KR20180086156A - A photo sensitive resin composition, a color filter comprising a black metrics, a column spacer or black column spacer prepared by using the composition, and a display devide comprising the color filter - Google Patents

A photo sensitive resin composition, a color filter comprising a black metrics, a column spacer or black column spacer prepared by using the composition, and a display devide comprising the color filter Download PDF

Info

Publication number
KR20180086156A
KR20180086156A KR1020180007276A KR20180007276A KR20180086156A KR 20180086156 A KR20180086156 A KR 20180086156A KR 1020180007276 A KR1020180007276 A KR 1020180007276A KR 20180007276 A KR20180007276 A KR 20180007276A KR 20180086156 A KR20180086156 A KR 20180086156A
Authority
KR
South Korea
Prior art keywords
resin composition
photosensitive resin
colored photosensitive
pigment
black
Prior art date
Application number
KR1020180007276A
Other languages
Korean (ko)
Other versions
KR101966803B1 (en
Inventor
이현보
권영수
이재을
조승현
김현우
이종수
Original Assignee
동우 화인켐 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 동우 화인켐 주식회사 filed Critical 동우 화인켐 주식회사
Publication of KR20180086156A publication Critical patent/KR20180086156A/en
Priority to KR1020190038356A priority Critical patent/KR102259147B1/en
Application granted granted Critical
Publication of KR101966803B1 publication Critical patent/KR101966803B1/en

Abstract

The present invention relates to a coloring photosensitive resin composition; a color filter comprising a black matrix, a column spacer or a black column spacer prepared by using the coloring photosensitive resin composition; and a display device comprising the color filter. An objective of the present invention is to provide a coloring photosensitive resin composition which has an excellent shading effect, i.e., optical properties, enables a curing process to be performed at low temperatures, and has excellent reliability and elastic recovery rate even when the coloring photosensitive resin composition comprises a high concentration coloring agent. The coloring photosensitive resin composition of the present invention comprises a coloring agent, an alkali soluble resin, a photopolymerizable compound, a photopolymerization initiator and a solvent. The coloring agent includes an organic black pigment, a blue pigment and a carbon black. The coloring photosensitive resin composition includes 25 to 55% of the coloring agent with respect to the total weight of a solid content and also comprises 3 to 25% of the organic black pigment, 5 to 25% of the blue pigment and 5 to 13% of the carbon black with respect to the total weight of the solid content.

Description

착색 감광성 수지 조성물, 이를 사용하여 제조된 블랙 매트릭스, 컬럼 스페이서 또는 블랙 컬럼 스페이서를 포함하는 컬러필터, 및 상기 컬러필터를 포함하는 표시장치{A PHOTO SENSITIVE RESIN COMPOSITION, A COLOR FILTER COMPRISING A BLACK METRICS, A COLUMN SPACER OR BLACK COLUMN SPACER PREPARED BY USING THE COMPOSITION, AND A DISPLAY DEVIDE COMPRISING THE COLOR FILTER}TECHNICAL FIELD [0001] The present invention relates to a colored photosensitive resin composition, a color filter including a black matrix, a column spacer or a black column spacer manufactured using the same, and a display device including the color filter COLUMN SPACER OR BLACK COLUMN SPACER PREPARED BY USING THE COMPOSITION, AND A DISPLAY DEVIDE COMPRISING THE COLOR FILTER}

본 발명은 유기 블랙 안료,청색 안료 및 카본블랙을 포함하는 착색제, 알칼리 가용성 수지, 광중합성 화합물, 광중합 개시제 및 용제를 포함하는 착색 감광성 수지 조성물, 상기 조성물을 이용하여 제조되는 컬러필터 및 상기 컬러필터를 포함하는 표시장치에 관한 것이다. The present invention relates to a colored photosensitive resin composition comprising an organic black pigment, a colorant containing a blue pigment and carbon black, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator and a solvent, a color filter manufactured using the composition, To a display device.

컬러필터는 촬상(撮像)소자, 액정표시장치(LCD) 등의 각종 표시장치에 널리 이용되는 것으로, 그 응용 범위가 급속히 확대되고 있다. 상기 촬상소자, 액정표시장치 등에 사용되는 컬러필터는 레드(Red), 그린(Green) 및 블루(Blue)의 3가지 컬러의 착색 패턴으로 이루어지거나, 옐로우(Yellow), 마젠타(Magenta) 및 시안(Cyan)의 3가지 컬러의 착색 패턴으로 이루어진다. BACKGROUND ART [0002] Color filters are widely used in various display devices such as an image pickup device and a liquid crystal display (LCD), and their application range is rapidly expanding. The color filter used in the image pickup device or the liquid crystal display device may be a color pattern of three colors of red, green and blue or a color pattern of three colors of yellow, magenta and cyan Cyan).

상기 컬러필터 각각의 착색 패턴은 일반적으로 안료 또는 염료 등의 착색제, 알칼리 가용성 수지, 광중합성 화합물, 광중합 개시제 및 용제를 포함하는 착색 감광성 수지 조성물을 이용하여 형성된다. 상기 착색 감광성 수지 조성물을 이용한 착색 패턴 가공은 통상적으로 리소그래피 공정으로 수행되고 있다. The coloring pattern of each of the color filters is generally formed using a colored photosensitive resin composition comprising a coloring agent such as pigment or dye, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator, and a solvent. The coloring pattern processing using the colored photosensitive resin composition is usually performed by a lithography process.

착색 감광성 수지는 컬러필터, 액정표시재료, 유기발광소자, 디스플레이 등의 필수적인 재료이다. 예로 컬러 액정 디스플레이의 컬러 필터에는 레드, 그린, 블루의 콘트라스트와 발색효과를 높이기 위해 착색 층간의 경계 부분에 흑색 감광성 조성물을 이용한 차광층을 형성한다. 또한 최근에는 어레이 기판상에 위치하여 블랙 매트릭스의 역할뿐만 아니라, 셀갭 유지용 스페이서도 형성하여 한번에 다양한 역할이 가능해 지도록 요구되고 있다. 이에 따라, 기본적인 차광을 위한 광학 효과뿐만 아니라, 탄성률 및 신뢰성이 좋은 특성을 필요로 한다. The colored photosensitive resin is an essential material such as a color filter, a liquid crystal display material, an organic light emitting element, and a display. For example, a color filter of a color liquid crystal display is provided with a light-shielding layer using a black photosensitive composition at a boundary portion between coloring layers to enhance the contrast, coloring effect of red, green and blue. In recent years, a spacer for cell gap is formed not only as a black matrix but also on an array substrate, and is required to have various roles at a time. Accordingly, not only the optical effect for the basic light shielding but also the characteristics of good elasticity and reliability are required.

이러한 요구에 맞추어 공개특허공보 제10-2010-0095633호에서는 착색제를 혼합하여 사용하여 차광성을 효과를 높인 감광성 수지 조성물이 기술되어 있다. 그러나, 종래기술로는 탄성률 및 신뢰성의 우수한 특성을 확보 하기 어려운 문제가 발생한다. 때문에, 우수한 차광 효과가 확보되면서도 신뢰성 및 탄성 회복률도 우수한 감광성 수지 조성물의 개발이 필요하다.In accordance with this demand, Japanese Patent Application Laid-Open No. 10-2010-0095633 discloses a photosensitive resin composition in which the effect of shielding light is enhanced by mixing and using a colorant. However, in the prior art, there arises a problem that it is difficult to ensure the excellent characteristics of the elastic modulus and the reliability. Therefore, it is necessary to develop a photosensitive resin composition which is excellent in light-shielding effect and also in reliability and elastic recovery rate.

대한민국 공개특허공보 제10-2010-0095633호Korean Patent Publication No. 10-2010-0095633

본 발명은, 상기 종래 기술의 문제를 해결하기 위하여 안출된 것으로서, 차광 효과 즉, 광특성이 우수하고, 저온경화가 가능하며, 고농도의 착색제를 포함하는 경우에도 신뢰성 및 탄성회복률이 우수한 착색 감광성 수지 조성물을 제공하는 것을 목적으로 한다. SUMMARY OF THE INVENTION The present invention has been conceived to solve the above problems of the prior art, and it is an object of the present invention to provide a color photosensitive resin composition which is excellent in light-shielding effect, that is, excellent in optical characteristics, capable of low-temperature curing, And to provide a composition.

또한, 본 발명은 착색 감광성 수지 조성물로 제조된 블랙 매트릭스, 컬럼 스페이서 또는 블랙 컬럼 스페이서를 포함하는 컬러필터 상기 컬러 필터를 포함하는 표시장치를 제공하는 것을 목적으로 한다.It is another object of the present invention to provide a color filter comprising a black matrix, a column spacer or a black column spacer made of a colored photosensitive resin composition.

본 발명은 The present invention

착색제, 알칼리 가용성 수지, 광중합성 화합물, 광중합 개시제 및 용제를 포함하는 착색 감광성 수지 조성물로,A colored photosensitive resin composition comprising a colorant, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator, and a solvent,

상기 착색제는 유기 블랙 안료, 청색 안료 및 카본 블랙을 포함하며, Wherein the colorant comprises an organic black pigment, a blue pigment and carbon black,

상기 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여 착색제 25~55%를 포함하며, And 25 to 55% of a colorant based on the total solid weight of the colored photosensitive resin composition,

상기 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여, 상기 유기 블랙 안료 3~25%, 상기 청색 안료 5~25%, 및 상기 카본 블랙 5~13% 를 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물을 제공한다.Based on the total solid weight of the colored photosensitive resin composition, 3 to 25% of the organic black pigment, 5 to 25% of the total weight of the colored photosensitive resin composition, and 5 to 13% of the carbon black.

본 발명은 상술한 착색 감광성 수지 조성물로 제조된 블랙 매트릭스, 컬럼 스페이서 또는 블랙 컬럼 스페이서를 포함하는 컬러 필터를 제공한다.The present invention provides a color filter comprising a black matrix, a column spacer, or a black column spacer made of the above-mentioned colored photosensitive resin composition.

본 발명은 상술한 컬러 필터를 포함하는 표시장치를 제공한다. The present invention provides a display device including the color filter described above.

본 발명은 광특성이 우수하고, 저온경화가 가능하며, 고농도의 착색제를 포함하는 경우에도 신뢰성 및 탄성회복률이 우수한 착색 감광성 수지 조성물을 제공 한다. The present invention provides a colored photosensitive resin composition excellent in optical characteristics, capable of low-temperature curing, and excellent in reliability and elastic recovery even when a high-concentration colorant is contained.

이하, 본 발명을 보다 자세히 설명한다.Hereinafter, the present invention will be described in more detail.

본 발명은, 착색제, 알칼리 가용성 수지, 광중합성 화합물, 광중합 개시제 및 용제를 포함하는 착색 감광성 수지 조성물로, The present invention relates to a colored photosensitive resin composition comprising a colorant, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator and a solvent,

상기 착색제는 유기 블랙 안료, 청색 안료 및 카본 블랙을 포함하며, Wherein the colorant comprises an organic black pigment, a blue pigment and carbon black,

상기 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여 착색제 25~55%를 포함하며, And 25 to 55% of a colorant based on the total solid weight of the colored photosensitive resin composition,

상기 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여, 상기 유기 블랙 안료 3~25%, 상기 청색 안료 5~25%, 및 상기 카본 블랙 5~13% 를 포함하는 포함함으로써 광특성이우수하고, 저온경화가 가능하며, 고농도의 착색제를 포함하는 경우에도 신뢰성 및 탄성회복률이 우수한 착색 감광성 수지 조성물 제공한다.Based on the total solid weight of the colored photosensitive resin composition, 3 to 25% of the organic black pigment, 5 to 25%, and 5 to 13% of the carbon black, thereby providing a colored photosensitive resin composition which is excellent in reliability and elastic recovery even when a high concentration of colorant is contained.

이하, 본 발명의 착색 감광성 수지 조성물을 구성하는 각 성분에 대하여 설명한다.        Each component constituting the colored photosensitive resin composition of the present invention will be described below.

착색제coloring agent

본 발명에서 착색제는 가시광선에 차광성이 있는 것을 사용하며, 본 발명의 착색제는 유기 블랙 안료, 청색 안료 및 카본블랙을 포함한다.The colorant used in the present invention is one which is shielding against visible light, and the colorant of the present invention includes an organic black pigment, a blue pigment, and carbon black.

상기 유기 블랙 안료는 락탐 블랙, 아닐린 블랙 및 페릴렌 블랙으로 이루어진 군으로부터 선택되는 1종 이상을 포함하며, 바람직하게는 락탐 블랙을 포함한다. 보다 구체적으로 유기 블랙 안료는 100CF(Basf 社) 등일 수 있다. 상기 유기 블랙 안료를 포함함으로써 광학밀도를 향상시킬 수 있고, 유전율 및 투과도 측면에서도 유리하다.The organic black pigment includes at least one member selected from the group consisting of lactam black, aniline black and perylene black, and preferably includes lactam black. More specifically, the organic black pigment may be 100 CF (Basf) or the like. By including the organic black pigment, the optical density can be improved, which is also advantageous in terms of dielectric constant and transmittance.

또한, 상기 청색 안료는 중심 금속을 포함하지 않는 화합물로, 상기 중심 금속을 포함하지 않는 청색 안료를 사용함으로써 공정상에 사용되는 액정과 접촉시 문제를 야기시키지 않아, 장비 구동에 이점을 확보할 수 있다. 본 발명에서 상기 청색 안료는 중심 금속을 포함하지 않는 화합물이라면 그 종류를 특별히 한정하는 것은 아니나, C.I. 피그먼트 블루 16, 60, 61 및/또는 66등으로 선택되는 1종 이상을 사용하는 것이 바람직하며, C.I. 피그먼트 블루 60을 사용하는 것이 더 바람직하다. The blue pigment is a compound which does not contain a center metal. By using a blue pigment which does not include the center metal, it does not cause a problem in contact with the liquid crystal used in the process, have. In the present invention, the type of the blue pigment is not particularly limited as long as it is a compound that does not include a center metal. Pigment Blue 16, 60, 61 and / or 66 is preferably used, and C.I. Pigment Blue 60 is more preferably used.

상기 카본블랙을 포함하는 경우 광학 밀도가 우수해 지는 효과를 얻을 수 있다. When the carbon black is included, an effect of improving the optical density can be obtained.

본 발명은 추가로 바이올렛 안료 및 레드 안료 중 어느 하나 이상을 포함할 수 있다. The present invention may further include at least one of a violet pigment and a red pigment.

상기 바이올렛 안료는 400 내지 600nm 영역에서 투과율을 감소시켜 광학밀도(optical density, O.D)를 향상시키는 역할을 한다. 또한, 상기 바이올렛 안료의 사용을 통하여 유기 블랙 안료의 함량을 줄일 수 있어, 착색 감광성 수지 조성물의 신뢰성을 향상시킬 수 있다. 상기 바이올렛 안료는 그 종류를 특별히 한정하는 것은 아니나, C.I. 피그먼트 바이올렛 14, 19, 23, 29, 32, 33, 36 및/ 또는 37등으로 구성되는 군으로 부터 선택되는 1종 이상을 사용하는 것이 바람직하며, C.I. 피그먼트 바이올렛 29를 사용 하는 것이 더 바람직하다. The violet pigment serves to improve the optical density (O.D.) by reducing the transmittance in the region of 400 to 600 nm. In addition, the content of the organic black pigment can be reduced through the use of the violet pigment, and the reliability of the colored photosensitive resin composition can be improved. The type of the violet pigment is not particularly limited, but C.I. Pigment Violet 14, 19, 23, 29, 32, 33, 36 and / or 37, and preferably at least one selected from the group consisting of C.I. It is more preferable to use Pigment Violet 29.

상기 레드 안료는 광밀도를 향상시키는 역할을 한다. 상기 레드 안료는 그 종류를 특별히 한정하는 것은 아니나, C.I. 피그먼트 레드 9, 97, 105, 122, 123, 144, 149, 166, 168, 176, 177, 180, 192, 208, 215, 216, 224, 242, 254, 255 및 264 등을 들 수 있다. The red pigment serves to improve the optical density. The kind of the red pigment is not particularly limited, but C.I. Pigment Red 9, 97, 105, 122, 123, 144, 149, 166, 168, 176, 177, 180, 192, 208, 215, 216, 224, 242, 254, 255 and 264.

본 발명에서 상기 착색제는 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여 25 내지 55 중량%로 포함되며, 바람직하게는 28 내지 50 중량%로 포함된다. 상기 착색제가 상기 범위 내로 포함되면 광학 밀도가 우수해지는 효과를 얻을 수 있다.In the present invention, the colorant is contained in an amount of 25 to 55% by weight, and preferably 28 to 50% by weight based on the total weight of the solid content of the colored photosensitive resin composition. When the colorant is contained within the above range, an effect of improving the optical density can be obtained.

상기 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여, 상기 유기 블랙 안료 3~25%, 상기 청색 안료 5~25%, 및 상기 카본 블랙 5~13% 를 포함할 수 있으며, 상기 유기 블랙 안료 8~20%, 상기 청색 안료 8~22%, 및 상기 카본 블랙 6~11%로 포함될 경우 보다 바람직 하다. Based on the total solid weight of the colored photosensitive resin composition, 3 to 25% of the organic black pigment, 5 to 25% of the organic black pigment, and 5 to 13% of the carbon black, and 8 to 20% of the organic black pigment, 8 to 22%, and 6 to 11% of the carbon black.

상기 유기 블랙안료를 상기 범위 내로 포함할 경우,400~600nm 범위의 광특성에 문제가 발생하지 않으며, 신뢰성이 우수해 진다는 점에서 바람직하다. 또한 청색 안료를 상기 범위 내로 포함할 경우, 광학 밀도가 우수한 착색 감광성 수지 조성물을 얻을 수 있으며, 700~750nm 범위 및 400~600nm범위의 광특성에 문제가 발생하지 않는 다는 점에서 바람직하다. When the organic black pigment is contained within the above range, it is preferable that the organic black pigment does not cause problems in the optical characteristics in the range of 400 to 600 nm and that the reliability is excellent. When the blue pigment is contained in the above range, a colored photosensitive resin composition having an excellent optical density can be obtained, and it is preferable from the viewpoint that no problems occur in the range of 700 to 750 nm and in the range of 400 to 600 nm.

상기 카본블랙을 상기 범위 내로 포함할 경우 광학밀도가 우수해 지며, 400~600nm 범위 및 950nm 범위에서의 광특성에 문제가 발생하지 않는 다는 점에서 바람직 하다. When the carbon black is contained within the above range, the optical density becomes excellent and it is preferable in that no problem occurs in the optical characteristics in the range of 400 to 600 nm and the range of 950 nm.

본 발명은 추가 착색제로서 바이올렛 안료 및 레드 안료 중 어느 하나 이상을 더 포함할 수 있으며, 바이올렛 안료를 더 포함할 경우 광학밀도 및 신뢰성이 보다 우수한 효과를 갖는 착색 감광성 수지 조성물을 얻을 수 있다. 또한 레드 안료를더 포함할 경우 광특성이 향상 될 수 있다. The present invention may further comprise at least one of a violet pigment and a red pigment as an additional colorant, and when the colorant further contains a violet pigment, a colored photosensitive resin composition having an effect of better optical density and reliability can be obtained. Further, when the red pigment is further included, the optical characteristics can be improved.

상기 바이올렛 안료는 조성물에 포함된 고형분 총 중량에 대하여 3~15 중량%로 포함되는 것이 바람직하다. 상기 바이올렛 안료가 상기 중량비로 포함되면 광학 밀도 및 신뢰성이 우수한 착색 감광성 수지 조성물을 얻을 수 있다. The violet pigment is preferably contained in an amount of 3 to 15% by weight based on the total weight of solids contained in the composition. When the violet pigment is contained in the above weight ratio, a colored photosensitive resin composition excellent in optical density and reliability can be obtained.

상기 레드 안료는 조성물에 포함된 고형분 총 중량에 대하여 3~15 중량%로 포함되는 것이 바람직하다. 상기 레드 안료가 상기 중량비로 포함되면 광학 밀도 및 신뢰성이 우수한 착색 감광성 수지 조성물을 얻을 수 있다. The red pigment is preferably contained in an amount of 3 to 15% by weight based on the total weight of solids contained in the composition. When the red pigment is contained in the above weight ratio, a colored photosensitive resin composition excellent in optical density and reliability can be obtained.

보다 구체적으로, 본 발명은 상기 착색 감광성 수지 조성물 중 유기 블랙안료: 청색 안료: 카본 블랙의 중량비는 1: 0.25 내지 3.3: 0.15 내지 1.7 로 혼합될 수 있다. 상기 범위 내로 혼합될 경우 혼합시 광 특성이 우수해 질 수 있으며, Near-IR에서 우수한 효과를 달성할 수 있다는 점에서 바람직하다.  More specifically, the weight ratio of the organic black pigment: blue pigment: carbon black in the colored photosensitive resin composition may be 1: 0.25 to 3.3: 0.15 to 1.7. When mixed within the above-mentioned range, the optical characteristics can be improved when mixed, and it is preferable in that the excellent effect can be achieved in Near-IR.

또한, 추가 착색제를 포함할 경우, 상기 착색 감광성 수지 조성물 중 유기 블랙안료: 레드 안료 및 바이올렛 안료 중 하나 이상: 청색 안료: 카본 블랙의 중량비는 1: 0.1 내지 1.7: 0.25 내지 3.3: 0.15 내지 1.7 로 혼합될 수 있으며, 상기 범위 내로 혼합될 경우 광특성 및 광학밀도가 우수해 질 수 있다는 점에서 바람직하다. When the coloring photosensitive resin composition contains the additional colorant, the weight ratio of at least one of the organic black pigment: red pigment and violet pigment: blue pigment: carbon black in the colored photosensitive resin composition is 1: 0.1 to 1.7: 0.25 to 3.3: 0.15 to 1.7 And it is preferable in that the optical characteristics and the optical density can be excellent when mixed within the above range.

본 발명에서 착색 감광성 수지 조성물 중 고형분이란, 용제를 제거한 성분의 합계를 의미한다.In the present invention, the solid content in the colored photosensitive resin composition means the sum of the components from which the solvent has been removed.

또한, 상기 착색제는 안료의 입경이 균일하게 분산된 안료 분산액을 사용하는 것이 바람직하다. 안료의 입경을 균일하게 분산시키기 위한 방법의 예로는 안료 분산제(a1)를 함유시켜 분산 처리하는 방법 등을 들 수 있으며, 상기 방법에 따라 안료가 용액 중에 균일하게 분산된 상태의 안료 분산액을 얻을 수 있다.In addition, it is preferable to use a pigment dispersion in which the particle diameter of the pigment is uniformly dispersed. Examples of a method for uniformly dispersing the particle diameter of the pigment include a method of dispersing the pigment dispersion (a1) by containing the pigment dispersant (a1), and a method of obtaining a pigment dispersion in which the pigment is uniformly dispersed in the solution have.

(a1)안료 분산제(a1) pigment dispersant

상기 안료 분산제는 안료의 탈응집 및 안정성 유지를 위해 첨가하는 것으로 안료 분산제의 구체적인 예로는 양이온계, 음이온계, 비이온계, 양성계, 폴리에스테르계, 폴리아민계 등의 계면활성제 등을 들 수 있고, 이들은 각각 단독 또는 2종 이상을 조합하여 사용할 수 있다.The pigment dispersant is added for deaggregation of the pigment and maintenance of stability. Specific examples of the pigment dispersant include a cationic surfactant, an anionic surfactant, a nonionic surfactant, a positive surfactant, a polyester surfactant, and a polyamine surfactant. , Which may be used alone or in combination of two or more.

상기 양이온계 계면 활성제의 구체적인 예로는 스테아릴아민염산염 및 라우릴트리메틸암모늄클로라이드 등의 아민염 또는 4급 암모늄염 등을 들 수 있다. Specific examples of the cationic surfactant include amine salts such as stearylamine hydrochloride and lauryltrimethylammonium chloride, and quaternary ammonium salts.

상기 음이온계 계면 활성제의 구체적인 예로는 라우릴알코올황산에스테르나트륨 및 올레일알코올황산에스테르나트륨 등의 고급 알코올 황산에스테르염류, 라우릴황산나트륨 및 라우릴황산암모늄 등의 알킬황산염류, 도데실벤젠술폰산나트륨 및 도데실나프탈렌술폰산나트륨 등의 알킬아릴술폰산염류 등을 들 수 있다.Specific examples of the anionic surfactant include higher alcohol sulfuric acid ester salts such as sodium lauryl alcohol sulfate ester and sodium oleyl alcohol sulfate ester, alkylsulfates such as sodium laurylsulfate and ammonium laurylsulfate, sodium dodecylbenzenesulfonate, And alkylarylsulfonic acid salts such as sodium dodecylnaphthalenesulfonate.

상기 비이온계 계면 활성제의 구체적인 예로는 폴리옥시에틸렌알킬에테르, 폴리옥시에틸렌아릴에테르, 폴리옥시에틸렌알킬아릴에테르, 그 밖의 폴리옥시에틸렌 유도체, 옥시에틸렌/옥시프로필렌 블록 공중합체, 소르비탄지방산에스테르, 폴리옥시에틸렌소르비탄지방산에스테르, 폴리옥시에틸렌소르비톨지방산에스테르, 글리세린지방산에스테르, 폴리옥시에틸렌지방산에스테르 및 폴리옥시에틸렌알킬아민 등을 들 수 있다.Specific examples of the nonionic surfactants include polyoxyethylene alkyl ethers, polyoxyethylene aryl ethers, polyoxyethylene alkyl aryl ethers, other polyoxyethylene derivatives, oxyethylene / oxypropylene block copolymers, sorbitan fatty acid esters, Polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol fatty acid esters, glycerin fatty acid esters, polyoxyethylene fatty acid esters, and polyoxyethylene alkylamines.

그 외에 폴리옥시에틸렌알킬에테르류, 폴리옥시에틸렌 알킬페닐에테르류, 폴리에틸렌글리콜디에스테르류, 소르비탄지방산에스테르류, 지방산변성폴리에스테르류, 3급아민변성폴리우레탄류 및 폴리에틸렌이민류 등을 들 수 있다.In addition, polyoxyethylene alkyl ethers, polyoxyethylene alkylphenyl ethers, polyethylene glycol diesters, sorbitan fatty acid esters, fatty acid modified polyesters, tertiary amine-modified polyurethanes, and polyethyleneimines have.

또한, 상기 안료분산제는 부틸메타아크릴레이트(BMA) 또는 N,N-디메틸아미노에틸메타아크릴레이트(DMAEMA)를 포함하는 아크릴레이트계 분산제 (이하, 아크릴레이트계 분산제)를 포함하는 것이 바람직하다. 상기 아크릴레이트계 분산제는 리빙 제어방법에 의해 제조된 것을 사용하는 것이 바람직하며, 시판품으로는 DISPER BYK-2000, DISPER BYK-2001, DISPER BYK-2070 또는 DISPER BYK-2150 등을 들 수 있으며, 상기 아크릴레이트계 분산제는 각각 단독 또는 2종 이상을 혼합하여 사용할 수 있다.Also, the pigment dispersant preferably includes an acrylate-based dispersant (hereinafter referred to as an acrylate-based dispersant) containing butyl methacrylate (BMA) or N, N-dimethylaminoethyl methacrylate (DMAEMA). Dispersing BYK-2000, DISPER BYK-2001, DISPER BYK-2070, DISPER BYK-2150 and the like may be used as the acrylate-based dispersing agent, The rate-based dispersing agents may be used alone or in combination of two or more.

상기 안료 분산제는 아크릴레이트계 분산제 이외에 다른 수지 타입의 안료 분산제를 사용할 수도 있다. 상기 다른 수지 타입의 안료 분산제로는 공지된 수지 타입의 안료 분산제, 특히 폴리우레탄, 폴리아크릴레이트로 대표되는 폴리카르복실산에스테르, 불포화폴리아미드, 폴리카르복실산, 폴리카르복실산의 (부분적)아민 염, 폴리카르복실산의 암모늄 염, 폴리카르복실산의 알킬아민 염, 폴리실록산, 장쇄 폴리아미노아미드 포스페이트 염, 히드록실기-함 폴리카르복실산의 에스테르 및 이들의 개질 생성물, 또는 프리(free) 카르복실기를 갖는 폴리에스테르와 폴리(저급 알킬렌이민)의 반응에 의해 형성된 아미드 또는 이들의 염과 같은 유질의 분산제; (메트)아크릴산-스티렌 코폴리머, (메트)아크릴산-(메트)아크릴레이트 에스테르 코폴리머, 스티렌-말레산 코폴리머, 폴리비닐 알코올 또는 폴리비닐 피롤리돈과 같은 수용성 수지 또는 수용성 폴리머 화합물; 폴리에스테르; 개질 폴리아크릴레이트; 에틸렌 옥사이드/프로필렌 옥사이드의 부가생성물; 및 포스페이트 에스테르 등을 들 수 있다. As the pigment dispersant, other resin type pigment dispersants other than the acrylate dispersant may be used. The other resin type pigment dispersing agent may be a known resin type pigment dispersing agent, especially a polycarboxylic acid ester such as polyurethane, polyacrylate, unsaturated polyamide, polycarboxylic acid, polycarboxylic acid (partial) Amine salts of polycarboxylic acids, alkylamine salts of polycarboxylic acids, polysiloxanes, long chain polyaminoamide phosphate salts, esters of hydroxyl group-containing polycarboxylic acids and their modified products, or free ) Oil-based dispersants such as amides formed by reaction of a polyester having a carboxyl group with poly (lower alkyleneimine) or salts thereof; Soluble resin or water-soluble polymer compound such as (meth) acrylic acid-styrene copolymer, (meth) acrylic acid- (meth) acrylate ester copolymer, styrene-maleic acid copolymer, polyvinyl alcohol or polyvinylpyrrolidone; Polyester; Modified polyacrylates; Adducts of ethylene oxide / propylene oxide; And phosphate esters.

상기 다른 수지타입의 안료 분산제의 시판품으로는 양이온계 수지 분산제로서는, 예를 들면, BYK(빅) 케미사의 상품명: DISPER BYK-160, DISPER BYK-161, DISPER BYK-162,DISPER BYK-163, DISPER BYK-164, DISPER BYK-166, DISPER BYK-171, DISPER BYK-182,DISPER BYK-184; BASF사의 상품명: EFKA-44, EFKA-46, EFKA-47, EFKA-48,EFKA-4010, EFKA-4050, EFKA-4055, EFKA-4020, EFKA-4015, EFKA-4060, EFKA-4300, EFKA-4330, EFKA-4400, EFKA-4406, EFKA-4510, EFKA-4800 ; Lubirzol사의 상품명:SOLSPERS-24000, SOLSPERS-32550, NBZ-4204 /10; 카와켄 파인 케미컬사의 상품명: 히노액트(HINOACT) T-6000, 히노액트 T-7000, 히노액트 T-8000; 아지노모토사의 상품명: 아지스퍼(AJISPUR) PB-821, 아지스퍼 PB-822, 아지스퍼 PB-823; 쿄에이샤 화학사의 상품명: 플로렌 (FLORENE) DOPA-17HF, 플로렌 DOPA-15BHF, 플로렌 DOPA-33, 플로렌 DOPA-44 등을 들 수 있다. DISPER BYK-160, DISPER BYK-161, DISPER BYK-162, DISPER BYK-163, and DISPER BYK-160 available from BYK (Big) Chemie are examples of commercially available pigment dispersants of other resin types. BYK-164, DISPER BYK-166, DISPER BYK-171, DISPER BYK-182, DISPER BYK-184; EFKA-4060, EFKA-4060, EFKA-4055, EFKA-4055, EFKA-4055, EFKA-4020, EFKA-4015, EFKA-4060, EFKA- 4330, EFKA-4400, EFKA-4406, EFKA-4510, EFKA-4800; SOLSPERS-24000, SOLSPERS-32550, NBZ-4204/10 from Lubirzol; Hinoact T-6000, Hinoact T-7000, Hinoact T-8000; available from Kawaken Fine Chemicals; AJISPUR PB-821, Ajisper PB-822, Ajisper PB-823 manufactured by Ajinomoto; FLORENE DOPA-17HF, fluorene DOPA-15BHF, fluorene DOPA-33, and fluorene DOPA-44 are trade names of Kyoeisha Chemical Co.,

상기한 아크릴레이트계 분산제 이외에 다른 수지 타입의 안료 분산제는 각각 단독 또는 2종 이상을 혼합하여 사용할 수 있으며, 아크릴레이트계 분산제와 병용하여 사용할 수도 있다.In addition to the acrylate-based dispersant, other resin-type pigment dispersants may be used alone or in combination of two or more, and may be used in combination with an acrylate-based dispersant.

상기 안료 분산제는 착색제 1 중량부에 대하여, 0 초과 1 중량부 이하로 포함되며, 바람직하게는 0.05 내지 0.5 중량부로 포함된다. 상기의 0 초과 1 중량부 이하로 안료 분산제가 포함되면, 균일하게 분산된 안료를 얻을 수 있으므로 바람직하다.The pigment dispersant is contained in an amount of more than 0 to 1 part by weight, preferably 0.05 to 0.5 part by weight based on 1 part by weight of the colorant. When the pigment dispersant is contained in an amount exceeding 0 to 1 part by weight, the uniformly dispersed pigment can be obtained.

(B)알칼리 가용성 수지(B) an alkali-soluble resin

상기 알칼리 가용성 수지는 통상적으로 착색 감광성 수지 조성물을 이용하여 형성된 착색 감광성 수지층의 비노광부를 알칼리 가용성으로 만들고, 착색제에 대한 결합제 수지 및 분산 매질로도 작용한다.The alkali-soluble resin usually makes the unexposed portion of the colored photosensitive resin layer formed using the colored photosensitive resin composition alkali-soluble, and also acts as a binder resin and a dispersing medium for the coloring agent.

상기 알칼리 가용성 수지는 컬러필터의 제조를 위한 현상 단계에서 사용된 알칼리성 현상액에 용해 가능한 중합체라면 특별히 제한 없이 사용할 수 있으나, 본 발명에서는 에폭시기를 포함하는 알칼리 가용성 수지를 사용하는 것이 바람직하다.The alkali-soluble resin may be any polymer as long as it is soluble in the alkaline developer used in the development step for the production of the color filter. However, in the present invention, it is preferable to use an alkali-soluble resin containing an epoxy group.

상기 알칼리 가용성 수지는 예를 들면 에폭시기를 포함하는 단량체, 및 상기 단량체와 공중합 가능한 다른 단량체와의 공중합체 등을 들 수 있다.The alkali-soluble resin includes, for example, a copolymer of a monomer containing an epoxy group and another monomer copolymerizable with the monomer.

상기 에폭시기를 포함하는 단량체는 구체적으로 예를 들어, 3,4-에폭시트리시클로[5.2.1.0,2,6]데칸-9-일아크릴레이트, 3,4-에폭시트리시클로[5.2.1.0,2,6]데칸-8-일아크릴레이트, 글리디실 메타아크릴레이트 및 4-하이드록시부틸 아크릴레이트 글리시딜에테르 등을 들 수 있다.Specific examples of the monomer containing an epoxy group include 3,4-epoxytricyclo [5.2.1.0,2,6] decan-9-yl acrylate, 3,4-epoxytricyclo [5.2.1.0 , 6] decan-8-yl acrylate, glycidyl methacrylate and 4-hydroxybutyl acrylate glycidyl ether.

상기 에폭시기를 포함하는 단량체와 공중합 가능한 다른 단량체로는 구체적으로 예를 들어, 불포화 카르복실산 아미노알킬에스테르류, 불포화 카르복실산 글리시딜에스테르류, 카르복실산 비닐에스테르류, 불포화에테르류, 시안화 비닐 화합물, 불포화 아미드류, 불포화이미드류, 지방족 공액 디엔류 및 폴리실록산의 중합체 분자쇄의 말단에 모노아클릴로일기 또는 모노메타크릴로일기를 갖는 거대 단량체류를 들 수 있으며, 이들 단량체는 각각 단독 또는 2종 이상을 혼합하여 사용할 수 있다.Specific examples of the other monomer copolymerizable with the monomer containing an epoxy group include unsaturated carboxylic acid aminoalkyl esters, unsaturated carboxylic acid glycidyl esters, carboxylic acid vinyl esters, unsaturated ethers, Vinyl monomers, vinyl monomers, vinyl compounds, unsaturated amides, unsaturated imides, aliphatic conjugated dienes and polysiloxanes having monoacyloyl groups or monomethacryloyl groups at the ends of the polymer molecular chain, Two or more species may be used in combination.

상기 알칼리 가용성 수지의 중량평균분자량은 3,000 내지 20,000이며, 바람직하게는 5,000 내지 15,000이다.The weight average molecular weight of the alkali-soluble resin is 3,000 to 20,000, preferably 5,000 to 15,000.

또한, 상기 알칼리 가용성 수지의 산가는 고형분 기준으로 50 내지 200mgKOH/g으로, 상기 범위 안에서 알칼리 현상에 대한 현상성이 우수하며, 잔사발생을 억제하고, 패턴의 밀착성을 향상시킬 수 있다.In addition, the acid value of the alkali-soluble resin is 50 to 200 mgKOH / g based on the solid content, and the developability against the alkali development in the above range is excellent, the occurrence of the residue can be suppressed and the adhesion of the pattern can be improved.

상기 알칼리 가용성 수지는 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여 5 내지 60 중량%로 포함되며, 20 내지 50 중량%로 포함되는 것이 바람직하다. 상기 알칼리 가용성 수지의 함량이 상기한 범위 이내이면 패턴 형성이 용이하고, 해상도 및 잔막율이 향상되므로 때문에 바람직하다.The alkali-soluble resin is contained in an amount of 5 to 60% by weight, preferably 20 to 50% by weight based on the total weight of the solid content of the colored photosensitive resin composition. When the content of the alkali-soluble resin is within the above-mentioned range, pattern formation is easy and resolution and residual film ratio are improved.

(C) (C) 광중합성Photopolymerization 화합물 compound

상기 (C)광중합성 화합물은 광중합 개시제의 작용으로 중합할 수 있는 화합물로, 3~10관능성 단량체 바람직하게는 4~8관능성 단량체를 포함할 수 있다. The above-mentioned (C) photopolymerizable compound is a compound capable of polymerizing under the action of a photopolymerization initiator, and may contain 3 to 10 functional monomers, preferably 4 to 8 functional monomers.

상기 단관능성 단량체의 구체적인 예로는, 노닐페닐카르비톨아크릴레이트, 2-히드록시-3-페녹시프로필아크릴레이트, 2-에틸헥실카르비톨아크릴레이트, 2-히드록시에틸아크릴레이트 및 N-비닐피롤리돈 등을 들 수 있으나 이에 한정되는 것은 아니다.Specific examples of the monofunctional monomers include nonylphenylcarbitol acrylate, 2-hydroxy-3-phenoxypropyl acrylate, 2-ethylhexylcarbitol acrylate, 2-hydroxyethyl acrylate and N- But are not limited thereto.

상기 3~10관능성 단량체의 구체적인 예로는, 트리메틸올 프로판트리(메타) 아크릴레이트, 에톡실레이티드트리메틸올프로판트리(메타)아크릴레이트, 프로폭실레이티드트리메틸올프로판트리(메타)아크릴레이트, 펜타에리스리톨트리 (메타)아크릴레이트, 펜타에리스리톨테트라(메타)아크릴레이트, 디펜타에리스 리톨펜타(메타)아크릴레이트, 에톡실레이티드디펜타에리스리톨헥사(메타)아크릴 레이트, 프로폭실레이티드디펜타에리스리톨헥사(메타)아크릴레이트 및 디펜타 에리스리톨헥사(메타)아크릴레이트 등을 들 수 있으나 이에 한정되는 것은 아니다. Specific examples of the above-mentioned 3 to 10 functional monomers include trimethylolpropane tri (meth) acrylate, ethoxylated trimethylolpropane tri (meth) acrylate, propoxylated trimethylolpropane tri (meth) acrylate, (Meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, ethoxylated dipentaerythritol hexa Hexa (meth) acrylate, and dipentaerythritol hexa (meth) acrylate, but are not limited thereto.

3관능성 단량체의 구체적인 예로는, 1,6-헥산디올디(메타)아크릴레이트, 에틸렌글리콜디(메타)아크릴레이트, 네오펜틸글리콜디(메타)아크릴레이트, 트리에틸렌글리콜디(메타)아크릴레이트, 비스페놀A의 비스(아크릴로일옥시에틸)에테르, 3-메틸펜탄디올디(메타)아크릴레이트 등을 들 수 있다.Specific examples of the trifunctional monomer include 1,6-hexanediol di (meth) acrylate, ethylene glycol di (meth) acrylate, neopentyl glycol di (meth) acrylate, triethylene glycol di (meth) , Bis (acryloyloxyethyl) ether of bisphenol A, 3-methylpentanediol di (meth) acrylate, and the like.

４관능성 단량체의 구체적인 예로는 펜타에리트리톨테트라아크릴레이트, 펜타에리트리톨테트라메타크릴레이트, 디트리메티롤프로판테트라아크릴레이트, 디트리메티롤프로판테트라메타크릴레이트, 디펜타에리트리톨테트라아크릴레이트, 테트라메틸올메탄테트라아크릴레이트, 에톡시화펜타에리트리톨테트라아크릴레이트, 글리세린테트라아크릴레이트, 글리세린테트라메타크릴레이트 등을 들 수 있다.Specific examples of the tetrafunctional monomer include pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, ditrimethylol propane tetraacrylate, ditrimethylol propane tetramethacrylate, dipentaerythritol tetraacrylate, Tetramethylolmethane tetraacrylate, ethoxylated pentaerythritol tetraacrylate, glycerin tetraacrylate, glycerin tetramethacrylate, and the like.

５관능성 단량체의 구체적인 예로는 디펜타에리트리톨펜타크릴레이트, 디펜타에리트리톨펜타메타크릴레이트, 디펜타에리트리톨모노히드록시펜타아크릴레이트, 디펜타에리트리톨모노히드록시펜타메타크릴레이트 등을 들 수 있다.Specific examples of the pentafunctional monomer include dipentaerythritol pentaacrylate, dipentaerythritol penta methacrylate, dipentaerythritol monohydroxypentaacrylate, dipentaerythritol monohydroxypentamethacrylate, and the like. .

６관능성 단량체의 구체적인 예로는 디펜타에리트리톨헥사아크릴레이트, 디펜타에리트리톨헥사메타크릴레이트 등을 들 수 있다. Specific examples of the hexafunctional monomer include dipentaerythritol hexaacrylate, dipentaerythritol hexa methacrylate, and the like.

이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다.These may be used alone or in combination of two or more.

본 발명에서 상기 “(메타)아크릴레이트”는 “아크릴레이트” 또는 “메타크릴레이트”를 의미한다.In the present invention, the term "(meth) acrylate" means "acrylate" or "methacrylate".

상기 광중합성 화합물은 본 발명의 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여 5 내지 50 중량%로 포함되며, 7 내지 45 중량%로 포함되는 것이 바람직하다. 상기 광중합성 화합물은 상기 5 내지 50 중량% 범위에서 화소부의 강도나 평탄성을 양호하게 할 수 있다  The photopolymerizable compound is included in the colored photosensitive resin composition of the present invention in an amount of 5 to 50% by weight, preferably 7 to 45% by weight based on the total weight of the solid component. The photopolymerizable compound can improve the strength and flatness of the pixel portion in the range of 5 to 50% by weight

또한, 본 발명의 알칼리 가용성 수지와 광중합성 화합물은 1:1 내지 5:1의 중량비로 혼합되며, 바람직하게는 1.2:1 내지 3.7:1의 중량비로 혼합된다. 상기 알칼리 가용성 수지와 광중합성 화합물이 1:1 내지 5:1의 중량비로 혼합되면 공정성이 향상되며, 패턴 형성이 용이한 착색 감광성 수지 조성물을 제공할 수 있다.In addition, the alkali-soluble resin and the photopolymerizable compound of the present invention are mixed in a weight ratio of 1: 1 to 5: 1, and preferably in a weight ratio of 1.2: 1 to 3.7: 1. When the alkali-soluble resin and the photopolymerizable compound are mixed at a weight ratio of 1: 1 to 5: 1, the processability is improved, and a colored photosensitive resin composition that can easily form a pattern can be provided.

(D)(D) 광중합Light curing 개시제Initiator

상기 광중합 개시제는 광중합성 화합물을 중합시킬 수 있는 것이라면 제한없이 사용할 수 있으나, 바람직하게는 중합특성, 개시효율, 흡수파장, 입수성, 가격 등을 고려하여 아세토페논계 화합물, 벤조인계 화합물, 벤조페논계 화합물, 트리아진계 화합물, 비이미다졸계 화합물, 옥심계 화합물 및 티오크산톤계 화합물로 이루어진 군에서 선택된 1종이상의 화합물일 수 있다.The photopolymerization initiator can be used without limitation as long as it can polymerize the photopolymerizable compound. Preferably, the photopolymerization initiator is an acetophenone-based compound, a benzoin-based compound, a benzophenone-based compound, Based compound, a triazine-based compound, a non-imidazole-based compound, an oxime-based compound, and a thioxanthone-based compound.

상기 아세토페논계 화합물로는 구체적으로 예를 들어, 디에톡시아세토페논, 2-히드록시-2-메틸-1-페닐프로판-1-온, 벤질디메틸케탈, 2-히드록시-1-[4-(2-히드록시에톡시)페닐]-2-메틸프로판-1-온, 1-히드록시시클로헥실페닐케톤, 2-메틸-1-(4-메틸티오페닐)-2-모르폴리노프로판-1-온, 2-벤질-2-디메틸아미노-1-(4-모르폴리노페닐)부탄-1-온, 2-히드록시-2-메틸-1-[4-(1-메틸비닐)페닐]프로판-1-온 및 2-(4-메틸벤질)-2-(디메틸아미노)-1-(4-모르폴리노페닐)부탄-1-온 등을 들 수 있다.Specific examples of the acetophenone compound include diethoxyacetophenone, 2-hydroxy-2-methyl-1-phenylpropan-1-one, benzyldimethylketal, 2- (2-hydroxyethoxy) phenyl] -2-methylpropan-1-one, 1-hydroxycyclohexyl phenyl ketone, 2- 1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) butan- ] Propane-1-one and 2- (4-methylbenzyl) -2- (dimethylamino) -1- (4-morpholinophenyl) butan-1-one.

상기 벤조인계 화합물로는, 구체적으로 예를 들어, 벤조인, 벤조인메틸에테르, 벤조인에틸에테르, 벤조인이소프로필에테르 및 벤조이소부틸에테르 등을 들 수 있다.Specific examples of the benzoin compound include benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, and benzoisobutyl ether.

상기 벤조페논계 화합물로는 구체적으로 예를 들어, 벤조페논, 0-벤조일벤조산 메틸, 4-페닐벤조페논, 4-벤조일-4'-메틸디페닐술피드, 3,3',4,4'-테트라(tert-부틸퍼옥시카르보닐)벤조페논 및 2,4,6-트리메틸벤조페논 등을 들 수 있다.Specific examples of the benzophenone compound include benzophenone, methyl 0-benzoylbenzoate, 4-phenylbenzophenone, 4-benzoyl-4'-methyldiphenylsulfide, 3,3 ' -Tetra (tert-butylperoxycarbonyl) benzophenone and 2,4,6-trimethylbenzophenone.

상기 트리아진계 화합물로는, 구체적으로 예를 들어, 2,4-비스(트리클로로메틸)-6-(4-메톡시페닐)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-(4-메톡시나프틸)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-(4-메톡시스티릴)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(5-메틸퓨란-2-일)에테닐]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(퓨란-2-일)에테닐]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(4-디에틸아미노-2-메틸페닐)에테닐]-1,3,5-트리아진, 및 2,4-비스(트리클로로메틸)-6-[2-(3,4디메톡시페닐)에테닐]-1,3,5-트리아진 등을 들 수 있다.Specific examples of the triazine compound include 2,4-bis (trichloromethyl) -6- (4-methoxyphenyl) -1,3,5-triazine, 2,4-bis (4-methoxynaphthyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (Trichloromethyl) -6- [2- (5-methylfuran-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis Yl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- Ethylamino-2-methylphenyl) ethenyl] -1,3,5-triazine and 2,4-bis (trichloromethyl) -6- [2- (3,4 dimethoxyphenyl) ethenyl] -1 , 3,5-triazine, and the like.

상기 비이미다졸 화합물로는 구체적으로 예를 들어, 2,2'-비스(2-클로로페닐)-4,4',5,5'-테트라페닐비이미다졸, 2,2'-비스(2,3-디클로로페닐)-4,4',5,5'-테트라페닐비이미다졸, 2,2'-비스(2-클로로페닐)-4,4',5,5'-테트라(알콕시페닐)비이미다졸, 2,2'-비스(2-클로로페닐)-4,4',5,5'-테트라(트리알콕시페닐)비이미다졸, 2,2-비스(2,6-디클로로페닐)-4,4',5,5'-테트라페닐-1,2'-비이미다졸, 또는 4,4',5,5' 위치의 페닐기가 카르보알콕시기에 의해 치환되어 있는 이미다졸 화합물 등을 들 수 있다.Specific examples of the imidazole compound include 2,2'-bis (2-chlorophenyl) -4,4 ', 5,5'-tetraphenylbimidazole, 2,2'-bis , 3-dichlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2-chlorophenyl) -4,4', 5,5'- ) Diimidazole, 2,2'-bis (2-chlorophenyl) -4,4 ', 5,5'-tetra (trialkoxyphenyl) ) -4,4 ', 5,5'-tetraphenyl-1,2'-biimidazole, or an imidazole compound in which the phenyl group at the 4,4', 5,5 'position is substituted by a carboalkoxy group .

보다 바람직하게는, 2,2'-비스(2-클로로페닐)-4,4',5,5'-테트라페닐비이미다졸, 2,2'-비스(2,3-디클로로페닐)-4,4',5,5'-테트라페닐비이미다졸, 2,2-비스(2,6-디클로로페닐)-4,4',5,5'-테트라페닐-1,2'-비이미다졸 등을 들 수 있다.More preferably, it is selected from the group consisting of 2,2'-bis (2-chlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2,3- , 4 ', 5,5'-tetraphenylbiimidazole, 2,2-bis (2,6-dichlorophenyl) -4,4', 5,5'-tetraphenyl- And the like.

상기 옥심 화합물로는 구체적으로 예를 들어, o-에톡시카르보닐-α-옥시이미노-1-페닐프로판-1-온 등을 들 수 있으며, 시판품으로 바스프사의 OXE01, OXE02일 수 있다.Specific examples of the oxime compound include o-ethoxycarbonyl-α-oximino-1-phenylpropan-1-one and the like. Commercially available oxime compounds may be OXE01 and OXE02 of BASF.

상기 티오크산톤계 화합물은 구체적으로 예를 들어, 2-이소프로필티오크산톤, 2,4-디에틸티오크산톤, 2,4-디클로로티오크산톤, 1-클로로-4-프로폭시티오크산톤 등을 들 수 있다.The thioxanthone compound is specifically exemplified by 2-isopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone, 1-chloro- Santon et al.

상기 광중합 개시제는 단독 또는 2종 이상을 혼합하여 사용할 수 있다.These photopolymerization initiators may be used singly or in combination of two or more.

본 발명에서 상기 광중합 개시제는 착색 감광성 수지 조성물 중 고형분총 중량에 대하여, 0.1 내지 40 중량%, 바람직하게는 1 내지 30 중량%로 포함된다. In the present invention, the photopolymerization initiator is contained in an amount of 0.1 to 40% by weight, preferably 1 to 30% by weight, based on the total solid content of the colored photosensitive resin composition.

상기 0.1 내지 40 중량% 범위 내에서 착색 감광성 수지 조성물이 고감도화되어 상기 착색 감광성 수지 조성물을 사용하여 형성한 화소부의 강도 및 상기 화소부의 표면에서의 평활성이 양호해질 수 있다. The colored photosensitive resin composition becomes highly sensitive within the range of 0.1 to 40% by weight, and the strength of the pixel portion formed using the colored photosensitive resin composition and the smoothness on the surface of the pixel portion can be improved.

또한, 본 발명에서는 광중합 개시제에 추가로 광중합 개시 보조제를 사용할 수 있다. In the present invention, a photopolymerization initiator may be used in addition to the photopolymerization initiator.

상기 광중합 개시 보조제는 광중합 개시제에 의해 중합이 개시된 광중합성 화합물의 중합을 촉진시키기 위해 사용되는 화합물이며, 광중합 개시 보조제로는, 예를 들어 아민계 화합물 또는 알콕시안트라센계 화합물 등을 들 수 있다.The photopolymerization initiation assistant is a compound used for promoting polymerization of the photopolymerizable compound initiated by the photopolymerization initiator. Examples of the photopolymerization initiation assistant include an amine compound or an alkoxyanthracene compound.

상기 아민계 화합물로는, 구체적으로 예를 들어, 트리에탄올아민, 메틸디에탄올아민, 트리이소프로판올아민, 4-디메틸아미노벤조산메틸, 4-디메틸아미노벤조산에틸, 4-디메틸아미노벤조산이소아밀, 벤조산2-디메틸아미노에틸, 4-디메틸아미노벤조산 2-에틸헥실, N,N-디메틸파라톨루이딘, 4,4'-비스(디메틸아미노)벤즈페논(통칭, 미힐러즈케톤), 4,4'-비스(디에틸아미노)벤조페논 및 4,4'-비스(에틸메틸아미노)벤조페논 등을 들 수 있으며, 이 중에서도 4,4'-비스(디에틸아미노)벤조페논이 바람직하다. Specific examples of the amine compound include triethanolamine, methyldiethanolamine, triisopropanolamine, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, isoamyl 4-dimethylaminobenzoate, benzoic acid 2 N, N-dimethyl para-toluidine, 4,4'-bis (dimethylamino) benzphenone (collectively, Michler's ketone), 4,4'-bis (Diethylamino) benzophenone, and 4,4'-bis (ethylmethylamino) benzophenone. Of these, 4,4'-bis (diethylamino) benzophenone is preferable.

상기 알콕시안트라센계 화합물로는, 구체적으로 예를 들어, 9,10-디메톡시안트라센, 2-에틸-9,10-디메톡시안트라센, 9,10-디에톡시안트라센 및 2-에틸-9,10-디에톡시안트라센 등을 들 수 있다. Specific examples of the alkoxyanthracene compound include 9,10-dimethoxyanthracene, 2-ethyl-9,10-dimethoxyanthracene, 9,10-diethoxyanthracene and 2-ethyl- Diethoxyanthracene and the like.

또한, 광중합 개시 보조제로서 시판되는 것을 사용할 수 있으며, 시판되는 광중합 개시 보조제로는, 상품명 「EAB-F」(제조원: 호도가야가가쿠고교가부시키가이샤) 등을 들 수 있다.Commercially available photopolymerization initiators may also be used. Commercially available photopolymerization initiators include trade names " EAB-F " (manufactured by Hodogaya Chemical Industry Co., Ltd.).

상기 광중합 개시 보조제를 사용하는 경우, 광중합 개시제 1몰에 대하여, 통상적으로 0 초과 10몰 이하, 0.01 내지 5몰로 사용하는 것이 바람직하다. 상기 0 초과 10몰 이하의 범위로 광중합 개시 보조제를 사용하면, 착색 감광성 수지 조성물의 감도가 더 높아지고, 착색 감광성 수지 조성물을 사용하여 형성되는 컬러필터의 생산성이 향상될 수 있다. When the photopolymerization initiator is used, it is preferably used in an amount of usually 0 to 10 mol, preferably 0.01 to 5 mol, per 1 mol of the photopolymerization initiator. When the photopolymerization initiator is used in the range of more than 0 to 10 moles, the sensitivity of the colored photosensitive resin composition becomes higher and the productivity of the color filter formed using the colored photosensitive resin composition can be improved.

(E)용제 (E) Solvent

상기 용제는 착색 감광성 수지 조성물에 포함되는 다른 성분들을 용해시키는데 효과적인 것이면, 통상의 착색 감광성 수지 조성물에서 사용되는 용제를 특별히 제한하지 않고 사용할 수 있으며, 특히 에테르류, 아세테이트류, 방향족 탄화수소류, 케톤류, 알코올류 또는 에스테르류 등이 바람직하다.The solvent used in the conventional colored photosensitive resin composition can be used without particular limitation so long as it is effective to dissolve the other components contained in the colored photosensitive resin composition. In particular, the solvent may be selected from ethers, acetates, aromatic hydrocarbons, ketones, Alcohols or esters are preferred.

상기 에테르류로는 예를 들어, 에틸렌글리콜모노메틸에테르, 에틸렌글리콜모노에틸에테르, 에틸렌글리콜모노프로필에테르 및 에틸렌글리콜모노부틸에테르 등의 에틸렌글리콜모노알킬에테르류; Examples of the ethers include ethylene glycol monoalkyl ethers such as ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, and ethylene glycol monobutyl ether;

디에틸렌글리콜디메틸에테르, 디에틸렌글리콜디에틸에테르, 디에틸렌글리콜디프로필에테르 및 디에틸렌글리콜디부틸에테르 등의 디에틸렌글리콜디알킬에테르류 등을 들 수 있다.And diethylene glycol dialkyl ethers such as diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol dipropyl ether and diethylene glycol dibutyl ether.

상기 아세테이트류로는 예를 들어, 메틸셀로솔브아세테이트, 에틸셀로솔브아세테이트, 에틸아세테이트, 부틸아세테이트, 아밀아세테이트, 메틸락테이트, 에틸락테이트, 부틸락테이트, 3-메톡시부틸아세테이트, 3-메틸-3-메톡시-1-부틸아세테이트, 메톡시펜틸아세테이트, 에틸렌글리콜모노아세테이트, 에틸렌글리콜디아세테이트, 메틸 3-메토시프로피오네이트, 프로필렌글리콜메틸에테르아세테이트, 3-메톡시-1-부틸아세테이트, 1,2-프로필렌글리콜디아세테이트, 에틸렌글리콜모노부틸에테르아세테이트, 디에틸렌글리콜모노에틸에테르아세테이트, 디프로필렌글리콜메틸에테르아세테이트, 1,3-부틸렌글리콜디아세테이트, 디에틸렌글리콜모노부틸에테르아세테이트, 에틸렌글리콜모노메틸에테르아세테이트, 에틸렌글리콜모노에틸에테르아세테이트, 디에틸렌글리콜모노아세테이트, 디에틸렌글리콜디아세테이트, 디에틸렌글리콜모노부틸에테르아세테이트, 프로필렌글리콜모노아세테이트, 프로필렌글리콜디아세테이트, 프로필렌글리콜모노메틸에테르아세테이트, 프로필렌글리콜모노에틸에테르아세테이트, 에틸렌카보네이트 및 프로필렌카보네이트 등을 들 수 있다.Examples of the acetates include methyl cellosolve acetate, ethyl cellosolve acetate, ethyl acetate, butyl acetate, amyl acetate, methyl lactate, ethyl lactate, butyl lactate, 3-methoxybutyl acetate, 3 Methoxy-1-butylacetate, methoxypentyl acetate, ethylene glycol monoacetate, ethylene glycol diacetate, methyl 3-methoxypropionate, propylene glycol methyl ether acetate, 3-methoxy- Butyl acetate, 1,2-propylene glycol diacetate, ethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, dipropylene glycol methyl ether acetate, 1,3-butylene glycol diacetate, diethylene glycol monobutyl ether Acetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, di Ethylene glycol monoacetate, diethylene glycol diacetate, diethylene glycol monobutyl ether acetate, propylene glycol monoacetate, propylene glycol diacetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, ethylene carbonate and propylene carbonate. .

상기 방향족 탄화수소류로는 예를 들어, 벤젠, 톨루엔, 크실렌 및 메시틸렌 등을 들 수 있다.Examples of the aromatic hydrocarbons include benzene, toluene, xylene, and mesitylene.

상기 케톤류로는 예를 들어, 메틸에틸케톤, 아세톤, 메틸아밀케톤, 메틸이소부틸케톤 및 시클로헥사논 등을 들 수 있다.The ketones include, for example, methyl ethyl ketone, acetone, methyl amyl ketone, methyl isobutyl ketone, and cyclohexanone.

상기 알콜류로는 예를 들어, 에탄올, 프로판올, 부탄올, 헥산올, 시클로헥산올, 에틸렌글리콜, 글리세린 및 4-하이드록시-4-메틸-2-펜탄온 등을 들 수 있다.The alcohols include, for example, ethanol, propanol, butanol, hexanol, cyclohexanol, ethylene glycol, glycerin and 4-hydroxy-4-methyl-2-pentanone.

상기 에스테르류로는 예를 들어, 3-에톡시프로피온산에틸, 3-메톡시프로피온산메틸 및 γ-부티로락톤 등을 들 수 있다.Examples of the esters include ethyl 3-ethoxypropionate, methyl 3-methoxypropionate and? -Butyrolactone.

상기 용제는 각각 단독 또는 2종 이상을 혼합하여 사용할 수 있다.These solvents may be used alone or in combination of two or more.

상기 용제는 도포성 및 건조성면에서 비점이 100℃ 내지 200℃인 유기 용제를 사용하는 것이 바람직하고, 예를 들어, 프로필렌글리콜모노메틸에테르아세테이트, 프로필렌글리콜모노에틸에테르아세테이트, 시클로헥사논, 3-에톡시프로피온산에틸 및 3-메톡시프로피온산메틸 등을 들 수 있다. The solvent is preferably an organic solvent having a boiling point of 100 ° C to 200 ° C in terms of coating property and drying property, and examples thereof include propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, cyclohexanone, 3- Ethyl ethoxypropionate and methyl 3-methoxypropionate.

상기 용제는 착색 감광성 수지 조성물 총 중량에 대하여 60 내지 90 중량%, 바람직하게는 65 내지 85 중량%로 포함된다. 상기 용제가 상기 60 내지 90중량%의 범위로 포함되면 롤 코터, 스핀 코터, 슬릿 앤드 스핀 코터, 슬릿 코터(다이 코터라고도 하는 경우가 있음) 및 잉크젯 등의 도포 장치로 도포했을 때 도포성이 양호해질 수 있다.The solvent is contained in an amount of 60 to 90% by weight, preferably 65 to 85% by weight based on the total weight of the colored photosensitive resin composition. When the solvent is contained in the range of 60 to 90% by weight, when the solvent is applied by a coating device such as a roll coater, a spin coater, a slit and spin coater, a slit coater (sometimes referred to as a die coater) .

(F)첨가제 (F) Additive

본 발명의 착색 감광성 수지 조성물은 상기한 성분들 외에 본 발명의 목적을 해치지 않는 범위에서 당업자의 필요에 따라 다른 첨가제를 포함한다.The colored photosensitive resin composition of the present invention includes other additives according to the needs of those skilled in the art, as long as the objects of the present invention are not impaired, in addition to the above-mentioned components.

상기 첨가제는 구체적으로 예를 들면 다른 고분자 화합물, 열 개시제, 경화제, 계면활성제, 밀착 촉진제, 산화 방지제, 자외선 흡수제 및 응집 방지제로 이루어진 군으로부터 선택되는 1종 이상의 첨가제를 추가로 포함할 수 있다.The additive may further include, for example, at least one additive selected from the group consisting of another polymer compound, a thermal initiator, a curing agent, a surfactant, an adhesion promoter, an antioxidant, an ultraviolet absorber and an anti-

또한, 본 발명은 첨가제로서 특히 열 개시제를 추가로 포함하는 것이 보다 바람직 할 수 있다.상기 열 개시제는 열에 의한 경화반응을 일으켜 개시 효율을 극대화시키는 역할을 한다. 상기 열 개시제는 퍼옥사이드계 화합물일 수 있으며, 상기 열 개시제는 60 내지 100℃ 에서 경화 반응을 개시함에 따라 저온에서 도막의 물리적 성질을 향상시키는 것이 특징이다.In addition, the present invention may further preferably include a thermal initiator as an additive. The thermal initiator causes a curing reaction by heat to maximize the initiation efficiency. The thermal initiator may be a peroxide compound, and the thermal initiator is characterized by improving the physical properties of the coating film at a low temperature as the curing reaction is initiated at 60 to 100 ° C.

상기 열 개시제의 구체적인 종류는 특별히 한정되지 않으나, TAG-2713(K-PURE사), 테트라메틸부틸퍼옥시 네오데카노에이트(ex. Perocta ND, NOF사(제)), 비스(4-부틸시클로헥실)퍼옥시디카보네이트(ex. Peroyl TCP, NOF사(제)), 디(2-에틸헥실)퍼옥시 카보네이트, 부틸퍼옥시 네오데카노에이트(ex. Perbutyl ND, NOF사(제)), 디프로필 퍼옥시 디카보네이트(ex. Peroyl NPP, NOF사(제)), 디이소프로필 퍼옥시 디카보네이트(ex. Peroyl IPP, NOF사(제)), 디에톡시에틸 퍼옥시 디카보네이트(ex. Peroyl EEP, NOF사(제)), 디에톡시헥실 퍼옥시 디카보네이트(ex. Peroyl OEP, NOF사(제)), 헥실 퍼옥시 디카보네이트(ex. Perhexyl ND, NOF사(제)), 디메톡시부틸 퍼옥시 디카보네이트(ex. Peroyl MBP, NOF사(제)), 비스(3-메톡시-3-메톡시부틸) 퍼옥시 디카보네이트(ex. Peroyl SOP, NOF사(제)), 디부틸 퍼옥시 디카보네이트, 디세틸(dicetyl)퍼옥시 디카보네이트, 디미리스틸 (dimyristyl)퍼옥시 디카보네이트, 1,1,3,3-테트라메틸부틸 퍼옥시피발레이트(peroxypivalate), 헥실 퍼옥시 피발레이트(ex. Perhexyl PV, NOF사(제)), 부틸 퍼옥시 피발레이트(ex. Perbutyl, NOF사(제)), 트리메틸 헥사노일 퍼옥시드(ex. Peroyl 355, NOF사(제)), 디메틸 히드록시부틸 퍼옥시네오데카노에이트(ex. Luperox 610M75, Atofina(제)), 아밀 퍼옥시네오데카노에이트(ex. Luperox 546M75, Atofina(제)), 부틸 퍼옥시네오데카노에이트(ex. Luperox 10M75, Atofina(제)), t-부틸퍼옥시 네오헵타노에이트, 아밀퍼옥시 피발레이트(pivalate)(ex. Luperox 546M75, Alofina(제)), t-부틸퍼옥시 피발레이트, t-아밀 퍼옥시-2-에틸헥사노에이트, 라우릴 퍼옥시드, 디라우로일(dilauroyl) 퍼옥시드, 디데카노일 퍼옥시드, 벤조일 퍼옥시드, 디벤조일 퍼옥시드, 2,2-비스(tert-부틸퍼옥시)부탄, 1,1-비스(tert-부틸퍼옥시)시클로헥산, 2,5-비스(부틸퍼옥시)-2,5-디메틸헥산, 2,5-비스(tert-부틸퍼옥시)-1-메틸에틸)벤젠, 1,1-비스(tert-부틸퍼옥시)-3,3,5-트리메틸시클로헥산, tert-부틸 히드로퍼옥시드, tert-부틸 퍼옥시드, tert-부틸 퍼옥시벤조에이트, tert-부틸퍼옥시 이소프로필 카보네이트, 큐멘 히드록시퍼옥시드, 디큐밀 퍼옥시드, 라우로일 퍼옥시드, 2,4-펜타네디온 퍼옥시드, tert-부틸 퍼아세테이트(tert-butyl peracetate), 퍼아세틱산(peracetic acid), 및 포타슘 퍼술페이트(potassium persulfate)로 이루어진 군으로부터 선택되는 1종 이상인 것일 수 있다.Specific examples of the thermal initiator include, but are not limited to, TAG-2713 (K-PURE), tetramethyl butyl peroxyneodecanoate (ex Perocta ND, NOF), bis (4-butylcyclo Perylyl TCP, NOF), di (2-ethylhexyl) peroxycarbonate, butyl peroxyneodecanoate (ex Perbutyl ND, NOF) Peroyl NPP, NOF), diisopropylperoxy dicarbonate (e.g., Peroyl IPP, NOF), diethoxyethyl peroxydicarbonate (e.g., Peroyl EEP (Manufactured by NOF Corporation), diethoxyhexyl peroxydicarbonate (ex Peroyl OEP, NOF), hexyl peroxydicarbonate (ex Perhexyl ND, NOF), dimethoxybutyl peroxide Peroxides such as oxydicarbonate (ex Peroyl MBP, NOF), bis (3-methoxy-3-methoxybutyl) peroxydicarbonate (ex Peroyl SOP, NOF), dibutylperoxy Dicarbonyl, dicetyl ) Peroxydicarbonate, dimyristyl peroxydicarbonate, 1,1,3,3-tetramethylbutyl peroxypivalate, hexyl peroxypivalate (e.g., Perhexyl PV, NOF Perbutyl, NOF), trimethylhexanoyl peroxide (e.g., Peroyl 355, NOF), dimethylhydroxybutyl peroxyneodecanoate (manufactured by Nippon Kayaku Co., Ltd.) such as Luperox 610M75, Atofina, amyl peroxyneodecanoate (ex Luperox 546M75, Atofina), butyl peroxyneodecanoate (ex Luperox 10M75, Atofina), t Butyl peroxy neoheptanoate, amyl peroxy pivalate (ex Luperox 546M75, Alofina), t-butyl peroxypivalate, t-amyl peroxy-2-ethylhexanoate, Di-n-butyl peroxide, lauryl peroxide, dilauroyl peroxide, didecanoyl peroxide, benzoyl peroxide, dibenzoyl peroxide, 2,2- 2,5-bis (tert-butylperoxy) -1-methylethyl) benzene, 1 (tert-butylperoxy) cyclohexane, 2,5- , Tert-butyl peroxide, tert-butyl peroxybenzoate, tert-butyl peroxyisobutyrate, tert-butyl peroxybenzoate, But are not limited to, carbonate, cumene hydroperoxide, dicumyl peroxide, lauroyl peroxide, 2,4-pentanedione peroxide, tert-butyl peracetate, peracetic acid, And potassium persulfate may be used.

상기 열 개시제 함량과 관련하여, 착색 감광성 수지 조성물 중 고형분 총중량에 대하여 1 내지 10중량%로 포함되는 것이 바람직하고 1 내지 5 중량%로 포함되는 것이 보다 바람직하다. 상기와 같은 함량으로 포함되는 경우에는 공정성 및 언더컷에 보다 바람직하다.With respect to the content of the thermal initiator, it is preferably contained in an amount of 1 to 10% by weight, and more preferably 1 to 5% by weight based on the total solid content of the colored photosensitive resin composition. When it is contained in the above-mentioned contents, it is more preferable for fairness and undercut.

상기 열 개시제 및 광중합성 개시제는 1:1.1 내지 1:8의 중량비로 혼합될 수 있으며, 바람직하게는1:1.2 내지 1:2.8의 중량비로 혼합 될 수 있다. 상기 범위를 만족할 경우 가교도 형성 및 표면 조도에 영향을 주어, 신뢰성이 향상되는 효과를 얻을 수 있다.The thermal initiator and the photopolymerization initiator may be mixed in a weight ratio of 1: 1.1 to 1: 8, preferably 1: 1.2 to 1: 2.8. When the above-mentioned range is satisfied, the crosslinking degree and the surface roughness are affected, and the reliability is improved.

상기 다른 고분자 화합물의 구체적인 예로는 에폭시 수지 및 말레이미드 수지 등의 경화성 수지; 폴리비닐알코올, 폴리아크릴산, 폴리에틸렌글리콜모노알킬에테르, 폴리플루오로알킬아크릴레이트, 폴리에스테르 및 폴리우레탄 등의 열가소성 수지 등을 들 수 있다.Specific examples of the other polymer compound include a curable resin such as an epoxy resin and a maleimide resin; And thermoplastic resins such as polyvinyl alcohol, polyacrylic acid, polyethylene glycol monoalkyl ether, polyfluoroalkyl acrylate, polyester and polyurethane.

상기 경화제는 심부 경화 및 기계적 강도를 높이기 위해 사용되며, 구체적인 예로는 에폭시 화합물, 다관능 이소시아네이트 화합물, 멜라민 화합물 및 옥세탄 화합물 등을 들 수 있다.The curing agent is used for increasing the curing depth and mechanical strength, and specific examples thereof include an epoxy compound, a polyfunctional isocyanate compound, a melamine compound and an oxetane compound.

상기 경화제에서 에폭시 화합물의 구체적인 예로는 비스페놀 A계 에폭시 수지, 수소화 비스페놀 A계 에폭시 수지, 비스페놀 F계 에폭시 수지, 수소화 비스페놀 F계 에폭시 수지, 노블락형 에폭시 수지, 기타 방향족계 에폭시 수지, 지환족계 에폭시 수지, 글리시딜에스테르계 수지, 글리시딜아민계 수지, 또는 이러한 에폭시 수지의 브롬화 유도체, 에폭시 수지 및 그 브롬화 유도체 이외의 지방족, 지환족 또는 방향족 에폭시 화합물, 부타디엔 (공)중합체 에폭시화물, 이소프렌 (공)중합체 에폭시화물, 글리시딜(메타)아크릴레트 (공)중합체, 트리글리시딜이소시아눌레이트 등을 들 수 있다.Specific examples of the epoxy compound in the curing agent include bisphenol A epoxy resin, hydrogenated bisphenol A epoxy resin, bisphenol F epoxy resin, hydrogenated bisphenol F epoxy resin, novolak epoxy resin, other aromatic epoxy resin, alicyclic epoxy resin Alicyclic or aromatic epoxy compounds, butadiene (co) polymeric epoxides and isoprene (co) polymers other than the brominated derivatives, epoxy resins and brominated derivatives of these epoxy resins, glycidyl ester resins, glycidyl amine resins, (Co) polymer epoxides, glycidyl (meth) acrylate (co) polymers, and triglycidyl isocyanurate.

상기 경화제에서 옥세탄 화합물의 구체적인 예로는 카르보네이트비스옥세탄, 크실렌비스옥세탄, 아디페이트비스옥세탄, 테레프탈레이트비스옥세탄, 시클로헥산디카르복실산비스옥세탄 등을 들 수 있다.Specific examples of the oxetane compound in the curing agent include carbonates bisoxetane, xylene bisoxetane, adipate bisoxetane, terephthalate bisoxetane, cyclohexanedicarboxylic acid bisoxetane, and the like.

상기 경화제는, 경화제와 함께 에폭시 화합물의 에폭시기, 옥세탄 화합물의 옥세탄 골격을 개환 중합하게 할 수 있는 경화 보조 화합물을 병용할 수 있다. 상기 경화 보조 화합물은 예를 들면 다가 카르본산류, 다가 카르본산 무수물류, 산발생제 등이 있다. 상기 다가 카르본산 무수물류는 에폭시 수지 경화제로서 시판되는 것을 이용할 수 있다. 상기 에폭시 수지 경화제의 구체적인 예로는 시판품으로서 상품명(아데카하도나 EH-700)(아데카공업㈜ 제조), 상품명(리카싯도 HH)(신일본이화㈜ 제조), 상품명(MH-700)(신일본이화㈜ 제조) 등을 들 수 있다. 상기에서 예시한 경화제는 단독으로 또는 2종 이상을 혼합하여 사용할 수 있다.The curing agent may be used together with a curing assistant compound capable of ring-opening polymerization of the epoxy group of the epoxy compound and the oxetane skeleton of the oxetane compound together with the curing agent. The curing assistant compound includes, for example, polyvalent carboxylic acids, polyvalent carboxylic anhydrides, and acid generators. The polyvalent carboxylic acid anhydrides may be those commercially available as an epoxy resin curing agent. Specific examples of the above-mentioned epoxy resin curing agents include commercial products such as ADEKA HARDONA EH-700 (ADEKA INDUSTRIAL CO., LTD.), Trade name (RICACIDO HH) (manufactured by New Japan Chemical Co., Ltd.) Manufactured by Shin-Etsu Chemical Co., Ltd.). The curing agents exemplified above may be used alone or in combination of two or more.

상기 계면활성제는 감광성 수지 조성물의 피막 형성성을 보다 향상시키기 위해 사용할 수 있으며, 실리콘계 계면활성제 또는 불소계 계면활성제 등이 바람직하게 사용될 수 있다.The surfactant may be used for further improving the film-forming property of the photosensitive resin composition, and a silicone surfactant or a fluorine surfactant may be preferably used.

상기 실리콘계 계면활성제는 예를 들면 시판품으로서 다우코닝 도레이 실리콘사의 DC3PA, DC7PA, SH11PA, SH21PA 및 SH-8400 등, GE 도시바 실리콘사의 TSF-4440, TSF-4300, TSF-4445, TSF-4446, TSF-4460 및 TSF-4452 등을 들 수 있다. 상기 불소계 계면활성제는 예를 들면 시판품으로서 메가피스 F-470, F-471, F-475, F-482, F-489 및 F-554(다이닛본 잉크 가가꾸 고교社), BM-1000, BM-1100(BM Chemie社), 프로라이드 FC-135/FC-170C/FC-430(스미토모 쓰리엠㈜) 등을 들 수 있다. 상기 예시된 계면활성제는 각각 단독으로 또는 2종 이상을 조합하여 사용할 수 있다.TS-4440, TSF-4300, TSF-4445, TSF-4446, and TSF-4400 of GE Toshiba Silicones such as DC3PA, DC7PA, SH11PA, SH21PA and SH-8400 from Dow Corning Toray Silicone Co., 4460 and TSF-4452. F-482, F-489 and F-554 (manufactured by Dainippon Ink and Chemicals, Incorporated), BM-1000, BM -1100 (BM Chemie), Proride FC-135 / FC-170C / FC-430 (Sumitomo 3M Co., Ltd.). The above-exemplified surfactants may be used alone or in combination of two or more.

상기 밀착 촉진제는 기판과의 코팅성 및 밀착성을 증진시키기 위해 사용되는 첨가제로, 카르복실기, 메타크릴로일기, 이소시아네이트기, 에폭시기 및 이들의 조합으로 이루어진 군에서 선택되는 반응성 치환기를 포함하는 실란 커플링제를 포함할 수 있다. 실란 커플링제는 구체적으로 예를 들어, 트리메톡시실릴 벤조산, γ-메타크릴 옥시프로필 트리메톡시 실란, 비닐트리아세톡시실란, 비닐 트리메톡시실란, γ-이소시아네이트 프로필 트리에톡시실란, r-글리시독시 프로필 트리메톡시실란, β-(3,4-에폭시시클로헥실)에틸트리메톡시실란 등을 들 수 있다.The adhesion promoter is an additive which is used for improving coatability and adhesion to a substrate, and is a silane coupling agent containing a reactive substituent selected from the group consisting of a carboxyl group, a methacryloyl group, an isocyanate group, an epoxy group, . Specific examples of the silane coupling agent include trimethoxysilylbenzoic acid,? -Methacryloxypropyltrimethoxysilane, vinyltriacetoxysilane, vinyltrimethoxysilane,? -Isocyanatepropyltriethoxysilane, r- Glycidoxypropyltrimethoxysilane, and? - (3,4-epoxycyclohexyl) ethyltrimethoxysilane.

상기 산화 방지제의 구체적인 예로는 2,2'-티오비스(4-메틸-6-t-부틸페놀) 및 2,6-디-t-부틸-4-메틸페놀 등을 들 수 있다.Specific examples of the antioxidant include 2,2'-thiobis (4-methyl-6-t-butylphenol) and 2,6-di-t-butyl-4-methylphenol.

상기 자외선 흡수제의 구체적인 예로는 2-(3-tert-부틸-2-히드록시-5-메틸페닐)-5-클로로벤조티리아졸 및 알콕시벤조페논 등을 들 수 있다.Specific examples of the ultraviolet absorber include 2- (3-tert-butyl-2-hydroxy-5-methylphenyl) -5-chlorobenzothiazole and alkoxybenzophenone.

상기 응집 방지제의 구체적인 예로는 폴리아크릴산 나트륨 등을 들 수 있다.Specific examples of the anti-aggregation agent include sodium polyacrylate and the like.

상기 첨가제는 착색 감광성 수지 조성물 중의 고형분 총 중량에 대하여 0.01 내지 10 중량%로 포함되며, 바람직하게는 0.05 내지 2 중량% 포함될 수 있다.The additive is contained in an amount of 0.01 to 10% by weight, preferably 0.05 to 2% by weight based on the total weight of the solid content of the colored photosensitive resin composition.

일예로, 착색제를 용제에 첨가한 후 나머지 조성 및 기타 첨가제를 첨가하여 교반을 통해 얻을 수 있다. 이때 상기 착색제는 안료 등을 미리 용제 또는 알칼리 가용성 수지에 용해시키거나 분산시킨 밀베이스 형태로 첨가될 수 있다. 첨가제는 용액 형태인 경우 착색제와 함께 용매에 미리 첨가될 수 있다.For example, a coloring agent may be added to a solvent, followed by addition of the rest of the composition and other additives, followed by stirring. At this time, the colorant may be added in the form of a mill base in which a pigment or the like is dissolved or dispersed in advance in a solvent or an alkali-soluble resin. The additive, if in solution form, may be added in advance to the solvent along with the colorant.

이렇게 제조된 착색 감광성 수지 조성물은 표시장치, 바람직하기로 액정 표시장치의 블랙 매트릭스, 셀갭 유지를 위한 컬럼 스페이서 또는 블랙 컬럼 스페이서의 제조에 바람직하게 사용될 수 있다.The thus-prepared colored photosensitive resin composition can be preferably used for the production of a display device, preferably a black matrix of a liquid crystal display, a column spacer for maintaining a cell gap, or a black column spacer.

본 발명은 또한, 상술한 착색 감광성 수지 조성물이 3.0μm의 두께를 갖는 경화막으로 형성시에 400~600nm 범위 파장에 대해 0.1% 이하의 광투과도를 나타내고; 700nm~750nm 범위 파장에 대해 10% 이하의 광투과도를 나타내며; 950nm 범위 파장에 대해 15% 이상의 광투과도를 나타내는 것을 특징으로 하는 착색 감광성 수지 조성물을 제공한다.The present invention is also characterized in that the above-mentioned colored photosensitive resin composition exhibits a light transmittance of 0.1% or less with respect to a wavelength in the range of 400 to 600 nm when formed into a cured film having a thickness of 3.0 탆; Exhibits a light transmittance of less than 10% for wavelengths in the range of 700 nm to 750 nm; And exhibits a light transmittance of not less than 15% with respect to a wavelength in the range of 1050 to 950 nm.

특히, 본 발명의 착색 감광성 수지 조성물은 블랙 컬럼 스페이서(블랙 매트릭스 일체형 스페이서)의 제조에 바람직하게 사용될 수 있으며, 상기 블랙 컬럼 스페이서는 블랙 매트릭스와 컬럼 스페이서를 각각 형성하는 것이 아니라, 하나의 패턴으로 블랙 매트릭스와 컬럼 스페이서가 일체로 형성된 것을 의미한다.In particular, the colored photosensitive resin composition of the present invention can be suitably used for producing a black column spacer (black matrix integrated spacer), and the black column spacer does not form a black matrix and a column spacer, Means that the matrix and the column spacer are integrally formed.

본 발명은 또한, 상기 착색 감광성 수지 조성물 사용하여 제조된 블랙 매트릭, 컬럼 스페이서 또는 블랙 컬럼 스페이서를 포함하는 컬러필터에 관한 것이다.The present invention also relates to a color filter comprising a black matrix, a column spacer or a black column spacer manufactured using the colored photosensitive resin composition.

또한, 상기 컬러필터를 포함하는 표시장치에 관한 것이다Further, the present invention relates to a display device including the color filter

포토리쏘그래피 방법에 따른 블랙 매트릭스, 컬럼 스페이서 또는 블랙 컬럼 스페이서를 형성하는 통상의 패터닝 공정은 A typical patterning process for forming a black matrix, column spacer or black column spacer according to the photolithography method

a) 기판에 착색 감광성 수지 조성물을 도포하는 단계;a) applying a colored photosensitive resin composition to a substrate;

b) 용매를 건조하는 프리베이크 단계;b) prebaking step of drying the solvent;

c) 얻어진 피막 위에 포토 마스크를 대어 활성 광선을 조사해 노광부를 경화시키는 단계;c) applying a photomask onto the obtained film to irradiate an actinic ray to cure the exposed portion;

d) 알칼리 수용액을 이용하여 미노광부를 용해하는 현상 공정을 수행하는 단계; 및d) performing a developing step of dissolving the unexposed portion using an aqueous alkali solution; And

e) 건조 및 포스트 베이크 수행단계를 포함하여 이루어진다.e) drying and post-baking.

상기 기판은 유리 기판이나 폴리머 판이 사용된다. 유리 기판으로는, 특히 소다 석회 유리, 바륨 또는 스트론튬 함유 유리, 납유리, 알루미노규산 유리, 붕규산 유리, 바륨 붕규산 유리 또는 석영 등이 바람직하게 사용할 수 있다. 또 폴리머 판으로는, 폴리카보네이트, 아크릴, 폴리에틸렌 테레프탈레이트, 폴리에테르 설파이드 또는 폴리 설폰 등을 들 수 있다.A glass substrate or a polymer plate is used as the substrate. As the glass substrate, in particular, soda lime glass, barium or strontium-containing glass, lead glass, aluminosilicate glass, borosilicate glass, barium borosilicate glass or quartz can be preferably used. Examples of the polymer plate include polycarbonate, acrylic, polyethylene terephthalate, polyether sulfide, and polysulfone.

이때 도포는 원하는 두께를 얻을 수 있도록 롤 코터, 스핀 코터, 슬릿 앤드 스핀 코터, 슬릿 코터(다이 코터라고도 하는 경우가 있음), 잉크젯 등의 도포 장치를 이용한 습식 코팅 방법에 의해 수행될 수 있다.The coating may be performed by a wet coating method using a coating apparatus such as a roll coater, a spin coater, a slit and spin coater, a slit coater (which may be referred to as a die coater), an ink jet or the like so as to obtain a desired thickness.

프리베이크는 오븐, 핫 플레이트 등에 의해 가열함으로써 행해진다. 이때 프리베이크에 있어서의 가열 온도 및 가열 시간은 사용하는 용제에 따라 적의 선택되어 예를 들면, 80 내지 150℃의 온도로 1 내지 30분간 행해진다.Prebaking is performed by heating with an oven, a hot plate or the like. At this time, the heating temperature and the heating time in the pre-baking are appropriately selected depending on the solvent to be used, for example, at a temperature of 80 to 150 ° C for 1 to 30 minutes.

또 프리베이크 후에 행해지는 노광은, 노광기에 의해 행해져 포토 마스크를 통하여 노광함으로써 패턴에 대응한 부분만을 감광시킨다. 이때 조사하는 빛은, 예를 들면, 가시광선, 자외선, X선 및 전자선 등이 가능하다.The exposure performed after the pre-baking is performed by an exposure machine, and exposed through a photomask to expose only the portion corresponding to the pattern. The light to be irradiated may be, for example, visible light, ultraviolet light, X-ray, electron beam, or the like.

노광 후의 알칼리 현상 비노광 부분의 제거되지 않는 부분의 착색 감광성 수지 조성물을 제거하는 목적으로 행해져 이 현상에 의해 원하는 패턴이 형성된다. 이 알칼리 현상에 적합한 현상액으로는, 예를 들면 알칼리 금속이나 알칼리 토류 금속의 탄산염의 수용액 등을 사용할 수 있다. 특히, 탄산나트륨, 탄산칼륨, 탄산 리튬 등의 탄산염을 1 내지 3 중량%를 함유하는 미만 알칼리 수용액을 이용하여 10 내지 50℃, 바람직하게는 20 내지 40℃의 온도 내에서 현상기 또는 초음파 세정기 등을 이용하여 수행한다.The alkali development after exposure is performed for the purpose of removing the colored photosensitive resin composition in a portion where the non-exposed portion is not removed, and a desired pattern is formed by this development. As the developer suitable for the alkali development, for example, an aqueous solution of a carbonate of an alkali metal or an alkaline earth metal may be used. Particularly, a weakly alkaline aqueous solution containing 1 to 3% by weight of a carbonate such as sodium carbonate, potassium carbonate or lithium carbonate is used at a temperature of 10 to 50 캜, preferably 20 to 40 캜, using a developing machine or an ultrasonic cleaner .

포스트 베이크는 패터닝 된 막과 기판과의 밀착성을 높이기 위해서 수행하며, 80 내지 220℃에서 10 내지 120 분의 조건으로 열처리를 통해 이루어진다. 포스트 베이크는 프리베이크와 같게, 오븐, 핫 플레이트 등을 이용하여 수행한다.The post-baking is performed in order to enhance the adhesion between the patterned film and the substrate, and is performed by heat treatment at 80 to 220 DEG C for 10 to 120 minutes. Post-baking is performed by using an oven, a hot plate, or the like as in pre-baking.

이때 블랙 매트릭스의 막 두께로는, 0.2㎛ 내지 20㎛가 바람직하고, 0.5㎛ 내지 10㎛가 보다 바람직하고, 0.8㎛ 내지 5㎛가 특히 바람직하다.In this case, the thickness of the black matrix is preferably 0.2 to 20 占 퐉, more preferably 0.5 to 10 占 퐉, and particularly preferably 0.8 to 5 占 퐉.

또한, 컬럼 스페이서 및 블랙 컬럼 스페이서의 막 두께로는, 0.1㎛ 내지 8㎛가 바람직하고, 0.1㎛ 내지 6㎛가 보다 바람직하고, 0.1㎛ 내지 4㎛가 특히 바람직하다.The film thickness of the column spacer and the black column spacer is preferably 0.1 탆 to 8 탆, more preferably 0.1 탆 to 6 탆, and particularly preferably 0.1 탆 to 4 탆.

본 발명의 착색 감광성 수지 조성물로 제조된 블랙 매트릭스, 컬럼 스페이서 또는 블랙 컬럼 스페이서는 광학밀도, 밀착성, 전기 절연성, 차광성 등의 물성이 우수할 뿐만 아니라, 내열성 및 내용제성 등이 우수하여 액정 표시장치의 신뢰도를 향상시킬 수 있다.The black matrix, the column spacer or the black column spacer made of the colored photosensitive resin composition of the present invention is excellent in physical properties such as optical density, adhesion, electrical insulation and light shielding property, and is excellent in heat resistance and solvent resistance, It is possible to improve the reliability.

이하에서, 실시예를 통하여 본 발명을 보다 상세히 설명한다. 그러나, 하기의 실시예는 본 발명을 더욱 구체적으로 설명하기 위한 것으로서, 본 발명의 범위가 하기의 실시예에 의하여 한정되는 것은 아니다. 하기의 실시예는 본 발명의 범위 내에서 당업자에 의해 적절히 수정, 변경될 수 있다.Hereinafter, the present invention will be described in more detail by way of examples. However, the following examples are intended to further illustrate the present invention, and the scope of the present invention is not limited by the following examples. The following examples can be appropriately modified and changed by those skilled in the art within the scope of the present invention.

제조예Manufacturing example 1. 알칼리 가용성 수지의 제조 1. Preparation of alkali-soluble resin

교반기, 온도계, 환류 냉각관, 적하 깔때기 및 질소 도입관을 구비한 내용적 1L의 분리형 플라스크에 메톡시부틸아세테이트 277g을 투입하고 80℃로 승온시킨 후, 3,4-에폭시트리시클로[5.2.1.0,2,6]데칸-9-일아크릴레이트와 3,4-에폭시트리시클로[5.2.1.0,2,6]데칸-8-일아크릴레이트를 50:50의 몰비로 혼합한 혼합물 301g, 메타크릴산 49g 및 아조비스디메틸발레로니트릴 23g을 메톡시부틸아세테이트 350g에 용해시킨 혼합 용액을 5 시간에 걸쳐서 적하하였다. 그 후, 3 시간 반응을 진행하여 알칼리 가용성 수지 용액(고형분(NV) 35 중량％)을 제조하였다. 상기 알칼리 가용성 수지의 산가(dry)는 69.8 KOH mg/g, 중량 평균 분자량(Mw)은 12,300, 분산도(Mw/Mn)는 2.1이었다.277 g of methoxybutyl acetate was added to an internal 1-L separable flask equipped with a stirrer, a thermometer, a reflux condenser, a dropping funnel and a nitrogen inlet tube, and the mixture was heated to 80 DEG C and 3,4-epoxytricyclo [5.2.1.0 , 2,6] decan-9-yl acrylate and 3,4-epoxytricyclo [5.2.1.0,2,6] decan-8-yl acrylate in a molar ratio of 50:50, 49 g of the acid and 23 g of azobisdimethylvaleronitrile in 350 g of methoxybutyl acetate was added dropwise over 5 hours. Thereafter, the reaction was carried out for 3 hours to prepare an alkali-soluble resin solution (solid content (NV) 35% by weight). The alkali-soluble resin had an acid value of 69.8 KOH mg / g, a weight average molecular weight (Mw) of 12,300 and a dispersion degree (Mw / Mn) of 2.1.

실시예Example 1 내지 11 및  1 to 11 and 비교예Comparative Example 1 내지 7. 착색 감광성 수지 조성물 제조 1 to 7. Preparation of colored photosensitive resin composition

착색제, 알칼리 가용성 수지, 분산제 및 용제를 혼합한 혼합물을 페인트 쉐이커에 상온에서 8시간 동안 분산처리 하였다. 0.1mm 지르코니아 비드를 이용하여 분산을 진행하였으며, 분산 종료 후 필터하여 착색 분산액을 제조하였다.A mixture of a colorant, an alkali-soluble resin, a dispersant and a solvent was dispersed in a paint shaker at room temperature for 8 hours. Dispersion was carried out using 0.1 mm zirconia beads, followed by dispersion and filtration to prepare a colored dispersion.

상기 착색 분산액과 알칼리 가용성 수지, 광중합성 화합물, 광중합 개시제 및 용제를 혼합하여 착색 감광성 수지 조성물을 제조하였으며, 그 함량을 하기 표 1에 나타내었다.The colored dispersion was mixed with an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator and a solvent to prepare a colored photosensitive resin composition, and the content thereof is shown in Table 1 below.

[표 1][Table 1]

Figure pat00001
Figure pat00001

(단위: g)(Unit: g)

(주)(week)

OBP: 유기 블랙 안료(100CF; Basf 社)OBP: Organic black pigment (100 CF; Basf)

V29: C.I. 피그먼트 바이올렛 29V29: C.I. Pigment Violet 29

B60: C.I. 피그먼트 블루 60B60: C.I. Pigment Blue 60

B15:6: C.I. 피그먼트 블루 15:6B15: 6: C.I. Pigment Blue 15: 6

CB: 카본 블랙CB: carbon black

PI-R: Red pigment(R264, CLARIANT)PI-R: Red pigment (R264, CLARIANT)

알칼리 가용성 수지(B): 제조예 1에서 제조한 알칼리 가용성 수지Alkali-soluble resin (B): The alkali-soluble resin

광중합성 화합물(M)(관능기로 (메타)아크릴레이트기 사용)Photopolymerizable compound (M) (using a (meth) acrylate group as a functional group)

M1: DPHA(DIPENTAERYTHRITOL HEXAACRYLATE, 6관능, 닛본 카야꾸)M1: DPHA (DIPENTAERYTHRITOL HEXAACRYLATE, 6-sensory, Nippon Kayaku)

M2: Viscoat#802 (8관능, 오사카유기화학)M2: Viscoat # 802 (octahedral, Osaka Organic Chemical)

광중합 개시제(PI): 1-[9-에틸-6-(2-메틸벤조일)-9H-카바졸-3-일]-에타논-1-(O-아세틸옥심) (Irgacure OXE-02: Ciba사)Photopolymerization initiator (PI): 1- [9-ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl] -ethanone- 1- (O- acetyloxime) (Irgacure OXE- four)

D1: TAG-2713(K-PURE사)D1: TAG-2713 (K-PURE)

D2: F554(DIC사; 표면조정제)D2: F554 (DIC Co., surface modifier)

S: 프로필렌글리콜모노메틸에테르아세테이트(용제)S: propylene glycol monomethyl ether acetate (solvent)

실험예Experimental Example 1. 착색 감광성 수지 조성물의 물성 측정 1. Measurement of physical properties of colored photosensitive resin composition

1-1. 기판 제작1-1. Board Fabrication

5cm X 5cm의 유리기판(코닝社)을 중성세제 및 물로 세정한 후 건조하였다. 상기 유리기판 상에 상기 실시예 및 비교예에서 제조된 착색 감광성 수지 조성물 각각을 최종 막 두께가 3.0㎛가 되도록 스핀 코팅을 하고, 80 내지 120에서 선 소성하여 1 내지 2분간 건조하여 용제를 제거하였다. 그런 다음, 노광량 25 내지 35 mJ/cm2로 노광하여 패턴을 형성하고 알카리 수용액을 사용하여 비노광부를 제거하였다. 이어서 200 내지 250℃에서 후 소성을 10 내지 30분간하여 착색기판을 제조하였다.A 5 cm x 5 cm glass substrate (Corning) was cleaned with a neutral detergent and water and then dried. Each of the colored photosensitive resin compositions prepared in the above Examples and Comparative Examples was spin-coated on the glass substrate to a final film thickness of 3.0 탆, prebaked at 80 to 120 and dried for 1 to 2 minutes to remove the solvent . Then, exposure was performed at an exposure amount of 25 to 35 mJ / cm 2 to form a pattern, and an unexposed area was removed using an aqueous alkaline solution. Followed by baking at 200 to 250 DEG C for 10 to 30 minutes to prepare a colored substrate.

1-2. 1-2. 광특성Optical property 측정 Measure

상기 1-1과 같은 제작 기준으로, 패턴 없이 전면에 흑색 감광성 수지가 도포 되도록 제작한 기판에 대하여 UV-vis(UV-2550, Shimadzu사)를 사용하여 광특성을 평가하였다. 광특성 평가시, 400~600nm에서는 광학밀도를 의미하고, 700~750nm 및 950nm에서는 근적외선(Near-IR) 영역으로 각 파장별 측정값을 확인하였다. 결과를 하기 표 2에 나타내었다.The optical characteristics were evaluated using a UV-vis (UV-2550, manufactured by Shimadzu) on a substrate prepared so that a black photosensitive resin was applied on the entire surface without a pattern in accordance with the same manufacturing standards as those in 1-1 above. In the evaluation of the optical characteristics, the optical density was measured at 400 to 600 nm, and the measured values at 700 to 750 nm and 950 nm were measured in the near-IR region. The results are shown in Table 2 below.

<광특성 평가 기준 1: 400~600nm 파장 범위 내>&Lt; Criteria for evaluating optical characteristics 1: within a wavelength range of 400 to 600 nm >

◎: 우수, 0.1T% 이하?: Excellent, 0.1T% or less

○: 양호, 0.1T% 초과 ~ 0.3T% 이하?: Good, more than 0.1T% to 0.3T% or less

△: 부족, 0.3T% 초과 ~ 0.5T% 이하?: Shortage, more than 0.3T% to 0.5T% or less

X: 악화, 0.5T% 초과 X: deteriorated, exceeding 0.5T%

<광특성 평가 기준 2: 700~750nm 파장 범위 내 >&Lt; Optical characteristic evaluation standard 2: Within 700 to 750 nm wavelength range >

◎: 우수, 10T% 이하⊚: excellent, 10T% or less

○: 양호, 10T% 초과 ~ 12T% 이하Good: 10T% to 12T% or less

△: 부족, 12T% 초과 ~ 15T% 이하?: Insufficient, more than 12T% to less than 15T%

X: 악화, 15T% 초과 X: worsening, exceeding 15T%

<광특성 평가 기준 3: 950nm 파장 범위 내 >&Lt; Evaluation criterion of optical characteristics 3: within 950 nm wavelength range >

◎: 우수, 15T% 이상⊚: Excellent, 15T% or more

○: 양호, 12T% 초과 ~ 15T% 미만○: Good, exceeding 12T% to less than 15T%

△: 부족, 10T% 초과 ~ 12T% 이하?: Insufficient, 10T% to 12T% or less

X: 악화, 10T% 이하 X: worse, 10T% or less

1-3. 신뢰성 측정1-3. Reliability measurement

상기 1-1과 같은 제작 기준으로, 패턴 없이 전면에 흑색 감광성 수지가 도포 되도록 제작한 기판을 3x3cm로 자른 후, 이를 NMP 용액에 침지시킨 후, 100℃에서 60분간 열을 가하였다. 그 후 NMP 용액만을 추출하여, NMP 용제에 용출 정도를 UV-vis spectrometer를 이용해 흡광도를 측정하여, 그 결과를 하기 표 2에 기재하였다.The substrate prepared to apply a black photosensitive resin to the entire surface without a pattern was cut into 3 × 3 cm, and the substrate was immersed in an NMP solution, followed by heating at 100 ° C. for 60 minutes. Thereafter, only the NMP solution was extracted, and the degree of elution in the NMP solvent was measured using a UV-vis spectrometer. The results are shown in Table 2 below.

< 신뢰성 평가 기준><Reliability Evaluation Standard>

◎: 우수, 0.5 이하?: Excellent, 0.5 or less

○: 양호, 0.5 초과 ~ 1.0 이하?: Good, more than 0.5 and less than 1.0

△: 부족, 1.0 초과 ~ 1.5 이하?: Insufficient, more than 1.0 and less than 1.5

X: 악화, 1.5 초과 X: worse, over 1.5

1-4. 1-4. 탄성회복률Elastic recovery rate 측정 Measure

상기 1-1과 같은 제작 기준으로, 컬럼스페이서 패턴이 있는 기판을 제작한다. 제작된 기판을 SNU(SIS-2000, SNU사)를 통해서, 기준상태에서의 패턴의 두께 및 높이를 측정한다. 이후, 경도계(Nano-indenter HM500, Fisher사)를 이용하여 패턴이 1㎛ 변형되는 지점까지 눌러준다. 경도계는 평면 압자를 이용하며, 2mN/sec의 속도로 눌러준다. 1㎛ 변형되는 지점에서 5초간 Holding Time을 갖는다. 이후, SNU(SIS-2000, SNU사)를 이용하여 패턴의 두께 및 높이를 측정하여 전과 후의 패턴의 두께 변화로 탄성회복률을 측정한다.A substrate having a column spacer pattern is fabricated on the same production basis as in 1-1 above. The fabricated substrate is measured by SNU (SIS-2000, manufactured by SNU) and the thickness and height of the pattern in the reference state. Thereafter, using a hardness meter (Nano-indenter HM500, Fisher), the pattern is pressed to the point where it is deformed by 1 占 퐉. The hardness meter uses a flat indenter and presses at a rate of 2 mN / sec. Holding time is 5 seconds at the point of 1μm deformation. Thereafter, the thickness and height of the pattern are measured using SNU (SIS-2000, SNU), and the elastic recovery rate is measured by the thickness change of the pattern before and after.

< 탄성 회복률 평가 기준>&Lt; Elasticity recovery rate evaluation standard &

◎: 우수, 98% 이상◎: Excellent, 98% or more

○: 양호, 97% 이상 ~ 98% 미만Good: 97% to less than 98%

△: 부족, 96% 이상 ~ 97% 미만△: insufficient, 96% to less than 97%

X: 악화, 96% 미만X: worse, less than 96%

[표 2] [Table 2]

Figure pat00002
Figure pat00002

Claims (18)

착색제, 알칼리 가용성 수지, 광중합성 화합물, 광중합 개시제 및 용제를 포함하는 착색 감광성 수지 조성물로,
상기 착색제는 유기 블랙 안료, 청색 안료 및 카본 블랙을 포함하며,
상기 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여 착색제 25~55%를 포함하며,
상기 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여, 상기 유기 블랙 안료 3~25%, 상기 청색 안료 5~25%, 및 상기 카본 블랙 5~13% 를 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.A colored photosensitive resin composition comprising a colorant, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator, and a solvent,
Wherein the colorant comprises an organic black pigment, a blue pigment and carbon black,
And 25 to 55% of a colorant based on the total solid weight of the colored photosensitive resin composition,
Wherein the colored photosensitive resin composition comprises 3 to 25% of the organic black pigment, 5 to 25% of the blue pigment, and 5 to 13% of the carbon black, based on the total solid weight of the colored photosensitive resin composition. 청구항 1에 있어서, 상기 유기 블랙 안료는 락탐 블랙, 아닐린 블랙 및 페닐렌 블랙으로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition according to claim 1, wherein the organic black pigment comprises at least one selected from the group consisting of lactam black, aniline black, and phenylene black. 청구항 1에 있어서, 상기 착색 감광성 수지 조성물은 레드 안료 및 바이올렛 안료 중 하나 이상을 더 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition according to claim 1, wherein the colored photosensitive resin composition further comprises at least one of a red pigment and a violet pigment. 청구항 3에 있어서, 상기 바이올렛 안료는 C.I 피그먼트 바이올렛 14, 19, 23, 29, 32, 33, 36 및 37으로 구성되는 군에서 선택되는 1종 이상을 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition according to claim 3, wherein the violet pigment comprises at least one selected from the group consisting of C.I. Pigment Violet 14, 19, 23, 29, 32, 33, 36 and 37. 청구항 3에 있어서, 상기 레드 안료는 C.I. 피그먼트 레드 9, 97, 105, 122, 123, 144, 149, 166, 168, 176, 177, 180, 192, 208, 215, 216, 224, 242, 254, 255 및 264 으로 구성되는 군에서 선택되는 1종 이상을 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.4. The method of claim 3, wherein the red pigment is selected from the group consisting of C.I. Selected from the group consisting of Pigment Red 9, 97, 105, 122, 123, 144, 149, 166, 168, 176, 177, 180, 192, 208, 215, 216, 224, 242, 254, Wherein the coloring photosensitive resin composition comprises at least one of the following components: 청구항 1에 있어서, 상기 청색 안료는 중심 금속을 포함하지 않는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition according to claim 1, wherein the blue pigment does not contain a center metal. 청구항 6에 있어서, 상기 청색 안료는 C.I. 피그먼트 블루 16, 60, 61 및 66으로 구성되는 군에서 선택되는 1종 이상을 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.7. The method of claim 6, wherein the blue pigment is selected from the group consisting of C.I. Pigment Blue 16, 60, 61, and 66. The colored photosensitive resin composition of Claim 1, 청구항 1에 있어서, 상기 알칼리 가용성 수지는 에폭시 수지를 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition according to claim 1, wherein the alkali-soluble resin comprises an epoxy resin. 청구항 1에 있어서, 상기 알칼리 가용성 수지 및 광중합성 화합물은 1:1 내지 5:1의 중량비로 혼합되는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition according to claim 1, wherein the alkali-soluble resin and the photopolymerizable compound are mixed in a weight ratio of 1: 1 to 5: 1. 청구항 1에 있어서, 상기 착색 감광성 수지 조성물은 열 개시제, 충진제, 경화제, 계면활성제, 밀착 촉진제, 산화 방지제, 자외선 흡수제 및 응집 방지제로 이루어진 군으로부터 선택되는 1종 이상의 첨가제를 추가로 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition according to claim 1, further comprising at least one additive selected from the group consisting of a thermal initiator, a filler, a curing agent, a surfactant, an adhesion promoter, an antioxidant, an ultraviolet absorber and an anti- By weight. 청구항 1에 있어서, 상기 착색 감광성 수지 조성물은 첨가제로서 열 개시제를 더 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물. The colored photosensitive resin composition according to claim 1, wherein the colored photosensitive resin composition further comprises a thermal initiator as an additive. 청구항 1에 있어서, 상기 착색 감광성 수지 조성물 중 고형분 총 중량에 대하여 착색제 25 내지 55 중량%, 알칼리 가용성 수지 5 내지 60 중량%, 광중합성 화합물 5 내지 50 중량% 및 광중합 개시제 0.1 내지 40 중량%를 포함하고, 상기 착색 감광성 수지 조성물 총 중량에 대하여 용제 60 내지 90 중량%를 포함하는 것을 특징으로 하는 착색 감광성 수지 조성물.The photosensitive resin composition according to claim 1, which comprises 25 to 55% by weight of a colorant, 5 to 60% by weight of an alkali-soluble resin, 5 to 50% by weight of a photopolymerizable compound and 0.1 to 40% by weight of a photopolymerization initiator based on the total solid content of the colored photosensitive resin composition By weight based on the total weight of the colored photosensitive resin composition, and 60 to 90% by weight of a solvent based on the total weight of the colored photosensitive resin composition. 청구항 11에 있어서, 상기 열 개시제 및 상기 착색 감광성 수지 조성물의 광중합성 개시제는 1:1.1 내지 1:8의 중량비로 혼합되는 것을 특징으로 하는 착색 감광성 수지 조성물. 12. The colored photosensitive resin composition according to claim 11, wherein the thermal initiator and the photopolymerization initiator of the colored photosensitive resin composition are mixed at a weight ratio of 1: 1.1 to 1: 8. 청구항 1에 있어서, 상기 착색제 중 유기 블랙안료: 청색 안료: 카본 블랙의 중량비는 1: 0.25 내지 3.3: 0.15 내지 1.7로 혼합되는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition according to claim 1, wherein the weight ratio of the organic black pigment: blue pigment: carbon black in the colorant is 1: 0.25 to 3.3: 0.15 to 1.7. 청구항 3에 있어서, 상기 착색제 중 유기 블랙안료: 레드 안료 및 바이올렛 안료 중 하나 이상: 청색 안료: 카본 블랙의 중량비는 1: 0.1 내지 1.7: 0.25 내지 3.3: 0.15 내지 1.7로 혼합되는 것을 특징으로 하는 착색 감광성 수지 조성물.The coloring agent according to claim 3, wherein the weight ratio of at least one of the organic black pigment: red pigment and violet pigment in the colorant to the blue pigment: carbon black is 1: 0.1 to 1.7: 0.25 to 3.3: 0.15 to 1.7. Sensitive resin composition. 청구항 1 내지 15항 중 어느 한 항의 착색 감광성 수지 조성물이 3.0μm의 두께를 갖는 경화막으로 형성시에 400~600nm 범위 파장에 대해 0.1% 이하의 광투과도를 나타내고; 700nm~750nm 범위 파장에 대해 10% 이하의 광투과도를 나타내며; 950nm 범위 파장에 대해 15% 이상의 광투과도를 나타내는 것을 특징으로 하는 착색 감광성 수지 조성물.The colored photosensitive resin composition of any one of claims 1 to 15 exhibits a light transmittance of 0.1% or less with respect to a wavelength in the range of 400 to 600 nm when formed into a cured film having a thickness of 3.0 탆; Exhibits a light transmittance of less than 10% for wavelengths in the range of 700 nm to 750 nm; And exhibits a light transmittance of 15% or more with respect to a wavelength in the range of 950 nm to 950 nm. 청구항 1 내지 15항 중 어느 한 항의 착색 감광성 수지 조성물로 제조된블랙 매트릭스, 컬럼 스페이서 또는 블랙 컬럼 스페이서를 포함하는 컬러 필터.A color filter comprising a black matrix, a column spacer or a black column spacer made of the colored photosensitive resin composition according to any one of claims 1 to 15. 청구항 17의 컬러 필터를 포함하는 표시장치.
A display device comprising the color filter of claim 17.
KR1020180007276A 2017-01-20 2018-01-19 A photo sensitive resin composition, a color filter comprising a black metrics, a column spacer or black column spacer prepared by using the composition, and a display devide comprising the color filter KR101966803B1 (en)