KR950016851A - 폴리설폰 중공사막 및 그 제조방법 - Google Patents
폴리설폰 중공사막 및 그 제조방법 Download PDFInfo
- Publication number
- KR950016851A KR950016851A KR1019930031503A KR930031503A KR950016851A KR 950016851 A KR950016851 A KR 950016851A KR 1019930031503 A KR1019930031503 A KR 1019930031503A KR 930031503 A KR930031503 A KR 930031503A KR 950016851 A KR950016851 A KR 950016851A
- Authority
- KR
- South Korea
- Prior art keywords
- hollow fiber
- fiber membrane
- diameter
- polysulfone hollow
- manufacturing
- Prior art date
Abstract
본 발명은 폴리설폰 중공사막 및 그 제조방법에 관한 것으로서, 더욱 상세하게는 중공사막 제조시 연속적으로 3단 응고공정(Coagulation process)을 거침으로써 막의 외표면이 둥근 미세공구조, 막의 내부표면은 슬리트상 구조, 외표면과 내표면사이는 망상구조를 나타내어 전체적으로 스폰지형태로서 선택분리능이 우수하고 유체 역학적인 저항이 최소화되어 수투과성이 우수하며 기계적 강도가 뛰어난 한외여과막 및 각종 복합막의 지지체로서 사용가능한 외압 방식의 폴리설폰 중공사막 및 그 제조방법에 관한 것이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (3)
- 외표면에 직경 0.001∼0.01㎛의 둥근 미세공구조를 가지며, 내표면에 직경 0.1∼0.5㎛의 슬리트상 구조를 가지며, 외표면과 내표면 사이에는 직경 0.5∼3㎛의 망상구조를 가지며, 중공사막 외표면에서 내표면까지 미세공 크기가 커지는 스폰지 구조를 가짐을 특징으로 하는 폴리설폰 중공사막.
- 1단 응고매체로서 유기용매 단독 혹은 물과의 혼합용매를 사용하여 외표면에 직경 0.001∼0.01㎛의 둥근 미세공 구조를 부여하고, 2단 응고매체로서 물 단독 혹은 유기용매와의 혼합용매를 사용하여 외표면과 내표면 사이의 직경 0.5∼3㎛의 망상구조를 부여하고, 3단 응고매체로서 에틸알코올, 프로필알코올, 또는 50∼95℃의 열수를 사용하여 내표면에 직경 0.1∼0.5㎛의 슬리트상 구조를 부여하는 3단 응고공정을 거침을 특징으로 하는 폴리술폰 중공사막의 제조방법.
- 제2항에 있어서, 유기용매가 메틸알코올, 에틸알코올, 프로필알코올, 이소프로필알코올, 글리세롤, 에틸렌글리콜, 콜리에틸렌글리콜, 폴리비닐피롤리돈, 또는 N－메틸－2－피롤리돈 임을 특징으로 하는 폴리설폰 중공사막의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.