KR860002585A - 공구용 다이어몬드 소결체 및 그 제조방법 - Google Patents

공구용 다이어몬드 소결체 및 그 제조방법 Download PDF

Info

Publication number
KR860002585A
KR860002585A KR1019850006553A KR850006553A KR860002585A KR 860002585 A KR860002585 A KR 860002585A KR 1019850006553 A KR1019850006553 A KR 1019850006553A KR 850006553 A KR850006553 A KR 850006553A KR 860002585 A KR860002585 A KR 860002585A
Authority
KR
South Korea
Prior art keywords
diamond
sintered body
powder
carbide
periodic table
Prior art date
Application number
KR1019850006553A
Other languages
English (en)
Other versions
KR900002701B1 (ko
Inventor
데쯔오 니까이 (외 1)
Original Assignee
나까하라 쯔네오
스미또모 덴끼 고교 가부시끼 가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP59188492A external-priority patent/JPS6167740A/ja
Priority claimed from JP59226574A external-priority patent/JPS61104045A/ja
Priority claimed from JP59246565A external-priority patent/JPS61125739A/ja
Application filed by 나까하라 쯔네오, 스미또모 덴끼 고교 가부시끼 가이샤 filed Critical 나까하라 쯔네오
Publication of KR860002585A publication Critical patent/KR860002585A/ko
Application granted granted Critical
Publication of KR900002701B1 publication Critical patent/KR900002701B1/ko

Abstract

내용 없음

Description

공구용 다이어몬드 소결체 및 그 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 결합상이 용출되는 내열성 다이어몬드 소결체에 있어서의 압축강도와 기공체적과의 관계 도시도.
제2도는 다이어몬드 소결체에 있어서의 다이어몬드 입도와 항절력과의 관계 도시도.
제3도는 실시예 4에서 얻어진 내열성 다이어몬드 소결체의 안산암 절삭 시험결과를 도시한 도.

Claims (32)

  1. 다이어몬드 함유량이 93용량%를 넘고 또 99용량%이하로서 나머지부가 주기율표 제IVa,Va,VI족의 금속 또는 탄화물과, 철금속과의 적어도 한쪽을 합계 0.1 내지 3용량% 및 기공 0.5용량% 이상 7용량%이하로 이루어진 것을 특징으로 하는 공구용 다이어몬드 소결체.
  2. 제1항에 있어서, 상기 다이어몬드 함유량이 95용량%를 넘고 99용량% 이하이고, 나머지의 기공이 0.5용량% 이상 5용량% 미만인 것을 특징으로 하는 공구용 다이어몬드 소결체.
  3. 제1항에 있어서, 함유되어 있는 상기 다이어몬드는 입경 3㎛ 이상의 거칠은 다이어몬드와, 입경 ㎛이하의 미립 다이어몬드를 용량비로 60:38 내지 90:6의 비율로 포함하는것을 특징으로 하는 공구용 다이어몬드 소결체.
  4. 제3항에 있어서, 거칠은 다이어몬드 입자의 입도가 5㎛이상 200㎛이하인 것을 특징으로 하는 공구용 다이어몬드 소결체.
  5. 제1항에 있어서, 주기율표 제IVa,Va,VIa족의 탄화물이 탄화텅스텐(WC) 또는 탄화텅스텐과 동일의 결정구조를 가지는 탄화 몰리브덴 텅스텐(MOWC)인 것을 특징으로 하는 공구용 다이어몬드 소결체.
  6. 제1항에 있어서, 붕소 및 붕화물의 적어도 한쪽을 합계 0.005 내지 0.25용량%를 추가로 포함하는 것을 특징으로 하는 공구용 다이어몬드 소결체.
  7. 제1항에 있어서, 공구용 다이어몬드 소결체와 상기 공구용 다이어몬드 소결체에 접합되는 초경 합금 기재를 포함하는 것을 특징으로 하는 공구용 다이어몬드 소결체.
  8. 제7항에 있어서, 상기 공구용 다이어몬드 소결체와, 상기 초경 합금기재는 중간접합층을 통하여 서로 접합되어 있는 것을 특징으로 하는 공구용 다이어몬드 소결체.
  9. 제1항에 있어서, 청구범위 제6항의 공구용 다어어몬드 소결체와, 상기 공구용 다이어몬드 소결체에 접합되는 초경합금 기재를 포함하는 것을 특징으로 하는 공구용 다이어몬드.
  10. 제9항에 있어서, 상기 공구용 다이어몬드 소결체와, 상기 초경 합금기재는 중간접합층을 통하여 접합되는 것이 특징인 공구용 다이어몬드 소결체.
  11. 청구범위 제1항의 공구용 다이어몬드 소결체의 제조방법에 있어서, 다이어몬드 분말, 또는 다이어몬드 분말과 주기율표 제 IVa,Va,VIa족의 금속 혹은 탄화물 및 철금속과의 혼합분말을 만드는 단계와 1300℃ 이상의 온도에서 상기 혼합 분말중의 다이어몬드의 일부를 흑연화하는 단계와, 철금속 또는 주기율표 IVa,Va,VIa족의 소결탄화물과 접촉되어 초고압, 고온 장치를 사용하여 다이어몬드가 안정한 고온 고압하에서 고온 프레스하고 소결체를 만드는 단계와, 얻어진 소결체를 산처리 함으로써 철금속 및 주기 율표 제IVa,Va,VIa족의 금속 또는 탄화물의 일부를 용출하는 단계를 구비하는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  12. 제11항에 있어서, 상기 주기율표 제IVa,Va,VIa족의 탄화물을 탄화텅스텐 또는 탄화텅스텐과 동일 결정구조를 가지는 탄화몰리브덴 텅스텐인 것이 특징인 공구용 다이어몬드 소결체의 제조방법.
  13. 제11항에 있어서, 청구범위 제7항의 공구용 다이어몬드 소결체의 제조방법으로서, 다이어몬드 분말 또는 다이어몬드 분말과 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물 및 철금속과의 혼합 분말을 만드는 단계화 1300℃이상의 온도에서 혼합분말중의 다이어몬드의 일부를 흑연화하는 단계와, 초경합금기재와 접촉되는 단계와 상기 혼합분말에 철금속 또는 주기율표 제IVa,Va,VIa족의 소결탄화물믈 접촉시켜 초고압고온 장치를 사용하여 다이어몬드가 안정한 고온 고압하에서 복합형 소결체를 만들고 상기 복합형 소결체를 산화성 액체로 처리함으로써 소결체중의 철금속 및 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물의 일부를 용출하는 단계를 구비하는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  14. 제13항에있어서, 상기 다이어몬드 혼합분말과 초경합금 기재와의 접촉시 다이어몬드와 초경합금 기재를 중간 접합층을 통하여 접촉시키는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  15. 제13항에있어서, 상기 산화성 액체에 의한 처리시 초경합금 기재의 표면에 산화피막층을 형성하고 그에 따라 초경합금 기재중의 철금속의 용출을 방지하는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  16. 제11항에 있어서, 다이어몬드 분말과 철금속 또는 다이어몬드 분말과 주기율표 제Va,Va,VIa족의 금속 또는 탄화물 및 철금속과의 혼합 분말을 만드는 단계와 1300℃이상의 온도에서 혼합분말중의 다이어몬드의 일부를 흑연화하는 단계와, 초고압, 고온 장치를 사용하여 다이어몬드가 안정한 고온 고합하에서 고온 프레스하여 소결체를 만드는 단계와, 상기 소결체를 산처리 함으로써 철금속 또는 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물의 일부를 용출하는 단계를 구비하는 공구용 다이어몬드 소결체의 제조방법.
  17. 제16항에 있어서, 상기 주기율표 제IVa,Va,VIa족의 탄화물은 탄화텅스텐 또는 탄화텅스텐과 동일의 결정 구조를 가지는 탄화 몰리브덴 텅스텐인 것이 특징인 공구용 다이어몬드 소결체의 제조방법.
  18. 제11항에 있어서, 청구범위 제7항의 공구용 다이어몬드 소결체의 제조방법으로서, 다이어몬드 분말과 철금속 또는 다이어몬드 분말과 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물 및 철금속과의 혼합분말을 만드는 단계화 1300℃이상의 온도에서 혼합분말중의 다이어몬드의 일부를 흑연화하는 단계와, 초경합금 기재와 상기 다이어몬드를 접촉시켜 초고압, 고온장치를 사용하여 다이어몬드가 안정한 고온고압하에서 고온프레스하여 소결체를 만드는 단계와 얻어진 소결체를 산화성액체로 처리함으로써 소결체중의 철금속 및 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물의 일부를 용출하는 단계를 구비하는 공구용 다이어몬드 소결체의 제조방법.
  19. 제18항에 있어서, 상기 다이어몬드와, 초경합금 기재는 중간 접합층을 통하여 접촉되는 것이 특징인 공구형 다이어몬드 소결체의 제조방법.
  20. 제18항에 있어서, 상기 산화성 액체의 처리시 초경합금 기재의 표면에 산화피막층을 형성하는 단계를 추가로 포함하는 것을 특징으로하는 공구용 다이어몬드 소결체의 제조방법.
  21. 제11항에 있어서, 청구범위 제7항의 공구용 다이어몬드 소결체의 제조방법으로서, 다이어몬드 분말과 붕소 혹은 붕화물과의 혼합분말 또는 다이어몬드 분말과 주기율표 제IVa,Va,VIa족의 금속 혹은 탄화물 철금속 및 붕소 또는 붕화물과의 혼합 분말을 만드는 단계와, 1300℃이상의 온도에서 혼합분말중의 다이어몬드의 일부를 흑연화하는 단계와, 철 금속 또는 주기율표 제IVa,Va,VIa족의 소결탄화물과 접촉시킨 후 초고압, 고온장치를 사용하여 다이어몬드가 안정한 고온고압하에서 고온프레스하여 소결체를 만드는 단계와 얻어진 소결체를 산처리함으로써 철금속, 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물 및 붕소 및 붕화물의 적어도 한쪽의 일부를 용출하는 단계를 구비하는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  22. 제21항에 있어서, 상기 주기율표 제IVa,Va,VIa족의 탄화물은 탄화텅스텐 또는 탄화텅스텐과 동일 결정구조를 가지는 탄화몰리브덴 텅스텐인 것이 특징인 공구용 다이어몬드 소결체의 제조방법.
  23. 제11항에 있어서, 청구범위 제9항의 공구용 다이어몬드 소결체의 제조방법으로서, 다이어몬드 분말과 붕소 혹은 붕화물과의 혼합분말 또는 다이어몬드 분말과 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물 철금속 또는 붕화물과의 혼합 분말을 만드는 단계화 1300℃이상의 온도에서 혼합분말중의 다이어몬드의 일부를 흑연화하는 단계와,초경합금 기재와 접촉시켜 상기 다이어몬드상에 철 금속 또는 주기율표 제IVa,Va,VIa족의 소결탄화물을 접촉시켜 초고압 고온장치를 사용하여 다이어몬드가 안정한 고온고압하에서 고온프레스하여 소결체를 만들고, 상기 소결체를 산화성 액체로 처리함으로써 다이어몬드 소결체중의 철 금속 및 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물의 일부를 용출하는 단계를 구비하는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  24. 제23항에 있어서, 상기 다이어몬드와 초경 합금기재는 중간 접합층을 통하여 접합되는 것이 특징인 공구용 다이어몬드 소결체의 제조방법.
  25. 제23항에 있어서, 상기 산화성 액체에 의한 처리시 초경합금기재 표면에 산화 피막층를 형성하는 단계를 추가로 포함하는 것이 특징인 공구용 다이어몬드 소결체의 제조방법.
  26. 제11항에 있어서, 청구범위 제7항의 공구용 다이어몬드 소결체의 제조방법으로서, 다이어몬드 분말과 철금속 및 붕소와 붕화물의 적어도 한쪽과의 혼합분말과 또는 다이어몬드 분말과, 주기율표 제IVa,Va,VIa족의 금속 혹은 탄화물, 철금속 및 붕소와 붕화물의 적어도 한쪽과의 혼합 분말을 만드는 단계와 1300℃이상의 온도에서 상기 혼합분말중의 다이어몬드의 일부를 흑연화하는 단계와, 초고압, 고온장치를 사용하여 다이어몬드가 안정한 고온 고압하에서 고온 프레스하여 소결체를 만드는 단계와, 얻어진 소결체를 산처리 함으로써 철금속, 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물 및 붕소 또는 붕화물의 적어도 한쪽의 일부를 용출하는 단계를 구비하는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  27. 제26항에 있어서, 상기 주기율표 제IVa,Va,VIa족의 탄화물을 탄화텅스텐 또는 탄화텅스텐과 동일결정 구조를 가지는 탄화 몰리브덴 텅스텐인 것이 특징인 공구용 다이어몬드 소결체의 제조방법.
  28. 제11항에 있어서, 청구범위 제9항의 공구용 다이어몬드 소결체의 제조방법으로서, 다이어몬드 분말과 철금속 및 붕소와 붕화물의 적어도 한쪽과의 혼합분말 또는 다이어몬드 분말과 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물, 철금속 및 붕소와 붕화물의 적어도 한쪽과의 혼합 분말을 만드는 단계와 1300℃이상의 온도에서 혼합분말중의 다이어몬드의 일부를 흑연화하는 단계와, 혼합분말을 초경 합급기재와 접촉시켜 초고압, 고온장치를 사용하여 다이어몬드가 안정한 고온 고압하에서 고온 프레스하여 소결체를 만드는 단계와, 얻어진 소결체를 산화성액체로 처리함으로써 다이어몬드 소결체중의 철금속 및 주기율표 제IVa,Va,VIa족의 금속 또는 탄화물의 일부를 용출하는 단계를 구비하는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  29. 제28항에 있어서, 상기 다이아몬드와 초경합금 기재는 중간접합층을 통하여 접촉되는 것이 특징인 공구용 다이어몬드 소결체의 제조방법.
  30. 제28항에 있어서, 상기 산화성 액체에의 한 처리시 초경합금 기재의 표면에 산화피막층을 형성하고 그에 따라 초경합금 기재중의 철금속의 용출을 방지하는 것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  31. 제11항에 있어서 청구범위 제3항의 공구용 다이어몬드 소결체의 제조방법으로서 3㎛이상의 다이어몬드 분말, 1㎛이하의 초미립 다이어몬드 분말, 1㎛이하의 주기율표 제IVa,Va,VIa족의 탄화물 및 철금속의 혼합 분말을 만들고, 1300℃ 이상의 온도에서 원료분말의 일부를 흑연화한 후, 초고압 고온 장치를 사용하여 다이어몬드가 안정한고온 고압하에서 고온 프레스하여 소결체를 만들고 상기 소결체를 산처리 함으로써 철금속의 일부를 용출하는것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
  32. 제11항에 있어서 청구범위 제6항의 공구용 다이어몬드 소결체의 제조방법으로서, 3㎛이상의 다이어몬드 분말, 1㎛이하의 초미립 다이어몬드 분말, 1㎛이하의 주기율표 제IVa,Va,VIa족의 탄화물, 철금속 및 붕소와 붕화물의 혼합 분말을 만들고, 1300℃ 이상의 온도에서 원료분말의 일부를 흑연화한 후 초고압 고온 장치를 사용하여 다이어몬드가 안정한고온 고압하에서 고온 프레스하여 소결체를 만들고, 상기 소결체를 산처리 함으로써 철금속의 일부를 용출하는것을 특징으로 하는 공구용 다이어몬드 소결체의 제조방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019850006553A 1984-09-08 1985-09-07 공구용 다이어몬드 소결체 및 그 제조 방법 KR900002701B1 (ko)