KR950016852A - 폴리설폰 다공성 중공사막과 그의 제조방법 - Google Patents
폴리설폰 다공성 중공사막과 그의 제조방법 Download PDFInfo
- Publication number
- KR950016852A KR950016852A KR1019930031996A KR930031996A KR950016852A KR 950016852 A KR950016852 A KR 950016852A KR 1019930031996 A KR1019930031996 A KR 1019930031996A KR 930031996 A KR930031996 A KR 930031996A KR 950016852 A KR950016852 A KR 950016852A
- Authority
- KR
- South Korea
- Prior art keywords
- hollow fiber
- fiber membrane
- polysulfone
- porous hollow
- coagulant
- Prior art date
Abstract
본 발명은 폴리설폰 다공성 중공사막과 그의 제조방법에 관한 것으로서, 더욱 상세하게는 내표면은 미세기 공의 치밀한 스킨층이 있으며 막내부 및 외표면은 미세 다공성 구조를 가지는 중공사막으로서 기존의 중공사막에 비하여 높은 수투과성을 지니면서도 내구성, 내압성 등 기계적 성질이 우수한 다공성 중공사막과 그의 제조방법에 관한 것이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명에 의해 얻어진 중공사막의 단면구조의 형태를 나타낸 것이고,
제2도는 본 발명의 중공사막의 제조에 이용되는 중공사 제조장치의 개략적인 구성도이다.
Claims (3)
- 내표면에 스킨층을 가지고 및 외표면은 미세다공 구조를 갖는 비대칭 구조의 폴리설폰 중공사막에 있어서, 중공사막을 이루는 원형단면에서 중앙으로부터 0.5∼1.0㎛ 두께의 내표면 스킨층(8)과 그에 인접된 50∼100㎛ 두께의 거대기공(9) 및 망상구조(10)가 차례로 형성되어 이루어진 것을 특징으로 하는 폴리설폰 다공성 중공사막.
- 폴리머, 극성용매, 무기염 및 무기산으로 이루어진 방사용액과, 내부응고제 및 외부응고제를 사용하여 건습식 방사방법으로 폴리설폰 중공사막을 제조함에 있어서, 소수성 폴리머로서 폴리설폰 12∼25중량%, 폴리비닐피롤리돈 또는 폴리에틸렌글리콜 중에서 선택된 수용성 폴리머 5∼40중량%, N－메틸피롤리돈, 디메틸포름아마이드, 디메틸설폭사이드 또는 디메틸아세트아마이드 중에서 선택된 극성용매 40∼75중량%, LiNO3, LiBr 또는 ZnCl2중에서 선택된 무기염 2∼8중량%, 무기산으로서 H2SO40.05∼0.50중량^가 함유된 방사용액을 사용하고, 내부응고제와 외부응고제로서 물단독성분 또는 물과 빈용매 또는 물과 용매를 70∼20/30∼80의 비율로 혼합하여 사용하여, 3∼40cm, 권취속도 8∼40m/min으로 방사하여 제조함을 특징으로 하는 폴리설폰 다공성 중공사막의 제조방법.
- 제2항에 있어서, 상기 방사용액은 온도를 25∼60℃로 유지하고 내부응고제 및 외부응고제는 온도를 20∼80℃ 유지하는 상태에서 방사하여 제조함을 특징으로 하는 폴리설폰 다공성 중공사막의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.