KR101897925B1 - A photo sensitive resin composition, a color filter comprising a black metrics, a column spacer or black column spacer prepared by using the composition, and a display device comprising the color filter - Google Patents

Abstract

The present invention relates to a colored photosensitive resin composition comprising an organic black pigment, a colorant containing a blue pigment and carbon black, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator and a solvent, a black matrix manufactured using the colored photosensitive resin composition, a color filter including a column spacer or a black column spacer, and a display device including the color filter. The composition can enhance reliability and can be sufficiently cured by ultraviolet exposure.

Description

TECHNICAL FIELD [0001] The present invention relates to a colored photosensitive resin composition, a color filter including a black matrix, a column spacer or a black column spacer manufactured using the same, and a display device including the color filter column spacer or black column spacer prepared by using the composition, and a display device comprising the color filter}

The present invention relates to a colored photosensitive resin composition, a black matrix made using the same, a color filter including a column spacer or a black column spacer, and a display device including the color filter.

BACKGROUND ART [0002] Color filters are widely used in various display devices such as an image pickup device and a liquid crystal display (LCD), and their application range is rapidly expanding. The color filter used in the image pickup device or the liquid crystal display device may be a color pattern of three colors of red, green and blue or a color pattern of three colors of yellow, magenta and cyan Cyan).

The coloring pattern of each of the color filters is generally formed using a colored photosensitive resin composition comprising a coloring agent such as pigment or dye, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator, and a solvent. The coloring pattern processing using the colored photosensitive resin composition is usually performed by a lithography process.

The colored photosensitive resin is an essential material such as a color filter, a liquid crystal display material, an organic light emitting element, and a display. For example, in the case of a color filter used in a liquid crystal display, the color filter includes pixels composed of red, green, and blue colors, A black matrix is formed at the boundary between the coloring layers of the respective colors. In addition, a black column spacer (BCS) is a portion directly contacting the liquid crystal, and it is required to have excellent solvent resistance and no residue on the organic film.

In recent years, the proportion of LCDs in flat panel displays has been increasing, and the backlight has been adopted as the screen becomes larger. As the backlight brighter, the black matrix also requires higher shading characteristics than the conventional one. However, when the content of carbon black is increased in order to improve the light shielding property, the process characteristics are continuously deteriorated to increase the defect rate, thereby causing a problem that the production yield is lowered.

Increasing the Pigment Weight Concentration (PWC) is inevitable in order to achieve higher light shielding characteristics by using the same colorant. For example, if a photosensitive resin composition of 40% PWC satisfies an optical density of 4.5 levels for a coating film having a thickness of 3 탆, optical density at a level of 1.5 / 탆 per unit thickness can be achieved. Here, in order to further increase the optical density by 0.1 / 占 퐉, it is required to satisfy the optical density of 4.8 level for the coating film of 3 占 퐉 thickness. In order to satisfy the optical density of the 0.3 level, which is further required, the PWC of the photosensitive resin composition must be increased. As a result, the process characteristics are deteriorated and the reliability is lowered.

Korean Patent No. 10-1658374 relates to a colored photosensitive resin composition, which comprises a black coloring agent and a blue coloring agent and satisfies elastic recovery rate and resolution when formed into a cured film, so that it can be manufactured using a column spacer, a black matrix or a black column spacer And can be used for a variety of electronic components including OLED displays and LCD panels. However, it seems to be insufficient for improvement of solvent resistance, optical density and ultraviolet wavelength transmittance.

Korean Patent No. 10-1658374

SUMMARY OF THE INVENTION The present invention has been made to solve the problems of the prior art, and it is an object of the present invention to provide a colored photosensitive resin composition excellent in solvent resistance, optical density and ultraviolet wavelength transmittance.

It is still another object of the present invention to provide a color filter including a pattern layer made of the colored photosensitive resin composition, and a display device including the color filter.

A colored photosensitive resin composition comprising a colorant, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator, and a solvent,

Wherein the colorant comprises an organic black pigment, a blue pigment and carbon black,

The blue pigment is a mixture of C.I. Pigment Blue 80. < / RTI >

The present invention also provides a pattern layer made of the colored photosensitive resin composition of the present invention.

The present invention also provides a color filter comprising the pattern layer of the present invention.

The present invention also provides a display device including the color filter of the present invention.

INDUSTRIAL APPLICABILITY The colored photosensitive resin composition of the present invention is excellent in coloring power. By introducing Pigment Blue 80, it is possible to improve the reliability such as solvent resistance by lowering the Pigment Weight Concentration (PWC) in the colored photosensitive resin composition required to obtain the same optical density (OD / 占 퐉), and the phthalocyanine blue The transmittance in the ultraviolet wavelength region is improved as compared with the pigment, so that the curing by the ultraviolet exposure can be sufficiently performed.

Hereinafter, the present invention will be described in more detail.

The present invention relates to a colored photosensitive resin composition comprising a colorant, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator and a solvent,

Wherein the colorant comprises an organic black pigment, a blue pigment and carbon black,

The blue pigment is a mixture of C.I. Pigment Blue 80. < / RTI >

The present invention relates to a coloring material comprising a blue pigment and a C.I. By including Pigment Blue 80, the colorant content (PWC) of the colored photosensitive resin composition for obtaining the same optical density (OD / 占 퐉) can be lowered. When the content of the coloring agent in the colored photosensitive resin composition is lowered, the components other than the coloring agent are increased and the phenomenon that the coloring agent is eluted in the solvent can be reduced, thereby improving the solvent resistance of the colored photosensitive resin composition and improving the reliability.

C.I. When Pigment Blue 80 is included, the transmittance of the ultraviolet wavelength region in comparison with the phthalocyanine blue pigment is increased. Thus, it is possible to sufficiently form a pattern by the ultraviolet ray exposure, thereby improving the surface hardness and improving the solvent resistance do.

Hereinafter, the colored photosensitive resin composition of the present invention will be described in detail for each component.

coloring agent

The colorant used in the present invention is one which is shielding against visible light, and the colorant of the present invention includes an organic black pigment, a blue pigment, and carbon black.

The organic black pigment includes at least one member selected from the group consisting of lactam black, aniline black and perylene black, and preferably includes lactam black. By including the organic black pigment, the optical density can be improved, the infrared region can be not affected, and the dielectric constant and the transmittance can be improved.

The blue pigment is a compound that does not include a center metal. When the center metal exists, it may affect the liquid crystal driving. In the present invention, by using a compound that does not include a center metal as a blue pigment, can do. In the present invention, the blue pigment is a mixture of C.I. Pigment Blue 80 ".

The C.I. It is possible to obtain a better optical density (OD / 占 퐉) than in the case where Pigment Blue 80 is contained, and the colorant content (PWC) in the colored photosensitive resin composition necessary for obtaining the same optical density can be lowered. When the content of the coloring agent in the colored photosensitive resin composition is lowered, the phenomenon in which the coloring agent is eluted in the solvent can be reduced, and thus reliability such as the solvent resistance of the colored photosensitive resin composition can be improved. C.I. By including Pigment Blue 80, the transmittance in the ultraviolet wavelength range is increased and the curing by the ultraviolet ray exposure is sufficiently performed, which is advantageous for pattern formation, and the surface hardening degree is increased and the solvent resistance is improved.

The carbon black is not particularly limited as long as it is a light-shielding pigment, and known carbon black can be used. Specifically, a channel black, a furnace black, a thermal black, a lamp black, and the like can be given. The carbon black may be coated with a resin, and the carbon black coated with the resin may have a lower conductivity than that of the uncoated carbon black, so that it is possible to impart excellent electrical insulation when forming the black matrix or the column spacer.

In the present invention, the colorant is contained in an amount of 13 to 60% by weight, preferably 25 to 45% by weight based on the total weight of the solid content of the colored photosensitive resin composition. When the colorant is included in an amount of 13 to 60% by weight, the optical density and reliability are excellent.

The organic black pigment may be contained in an amount of 7 to 15% by weight, and preferably 9 to 14% by weight based on the total weight of the solid content of the colored photosensitive resin composition. The blue pigment may be contained in an amount of 11 to 20% by weight, preferably 13 to 20% by weight based on the total weight of the solid content of the colored photosensitive resin composition. The carbon black may be contained in an amount of 5 to 7% by weight, preferably 6 to 6.5% by weight based on the total weight of the solid content of the colored photosensitive resin composition. When the organic black pigment, the blue pigment, and the carbon black are included in the above ranges, a colored photosensitive resin composition having excellent optical density and reliability can be obtained.

In addition, the colored photosensitive resin composition of the present invention contains C.I. Pigment Blue 60 < / RTI > When the colorant is a blue pigment, C.I. When Pigment Blue 60 is further contained, the C.I. Pigment Blue 80 and C.I. Pigment Blue 60 may be mixed in a weight ratio of 1: 1 to 3. Further, it may preferably be mixed in a weight ratio of 1: 1.3 to 2.5. The C.I. Pigment Blue 80 and C.I. When Pigment Blue 60 is contained in the above weight ratio, excellent optical density can be obtained in the region of the propagation field, and a colored photosensitive resin composition having excellent optical density at a wavelength of 600 nm or more can be obtained.

In addition, the colored photosensitive resin composition of the present invention may further comprise a violet pigment as an additional colorant. The violet pigment serves to improve the optical density (O.D.) by reducing the transmittance in the region of 400 to 600 nm. In addition, the content of the organic black pigment can be reduced through the use of the violet pigment, and the reliability of the colored photosensitive resin composition can be improved. The type of the violet pigment is not particularly limited, but C.I. Pigment Violet 19, 23, 29, 31 and 37, and it is preferable to use at least one selected from the group consisting of C.I. It is most preferred to use Pigment Violet 29.

The violet pigment may be contained in an amount of 2 to 8% by weight, preferably 3 to 5% by weight based on the total weight of the solid content of the colored photosensitive resin composition. When the violet pigment is included in the above range, a colored photosensitive resin composition excellent in optical density and reliability can be obtained.

In the present invention, the solid content in the colored photosensitive resin composition means the sum of the components from which the solvent has been removed.

In addition, it is preferable to use a pigment dispersion in which the particle diameter of the pigment is uniformly dispersed. Examples of a method for uniformly dispersing the particle diameter of the pigment include a method of dispersing the pigment by adding a dispersant and the like, and a pigment dispersion in which the pigment is uniformly dispersed in the solution can be obtained by the above method.

Dispersion resin

The dispersing resin serves to prevent the pigment particles present in the colored dispersion liquid from being dissolved in the solvent by coating with a dispersing resin and to inhibit agglomeration between the pigment particles to prevent viscosity increase due to agglomeration of the pigment particles.

The dispersion resin of the present invention may comprise a copolymer of the following formula (1).

[Chemical Formula 1]

Wherein R ₁ and R ₂ are each independently hydrogen or a methyl group, and the molar ratio of a monomer and b monomer is 1:20 to 20: 1.

In the present invention, by including the copolymer of the above formula (1) containing an epoxy group as the dispersion resin, the solvent resistance, storage stability and residual film ratio can be improved.

The weight average molecular weight of the dispersion resin is not particularly limited, but may be 3,000 to 100,000, preferably 3,000 to 50,000, and more preferably 5,000 to 50,000.

The acid value of the dispersion resin is 50 to 200 mgKOH / g based on the solid content. The dispersion stability of the pigment can be improved within the above range.

The dispersion resin may be a copolymer of the copolymer represented by the formula (1) and other monomer copolymerizable therewith.

Specific examples of the monomer capable of copolymerizing with the dispersion resin (1) include styrene, vinyltoluene,? -Methylstyrene, p-chlorostyrene, o-methoxystyrene, m-methoxystyrene, p- Aromatic vinyl compounds such as vinyl benzyl methyl ether, m-vinyl benzyl methyl ether, p-vinyl benzyl methyl ether, o-vinyl benzyl glycidyl ether, m- vinyl benzyl glycidyl ether and p- ; Propyl (meth) acrylate, n-butyl (meth) acrylate, i-butyl (meth) acrylate, alkyl (meth) acrylates such as sec-butyl (meth) acrylate and t-butyl (meth) acrylate; (Meth) acrylate, cyclopentyl (meth) acrylate, cyclohexyl (meth) acrylate, 2-methylcyclohexyl (meth) acrylate, tricyclo [5.2.1.0 2,6] decan- Alicyclic (meth) acrylates such as dicyclopentanyloxyethyl (meth) acrylate and isobornyl (meth) acrylate; Aryl (meth) acrylates such as phenyl (meth) acrylate and benzyl (meth) acrylate; Hydroxyalkyl (meth) acrylates such as 2-hydroxyethyl (meth) acrylate and 2-hydroxypropyl (meth) acrylate; N-cyclohexylmaleimide, N-benzylmaleimide, N-phenylmaleimide, No-hydroxyphenylmaleimide, Nm-hydroxyphenylmaleimide, Np-hydroxyphenylmaleimide, No-methylphenylmaleimide, Nm N-substituted maleimide compounds such as methylphenylmaleimide, Np-methylphenylmaleimide, No-methoxyphenylmaleimide, Nm-methoxyphenylmaleimide and Np-methoxyphenylmaleimide; (meth) acrylamide, Unsaturated amide compounds such as N, N-dimethyl (meth) acrylamide; 3- (methacryloyloxymethyl) -2-trifluoromethyl oxetane, 3- (methacryloyloxymethyl) oxetane, 3- (methacryloyloxymethyl) 2- (methacryloyloxymethyl) oxetane, 2- (methacryloyloxymethyl) -4-trifluoromethyloxetane, and the like Unsaturated oxetane compounds, and the like.

The above-exemplified compounds may be used alone or in combination of two or more.

The dispersing resin of the present invention may be used by further mixing various other alkali-soluble resins known in the art commonly used in the art.

The dispersion resin is contained in an amount of 1 to 20% by weight, and preferably 5 to 15% by weight based on the total weight of the solid content in the colored dispersion. When the content of the dispersing resin is within the above range, the pigment particles are dispersed evenly, aggregation between the pigment particles can be prevented, and solvent resistance and storage stability are improved.

Dispersant

Examples of the dispersing agent include cationic surfactants, anionic surfactants, nonionic surfactants, polyester surfactants, and polyamine surfactants. These surfactants may be used alone or in combination of two or more. Two or more species can be used in combination.

Specific examples of the cationic surfactant include amine salts such as stearylamine hydrochloride and lauryltrimethylammonium chloride, and quaternary ammonium salts.

Specific examples of the anionic surfactant include higher alcohol sulfuric acid ester salts such as sodium lauryl alcohol sulfate ester and sodium oleyl alcohol sulfate ester, alkylsulfates such as sodium laurylsulfate and ammonium laurylsulfate, sodium dodecylbenzenesulfonate, And alkylarylsulfonic acid salts such as sodium dodecylnaphthalenesulfonate.

Specific examples of the nonionic surfactants include polyoxyethylene alkyl ethers, polyoxyethylene aryl ethers, polyoxyethylene alkyl aryl ethers, other polyoxyethylene derivatives, oxyethylene / oxypropylene block copolymers, sorbitan fatty acid esters, Polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol fatty acid esters, glycerin fatty acid esters, polyoxyethylene fatty acid esters, and polyoxyethylene alkylamines.

In addition, polyoxyethylene alkyl ethers, polyoxyethylene alkylphenyl ethers, polyethylene glycol diesters, sorbitan fatty acid esters, fatty acid modified polyesters, tertiary amine-modified polyurethanes, and polyethyleneimines have.

Also, the dispersant preferably includes an acrylate-based dispersant (hereinafter referred to as an acrylate-based dispersant) including butyl methacrylate (BMA) or N, N-dimethylaminoethyl methacrylate (DMAEMA). Dispersing BYK-2000, DISPER BYK-2001, DISPER BYK-2070, DISPER BYK-2150 and the like may be used as the acrylate-based dispersing agent, The rate-based dispersing agents may be used alone or in combination of two or more.

As the dispersant, other resin type pigment dispersants other than the acrylate dispersant may be used. The other resin type dispersing agent may be a known resin type dispersing agent, particularly a polycarboxylic acid ester represented by polyurethane, polyacrylate, an unsaturated polyamide, a polycarboxylic acid, a (partial) amine salt of polycarboxylic acid , An ammonium salt of a polycarboxylic acid, an alkylamine salt of a polycarboxylic acid, a polysiloxane, a long chain polyaminoamide phosphate salt, an ester of a hydroxyl group-containing polycarboxylic acid and a modified product thereof, or a free carboxyl group Amide formed by reaction of polyester with poly (lower alkyleneimine) or salts thereof; Soluble resin or water-soluble polymer compound such as (meth) acrylic acid-styrene copolymer, (meth) acrylic acid- (meth) acrylate ester copolymer, styrene-maleic acid copolymer, polyvinyl alcohol or polyvinylpyrrolidone; Polyester; Modified polyacrylates; Adducts of ethylene oxide / propylene oxide; And phosphate esters.

Examples of the cationic resinous dispersant that can be used as a commercially available product of the other resin type dispersing agent include DISPER BYK-160, DISPER BYK-161, DISPER BYK-162, DISPER BYK-163, DISPER BYK-163 manufactured by BYK -164, DISPER BYK-166, DISPER BYK-171, DISPER BYK-182, DISPER BYK-184, DISPER BYK-2000; EFKA-4060, EFKA-4060, EFKA-4055, EFKA-4055, EFKA-4055, EFKA-4020, EFKA-4015, EFKA-4060, EFKA- 4330, EFKA-4400, EFKA-4406, EFKA-4510, EFKA-4800; SOLSPERS-24000, SOLSPERS-32550, NBZ-4204/10 from Lubirzol; Hinoact T-6000, Hinoact T-7000, Hinoact T-8000; available from Kawaken Fine Chemicals; AJISPUR PB-821, Ajisper PB-822, Ajisper PB-823 manufactured by Ajinomoto; FLORENE DOPA-17HF, fluorene DOPA-15BHF, fluorene DOPA-33, and fluorene DOPA-44 are trade names of Kyoeisha Chemical Co.,

In addition to the acrylate-based dispersant, other resin-type dispersants may be used alone or in combination of two or more, and may be used in combination with an acrylate-based dispersant.

The dispersant is contained in an amount of more than 0 parts by weight and less than 1 part by weight, preferably 0.05 to 0.5 parts by weight, based on 1 part by weight of the colorant. If the dispersant is contained in an amount of more than 0 to 1 part by weight, the uniformly dispersed pigment can be obtained.

Alkali-soluble resin

The alkali-soluble resin contained in the colored photosensitive resin composition of the present invention is a component that imparts solubility to the alkali developing solution used in the developing process. In the present invention, the alkali-soluble resin is not particularly limited, but is preferably a copolymer of a monomer having a carboxyl group and another monomer copolymerizable therewith.

Examples of the monomer having a carboxyl group include unsaturated carboxylic acids having at least one carboxyl group in the molecule, such as unsaturated monocarboxylic acids and unsaturated dicarboxylic acids. Specific examples thereof include acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, and fumaric acid. The monomer having a carboxyl group is a compound having a carbon-carbon unsaturated bond, and each may be used alone or in combination of two or more.

Specific examples of the other monomer include an aromatic vinyl compound, an unsaturated carboxylate compound, an unsaturated aminoalkyl carboxylate compound, an unsaturated glycidyl carboxylate compound, a vinyl carboxylate compound, a vinyl cyanide compound and an unsaturated oxetanecarboxylic acid And the like.

Specific examples of the vinyl compound include styrene,? -Methylstyrene, vinyltoluene, and the like. Specific examples of the unsaturated carboxylate compound include methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, 2-hydroxyethyl acrylate, 2-hydroxyethyl Methacrylate, benzyl acrylate, benzyl methacrylate, and 2-phenylthioethyl acrylate. Specific examples of the unsaturated aminoalkyl carboxylate compound include aminoethyl acrylate and the like. Specific examples of the unsaturated glycidyl carboxylate compound include glycidyl methacrylate and the like. Specific examples of the vinyl carboxylate compound include vinyl acetate and vinyl propionate. Specific examples of the vinyl cyanide compound include acrylonitrile, methacrylonitrile,? -Chloroacrylonitrile, azobisdimethyl valeronitrile, and the like. Specific examples of the unsaturated oxetanecarboxylate compound include 3-methyl-3-acryloxymethyloxetane, 3-methyl-3-methacryloxymethyloxetane, 3-ethyl- Methyl-3-acryloxyethyl oxetane, 3-methyl-3-acryloxyethyl oxetane, 3-methyl- Methyl-3-methacryloxyethyloxetane and the like. These other monomers may be used alone or in combination of two or more.

The alkali-soluble resin may include a copolymer of the formula (1). The alkali-soluble resin may improve the solvent resistance and the storage stability by incorporating the copolymer of the formula (1) containing an epoxy group .

The weight average molecular weight of the alkali-soluble resin is not particularly limited, but may be 3,000 to 100,000, preferably 3,000 to 50,000, and more preferably 5,000 to 50,000.

The alkali-soluble resin is contained in an amount of 5 to 60% by weight, preferably 20 to 50% by weight based on the total weight of the solid content of the colored photosensitive resin composition. When the content of the alkali-soluble resin is within the above-mentioned range, pattern formation is easy and resolution and residual film ratio are improved.

The alkali-soluble resin of the present invention is mixed in an amount of 5 to 80 parts by weight, preferably 20 to 70 parts by weight per 100 parts by weight of the total amount of the alkali-soluble resin and the photopolymerizable compound. When the alkali-soluble resin is mixed within the above-mentioned range, it is possible to provide a colored photosensitive resin composition which has satisfactory solubility and is easy to form a pattern, and prevents reduction of a film portion of a picture element portion at the time of development, have.

Photopolymerizable compound

The photopolymerizable compound contains an unsaturated bond and forms a colored photosensitive resin layer by proceeding a photoreaction with a photopolymerization initiator. The photopolymerizable compound should be a compound capable of polymerizing under the action of a photopolymerization initiator described later.

In the present invention, the functional group of the photopolymerizable compound may be a commonly used (meth) acrylate.

The photopolymerizable compound contains 3 to 10 functional groups, preferably 4 to 8 functional groups.

Specific examples of the trifunctional monomer in the polyfunctional monomer include trimethylolpropane tri (meth) acrylate, ethoxylated trimethylolpropane tri (meth) acrylate, propoxylated trimethylolpropane tri (meth) acrylate And pentaerythritol tri (meth) acrylate.

Specific examples of the tetrafunctional monomer in the polyfunctional monomer include pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, ditrimethylol propane tetraacrylate, ditrimethylol propane tetramethacrylate, dipentaerythritol tetramethacrylate, Tetramethylolmethane tetraacrylate, ethoxylated pentaerythritol tetraacrylate, glycerin tetraacrylate, glycerin tetramethacrylate, and the like.

Specific examples of the monofunctional monomer in the polyfunctional monomer include dipentaerythritol pentaacrylate, dipentaerythritol penta methacrylate, dipentaerythritol monohydroxypentaacrylate, dipentaerythritol monohydroxypentaacrylate, Acrylate and the like.

Specific examples of the hexafunctional monomer in the polyfunctional monomer include dipentaerythritol hexaacrylate, dipentaerythritol hexa methacrylate, and the like.

Specific examples of the 7 to 10 functional monomer in the polyfunctional monomer include tripentaerythritol octamethacrylate, tripentaerythritol octaacrylate, tetrapentaerythritol heptamethacrylate, and tetrapentaerythritol heptaacrylate. .

The photopolymerizable compound is included in the colored photosensitive resin composition of the present invention in an amount of 5 to 50% by weight, preferably 7 to 45% by weight based on the total weight of the solid component. The photopolymerizable compound can improve the strength and flatness of the pixel portion in the range of 5 to 50% by weight.

Photopolymerization initiator

The photopolymerization initiator can be used without limitation as long as it can polymerize the photopolymerizable compound. Preferably, the photopolymerization initiator is an acetophenone-based compound, a benzoin-based compound, a benzophenone-based compound, Based compound, a triazine-based compound, a non-imidazole-based compound, an oxime-based compound, and a thioxanthone-based compound.

Specific examples of the acetophenone compound include diethoxyacetophenone, 2-hydroxy-2-methyl-1-phenylpropan-1-one, benzyldimethylketal, 2- (2-hydroxyethoxy) phenyl] -2-methylpropan-1-one, 1-hydroxycyclohexyl phenyl ketone, 2- 1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) butan- ] Propane-1-one and 2- (4-methylbenzyl) -2- (dimethylamino) -1- (4-morpholinophenyl) butan-1-one.

Specific examples of the benzoin compound include benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, and benzoisobutyl ether.

Specific examples of the benzophenone compound include benzophenone, methyl 0-benzoylbenzoate, 4-phenylbenzophenone, 4-benzoyl-4'-methyldiphenylsulfide, 3,3 ' -Tetra (tert-butylperoxycarbonyl) benzophenone and 2,4,6-trimethylbenzophenone.

Specific examples of the triazine compound include 2,4-bis (trichloromethyl) -6- (4-methoxyphenyl) -1,3,5-triazine, 2,4-bis (4-methoxynaphthyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (Trichloromethyl) -6- [2- (5-methylfuran-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis Yl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- Ethylamino-2-methylphenyl) ethenyl] -1,3,5-triazine and 2,4-bis (trichloromethyl) -6- [2- (3,4 dimethoxyphenyl) ethenyl] -1 , 3,5-triazine, and the like.

Specific examples of the imidazole compound include 2,2'-bis (2-chlorophenyl) -4,4 ', 5,5'-tetraphenylbimidazole, 2,2'-bis , 3-dichlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2-chlorophenyl) -4,4', 5,5'- ) Diimidazole, 2,2'-bis (2-chlorophenyl) -4,4 ', 5,5'-tetra (trialkoxyphenyl) ) -4,4 ', 5,5'-tetraphenyl-1,2'-biimidazole, or an imidazole compound in which the phenyl group at the 4,4', 5,5 'position is substituted by a carboalkoxy group .

More preferably, it is selected from the group consisting of 2,2'-bis (2-chlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (2,3- , 4 ', 5,5'-tetraphenylbiimidazole, 2,2-bis (2,6-dichlorophenyl) -4,4', 5,5'-tetraphenyl- And the like.

Specific examples of the oxime compound include o-ethoxycarbonyl-α-oximino-1-phenylpropan-1-one and the like. Commercially available oxime compounds may be OXE01 and OXE02 of BASF.

The thioxanthone compound is specifically exemplified by 2-isopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone, 1-chloro- Santon et al.

These photopolymerization initiators may be used singly or in combination of two or more.

In the present invention, the photopolymerization initiator is contained in an amount of 0.1 to 40% by weight, preferably 1 to 30% by weight, based on the total solid content of the colored photosensitive resin composition.

The colored photosensitive resin composition becomes highly sensitive within the range of 0.1 to 40% by weight, and the strength of the pixel portion formed using the colored photosensitive resin composition and the smoothness on the surface of the pixel portion can be improved.

In the present invention, a photopolymerization initiator may be used in addition to the photopolymerization initiator.

The photopolymerization initiation assistant is a compound used for promoting polymerization of the photopolymerizable compound initiated by the photopolymerization initiator. Examples of the photopolymerization initiation assistant include an amine compound or an alkoxyanthracene compound.

Specific examples of the amine compound include triethanolamine, methyldiethanolamine, triisopropanolamine, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, isoamyl 4-dimethylaminobenzoate, benzoic acid 2 N, N-dimethyl para-toluidine, 4,4'-bis (dimethylamino) benzphenone (collectively, Michler's ketone), 4,4'-bis (Diethylamino) benzophenone, and 4,4'-bis (ethylmethylamino) benzophenone. Of these, 4,4'-bis (diethylamino) benzophenone is preferable.

Specific examples of the alkoxyanthracene compound include 9,10-dimethoxyanthracene, 2-ethyl-9,10-dimethoxyanthracene, 9,10-diethoxyanthracene and 2-ethyl- Diethoxyanthracene and the like.

Commercially available photopolymerization initiators may also be used. Commercially available photopolymerization initiators include trade names " EAB-F " (manufactured by Hodogaya Chemical Industry Co., Ltd.).

 When the photopolymerization initiator is used, it is preferably used in an amount of usually 0 to 10 mol, preferably 0.01 to 5 mol, per 1 mol of the photopolymerization initiator. When the photopolymerization initiator is used in the range of more than 0 to 10 moles, the sensitivity of the colored photosensitive resin composition becomes higher and the productivity of the color filter formed using the colored photosensitive resin composition can be improved.

solvent

The solvent used in the conventional colored photosensitive resin composition can be used without particular limitation so long as it is effective in dissolving other components contained in the colored photosensitive resin composition and does not react with the solvent. In particular, an ether, an acetate, an aromatic Hydrocarbons, ketones, alcohols or esters.

Examples of the ethers include ethylene glycol monoalkyl ethers such as ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, and ethylene glycol monobutyl ether;

And diethylene glycol dialkyl ethers such as diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol dipropyl ether and diethylene glycol dibutyl ether.

Examples of the acetates include methyl cellosolve acetate, ethyl cellosolve acetate, ethyl acetate, butyl acetate, amyl acetate, methyl lactate, ethyl lactate, butyl lactate, 3-methoxybutyl acetate, 3 Methoxy-1-butylacetate, methoxypentyl acetate, ethylene glycol monoacetate, ethylene glycol diacetate, methyl 3-methoxypropionate, propylene glycol methyl ether acetate, 3-methoxy- Butyl acetate, 1,2-propylene glycol diacetate, ethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, dipropylene glycol methyl ether acetate, 1,3-butylene glycol diacetate, diethylene glycol monobutyl ether Acetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, di Ethylene glycol monoacetate, diethylene glycol diacetate, diethylene glycol monobutyl ether acetate, propylene glycol monoacetate, propylene glycol diacetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, ethylene carbonate and propylene carbonate. .

Examples of the aromatic hydrocarbons include benzene, toluene, xylene, and mesitylene.

The ketones include, for example, methyl ethyl ketone, acetone, methyl amyl ketone, methyl isobutyl ketone, and cyclohexanone.

The alcohols include, for example, ethanol, propanol, butanol, hexanol, cyclohexanol, ethylene glycol, glycerin and 4-hydroxy-4-methyl-2-pentanone.

Examples of the esters include ethyl 3-ethoxypropionate, methyl 3-methoxypropionate and? -Butyrolactone.

These solvents may be used alone or in combination of two or more.

It is preferable to use an organic solvent having a boiling point of 100 to 200 in terms of coating property and drying property, and examples thereof include propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, cyclohexanone, 3-ethoxy Ethyl propionate and methyl 3-methoxypropionate.

The solvent is contained in an amount of 60 to 90% by weight, preferably 65 to 85% by weight based on the total weight of the colored photosensitive resin composition. When the solvent is contained in the range of 60 to 90% by weight, when the solvent is applied by a coating device such as a roll coater, a spin coater, a slit and spin coater, a slit coater (sometimes referred to as a die coater) .

additive

The colored photosensitive resin composition of the present invention includes other additives in addition to the above-mentioned components according to the needs of the ordinary skilled artisan to the extent that the object of the present invention is not impaired.

The additive may further include, for example, at least one additive selected from the group consisting of another polymer compound, a thermal initiator, a curing agent, a surfactant, a adhesion promoter, an antioxidant, an ultraviolet absorber and an anti-

Specific examples of the other polymer compound include a curable resin such as an epoxy resin and a maleimide resin; And thermoplastic resins such as polyvinyl alcohol, polyacrylic acid, polyethylene glycol monoalkyl ether, polyfluoroalkyl acrylate, polyester and polyurethane.

The thermal initiator causes a curing reaction by heat to maximize the initiation efficiency. The thermal initiator may be a peroxide-based compound.

Specific examples of the thermal initiator include, but are not limited to, tetramethyl butyl peroxyneodecanoate (eg Perocta ND, NOF), bis (4-butylcyclohexyl) peroxydicarbonate (eg Peroyl TCP Perfluoroalkane (ex. Perbutyl ND, manufactured by NOF), dipropyl peroxydicarbonate (ex. Peroyl NPP, manufactured by NOF Corporation), di (2-ethylhexyl) peroxycarbonate, butyl peroxyneodecanoate , NOF Corp.), diisopropyl peroxy dicarbonate (e.g., Peroyl IPP, NOF), diethoxyethyl peroxydicarbonate (e.g., Peroyl EEP, NOF), diethoxy (Peroyl OEP, NOF), hexyl peroxydicarbonate (e.g., Perhexyl ND, NOF), dimethoxybutyl peroxydicarbonate (e.g. Peroyl MBP, NOF Peroyl SOP, NOF), dibutyl peroxydicarbonate, dicetyl peroxy dicyclohexylcarbodiimide, bis (3-methoxy-3-methoxybutyl) peroxydicarbonate Dicabo Peroxypivalate, hexyl peroxypivalate (ex. Perhexyl PV, NOF), and the like. Perbutyl (NOF), trimethyl hexanoyl peroxide (e.g., Peroyl 355, NOF), dimethylhydroxybutyl peroxyneodecanoate (ex Luperox 610M75) , Atofina (manufactured by Atofina), amyl peroxyneodecanoate (ex Luperox 546M75, Atofina), butyl peroxyneodecanoate (ex Luperox 10M75, Atofina), t-butyl peroxy Butyl peroxypivalate, neopentyl peroxypivalate, neoheptanoate, amyl peroxypivalate (ex Luperox 546M75, Alofina), t-butyl peroxypivalate, t-amylperoxy-2-ethylhexanoate, Oxy-2-ethylhexanoate, lauryl peroxide, dilauroyl peroxide, didecanoyl peroxide, benzoyl peroxide, dibenzoyl peroxide, 2,2- Bis (tert-butylperoxy) -cyclohexane, 2,5-bis (butylperoxy) -2,5-dimethylhexane, 2,5- Butyl peroxide, tert-butyl peroxide, tert-butyl peroxybenzoate, tert-butyl peroxyacetate, cumene hydroperoxide, dicumyl peroxide, lauroyl peroxide, 2,4-pentanedione peroxide, tert-butyl peracetate, Peracetic acid, and potassium persulfate may be used.

With respect to the content of the thermal initiator, it is preferably contained in an amount of 1 to 10% by weight, and more preferably 1 to 5% by weight based on the total solid content of the colored photosensitive resin composition. When it is contained in the above-mentioned contents, it is more preferable for fairness and undercut.

The curing agent is used for increasing the curing depth and mechanical strength, and specific examples thereof include an epoxy compound, a polyfunctional isocyanate compound, a melamine compound and an oxetane compound.

Specific examples of the epoxy compound in the curing agent include bisphenol A epoxy resin, hydrogenated bisphenol A epoxy resin, bisphenol F epoxy resin, hydrogenated bisphenol F epoxy resin, novolak epoxy resin, other aromatic epoxy resin, alicyclic epoxy resin Alicyclic or aromatic epoxy compounds, butadiene (co) polymeric epoxides and isoprene (co) polymers other than the brominated derivatives, epoxy resins and brominated derivatives of these epoxy resins, glycidyl ester resins, glycidyl amine resins, (Co) polymer epoxides, glycidyl (meth) acrylate (co) polymers, and triglycidyl isocyanurate.

Specific examples of the oxetane compound in the curing agent include carbonates bisoxetane, xylene bisoxetane, adipate bisoxetane, terephthalate bisoxetane, cyclohexanedicarboxylic acid bisoxetane, and the like.

The curing agent may be used together with a curing assistant compound capable of ring-opening polymerization of the epoxy group of the epoxy compound and the oxetane skeleton of the oxetane compound together with the curing agent. The curing assistant compound includes, for example, polyvalent carboxylic acids, polyvalent carboxylic anhydrides, and acid generators. The polyvalent carboxylic acid anhydrides may be those commercially available as an epoxy resin curing agent. Specific examples of the above-mentioned epoxy resin curing agents include commercial products such as ADEKA HARDONA EH-700 (ADEKA INDUSTRIAL CO., LTD.), Trade name (RICACIDO HH) (manufactured by New Japan Chemical Co., Ltd.) Manufactured by Shin-Etsu Chemical Co., Ltd.). The curing agents exemplified above may be used alone or in combination of two or more.

The surfactant can be used for further improving the film-forming property of the photosensitive resin composition, and for example, a surfactant such as silicon, fluorine, ester, cationic, anionic, nonionic or amphoteric surfactant can be used , A silicone surfactant or a fluorine surfactant can be preferably used.

TS-4440, TSF-4300, TSF-4445, TSF-4446, and TSF-4400 of GE Toshiba Silicones such as DC3PA, DC7PA, SH11PA, SH21PA and SH-8400 from Dow Corning Toray Silicone Co., 4460 and TSF-4452. F-472, F-482 and F-489 (Dainippon Ink and Chemicals, Inc.), BM-1000 and BM-1100 (trade names, (BM Chemie), Proride FC-135 / FC-170C / FC-430 (Sumitomo 3M Co., Ltd.), and the like.

Further examples of the surfactant include polyoxyethylene alkyl ethers, polyoxyethylene alkylphenyl ethers, polyethylene glycol diesters, sorbitan fatty acid esters, fatty acid modified polyesters, tertiary amine modified polyurethanes, polyethylene (Shin-Etsu Chemical Co., Ltd.), Polyflow (Kyoei Chemical Co., Ltd.), F-Top (Tochem Products Inc.), Megapack (Dainippon Ink Chemical Industry Co., Ltd.), Florad (Asahi Glass Co., Ltd.), Sorusparas (Zeneca Co., Ltd.), EFKA (EFKACHEMICALS Co., Ltd.), and PB821 (Ajinomoto Co., Ltd.).

The above-exemplified surfactants may be used alone or in combination of two or more.

The adhesion promoter is an additive which is used for improving coatability and adhesiveness with a substrate, and is a silane coupling agent containing a reactive substituent selected from the group consisting of a carboxyl group, a methacryloyl group, an isocyanate group, an epoxy group, . Specific examples of the silane coupling agent include vinyltrimethoxysilane, vinyltriethoxysilane, vinyltris (2-methoxyethoxy) silane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxy Silane, N- (2-aminoethyl) -3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3- glycidoxypropylmethyldimethoxysilane , 3-chloropropylmethyldimethoxysilane, 3-chloropropyltrimethoxysilane, 3-methacryloyloxypropyltrimethoxysilane, 3-chloropropyltrimethoxysilane, 3-chloropropyltrimethoxysilane, -Mercaptopropyltrimethoxysilane, trimethoxysilylbenzoic acid, vinyltriacetoxysilane,? -Isocyanate propyltriethoxysilane, and the like.

Specific examples of the antioxidant include 2,2'-thiobis (4-methyl-6-t-butylphenol) and 2,6-di-t-butyl-4-methylphenol.

Specific examples of the ultraviolet absorber include 2- (3-tert-butyl-2-hydroxy-5-methylphenyl) -5-chlorobenzothiazole and alkoxybenzophenone.

Specific examples of the anti-aggregation agent include sodium polyacrylate and the like.

The additive is contained in an amount of 0.01 to 10% by weight, preferably 0.05 to 2% by weight based on the total weight of the solid content of the colored photosensitive resin composition.

The thus-prepared colored photosensitive resin composition can be preferably used for the production of a display device, preferably a black matrix of a liquid crystal display, a column spacer for maintaining a cell gap, or a black column spacer.

The column spacer, the black matrix and / or the black column spacer according to the present invention has an advantage of high reliability and excellent shielding due to high optical density.

In particular, the colored photosensitive resin composition of the present invention can be suitably used for producing a black column spacer (black matrix integrated spacer), and the black column spacer does not form a black matrix and a column spacer, Means that the matrix and the column spacer are integrally formed.

The present invention also relates to a color filter comprising a pattern layer produced using the colored photosensitive resin composition.

The color filter according to the present invention has an advantage of high reliability due to high optical density and excellent shielding property. The color filter includes a substrate and a pattern layer formed on the substrate.

The substrate may be the substrate of the color filter itself, or may be a portion where a color filter is placed on a display device or the like, and is not particularly limited. The substrate can be glass, silicon (Si), may be a silicon oxide (SiO _x) or a polymer substrate, the polymer substrate, such as polyether sulfone (polyethersulfone, PES), or polycarbonate (polycarbonate, PC).

The pattern layer may include a column spacer, a black matrix and / or a black column spacer as a layer containing a cured product of the colored photosensitive resin composition of the present invention.

The pattern layer may be a layer formed by applying the above-mentioned colored photosensitive resin composition and exposing, developing, and thermosetting in a predetermined pattern, and the pattern layer may be formed by performing a method commonly known in the art.

The color filter including the substrate and the pattern layer as described above may further include a partition wall formed between the respective patterns, and may further include a black matrix, but is not limited thereto.

The present invention also relates to a display device including the color filter. In short, the liquid crystal display device according to the present invention may include a color filter including a pattern layer containing a cured product of the above-mentioned colored photosensitive resin composition.

The color filter of the present invention is applicable not only to a general liquid crystal display device but also to various image display devices such as an electroluminescence display device, a plasma display device, and a field emission display device.

When the liquid crystal display device includes the color filter including the pattern layer according to the present invention, there is an advantage that the shielding property and the reliability are excellent.

A typical patterning process for forming a black matrix, column spacer or black column spacer according to the photolithography method

a) applying a colored photosensitive resin composition to a substrate;

b) prebaking step of drying the solvent;

c) applying a photomask onto the obtained film to irradiate an actinic ray to cure the exposed portion;

d) performing a developing step of dissolving the unexposed portion using an aqueous alkali solution; And

e) drying and post-baking.

A glass substrate or a polymer plate is used as the substrate. As the glass substrate, in particular, soda lime glass, barium or strontium-containing glass, lead glass, aluminosilicate glass, borosilicate glass, barium borosilicate glass or quartz can be preferably used. Examples of the polymer plate include polycarbonate, acrylic, polyethylene terephthalate, polyether sulfide, and polysulfone.

The coating may be performed by a wet coating method using a coating apparatus such as a roll coater, a spin coater, a slit and spin coater, a slit coater (which may be referred to as a die coater), an ink jet or the like so as to obtain a desired thickness.

Prebaking is performed by heating with an oven, a hot plate or the like. At this time, the heating temperature and the heating time in the pre-baking are appropriately selected depending on the solvent to be used, for example, at a temperature of 80 to 150 for 1 to 30 minutes.

The exposure performed after the pre-baking is performed by an exposure machine, and exposed through a photomask to expose only the portion corresponding to the pattern. The light to be irradiated may be, for example, visible light, ultraviolet light, X-ray, electron beam, or the like.

The alkali development after exposure is performed for the purpose of removing the colored photosensitive resin composition in a portion where the non-exposed portion is not removed, and a desired pattern is formed by this development. As the developer suitable for the alkali development, for example, an aqueous solution of a carbonate of an alkali metal or an alkaline earth metal may be used. Particularly, using a weakly alkaline aqueous solution containing 1 to 3% by weight of a carbonate such as sodium carbonate, potassium carbonate, lithium carbonate or the like is carried out using a developing machine or an ultrasonic cleaner at a temperature of 10 to 50, preferably 20 to 40 do.

The post bake is performed in order to improve the adhesion between the patterned film and the substrate, and is performed by heat treatment at 80 to 220 for 10 to 120 minutes. Post-baking is performed by using an oven, a hot plate, or the like as in pre-baking.

In this case, the thickness of the black matrix is preferably 0.2 to 20 占 퐉, more preferably 0.5 to 10 占 퐉, and particularly preferably 0.8 to 5 占 퐉.

The film thickness of the column spacer and the black column spacer is preferably 0.1 탆 to 8 탆, more preferably 0.1 탆 to 6 탆, and particularly preferably 0.1 탆 to 4 탆.

The black matrix, the column spacer or the black column spacer made of the colored photosensitive resin composition of the present invention is excellent in physical properties such as optical density, adhesion, electrical insulation and light shielding property, and is excellent in heat resistance and solvent resistance, It is possible to improve the reliability.

Hereinafter, the present invention will be described in more detail by way of examples. However, the following examples are intended to further illustrate the present invention, and the scope of the present invention is not limited by the following examples. The following embodiments can be appropriately modified and changed by a person skilled in the art within the scope of the present invention.

Synthetic example. Dispersion resin synthesis

277 g of methoxybutyl acetate was added to an internal 1 L separable flask equipped with a stirrer, a thermometer, a reflux condenser, a dropping funnel and a nitrogen inlet tube, and heated to 80 ° C. Then, a solution of 3,4-epoxytricyclo [5.2.1.0 ^2,6 ] decan-9-yl acrylate and 3,4-epoxytricyclo [5.2.1.0 ^2,6 ] decan- 50 molar ratio, 49 g of methacrylic acid and 23 g of azobisdimethylvaleronitrile were dissolved in 350 g of methoxybutyl acetate to prepare a mixed solution. The mixed solution was dropped into the flask over 5 hours using a dropping funnel, and the reaction was carried out for 3 hours to prepare a dispersion resin (solid content (NV) 35.0% by weight). The prepared dispersion resin had an acid value of 69.8 KOH mg / g, a weight average molecular weight (Mw) of 12,300 and a dispersion degree (Mw / Mn) of 2.1.

Production Examples 1 to 6. Preparation of colored dispersion

A mixture of the dispersion resin with the colorant, the dispersant and the solvent was prepared. Then, zirconia beads (average particle diameter: 0.1 mm) were mixed with the mixture at a weight ratio of 50:50 and dispersed for 4 to 6 hours using a bead mill. After dispersion was completed, the mixture was filtered to prepare a colored dispersion, and the content thereof is shown in Table 1 below.

[Table 1]

(Unit: parts by weight)

coloring agent

100CF: Organic black pigment (BASF)

B15: 6: C.I. Pigment Blue 15: 6

CB: carbon black

B80: C.I. Pigment Blue 80

B60: C.I. Pigment Blue 60

V29: C.I. Pigment Violet 29

Dispersion resin: The dispersion resin synthesized in Synthesis Example

Dispersant: DisperBYK-2000 (BYK)

Solvent: Propylene glycol monomethyl ether acetate (PGMEA)

Examples 1 to 9 and Comparative Examples 1 to 2

A colored photosensitive resin composition was prepared by mixing the above colored dispersion with an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator, an additive and a solvent, and the content thereof is shown in Table 2 below.

[Table 2]

(Unit: parts by weight)

Colored dispersion

A1: The coloring dispersion prepared in Production Example 1

A2: The coloring dispersion prepared in Production Example 2

A3: Colored dispersion prepared in Production Example 3

A4: The coloring dispersion prepared in Production Example 4

A5: The coloring dispersion prepared in Production Example 5

A6: The coloring dispersion prepared in Production Example 6

Alkali-soluble resin: The dispersion resin

Photopolymerizable compound: dipentaerythritol hexaacrylate (DPHA) (Nippon Kayaku Co., Ltd.)

Photopolymerization initiator: 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) butan-1-one (Irgacure 369: Ciba)

Additive: DisperBYK-163 (BYK)

Solvent: Propylene glycol monomethyl ether acetate (PGMEA)

Experimental Example

1. Evaluation of solvent resistance

(Corning), which had been washed with a neutral detergent and water, was post-dried, and then each of the colored photosensitive resin compositions prepared in Examples 1 to 9 and Comparative Examples 1 and 2 was spin-coated so as to have a final film thickness of 3.0 탆 Respectively. Then, it was placed on a heating plate and dried at a temperature of 80 to 120 for 1 to 2 minutes to remove the solvent. Subsequently, exposure was performed at an exposure amount of 25 to 35 mJ / cm 2, followed by baking at 200 to 250 for 10 to 30 minutes to prepare a colored substrate coated with the patterned photosensitive resin composition on the entire surface without a pattern.

The substrate was cut to a size of 3 cm x 3 cm and immersed in 100 N-methyl pyrrolidone (NMP) solvent for 60 minutes. Then, only the NMP solvent was extracted, and the degree of dissolution in the NMP solvent was evaluated by measuring the absorbance at a wavelength of visible light using a UV-vis spectrometer (UV-2600, Shimadzu) to evaluate the solvent resistance. The measurement results of the absorbance are shown in Table 3 below.

2. Optical density evaluation

A substrate was prepared in the same manner as in the method for producing a substrate prepared in the above solvent resistance evaluation.

The absorbance (OD) was measured using a photometer (X-rite) and the film thickness was measured using a film thickness meter (Dektak). The optical density (OD / 占 퐉) was calculated using the measurement results, and the results are shown in Table 3 below.

3. Evaluation of substrate absorbance

A substrate was prepared in the same manner as in the method for producing a substrate prepared in the above solvent resistance evaluation.

The absorbance at ultraviolet wavelength was measured using a UV-vis spectrometer (UV-2600, Shimadzu). The results are shown in Table 3 below.

[Table 3]

Examples 1 to 9 of the colored photosensitive resin compositions of the present invention exhibited excellent results in solvent resistance as measured by NMP solvent absorbance at a low value and exhibited excellent optical density characteristics even when PWC was low and absorbance in the ultraviolet wavelength range It was confirmed that the surface hardening degree was further improved in ultraviolet ray hardening, which is advantageous for pattern formation.

C.I. Pigment Blue 80 or 60, and C.I. The colored photosensitive resin compositions of Comparative Examples 1 and 2 including Pigment Blue 15: 6 showed relatively low optical density due to the relatively high absorbance of NMP solvent measured and showed poor solvent resistance. In the ultraviolet wavelength region Was measured to be relatively high.

Claims (13)

A colored photosensitive resin composition comprising a colorant, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator, and a solvent,
Wherein the colorant comprises an organic black pigment, a blue pigment not containing a center metal, and carbon black,
Wherein the blue pigment is CI Pigment Blue 80. 12. The colored photosensitive resin composition according to claim 1, The colored photosensitive resin composition according to claim 1, wherein the organic black pigment comprises at least one selected from the group consisting of lactam black, aniline black, and perylene black. The colored photosensitive resin composition according to claim 1, wherein the colored photosensitive resin composition is a blue pigment. Pigment Blue < SEP > 60 < SEP > 4. The method according to claim 3, wherein the C.I. Pigment Blue 80 and C.I. Pigment Blue 60 is mixed at a weight ratio of 1: 1 to 3. The colored photosensitive resin composition according to claim 1, wherein the colored photosensitive resin composition further comprises a violet pigment as an additional colorant. 6. The composition of claim 5, wherein the violet pigment is selected from the group consisting of C.I. Pigment Violet 19, 23, 29, 31 and 37. The colored photosensitive resin composition according to claim 1, The colored photosensitive resin composition according to claim 1, wherein the colored photosensitive resin composition comprises 7 to 15% by weight of an organic black pigment, 11 to 20% by weight of a blue pigment, and 5 to 7% by weight of carbon black based on the total solid content of the colored photosensitive resin composition Composition. The photosensitive resin composition according to claim 1, which comprises 13 to 60% by weight of a colorant, 5 to 60% by weight of an alkali-soluble resin, 5 to 50% by weight of a photopolymerizable compound and 0.1 to 40% by weight of a photopolymerization initiator based on the total weight of solid components in the colored photosensitive resin composition By weight based on the total weight of the colored photosensitive resin composition, and 60 to 90% by weight of a solvent based on the total weight of the colored photosensitive resin composition. The colored photosensitive resin composition according to claim 1, wherein the colored photosensitive resin composition further comprises at least one additive selected from the group consisting of another polymer compound, a curing agent, a surfactant, an adhesion promoter, an antioxidant, an ultraviolet absorber and an anti- Colored photosensitive resin composition. A pattern layer made of the colored photosensitive resin composition according to any one of claims 1 to 9. 11. The pattern layer according to claim 10, wherein the pattern layer is at least one selected from the group consisting of a column spacer, a black matrix and a black column spacer. A color filter comprising the patterned layer of claim 10. A display device comprising the color filter of claim 12.