MD814C2 - Способ микродугового анодирования алюминия - Google Patents

Способ микродугового анодирования алюминия

Info

Publication number
MD814C2
MD814C2 MD96-0351A MD960351A MD814C2 MD 814 C2 MD814 C2 MD 814C2 MD 960351 A MD960351 A MD 960351A MD 814 C2 MD814 C2 MD 814C2
Authority
MD
Moldova
Prior art keywords
current density
aluminum
microarc
porosity
decrease
Prior art date
Application number
MD96-0351A
Other languages
English (en)
Romanian (ro)
Other versions
MD814B1 (en
Inventor
Valeriu KAPLIN
Ефим БАДИНТЕР
Vladlen Vinogradov
Mihai Rotari
Ivan Grisanov
Ion Tanas
Cezar Canter
Leonid Spivac
Pavel Visokii
Filip Magalnic
Valerii Fedotov
Original Assignee
Сочиетате Пе Акциунь, Институтул Де Черчетэрь Штиинцифиче "Елири"
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Сочиетате Пе Акциунь, Институтул Де Черчетэрь Штиинцифиче "Елири" filed Critical Сочиетате Пе Акциунь, Институтул Де Черчетэрь Штиинцифиче "Елири"
Priority to MD96-0351A priority Critical patent/MD814C2/ru
Publication of MD814B1 publication Critical patent/MD814B1/xx
Publication of MD814C2 publication Critical patent/MD814C2/ru

Abstract

Изобретение касается анодирования алюминия и может быть использовано в микроэлектронике при изготовлении подложек для гибридно-интегральных схем.Цель изобретения - уменьшение шероховатости и пористости покрытия. Процесс ведут в микродуговом режиме при плотности тока до 15 А/дм2 и рабочем напряжении 400 - 700 В. Уменьшение шероховатости и пористости покрытия достигается при анодировании в водном растворе, содержащем 1,4-1,6 мас.% гексаметафосфата, с использованием пульсирующего напряжения, которое поднимают до рабочих значений в течение 5-8 мин., снижают на 10-15% после уменьшения плотности тока на 4-5 А/дм2 и полностью снимают после уменьшения плотности тока до 0,2-0,4 А/дм2.
MD96-0351A 1986-03-18 1996-10-25 Способ микродугового анодирования алюминия MD814C2 (ru)

Priority Applications (1)

Application Number Priority Date Filing Date Title
MD96-0351A MD814C2 (ru) 1986-03-18 1996-10-25 Способ микродугового анодирования алюминия

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
SU4057022 1986-03-18
MD96-0351A MD814C2 (ru) 1986-03-18 1996-10-25 Способ микродугового анодирования алюминия

Publications (2)

Publication Number Publication Date
MD814B1 MD814B1 (en) 1997-08-31
MD814C2 true MD814C2 (ru) 1997-10-31

Family

ID=26640670

Family Applications (1)

Application Number Title Priority Date Filing Date
MD96-0351A MD814C2 (ru) 1986-03-18 1996-10-25 Способ микродугового анодирования алюминия

Country Status (1)

Country Link
MD (1) MD814C2 (ru)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3293158A (en) * 1963-09-17 1966-12-20 Mcneill William Anodic spark reaction processes and articles
SU926083A1 (ru) * 1980-01-04 1982-05-07 Институт Неорганической Химии Со Ан Ссср Способ электролитического нанесени силикатных покрытий

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3293158A (en) * 1963-09-17 1966-12-20 Mcneill William Anodic spark reaction processes and articles
SU926083A1 (ru) * 1980-01-04 1982-05-07 Институт Неорганической Химии Со Ан Ссср Способ электролитического нанесени силикатных покрытий

Also Published As

Publication number Publication date
MD814B1 (en) 1997-08-31

Similar Documents

Publication Publication Date Title
EP0405624A3 (en) Method for anodizing aluminium
AU7581887A (en) Method of coating articles of aluminum and an electrolytic bath therefor
EP0940483A3 (en) Anodizing method and apparatus and semiconductor substrate manufacturing method
DE50105209D1 (de) Verfahren zur oberflächenbehandlung von aluminium oder aluminium-legierungen mittels alkansulfonsäurehaltigen formulierungen
US4676879A (en) Method for the production of an aluminum foil for electrolytic _capacitors, and electrolytic capacitors thus produced
MD814C2 (ru) Способ микродугового анодирования алюминия
US4548683A (en) Method of electrolytically graining a lithographic plate
ES8205885A2 (es) Mejoras introducidas en el objeto de la patente principal por proceso para la coloracion electrolitica del aluminio a-nodizado.
KR860004172A (ko) 양극 산화처리된 알루미늄 기재금속 피처리재를 착색하는 방법
JPS5732396A (en) Method for forming opaque colored film on aluminum surface
Sells Anodizing Aluminium Foil
JPS55152196A (en) Treatment for aluminum surface
ES2032769T3 (es) Metodo para el coloreado electronico de aluminio o de aleaciones de aluminio.
JPS55154599A (en) Plating method for aluminum or its alloy
Dowell Pre-Anodized Aluminum Coil
ZA895471B (en) Use of p-toluenesulfonic acid for electrolytically coloring anodically produced surfaces of aluminum
JPS56130490A (en) Surface treatment of anodically oxidized coating of aluminum or aluminum alloy
Tagai Anodic Formation of a Colored Oxide Coating on an Aluminum Surface
Samsonov Electrolytical Blackening of Anodized Aluminum
KR970006551A (ko) 알루미늄재의 표면에 나뭇결 무늬를 형성하는 방법
Huang Application of Galvanostatic Pulses on the Anodization of Aluminum in Sulfuric Acid
JPS5681698A (en) Aluminum or aluminum alloy coloring method
Pautov Influence of Solution Potential on Surface Roughness of Aluminum and Its Alloys in NaOH Solutions
Paulet Process for Electrolytically Colouring an Anodic Oxide Layer on Aluminium or Aluminium Alloys
JPS6438291A (en) Production of aluminum support for printing plate

Legal Events

Date Code Title Description
FG4A Patent for invention issued
IF99 Valid patent on 19990615

Free format text: EXPIRES: 20060318