KR920010014A - 건식플락스법에 의한 용융금속도금용플락스 및 이 플락스를 사용한 용융금속 도금강재의 제조방법 - Google Patents
건식플락스법에 의한 용융금속도금용플락스 및 이 플락스를 사용한 용융금속 도금강재의 제조방법 Download PDFInfo
- Publication number
- KR920010014A KR920010014A KR1019910021847A KR910021847A KR920010014A KR 920010014 A KR920010014 A KR 920010014A KR 1019910021847 A KR1019910021847 A KR 1019910021847A KR 910021847 A KR910021847 A KR 910021847A KR 920010014 A KR920010014 A KR 920010014A
- Authority
- KR
- South Korea
- Prior art keywords
- flux
- molten metal
- chloride
- chlorides
- metal plating
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 아연 알루미늄 합금의 상태도.
제2도는 도금온도와 도금부착량의 관계를 표시하는 그래프.
Claims (10)
- 적어도 염화물과 지방족 질소유도체로 이루어지며, 염화물로서 염화아연, 염화제1주석, 알칼리금속의 염화물 혹은 알칼리토류금속의 염화물 내의 1종 또는 2종 이상과, 탄소수 1내지 18의 알킬기를 보유하는 지방족 질소유도체의 1종 또는 2종 이상을 함유하는 것을 특징으로 하는 건식플락스법에 의한 용융금속도금용 플락스.
- 제1항에 있어서, 상기한 지방족 질소유도체로서, 탄소수 7 내지 18의 알킬기를 보유하는 알킬제4급 암모늄염이나, 혹은 탄소수 1 내지 18의 알킬기를 보유하는 알킬아민류를 사용하여 이루어지는 것을 특징으로 하는 건식플락스법에 의한 용융금속도금용 플락스.
- 제1항 또는 제2항에 있어서, 염화아연이나 혹은 염화제1주석 10 내지 50중량%와, 알킬제4급 암모늄염 혹은 알킬아민류의 1종 또는 2종 이상을 0.1 내지 30중량% 함유하는 것을 특징으로 하는 건식플락스법에 의한 용융금속도금용 플락스.
- 제1항 또는 제2항에 있어서, 알칼리금속의 염화물 혹은 알칼리토류 금속의 염화물 1종 또는 2종 이상을 1내지 20중량%와, 알킬제4급 암모늄염, 혹은 알칼아민류 1종 또는 2종 이상을 0.1 내지 30중량% 함유하는 것을 특징으로 하는 건식플락스법에 의한 용융금속도금용 플락스.
- 제1항 또는 제2항에 있어서, 염화아연 혹은 염화제1주석 10 내지 50중량%와, 알칼리금속의 염화물 혹은 알칼리토류 금속염화물의 1종 또는 2종 이상을 1 내지 20중량%와, 알킬제4급 암모늄염 혹은 알킬아민류의 1종 또는 2종 이상을 0.1 내지 30중량% 함유하는 것을 특징으로 하는 건식플락스법에 의한 용융금속도금용 플락스.
- 제2항 내지 제5항중의 어느 한 항에 있어서, 상기한 알킬 제4급 암모늄염이, 알킬트리메틸암모늄클로라이드, 디알킬디메틸암모늄 클로라이드인 것을 특징으로 하는 건식플락스법에 의한 용융금속도금용 플락스.
- 피도금 강재를, 알칼리욕탕에 침지하여, 탈지한 후, 수세하며 산세하는 전처리공정과 전처리한 피도금강재를, 적어도 염화물과 지방족질소유도체로 이루어지며, 염화물로써 염화아연, 염화제1주석, 알칼리금속의 염화물 혹은 알칼리토류금속 염화물내의 1종 또는 2종 이상과, 탄소수 1내지 18의 알킬기를 보유하는 지방족소유도체의 1종 또는 2종 이상을 함유하는 플락스에 침지하는 플락스 처리공정과, 플락스 처리한 피도금강재를, 용융금속도금욕탕에 침지하여 피막을 형성하는 도금용 침지공정과, 도금피막을 형성한 피도금강재를 냉각수에 침지 또는 공냉하는 냉각공정으로 이루어짐을 특징으로 하는 건식 플락스법에 의한 용융금속 도금강재의 제조방법.
- 제7항에 있어서, 상기한 지방족 질소유도체로서 탄소수 7 내지 18의 알킬기를 보유하는 알킬제4급 암모늄염 또는 탄소수 1내지 18의 알킬기를 보유하는 알킬아민류를 사용해서 이루어지는 것을 특징으로 하는 건식플락스법에 의한 용융금속도금강재의 제조방법.
- 제8항에 있어서, 상기한 알킬제4급 암모늄염이, 알킬트리메틸암모늄클로라이드, 디알킬디메틸암모늄클로라이드인 것을 특징으로 하는 건식플락스법에 의한 용융금속도금강재의 제조방법.
- 제7항에 있어서, 상기한 용융금속도금욕탕으로서, 용융아연도금욕, 용융아연 알루미늄 합금도금욕, 혹은 각종 원소를 첨가한 용융아연 알루미늄 합금도금욕 또는 알루미늄 도금욕을 사용하여 이루어지는 것을 특징으로 하는 건식플락스법에 의한 용융금속 도금강재의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.