KR900015373A - 외부다공성 서어멧 연료전극 및 코팅방법 - Google Patents
외부다공성 서어멧 연료전극 및 코팅방법 Download PDFInfo
- Publication number
- KR900015373A KR900015373A KR1019890017010A KR890017010A KR900015373A KR 900015373 A KR900015373 A KR 900015373A KR 1019890017010 A KR1019890017010 A KR 1019890017010A KR 890017010 A KR890017010 A KR 890017010A KR 900015373 A KR900015373 A KR 900015373A
- Authority
- KR
- South Korea
- Prior art keywords
- mixtures
- group
- electrode
- particles
- micrometers
- Prior art date
Abstract
내용 없음.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 전해질의 상부 전면에 배치된 세라믹 산화물 매트릭스에 분리된 니켈 및/또는 코발트 소립자를 포함하는 본 발명의 분리된 다상코팅으로 피복된 산화물 골격구조에 일부 삽입된 조립금속 입자를 갖는 연료전극의 한 실시예를 도시하는 단면도의 약단면도(略湍面圖),
제2도는 본 발명의 방법을 도시하는 블록 다이어그램, 제3도는 본 발명에 따라, 예에 기술된 바와같이 제작되고 작동되는 전지에 관하여, 볼트로 나타낸 전지전압대 시간(hour)으로 표시된 시간(time)에 대한 곡선.
Claims (9)
- 내부전극(14)과 접촉하고 있는 고체 산소이온을 전도하는 전해질(13)에 결합되고, 3-35마이크로미터의 직경을 갖는 니켈 입자, 코발트 입자, 및 이들의 혼합물로 구성되는 외부 다공성 전극(10)에 있어서, 외부 전극의 입자는 (a) 0.05-1.75마이크로미터의 직경을 갖는 분리된 니켈 입자, 분리된 코발트 입자, 및 이들의 혼합물로 구성되는 그룹에서 선택되는 미세 금속입자(18), 및 (b) 새름 산화물, 도우프된 세름 산화물, 스트론름 티탄산염, 도우프된 스트론틈 티탄산염, 및 이들이 혼합물로 구성되는 그룹에서 선택된 전도성 산화뮬(19)로 주로 구성되는 분리된 전자 전도성의 다공성 다상층(17)으로 코트 되는것을 특징으로 하는 외부 다공성 서어멧 연료전극.
- 제1항에 있어서, 미세금속 입자(18) 는 025-0.75마이크로미터의 직경을 가지며 조립 금속입자(12)는 5-35마이크로미터의 직경을 가지는 것을 특징으로 하는 외부 다공성 서어멧 연료전극.
- 제1항에 있어서, 다상층(17)은 완전히 피복되며 0.5-2.0마이크로미터의 두께를 가지는 것을 특징으로 하는 외부 다공성 서어멧 연료전극.
- 제1항에 있어서, 다상층(17)에서 전도성 산화물(l9)과 함께 사용된 도우펀트는 Mg, Ca. Sr, Ba, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Y, Al, 및 이들의 혼합물로 구성되는 그룹에서 선택되는 것을 특징으로 하는 외부 다공성 서어멧 연료전극.
- 제1항에 있어서, 전도성 산화물(19)은 Mg, Ca, Sr, Ba, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Y, A1, 및 이들의 혼합물로 구성되는 그룹에서 선택된 재료로 도우프된 새름산화물 및 새름산화물로 구성되는 그룹에서 선택되는 것을 특징으로 하는 외부 다공성 서어멧 연료전극.
- 제1항에 있어서, 미세금속입자(18)는 다상층 내부의 입자가 전극상의 전기화학적 활성자리수를 증가시키는 니켈 입자이고, 전도성 산화물(19)은 Ca, Sm, 및 이들의 혼합물로 구성되는 그룹에서 선택된 재료로 도우프된 새름 산화물 및 세름 산화물로 구성되는 그룹에서 선택되며, 조립 금속입자(12)는 지르코니아를 구성하는 골격구조물에 부분적으로 삽입되는 것을 특징으로 하는 외부 다공성 서어멧 연료전극.
- 또한 내부전극(14)과 접촉하고 있는 고체 산소이온을 전도하는 전해질(13)에 결합되는 외부 다공성 전극상에 분리된 전자 전도성층을 코팅하는 방법에 있어서, (1) (a)금속 구성성분이 니켈, 코발트 및 이들의 혼합물로 구성되는 그룹에서 선택되고, 염성분이 질산염, 초산염, 프로피온산염, 부티르산염, 및 이들의 혼합물로 구성되는 그룹에서 선택되는 제1금속염, (b)금속성분이 세름, 도우프된 새름, 스트론름-티탄, 도우프된 스트론륨-티탄, 및 이들의 혼합물로 구성되는 그룹에서 선택되고, 염성분이 질산염, 초산염, 프로피온산염, 부티르산염, 및 이들의 혼합물로 구성되는 그룹에서 선택되는 제2금속염, 및 (c) 비 이온성 계면활성제로 주로 구성되는 혼합물을 외부 다공성 전극(10)에 사용하는 단계와, (2) 0.05-1.75마이크로이터의 직경을 갖는 분리된 니켈입자, 분리된 코발트 입자, 및 이들의 혼합물로 구성되는 그룹에서 선택되는 미세 금속입자(18)와, 세륨산화물, 도우프된 세륨산화물, 스트론륨 티탄산염, 도우프된 스트론륨 티탄산염, 및 이들의 혼합물로 구성되는 그룹에서 선택되는 전도성 산화물(19)로 주로 구성되는 분리된 고체 전자 전도성의 다공성 다상층(17)을 형성시키기에 유효한 온도에서, 니켈, 코발트, 및 이들의 혼합물로 환원시키는 분위기에서 코팅 혼합물을 히팅시키는 단계로 구성되는 것을 특징으로 하는 외부 다공성 서어멧 연료 전극 코팅 방법.
- 제7항에 있어서, 코트된 외부 다공성 전극(10)은 지르코니아를 구성하는 골격 구조물에 부분적으로 삽입된 3-35마이크로미터의 직경을 갖는 조립금속입자(12)및 0.25-0.75마이크로이터의 직경을 갖고 단계(2)에서 형성된 미세금속입자(18)침전물로 구성되는 것을 특징으로 하는 외부 다공성 서어멧 연료 전극 코팅 방법.
- 제7항에 있어서, 제2금속염의 금속과 함께 사용된 도우 펀트는 Mg, Ca, Sr, Ba, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Y, Al, 및 이들의 혼합물로 구성되는 그룹에서 선택되고, 단계(2)의 히팅은 50℃/시-100℃/시의 비율로 행해지는 것을 특징으로 하는 외부 다공성 서어멧 연료 전극 코팅 방법.※참고사항:최초출원 내용에 의하여 공개하는 것임.