KR20200056440A - 카르바졸 및 피리딘 구성 유닛에 기초한 전계 발광 물질 - Google Patents
카르바졸 및 피리딘 구성 유닛에 기초한 전계 발광 물질 Download PDFInfo
- Publication number
- KR20200056440A KR20200056440A KR1020207011728A KR20207011728A KR20200056440A KR 20200056440 A KR20200056440 A KR 20200056440A KR 1020207011728 A KR1020207011728 A KR 1020207011728A KR 20207011728 A KR20207011728 A KR 20207011728A KR 20200056440 A KR20200056440 A KR 20200056440A
- Authority
- KR
- South Korea
- Prior art keywords
- substituted
- hydrogen
- electroluminescent material
- tert
- phenyl
- Prior art date
Abstract
본 발명은 카르바졸(carbazole) 및 피리딘(pyridine) 구성 유닛에 기초한 전계 발광 물질을 제공하며, 식 (I)의 구조를 가진다. 실험 결과는 상기 전계 발광 물질을 OLED에 사용하면 발광 효율이 우수하여 유기 전계 발광 소자의 분야에 활용될 가능성이 있음을 보여준다.
Description
본 발명은 신규한 유기 발광 다이오드 전계 발광 물질에 관한 것으로, 더욱 상세하게는 카르바졸(carbazole) 및 피리딘(pyridine) 구성 유닛에 기초한 전계 발광 물질에 관한 것이고, 진공 증착으로 박막을 형성하며 유기 발광 다이오드 소자에 발광층 물질로 사용된다.
최근 활용 전망이 우수한 조명 및 디스플레이 기술로서 유기 발광 다이오드(OLED)가 학계와 산업계에서 널리 주목을 받고 있다. OLED 소자는 자체 발광, 광시야각, 짧은 반응시간 및 플렉시블 소자 제조 가능성 등의 특성을 가지고 있어 차세대 디스플레이 및 조명 기술 분야의 강력한 경쟁자이다. 그러나 현재 OLED는 여전히 낮은 효율 및 짧은 수명 등과 같은 문제점이 있으므로 이에 대한 추가적인 연구가 필요하다.
유기 발광 다이오드는 전자 발광 소자이며, 전압 구동 하에서 전자와 정공이 각각 전자수송층과 정공수송층을 통해 발광층으로 유입되어 재결합되며 엑시톤(exciton)을 형성한다. 그 후, 엑시톤은 발광 특성을 갖는 유기 분자로 에너지를 전달하여 여기시키고, 여기 상태 분자가 기저 상태로 돌아올 때 방사 전이가 일어나면서 발광한다. 1998년 Forrest 등이 전계 발광 인광 소자(PHOLED)를 보고한 이래, PHOLED는 삼중항 및 일중항 엑시톤 발광을 고효율로 사용하면서 많은 주목을 받았다. 고효율 PHOLED 소자는 통상적으로 다층 구조이며, 캐리어 주입, 전송 및 재결합 등의 과정을 편리하게 조절할 수 있는 이점이 있다. 발광층에서 게스트 물질의 도핑 농도가 높을 경우 농도 소광 및 T1-T1 소멸이 발생하여 발광 효율이 떨어질 수 있다. 이러한 문제를 해결하기 위하여, 통상적으로 게스트 물질을 호스트 물질에 도핑시켜 게스트 물질의 농도를 "희석"시킨다. 호스트에 형성된 엑시톤은 
및 덱스터(Dexter) 에너지 전달 방식을 통해 게스트로 전달되며, 여기된 게스트 방사 발광은 기저 상태로 돌아온다. 따라서 고효율 PHOLED 소자를 얻기 위해서는 신규한 고성능의 호스트 물질을 개발하는 것이 중요하다.
호스트 물질은 정공형, 전자형 및 양극형의 세 가지 유형으로 나눌 수 있다. 정공형 호스트 물질을 사용하면 정공, 전자 재결합이 통상적으로 발광층과 전자수송층 계면에서 발생하고, 전자형 호스트 물질을 사용하면 정공, 전자 재결합이 통상적으로 발광층과 정공수송층 계면에서 발생한다. 여기에서 단극성 호스트 물질은 캐리어 재결합 영역을 좁게 만드는 경향이 있음을 알 수 있다. 좁은 재결합 영역은 국부적으로 엑시톤 밀도가 높아져 T1-T1 소멸을 가속화시키므로 소자 성능의 개선에 유익하지 않다. 반면 양극형 호스트 물질은 상기 문제를 효과적으로 해결할 수 있다. 양극형 호스트 물질을 사용하면 소자 내에서 정공과 전자의 균형을 맞추고, 캐리어 재결합 영역을 넓힐 뿐만 아니라 소자 구조를 단순화할 수 있기 때문에, 이 분야의 연구원들로부터 큰 관심을 받고 있다.
본 발명의 목적은 피리딘(pyridine) 및 카르바졸(carbazole) 구성 유닛에 기초한 신규한 양극형 호스트 물질을 제공하는 것이며, 상기 물질은 유기 발광 다이오드 소자에 사용되어 우수한 발광 효율을 수득하였다.
카르바졸 및 피리딘 구성 유닛에 기초한 전계 발광 물질은 화학식 (I)의 구조를 갖는다.
Ar은 하기 그룹 중의 하나이다.
여기에서, R1 및 R2는 독립적으로 수소, C1-C4 치환 또는 미치환된 알킬(alkyl), C2-C4 치환 또는 미치환된 알케닐(alkenyl), C2-C4 치환 또는 미치환된 알키닐(alkynyl), C6-C10의 하나 이상의 치환기를 함유하는 치환 또는 미치환된 아릴(aryl), 방향족 탄화수소기, C3-C8의 하나 이상의 치환기를 함유하는 치환 또는 미치환된 하나 이상의 헤테로 원자를 함유하는 헤테로아릴(heteroaryl)로부터 선택되고; 상기 치환은 할로겐 원소, C1-C4의 알킬로 치환된다.
바람직하게는, R1 및 R2는 독립적으로 수소, C1-C4 알킬, C6-C10의 하나 이상의 치환 또는 미치환된 아릴, 방향족 탄화수소기로부터 선택되고;
더욱 바람직하게는, R1 및 R2는 독립적으로 수소, 메틸(methyl), tert-부틸(tert-butyl), 페닐(phenyl), 톨릴(tolyl), 나프틸(naphthyl)로부터 선택되고;
보다 바람직하게는, R1 및 R2는 수소, tert-부틸, 페닐 및 메틸로부터 선택된 동일한 치환기이고,
특히 바람직하게는, 여기에서 Ar은 하기 그룹이고,
보다 바람직하게는, 여기에서 Ar은 하기 그룹 중 하나이다.
특히 바람직하게는, R1은 수소이고, R2는 tert-부틸, 페닐, 톨릴, 나프틸이다.
유기 전계 발광 다이오드 소자는 음극, 양극 및 유기층을 포함하고, 상기 유기층은 정공수송층, 발광층, 정공차단층 및 전자수송층 중 하나 이상이며, 이러한 유기층은 각층이 반드시 존재할 필요는 없다.
상기 정공수송층, 정공차단층, 발광층 및/또는 전자수송층은 식 (I)의 화합물을 포함한다.
상기 식 (I)의 화합물은 발광층에 사용되는 호스트 물질이다.
본 발명의 소자 유기층의 총 두께는 1 내지 1000nm이며, 바람직하게는 1 내지 500nm, 더욱 바람직하게는 5 내지 300nm이다.
상기 유기층은 증착 또는 용액법에 의해 박막을 형성할 수 있다.
상기에서 언급한 바와 같이, 본 발명의 식 (I)의 화합물은 하기와 같지만 하기에 나열된 구조에 한정되지 않는다.
또한 바람직하게는 식 (I)로 표시되는 화합물의 구조는 하기와 같다.
상기 화합물은 유기 전계 발광 소자, 전계 발광 소자, 유기 전계 효과 트랜지스터, 유기 태양 전지 및 화학 센서에 사용된다.
실험 결과는 본 발명의 유기 호스트 물질을 OLED에 사용하면 발광 효율이 우수하여 유기 전계 발광 소자 분야에 활용될 가능성이 있음을 보여준다.
도 1은 본 발명에 따른 유기 전계 발광 소자의 구조도이다.
본 발명을 보다 상세하게 설명하기 위해, 이하의 예시를 특별히 나열하였으나 이에 한정되지 않는다.
실시예 1
화합물 1의 합성 경로
화합물 1의 합성
질소 보호 하에서, 화합물 a(3.2g, 9.5mmol)(참고문헌: J. Heterocycl. Chem., 2016, 53, 615-619 합성), 화합물 1a(3.0g, 10.5mmol)(참고문헌: J. Mater. Chem. C, 2015, 3, 12529-12538), Pd(PPh3)4(208mg, 0.2mmol), 디옥산(dioxane)(40mL) 및 탄산칼륨 수용액(2M, 5mL)을 Schlenk관에 순차적으로 첨가한다. 80℃까지 가열하고 12시간 동안 반응시킨다. 실온으로 냉각시킨 후 상기 반응액을 물에 넣고, 디클로로메탄(dichloromethane)으로 3회 추출하여 유기상을 합친다. 유기층은 무수 황산나트륨으로 건조한 후, 용매를 제거하고, 잔여물은 칼럼 크로마토그래피로 분리하여 담황색 고체를 수득하였고(5.4g, 수율 85%), 승화 후 순도는 99.8%였다. MS(EI):m/z: 662.5(M+).
실시예 2
화합물 2의 합성 경로
화합물 2의 합성
질소 보호 하에서, 화합물 a(2.2g, 6.5mmol), 화합물 2a(2.3g, 8.0mmol)(참고문헌: J. Mater. Chem. C, 2015, 3, 12529-12538 합성), Pd(PPh3)4(208mg, 0.2mmol), 디옥산(40mL) 및 탄산칼륨 수용액(2M, 5mL)을 Schlenk관에 순차적으로 첨가한다. 80℃까지 가열하고 12시간 동안 반응시킨다. 실온으로 냉각시킨 후 상기 반응액을 물에 넣고, 디클로로메탄으로 3회 추출하여 유기상을 합친다. 유기층은 무수 황산나트륨으로 건조한 후, 용매를 제거하고, 잔여물은 칼럼 크로마토그래피로 분리하여 담황색 고체를 수득하였고(3.1g, 수율 72%), 승화 후 순도는 99.8%였다. MS(EI):m/z: 662.5(M+).
실시예 3
화합물 3의 합성 경로
화합물 3의 합성
질소 보호 하에서, 화합물 a(3.2g, 9.5mmol), 화합물 3a(3.0g, 10.5mmol)(참고문헌: J. Mater. Chem. C, 2015, 3, 12529-12538 합성), Pd(PPh3)4(208mg, 0.2mmol), 디옥산(40mL) 및 탄산칼륨 수용액(2M, 5mL)을 Schlenk관에 순차적으로 첨가한다. 80℃까지 가열하고 12시간 동안 반응시킨다. 실온으로 냉각시킨 후 상기 반응액을 물에 넣고, 디클로로메탄으로 3회 추출하여 유기상을 합친다. 유기층은 무수 황산나트륨으로 건조한 후, 용매를 제거하고, 잔여물은 칼럼 크로마토그래피로 분리하여 담황색 고체를 수득하였고(3.4g, 수율 54%), 승화 후 순도는 99.8%였다. MS(EI):m/z: 662.2(M+).
실시예4
화합물 12의 합성 경로
화합물 12의 합성
질소 보호 하에서, 화합물 a(1.2g, 3.6mmol), 화합물 12a(1.1g, 3.83mmol)(참고문헌: CN105601613A 합성), Pd(PPh3)4(50mg, 0.04mmol), 디옥산(20mL) 및 탄산칼륨 수용액(2M, 5mL)을 Schlenk관에 순차적으로 첨가한다. 80℃까지 가열하고 12시간 동안 반응시킨다. 실온으로 냉각시킨 후 상기 반응액을 물에 넣고, 디클로로메탄으로 3회 추출하여 유기상을 합친다. 유기층은 무수 황산나트륨으로 건조한 후, 용매를 제거하고, 잔여물은 칼럼 크로마토그래피로 분리하여 담황색 고체를 수득하였고(2.4g, 수율 83%), 승화 후 순도는 99.7%였다. MS(EI):m /z: 814.5(M+).
실시예 5
유기 전계 발광 소자(1)의 제조
본 발명의 유기 호스트 물질을 사용하여 OLED를 제조하며 도 1과 같다.
먼저, 투명 전도성 ITO 유리 기판(10)(상표면에 양극(20)이 있음)을 순차적으로 세정제 용액, 탈이온수, 에탄올, 아세톤, 탈이온수로 세정한 후 다시 산소 플라즈마로 30초간 처리한다.
그 후, ITO 상에 10nm 두께의 HATCN을 정공주입층(30)으로 증착한다.
그 후, 화합물 TAPC를 증착시켜 40nm 두께의 정공수송층(40)을 형성한다.
그 후, 정공수송층 상에 30nm 두께의 AG-Pt-1(10%), TCTA(60%) 및 화합물 1(30%)을 발광층(50)으로 증착한다.
그 후, 발광층 상에 50nm 두께의 TmPyPb를 정공차단층(60)으로 증착한다.
마지막으로, 1nm LiF를 전자주입층(70)으로, 100nm Al을 소자 음극(80)으로 증착한다.
소자 중 상기 구조식
제조된 소자는 20mA/cm2의 작동 전류 밀도 하에서 9060cd/m2의 밝기, 45.3cd/A의 전류 효율로 녹색광을 방출한다. 본 발명의 유기 물질로 제조된 소자는 전계 발광 성능이 우수하여 고성능 OLED 소자의 호스트 물질의 요건을 충족시킨다.
10: 유리 기판
20: 양극
30: 정공주입층
40: 정공수송층
50: 발광층
60: 정공차단층
70: 전자주입층
80: 음극
20: 양극
30: 정공주입층
40: 정공수송층
50: 발광층
60: 정공차단층
70: 전자주입층
80: 음극
Claims (10)
- 카르바졸 및 피리딘 구성 유닛에 기초한 전계 발광 물질에 있어서,
화학식 (I)의 구조를 갖고,
Ar은 하기 그룹 중의 하나이고,
여기에서, R1 및 R2는 독립적으로 수소, C1-C4 치환 또는 미치환된 알킬(alkyl), C2-C4 치환 또는 미치환된 알케닐(alkenyl), C2-C4 치환 또는 미치환된 알키닐(alkynyl), C6-C10의 하나 이상의 치환기를 함유하는 치환 또는 미치환된 아릴(aryl), 방향족 탄화수소기, C3-C8의 하나 이상의 치환기를 함유하는 치환 또는 미치환된 하나 이상의 헤테로 원자를 함유하는 헤테로아릴(heteroaryl)로부터 선택되고; 상기 치환은 할로겐 원소, C1-C4의 알킬로 치환되는 것을 특징으로 하는 카르바졸 및 피리딘 구성 유닛에 기초한 전계 발광 물질. - 제1항에 있어서,
여기에서, R1 및 R2는 독립적으로 수소, C1-C4 알킬, C6-C10의 하나 이상의 치환 또는 미치환된 아릴, 방향족 탄화수소기로부터 선택되고; 상기 치환은 할로겐 원소, C1-C4의 알킬로 치환되는 것을 특징으로 하는 전계 발광 물질. - 제2항에 있어서,
여기에서, R1 및 R2는 독립적으로 수소, 메틸(methyl), tert-부틸(tert-butyl), 페닐(phenyl), 톨릴(tolyl), 나프틸(naphthyl)로부터 선택되는 것을 특징으로 하는 전계 발광 물질. - 제3항에 있어서,
여기에서, R1 및 R2는 수소, tert-부틸, 페닐 및 메틸로부터 선택된 동일한 치환기인 것을 특징으로 하는 전계 발광 물질. - 제4항에 있어서,
여기에서, Ar은 하기 그룹이고
,
여기에서, R1 및 R2는 수소, tert-부틸, 페닐로부터 선택된 동일한 치환기인 것을 특징으로 하는 전계 발광 물질. - 제2항에 있어서,
여기에서 Ar은 하기 그룹 중 하나인 것을 특징으로 하는 전계 발광 물질.
- 제6항에 있어서,
R1은 수소이고, R2는 tert-부틸, 페닐, 톨릴, 나프틸인 것을 특징으로 하는 전계 발광 물질. - 제2항에 있어서,
상기 식 (I)의 구조는 하기 화합물 중의 하나인 것을 특징으로 하는 전계 발광 물질.
- 제8항에 있어서,
상기 식 (I)의 구조가 하기 화합물인 것을 특징으로 하는 전계 발광 물질.
- 유기 전계 발광 소자, 전계 발광 소자, 유기 전계 효과 트랜지스터, 유기 태양 전지 및 화학 센서에서의 제1항 내지 제9항 중 어느 한 항에 따른 물질의 응용.