KR960007796A - 고자속밀도급 방향성 전기강판의 제조방법 - Google Patents
고자속밀도급 방향성 전기강판의 제조방법 Download PDFInfo
- Publication number
- KR960007796A KR960007796A KR1019940021388A KR19940021388A KR960007796A KR 960007796 A KR960007796 A KR 960007796A KR 1019940021388 A KR1019940021388 A KR 1019940021388A KR 19940021388 A KR19940021388 A KR 19940021388A KR 960007796 A KR960007796 A KR 960007796A
- Authority
- KR
- South Korea
- Prior art keywords
- steel sheet
- annealing
- oriented electrical
- electrical steel
- less
- Prior art date
Abstract
본 발명은 변압기, 전동기, 발전기 및 기타 전자기기등의 철심재료로 사용되는 방향성 전기강판의 제조방법에 관한 것으로써 제강용해시낮은 용존 Al량을 조정한 후 최종 마무리 소둔 공정에서의 1차 재결정 형성조건을 제어함으로써 저온스라브 가열법에서도 우수한 자기적 특성을 확보할 수 있는고자속 밀도급 방향성 전기강판의 제조방법을 제공하고자 한다. 본 발명은 저온스라브 가열방식에 의해 방향성 전기강판을 제조하는 방법에 있어서 중량%로 C;0.020-0.050%, Si;2.9-3.3%, P:0.016% 이하, 용존 Al:0.018-0.030%, N:0.008-0.012%, S:0.007%, 이하 Ni과 Cr의 단독 또는 복합:0.06-0.18%, Mn:0.32%이하 Cu:0.6%이하 잔부 Fe 및 기타 불가피한 불순물 조성되는 강 슬라브를 1250-1320℃의 온도구간에서 재가열하여 열간압연한후 이후 열연판 소둔을 행하지 않고 중간의 탈탄소둔을 포함한 2회의 냉간압연에 의해 최종 두께로 조정한 다음 증간회복소둔 및 MgO를 주성분으로 하는 소둔분리제를 도포한 후 1150-1200℃에소 최종 마무리 소둔을 행하고 최종 마무리 소둔시 400-700℃에서의 승온속도를 25℃/hr 이상으로 유지하는 것을 특징으로 하는 고자속밀도급 방향성 전기강판의 제조방법을 그 요지로 한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (1)
- 저온슬라브 가열방식에 의해 방향성 전기강판을 제조하는 방법에 있어서 중량%로 C;0.020-0.050%, Si;2.9-3.3%, P:0.016% 이하, 용존 Al:0.018-0.030%, N:0.008-0.012%, S:0.007%, 이하 Ni과 Cr의 단독 또는 복합:0.06-0.18%, Mn:0.32%이하 Cu:0.6%이하 잔부 Fe 및 기타 불가피한 불순물 조성되는 강 슬라브를 1250-1320℃의 온도구간에서 재가열하여 열간압연한후 이후 열연판 소둔을 행하지 않고 중간의 탈탄소둔을 포함한 2회의 냉간압연에 의해 최종 두께로 조정한 다음 중간회복소둔 및 MgO를 주성분으로 하는 소둔분리제를 도포한 후 1150-1200℃에소 최종 마무리 소둔을 행하고 최종 마무리 소둔시 400-700℃에서의 승온속도를 25℃/hr 이상으로 유지하는 것을 특징으로 하는 고자속밀도급 방향성 전기강판의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.