KR20180022802A - 자가-보수 특성을 갖는 자가-지지형 합성 폴리머 방수 멤브레인 - Google Patents
자가-보수 특성을 갖는 자가-지지형 합성 폴리머 방수 멤브레인 Download PDFInfo
- Publication number
- KR20180022802A KR20180022802A KR1020187001405A KR20187001405A KR20180022802A KR 20180022802 A KR20180022802 A KR 20180022802A KR 1020187001405 A KR1020187001405 A KR 1020187001405A KR 20187001405 A KR20187001405 A KR 20187001405A KR 20180022802 A KR20180022802 A KR 20180022802A
- Authority
- KR
- South Korea
- Prior art keywords
- membrane
- self
- single layer
- layer
- polymer
- Prior art date
Abstract
본 발명의 자가-보수 특성을 갖는 자가-지지형 합성 폴리머 방수 멤브레인은 건설 분야에서 적용 가능한 것이다. 이 멤브레인은 단일층 또는 다중층일 수 있다. 이러한 멤브레인 조성물은 열가소성 폴리머, 스멕타이트-타입 점토 및 고 물-흡수성 폴리머를 포함한다.
Description
본 발명은 자가-보수(self-repair) 특성을 갖는 자가-지지형(self-supporting) 합성 폴리머 방수 멤브레인으로서, 건설 분야에 적용 가능한 합성 멤브레인에 관한 것이다.
본 발명은 자가-보수 특성을 갖는 자가-지지형 합성 폴리머 방수 멤브레인으로서, 건설 분야에 적용 가능한 합성 멤브레인에 관한 것이다. 이러한 자가-지지형 멤브레인은 단일층 또는 다중층일 수 있다. 단일층 멤브레인 조성물은 열가소성 폴리머, 스멕타이트-타입 점토 재료 및 고흡수성(superabsorbent) 폴리머류(super water absorbent polymers, SAP)를 포함하고, 단일층 멤브레인을 위한 지지층으로서 작용하는, 예를 들어 지오텍스타일(geotextile), 보강재 또는 인조토양(geosynthetic) 배수 메쉬 타입의 보조 층을 수반하지 않는 자가-지지형이다. 마찬가지로, 여기에 기재된 단일층 멤브레인은 다른 인조토양 보조 층을 수반하여, 적어도 두 개 층, 바람직하게는 세 개 층으로 이루어지는 다중층으로 될 수 있고, 이 다중층은 기존의 것과 유사한 조성을 가지는 외부(outer) 층, 인조토양, 및 상기한 바와 같고 본 발명의 목적을 달성할 수 있는 조성물을 갖는 중간 층으로 구성된다.
본 발명의 자가-지지형 자가-보수형 합성 멤브레인은 빌딩 공사, 지붕 및 지하 구조물(바닥, 벽…)의 방수의 분야와 토목 공사 분야, 매립지, 운하, 터널, 침전물, 도로, 벽, 다리…의 밀봉작업에 적용 가능하다.
합성 재료(폴리머)는 현재 폴리에틸렌(PE), 폴리프로필렌(PP), 폴리비닐 클로라이드(PVC), 에틸렌 프로필렌 디엔 모노머(EPDM), 역청… 및/또는 적은 비율의 첨가제와 혼합된 이들의 조합물과 같은 방수 멤브레인의 제조에 사용된다.
상이한 인조토양 재료의 조합도 또한 사용되는데, 이는 지오조성(geocomposites), 즉, 상이한 인조토양 재료, 예를 들어 지오텍스타일-벤토나이트-지오텍스타일, 지오텍스타일-벤토나이트-플라스틱 멤브레인 등의 조합으로부터 형성된 생성물로 만들어진 “벤토나이트 블랭킷”의 경우에 또한 사용되고, 이들 모두는 인조토양의 다른 층들 사이에 갇혀있는 벤토나이트 분말을 함유함으로써 빌딩 및 토목 공사를 위한 벤토나이트-계 방수 시스템을 얻는다.
이들 합성 또는 천연 기초 재료(PE, PP, PVC, EPDM, 역청...)는 그 중에서도 고도의 내수성, 우수한 기계적 특성 및 고내구성 특성을 반드시 가져야 하는 공사에서 설치하기 위한 방수 멤브레인의 제조를 위한 기초 재료로 사용된다. 기존 방수 멤브레인은 극히 낮은 수분 흡수력을 특징으로 하고, 이 특징으로 인해 이러한 작업에 사용된다. 또한, 이들은 아무런 흡수 효과도 나타내지 않고, 따라서 물과 접촉시 팽창하지 않는다.
방수 멤브레인의 주요 한계 중 하나는 일단 파손(break)이 발생하면 이들이 함유하는 유체의 누출을 멈출 수 없기 때문에, 이들이 파손되면 이들의 수밀성(water-tightness)을 유지할 수 없다는 것이다.
상이한 벤토나이트-계 용액은 또한 토목 공학 및 빌딩 공사에서 방수 배리어로 사용된다, 이외에:
● 터널 건설에서 침하 방지 또는 크랙을 충전하기 위한 벤토나이트 그라우트 또는 슬러리.
● 지오멤브레인(부착된 벤토나이트의 층을 지지하는 주요 기능을 갖는 방수 멤브레인)을 포함하는 벤토나이트-계 방수 블랭킷.
● 직조 지오텍스타일의 하나 또는 두 층 사이에 캡슐화된 벤토나이트를 포함하는 지오조성으로 사용된다.
이들 제품들은 예를 들어 절연 구성 요소를 지지하기 위한, 예를 들어 용접, 재봉 또는 접착 등에 의해 후속적으로 기계적으로 결합되는 인조토양의 독립적인 제조를 필요로 한다. 유사하게, 이 제조 과정은 멤브레인의 크기를 제한한다.
당 업계의 기술 수준에서 소듐 벤토나이트 또는 몬모릴로나이트(montmorillonite)가 알려져 있으며, 이는 녹점토(smectite) 군의 3층 필로실리케이트 타입(도 1)의 점토이고, 그 구조는 단순하거나 수화된 보상 양이온을 포함하는 실리콘 (Si) 사면체의 두 평면 사이에, 메쉬의 형태로 주로 알루미늄으로 된 팔면체 단위의 적층에 의해 구성된다.
스멕타이트-타입 점토의 주요 구조적 특징은 물과 유기 분자를 포함하는 다른 극성 분자 모두가 층간 공간을 관통할 수 있어 메쉬의 팽창을 일으킨다는 것이다. 이 현상은 이 군의 점토를 구성하는 평행한 시트가 반 데르 발스의 힘 및 다른 정전력에 의해 결합되는 사실에 기인한다. 이러한 구조적 설계는 이들 제품을 수압 배리어로 작용하기에 이상적인 것으로 만든다. 특히, 소듐 벤토나이트 계열의 점토는 칼슘 벤토나이트 또는 칼슘과 소듐의 혼합물도 또한 사용될지라도, 이들이 물과 접촉할 때 이들의 부피가 몇 배로 팽창할 수 있는 능력을 가지기 때문에 이 어플리케이션에 가장 적합하다.
벤토나이트는 높은 비율의 몬모릴로나이트로 구성된다. 양이온의 존재와 이들 비율에 따라 벤토나이트는 상이한 유형으로 분류된다. 산업적 어플리케이션에서 헥토라이트는 이들의 팽창 및 분산성 능력 때문에 일부 경우에 벤토나이트(주로 몬모릴로나이트) 보다 뛰어난 점을 보여준다. 이는 보다 작은 입자 크기에 기인한다.
천연 스멕타이트 이외에, 라포나이트(Laponite)(합성 헥토라이트), 플루오로헥토라이트 또는 플루오로화 백운모와 같은 다른 합성 옵션이 있고, 이는 스멕타이트와 유사한 방식으로 물을 흡수하고 팽창할 수 있다. 소듐 활성화(소듐 벤토나이트를 얻기 위한 칼슘 벤토나이트)를 갖는 점토도 있다.
벤토나이트 분말을 함유한 방수 배리어에 의해 나타나는 주요 한계는 지오텍스타일, 지오멤브레인, 지오메쉬 또는 이들의 조합과 같은 시스템을 구성하는 층들 사이에 부착, 지지 및/또는 한정되기 위한 벤토나이트의 필요성에서 이들은 인조토양의 상이한 층의 방수 시스템을 따름으로써 벤토나이트 분말의 응집을 보장하고 설치 중 및 설치 후에 그것의 이동 및/또는 분산을 억제하는 것이다.
또한, 고흡수성 폴리머(SAP - 고흡수성 폴리머)는 이들 자신의 질량에 비해 극도로 많은 양의 액체를 흡수하고 유지할 수 있는 폴리머이다. 수분-흡수성 폴리머는 망상화(reticulate) 할 때 하이드로겔로 분류되어 물 분자와의 수소 결합을 통해 수용액을 흡수한다. 물을 흡수하기 위한 SAP의 능력은 수용액의 이온 농도의 요인이다.
낮은 밀도 망상을 갖는 SAP는 일반적으로 보다 높은 흡수 능력을 가지고 보다 큰 정도로 팽창한다. 이러한 유형의 SAP는 또한 보다 부드럽고 끈적끈적한 겔 형성을 가진다. 높은 밀도 망상을 갖는 폴리머는 보다 낮은 흡수 능력과 보다 적은 팽창을 나타내지만, 겔 강도가 보다 견고하고 통상의 압력 하에서도 입자의 모양이 유지될 수 있다.
SAP의 주요 용도는 유아용 기저귀, 성인용 보호 속옷 및 위생 패드와 같은 일회용 위생 용품에서 발견된다. SAP는 또한 지하 전력 또는 통신 케이블, 원예 보수제, 누출 및 수성 유체 제어 및 인공 눈(snow)의 생산에 있어 물의 침투를 차단하는데도 사용된다.
건조 상태에서의 아크릴 폴리머 또는 고흡수성 폴리머(SAP)는 꼬인(curled) 코일(도 2)과 유사하다. 이들 분자가 물에 배치되면, 수소 가교 연결이 주변의 HOH와 연결되어 꼬임이 풀려 곧게 펴진다(도 3).
분자가 곧게 펴지면, 이들은 주변 유체의 점도를 증가시킨다. 고흡수성 화학은 메쉬(망상)을 형성하는 폴리머 가닥을 가로로 결합하는 작은 분자의 첨가와 주요 폴리머 사슬(-COO-Na+)을 따르는 카르복실산기(-COOH)의 부분적 중화, 두 가지 사항을 요구한다.
물 분자는 주요 폴리머 사슬에서 소듐의 중화에 의해 형성된 확산 기울기를 통해 메쉬 쪽으로 끌어당겨진다. 폴리머 사슬은 곧게 펴지기를 시도하지만 망상화 때문에 제한된다. 따라서, 입자는 물이 메쉬로 통과할 때 팽창한다(도 4).
물 분자는 수소 가교 연결을 통해 고흡수성 폴리머 메쉬의 카르복실레이트 이온에 견고히 부착된다. 많은 종류의 용해성 금속도 주요 폴리머 사슬에 따라 소듐과 이온 교환하는 경향을 가지고 유지되고, 이는 폴리아크릴레이트가 경수에서 사용하기 위한 일부 세정제에서 격리제 또는 킬레이트제로 사용될 수 있는 이유이다. 고흡수성 분자의 외관은 도 5에서 보다 상세히 나타나고, 보다 큰 스테일로, 고흡수성 폴리머 메쉬의 외관은 도 6에서 상세하게 볼 수 있다.
유사하게, 당 업계의 기술 수준에서 열가소성 폴리머, 스멕타이트-타입 점토 및 가소제(plasticiser)를 포함하는 고흡수성 폴리머를 포함하는 조성물인 멤브레인이 있을 수 있다. 가소제는 공정을 용이하게 하고 유연성을 향상시키기 위해 플라스틱에 혼입되는 재료이다.
가소제의 사용은 그 조성물에서 다음 사항을 감소시킨다.
- 용융 상태에서의 점도,
- 탄성 계수, 및
- 플라스틱의 유리 전이 온도(Tg).
따라서, 가소제는 주로
- 재료의 변형을 용이하게 하고,
- 충격 저항을 증가시키고,
- 유연성을 증가시키고,
- 폴리머의 연성 및 점성을 향상시키고,
- 경도 및 취약성을 감소시키기 위해 조성물에 혼입된다.
그러나, 전술한 이점 이외에, 가소제의 사용은 다음과 같은 특정한 문제점을 수반한다:
- 독성 문제: 예를 들어, 고-독성 폴리클로라이네이트 비페닐은 가소제로 더 이상 사용되지 않는다. DOP와 같은 프탈산 에스테르는 가소화된 PVC 백 및 튜브에 저장된 블러드(blood)로부터 추출될 수 있다. 이러한 아로마틱 에스테르는 또한 열에 의해 PVC 자동차 시트 커버로부터 분리될 수 있다.
- 플라스틱 재료에서 가소제가 손실되면 그것의 유용한 수명을 거대하게 단축시키기 때문에 그것이 제조되는 목적에 적합하지 않은 취약한 재료로 변환되고, 및
- 플라스틱 산업에서 사용되는 예를 들어, 발암성이 있어 “디-2-에틸헥실 프탈레이트”와 같은 일부 가소제는 실험실 분석에서 동물에게 위험하고, 현재 이 제품은 잠재적으로 발암성이 있는 것으로 간주된다.
따라서, 본 발명의 목적은 위와 같은 단점을 피하기 위하여 어떠한 타입의 가소제도 포함하지 않고, 열가소성 폴리머, 스멕타이트-타입 점토 및 고흡수성 폴리머를 포함하여 이루어지는 조성물인 자가-지지형 단일층 멤브레인을 제공하는 것이다.
본 발명의 목적인 자가-지지형 방수 멤브레인의 자가-보수 특성은 열가소성 폴리머, 스멕타이트 또는 벤토나이트 타입 필로실리케이트 점토 및 고흡수성 폴리머(SAP)의 상이한 비율의 혼합에 기인한다.
본 발명에서의 스멕타이트-타입 필로실리케이트 점토는 다음 몬모릴로나이트(벤토나이트), 바이델라이트(Beidellite), 논트로나이트(Nontronite), 라포나이트(Laponite), 플루오로헵토라이트(fluorohectorites)등 일 수 있다.
열가소성 폴리머는 폴리에틸렌, 폴리프로필렌, EVA 코폴리머…일 수 있다.
유사하게, 고흡수성 폴리머는 친수성 수지(전분-계, 폴리아크릴레이트, 폴리비닐 알코올, PVA, PVOH) 등, 및 가교-결합된 소듐 카르복시메틸 셀룰로오스, 폴리아크릴산 폴리머, 가교-결합된 폴리비닐 알코올, 칼슘 알기네이트, 전분-g-소듐 아크릴레이트 코폴리머일 수 있다.
따라서, 본 발명의 목적은 자체-밀봉 특성을 가져 자가-보수 능력을 가지는 자가-지지형 방수 멤브레인을 갖추기 위해서, 이러한 목적으로 이들은 보다 큰 팽창 및 물 흡수 특성을 가져야만 하고, 상이한 양의 벤토나이트 점토를 폴리머에 첨가하고(1 중량% 내지 95중량%), 특히, 흡수성 폴리머를 첨가하여, 벤토나이트 분말을 결합, 지지 또는 한정하도록, 현재까지는 다른 층의 사용이 필요 없이, 단일 및 연속적인 공정으로 제조된 단일층 또는 다중층 제품을 얻음으로써 내부(수분 배리어)에서 파손될 때 자체-밀봉되는 멤브레인을 제공하는 것이다.
발명의 설명을 보완하고 본 발명의 특징을 보다 잘 이해하도록 돕기 위해, 일련의 도면이 본 명세서에 통합된 일부분으로서 첨부되며, 이들 도면은 예시적이고 비제한적인 방식으로 다음과 같이 나타낸다:
도 1은 소듐 벤토나이트의 구조, 또는 몬모릴로나이트의 개략도로서, 이는 단순하거나 수화된 보상 양이온을 포함하는 실리콘(Si) 팔면체의 두 평면 사이에 샌드위치된 메쉬의 형태로 주로 알루미늄으로 된 팔면체 단위의 적층에 의해 구성되는 것을 개략적으로 보여준다.
도 2는 꼬인(curled) 코일 모양을 갖는 건조 상태에서의 고흡수성 폴리머를 개략적으로 보여준다.
도 3은 물(H2O)에 배치될 때 건조 상태에서의 고흡수성 폴리머의 분자를 혼합하는 절차를 개략적으로 보여준다.
도 4는 물(H2O)에서 고흡수성 폴리머의 메쉬를 혼합하는 절차를 개략적으로 보여준다.
도 5는 고흡수성 분자를 개략적으로 보여준다.
도 6은 고흡수성 폴리머 메쉬를 개략적으로 보여준다.
도 7은 본 발명의 목적인 다중층 멤브레인을 보여준다.
도 1은 소듐 벤토나이트의 구조, 또는 몬모릴로나이트의 개략도로서, 이는 단순하거나 수화된 보상 양이온을 포함하는 실리콘(Si) 팔면체의 두 평면 사이에 샌드위치된 메쉬의 형태로 주로 알루미늄으로 된 팔면체 단위의 적층에 의해 구성되는 것을 개략적으로 보여준다.
도 2는 꼬인(curled) 코일 모양을 갖는 건조 상태에서의 고흡수성 폴리머를 개략적으로 보여준다.
도 3은 물(H2O)에 배치될 때 건조 상태에서의 고흡수성 폴리머의 분자를 혼합하는 절차를 개략적으로 보여준다.
도 4는 물(H2O)에서 고흡수성 폴리머의 메쉬를 혼합하는 절차를 개략적으로 보여준다.
도 5는 고흡수성 분자를 개략적으로 보여준다.
도 6은 고흡수성 폴리머 메쉬를 개략적으로 보여준다.
도 7은 본 발명의 목적인 다중층 멤브레인을 보여준다.
본 발명의 목적인 멤브레인을 형성하는 층에서 강화(reinforcement) 재료를 사용하지 않고 그것이 조성물로 인해 자제-지지가 되는 특성은 단일층 멤브레인이 그 자체로 지지하도록 허용하여, 즉, 그 조성물에 매입되는 강화 재료를 필요로 하지 않으며, 당 업계 기술 수준에서 자가-지지 되지 않는 단일층 멤브레인에서 발생하는 것처럼, 단일층 멤브레인의 지지 층으로 작용하는 배수 지오텍스타일 또는 지오조성(지오배수)를 사용하지 않는 것이다. 한편, 본 발명의 목적인 단일층 멤브레인은 이를 적용함에 있어서는, 단일층 멤브레인의 지지층으로 작용하는 예를 들어, 방수 지오멤브레인, 지오텍스타일 또는 배수 지오조성(지오배수)과 같은 다른 보조 인조토양층과 같이 사용될 수 있다. 또한, 본 발명의 단일층 멤브레인은 이를 적용함에 있어서는 예를 들어, 방수 멤브레인, 지오텍스타일 또는 배수 지오조성(지오배수)와 같은 다른 인조토양 보조 층과 함께 사용될 수 있다. 위에서 언급하였듯이, 이들 보조 층은 그것의 특정 기능인, 보호 또는 여과(지오텍스타일) 또는 배수(지오배수)기능으로 인해 본 발명의 목적인 단일층 멤브레인의 밀폐된 밀봉 용액에 혼입된다.
방수 멤브레인에서 발생할 수 있는 임의의 파손은 그들의 주요 특성의 수밀성을 손실하도록 하는 원인이 된다. 이러한 파손은 설치 중, 상이한 기계 사용(굴착기, 지게차, 트럭)의 작용을 통해, 상이한 지형(날카로운 물건, 돌 등) 등 불규칙성 때문에, 및 심지어 동물, 식물 등의 작용을 통해 설치 후에 발생할 수 있다.
따라서, 상기에 따른 본 발명의 목적은 제1 항에 따른 자가-보수 특성을 갖는 자가-지지 방수 멤브레인이다. 상기 멤브레인은 상이한 구성을 가질 수 있으며, 단일 층, 즉, 단일층 멤브레인; 또는 두 개 이상의 층, 즉, 다중층 멤브레인에 의해 형성될 수 있다.
자가-지지형 단일층 멤브레인은 단일 층으로 구성되고, 그 조성은:
● 폴리에틸렌, 폴리프로필렌, EVA 코폴리머 또는 유사한 특성을 갖는 화합물을 포함하여 이루어지는 폴리올레핀 열가소성 폴리머.
● 친수성 수지 (전분-계, 폴리아크릴레이트, 폴리비닐 알코올, PVA, PVOH) 등, 및 가교-결합된 소듐 카르복시메틸 셀룰로오스, 폴리아크릴산 폴리머, 가교-결합된 폴리비닐 알코올, 칼슘 알기네이트, 칼슘 알기네이트, 전분-g-소듐 아크릴레이트 코폴리머 또는 유사한 특성을 갖는 화합물을 포함하는 군으로부터 선택된 고흡수성 폴리머(SAP), 및
● 스멕타이트-타입 필로실리케이트 점토, 몬모릴로나이트(벤토나이트), 바이델라이트, 논트로나이트, 라포나이트, 플루오로헥토라이트… 무기 안료(카본 블랙, 티타늄 옥사이드, 등)과 같은 무기 충전재 또는 이들의 조합이 상이한 양으로 혼합된다.
이러한 결과 혼합물은 멤브레인에서 파손(구멍, 크랙)을 밀봉하는 자가-보수 단일층 멤브레인이고, 그렇게 함으로써 그에 함유된 유체(물, …)가 누출되는 것을 방지한다.
다중층 멤브레인은, 이 경우 두 개 이상의 층에 의해 형성되는 자가-보수 멤브레인이고, 이들 층의 하나, 통상적으로 내부 층은 상기 기재된 자가-지지형 단일층 멤브레인으로 형성되고 다른 층은 현재의 방수 멤브레인과 같은 방법으로 형성되어, 방수 멤브레인에 구멍이나 크랙-모양의 파손이 있더라도, 이는 상기 언급된 것처럼, 물과 접촉 시 열가소성 폴리머(TPO), 벤토나이트 점토 및 고흡수성 폴리머(SAP)를 포함하는 내부 층의 자가-보수 특성 덕분에 밀봉될 수 있다.
또한, 본 발명의 목적인 멤브레인은 청구항 제1 항에 따른 자가-지지형 단일층이든지, 또는 청구항 제1 항에 따른 자가-지지형 단일층 멤브레인을 포함하는 다중층이던 간에, 예를 들어 결합된 멤브레인을 강화하는 용접에 의해 함께 결합될 수 있다.
자가-보수형 단일층 멤브레인 및 자가-보수형 다중층 멤브레인을 구성하는 구성 요소는:
a) 아래의 플라스틱 구성 요소로 이루어지는 열가소성 재료:
i) 폴리에틸렌, 폴리프로필렌, 코폴리머 EVA…를 포함하는 폴리올레핀 열가소성 플라스틱과 같은 재료,
ii) 고흡수성 폴리머(SAP), 친수성 수지(전분-계, 폴리아크릴레이트, 폴리비닐 알코올, PVA, PVOH) 등, 및 가교-결합된 소듐 카르복시메틸 셀룰로오스, 폴리아크릴산 폴리머, 가교-결합된 폴리비닐 알코올, 칼슘 알기네이트, 전분-g-소듐 아크릴레이트 코폴리머.
b) 전체 조성이 1 중량% 내지 95 중량% 비율인 몬모릴로나이트(벤토나이트), 바이델라이트, 논트로나이트, 라포나이트 및 플루오로헥토라이트를 포함하는 스멕타이트-타입 필로실리케이트 점토에 의해 형성되거나 카보네이트, 바이카보네이트, 설페이트 등과 같은 다른 무기 충전재와 소듐 벤토나이트의 혼합물에 의해 형성되는 무기 성분이다.
양호한 혼화성을 달성하기 위해서 상기 혼합물(플라스틱 및 미네랄 충전재)의 상이한 구성 요소들 사이에서 가교 또는 연결을 형성하기 위해 상이한 비율의 상용화 화합물을 첨가하는 것도 가능하다. 이는 안정제, 충전재, 가황 화합물, 고무화 촉진제, 착색제, 정전하의 형성 방지제, 가공 보조제, 산화방지제, 자외선 흡수제, 난연성 화합물, 발포제 및 다른 수지 성분을 포함한다.
단일층 멤브레인은 그 조성물에 가소제를 가지지 않음에도 불구하고, 점도, 탄성 계수, 유리 전이 온도, 충격 저항, 유연성, 연성 및 점성, 경도 및 취약성…등과 같은 가소제에 의해 향상되는 특징보다 뛰어난 특징을 나타내며, 요약하면, 가소제를 혼입할 필요없이 그 자체로 가소제를 사용하는 플라스틱 보다 뛰어난 특징을 나타낸다. 본 발명의 목적인 자가-지지형 단일층 멤브레인은 후속적으로 캘린더링(calendering)을 갖는 압출 공정으로 얻어진다. 유사하게, 지오조성을 형성하기 위해 제1 항의 목적인 단일층 멤브레인, 예를 들어, 하나 또는 두 개의 외부 층을 갖는, 지오멤브레인에 의해 형성되고, 또한 요구되는 후-공정 또는 임의의 후속 조작없이 압출 절차를 사용하여 제조된다.
개략적으로, 압출-캘린더링 장비는
● 1 중량% 내지 95 중량%의 플라스틱에 하중을 가할 수 있는 압출기 공급 장비.
● 압출기(들).
● 제1 항에 따른 단일층 멤브레인을 혼입하는 단일층 및 다중층 멤브레인 모두를 얻을 수 있는 코-압출 장비.
● 0.25m 이상의 최소 헤더(header) 폭.
● 하나 이상의 롤러를 갖는 캘린더.
● 와인딩(winding) 기계.
● 컨베이어로 구성된다.
코-압출 절차에 따라 얻어진 단일층 또는 다중층(도 7) 어느 쪽이든, 본 발명에 기재된 멤브레인은 0.01 mm 내지 20 mm의 두께를 가질 수 있지만, 이들 멤브레인의 가장 일반적인 두께는 1.00 mm 내지 5.00 mm 범위이다.
유사하게, 본 발명의 목적인 자가-지지형 단일층 멤브레인은 그것의 조성과 제조 절차 때문에 12 미터 높이까지 도달할 수 있다.
본 발명을 수행하기 위한 바람직한 모드의 설명
본 출원의 목적을 수행하기 위한 바람직한 모드는 아래 기재될 것이지만, 본 발명은 이 특정 실시예에 제한되지 않는다.
다음 구성 요소를 포함하는 제제가 자가-지지형 자가-보수 멤브레인을 생산하고 얻기 위해 사용되어 왔다:
● 밀도가 0.820 g/cc 내지 0.940 g/cc인 열가소성 폴리올레핀(TPO) 수지.
● 소듐 벤토나이트
● SAP와 같은 소듐 폴리아크릴레이트
● 카본 블랙 마스터배치 및 가소제와 윤활유를 제외한 기타 첨가물
이 제제는 평평한 헤더에 부탁된 동회전(co-rotating) 트윈 스풀 기계(압출기)에서 처리 되었으며, 멤브레인 1 및 멤브레인 2의 제제는 다음 두 개 표(표 1 - 멤브레인 1 및 표 2 - 멤브레인 2)에서 보여진다.
용융된 재료는 압출 기계의 헤더로부터 멤브레인의 형태로 유출된다. 이 고온, 용융 멤브레인은 캘린더의 롤러를 통과하게 되고 여기서 멤브레인은 적합한 냉각 공정을 거친다. 일단 생성된 멤브레인이 적절하게 냉각되면, 스풀 상에 감겨진다(wound).
그 결과는 12 미터까지의 상이한 길이 및 폭의 롤이다.
두께 1.00 mm 내지 5.00 mm 범위의 멤브레인이 얻어진다.
도 7은 본 발명의 목적인 다중층 멤브레인의 실시예를 보여주는데, 이는, 전체 두께의 1% 내지 75%의 범위인 두께를 가지는 제1 항에 따른 자가-지지형 중간 층(2)과, 이 층의 각각의 측면 상에 점토 또는 물-흡수 폴리머가 없는 외부 소수성 층(1)을 적어도 하나 가진다. 바람직하게는, 자가-지지형 중간 층은 전체 두께의 25% 내지 99%의 두께를 가지며, 또한, 외부 층(1)은 강화 층으로서 작용한다. 상기 강화 층 또는 층들은 적어도 하나의 강화 메쉬를 포함할 수 있고, 이는 폴리에스테르, 유리섬유, 폴리프로필렌 또는 이들의 조합과 같은 상이한 재료로 만들어질 수 있다.
1: 외부 층
2: 중간 층
2: 중간 층
Claims (11)
- - 1중량% 내지 95중량%의 스멕타이트 군(smectite group)의 필로실리케이트-타입 점토(phyllosilicate-type clays)의 무기 충전재, 및
- 열가소성(TPO) 타입의 폴리올레핀과 고-물흡수성 폴리머(SAP)의 플라스틱 화합물와 함께, 강화 또는 가소성 재료 없이, 자가-지지형 단일층을 포함하여 이루어지며, 상기 무기 충전재 부분이 멤브레인의 전체 조성물의 15중량% 내지 75중량% 범위를 갖는 것을 특징으로 하는 합성 폴리머 방수 멤브레인. - 제1 항에 있어서, 상기 무기 충전재는 카본 블랙과 같은 다른 무기 충전재를 갖는 스멕타이트 군(벤토나이트)의 필로실리케이트의 혼합물인 것을 특징으로 하는 멤브레인.
- 제1 항에 있어서, 상기 자가-지지형 단일층은 점토 또는 물-흡수성 폴리머가 없는 적어도 하나의 외부 소수성 층을 자가-지지형 단일층의 적어도 하나의 측면 상에 포함하고, 상기 외부 소수성 층은 상기 자가-지지형 단일층 및 상기 적어도 하나의 외부 층에 의해 형성된 전체 두께의 1% 내지 75% 범위의 두께를 나타내는 것을 특징으로 하는 멤브레인.
- 제3 항에 있어서, 상기 자가-지지형 단일층은 상기 자가-지지형 단일층 및 상기 적어도 하나의 외부 층에 의해 형성된 전체 두께의 25% 내지 99%를 나타내는 두께를 가지는 것을 특징으로 하는 멤브레인.
- 제1 항 또는 제3 항에 있어서, 상기 멤브레인은 추가적인 강화 층을 가지는 것을 특징으로 하는 멤브레인.
- 제1 항 또는 제3 항에 있어서, 상기 멤브레인은 0.01 mm 초과의 두께를 가지는 것을 특징으로 하는 멤브레인.
- 제5 항에 있어서, 상기 강화 층은 적어도 하나의 강화 메쉬를 포함하는 것을 특징으로 하는 멤브레인.
- 제7 항에 있어서, 상기 강화 메쉬는 폴리에스테르, 유리섬유, 폴리프로필렌 또는 이들의 조합과 같은 상이한 재료로 만들어지는 것을 특징으로 하는 멤브레인.
- 제1 항 내지 제8 항 중 어느 한 항에 있어서, 상기 스멕타이트 군의 필로실리케이트-타입 점토는 그 중에서도 몬모릴로나이트, 바이델라이드, 논트로나이트, 라포나이트 및 플루오로헥토라이트인 것을 특징으로 하는 멤브레인.
- 제1 항에 있어서, 상기 열가소성(TPO) 타입의 폴리올레핀 플라스틱 화합물은 그 중에서도 폴리에틸렌, 폴리프로필렌 또는 EVA 코폴리머인 것을 특징으로 하는 멤브레인.
- 제1 항에 있어서, 상기 물-흡수성 폴리머는 그 중에서도 소수성 수지, 전분-계, 폴리아크릴레이트, 폴리비닐 알코올, PVA 또는 PVOH, 및 가교-결합된 소듐 카르복시메틸 셀룰로오스, 폴리아크릴산 폴리머, 가교-결합된 폴리비닐 알코올, 칼슘 알기네이트 또는 전분-g-소듐 아크릴레이트 코폴리머인 것을 특징으로 하는 멤브레인.