KR880002200A - 네오디뮴-철-붕소계 영구자석의 제조방법 - Google Patents

네오디뮴-철-붕소계 영구자석의 제조방법 Download PDF

Info

Publication number
KR880002200A
KR880002200A KR1019870007906A KR870007906A KR880002200A KR 880002200 A KR880002200 A KR 880002200A KR 1019870007906 A KR1019870007906 A KR 1019870007906A KR 870007906 A KR870007906 A KR 870007906A KR 880002200 A KR880002200 A KR 880002200A
Authority
KR
South Korea
Prior art keywords
neodymium
calcium
iron
boron
fluoride
Prior art date
Application number
KR1019870007906A
Other languages
English (en)
Other versions
KR900006193B1 (ko
Inventor
마사아끼 도꾸나가
기미오 우찌다
아끼또시 히라끼
Original Assignee
원본미기재
히다찌 긴조꾸 가부시기 가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 원본미기재, 히다찌 긴조꾸 가부시기 가이샤 filed Critical 원본미기재
Publication of KR880002200A publication Critical patent/KR880002200A/ko
Application granted granted Critical
Publication of KR900006193B1 publication Critical patent/KR900006193B1/ko

Abstract

내용 없음

Description

네오디뮴-철-붕소계 영구자석의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명의 1실시예에 따라 제조된 네오디뮴-철-붕소계 영구자석의 자기적 성질과 네오디뮴량 사이에 관계를 도시하는 그래프
제2도는 본 발명의 또 다른 실시예에 따라 제조된 네오디뮴-철-붕소계 영구자석의 자기적 성질과 붕소량 사이의 관계를 도시하는 그래프

Claims (8)

  1. 네오디뮴 25.0 내지 50.0중량%, 붕소 0.3 내지 5.0중량% 및 잔부는 철로 구성되어 있는 네오디뮴-철-붕소계 영구자석 합금의 제조 방법에 있어서, 플로오르화 네오디뮴, 철 및 붕소(또는 페로 붕소)에 대한 환원제로써 칼슘, 수소화 칼슘 또는 그것의 화합물을 첨가하고, 거기에 용제로써 적어도 염화 칼슘, 염화 나트륨 및 염화 칼륨중의 하나를 더 첨가하고, 이 최종 혼합물을 비활성 가스 분위기, 또는 환원 가스 분위기 또는 진공에서 1000내지 1300℃로 용융시켜, 이에 따라 상기 플로오르화 네오디뮴을 환원시켜 극소량의 칼슘 함유량을 갖는 상기 합금을 만드는 단계를 구비하고 있는 것을 특징으로 하는 네오디뮴-철-붕소계 영구자석 합금의 제조 방법.
  2. 제1항에 있어서, 환원제로써 금속 칼슘, 수소화 칼슘 또는 그것의 혼합물을 상기 플로오르화 네오디뮴의 환원반응을 위하여 화학량론적으로 필요한 양의(중량으로) 1.0내지 4.0배의 양으로 첨가하는 것을 특징으로 하는 네오디뮴-철-붕소계 영구자석 합금의 제조 방법.
  3. 제1항에 있어서, 용제로써 적어도 염화 칼슘, 염화 나트륨 및 염화 칼륨 중의 하나를 상기 플로오르화 네오디뮴의 환원반응에 의해 폴로오르화 칼슘을 생성하기 위하여 화학량론적으로 필요한 양의(몰로) 0.05 내지 4.0배의 양으로 첨가하는 것을 특징으로 하는 네오디뮴-철-붕소계 영구자석 합금의 제조방법.
  4. 제1항에 있어서, 최종 합금의 칼슘 함유량이 0.1중량% 이하인 것을 특징으로 하는 네오디뮴-철-붕소계 영구자석 합금의 제조방법.
  5. 네오디뮴 25.0 내지 50.0중량%, 디스프로슘 0.5내지 15.0중량%, 붕소 0.3내지 5.0중량%, 니오브 0.05내지 5.0중량% 및 잔부는 철로 구성되어 있는 네오디뮴-디스프로슘-철-붕소-니오브계 영구자석 합금의 제조 방법에 있어서, 플로오르화 네오디뮴, 플로오르화 디스프로슘, 철, 붕소(또는 페로 붕소), 그리고 니오브(또는 페로니오브)에 환원제로써 금속 칼슘, 수소화 칼슘, 또는 그것의 혼합물을 첨가하고, 용제로써 적어도 염화 칼슘, 염화 나트륨 및 염화 칼륨 중의 하나를 더 첨가하고, 이 최종 혼합물을 비활성 가스 분위기, 또는 환원 가스 분위기 또는 진공에서 1000내지 1300℃로 용융시켜, 이에 따라 상기 플로오르화 네오디뮴 및 상기 플로오르화 디스프로슘을 환원시켜 극소량의 칼슘 함유량을 갖는 상기 합금을 만드는 단계를 구비하고 있는 것을 특징으로 하는 네오디뮴-디스프로슘-철-붕소-니오브계 영구자석 합금의 제조 방법.
  6. 제5항에 있어서, 환원제로써 금속 칼슘, 수소화 칼슘 또는 그것의 혼합물을 상기 플로오르화 네오디뮴 및 상기 플로오르화 디스프로슘의 환원 반응을 위하여 화학량론적으로 필요한 양의(중량으로) 1.0내지 4.0배의 양으로 첨가하는 것을 특징으로 하는 네오디뮴-디스프로슘-철-붕소-니오브계 영구자석 합금의 제조방법.
  7. 제5항에 있어서, 용제로써 적어도 염화 칼슘, 염화 나트륨 및 염화 칼륨 중의 하나를 상기 플로오르화 네오디뮴 및 상기 플로오르화 디스프로슘의 환원반응에 의해 플로오르화 칼슘을 생성하기 위하여 화학량론적으로 필요한 양의(몰로) 0.05내지 4.0배의 양으로 첨가하는 것을 특징으로 하는 네오디뮴-디스프로슘-철-붕소-니오브계 영구자석 합금의 제조방법.
  8. 제5항에 있어서, 최종 합금의 칼슘 함유량이 0.1중량% 이하인 것을 특징으로 하는 네오디뮴-디스프로슘-철-붕소-니오브계 영구자석 합금의 제조 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019870007906A 1986-07-21 1987-07-21 네오디뮴-철-붕소계 영구 자석의 제조방법 KR900006193B1 (ko)