KR20180084974A - Mn 함유 합금화 용융 아연 도금 강판 및 그의 제조 방법 - Google Patents
Mn 함유 합금화 용융 아연 도금 강판 및 그의 제조 방법 Download PDFInfo
- Publication number
- KR20180084974A KR20180084974A KR1020187017602A KR20187017602A KR20180084974A KR 20180084974 A KR20180084974 A KR 20180084974A KR 1020187017602 A KR1020187017602 A KR 1020187017602A KR 20187017602 A KR20187017602 A KR 20187017602A KR 20180084974 A KR20180084974 A KR 20180084974A
- Authority
- KR
- South Korea
- Prior art keywords
- manufacturing
- steel sheet
- same
- galvanized steel
- dip galvanized
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/18—Layered products comprising a layer of metal comprising iron or steel
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/002—Heat treatment of ferrous alloys containing Cr
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/005—Heat treatment of ferrous alloys containing Mn
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/008—Heat treatment of ferrous alloys containing Si
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0224—Two or more thermal pretreatments
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/261—After-treatment in a gas atmosphere, e.g. inert or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
- C23C2/29—Cooling or quenching
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
- C23C2/36—Elongated material
- C23C2/40—Plates; Strips
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/001—Austenite
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JPJP-P-2015-250124 | 2015-12-22 | ||
JP2015250124A JP6164280B2 (ja) | 2015-12-22 | 2015-12-22 | 表面外観および曲げ性に優れるMn含有合金化溶融亜鉛めっき鋼板およびその製造方法 |
PCT/JP2016/005079 WO2017110054A1 (ja) | 2015-12-22 | 2016-12-08 | Mn含有合金化溶融亜鉛めっき鋼板およびその製造方法 |
Publications (2)
Publication Number | Publication Date |
---|---|
KR20180084974A true KR20180084974A (ko) | 2018-07-25 |
KR102127776B1 KR102127776B1 (ko) | 2020-06-29 |
Family
ID=59089926
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
KR1020187017602A KR102127776B1 (ko) | 2015-12-22 | 2016-12-08 | Mn 함유 합금화 용융 아연 도금 강판 및 그의 제조 방법 |
Country Status (7)
Country | Link |
---|---|
US (1) | US11136641B2 (ko) |
EP (1) | EP3396005B1 (ko) |
JP (1) | JP6164280B2 (ko) |
KR (1) | KR102127776B1 (ko) |
CN (1) | CN108474094B (ko) |
MX (1) | MX2018007574A (ko) |
WO (1) | WO2017110054A1 (ko) |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102018102624A1 (de) * | 2018-02-06 | 2019-08-08 | Salzgitter Flachstahl Gmbh | Verfahren zur Herstellung eines Stahlbandes mit verbesserter Haftung metallischer Schmelztauchüberzüge |
DE102019108457B4 (de) * | 2019-04-01 | 2021-02-04 | Salzgitter Flachstahl Gmbh | Verfahren zur Herstellung eines Stahlbandes mit verbesserter Haftung metallischer Schmelztauchüberzüge |
WO2023094856A1 (en) | 2021-11-24 | 2023-06-01 | Arcelormittal | Zinc coated mn-containing advanced high strength steel and method of manufacturing the same |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS4718782Y1 (ko) | 1967-11-02 | 1972-06-28 | ||
JP4464720B2 (ja) | 2003-04-10 | 2010-05-19 | 新日本製鐵株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP2013194270A (ja) | 2012-03-19 | 2013-09-30 | Jfe Steel Corp | 高強度溶融亜鉛めっき鋼板の製造方法および高強度溶融亜鉛めっき鋼板 |
JP2014015676A (ja) | 2012-06-15 | 2014-01-30 | Jfe Steel Corp | 高強度溶融亜鉛めっき鋼板の製造方法および高強度溶融亜鉛めっき鋼板 |
KR20140068122A (ko) * | 2011-09-30 | 2014-06-05 | 신닛테츠스미킨 카부시키카이샤 | 용융 아연 도금 강판 및 그 제조 방법 |
Family Cites Families (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6087019A (en) * | 1996-05-31 | 2000-07-11 | Kawasaki Steel Corporation | Plated steel sheet |
JP4718782B2 (ja) | 2003-02-06 | 2011-07-06 | 新日本製鐵株式会社 | 合金化溶融亜鉛めっき鋼板、およびその製造方法 |
JP4415579B2 (ja) * | 2003-06-30 | 2010-02-17 | Jfeスチール株式会社 | 溶融亜鉛めっき鋼板の製造方法 |
FR2876711B1 (fr) * | 2004-10-20 | 2006-12-08 | Usinor Sa | Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese |
EP2009127A1 (en) * | 2007-06-29 | 2008-12-31 | ArcelorMittal France | Process for manufacturing a galvanized or a galvannealed steel sheet by DFF regulation |
JP5444752B2 (ja) * | 2009-02-23 | 2014-03-19 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法および高強度合金化溶融亜鉛めっき鋼板の製造方法 |
DE102009018577B3 (de) * | 2009-04-23 | 2010-07-29 | Thyssenkrupp Steel Europe Ag | Verfahren zum Schmelztauchbeschichten eines 2-35 Gew.-% Mn enthaltenden Stahlflachprodukts und Stahlflachprodukt |
JP5521446B2 (ja) * | 2009-09-07 | 2014-06-11 | Jfeスチール株式会社 | 耐めっき剥離性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5667363B2 (ja) * | 2009-11-02 | 2015-02-12 | 株式会社神戸製鋼所 | 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法 |
JP5862002B2 (ja) * | 2010-09-30 | 2016-02-16 | Jfeスチール株式会社 | 疲労特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
KR20120056588A (ko) * | 2010-11-25 | 2012-06-04 | 주식회사 포스코 | 도금성 및 도금밀착성이 우수한 용융아연도금강판 |
JP5966528B2 (ja) * | 2011-06-07 | 2016-08-10 | Jfeスチール株式会社 | めっき密着性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
RU2584060C2 (ru) * | 2011-09-30 | 2016-05-20 | Ниппон Стил Энд Сумитомо Метал Корпорейшн | Стальной лист, снабженный образованным горячей гальванизацией погружением слоем с превосходными смачивающей способностью плакирующего покрытия и адгезией слоя покрытия, и способ его получения |
JP6111522B2 (ja) * | 2012-03-02 | 2017-04-12 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板及びその製造方法 |
JP5982906B2 (ja) * | 2012-03-19 | 2016-08-31 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
WO2013157222A1 (ja) * | 2012-04-18 | 2013-10-24 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP2013256714A (ja) * | 2012-05-14 | 2013-12-26 | Jfe Steel Corp | めっき後外観に優れた高強度合金化溶融亜鉛めっき鋼板及びその製造方法 |
KR20160143893A (ko) * | 2012-06-15 | 2016-12-14 | 제이에프이 스틸 가부시키가이샤 | 고강도 강판 및 고강도 용융 아연 도금 강판 그리고 그것들의 제조 방법 |
KR101510505B1 (ko) | 2012-12-21 | 2015-04-08 | 주식회사 포스코 | 우수한 도금성과 초고강도를 갖는 고망간 용융아연도금강판의 제조방법 및 이에 의해 제조된 고망간 용융아연도금강판 |
JP5852690B2 (ja) * | 2013-04-26 | 2016-02-03 | 株式会社神戸製鋼所 | ホットスタンプ用合金化溶融亜鉛めっき鋼板 |
JP2015193907A (ja) * | 2014-03-28 | 2015-11-05 | 株式会社神戸製鋼所 | 加工性、および耐遅れ破壊特性に優れた高強度合金化溶融亜鉛めっき鋼板、並びにその製造方法 |
-
2015
- 2015-12-22 JP JP2015250124A patent/JP6164280B2/ja active Active
-
2016
- 2016-12-08 EP EP16877959.3A patent/EP3396005B1/en active Active
- 2016-12-08 MX MX2018007574A patent/MX2018007574A/es unknown
- 2016-12-08 US US16/064,526 patent/US11136641B2/en active Active
- 2016-12-08 KR KR1020187017602A patent/KR102127776B1/ko active IP Right Grant
- 2016-12-08 WO PCT/JP2016/005079 patent/WO2017110054A1/ja active Application Filing
- 2016-12-08 CN CN201680075276.3A patent/CN108474094B/zh active Active
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS4718782Y1 (ko) | 1967-11-02 | 1972-06-28 | ||
JP4464720B2 (ja) | 2003-04-10 | 2010-05-19 | 新日本製鐵株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
KR20140068122A (ko) * | 2011-09-30 | 2014-06-05 | 신닛테츠스미킨 카부시키카이샤 | 용융 아연 도금 강판 및 그 제조 방법 |
JP2013194270A (ja) | 2012-03-19 | 2013-09-30 | Jfe Steel Corp | 高強度溶融亜鉛めっき鋼板の製造方法および高強度溶融亜鉛めっき鋼板 |
JP2014015676A (ja) | 2012-06-15 | 2014-01-30 | Jfe Steel Corp | 高強度溶融亜鉛めっき鋼板の製造方法および高強度溶融亜鉛めっき鋼板 |
Also Published As
Publication number | Publication date |
---|---|
WO2017110054A1 (ja) | 2017-06-29 |
US11136641B2 (en) | 2021-10-05 |
JP2017115189A (ja) | 2017-06-29 |
EP3396005A4 (en) | 2018-10-31 |
EP3396005A1 (en) | 2018-10-31 |
CN108474094A (zh) | 2018-08-31 |
KR102127776B1 (ko) | 2020-06-29 |
US20190003006A1 (en) | 2019-01-03 |
CN108474094B (zh) | 2020-06-19 |
MX2018007574A (es) | 2018-09-21 |
JP6164280B2 (ja) | 2017-07-19 |
EP3396005B1 (en) | 2020-04-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP3564400A4 (en) | HIGH STRENGTH GALVANIZED STEEL SHEET AND METHOD FOR MANUFACTURING THE SAME | |
EP3257962A4 (en) | High-strength hot-dip galvanized steel sheet and manufacturing method therefor | |
EP3219821A4 (en) | High-strength hot-dip galvanized steel sheet and production method thereof | |
EP3309273A4 (en) | Galvannealed steel sheet and method for manufacturing same | |
EP3219822A4 (en) | High-strength hot-dip galvanized steel sheet and production method thereof | |
EP3144406A4 (en) | High-strength cold rolled steel sheet having excellent ductility, hot-dip galvanized steel sheet and method for manufacturing same | |
EP3438307A4 (en) | HOT GALVANIZED STEEL SHEET | |
EP3318652A4 (en) | High-strength cold-rolled steel sheet, high-strength galvanized steel sheet, and high-strength galvannealed steel sheet | |
EP3399062A4 (en) | High-strength steel sheet, high-strength galvanized steel sheet, and method for manufacturing same | |
EP3272906A4 (en) | Hot-dip galvanized steel sheet | |
PL3216887T3 (pl) | Blacha stalowa cienka cynkowana zanurzeniowo na gorąco | |
EP3214193A4 (en) | High-strength steel sheet, high-strength hot-dip galvanized steel sheet, high-strength hot-dip aluminum-coated steel sheet, and high-strength electrogalvanized steel sheet, and methods for manufacturing same | |
EP3719157A4 (en) | HIGH STRENGTH GALVANIZED STEEL SHEET AND METHOD FOR MANUFACTURING IT | |
EP3040440A4 (en) | HOT GALVANIZED STEEL SHEET WITH HIGH STRENGTH AND METHOD OF MANUFACTURING THE SAME | |
EP3106528A4 (en) | High-strength hot-dip galvanized steel sheet, and method for manufacturing high-strength alloyed hot-dip galvanized steel sheet | |
EP3623492A4 (en) | PROCESS FOR PRODUCING HOT GALVANIZED STEEL SHEET | |
EP3719156A4 (en) | HIGH STRENGTH GALVANIZED STEEL SHEET AND METHOD FOR MANUFACTURING IT | |
PL3216892T3 (pl) | Blacha stalowa cienka ocynkowana ogniowo | |
EP3604582A4 (en) | COLD ROLLED STEEL SHEET AND HOT GALVANIZED COLD ROLLED STEEL SHEET | |
EP3187607A4 (en) | High-strength hot-dip galvanized steel sheet having superb stretch-flangeability, in-plane stability of stretch-flangeability, and bendability, and method for producing same | |
KR20180084997A (ko) | 고강도 용융 도금 열연 강판 및 그의 제조 방법 | |
EP3257961A4 (en) | High-strength hot-dip galvanized steel sheet and manufacturing method therefor | |
EP3235922A4 (en) | Hot dipped galvanized steel sheet with excellent hole expansibility, hot dipped galvannealed steel sheet, and manufacturing method therefor | |
EP3138931A4 (en) | Method for manufacturing high-strength hot-dip galvanized steel sheet | |
PL3018230T3 (pl) | Blacha stalowa cienka walcowana na zimno, ocynkowana blacha stalowa cienka walcowana na zimno oraz sposób ich wytwarzania |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
A201 | Request for examination | ||
E902 | Notification of reason for refusal | ||
E701 | Decision to grant or registration of patent right | ||
GRNT | Written decision to grant |