KR840004182A - 가단주철과 컴팩트된 흑연 주철의 제조방법 - Google Patents
가단주철과 컴팩트된 흑연 주철의 제조방법 Download PDFInfo
- Publication number
- KR840004182A KR840004182A KR1019830001268A KR830001268A KR840004182A KR 840004182 A KR840004182 A KR 840004182A KR 1019830001268 A KR1019830001268 A KR 1019830001268A KR 830001268 A KR830001268 A KR 830001268A KR 840004182 A KR840004182 A KR 840004182A
- Authority
- KR
- South Korea
- Prior art keywords
- iron
- alloy
- molten iron
- magnesium
- vessel
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (35)
- 용기에 탄소를 포함한 용해된 철을 간직하면서 거기에 필수원소로써 무게비로 약 1.0%내지 6.0%의 실리콘과 약 0.5%내지 2.0%의 마그네슘을 포함한 철을 합금을 넣어 마그네슘과 철 사이의 반응이 일어날 때까지 상기의 용기를 유지한 후에 상기의 용해된 철에 상기의 합금을 더 첨가함으로써 원하는 화학 구성비를 얻도록 하는 과정을 포함한 가단주철과 컴팩트된 흑연 주철을 제조하는 방법.
- 용해된 철의 밀도보다 더 큰 밀도를 가진 합금으로된 상기 1항의 방법.
- 약 6.5내지 7.5gms/㎤의 밀도를 가진 합금으로된 상기 1항의 방법.
- 무게비로 약 2.0%를 넘지않는 세륨을 포함한 주로 철로된 합금으로된 상기 1항의 방법.
- 무게비로 약 2.0%를 넘지않는 하나 또는 그 이상의 회토류 원소를 포함한 주로 철로된 합금으로된 상기 1항의 방법.
- 무게비로 약 0.1내지 10.0%의 실리콘과 약 0.05%내지 2.0%의 회토류 원소와 약 0.5%내지 4.0%의 마그네슘과 약 0.5%내지 6.5%의 탄소를 포함한 주로 철로된 합금으로 된 상기 1항의 방법.
- 무게비로 약 1.0%내지 6.0%의 실리콘과 약 2.0%까지의 세륨과 약 0.5%내지 2.0%의 마그네슘을 포함하고 나머지는 철로 이루어진 합금으로 된 상기 1항의 방법.
- 지지용기(holding vessel)는 용광로의 용기인 상기 1항의 방법.
- 용기안에 탄소를 포함한 용해된 철을 간직하면서 거기에 필수원소로써 무게비로 약 0.1%내지 10.0%의 실리콘과 약 0.5%내지 4.0%의 마그네슘을 포함한 주로 철로된 합금을 넣어 상기의 용해된 철을 처리하고 상기의 합금으로 부터의 마그네슘양이 처리 용해된 철의 마그네슘 양보다 많아질때까지 상기의 용기에서 용해된 철을 간직한 후에 상기의 용기에 연소가 포함된 처리가 되지 않은 용해된 철을 넣고 거기에 장기의 처리가 되지않고 더해진 철의 마그네슘 양을 증가시키기 위해 상기의 합금을 넣는 방법으로 이루어진 가단주철과 컴팩트된 흑연주철을 제조하는 방법.
- 용기에 탄소를 포함한 용해된 철을 간직하면서 거기에 필수원소로써 무게비로 약 0.1%내지 10.0%의 실리콘과 약 0.5%내지 4.0%의 마그네슘을 포함한 주로 철로된 합금을 용해된 철에 더하고 용해된 철에서 마그네슘 함유량을 어느 선택된 선까지 증가시키기 위해 상기의 합금의 마그네슘과 용해된 철을 반응시키고 상기의 용기에서 처리 용해된 철에서 마그네슘 함유량이 어느 선택된 선 아래로 떨어질 때까지 용기를 유지시키고 그 때 상기의 용해된 철에 상기의 합금을 더하여 적어도 선택된 선까지 마그네슘 함유량을 증가시키는 개선된 방법을 포함하는 가단주철과 컴팩트된 흑연주철을 제조하는 방법.
- 용기에 탄소와 황을 포함한 용해된 철을 간직하면서 거기에 필수원소로써 무게비로 약 0.1%내지 10.0%의 실리콘과 약 0.5%내지 2.0%의 마그네슘을 포함한 주로 철로된 합금을 용해된 철에 더하고 상기의 용기에서 처리된 철에서 황의 함유량이 감소할때까지 처리 용해된 철을 유지한 후에 마그네슘 함유량을 증가시키기 위해 용해된 철에 상기의 합금을 더하는 개선된 방법을 포함하는 가단주철과 컴팩트된 흑연 주철을 제조하는 방법.
- 용기에 탄소를 포함한 용해된 철을 간직하면서 용해된 철을 뒤섞어 용기의 중앙에서 아래쪽으로 순환시키고 그 용기의 중앙의 표면에 필수원소로써 무게비로 약 0.1%내지 10.0%의 실리콘과 약 0.5%내지 4.0%의 마그네슘을 포함한 주로 철로된 합금을 더함으로써 용해된 철의 아래 방향으로 순환함에 따라 합금이 용기의 표면 아래로 움직이게 하는 개선된 방법을 포함하는 가단주철과 컴팩트된 흑연주철을 제조하는 방법.
- 용해된 철을 뒤섞는 것을 전기 유도를 일으키는 코일로 하는 상기 12항의 방법.
- 용해된 철이 용기의 중앙에서는 위쪽으로 양쪽편에서는 아래쪽으로 순환할때 합금이 용기의 표면아래로 이동하기 위해서는 아래쪽으로 움직이는 용해된 철 위에 더해지는 상기 12항의 방법.
- 무게비로 약 2.0%까지의 세륨을 포함하는 합금으로 된 상기 12항의 방법.
- 탄소를 포함한 용해된 철을 주형에 부울대 그 용해된 철이 주형에 들어갈때 거기에 필수원소로써 무게비로 약 0.1%내지 10.0%의 실리콘과 약 0.5%내지 2.0%의 마그네슘을 포함한 주로 철로된 합금을 더함으로써 용해된 철의 흐름에 의해서 합금이 주형으로 들어가게 함으로써 가단주철과 컴팩트된 흑연주철을 제조하는 방법.
- 지지용기(hoding vessel)에 탄소를 포함한 용해된 철을 부으면서 무게비로 약 0.1%내지 10.0%의 실리콘과 약 0.1%내지 2.0%의 마그네슘을 포함한 주로 철로 된 합금을 부어지는 철에 더함으로써 그 용해된 철이 흐르는 것에 의해서 합금이 지지용기로 들어가서 용기의 표면 아래로 움직이게 함으로써 가단주철 및 컴팩트된 흑연주철을 제조하는 방법.
- 적어도 하나의 지지용기에 탄소를 포함한 용해된 철을 공급하고, 필수원소로써 무게비로 약 0.1%내지 10.0%의 실리콘과 약 0.5%내지 2.0%의 마그네슘을 포함하는 주로 철로된 합금을 용기안의 용해된 철에 더함으로써 상기의 용해된 철을 처리하고 다수의 주형을 계속적으로 한번에 하나씩 상기의 용기 아래의 위치로 가져가 상기의 용기로 부터 처리 용해된 철을 채우고 상기의 지지용기에 탄소를 포함한 처리되지 않은 용해된 철과 상기된 합금을 넣은 방법으로 된 가단주철 및 컴팩트 된 흑연주철의 주물을 제조하는 방법.
- 다수의 주형을 정상(定常)상태로 유지하고 지지용기를 주형에 처리된 철을 채우기위한 위치로 움직이는 상기 18항의 방법.
- 지지용기를 정상(定常)상태로 유지하고 지지용기로 부터 처리된 철을 받기 위한 위치로 다수의 주형을 움직이는 상기 18항의 방법.
- 용해된 철을 용기 중앙에서 아래쪽으로 순환시키고 합금을 용기의 중앙의 표면에 더해서 아래쪽으로 순환하는 철에 의해서 합금이 표면 아래로 움직이게 하는 상기 18항의 방법.
- 필수 원소로써 무게비로 약 0.1%내지 10.0%의 실리콘과 약 0.5%내지 4.0%의 마그네슘을 포함한 주로 철로 되어 있고 밀도가 약 6.5내지 7.5gms/㎤인 합금을 사용하는 상기 18항의 방법.
- 무게비로 약 2.0%까지의 세륨을 포함한 합금을 사용하는 상기 18항의 방법.
- 용해된 철을 합금으로 처리하고 그 처리 용해된 철을 주형에 공급하기 위해 다수의 지지용기(holding vessel)를 사용하는 상기 18항의 방법.
- 다수의 지지용기를 첫 원의 행로로 움직이고 또 다수의 주형을 그것이 상기의 지지용기의 아래 위치로 오도록 두번째 원의 행로에 따라 움직여서, 지지용기에서 주형에 처리 용해된 철을 준 후에 필수원소로써 무게비로 약 0.1내지 6.0%의 실리콘과 약 0.5%내지 2.0%의 마그네슘을 포함한 주로 철로된 합금으로 처리된 탄소를 포함한 철을 상기한 다수의 지지용기에 공급해야 하는데 이것을 주조작업을 위해서 적어도 하나의 지지용기로부터 처리 용해된 철을 받기 위해서 지지용기와 주형을 정상(定常)상태로 유지할때 상기의 지지용기에 처리 용해된 철을 공급함으로써 이루어지는 개선점을 지닌 가단 주철이나 컴팩트된 흑연 주철의 주물을 제조하는 방법.
- 필수원소로써 무게비로 약 0.1내지 10.0%의 실리콘과 약 0.5%내지 4.0%의 마그네슘을 포함한 철합금을 사용하는 상기 25항의 방법.
- 무게비로 약 2.0%까지의 세륨을 포함한 합금을 사용하는 상기 26항의 방법.
- 다수의 용기에 주형에 공급하기 위한 처리 용해된 철을 재공급하기 위해서는 다수의 용기에 처리되지 않은 용해된 철과 상기의 합금을 그 철에 더하는 방법도 사용할 수 있는 상기 25항의 방법.
- 하나 또는 여럿의 분리된 공급 용기에서 용해된 철이 합금으로 처리되어 거기서 주형에 공급하기 위한 처리 용해된 철을 다수의 지지용기에 재공급하는 상기 25항의 방법.
- 주형에 공급하는 처리 용해된 철의 화학적 구성을 원하는 대로 얻기 위해서 상기의 지지용기에 있는 처리 용해된 철에 합금을 더하는 상기 25항의 방법.
- 처리되지 않은 용해된 철을 하나 또는 여럿의 분리된 공급 용기에서 상기의 합금으로 부분적으로 처리하여 그 부분적으로 처리 용해된 철을 상기의 다수의 지지용기에 공급한 후 거기서 부분적으로 처리 용해된 철에 합금을 부가하여 용해된 철을 완전히 처리하여 주형에 공급될 용해 처리된 철을 재공급하는 상기 25항의 방법.
- 필수원소로써 무게비로 약 3.0%내지 6%의 실리콘과 약 0.5%내지 2.0%의 마그네슘과 약 2.0%까지의 세륨과 약 3.0%내지 6.5%의 탄소를 포함하는 주로 철로된 합금을 사용하는 상기 25항의 방법.
- 약 6.5내지 7.5gms/㎤의 밀도를 가진 합금을 사용하는 상기 25항의 방법.
- 원이 아닌 선택된 교차하는 행로를 따라서 다수의 지지용기와 다수의 주형을 움직여 서로 행로가 교차되었을 때 용기로부터 주형으로 처리 용해된 철을 옮기는 법도 사용할 수 있는 상기 25항의 방법.
- 선택된 행로가 장방형일 경우 지지용기와 주형의 행로가 서로 교차하면서 장방형 행로의 첫 직선부분을 따라서 지지용기와 주형이 움직일 때 처리 용해된 철이 주형으로 옮겨진다. 그리고 상기한 지지용기의 장방형 행로의 두번째 직선부분과 일치하는 행로를 따라 움직이는 분리된 공급용기가 주형에 공급하기 위한 처리 용해된 철을 지지용기에 다시 채우는 상기 34항의 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.