KR20210067803A - 축광용 조성물 - Google Patents

축광용 조성물 Download PDF

Info

Publication number
KR20210067803A
KR20210067803A KR1020190157784A KR20190157784A KR20210067803A KR 20210067803 A KR20210067803 A KR 20210067803A KR 1020190157784 A KR1020190157784 A KR 1020190157784A KR 20190157784 A KR20190157784 A KR 20190157784A KR 20210067803 A KR20210067803 A KR 20210067803A
Authority
KR
South Korea
Prior art keywords
composition
formula
zns
weight
parts
Prior art date
Application number
KR1020190157784A
Other languages
English (en)
Inventor
김민철
구동욱
강칠세
김지영
Original Assignee
주식회사아이플러스원
구동욱
김민철
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사아이플러스원, 구동욱, 김민철 filed Critical 주식회사아이플러스원
Priority to KR1020190157784A priority Critical patent/KR20210067803A/ko
Publication of KR20210067803A publication Critical patent/KR20210067803A/ko

Abstract

본 발명은 바인더 수지, 축광안료 및 형광증백제를 포함함으로써 현저히 개선된 휘도를 갖는 축광용 조성물에 관한 것이다.

Description

축광용 조성물{COMPOSITION FOR LUMINISCENT}
본 발명은 축광용 조성물에 관한 것이다.
일반적으로, 축광이란 빛을 잠시 축적하였다가 축적된 빛 에너지가 어두운 암전상태에서 발광하는 것을 의미하는 것으로, 상기 축광은 형광(fluorescence), 인광(phosphorescence), 화학발광(chemiluminescence)으로 나뉜다.
축광과 형광은 모두 빛 (짧은 파장의 가시광선) 또는 여러 형태의 에너지 (전기장, 고속전자, 화학에너지 등)를 받아서 빛을 내는 발광 현상을 나타낸다는 점에서 공통점이 있으나, 발광하는 시점에서의 차이가 존재한다. 즉, 에너지를 받는 중에 발광하면 형광, 에너지를 받고도 어느 시간 지나서 발광하는 현상을 축광이라 한다.
한편, 축광 물질은 평상시에 빛을 축적하고 있다가 일몰 및 정전 등에 의해 어두워지면 빛을 내는 특징이 있는데, 축광 물질의 특성을 이용한 제품으로서는 축광 안료, 축광 시트, 혹은 축광 필름, 축광 테이프 등이 있으며, 이들 제품은 안전표지, 유도표지, 도로표지, 위치표지 등의 각종 표지판으로 사용되거나, 헬멧이나 작업복 등의 안전용품에 응용되거나, 지하철이나 지하실 (지하차고, 창고, 기관실) 혹은 빌딩 등 안전관리 대상지역에 적용되며, 기타 광고용품이나 인테리어용품, 팬시용품 등에 응용될 수 있다.
그러나, 기존의 축광 재료는 축광 시간과 축광 휘도가 낮아 실제 생활 전반에 적용하기가 쉽지 않은 단점도 있다.
한국등록특허 제1409743호
본 발명은 개선된 휘도를 갖는 축광용 조성물을 제공하는 것을 목적으로 한다.
1. 바인더 수지, 축광안료 및 형광증백제를 포함하는 축광용 조성물.
2. 위 1에 있어서, 상기 바인더 수지는 폴리에틸렌테레프탈레이트(polyethyleneterephtalate, PET), 폴리에스테르(polyester), 에틸렌 비닐 아세테이트(ethylene vinyl acetate, EVA), 폴리에틸렌(polyethylene), 사이클릭 올레핀 중합체(cyclic olefin polymer, COP), 사이클릭 올레핀 공중합체(cyclic olefin copolymer, COC), 폴리아크릴레이트(polyacrylate, PAC), 폴리카보네이트(polycarbonate, PC), 폴리에틸렌(polyethylene, PE), 폴리메틸메타크릴레이트(polymethylmethacrylate, PMMA), 폴리에테르에테르케톤(polyetheretherketon, PEEK), 폴리에틸렌나프탈레이트(polyethylenenaphthalate, PEN), 폴리에테르이미드(polyetherimide, PEI), 폴리이미드(polyimide, PI), 트리아세틸셀룰로오스(triacetylcellulose, TAC), 및 폴리비닐클로라이드(Polyvinyl chloride, PVC)로 이루어진 군에서 선택된 적어도 하나인, 조성물.
3. 위 1에 있어서, 상기 축광 안료는 유화아연(ZnS)계 또는 스트론튬알루마트(SrAlOEuDy)계 안료인, 조성물.
4. 위 1에 있어서, 상기 형광증백제는 벤조트리아졸계, 나프토트리아졸계 및 쿠마린계 형광증백제로 이루어진 군에서 선택된 적어도 하나인, 조성물.
5. 위 1에 있어서, 상기 형광증백제는 하기 화학식 1 내지 6 중 어느 하나로 표시되는 것인, 조성물:
[화학식 1]
Figure pat00001
[화학식 2]
Figure pat00002
[화학식 3]
Figure pat00003
[화학식 4]
Figure pat00004
[화학식 5]
Figure pat00005
[화학식 6]
Figure pat00006
.
6. 위 1에 있어서, 상기 형광증백제는 바인더 수지 고형분 100중량부에 대하여 1 내지 5 중량부 포함되는, 조성물.
7. 위 1에 있어서, 바인더 수지 100중량부에 대하여 축광 안료는 10 내지 25 중량부, 형광 증백제는 1 내지 5 중량부 포함되는, 조성물.
본 발명의 축광용 조성물은 현저히 개선된 휘도를 갖는다.
이하 본 발명을 상세히 설명한다.
본 발명의 축광용 조성물은 바인더 수지, 축광안료 및 형광증백제를 포함한다.
축광은 빛을 내부에 흡수해 저장하고 방출·발광하는 성질을 의미하는 것으로, 태양을 비롯해 수은등, 형광등, 백열등 같은 일상생활에서 사용되는 자연광 및 인조광의 에너지를 흡수ㆍ축적해서 어두운 곳에서 형광빛을 방출한다.
바인더 수지로는 당 분야에 공지된 것을 제한없이 사용할 수 있으며, 예를 들면 폴리에틸렌테레프탈레이트(polyethyleneterephtalate, PET), 폴리에스테르(polyester), 에틸렌 비닐 아세테이트(ethylene vinyl acetate, EVA), 폴리에틸렌(polyethylene), 사이클릭 올레핀 중합체(cyclic olefin polymer, COP), 사이클릭 올레핀 공중합체(cyclic olefin copolymer, COC), 폴리아크릴레이트(polyacrylate, PAC), 폴리카보네이트(polycarbonate, PC), 폴리에틸렌(polyethylene, PE), 폴리메틸메타크릴레이트(polymethylmethacrylate, PMMA), 폴리에테르에테르케톤(polyetheretherketon, PEEK), 폴리에틸렌나프탈레이트(polyethylenenaphthalate, PEN), 폴리에테르이미드(polyetherimide, PEI), 폴리이미드(polyimide, PI), 트리아세틸셀룰로오스(triacetylcellulose, TAC) 및 폴리비닐클로라이드(Polyvinyl chloride, PVC)로 이루어진 군에서 선택된 적어도 하나일 수 있다.
축광 안료(phosphorescent pigments)는 빛을 내부에 흡수해 저장하고 방출·발광하는 성질을 지닌 안료로서, 당 분야에 공지된 인광체, 형광체 등이 제한없이 사용될 수 있다.
예를 Ba2SiO4:Eu2+, BaSi2O5:Pb2+, BaxSr1-xF2:Eu2+, BaSrMgSi2O7:Eu2+, BaTiP2O7, (Ba,Ti)2P2O7:Ti, Ba3WO6:U, BaY2F8:Er3+,Yb+, Be2SiO4:Mn2+, Bi4Ge3O12, CaAl2O4:Ce3+, CaLa4O7:Ce3+, CaAl2O4:Eu2+, CaAl2O4:Mn2+, CaAl4O7:Pb2+, Mn2+, CaAl2O4:Tb3+, Ca3Al2Si3O12:Ce3+, Ca3Al2Si3Oi2:Ce3+, Ca3Al2Si3O2:Eu2+, Ca2B5O9Br:Eu2+, Ca2B5O9Cl:Eu2+, Ca2B5O9Cl:Pb2+, CaB2O4:Mn2+, Ca2B2O5:Mn2+, CaB2O4:Pb2+, CaB2P2O9:Eu2+, Ca5B2SiO10:Eu3+, Ca0.5Ba0.5Al12O19:Ce3+,Mn2+, Ca2Ba3(PO4)3Cl:Eu2+, SiO2　중 CaBr2:Eu2+, SiO2　중 CaCl2:Eu2+, SiO2　중 CaCl2:Eu2+,Mn2+, CaF2:Ce3+, CaF2:Ce3+,Mn2+, CaF2:Ce3+,Tb3+, CaF2:Eu2+, CaF2:Mn2+, CaF2:U, CaGa2O4:Mn2+, CaGa4O7:Mn2+, CaGa2S4:Ce3+, CaGa2S4:Eu2+, CaGa2S4:Mn2+, CaGa2S4:Pb2+, CaGeO3:Mn2+, SiO2　중 CaI2:Eu2+, SiO2　중 CaI2:Eu2+,Mn2+, CaLaBO4:Eu3+, CaLaB3O7:Ce3+,Mn2+, Ca2La2BO6.5:Pb2+, Ca2MgSi2O7, Ca2MgSi2O7:Ce3+, CaMgSi2O6:Eu2+, Ca3MgSi2O8:Eu2+, Ca2MgSi2O7:Eu2+, CaMgSi2O6:Eu2+,Mn2+, Ca2MgSi2O7:Eu2+,Mn2+, CaMoO4, CaMoO4:Eu3+, CaO:Bi3+, CaO:Cd2+, CaO:Cu+, CaO:Eu3+, CaO:Eu3+, Na+, CaO:Mn2+, CaO:Pb2+, CaO:Sb3+, CaO:Sm3+, CaO:Tb3+, CaO:Tl, CaO:Zn2+, Ca2P2O7:Ce3+, α-Ca3(PO4)2:Ce3+, β-Ca3(PO4)2:Ce3+, Ca5(PO4)3Cl:Eu2+, Ca5(PO4)3Cl:Mn2+, Ca5(PO4)3Cl:Sb3+, Ca5(PO4)3Cl:Sn2+, β-Ca3(PO4)2:Eu2+,Mn2+, Ca5(PO4)3F:Mn2+,　Cas(PO4)3F:Sb3+,　Cas(PO4)3F:Sn2+, α-Ca3(PO4)2:Eu2+, β-Ca3(PO4)2:Eu2+, Ca2P2O7:Eu2+, Ca2P2O7:Eu2+,Mn2+, CaP2O6:Mn2+, α-Ca3(PO4)2:Pb2+, α-Ca3(PO4)2:Sn2+, β-Ca3(PO4)2:Sn2+, β-Ca2P2O7:Sn,Mn, α-Ca3(PO4)2:Tr,　CaS:Bi3+,　CaS:Bi3+,Na,　CaS:Ce3+,　CaS:Eu2+,　CaS:Cu+,Na+,　CaS:La3+,　CaS:Mn2+,　CaSO4:Bi,　CaSO4:Ce3+,　CaSO4:Ce3+,Mn2+,　CaSO4:Eu2+,　CaSO4:Eu2+,Mn2+,　CaSO4:Pb2+,　CaS:Pb2+,　CaS:Pb2+,Cl,　CaS:Pb2+,Mn2+,　CaS:Pr3+,Pb2+,Cl,　CaS:Sb3+,　CaS:Sb3+,Na,　CaS:Sm3+,　CaS:Sn2+,　CaS:Sn2+,F,　CaS:Tb3+,　CaS:Tb3+,Cl,　CaS:Y3+,　CaS:Yb2+,　CaS:Yb2+,Cl,　CaSiO3:Ce3+, Ca3SiO4Cl2:Eu2+, Ca3SiO4Cl2:Pb2+,　CaSiO3:Eu2+,　CaSiO3:Mn2+,Pb,　CaSiO3:Pb2+,　CaSiO3:Pb2+,Mn2+,　CaSiO3:Ti4+,　CaSr2(PO4)2:Bi3+, β-(Ca,Sr)3(PO4)2:Sn2+Mn2+, CaTi0.9Al0.1O3:Bi3+, CaTiO3:Eu3+, CaTiO3:Pr3+, Ca5(VO4)3Cl, CaWO4, CaWO4:Pb2+, CaWO4:W, Ca3WO6:U, CaYAlO4:Eu3+, CaYBO4:Bi3+, CaYBO4:Eu3+, CaYB0.8O3.7:Eu3+, CaY2ZrO6:Eu3+, (Ca,Zn,Mg)3(PO4)2:Sn, CeF3, (Ce,Mg)BaAl11O18:Ce, (Ce,Mg)SrAl11O18:Ce, CeMgAl11O19:Ce:Tb, Cd2B6O11:Mn2+, CdS:Ag+,Cr, CdS:In, CdS:In, CdS:In,Te, CdS:Te, CdWO4, CsF, Csl, CsI:Na+, CsI:Tl, (ErCl3)0.25(BaCl2)0.75, GaN:Zn, Gd3Ga5O12:Cr3+, Gd3Ga5O12:Cr,Ce, GdNbO4:Bi3+, Gd2O2S:Eu3+, Gd2O2Pr3+, Gd2O2S:Pr,Ce,F, Gd2O2S:Tb3+, Gd2SiO5:Ce3+, KAI11O17:Tl+, KGa11O17:Mn2+, K2La2Ti3O10:Eu, KMgF3:Eu2+, KMgF3:Mn2+, K2SiF6:Mn4+, LaAl3B4O12:Eu3+, LaAlB2O6:Eu3+, LaAlO3:Eu3+, LaAlO3:Sm3+, LaAsO4:Eu3+, LaBr3:Ce3+, LaBO3:Eu3+, (La,Ce,Tb)PO4:Ce:Tb, LaCl3:Ce3+, La2O3:Bi3+, LaOBr:Tb3+, LaOBr:Tm3+, LaOCl:Bi3+, LaOCl:Eu3+, LaOF:Eu3+, La2O3:Eu3+, La2O3:Pr3+, La2O2S:Tb3+, LaPO4:Ce3+, LaPO4:Eu3+, LaSiO3Cl:Ce3+, LaSiO3Cl:Ce3+,Tb3+, LaVO4:Eu3+, La2W3O12:Eu3+, LiAlF4:Mn2+, LiAl5O8:Fe3+, LiAlO2:Fe3+, LiAlO2:Mn2+, LiAl5O8:Mn2+, Li2CaP2O7:Ce3+,Mn2+, LiCeBa4Si4O14:Mn2+, LiCeSrBa3Si4O14:Mn2+, LiInO2:Eu3+, LiInO2:Sm3+, LiLaO2:Eu3+, LuAlO3:Ce3+, (Lu,Gd)2SiO5:Ce3+, Lu2SiO5:Ce3+, Lu2Si2O7:Ce3+, LuTaO4:Nb5+, Lu1-xYxAlO3:Ce3+, MgAl2O4:Mn2+, MgSrAl10O17:Ce, MgB2O4:Mn2+, MgBa2(PO4)2:Sn2+, MgBa2(PO4)2:U, MgBaP2O7:Eu2+, MgBaP2O7:Eu2+,Mn2+, MgBa3Si2O8:Eu2+, MgBa(SO4)2:Eu2+, Mg3Ca3(PO4)4:Eu2+, MgCaP2O7:Mn2+, Mg2Ca(SO4)3:Eu2+, Mg2Ca(SO4)3:Eu2+,Mn2, MgCeAlnO19:Tb3+, Mg4(F)GeO6:Mn2+, Mg4(F)(Ge,Sn)O6:Mn2+, MgF2:Mn2+, MgGa2O4:Mn2+, Mg8Ge2O11F2:Mn4+, MgS:Eu2+, MgSiO3:Mn2+, Mg2SiO4:Mn2+, Mg3SiO3F4:Ti4+, MgSO4:Eu2+, MgSO4:Pb2+, MgSrBa2Si2O7:Eu2+, MgSrP2O7:Eu2+, MgSr5(PO4)4:Sn2+, MgSr3Si2O8:Eu2+,Mn2+, Mg2Sr(SO4)3:Eu2+, Mg2TiO4:Mn4+, MgWO4, MgYBO4:Eu3+, Na3Ce(PO4)2:Tb3+, NaI:Tl, Na1.23KO.42Eu0.12TiSi4O11:Eu3+, Na1.23K0.42Eu0.12TiSi5O13·xH2O:Eu3+, Na1.29K0.46Er0.08TiSi4O11:Eu3+, Na2Mg3Al2Si2O10:Tb, Na(Mg2-xMnx)LiSi4O10F2:Mn, NaYF4:Er3+, Yb3+, NaYO2:Eu3+, P46(70%) + P47 (30%),　SrAl12O19:Ce3+, Mn2+,　SrAl2O4:Eu2+,　SrAl4O7:Eu3+,　SrAl12O19:Eu2+,　SrAl2S4:Eu2+,　Sr2B5O9Cl:Eu2+,　SrB4O7:Eu2+(F,Cl,Br),　SrB4O7:Pb2+,　SrB4O7:Pb2+, Mn2+,　SrB8O13:Sm2+,　SrxBayClzAl2O4-z/2: Mn2+, Ce3+,　SrBaSiO4:Eu2+, SiO2중　Sr(Cl,Br,I)2:Eu2+, SiO2중　SrCl2:Eu2+,　Sr5Cl(PO4)3:Eu,　SrwFxB4O6.5:Eu2+,　SrwFxByOz:Eu2+,Sm2+,　SrF2:Eu2+,　SrGa12O19:Mn2+,　SrGa2S4:Ce3+,　SrGa2S4:Eu2+,　SrGa2S4:Pb2+,　SrIn2O4:Pr3+,　Al3+, (Sr,Mg)3(PO4)2:Sn,　SrMgSi2O6:Eu2+,　Sr2MgSi2O7:Eu2+,　Sr3MgSi2O8:Eu2+,　SrMoO4:U,　SrO·3B2O3:Eu2+,Cl, β-SrO·3B2O3:Pb2+, β-SrO·3B2O3　:Pb2+,Mn2+, α-SrO·3B2O3:Sm2+,　Sr6P5BO20:Eu,　Sr5(PO4)3Cl:Eu2+,　Sr5(PO4)3Cl:Eu2+,Pr3+,　Sr5(PO4)3Cl:Mn2+,　Sr5(PO4)3Cl:Sb3+,　Sr2P2O7:Eu2+, β-Sr3(PO4)2:Eu2+,　Sr5(PO4)3F:Mn2+,　Sr5(PO4)3F:Sb3+,　Sr5(PO4)3F:Sb3+,Mn2+,　Sr5(PO4)3F:Sn2+,　Sr2P2O7:Sn2+, β-Sr3(PO4)2:Sn2+, β-Sr3(PO4)2:Sn2+,Mn2+(Al),　SrS:Ce3+,　SrS:Eu2+,　SrS:Mn2+,　SrS:Cu+,Na,　SrSO4:Bi,　SrSO4:Ce3+,　SrSO4:Eu2+,　SrSO4:Eu2+,Mn2+,　Sr5Si4O10Cl6:Eu2+,　Sr2SiO4:Eu2+,　SrTiO3:Pr3+,　SrTiO3:Pr3+,Al3+,　Sr3WO6:U,　SrY2O3:Eu3+, ThO2:Eu3+, ThO2:Pr3+, ThO2:Tb3+, YAl3B4O12:Bi3+, YAl3B4O12:Ce3+, YAl3B4O12:Ce3+,Mn, YAl3B4O12:Ce3+,Tb3+, YAl3B4O12:Eu3+, YAl3B4O12:Eu3+,Cr3+, YAl3B4O12:Th4+,Ce3+,Mn2+, YAlO3:Ce3+, Y3Al5O12:Ce3+, Y3Al5O12:Cr3+, YAlO3:Eu3+, Y3Al5O12:Eu3r, Y4Al2O9:Eu3+, Y3Al5O12:Mn4+, YAlO3:Sm3+, YAlO3:Tb3+, Y3Al5O12:Tb3+, YAsO4:Eu3+, YBO3:Ce3+, YBO3:Eu3+, YF3:Er3+,Yb3+, YF3:Mn2+, YF3:Mn2+,Th4+, YF3:Tm3+,Yb3+, (Y,Gd)BO3:Eu, (Y,Gd)BO3:Tb, (Y,Gd)2O3:Eu3+, Y1.34Gd0.60O3(Eu,Pr), Y2O3:Bi3+, YOBr:Eu3+, Y2O3:Ce, Y2O3:Er3+, Y2O3:Eu3+(YOE), Y2O3:Ce3+,Tb3+, YOCl:Ce3+, YOCl:Eu3+, YOF:Eu3+, YOF:Tb3+, Y2O3:Ho3+, Y2O2S:Eu3+, Y2O2S:Pr3+, Y2O2S:Tb3+, Y2O3:Tb3+, YPO4:Ce3+, YPO4:Ce3+,Tb3+, YPO4:Eu3+, YPO4:Mn2+,Th4+, YPO4:V5+, Y(P,V)O4:Eu, Y2SiO5:Ce3+, YTaO4, YTaO4:Nb5+, YVO4:Dy3+, YVO4:Eu3+, ZnAl2O4:Mn2+, ZnB2O4:Mn2+, ZnBa2S3:Mn2+, (Zn,Be)2SiO4:Mn2+, Zn0.4Cd0.6S:Ag, Zn0.6Cd0.4S:Ag, (Zn,Cd)S:Ag,Cl, (Zn,Cd)S:Cu, ZnF2:Mn2+, ZnGa2O4, ZnGa2O4:Mn2+, ZnGa2S4:Mn2+, Zn2GeO4:Mn2+, (Zn,Mg)F2:Mn2+, ZnMg2(PO4)2:Mn2+, (Zn,Mg)3(PO4)2:Mn2+, ZnO:Al3+,Ga3+, ZnO:Bi3+, ZnO:Ga3+, ZnO:Ga, ZnO-CdO:Ga, ZnO:S, ZnO:Se, ZnO:Zn,　ZnS:Ag+,Cl-,　ZnS:Ag,Cu,Cl,　ZnS:Ag,Ni,　ZnS:Au,In,　ZnS-CdS (25-75),　ZnS-CdS (50-50),　ZnS-CdS(75-25),　ZnS-CdS:Ag,Br,Ni,　ZnS-CdS:Ag+,Cl,　ZnS-CdS:Cu,Br,　ZnS-CdS:Cu,I,　ZnS:Cl-,　ZnS:Eu2+,　ZnS:Cu,　ZnS:Cu+,Al3+,　ZnS:Cu+,Cl-,　ZnS:Cu,Sn,　ZnS:Eu2+,　ZnS:Mn2+,　ZnS:Mn,Cu,　ZnS:Mn2+,Te2+,　ZnS:P,　ZnS:P3-,Cl-,　ZnS:Pb2+,　ZnS:Pb2+,Cl-,　ZnS:Pb,Cu, Zn3(PO4)2:Mn2+, Zn2SiO4:Mn2+, Zn2SiO4:Mn2+,As5+, Zn2SiO4:Mn,Sb2O2, Zn2SiO4:Mn2+,P, Zn2SiO4:Ti4+,　ZnS:Sn2+,　ZnS:Sn,Ag,　ZnS:Sn2+,Li+,　ZnS:Te,Mn,　ZnS-ZnTe:Mn2+,　ZnSe:Cu+,Cl 또는 ZnWO4., SrAl2O4:Eu2+,Dy3+ 등을 들 수 있다. 구체적으로는 상기 예시한 것 중 황화아연(ZnS)계 또는 스트론튬알루마트(SrAlOEuDy)계 물질을 사용할 수 있으나, 이에 제한되는 것은 아니다.
축광 안료는 예를 들면 입경이 1 내지 100㎛일 수 있고, 구체적으로 5 내지 50㎛, 보다 구체적으로 5 내지 20㎛인 것을 사용할 수 있으나, 이에 제한되는 것은 아니다.
축광 안료는 예를 들면 바인더 수지 고형분 100중량부에 대하여 3 내지 30중량부, 구체적으로 10 내지 25중량부, 보다 구체적으로 15 내지 20중량부 포함될 수 있으나, 이에 제한되는 것은 아니다.
형광증백제는 축광 안료와 함께 사용되어 조성물의 휘도를 현저히 개선하는 역할을 한다.
형광증백제로는 예를 들면 벤조트리아졸계, 나프토트리아졸계 및 쿠마린계 화합물을 사용할 수 있으나, 이에 제한되는 것은 아니다. 구체적으로 형광증백제는 사용 용도에 따라 다른 것을 사용할 수 있는데, 본 발명의 조성물이 잉크, 페인트 등의 도료로 사용되는 경우에는 벤조트리아졸계, 나프토트리아졸계를 사용할 수 있고, 성형 소재로 사용되는 경우에는 쿠마린계를 사용할 수 있으나, 이에 제한되는 것은 아니다.
구체적으로는 하기 화학식 1 내지 6 중 적어도 하나를 사용할 수 있다.
[화학식 1]
Figure pat00007
[화학식 2]
Figure pat00008
[화학식 3]
Figure pat00009
[화학식 4]
Figure pat00010
[화학식 5]
Figure pat00011
[화학식 6]
Figure pat00012
.
형광 증백제는 예를 들면 바인더 수지 고형분 100중량부에 대하여 1 내지 10 중량부, 구체적으로 1 내지 8중량부, 보다 구체적으로 1 내지 5 중량부 포함될 수 있으나, 이에 제한되는 것은 아니다.
필요에 따라, 본 발명의 조성물은 용제를 더 포함할 수 있다.
용제는 당 분야에 공지된 것을 제한없이 사용할 수 있으며, 예를 들면 물, 휘발성 용제인 에틸알콜, 아세톤, 부틸아세테이트, 메탄올, 에탄올, n-프로필알코올, 이소프로필 알코올, n-부탄올에서 선택되는 하나 상을 사용하며, 상기 휘발성 용제는 본 발명의 조성물을 잉크 또는 페인트 등의 도료로 사용하기 위하여 사용 용도에 맞도록 알맞은 점도를 갖도록 조절하는데 사용할 수 있으며, 그 점도는 공지의 기술의 점도를 사용하고, 그에 맞도록 용제와 증점제의 양을 조절하여 사용한다.
본 발명의 조성물은 상기 외에도 공지된 첨가제를 더 사용할 수 있다. 예를 들면 소포제, 분산제, 증점제, 실리카졸, 가소제, 건조제, 표면조정제, 안티-실킹 에이전트(anti-silking agent), 레올러지(rheological) 조절제, 축광 입자의 응결방지제 및 자외선 흡수제를 사용할 수 있다.
본 발명의 조성물은 다양한 방법으로, 다양한 용도로 사용될 수 있다. 예를 들면 잉크, 페인트 등의 도료로서 사용될 수도 있고, 성형 소재로서 사용될 수도 있다. 성형은 예를 들면 사출 성형, 압출 성형 등 당 분야에 공지된 방법으로 성형될 수 있으나, 이에 제한되는 것은 아니다.
이하, 본 발명을 구체적으로 설명하기 위해 실시예를 들어 상세하게 설명하기로 한다.
실시예
1. 축광용 조성물의 제조
하기 표 1의 조성 및 함량을 갖는 조성물을 제조하였다(축광안료 입경은 8 내지 12㎛).
바인더수지(A) 축광안료(B) 형광증백제(C)
종류 함량 종류 함량 종류 함량
실시예1 아크릴 100 SrAlOEuDy 18 화학식 5 2
실시예2 PVC 100 SrAlOEuDy 18 화학식 5 2
실시예3 PC 100 SrAlOEuDy 18 화학식 5 2
실시예4 TAC 100 SrAlOEuDy 18 화학식 5 2
실시예5 아크릴 100 ZnS 18 화학식 5 2
실시예6 PVC 100 ZnS 18 화학식 5 2
실시예7 아크릴 100 SrAlOEuDy 18 화학식 1 2
실시예8 아크릴 100 SrAlOEuDy 18 화학식 2 2
실시예9 아크릴 100 SrAlOEuDy 18 화학식 3 2
실시예10 아크릴 100 SrAlOEuDy 18 화학식 4 2
실시예11 아크릴 100 SrAlOEuDy 18 화학식 6 2
실시예12 아크릴 100 SrAlOEuDy 18 화학식 5 7
실시예13 아크릴 100 SrAlOEuDy 18 화학식 5 0.5
비교예1 아크릴 100 SrAlOEuDy 18 - -
비교예2 아크릴 100 ZnS 18 - -
비교예3 PVC 100 SrAlOEuDy 18 - -
비교예4 PVC 100 ZnS 18 - -
2. 축광층 형성 및 휘도 측정
도료(아크릴 외의 수지)의 경우, 아크릴 시트 상에 도포하고 건조시켜 두께 2mm의 축광층(도료층)을 형성하고, 압출 소재(아크릴 수지 사용)의 경우, 두께 3mm의 축광층(압출 시편)을 형성하였다.
각각의 축광층에 축광층으로부터 2m 높이에서 18W 형광등을 20분간 조사하고, 이후 축광층의 밝기를 측정하고, 그 결과는 하기 표 2에 나타내었다.
구분 휘도(cd/m2) 구분 휘도(cd/m2)
실시예 1 1310 실시예 10 1250
실시예 2 1300 실시예 11 1275
실시예 3 1300 실시예 12 1320
실시예 4 1305 실시예 13 1200
실시예 5 900 비교예 1 1000
실시예 6 920 비교예 2 750
실시예 7 1280 비교예 3 1015
실시예 8 1285 비교예 4 760
실시예 9 1270 - -
상기 표 2를 참고하면, 형광증백제의 첨가 여부를 제외하고는 비교예와 동일한 실시예의 조성물로 제조된 축광층이 비교예의 축광층 대비 개선된 휘도를 갖는 것을 확인할 수 있다.

Claims (7)

  1. 바인더 수지, 축광안료 및 형광증백제를 포함하는 축광용 조성물.
  2. 청구항 1에 있어서, 상기 바인더 수지는 폴리에틸렌테레프탈레이트(polyethyleneterephtalate, PET), 폴리에스테르(polyester), 에틸렌 비닐 아세테이트(ethylene vinyl acetate, EVA), 폴리에틸렌(polyethylene), 사이클릭 올레핀 중합체(cyclic olefin polymer, COP), 사이클릭 올레핀 공중합체(cyclic olefin copolymer, COC), 폴리아크릴레이트(polyacrylate, PAC), 폴리카보네이트(polycarbonate, PC), 폴리에틸렌(polyethylene, PE), 폴리메틸메타크릴레이트(polymethylmethacrylate, PMMA), 폴리에테르에테르케톤(polyetheretherketon, PEEK), 폴리에틸렌나프탈레이트(polyethylenenaphthalate, PEN), 폴리에테르이미드(polyetherimide, PEI), 폴리이미드(polyimide, PI), 트리아세틸셀룰로오스(triacetylcellulose, TAC), 및 폴리비닐클로라이드(Polyvinyl chloride, PVC)로 이루어진 군에서 선택된 적어도 하나인, 조성물.
  3. 청구항 1에 있어서, 상기 축광 안료는 유화아연(ZnS)계 또는 스트론튬알루마트(SrAlOEuDy)계 안료인, 조성물.
  4. 청구항 1에 있어서, 상기 형광증백제는 벤조트리아졸계, 나프토트리아졸계 및 쿠마린계 형광증백제로 이루어진 군에서 선택된 적어도 하나인, 조성물.
  5. 청구항 1에 있어서, 상기 형광증백제는 하기 화학식 1 내지 6 중 어느 하나로 표시되는 것인, 조성물:
    [화학식 1]
    Figure pat00013

    [화학식 2]
    Figure pat00014

    [화학식 3]
    Figure pat00015

    [화학식 4]
    Figure pat00016

    [화학식 5]
    Figure pat00017

    [화학식 6]
    Figure pat00018
    .
  6. 청구항 1에 있어서, 상기 형광증백제는 바인더 수지 고형분 100중량부에 대하여 1 내지 5 중량부 포함되는, 조성물.
  7. 청구항 1에 있어서, 바인더 수지 100중량부에 대하여 축광 안료는 10 내지 25 중량부, 형광 증백제는 1 내지 10 중량부 포함되는, 조성물.
KR1020190157784A 2019-11-29 2019-11-29 축광용 조성물 KR20210067803A (ko)