KR930007837A - 리드 실리케이트 유리 - Google Patents
리드 실리케이트 유리 Download PDFInfo
- Publication number
- KR930007837A KR930007837A KR1019920019392A KR920019392A KR930007837A KR 930007837 A KR930007837 A KR 930007837A KR 1019920019392 A KR1019920019392 A KR 1019920019392A KR 920019392 A KR920019392 A KR 920019392A KR 930007837 A KR930007837 A KR 930007837A
- Authority
- KR
- South Korea
- Prior art keywords
- glass
- weight
- sro
- bao
- zno
- Prior art date
Abstract
본 발명은 음극선관의 넥크 부분에 사용하기 위하여 관모양으로 인출하는데 적합한 리드 실리케이트 유리군에 관한 것이다. 상기 유리는 750℃ 보다 낮은 내부 액화온도, 8.0ohm-㎝(Log R350℃)보다 높은 전기저항 및 0.6Å 단위의 파장에서 적어도 95㎝-1의 선형 X-레이 흡수값을 가진다. 그의 조성물은 필수적으로 기본 산화물에 대하여 SiO246~51 중량%, Al2O30.5~2 중량%, Na2O 0.3~3 중량%, K2O 9~13 중량%, SrO 2.5~6 중량%, BaO 1~4 중량%, PbO 30~33 중량%, ZnO 0~2 중량% 및 Sb2O30.3~1 중량%로 이루어진다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제2도는 본 발명에 의한 유리의 실투현상으로부터 얻은 데이터를 그래프로 도시한 것이다.
Claims (12)
- 750℃ 보다 낮은 내부 액화온도, 8.0ohm-㎝(Log R350℃)보다 높은 전기저항 및 0.6Å 단위의 파장에서 적어도 95㎝-1의 선형 X-레이 흡수값을 가지며, 필수적으로 기본 산화물에 대하여 SiO246~51 중량%, Al2O30.5~2 중량%, Na2O 0.3~3 중량%, K2O 9~13 중량%, SrO 2.5~6 중량%, BaO 1~4 중량%, PbO 30~33 중량% 및 Sb2O30.3~1 중량%로 구성된 조성물로 이루어진 것을 특징으로 하는 리드 실리케이트 유리.
- 제1항에 있어서, 상기 유리 조성물에는 2%를 초과하지 않는 ZnO가 더 포함되는 것을 특징으로 하는 리드 실리케이트 유리.
- 제2항에 있어서, 상기 유리 조성물에는 SrO+BaO+ZnO의 총량이 5~8%인 것을 특징으로 하는 리드 실리케이트 유리.
- 제1항에 있어서, 상기 조성물은 필수적으로 SiO247~50%, Al2O30.5~2.0 %, Na2O 0.3~1.0 %, K2O 12~13 %, SrO 2.5~3.5 %, BaO 1~3 %, ZnO 0.5~1.5 % Pbo 30~33 % 및 Sb2O30.3~1 %인 것을 특징으로 하는 리드 실리케이트 유리.
- 750℃ 보다 낮은 내부 액화온도, 8.0ohm-㎝(Log R350℃)보다 높은 전기저항 및 0.6Å 단위의 파장에서 적어도 95㎝-1의 선형 X-레이 흡수값을 가지며, 필수적으로 기본 산화물에 대하여 SiO246~51 중량%, Al2O30.5~2 중량%, Na2O 0.3~3 중량%, K2O 9~13 중량%, SrO 2.5~6 중량%, BaO 1~4 중량%, PbO 30~33 중량%, 및 Sb2O30.3~1 중량%로 구성된 조성물로 이루어진 리드 실리케이트 유리를 용융시켜 그로부터 인출되는 것을 특징으로 하는 유리관.
- 제5항에 있어서, 상기 유리 조성물에는 2%를 초과하지 않는 ZnO가 더 포함되는 것을 특징으로 하는 유리관.
- 제6항에 있어서, 상기 유리 조성물에는 SrO+BaO+ZnO의 총량이 5~8%인 것을 특징으로 하는 유리관.
- 제5항에 있어서, 상기 조성물은 필수적으로 SiO247~50%, Al2O30.5~2.0 %, Na2O 0.3~1.0 %, K2O 12~13 %, SrO 2.5~3.5 %, BaO 1~3 %, ZnO 0.5~1.5 % Pbo 30~33 % 및 Sb2O30.3~1 %인 것을 특징으로 하는 유리관.
- 750℃ 보다 낮은 내부 액화온도, 8.0ohm-㎝(Log R350℃)보다 높은 전기저항 및 0.6Å 단위의 파장에서 적어도 95㎝-1의 선형 X-레이 흡수값을 가지며, 필수적으로 기본 산화물에 대하여 SiO246~51 중량%, Al2O30.5~2 중량%, Na2O 0.3~3 중량%, K2O 9~13 중량%, SrO 2.5~6 중량%, BaO 1~4 중량%, PbO 30~33 중량%, 및 Sb2O30.3~1 중량%로 구성된 조성물로 이루어진 리드 실리케이트 유리로부터 제조된 넥크와 페이스플레이트, 퓨널 및 전자총으로 구성된 것을 특징으로 하는 음극선관.
- 제9항에 있어서, 상기 넥크 유리 조성물에는 2%를 초과하지 않는 ZnO가 더하여 포함되는 것을 특징으로 하는 음극선관.
- 제10항에 있어서, 상기 넥크 유리 조성물에는 SrO+BaO+ZnO의 총량이 5~8%인 것을 특징으로 하는 유리관.
- 제9항에 있어서, 상기 넥크 유리조성물은 필수적으로 SiO247~50%, Al2O30.5~2.0 %, Na2O 0.3~1.0 %, K2O 12~13 %, SrO 2.5~3.5 %, BaO 1~3 %, ZnO 0.5~1.5 % Pbo 30~33 % 및 Sb2O30.3~1 %인 것을 특징으로 하는 음극선관.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.