KR20210018289A - 적어도 2개의 0° 층을 갖는 다축 제품 - Google Patents

적어도 2개의 0° 층을 갖는 다축 제품 Download PDF

Info

Publication number
KR20210018289A
KR20210018289A KR1020207035656A KR20207035656A KR20210018289A KR 20210018289 A KR20210018289 A KR 20210018289A KR 1020207035656 A KR1020207035656 A KR 1020207035656A KR 20207035656 A KR20207035656 A KR 20207035656A KR 20210018289 A KR20210018289 A KR 20210018289A
Authority
KR
South Korea
Prior art keywords
multiaxial
thread
product
layers
thread layers
Prior art date
Application number
KR1020207035656A
Other languages
English (en)
Inventor
론니 보카츠
요하네스 레바인
Original Assignee
테이진 카르본 오이로페 게엠베하
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 테이진 카르본 오이로페 게엠베하 filed Critical 테이진 카르본 오이로페 게엠베하
Publication of KR20210018289A publication Critical patent/KR20210018289A/ko

Abstract

본 발명은 적어도 3개의 쓰레드 층을 포함하는 다축 제품에 관한 것이고, 여기서, 상기 쓰레드 층 각각은, 상기 쓰레드 층 내에서 서로 평행하고 서로 바로 옆에 인접하도록 배열된 멀티-필라멘트 보강용 얀으로 형성되고, 적어도 2개의 쓰레드 층은, 상기 다축 제품 내에서 상기 쓰레드 층이 0° 방향을 한정하도록, 상기 다축 제품 내에 배열되고, 상기 적어도 하나의 추가 쓰레드 층은 상기 다축 제품 내에서 0° 방향에 대해 ± 10° 초과의 각도로 배열되고, 상기 0° 방향으로의 적어도 2개의 쓰레드 층은, 상기 다축 제품 내에 상기 적어도 3개의 쓰레드 층의 상대적 배열을 기준으로 하여, 그 사이에 추가의 멀티-필라멘트 보강용 얀의 층 없이, 차례로 직접적으로(directly) 이어진다. 본 발명은 또한 다축 제품의 제조 방법에 관한 것이다. 본 발명은 추가로 상기 다축 제품으로부터 제조된 복합체 및 상기 다축 제품으로부터 복합체의 제조 방법에 관한 것이다.

Description

적어도 2개의 0° 층을 갖는 다축 제품
본 발명은 적어도 3개의 쓰레드 층을 포함하는 다축 제품에 관한 것이다.
다축 제품은 오랜 기간 동안 공지되었다.
EP 2547816 또는 EP 2547510은, 예를 들면, 다축 제품 내에 서로에 대해 상이한 각을 갖는 다수의 층을 갖는 다축 제품을 기술한다.
공지된 다축 제품의 단점은, 그러나, 다축 제품의 기계적 성질이 단지 작은 범위까지만 조절될 수 있다는 것이다. 예를 들면, 0° 방향으로 다축 제품의 압력 적용은 0° 방향으로의 쓰레드 층의 표면 중량(surface weight)에 강하게 의존한다. 표면 중량의 증가는 기계적 성질의 개선을 야기할 것이다. 그러나, 표면 중량은 문제 없이 증가될 수 없다. 높은 표면 중량은 종종 층 내에 섬유 편차 또는 섬유 응축(condensing) (소위 파상(undulation))을 야기하고, 이의 결과로서 쓰레드 층 또는 이의 인접 층은 파상마모(corrugation)를 포함한다. 파상마모는 또한 쓰레드 층의 기계적 성질을 저하시킨다.
EP 3023241에서 섬유-보강된 물질이 공지되어 있고, 이는 테이프(tape) 물질 및 서로에 대해 각이 지게 부착된 상이한 층으로 구성될 수 있다. 상기 문서에 따르면, 테이프는 서로로부터 이격 배열되도록 제공된다 (이들은 분리 채널을 형성한다). 따라서, 얀-부재 영역(yarn-free regions)이 야기되기 때문에 상기 물질의 기계적 성질에 영향을 준다.
따라서, 본 발명의 과제는 기계적 성질이 더 우수하게 적용될 수 있는 다축 제품을 제공하는 것이다.
이러한 과제는 적어도 3개의 쓰레드 층을 갖는 다축 제품에 의해 해결되고, 여기서, 쓰레드 층 각각은, 상기 쓰레드 층 내에서 서로 평행하고 서로 바로 옆에 인접하도록 배열된 멀티-필라멘트 보강용 얀으로 형성되고, 적어도 2개의 쓰레드 층은, 다축 제품 내에서 쓰레드 층이 0° 방향을 한정하도록, 상기 다축 제품 내에 배열되고, 적어도 하나의 추가 쓰레드 층은 다축 제품 내에서 0° 방향에 대해 ± 10° 초과의 각도로 배열되고, 상기 0° 방향으로의 적어도 2개의 쓰레드 층은, 다축 제품 내에 적어도 3개의 쓰레드 층의 상대적 배열을 기준으로 하여, 그 사이에 추가의 멀티-필라멘트 보강용 얀의 층 없이, 차례로 직접적으로 이어진다(follow directly one after the other).
다축 제품 내에 (그 사이에 쓰레드 층으로서 멀티-필라멘트 보강용 얀의 임의의 추가 층 없이) 차례로 직접적으로 이어지는, 0° 방향으로의 적어도 2개의 쓰레드 층을 사용하여, 다축 제품의 기계적 성질에 유리하게 영향을 줄 수 있다. 예를 들면, 0° 방향으로의 적어도 2개의 쓰레드 층은 상이한 멀티-필라멘트 보강용 얀으로 구성될 수 있고, 여기서, 상이한 얀 타입은, 하나의 층 내에 존재하지 않기 때문에, 서로 부정적으로 영향을 미칠 수 없거나, 약간의 범위까지만 부정적으로 영향을 미친다.
다축 제품 내에 0° 방향에 대해 ± 10° 초과의 각도의 적어도 하나의 추가 쓰레드 층은 바람직하게는 다축 제품 내에 0° 방향에 대해 ± 30°, ± 45°, ± 60° 및/또는 90°의 각을 갖는다. 0° 방향에 대해 ± 10° 초과의 각도의 적어도 하나의 추가 쓰레드 층은 그러나, 실제로 0° 방향으로 부착되어야 하지만 단지 부정확의 이유만으로 0° 방향에서 약간 벗어나는 각으로 부착되는 쓰레드 층이 아니다. 0° 방향에 대해 ± 10° 초과의 각도의 적어도 하나의 추가 쓰레드 층은 또한 로 하기에 적어도 하나의 추가 쓰레드 층으로서 유일하게 기술될 것이다.
명확함을 목적으로: 다축 제품은 멀티-필라멘트 보강용 얀으로 만들어진 다수의 쓰레드 층을 포함할 수 있다. 본 발명에 따라서, 그러나, 0° 층에 대해 적어도 ± 10°의 각도를 갖는 멀티-필라멘트 보강용 얀으로 만들어진 어떠한 층도, 0° 층을 형성하는 적어도 2개의 쓰레드 층 사이에 개재되어 있지 않다(어떠한 추가 쓰레드 층도 없음). 0° 방향으로의 쓰레드 층 사이에, 결과적으로, 예를 들면, 부직포 층과 같은 단지 소위 중간(interim) 층만이 있을 수 있다. 2000 MPa 미만의 강도 및/또는 층 내에 주로 비-평행 섬유 배열을 갖는 섬유(예를 들면, 부직포, 랜덤 배향된 섬유 층)를 갖는 층 각각은 이와 관련하여 중간 층으로서 고려되어야 한다.
쓰레드 층은 바람직하게는 또한 테이프로 기술될 수 있는 스프레드(spread) 멀티-필라멘트 보강용 얀으로 이루어진다. 테이프는 바람직하게는 80 내지 800 mm의 너비를 갖고, 특히 바람직하게는 테이프는 250 내지 360 mm 및 특히 가장 바람직하게는 600 내지 700 mm의 너비를 갖는다. 쓰레드 층의 제조를 위해, 스프레드 멀티-필라멘트 보강용 얀을 쓰레드 층 내에 구멍이 실질적으로 없도록 (얀-부재 영역) 부착한다. 멀티-필라멘트 보강용 얀은 결과적으로 서로에 대해 구멍-부재(hole-free) 방식으로 존재한다. 추가로 바람직한 실시형태에서, 적어도 3개의 쓰레드 층은 각각 하나의 단방향 패브릭(unidirectional fabric)으로 이루어진다. 단방향 패브릭에서, 멀티-필라멘트 보강용 얀은 또한 스프레드되고, 서로 평행하고 서로 바로 옆에 인접하도록 배열되고, 그러나 보조(auxiliary) 얀과 함께 교착(interwoven)되어 층의 안정성을 증가시킨다. 보조 얀으로서, 예를 들면, 200 dtex의 타이터(titre)를 갖는 이성분 핫멜트(hotmelt) 접착(adhesive) 얀을 사용할 수 있다.
바람직하게는, 0° 방향으로의 적어도 2개의 쓰레드 층을 다축 제품에서 서로 직접적으로 접촉되게 위치시킨다. 여기서 "직접적 접촉(direct contact)"은 다축 제품에서 0° 방향으로의 적어도 2개의 쓰레드 층을 0° 방향으로의 적어도 2개의 쓰레드 층 사이에 어떠한 추가 중간 층 없이 (또한 부직포 없이) 서로 위에 놓여져 있는 것을 의미하는 것으로 여겨진다.
바람직하게는, 0° 방향으로의 적어도 2개의 쓰레드 층은 각각의 경우에 적어도 100 g/㎡, 보다 바람직하게는 적어도 150 g/㎡ 및 특히 바람직하게는 적어도 180 g/㎡의 표면 중량을 갖는다. 바람직한 실시형태에서, 0° 방향으로의 쓰레드 층 모두는 동일한 표면 중량을 갖는다. 그러나, 또한 0° 방향으로의 적어도 2개의 쓰레드 층이 상이한 표면 중량을 갖는 것이 가능할 것이다. 0° 방향으로의 적어도 2개의 쓰레드 층이 다축 제품에 사용되기 때문에, 유리하게는 높은 표면 중량을 0° 방향으로 성취할 수 있어서, 예를 들면, 0° 방향으로 압축 강도가 증가된다. 높은 표면 중량을 갖는 하나의 단일 층의 사용과 비교하여, 그러나, 예를 들면, 쓰레드 파상이 0° 방향으로의 개별적인 쓰레드 층 또는 이들의 인접한 층에서 발생하지 않거나 단지 약간 발생하는 이점을 야기한다.
바람직하게는, 적어도 하나의 추가 쓰레드 층은 적어도 100 g/㎡, 특히 바람직하게는 적어도 120 g/㎡의 표면 중량을 갖는다. 다수의 이러한 추가 쓰레드 층을 사용하는 경우, 모든 쓰레드 층은 각각의 경우에 동일한 표면 중량을 갖거나 상이한 표면 중량을 가질 수 있다.
바람직하게는, 적어도 3개의 쓰레드 층은 멀티-필라멘트 보강용 쓰레드로서 탄소 섬유, 유리 섬유, 아라미드 얀 및/또는 고충진 UHMW-폴리에틸렌 얀 또는 상기 얀의 혼합물을 갖는다. 특히 바람직하게는, 적어도 3개의 쓰레드 층은, 적어도 90% 이하의, 상기 언급된 섬유 또는 얀 또는 상기 언급된 섬유 또는 얀의 혼합물로 이루어진다.
바람직한 실시형태에서, 0° 방향으로의 적어도 2개의 쓰레드 층은 적어도 하나의 추가 쓰레드 층과 동일한 섬유 타입 또는 얀 타입을 갖는다. 상이한 쓰레드 층은 이용되는 얀 타이터에 대해 동일하거나 상이할 수 있다.
바람직하게는, 멀티-필라멘트 보강용 얀은 JIS-R-7608에 따라 측정하여 적어도 5000 MPa의 강도 및 JIS-R-7608에 따라 측정하여 적어도 260 GPa의 인장 계수를 갖는 탄소 섬유 얀이다. 사용되는 이러한 탄소 섬유 얀과 관련하여, 출원 번호 JP 2017-231749를 갖는 아직 공개되지 않은 일본 출원을 참조한다. 추가로 바람직하게는, 멀티-필라멘트 보강용 얀은 JIS-R-7608에 따라 측정하여 적어도 4500 MPa의 강도 및 JIS-R-7608에 따라 측정하여 적어도 240 GPa의 인장 계수를 갖는 탄소 섬유 얀이다.
바람직하게는, 다축 제품은 적어도 하나의 부직포 층을 갖는다. 바람직하게는 적어도 하나의 부직포는 적어도 3개의 쓰레드 층 위에, 아래에 및/또는 그 사이에 배열된다. 특히 바람직하게는, 부직포은 각각의 쓰레드 층 사이에 배열되고/되거나, 다축 제품은 상부 면에 및/또는 하부 면에 각각의 경우에 추가 부직포를 갖는다. 이와 관련하여, 부직포는 또한 0° 방향으로의 2개의 쓰레드 층 사이에 배열될 수 있다는 것이 명백하여야 하고, 이는 적어도 3개의 쓰레드 층의 상대적 배열을 기준으로 하여 차례로 직접적으로 이어진다 (다축 제품에서), (0° 방향으로의 쓰레드 층이 서로 직접적으로 접촉하고 있는 실시형태 예시는 제외함). 추가로 바람직하게는, 다축 제품은 분말 결합제를 갖는다. 예를 들면, 부직포는 분말 결합제를 가질 수 있다. 바람직하게는, 적어도 하나의 부직포는 3 내지 25 g/㎡의 표면 중량을 갖는다. 하나 초과의 부직포를 갖는 실시형태에서, 사용되는 모든 부직포 층은 동일한 표면 중량 또는 상이한 표면 중량을 가질 수 있다. 다축 제품의 특히 바람직한 구조는 하기와 같다:
ㆍ 적어도 하나의 추가 쓰레드 층
ㆍ 부직포
ㆍ 적어도 하나의 추가 쓰레드 층
ㆍ 부직포
ㆍ 0° 방향으로의 쓰레드 층
ㆍ 부직포
ㆍ 0° 방향으로의 쓰레드 층
ㆍ 분말 결합제를 갖는 부직포
하나의 실시형태에서, 다축 제품은 금속 메쉬를 갖는다. 바람직하게는, 금속 메쉬는 적어도 3개의 쓰레드 층 위에 및/또는 아래에 배열된다. 바람직하게는, 금속 메쉬는 다축 제품의 최외 층을 형성한다. 특히 바람직하게는, 금속 메쉬는 50 내지 250 g/㎡, 특히 바람직하게는 70 내지 175 g/㎡ 및 특히 가장 바람직하게는 90 내지 139 g/㎡의 표면 중량을 갖는다. 금속 메쉬는 바람직하게는 하나 또는 수개의 쓰레드 층과, 예를 들면, 스티칭(stitching)에 의해 또는 다축 제품을 함께 유지하는 편물 쓰레드 시스템에 의해 연결된다. 금속 메쉬에 의하여, 다축 제품의 전도성은 유리하게 개선될 수 있고, 이는 특히 항공 및 우주여행 분야에서 적용하기에 유리하다. 바람직하게는, 금속 메쉬는 구리 메쉬이다.
바람직하게는, 적어도 하나의 부직포는 적어도 하나의 첫번째 및 하나의 두번째 열가소성 중합체 성분으로 이루어지고, 여기서, 상기 첫번째 및 두번째 중합체 성분은 상이한 용융 온도를 갖는다.
바람직하게는, 더 낮은 용융 온도를 갖는 중합체 성분은 80 내지 135℃ 범위의 용융 온도를 갖고/갖거나, 더 높은 용융 온도를 갖는 중합체 성분은 140 내지 250℃ 범위의 용융 온도를 갖는다.
바람직하게는, 첫번째 중합체 성분은 에폭시, 시아네이트 에스테르 또는 벤즈옥사진 매트릭스 수지 또는 이들 매트릭스 수지의 혼합물에 가용성이고, 두번째 중합체 성분은 에폭시, 시아네이트 에스테르 또는 벤즈옥사진 매트릭스 수지 또는 이들 매트릭스 수지의 혼합물에 불용성이다.
실시형태에서, 첫번째 중합체 성분은 폴리아미드이고/이거나, 부직포는 에폭사이드를 갖는다. 특히 바람직하게는, 에폭사이드는 분말 결합제의 형태로 존재하는데, 이는 부직포 상에 뿌려지거나 부직포와 열적으로 결합된다.
결합 물질은 일부 실시형태에서 미립자 형태로 사용되는 것을 고려하면, 바람직한 입자 크기는 50 내지 160 μm, 특히 바람직하게는 80 내지 140 μm의 범위로 존재한다.
부직포를 갖는 모든 실시형태의 경우에서, 하나 초과의 부직포 층이 사용되는 경우, 각각의 경우에 상이한 부직포 또는 동일한 부직포를 다축 제품에서 사용할 수 있다. 상이한 부직포 층을 사용하는 경우, 부직포 층은 이들의 표면 중량, 이들의 재료 및/또는 이들의 구조가 상이할 수 있다.
이전에 공지된 다축 제품과 비교하여, 제안된 다축 제품은 편평한 쓰레드 패턴을 갖고 동시에, 파상의 위험성이 줄어들기 때문에 높은 섬유 용적 비율을 갖는다는 이점이 있다. 이에 의해, 특히 다축 제품의 압축 강도가 증가될 수 있다. 제안된 다축 제품은 추가로 비슷한 표면 중량을 갖지만 더 적은 쓰레드 층을 갖는 다축 제품과 비교하여 뿐만 아니라 사전에 미리-고정된 0° 층 (예를 들면, UD 테이프로서, 위사(weft) 쓰레드, 분말 결합제 또는 열가소성 메쉬로 고정됨)을 사용하여 보다 용이하게 드래이핑될(draped) 수 있다.
본 발명의 추가 주제는 상기한 다축 제품의 제조 방법에 관한 것이다.
다축 제품의 제조를 위해, 적어도 3개의 쓰레드 층을 부착하고, 여기서, 각각의 쓰레드 층을, 쓰레드 층 내에 서로 평행하고 서로 바로 옆에 인접하도록 배열되는 멀티-필라멘트 보강용 얀으로 형성하고, 다축 제품의 제조에서 적어도 2개의 쓰레드 층은 0° 방향으로 부착되고, 0° 방향으로의 적어도 2개의 쓰레드 층 모두 위에 및/또는 아래에 적어도 하나의 추가 쓰레드 층이 상기 다축 제품 내에서 0° 방향에 대해 ± 10° 초과의 각도로 부착된다.
다축 제품을 제조하기 위한 적어도 3개의 쓰레드 층은 먼저 다축 제품의 제조 동안 형성될 수 있거나 (온라인), 최종 층으로서 제조 방법에서 다축 제품을 제조하기 위한 미리-제작된 제품 (예를 들면, 테이프)로서 미리 부착될 수 있다 (오프라인).
0° 방향으로의 적어도 2개의 쓰레드 층을 그 사이에 추가 쓰레드 층 없이 (멀티-필라멘트 보강용 얀이 0° 방향에 대해 ± 10° 초과의 각도로 배열됨) 서로 부착한다. 적어도 하나의 추가 쓰레드 층은 결과적으로 0° 방향으로의 적어도 2개의 쓰레드 층 위 또는 아래에 배열될 수 있다. 하나 초과의 추가 쓰레드 층이 사용되는 경우, 0° 방향으로의 추가 쓰레드 층이 쓰레드 층 위에 및/또는 아래에 위치하지만, 그 사이에 위치하지 않는다. 하나 초과의 추가 쓰레드 층을 사용하는 경우, 이에 따라 제조된 다축 제품은 0° 방향으로 적어도 2개의 쓰레드 층에 대해 대칭 구조를 가질 수 있다. 0° 방향에 대한 대칭 구조는 예를 들면, 하기 구조를 갖는 다축 제품의 경우로 존재한다:
+45°/0°/0°/-45°
바람직하게는, 다축 제품을 제조하는 경우, 적어도 하나의 부직포 층은 쓰레드 층 중 하나 사이에 부착된다. 바람직하게는, 부직포 층은 모든 쓰레드 층 사이에 및/또는 마지막 층으로서 외부 쓰레드 층 상 한 면 또는 둘 다의 면 상에 부착된다. 부직포 층으로서 사용되는 부직포에 대해, 다축 제품의 부직포에 대해서 이미 기재된 실시형태를 참조하여야 한다.
하나의 실시형태 예에서, 추가로 금속 메쉬가 다축 제품의 외부 면에 부착될 수 있다. 금속 메쉬의 디자인을 위해서, 다축 제품의 금속 메쉬에 대해 이미 기술되어 있는 것을 참조한다.
바람직한 실시형태에서, 0° 방향으로 부착된 적어도 2개의 쓰레드 층 각각은 각각의 경우에 하나의 부착 장치로 부착된다. 사전-제작된 쓰레드 층을 이미 사용한 경우, 결과적으로 롤업(rolled-up) 쓰레드 층을 갖는 하나의 부착 장치가 각각의 0° 방향으로의 쓰레드 층에 대해 사용된다.
또다른 실시형태에서, 0° 방향으로의 적어도 2개의 쓰레드 층을, 다축 제품을 제조하는 경우, 온라인 공급이 제공되는 경우, 각각의 경우에 하나의 고정 쓰레드 크릴(standing thread creel)로 생성한다.
추가 실시형태에서, 0° 방향으로의 적어도 2개의 쓰레드 층을 다축 제품을 제조하는 경우 소위 단방향 패브릭으로서 부착된다. 제조 동안, 이어서, 각각의 단방향 패브릭을 0° 방향으로의 쓰레드 층으로서 바람직하게는 제조 방법에서 자체 부착 장치에 의해 위치시킨다.
본 발명의 추가 주제는 방금 기재된 방법에 따른 적어도 하나의 다축 제품를 포함하는 섬유-보강된 복합체에 관한 것이다. 바람직하게는, 복합체는 그 사이에 멀티-필라멘트 보강용 얀의 다수의 쓰레드 층 및 부직포 층을 갖는다. 특히 바람직하게는, 복합체는, 쓰레드 층 및 부직포 층이 함침되는 추가 또는 부가의 매트릭스 물질을 갖는다.
따라서 본 발명의 추가의 주제는 또한 추가 매트릭스 물질에 의한 복합체의 제조 방법이다. 바람직하게는, 이러한 목적을 위해, 처음에 언급된 종류의 다수의 다축 제품을 서로 적층시키고, 열 및 압력으로 및 추가 매트릭스 물질과 통합하여, 콤포넌트 (복합체)를 형성한다. 이러한 종류의 복합체는 예를 들면, 항공 및 우주여행 분야에서 또는 자동차 분야에서 콤포넌트로서 사용될 수 있다.

Claims (18)

  1. 적어도 3개의 쓰레드(thread) 층을 포함하는 다축 제품(Multiaxial product)으로서, 상기 쓰레드 층 각각은, 상기 쓰레드 층 내에서 서로 평행하고 서로 바로 옆에 인접하도록 배열된 멀티-필라멘트 보강용 얀(multi-filament reinforcing yarns)으로 형성되고, 적어도 2개의 쓰레드 층은, 상기 다축 제품 내에서 상기 쓰레드 층이 0° 방향을 한정하도록, 상기 다축 제품 내에 배열되고, 상기 적어도 하나의 추가 쓰레드 층은 상기 다축 제품 내에서 0° 방향에 대해 ± 10° 초과의 각도로 배열되고, 상기 0° 방향으로의 적어도 2개의 쓰레드 층은, 상기 다축 제품 내에 상기 적어도 3개의 쓰레드 층의 상대적 배열을 기준으로 하여, 그 사이에 추가의 멀티-필라멘트 보강용 얀의 층 없이, 차례로(one after the other) 직접적으로 이어지는(follow), 다축 제품.
  2. 제1항에 있어서, 상기 0° 방향으로의 적어도 2개의 쓰레드 층이 상기 다축 제품에서 서로 직접적으로 접촉하는, 다축 제품.
  3. 제1항 또는 제2항에 있어서, 상기 0° 방향으로의 적어도 2개의 쓰레드 층이, 각각의 경우에 적어도 150 g/㎡, 바람직하게는 적어도 180 g/㎡의 표면 중량(surface weight)을 갖는, 다축 제품.
  4. 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 다축 제품 내에서 0° 방향에 대해 ± 10° 초과의 각도로 배열된, 상기 적어도 하나의 추가 쓰레드 층이, 각각의 경우에 적어도 100 g/㎡, 바람직하게는 적어도 120 g/㎡의 표면 중량을 갖는, 다축 제품.
  5. 제1항 내지 제4항 중 어느 한 항에 있어서, 상기 멀티-필라멘트 보강용 얀이 탄소 섬유, 유리 섬유 또는 아라미드 얀 또는 고충진(highly-extended) UHMW-폴리에틸렌 얀인, 다축 제품.
  6. 제1항 내지 제5항 중 어느 한 항에 있어서, 상기 멀티-필라멘트 보강용 얀이, JIS-R-7608에 따라 측정하여 적어도 5000 MPa의 강도, 및 JIS-R-7608에 따라 측정하여 적어도 260 GPa의 인장 계수(modulus of tension)를 갖는 탄소 섬유 얀, 및/또는 JIS-R-7608에 따라 측정하여 적어도 4500 MPa의 강도, 및 JIS-R-7608에 따라 측정하여 적어도 240 GPa의 인장 계수를 갖는 탄소 섬유 얀인, 다축 제품.
  7. 제1항 내지 제6항 중 어느 한 항에 있어서, 상기 적어도 3개의 쓰레드 층 위에, 아래에 및/또는 그 사이에 적어도 하나의 부직포가 배열되고/되거나, 적어도 하나의 금속 메쉬(metal mesh)가 상기 적어도 3개의 쓰레드 층 위에 및/또는 아래에 배열되는, 다축 제품.
  8. 제7항에 있어서, 상기 적어도 하나의 부직포가 3 내지 25 g/㎡ 범위의 표면 중량을 갖고/갖거나, 상기 금속 메쉬가 60 내지 200 g/㎡의 표면 중량을 갖는, 다축 제품.
  9. 제7항 또는 제8항에 있어서, 상기 적어도 하나의 부직포가 적어도 하나의 첫번째 및 하나의 두번째 열가소성 중합체 성분으로 이루어지고, 상기 첫번째 및 두번째 중합체 성분은 상이한 용융 온도를 갖는, 다축 제품.
  10. 제9항에 있어서, 더 낮은 용융 온도를 갖는 상기 중합체 성분이 80 내지 135℃ 범위의 용융 온도를 갖고/갖거나, 더 높은 용융 온도를 갖는 상기 중합체 성분이 140 내지 250℃ 범위의 용융 온도를 갖는, 다축 제품.
  11. 제9항 또는 제10항에 있어서, 상기 첫번째 중합체 성분이 폴리아미드이고/이거나, 상기 부직포가 에폭사이드를 갖는, 다축 제품.
  12. 제10항에 있어서, 상기 첫번째 중합체 성분이 에폭시, 시아네이트 에스테르 또는 벤즈옥사진 매트릭스 수지 또는 이들 매트릭스 수지의 혼합물에 가용성이고, 상기 두번째 중합체 성분이 에폭시, 시아네이트 에스테르 또는 벤즈옥사진 매트릭스 수지 또는 이들 매트릭스 수지의 혼합물에 불용성인, 다축 제품.
  13. 제1항 내지 제12항 중 어느 한 항에 있어서, 상기 적어도 하나의 부직포가 미립자 형태의 결합 물질을 갖고, 상기 결합 물질의 입자 크기가 50 내지 160 μm인, 다축 제품.
  14. 제1항 내지 제13항 중 어느 한 항에 따른 적어도 하나의 다축 제품을 갖는 섬유-보강된 복합체(Fibre-reinforced composite).
  15. 적어도 3개의 쓰레드 층으로부터 제1항에 따른 다축 제품의 제조 방법으로서, 상기 쓰레드 층 각각은, 상기 쓰레드 층 내에서 서로 평행하고 서로 바로 옆에 인접하도록 배열된 멀티-필라멘트 보강용 얀으로 형성되고, 상기 다축 제품의 제조 동안 적어도 2개의 쓰레드 층이 0° 방향으로 부착되고(deposited), 상기 0° 방향으로의 적어도 2개의 쓰레드 층 모두 위에 또는 아래에, 상기 다축 제품 내에서 0° 방향에 대해 ± 10° 초과의 각도로 적어도 하나의 추가 쓰레드 층이 부착되는, 방법.
  16. 제15항에 있어서, 상기 적어도 3개의 쓰레드 층 위에, 아래에 및/또는 그 사이에 적어도 하나의 부직포가 부착되는, 방법.
  17. 제14항 내지 제16항 중 어느 한 항에 있어서, 0° 방향으로 부착된 상기 적어도 2개의 쓰레드 층 각각이 각각의 경우에 하나의 부착 장치(depositing device)로 부착되는, 방법.
  18. 제1항 내지 제13항 중 어느 한 항에 따른 적어도 하나의 다축 제품 및 추가 매트릭스 물질이 사용되는, 제14항에 따른 복합체의 제조 방법
KR1020207035656A 2018-06-07 2019-05-29 적어도 2개의 0° 층을 갖는 다축 제품 KR20210018289A (ko)