KR970049011A - 매끄럽고 광택나는 표면을 가진 석판인쇄용 인쇄판 - Google Patents
매끄럽고 광택나는 표면을 가진 석판인쇄용 인쇄판 Download PDFInfo
- Publication number
- KR970049011A KR970049011A KR1019960061589A KR19960061589A KR970049011A KR 970049011 A KR970049011 A KR 970049011A KR 1019960061589 A KR1019960061589 A KR 1019960061589A KR 19960061589 A KR19960061589 A KR 19960061589A KR 970049011 A KR970049011 A KR 970049011A
- Authority
- KR
- South Korea
- Prior art keywords
- range
- microns
- color coordinate
- support
- coordinate value
- Prior art date
Abstract
본 발명은 석판인쇄용 인쇄판에 사용되는 지지체 및 이것의 제조 방법에 관한 것이다. 구체적으로, 본 발명은 매끄럽고 광택나는 표면을 가지고 있어, 표면상에 석판인쇄 화상을 형성시켰을 때 화상 대비가 더욱 큰, 전기화학적으로 그래이닝(graining) 및 양극처리(anodizing)한 표면을 가진 알루미늄판에 관한 것이다. 이 표면은 피이크와 밸리를 가지고 있어 표면 조도 매개변수(roughness parameter) Ra가 약 0.10 내지 약 0.50 마이크론의 범위이고, Rz가 약 0.00 내지 약 5.00 마이크론의 범위이며, Rt가 약 0.00 내지 약 6.00 마이크론의 범위이고, Rp가 약 0.00 내지 약4.00 마이크론의 범위인 거의 균일한 표면 지형을 가진다. 이 표면은 L이 약 35.00 내지 약75.00의 범위이고, a가 약-4.00 내지 약+4.00의 범위이며, b가 약 -4.00 내지 약 +4.00의 범위인 삼자극 색상 좌표값(tristimulus color coordinate value) L, a 및 b를 가지는 것이 바람직하다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (23)
- 그래이닝되고 양극처리된 표면을 지니며, 또 피이크와 밸리를 포함하고 있어 표면 조도 매개변수 Ra가 약 0.10 내지 약 0.50 마이크론의 범위이고, Rz가 약 0.00 내지 약 5.00 마이크론의 범위이며, Rt가 약 0.00 내지 약 6.00 마이크론의 범위이고, Rp가 약 0.00 내지 약4.00 마이크론의 범위인 거의 균일한 표면 지형을 가진 알루미늄 기판을 포함하는 석판인쇄용 인쇄판에 대한 지지체.
- 제1항에 있어서, 상기 Ra가 약 0.20 내지 약0.40 마이크론의 범위이고, Rz가 약 1.00 내지 약 4.00 마이크론의 범위이며, Rt가 약 1.00 내지 약 5.00 마이크론의 범위이고, Rp가 약 1.00 내지 약 3.00 마이크론의 범위인 것을 특징으로 하는 지지체.
- 제1항에 있어서, 상기 Ra가 약 0.25 내지 약0.35 마이크론의 범위이고, Rz가 약 2.50 내지 약 3.50 마이크론의 범위이며, Rt가 약 2.00 내지 약 4.00 마이크론의 범위이고, Rp가 약 1.50 내지 약 2.50 마이크론의 범위인 것을 특징으로 하는 지지체.
- 제1항에 있어서, 상기 표면을 양극처리하여 약 0.10 내지 약 1.50g/㎡ 범위의 양극 산화물 중량을 생성하는 것을 특징으로 하는 지지체.
- 제1항에 있어서, 상기 표면이 약 35.00 내지 약 75.00 범위의 삼자극 색상 좌표값 L, 약 -4.00 내지 약 +4.00 범위의 삼자극 색상 좌표값 a 및 약 -4.00 내지 약 +4.00 범위의 삼자극 색상 좌표값 b를 가지는 것을 특징으로 하는 지지체.
- 제1항에 있어서, 상기 표면이 약 54.00 내지 약 64.00 범위의 삼자극 색상 좌표값 L, 약 -2.500 내지 약 +2.50 범위의 삼자극 색상 좌표값 a 및 약 -2.50 내지 약 +2.50 범위의 삼자극 색상 좌표값 b를 가지는 것을 특징으로 하는 지지체.
- 제1항에 있어서, 상기 표면이 약 56.00 내지 약 62.00 범위의 삼자극 색상 좌표값 L, 약 -1.50 내지 약 +1.50 범위의 삼자극 색상 좌표값 a 및 약 -1.50 내지 약 +1.50 범위의 삼자극 색상 좌표값 b를 가지는 것을 특징으로 하는 지지체.
- 제1항에 있어서, 상기 Ra가 약 0.25 내지 약0.35 마이크론의 범위이고, Rz가 약 2.50 내지 약 3.50 마이크론의 범위이며, Rt가 약 2.00 내지 약 4.00 마이크론의 범위이고, Rp가 약 1.50 내지 약 2.50 마이크론의 범위이며, 삼자극 색상 좌표값 L, a 및 b에서 L이 약 56.00 내지 약 62.00의 범위이고, a가 약 -1.50 내지 약 +1.50의 범위이며, b가 약 -1.50 내지 약 +1.50의 범위인 것을 특징으로 하는 지지체.
- 제1항에 있어서, 표면상에 친수화제를 가지는 지지체.
- 제9항에 있어서, 상기 친수화제가 폴리비닐 포스폰산을 포함하는 것을 특징으로 하는 지지체.
- 제1항의 지지체와 그 표면상에 감광성 조성물을 포함하는 석판인쇄용 인쇄판.
- 제10항의 지지체와 그 표면상에 감광성 조성물을 포함하는 석판인쇄용 인쇄판.
- 제11항에 있어서, 상기 감광성 조성물층이 1종 이상의 결합성 수지와 1종 이상의 착색제와의 혼합물의 형태로 감광성 디아조늄 화합물을 포함하는 것을 특징으로 하는 석판인쇄용 인쇄판.
- 제11항에 있어서, 상기 감광성 조성물층이 약 0.1g/㎡ 내지 약 2.0g/㎡의 코팅 중량을 가지는 것을 특징으로 하는 석판 인쇄용 인쇄판.
- 알루미늄 기판의 표면을 그래이닝 및 양극 처리함으로써 피이크와 밸리를 포함하고, 표면 조도 매개 변수 Ra가 약 0.10 내지 약0.50 마이크론의 범위이고, Rz가 약 0.00 내지 약 5.00 마이크론의 범위이며, Rt가 약 0.00 내지 약 6.00 마이크론의 범위이고, Rp가 약 0.00 내지 약 4.00 마이크론의 범위인 거의 균일한 표면지형을 생성하는 것을 포함하며, 석판인쇄용 인쇄판에 대한 지지체를 제조하는 방법.
- 제15항에 있어서, 상기 표면을 화학적 탈지, 화학적 에칭 및 전기화학적 그래이닝으로 구성된 군중에서 선택된 한 가지 이상의 공정으로 처리하는 것을 특징으로 하는 방법.
- 제16항에 있어서, 상기 표면을 양극처리하여 약 0.10 내지 약 1.50g/㎡ 범위의 양극성 산화물 중량을 생성하는 것을 특징으로 하는 방법.
- 제15항에 있어서, 상기 수득된 표면이 약 35.00 내지 약 75.00 범위의 삼자극 색상 좌표값 L, 약-4.00 내지 약 +4.00 범위의 삼자극 색상 좌표값 a 및 약 -4.00 내지 +4.00 범위의 삼자극 색상 좌표값 b를 가지는 것을 특징으로 하는 방법.
- 제16항에 있어서, 상기 화학적 탈지 및 화학적 에칭을 알칼리 수산화물 농도가 약 5g/ℓ내지 약 25g/ℓ이고, 온도가 약 100°F 내지 약 200°F인 1종 이상의 알칼리 수산화물 수용액중에서 수행하는 것을 특징으로 하는 방법.
- 제19항에 있어서, 상기 알칼리 수산화물이 약 100°F 내지 약 200°F의 온도에서 유지된 약 5g/ℓ내지 약 25g/ℓ용액 농도의 수산화 나트륨인 것을 특징으로 하는 방법.
- 제16항에 있어서, 상기 전기화학적 그래이닝을 전하 밀도가 약 5 내지 약 100쿨롱/d㎡인 염산이나 질산 전해질중에서 수행하는 것을 특징으로 하는 방법.
- 제15항에 있어서, 상기 양극처리를 농도가 약 100 내지 약200g/ℓ이고, 온도가 약 100°F 내지 약 200°F인 황산 전해질중에서 수행하는 것을 특징으로 하는 방법.
- 제16항에 있어서, 상기 화학적 탈지 및 화학적 에칭을, 수산화 나트륨 농도가 약 5g/ℓ 내지 약 25g/ℓ이고, 온도가 약 100°F 내지 약 200°F인 1종 이상의 수산화 나트륨 수용액중에서 수행하고; 전기화학적 그래이닝을, 전하 밀도가 약 5 내지 약 100쿨롱/d㎡인 질산 전해질중에서 수행하며; 양극처리를, 농도가 약 100 내지약 200g/ℓ이고 온도가 약 100°F 내지 약 200°F 황산 전해질중에서 수행하며; 수득된 표면이 약 0.10 내지 약 1.50g/㎡ 범위의 양극성 산화물 중량을 가지고; 약 35.00 내지 약 75.00 범위의 삼자극 색상 좌표값 L, 약 -4.00 내지 약 +4.00 범위의 삼자극 색상 좌표값 a 및 약 -4.00 내지 약 +4.00 범위의 삼자극 색상 좌표값 b를 가지는 것을 특징으로 하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.