous formulations
US7799128B2 (en) 2008-10-10 2010-09-21 Roman Cement, Llc High early strength pozzolan cement blends
FR2943662B1 (fr) * 2009-03-24 2015-01-16 Lafarge Sa Beton a faible teneur en clinker
FR2943663B1 (fr) * 2009-03-25 2011-05-06 Lafarge Sa Beton a haute ou ultra haute performance
US8293005B2 (en) * 2009-09-01 2012-10-23 Barbour Ronald L Pre-blend cement compositions containing pulverized fly ash or bottom ash
US8414700B2 (en) 2010-07-16 2013-04-09 Roman Cement, Llc Narrow PSD hydraulic cement, cement-SCM blends, and methods for making same
MY178492A (en) * 2010-08-26 2020-10-14 Ohbayashi Corp Cement composition, method for producing mixed material and method for producing cement composition
WO2012075208A2 (en) * 2010-11-30 2012-06-07 Roman Cement, Llc Engineered portland cement incorporating scms and methods for making and using same
US9272953B2 (en) 2010-11-30 2016-03-01 Roman Cement, Llc High early strength cement-SCM blends
US9102567B1 (en) 2010-11-30 2015-08-11 Roman Cement, Llc Engineered Portland cement incorporating SCMs and methods for making same
FR2970962B1 (fr) * 2011-01-28 2022-04-15 Lafarge Sa Composition hydraulique a faible teneur en clinker
WO2013032536A2 (en) * 2011-04-01 2013-03-07 Maryland Environmental Restoration Group, Inc. Geothermal grout, methods of making geothermal grout, and methods of use
DE102011050134B3 (de) * 2011-05-05 2012-07-26 Thyssenkrupp Polysius Ag Verfahren und Anlage zur Herstellung eines hydraulischen Bindemittels
CN102887692A (zh) * 2011-07-21 2013-01-23 广东省航盛建设集团有限公司 一种利用高石粉含量花岗岩石屑制备混凝土的方法
ITMI20111642A1 (it) * 2011-09-12 2013-03-13 Italcementi Spa Manufatto cementizio a basso spessore ed elevate qualita' superficiali per applicazioni non strutturali, e metodo per la sua produzione
PE20142096A1 (es) 2011-10-20 2014-12-06 Roman Cement Llc Mezclas de cemento-scm de particulas empacadas
CA2859455C (en) 2011-12-16 2020-01-07 Lafarge Grinding process and unit, and corresponding production process of a hydraulic binder
EP2634151A1 (en) * 2012-02-28 2013-09-04 Omya Development AG Process for the preparation of cement, mortars, concrete compositions containing calcium carbonate-based filler(s) (pre) - treated with ultrafine (UF) filler(s), compositions and cement products obtained and their applications
EP2634154A1 (en) * 2012-02-28 2013-09-04 Omya Development AG Process for the preparation of cement, mortars, concrete compositions containing a calcium carbonate-based filler treated with ultrafine filler and a superplasticizer, compositions and cement products obtained and their applications
EP2634153A1 (en) * 2012-02-28 2013-09-04 Omya Development AG Process for the preparation of cement, mortars, concrete compositions containing a calcium carbonate-based filler containing an aluminosiliceous material, the said "filler(s) blend" being treated with a superplastifier, cement compositions and cement products obtained, and their applications.
US8851173B2 (en) * 2012-03-09 2014-10-07 Halliburton Energy Services, Inc. Set-delayed cement compositions comprising pumice and associated methods
RU2503637C2 (ru) * 2012-04-09 2014-01-10 Федеральное государственное бюджетное образовательное учреждение высшего профессионального образования "Тверской государственный технический университет" Сырьевая смесь для приготовления тяжелого бетона
FR2992960B1 (fr) * 2012-07-06 2015-07-24 Lafarge Sa Beton leger a faible conductivite thermique
US10858570B2 (en) * 2012-07-17 2020-12-08 Dow Global Technologies Llc Aqueous cement compositions incorporating particles that are activated to control rheology when water soluble portions of the particles are released in the presence of water
WO2014045583A1 (ja) * 2012-09-24 2014-03-27 パナソニック株式会社 撥水砂の混合物及び撥水砂構造体
CN103030354B (zh) * 2012-12-05 2014-07-30 王建友 水泥火山石复合混凝土制作方法
RU2621818C1 (ru) * 2013-09-09 2017-06-07 Хэллибертон Энерджи Сервисиз, Инк. Текучесть гашеной извести в композициях с отсроченным схватыванием и других композициях, способных затвердевать
CA2921428C (en) * 2013-09-09 2019-01-29 Halliburton Energy Services, Inc. Mitigation of contamination effects in set-delayed cement compositions comprising pumice and hydrated lime
BE1021769B1 (fr) * 2013-12-06 2016-01-15 S.A.Lhoist Recherche Et Developpement Composition de liant pour mortiers et enduits perctionnes.
CA2937156C (en) * 2014-01-17 2019-12-10 Multiquip, Inc. Addition of colloidal silica to concrete
FR3022540B1 (fr) * 2014-06-20 2021-05-14 Lafarge Sa Betons a ultra haute performance a faible teneur en ciment
US9499742B2 (en) * 2014-12-16 2016-11-22 King Fahd University Of Petroleum And Minerals Method for enhancing strength and durability of weak soils
AT517029B1 (de) 2015-03-24 2017-02-15 Holcim Technology Ltd Mischzementzusammensetzung
WO2017067956A1 (en) 2015-10-20 2017-04-27 Hilti Aktiengesellschaft Fastening system and use thereof
CA3000895C (en) 2015-10-20 2023-09-19 Hilti Aktiengesellschaft Use of a calcium sulfate comprising 2-k mortar system based on aluminous cement in anchoring applications to increase load values and reduce shrinkage
KR102662504B1 (ko) 2015-10-20 2024-04-30 힐티 악티엔게젤샤프트 알루미나 시멘트를 기초로 하는 2-성분 모르타르 시스템 및 이의 용도
EP3199501B1 (de) * 2016-01-29 2023-06-07 Daw Se Staubreduzierte pulverförmige mischungen
US10150703B2 (en) 2016-06-28 2018-12-11 King Fahd University Of Petroleum And Minerals Cementitious blend and concrete mix compositions resistant to high temperatures and alkaline conditions
US10131575B2 (en) 2017-01-10 2018-11-20 Roman Cement, Llc Use of quarry fines and/or limestone powder to reduce clinker content of cementitious compositions
US11168029B2 (en) 2017-01-10 2021-11-09 Roman Cement, Llc Use of mineral fines to reduce clinker content of cementitious compositions
US10730805B2 (en) 2017-01-10 2020-08-04 Roman Cement, Llc Use of quarry fines and/or limestone powder to reduce clinker content of cementitious compositions
US10737980B2 (en) 2017-01-10 2020-08-11 Roman Cement, Llc Use of mineral fines to reduce clinker content of cementitious compositions
CA3054020A1 (en) * 2017-04-07 2018-10-11 Hilti Aktiengesellschaft Use of fine calcium carbonate in an inorganic mortar system based on aluminous cement to increase load values
WO2018184973A1 (en) * 2017-04-07 2018-10-11 Hilti Aktiengesellschaft Use of amorphous calcium carbonate in a fire-resistant inorganic mortar system based on aluminous cement to increase load values at elevated temperatures
KR102191877B1 (ko) * 2017-06-29 2020-12-16 미쓰이스미토모겐세쓰 가부시키가이샤 콘크리트 조성물 및 그 제조 방법
BR112020019084A2 (pt) 2018-03-22 2020-12-29 Dustin A. Hartman Método para preparar um produto de concreto acabado melhorado
FR3080904B1 (fr) * 2018-05-07 2020-05-22 Saint Gobain Pam Element de canalisation ou de reservoir avec revetement interne cimentaire
EP3581549A1 (en) * 2018-06-15 2019-12-18 Holcim Technology Ltd. Fresh concrete composition for encasing underground electrical cables
EP3844122A4 (en) * 2018-09-01 2022-09-28 Dustin A. Hartman WEAR-RESISTANT CONCRETE FORMULATIONS AND METHODS OF PRODUCTION
CN109553365A (zh) * 2019-01-29 2019-04-02 临沂博泰国际贸易有限公司 一种无机胶凝材料及其制备方法
US11866366B2 (en) 2019-09-03 2024-01-09 Specification Products, Inc. Wear-resistant concrete formulations and methods for their preparation
CN112500075A (zh) * 2020-12-08 2021-03-16 上海市建筑科学研究院有限公司 一种生活垃圾焚烧炉底渣干硬性混凝土及其制备方法
RU2770702C1 (ru) * 2021-08-17 2022-04-21 Публичное Акционерное Общество "Новолипецкий металлургический комбинат" Высокопрочная бетонная смесь с низким расходом цемента
FR3130269A1 (fr) 2021-12-10 2023-06-16 Vinci Construction France Béton à faible dosage en ciment
CN114907070A (zh) * 2022-05-11 2022-08-16 湖南人健宝固高新科技发展有限公司 一种无收缩可喷射超高性能混凝土及其施工方法
CN115436126A (zh) * 2022-08-31 2022-12-06 中国建筑材料科学研究总院有限公司 一种水泥基材料高通量制备的方法及装置
CN115536338A (zh) * 2022-10-08 2022-12-30 北京市高强混凝土有限责任公司 一种高流态透水混凝土组合物和一种高流态透水混凝土

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1190947A (en) * 1978-11-03 1985-07-23 Hans H. Bache Shaped article and composite material and method for producing same
FR2677640B1 (fr) * 1991-06-12 1996-03-08 Bouygues Sa Mortier a tres haute performance, betons obtenus a partir de ce mortier et les elements fabriques avec ce mortier ou ce beton.
DK49592D0 (da) * 1992-04-13 1992-04-13 Aalborg Portland As Cementkomposition
FR2707977B1 (fr) 1993-07-01 1996-01-12 Bouygues Sa Procédé et composition pour fabriquer des éléments en béton ayant une résistance à la compression et une énergie de fracturation remarquables et éléments ainsi obtenus.
FR2708263B1 (fr) 1993-07-01 1995-10-20 Bouygues Sa Composition de béton de fibres métalliques pour mouler un élément en béton, éléments obtenus et procédé de cure thermique.
GB2293376B (en) * 1994-09-23 1998-08-26 Trafalgar House Technology Ltd Concrete compositions
JP3201458B2 (ja) * 1996-01-17 2001-08-20 株式会社大林組 流動制御型コンクリート
FR2770517B1 (fr) 1997-11-03 1999-12-03 Bouygues Sa Laitier de cimentation d'un puits, notamment d'un puits petrolier
FR2771406B1 (fr) 1997-11-27 2000-02-11 Bouygues Sa Beton de fibres metalliques, matrice cimentaire et premelanges pour la preparation de la matrice et du beton
FR2774683B1 (fr) * 1998-02-06 2000-04-07 Quillery & Cie Entreprise Beton tres haute perfomance, autonivelant, son procede de preparation et son utilisation
FR2778654B1 (fr) * 1998-05-14 2000-11-17 Bouygues Sa Beton comportant des fibres organiques dispersees dans une matrice cimentaire, matrice cimentaire du beton et premelanges
JP3429689B2 (ja) * 1998-10-20 2003-07-22 株式会社熊谷組 防蝕性モルタル
FR2804952B1 (fr) 2000-02-11 2002-07-26 Rhodia Chimie Sa Composition de beton ultra haute performance resistant au feu
GB2376462A (en) * 2001-06-08 2002-12-18 Rmc Readymix Ltd A low cement concrete composition
JP2007031262A (ja) * 2005-06-20 2007-02-08 Ohbayashi Corp 水硬性無機材料及び高度浄水処理施設用のコンクリート

Also Published As

Publication number Publication date
RU2008149704A (ru) 2010-06-27
CN101448757B (zh) 2012-08-29
CA2652276C (fr) 2016-03-22
JP5412279B2 (ja) 2014-02-12
EP2029498A1 (fr) 2009-03-04
JP2009537435A (ja) 2009-10-29
US8043425B2 (en) 2011-10-25
CA2652276A1 (fr) 2007-11-22
CN101448757A (zh) 2009-06-03
KR101382751B1 (ko) 2014-04-08
MY147473A (en) 2012-12-14
BRPI0711469A2 (pt) 2011-11-16
RU2434822C2 (ru) 2011-11-27
FR2901268B1 (fr) 2008-07-18
EG25870A (en) 2012-09-12
KR20090012324A (ko) 2009-02-03
WO2007132098A1 (fr) 2007-11-22
US20070266906A1 (en) 2007-11-22
FR2901268A1 (fr) 2007-11-23
UA96448C2 (uk) 2011-11-10

Similar Documents

Publication Publication Date Title
MX2008013906A (es) Hormigon con bajo contenido de cemento.
KR101247707B1 (ko) 페로니켈 슬래그를 포함하는 시멘트, 모르타르 및 콘크리트용 혼합재
JP5931317B2 (ja) 水硬性組成物および該水硬性組成物を用いたコンクリート
MX2007011640A (es) Composiciones de concreto de peso ligero.
ZA200909116B (en) Process for preparing a filler for asphalt or concrete starting from a slag material
CN109608069A (zh) 一种42．5级缓凝水泥及其制备方法和应用
WO2007026352A3 (en) Compressive strenght imrpovement of cement and gypsum products
JP2016088767A (ja) セメント組成物及びその製造方法
WO2015037593A1 (ja) 水硬性組成物
JP2009173498A (ja) 水硬性組成物及び硬化体
JP6096039B2 (ja) 急結剤
MX2009009209A (es) Cemento resistente al sulfato.
JP6465432B2 (ja) 高強度吹付コンクリート
KR20110113329A (ko) 페로니켈 슬래그를 이용한 항균·탈취 기능성 조성물 제조방법.
JP5759801B2 (ja) 水硬性粉体の製造方法
JP5883243B2 (ja) 水硬性粉体の製造方法
JP5024669B2 (ja) セメントの粉砕助剤
RU2514477C1 (ru) Шихта для производства пористого заполнителя
CN105408275B (zh) 水硬性粉体的制造方法
JP4157720B2 (ja) 遅硬型土質改良用固化材
JP5057909B2 (ja) セメント組成物
KR100896005B1 (ko) 레미콘 혼화재용 강도증진 혼합재 조성물과 이를 이용한 레미콘 생산방법
JP2007126304A (ja) 鉱物の微粒子、該微粒子を用いた混合セメント及び該混合セメントを用いた硬化体
JP6285135B2 (ja) セメントクリンカ及びセメント
RU2393129C1 (ru) Тяжелый бетон

Legal Events

Date Code Title Description
FG Grant or registration