KR20230079435A - 고강도 유리 - Google Patents
고강도 유리 Download PDFInfo
- Publication number
- KR20230079435A KR20230079435A KR1020237015137A KR20237015137A KR20230079435A KR 20230079435 A KR20230079435 A KR 20230079435A KR 1020237015137 A KR1020237015137 A KR 1020237015137A KR 20237015137 A KR20237015137 A KR 20237015137A KR 20230079435 A KR20230079435 A KR 20230079435A
- Authority
- KR
- South Korea
- Prior art keywords
- glass
- layer
- glass plate
- light
- strength
- Prior art date
Abstract
본 발명은 투명한 해양창이나 건물이나 차량용 유리창으로 사용할 수 있는 고강도 유리(1;1.1;7;9)과 그 제조방법에 관한 것이다. 본 발명의 유리판은 층상구조의 적어도 하나의 외측 고강도 유리판(3)과 내측 고강도 유리판(4), 및 이들 유리판들(3,4) 사이에 배치되는 차단층을 포함한다. 층상 차단재, 예컨대 층상 차광수단은 적어도 하나의 어닐링된 유리판(2.19;7.22;9.27)을 가질 수 있다.
Description
본 발명은 고강도 유리 및 특히 투명한 해상 창뿐만 아니라 건축용 유리판 또는 지상 또는 항공 운송용 차량 창으로도 사용될 수 있는 유리판과 그 제조 방법에 관한 것이다.
예를 들어 파도나 바람의 돌풍이나 창에 충돌하는 스콜로 인해 해양 창에 높은 부하가 생기고 이런 높은 부하는 창이나 유리의 손상이나 파괴도 초래하여, 선박 내부의 승객과 승무원에게 위험이 생길 수 있다. 건물이나 지상 및 항공기에 사용되는 고강도 유리도 비슷하다.
따라서, 본 발명의 목적은 높은 기계적 부하에도 손상 가능성이 낮은 고강도 유리를 제공하는데 있다.
이 목적은 청구항 1에 기재된 본 발명의 고강도 유리나 창에 의해 해결된다. 따라서, 특히 해양 창용 고강도 유리는 외측 고강도 유리판과 내측 고강도 유리판, 및 이들 외측, 내측 고강도 유리판들 사이에 배치된 층상 차단제를 포함한다.
본 발명의 유리는 기능성 차단재가 고강도 유리판들 사이에 배치되기 때문에 차단재 자체가 강한 기계적 응력에서 보호된다는 장점이 있다. 따라서, 본 발명은 예를 들어 기능성 차단재의 균열과 같은 손상 없이 긴 내구성이 보장되어, 유리의 전체 판구조들의 내구성이 길어진다.
본 발명의 "고강도 유리판"은 파괴강도 160~400MPa 정도의 강화유리이다. 이는 고강도 유리판의 기계적 허용응력이 짧은 부하지속기간 40 - 100MPa 정도임을 의미한다. 강화 유리는 플로트 유리 또는 어닐링된 유리에 비해 강도를 증가시키기 위해 제어된 열이나 화학적 처리된 강화유리나 안전유리에 해당한다.
층상 기능성 차단재는 태양광 차단 외에, 유리의 투과율 변환, 전기회로층, 안테나층 등 레이어 등의 다른 기능도 제공하되, 이에 한정되는 것도 아니다.
층상 기능성 차단재는 바람직하게는 라미네이트의 외측, 내측 고강도 유리판 사이에 배치되고 층상 차광수단을 포함하는데, 층상 차광수단은 IR(적외선 및/또는 UV(자외선)을 억제한다. 층상 차광수단 자체는 고강도 유리판들 사이에 있는 위치로 인해 강하고 허용되지 않는 기계적 응력에 대해 보호된다. 따라서, 본 발명은 구조의 균열과 같은 손상 없이 내구성이 긴 차광효과를 내어, 결과적으로 고강도 유리의 전체 층상구조의 내구성이 길어진다.
바람직하게는, 이 유리는 기능성 차단재나 차광층에 허용되지 않는 너무 높은 기계적 응력을 피하기 위해 층상 기능성 차단재나 차광수단 내부, 인접 또는 근접해 뻗는 중립층을 포함한다. "중립층"은 유리가 외부로부터 기계적 부하를 받는 경우 거의 0이나 기계적 허용응력을 보이는 유리의 단면구역의 선이나 중립층이다. 유리의 중립층은 언로드된 유리의 단면 영역의 중심이나 주요부를 통해 확장한다.
기능성 차단재나 층상 차광수단은 외측 고강도 유리판에 작용하는 외부 굽힘 부하로 인한 기계적 응력이 파손시키는 것을 피하도록 기능성 차단재의 허용 굽힘 인장 응력보다 높지 않도록 본 발명의 유리판에 위치할 수 있다.
층상 기능성 차단재는 적어도 하나의 어닐링된 유리판을 포함할 수 있다. 바람직하게는, 어닐링된 유리판은 외측 고강도 유리판에 작용하는 외부 굽힘 부하로 인한 기계적 응력이 어닐링된 유리판의 허용 굽힘 인장 응력보다 높지 않도록 유리판에 위치한다. 어닐링된 유리판은 유리판의 중립층을 따라 또는 평행하게 뻗을 수 있다.
층상 차광수단은 바람직하게는 적어도 하나의 어닐링된 유리판과, 이 어닐링된 유리판에 제공되는 차광층을 포함하며, 여기서 어닐링된 유리판은 외측 고강도 유리판에 작용하는 외부 굽힘 부하로 인한 기계적 응력이 어닐링된 유리판의 허용 굽힘 인장 응력보다 높지 않도록 유리에 위치하고, 어닐링된 유리판은 유리판의 중립선이나 중립 영역에서, 이를 따라서나 나란히 연장한다.
유리의 중립선이나 중립층에 가까운 유리 단면 영역의 중앙 부분은 일반적으로 약간의 압축을 받거나 기껏해야 약간의 장력을 받는다.
본 발명에 따르면, 어닐링된 유리판의 응력이 작거나 최소인 최상의 위치는 유리의 외측 고강도 유리판에 보이는 측면의 중립선이나 중립층에 근접한 곳이다. 본 발명은 이런 기능적 차단재나 차광 요소를 구조적으로 유리에 통합하여, 유리판의 중립층에 접하거나 근방에 위치시킨다.
비강화 유리나 플로트 유리라고도 하는 어닐링된 유리는 일반적으로 40 - 70MPa 범위의 파손 강도를 보인다. 이는 어닐링된 유리판의 기계적 허용응력이 짧은 부하지속 시간 동안 10~18MPa 범위임을 의미한다.
바람직하게는, 층상 차광수단은 어닐링된 유리판에 과도한 인장 응력을 줄이기 위해 탄성계수가 높은 중간층을 하나 이상 포함한다.
본 발명의 층상 차광수단은 바람직하게는 어닐링된 유리판 및 UV(자외선) 및/또는 IR(적외선)을 억제하기 위한 차광층을 포함하며, 차광층은 외측 고강도 유리판와 어닐링 유리창 사이에 위치한다. 차광층은 은, 금, 구리, 알루미늄 및 이들의 조합으로 이루어진 그룹으로부터 선택될 수 있는 얇은 금속층을 포함할 수 있다. 바람직하게는, 얇은 금속층은 실버 층 또는 다중 실버 층으로 이루어진다. 본 발명의 층상 차광수단은 단일 또는 다중 실버 층을 포함하는 스퍼터링 공정으로 제조된 차광층을 포함할 수 있으며, 이때 삼중 실버 층은 IR이나 NIR 및/또는 UV를 거의 완전히 반사하고 가시광은 거의 완전히 투과시킨다.
공업적 스퍼터링 공정을 이용해, 차광층으로서의 실버 층이 어닐링된 유리판에 스퍼터링이나 증착되어, 예를 들어 380nm - 780nm 파장대의 가시광은 거의 완전히 투과시키고 UV 300nm - 380nm 및 NIR 780nm - 2500nm 부분은 거의 완전히 반사시키는 이상적인 특성에 접근하는 이중, 삼중 및 사중 실버 층을 생성한다. 특히, 삼중실버 층은 UV 및/또는 IR이나 NIR을 거의 완벽히 반사시키고 가시광은 거의 완벽히 투과시킨다.
본 발명의 고강도 유리판은 이온교환에 의해 화학적으로 강화된 유리로 제조될 수 있거나 열적으로 강화된 유리로 제조될 수 있다. 또는, 고강도 유리판이 이온교환에 의해 화학적으로 강화될 수 있고 열적으로 강화되거나, 고강도 유리판 중 하나는 이온교환에 의해 화학적으로 강화되고 다른 하나는 열적으로 강화될 수 있다. 따라서, 다양한 여러가지 기계적 부하 케이스나 적용례도 본 발명에 포함될 수 있다.
층상 차광수단은 어닐링된 유리판과 이 유리판에 물리화학적 증착 코팅으로 이루어진 차광층을 포함할 수 있다.
층상 차광수단은 투명 전도층, 반사층, 반사방지층 또는 흡수층을 생산하기 위해 스퍼터링 공정이나 화학적 공정으로 제조될 수 있다. 층상 차광수단은 투명 전도층, 반사층, 반사 방지층 또는 흡수층을 생성하기 위한 화학적 공정에 의해 제조될 수 있다. 층상 기능성 차단재나 층상 차광수단은 스퍼터링되거나 증착된 상단 보호간섭층, 스퍼터링되거나 증착된 차단층, 스퍼터링되거나 증착된 실버 층, 스퍼터링되거나 증착된 시드층, 스퍼터링되거나 증착된 간섭 기저층 및 이런 박막 시스템을 위한 기판인 어닐링된 유리판을 포함할 수 있다.
본 발명의 내측, 외측 고강도 유리판은 차광층 수단에서 인장응력을 줄이거나 없애기 위해 유리가 굴곡부하를 받았을 때 유리의 인장부나 그 단면부에 제공될 수 있다.
바람직하게는, 내측, 외측 고강도 유리판은 응력이 허용치보다 낮은 부분이나 단면부에 배치된다.
본 발명은 또한 하기 단계를 포함하는 청구항 15에 따른 고강도 유리를 제조하는 방법에 관한 것이다:
적어도 외측 고강도 유리판과 내측 고강도 유리판, 및 층상 기능성 차단재나 층상 차광수단을 제공하는 단계;
층상 기능성 차단재나 층상 차광수단을 외측, 내측 고강도 유리판들 사이에 배치하여 가소결 스택을 얻는 단계; 및
고강도 유리를 얻기 위해 가소결 스택을 가마에서 층상 구조로 처리하는 단계.
도 1실버 층상 차광수단을 포함하는 본 발명의 바람직한 제1 실시예에 따른 고강도 유리의 개략 단면도이다.
도 2는 층상의 단일 실버 차광수단을 포함하는 본 발명의 제2 실시예에 따른 고강도 유리의 개략 단면도이다.
도 3은 층상 이중 실버 차광수단을 포함하는 본 발명의 제3 실시예에 따른 고강도 유리의 개략 단면도이다.
도 4는 층상 3중 실버 차광수단을 포함하는 본 발명의 제4 실시예에 따른 고강도 유리의 개략 단면도이다.
도 2는 층상의 단일 실버 차광수단을 포함하는 본 발명의 제2 실시예에 따른 고강도 유리의 개략 단면도이다.
도 3은 층상 이중 실버 차광수단을 포함하는 본 발명의 제3 실시예에 따른 고강도 유리의 개략 단면도이다.
도 4는 층상 3중 실버 차광수단을 포함하는 본 발명의 제4 실시예에 따른 고강도 유리의 개략 단면도이다.
도 1은 본 발명의 바람직한 제1 실시예에 따른 고강도 유리(1)의 단면도이다. 고강도 유리(1)는 기능적 차단제로서 층상 차광수단(2)을 갖는다. 고강도 유리(1)는 가시광을 투과시킨다. 고강도 유리의 치수는 대략 3000mm x 2000mm이지만, 이에 한정되지 않는다.
차량내 선창으로 사용될 수 있는 고강도 유리(1)나 창은 차량이나 선박의 외부를 향한 바깥 고강도 유리판(3), 차량이나 선박이나 건물의 내부를 향한 안쪽 고강도 유리판(4), 및 안팍의 고강도 유리판들(3,4) 사이에 배치된 층상 차광수단(2)을 포함한다.
이런 고강도 유리판(3,4)은 파괴강도 약 240MPa의 강화유리인데, 이는 고강도 유리판(3,4) 각각의 허용 기계적 응력이 짧은 부하지속시간 동안 약 60MPa임을 의미한다. 고강도 유리판(3,4)은 강화유리나 안전유리로 이루어진다.
층상 차광수단(2)은 외부 접착층(2.1)과 내부 접착층(2.2)을 갖고 UV(자외선) 및/또는 IR(적외선)을 억제한다. 외부 접착층(2.1)은 외측 고강도 유리판(3)에 접하고 내부 접착층(2.2)은 내측 고강도 유리판(4)에 접한다. 내외부 접착층들(2.1,2.2)은 PVB(Poly Vinyl Butyral)로 제조될 수 있다. 층상 차광수단(2)은 바람직하게는 기능성 차광 박막 코팅된 어닐링된 비강화 유리판을 포함하지만, 이에 제한되지 않는다.
고강도 유리(1)는 외부에서 부하를 받는 경우 기계적 응력이 0인 중립층(5)을 갖는데, 중립층(5)실버 층상 차광수단(2)에 기계적 응력이 너무 높게 걸리지 않도록 차광수단(2)의 내부나 그 부근에서 뻗는다.
도 2는 본 발명의 고강도 유리(1.1)의 다른 단면도이다. 이 고강도 유리(1.1)는 기능성 차단제로서 층상 차광수단(2.11)을 갖는다.
고강도 유리(1.1)는 외측 고강도 유리판(3.1), 층상의 내측 고강도 유리판(4.1), 및 내외측 고강도 유리판들(3.1,4.1) 사이에 배치된 층상 차광수단(2.11)을 포함한다..
층상 차광수단(2.11)은 외부 접착층(2.12), 내부 접착층(2.13) 및 어닐링된 유리판(2.19)를 포함한다. 층상 차광수단(2.11)은 UV(자외선) 및/또는 IR(적외선)을 억제한다. 이 고강도 유리(1.1)도 차광수단(2.11) 안에서 뻗는 중립층(5.1)을 갖는다. 외부 접착층(2.12)은 외측 고강도 유리판(3.1)에 접하고 내부 접착층(2.13)은 내측 고강도 유리판(4.1)에 접한다.
내외 접착층들(2.12,2.13)은 PVB로 구성되는데, Eastmann의 DG41®이나 Kuraray-Trosifol의 Extra-Strong ES®와 같은 고강도 PVB가 바람직하다. 다른 재료로는 Kuraray-Trosifol의 Sentryglass® ionoplast interlayer와 같은 이오노머 수지가 있다. 유리판에 사용되는 다른 중간층으로 지방족 열가소성 폴리우레탄(TPU)이 있지만, 그 탄성 계수는 일반적으로 구조용 PVB나 Ionomeric interlayer보다 낮다. 외부 굽힘 부하 하에서 최적의 층상 단면은 이런 층들을 통해 응력이 균일하게 전달될 때 외부 굽힘부하에 최적의 층상 단면이 때 얻어지며, 이는 연결 접착층들(2.12,2.13)의 전단탄성율이 50MPa보다 클 때 달성된다. 접착층들(2.12,2.13)의 두께는 0.3mm 내지 3mm, 바람직하게는 1.52mm 정도이다.
도 2의 실시예에서는 두께 2mm 내지 6mm, 바람직하게는 4mm인 기판이나 캐리어로서 어닐링된 유리판(2.19)에 배치되거나 증착된 박막 시스템에 의해 차광한다
두께 10nm 내지 20nm, 바람직하게는 15nm의 차광층으로서 실버 층(2.16)으로 태양복사파장 780nm 내지 2500nm의 근적외선 부분을 반사해 태양광 보호기능을 한다. 파장 380nm 내지 780nm의 태양복사선의 가시 부분의 투과를 위해, 실버 층(2.16)은 박막 시스템의 상단 보호간섭층(2.14)과 간섭 기저층(2.18) 사이에 배치된다.
또, 실버 층(2.16)의 최적의 핵 생성과, 부식과 열화를 일으킬 수 있는 화학 반응으로부터 보호하기 위해, 실버 층(2.16)은 예를 들어 두께 15nm 미만이고 ZnO로 이루어진 시드층(2.17)에 증착된다. 시드층(2.17)의 두께는 10nm가 바람직하다. 또, 실버 층(2.16)은 차단층(2.15)에 의해 보호되고, 차단층은 금속이나 금속아산화물, 바람직하게는 NiCr이나 NiCrOx이고 두께 2nm 내지 8nm이다.
외측, 내측 접착층들(2.12,2.13) 사이의 층상 차광수단(2)은 아래 순서로 층과 코팅을 갖는다:
- 상단 보호간섭층(2.14), 두께 2nm - 20nm, 바람직하게는 11nm의 Si3N4, 및/또는 두께 30nm - 70nm, 바람직하게는 50nm의 ZnO로 구성됨;
- 스퍼터링 차단층(2.15), 두께 2nm - 6nm, 바람직하게는 4nm의 NiCr이나 NiCrOx로 구성됨;
- 스퍼터링 실버 층(2.16), 두께 12nm - 15nm, 바람직하게는 13.5nm;
- 시드층(2.17), 두께 3nm - 10nm, 바람직하게는 6.5nm의 ZnO 또는 ZnO:SnO2:Al2O3로 구성됨;
- 간섭 기저층(2.18), 두께 30nm - 80nm, 바람직하게는 55nm의 ZTO나 SnC2로 구성됨; 및
- 내부 접착층(2.13)에 접한 어닐링된 유리판(2.19).
투명한 어닐링된 유리판(2.19)은 어닐링된 비강화나 플로트 유리이고 파괴강도는 70MPa 정도인데, 이는 유리판(2.19)의 기계적 허용응력이 짧은 부하지속 동안 17.5MPa임을 뜻한다. 어닐링된 유리판(2.19)는 고강도 유리(1.1)의 중립층(5.1)에 접해 있다.
외측, 내측 접착층(2.12,2.13)은 탄성계수가 높아 전단계수가 50MPa 정도여서, 어닐링 유리판(2.19)의 인장응력이 17.5MPa 이상으로 과도해질 가능성을 줄인다.
스퍼터링 실버 층(2.16)은 380nm - 780nm의 가시광을 거의 전부 투과시키고 UV 300nm - 380nm 및 IR 780nm ~ 2500nm을 거의 전부 반사하는 거의 이상적인 특성의 차광층이다.
고강도 유리판(1.1)은 외측 고강도 유리판(3.1)과 내측 고강도 유리판(4.1), 및 이들 유리판(3.1,4.1) 사이의 층상 차광수단(2.11)으로 구성되어, 가소결 스택을 형성할 수 있다.
층상 차광수단(2.11)의 박막 시스템은 아래와 같은 단계로 생산될 수 있다:
- 간섭 기저층(2.18)이 어닐링된 유리판(2.19)에 스퍼터링되거나 화학 증착법으로 증착;
- 이어서 시드층(2.17)이나 코팅이 간섭 기저층(2.18)에 스퍼터링되거나 화학적 증착법으로 증착;
- 이제 실버 층(2.16)이 시드층(2.17)에 스퍼터링되거나 증착;
- 이후 차단층이나 흡수층(2.15)인 코팅이 실버 층(2.16)에 스퍼터링되거나 증착;
- 이어서 상단 보호간섭층(2.14)이 차단층(2.15)에 증착되거나 스퍼터링된다.
이렇게 얻어진 박막 시스템은 고탄성율 중합체 외측, 내측 접착층들(2.12,2.13) 사이에 배치되어 층상 차광수단(2.11)을 형성하고, 이것은 외부와 내부 고강도 유리판들(3.1,4.1) 사이에 조립되어, 가소결 스택을 제공한다.
마지막으로, 가소결 스택을 가마에서 처리하여 층들 사이를 완전 접착하고 완전한 층상 고강도 유리판을 형성한다.
도 3은 본 발명의 바람직한 제3 실시예에 따른 고강도 유리(7)의 단면도이다. 이 고강도 유리(7)는 기능성 차단재로서 층상 차광수단(7.11)을 갖는다.
고강도 유리(7)는 층구조내 외측 고강도 유리판(7.1)과 내측 고강도 유리판(7.2), 및 층구조내 외측, 내측 고강도 유리판들(7.1,7.2) 사이에 배치된 층상 차광수단(7.11)을 포함한다..
층상 차광수단(7.11)은 외측 접착층(7.12)과 내측 접착층(7.13)을 갖고, UV(자외선) 및/또는 IR(적외선)을 억제한다. 고강도 유리(7) 역시 차광수단(7.11) 내에서 뻗는 중립층(8)을 포함한다. 외측 접착층(7.12)은 외측 고강도 유리판(7.1)에 접하고 내측 접착층(7.13)은 내측 고강도 유리판(7.1)에 접한다. 내외측 접착층들(7.12,7.13)은 PVB(Poly Vinyl Butyral), 바람직하게는 고탄성율 PVB나 이오노머 수지 SGP®로 이루어질 수 있다.
외측, 내측 접착층들(7.12,7.13) 사이에서, 층상 차광수단(7.11)은 박막 시스템으로서 아래 층들을 갖는다:
Si3N4 및/또는 ZnO로 구성되고 스퍼터링이나 증착된 상단 보호간섭층(7.14);
NiCr이나 NiCrOx로 구성된 스퍼터링이나 증착된 차단층(7.15) ;
스퍼터링된 제1 실버 층(7.16);
ZnO 또는 ZnO:SnO2:Al2O3로 구성된 시드층(7.17);
Si3N4 및/또는 ZnO로 구성된 간섭층(7,23);
NiCr이나 NiCrOx로 구성된 다른 스퍼터링 차단층(7.18) ;
스퍼터링된 제2 실버 층(7.19);
ZnO 또는 ZnO:SnO2:Al2O3로 구성된 다른 시드층(7.20);
ZTO나 SnO2로 구성된 간섭 기저층(7.21'); 및
내부 접착층(7.13)에 접한 어닐링된 유리판(7.22).
어닐링된 유리판(7.22)은 중립축(8)에 접해 뻗는다. 도 3의 실시예는 이중 실버층을 기초로 하는데, 이는 가시광 고투과율 대 근적외선과 UV의 고반사율의 필터 선택도를 향상시킨다.
도 4는 본 발명의 제4 실시예에 따른 고강도 유리(9)의 부분 단면도이다. 이 고강도 유리(9)은 기능성 차단제로서 층상 차광수단(9.11)을 갖는다.
고강도 유리(9)는 층상 구조의 외측 고강도 유리판(9.1)과 내측 고강도 유리판(9.2), 및 외측, 내측 고강도 유리판들(9.1,9.2) 사이에 배치된 층상 차광수단(9.11)을 포함한다..
층상 차광수단(9.11)은 외부 접착층(9.12)과 내부 접착층(9.13)을 갖고 UV(자외선) 및/또는 IR(적외선)을 억제한다. 고강도 유리(9)도 층상 차광수단(9.11) 내에서 뻗는 중립층(10)을 포함한다. 외부 접착층(9.12)은 외측 고강도 유리판(9.1)에 접하고 내부 접착층(9.13)은 내측 고강도 유리판(9.2)에 접한다. 내외부 접착층(9.12,9.13)은 고탄성 PVB(Poly Vinyl Butyral)나 SGP®로 만들 수 있다.
외측, 내측 접착층들(9.12,9.13) 사이에서, 층상 차광수단(9.11)은 아래 층들을 포함한다:
Si3N4 및/또는 ZnO로 구성되고 스퍼터링이나 증착된 상단 보호간섭층(9.14) ;
NiCr이나 NiCrOx로 구성된 스퍼터링이나 증착된 차단층(9.15) ;
스퍼터링이나 증착된 제1 실버 층(9.16);
ZnO 또는 ZnO:SnO2:Al2O3로 구성되고 스퍼터링이나 증착된 시드층(9.17);
Si3N4 및/또는 ZnO로 구성되고 스퍼터링이나 증착된 간섭층(9.23);
NiCr이나 NiCrOx로 구성되고 스퍼터링이나 증착된 다른 차단층(9.18);
스퍼터링이나 증착된 제2 실버 층(9.19);
ZnO 또는 ZnO:SnO2:Al2O3로 구성되고 스퍼터링이나 증착된 다른 시드층(9.20);
ZnO로 구성되고 스퍼터링이나 증착된 다른 간섭층(9.21) ;
NiCr이나 NiCrOx로 구성되고 스퍼터링이나 증착된 차단층(9.22) ;
스퍼터링이나 증착된 제3 실버 층(9.24);
ZnO 또는 ZnO: SnO2:Al2O3로 구성되고 스퍼터링이나 증착된 시드층(9.25) ;
ZTO나 SnO2로 구성되고 스퍼터링이나 증착된 간섭층(9.26); 및
내부 접착층(9.13)에 접하고 어닐링된 유리판(9.27). 어닐링된 유리판(9.27)은 중립층(10)에 접해 뻗는다.
Claims (15)
- 해양창용 고강도 유리(1;1.1;7;9)에 있어서:
층상구조의 적어도 하나의 외측 고강도 유리판(3)과 내측 고강도 유리판(4), 및 이들 유리판들(3,4) 사이에 배치되는 차단층을 포함하는 것을 특징으로 하는 유리. - 제1항에 있어서, 상기 차단층이 상기 유리판들(3,4) 사이에 배치되는 층상 차광수단(2;2.11;7.11;9.11)을 포함하고, 상기 층상 차광수단(2;2.11;7.11;9.11)이 NIR/IR(근적외선/적외선) 및/또는 UV(자외선)을 억제하는 것을 특징으로 하는 유리.
- 제1항 또는 제2항에 있어서, 상기 차단층이나 차광수단(2;2.11;7.11;9.11)에 접해서 또는 그 내부에서 뻗는 중립층(5;5.1;8;10)을 더 포함하는 것을 특징으로 하는 유리.
- 제2항 또는 제3항에 있어서, 상기 차단층이나 차광수단(2;2.11;7.11;9.11)이 유리(1;1.1;7;9) 안에 위치하여 외측 고강도 유리판(3)에 작용하는 외부 굽힘부하로 인한 기계적 응력이 차단층이나 차광수단(2;2.11;7.11;9.11)의 허용 굽힘 인장응력보다 높지 않은 것을 특징으로 하는 유리.
- 제1항 내지 제4항 중 어느 한 항에 있어서, 상기 차단층이나 차광수단(2;2.11;7.11;9.11)이 적어도 하나의 어닐링된 유리판(2.19;7.22;9.27)을 포함하고, 어닐링된 유리판(2.19;7.22;9.27)이 유리(1;1.1;7;9) 안에 위치하여 외측 고강도 유리판(3)에 작용하는 외부 굴곡부하로 인한 기계적 응력이 어닐링된 유리판(2.19;7.22;9.27)의 허용 굽힘 인장응력보다 높지 않은 것을 특징으로 하는 유리.
- 제5항에 있어서, 상기 어닐링된 유리판(2.19;7.22;9.27)이 유리(1;1.1;7;9)의 중립층(5;5.1;8;10)에서 중립층에 접하거나 나란하게 뻗는 것을 특징으로 하는 유리.
- 제5항에 있어서, 상기 차광수단(2;2.11;7.11;9.11)이 적어도 하나의 어닐링된 유리판(2.19;7.22;9.27)과, 이 어닐링된 유리판(2.19;7.22;9.27)에 제공된 차광층을 포함하고, 상기 어닐링된 유리판(2.19;7.22;9.27)이 유리(1;1.1;7;9) 안에 위치하여 외측 고강도 유리판에 작용하는 외부 굽힘부하로 인한 기계적 응력이 어닐링된 유리판(2.19;7.22;9.27)의 허용 굽힘 인장응력보다 높지 않으며, 상기 어닐링된 유리판(2.19;7.22;9.27)이 유리(1;1.1;7;9)의 중립층(5;5.1;8;10)에서 중립층에 접하거나 나란하게 뻗는 것을 특징으로 하는 유리.
- 제7항에 있어서, 상기 차광수단(2; 2.11;7.11;9.11)이 중간 접착층들(2.12, 2.13)을 갖고, 이들 접착층들의 전단계수 G가 50MPa보다 높은 것을 특징으로 하는 유리.
- 제2항 내지 제8항 중 어느 한 항에 있어서, 상기 차광수단(2;2.11;7.11;9.11)이 어닐링된 유리판(2.19;7.22;9.27)과 차광층이나 박막시스템을 갖고, 상기 차광층이나 박막시스템은 NIR/IR(근적외선/적외선) 및/또는 UV(자외선)을 억제하며 외측 고강도 유리판(3)과 어닐링된 유리판(2.19;7.22;9.27) 사이에 배치되는 것을 특징으로 하는 유리.
- 제1항 내지 제9항 중 어느 한 항에 있어서, 상기 고강도 유리판들(3,4)이 이온교환에 의해 화학적으로 또는 열적으로 강화되거나 열적으로 강화된 다음 이온교환에 의해 화학적으로 강화되거나, 상기 고강도 유리판들(3,4) 중의 하나는 이온교환에 의해 화학적으로 강화되고 나머지 하나는 열적으로 강화된 것을 특징으로 하는 유리.
- 제2항 내지 제10항 중 어느 한 항에 있어서, 상기 차광수단(2;2.11;7.11;9.11)이 어닐링된 유리판(2.19;7.22;9.27)과 차광층이나 박막 시스템을 갖고, 상기 차광층이나 박막 시스템은 어닐링된 유리판상의 코팅을 가지며, 이 코팅은 물리적이나 화학적으로 증착되거나, 또는 단일이나 다중의 금속 코팅이나 실버 층(2.16)으로 이루어진 것을 특징으로 하는 유리.
- 제1항 내지 제11항 중 어느 한 항에 있어서, 상기 차광층이나 차광수단(2;2.11;7.11;9.11)이 아래 순서로 아래 층들을 포함하는 것을 특징으로 하는 유리판:
스퍼터링이나 증착된 상단 보호 간섭층(2.14);
스퍼터링이나 증착된 차단층(2.15);
스퍼터링이나 증착된 실버 층(2.16);
스퍼터링이나 증착된 시드층(2.17),
스퍼터링이나 증착된 간섭 기저층(2.18); 및
어닐링된 유리판(2.19). - 제1항 내지 제12항 중 어느 한 항에 있어서, 유리판이 굴곡부하를 받았을 때 인장되는 부분이나 그 단면에 상기 내측, 외측 고강도 유리판들(3,4)이 제공되는 것을 특징으로 하는 유리..
- 제1항 내지 제13항 중 어느 한 항에 있어서, 상기 내측, 외측 고강도 유리판들(3,4)는 응력이 허용치 미만인 부분에 배치되는 것을 특징으로 하는 유리.
- 제1항 내지 제14항 중 어느 한 항에 따른 고강도 유리(1;1.1;7;9)의 제조 방법에 있어서:
적어도 하나의 외측 고강도 유리판(3)과 내측 고강도 유리판(4), 및 층상 차광수단을 제공하는 단계;
상기 외측, 내측 고강도 유리판들(3,4) 사이에 차광수단(2;2.11;7.11;9.11)을 배치하여 가소결 스택을 얻는 단계; 및
가소결 스택을 가마에서 층상 구조로 처리하여 고강도 유리(1;1.1;7;9)를 얻는 단계;를 포함하는 것을 특징으로 하는 방법.