KR960022330A - Carbon molding method - Google Patents
Carbon molding method Download PDFInfo
- Publication number
- KR960022330A KR960022330A KR1019940038970A KR19940038970A KR960022330A KR 960022330 A KR960022330 A KR 960022330A KR 1019940038970 A KR1019940038970 A KR 1019940038970A KR 19940038970 A KR19940038970 A KR 19940038970A KR 960022330 A KR960022330 A KR 960022330A
- Authority
- KR
- South Korea
- Prior art keywords
- pitch
- powder
- carbon molded
- molded body
- producing
- Prior art date
Abstract
본 발명은 핏치류를 원료로 하여 기계용 부품, 전기부품 및 화학장치구조용으로 사용되는 고강도, 고밀도 탄소성형체 제조방법에 관한 것이다.The present invention relates to a method for producing a high strength, high density carbon molded body which is used as a raw material for pitches for machine parts, electrical parts, and chemical device structures.
본 발명에 의하면, 연화점이 280℃ 이상인 핏치를 크기가 100μm 이하인 분말로 분쇄한 후, 산소분위기하에서 200~270℃에서 0.5~24시간 산화처리하여 산화핏치 분말을 제조한 다음, 상기 산화핏치 분말을 실온에서 100~2000kg/cm2의 압력으로 가압성형한 후, 불활황성분위기하에서 900℃ 이상의 온도에서 소성함을 특징으로 하는 핏치를 이용한 고밀도, 고강도 탄소성형체 제조방법이 제공된다.According to the present invention, a pitch having a softening point of 280 ° C. or more is pulverized into a powder having a size of 100 μm or less, followed by oxidation treatment at 200 to 270 ° C. for 0.5 to 24 hours in an oxygen atmosphere to prepare an oxide pitch powder, and then After press molding at a pressure of 100 ~ 2000kg / cm 2 at room temperature, there is provided a high-density, high-strength carbon molded article using a pitch characterized in that the firing at a temperature of 900 ℃ or more under the inert sulfur component crisis.
산화처리하여 적정량의 산소를 함유하는 산화핏치 분말을 원료로 하여 탄소성형체론 제조함으로써 간단한 제조방법으로 고밀도, 고장도 탄소성형체를 제조할 수 있다.By oxidizing and producing a carbon molded body using an oxidized pitch powder containing an appropriate amount of oxygen as a raw material, a high density, high-tension carbon molded body can be produced by a simple manufacturing method.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음As this is a public information case, the full text was not included.
Claims (3)