KR20170088778A - 기능성 이미지 타일 및 그 제조방법 - Google Patents
기능성 이미지 타일 및 그 제조방법 Download PDFInfo
- Publication number
- KR20170088778A KR20170088778A KR1020170012249A KR20170012249A KR20170088778A KR 20170088778 A KR20170088778 A KR 20170088778A KR 1020170012249 A KR1020170012249 A KR 1020170012249A KR 20170012249 A KR20170012249 A KR 20170012249A KR 20170088778 A KR20170088778 A KR 20170088778A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- tile
- image
- functional image
- Prior art date
Abstract
본 발명은 석고와 물을 혼합하여 조성된 원료에 황토와, 바잘트섬유와, 닥섬유를 혼합한 혼합물을 통해 제조된 타일의 표면에 소망하는 이미지를 인쇄하여 제조되며, 흡수성이 우수한 석고와 황토가 혼합되어 이미지 인쇄시 잉크를 원활하게 흡수할 수 있고, 표면에 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있고, 바잘트섬유와 닥섬유가 혼합되어 내열성, 강도, 습도조절능력이 우수한 것을 특징으로 하는 기능성 이미지 타일 및 그 제조방법을 개시한다.
Description
본 발명은 기능성 이미지 타일 및 그 제조방법에 관한 것으로, 더욱 상세하게는 석고와 물을 혼합하여 조성된 원료에 황토와, 바잘트섬유(basalt fiber)와, 닥섬유(mulberry fiber)를 혼합한 혼합물을 통해 제조된 타일의 표면에 소망하는 이미지를 인쇄하여 제조되며, 흡수성이 우수한 석고와 황토가 혼합되어 이미지 인쇄시 잉크를 원활하게 흡수할 수 있고, 표면에 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있고, 바잘트섬유와 닥섬유가 혼합되어 내열성, 강도, 습도조절능력이 우수한 것을 특징으로 하는 기능성 이미지 타일 및 그 제조방법에 관한 것이다.
일반적으로, 콘크리트는 시멘트를 모래, 자갈, 물과 함께 혼합해서 만든 복합재료로서 목재나 강재에 비하여 물에 대한 저항력이 크며 다양한 형태와 치수로 가공이 용이하여 지구상에서 가장 널리 사용되는 건설재료이다.
근래에 들어 국민소득의 증가로 주변 환경에 대한 인식이 제고되면서 각종 토목 및 건축용 구조물들의 회색 일변도의 규격화, 획일화된 기존의 틀에서 벗어나 다양한 칼라 및 디자인을 부여하여 도시 미관을 개선하는 데 많은 투자가 이루어지고 있다.
최근들어 시멘트와 각종 접착제를 이용한 벽지 및 바닥재 등에서 발생하는 포름알데하이드에 의한 "새집 증후군"이 이슈화됨에 따라서 천연성분을 이용한 건축재료에 대한 관심이 높아지고 있고, 심미성을 향상시키기 위하여 무늬가 표현된 벽지 혹은 타일 등을 부착 설치하여 인테리어를 하고 있다.
근래들어 장식효과를 높이기 위하여 타일(tile)에 소망하는 이미지를 구현하여 벽이나 바닥을 장식하는 이미지 타일이 보급되고 있다. 종래의 이미지 타일은 실크스크린 인쇄기법을 이용하여 이미지를 타일에 구현하고 있는데, 이러한 스크린기법은 무늬의 원도(原圖)를 원색분해기법에 의해 색분해하고, 분해된 각 원색별로 필름을 제작하고 각 원색별로 스크린 인쇄판을 제작한다. 그러나 이러한 스크린 인쇄기법은 색분해를 위한 다수의 공정이 요구되므로 이미지타일의 생산효율이 저하되는 문제점이 있으며, 또한, 통상의 타일들은 점토질의 재료를 소성하여 제조함으로써, 운반이나 설치시 깨지기 쉽고 무거워서 운반/보관등 취급이 불편한 문제점이 있었다.
다음으로, 대한민국 등록실용신안공보 제20-0402140호에는 "벽화용 세라믹 이미지타일"이 개시되어 있다.
상기의 이미지타일은 타일층과, 상기 타일층 위로 주제 : 경화제 : 희석제의 비율을 2 : 1 : 1로 희석하여 구성되는 에폭시수지가 도포되어 구성되는 에폭시수지 도포층과, 상기 도포층 상에 UV 경화방식의 프린터기를 사용하여 타일에 직접 이미지를 프린팅하여 구성되는 이미지층 및 상기 이미지층상으로 주제 : 희석제의 비율을 2 : 1로 구성되는 우레탄 수지코팅층으로 구성된다.
상기의 이미지타일을 포함하는 종래의 이미지 타일은 표면에 인쇄된 이미지를 보호하기 위하여 표면에 코팅층을 형성하는 작업이 동반되어야 했다.
본 발명은 상기와 같은 문제점을 해결하기 위하여 발명된 것으로, 표면에 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있고, 내열성, 강도, 습도조절능력이 우수한 이미지 타일 및 그 제조방법을 제공하는데 그 목적이 있다.
상기와 같은 목적을 위하여 본 발명은 석고와 물을 혼합하여 조성된 원료에 황토와, 바잘트섬유와, 닥섬유를 혼합한 혼합물을 통해 제조된 타일의 표면에 소망하는 이미지를 인쇄하여 제조되며, 흡수성이 우수한 석고와 황토가 혼합되어 이미지 인쇄시 잉크를 원활하게 흡수할 수 있고, 표면에 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있고, 바잘트섬유와 닥섬유가 혼합되어 내열성, 강도, 습도조절능력이 우수한 것을 특징으로 한다.
또한, 본 발명에서 상기 기능성 이미지 타일은 석고 55~61중량%와 물 39~45중량%를 혼합하여 조성된 원료 100중량부에 대하여 황토 1~30중량부와, 바잘트섬유 2~10중량부와, 닥섬유 2~10중량부가 혼합되는 것을 특징으로 한다.
또한, 본 발명에서 상기 기능성 이미지 타일은 원료 100중량부에 대하여 구문초 추출액 1~30중량부, 피톤치드 1~30중량부, 숯 1~30중량부가 더 혼합되는 것을 특징으로 한다.
또한, 본 발명은 석고 55~61중량%와 물39~45중량%을 혼합하여 원료를 형성하는 단계와; 상기 원료 100중량부에 황토 1~30중량부와, 바잘트섬유 2~10중량부와, 닥섬유 2~10중량부를 혼합하여 혼합물을 형성하는 단계와; 상기 혼합물을 성형틀 또는 금형 내부에 투입한 다음 탈형하여 타일을 제조하는 단계; 및 상기 타일의 표면에 소망하는 이미지를 인쇄하는 단계;를 포함하여 이루어지는 것을 특징으로 한다.
상기와 같이 이루어지는 본 발명에 따른 기능성 이미지 타일은 표면에 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있고, 바잘트섬유와 닥섬유가 혼합되어 내열성, 강도, 습도조절능력이 우수한 장점이 있다.
특히, 본 발명은 흡수성이 우수한 석고와 황토가 혼합되어 이미지 인쇄시 표면에 분사되는 잉크를 원활하게 흡수함으로써 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있고, 상기 이미지를 보호하기 위한 코팅작업을 생략할 수 있으므로 작업공정이 간략해지고 비용을 절감할 수 있는 현저한 장점이 있다.
또한, 본 발명은 상기 원료에 구문초 추출액이 더 혼합되어 모기를 비롯한 각종의 해충들이 가까이 접근하는 것을 차단 및 퇴치하는 효과가 있고, 피톤치드가 더 혼합되어 항균작용과, 스트레스 완화 및 면역기능향상의 효과를 기대할 수 있다.
도 1은 본 발명에 따른 기능성 이미지 타일의 제조공정도.
도 2는 본 발명에 따른 기능성 이미지 타일의 전자현미경사진.
도 3은 본 발명의 실시예에 따른 기능성 이미지 타일이 복수개로 결합된 상태를 도시한 예시도.
도 2는 본 발명에 따른 기능성 이미지 타일의 전자현미경사진.
도 3은 본 발명의 실시예에 따른 기능성 이미지 타일이 복수개로 결합된 상태를 도시한 예시도.
이하, 첨부된 도면을 참조하면서 본 발명에 따른 기능성 이미지 타일 및 그 제조방법에 대하여 더욱 상세하게 설명하도록 한다.
본 발명에 따른 기능성 이미지 타일은 석고와 물을 혼합한 원료에 황토와, 바잘트섬유와, 닥섬유를 혼합하여 조성된 혼합물을 통해 제조된 타일의 표면에 소망하는 이미지를 인쇄하여 제조된다. 본 발명에서 상기 타일의 표면에 이미지를 인쇄하는 방법은 본 발명의 권리범위에 한정하지 않으며, 예를 들어 직접인쇄방식을 통해 인쇄할 수 있다. 물론, 전사지에 이미지층을 형성한 후 타일 위에 전사지를 부착하여 인쇄하는 방법을 사용할 수도 있지만, 본 발명에 따른 타일 제조시 흡수성이 우수한 석고와 황토가 혼합되어 이미지 인쇄시 잉크가 원활하게 흡수되면서 이미지 인쇄가 용이하게 이루어질 수 있다.
본 발명에 따른 상기 원료는 석고 55~61중량%와 물 39~45중량%를 혼합하여 조성된다. 상기 물이 39~45중량%가 혼합되는 이유는 물의 혼합량에 따라 경화속도가 달라지기 때문인데, 경화속도를 조절하는 이유는 상기 원료를 통해 형성된 혼합물을 복수의 성형틀에 순차적으로 부은 후 성형틀 내부에 잔류하는 기포를 제거하는 작업을 해주어야 하는데, 경화속도가 너무 빠르면 기포를 제거할 수 없기 때문에 타일 제조시 품질이 저하되거나 불량이 발생하기 때문이다.
상기에서 석고가 55 중량% 미만의 경우에는 경화가 늦으며 물이 많기 때문에 성형 시 뒤면 마감의 효율이 떨어지며 제품완성 시 강도가 떨어지는 악영향이 있다. 또한 다공성 물질의 기능성 유지를 위한 기공 구현이 어렵다.
한편, 석고가 61 중량%를 초과하는 경우에는 경화 속도가 너무 빠르기 때문에 성형작업이 어려우며 표면 기포의 제거가 어려워 완성 시 불량이 발생하기 쉽다. 또한 다공성 물질의 기능성 유지를 위한 기공이 작아져 기능성 떨어진다.
물이 39중량% 미만의 경우에는 상기 석고 61% 초과시와 동일한 현상이 발생하고, 물이 45 중량%를 초과하는 경우에는 상기 석고 55% 미만시와 동일한 현상이 발생한다.
다음으로, 본 발명은 상기 원료에 황토와, 바잘트섬유와, 닥섬유를 혼합하여 혼합물을 조성한다.
상기 황토는 주거공간에서 발생하는 각종유해 물질을 차단하며, 고유의 기능에 의해 제독력, 분해력, 제습력과 보습력 등 탈취, 정화작용을 비롯한 원적외선 방사와 불연재의 특성을 가지고 있으며, 효소성분에는 카탈아아제(katalase), 디페놀옥시다아제(Diphenol Oxydase), 사카라아제(Saccharase), 프로테아제(Protease) 등 총 4종의 효소성분의 기능성을 가지고 있다. 카탈아아제(katalase)는 독소인 과산화수소를 제거하는 역할을 한다. 인체에서 대사 작용 과정에서 발생한 독소가 노화현상을 일으키는데, 흙의 강한 흡수력으로 체내 독소인 과산화 지질이 중화 또는 희석되는 노화현상을 방지한다. 디페놀옥시다아제(Diphenol Oxydase)는 분자상의 산소를 이용하여 일어나는 산화반응을 촉매하는 역할을 한다. 생활이나 생체 구성 성분위 합성에 필요한 에너지를 얻는데 필수적이며, 생체내에서는 여러가지 유/무기화합물의 산화환원이 이루어지도록 한다. 사카라아제(Saccharase)수크로오스를 가수분해하여 클로코오스(포도당)과 프룩토오스를 만드는 효소이고, 프로테아제(Protease)는 단백질 속 질소가 무기화 될 때에 단백질을 아미노산으로 가수분해 하는 역할을 한다. 면역력 밖의 불필요한 암 등 기타 부패한 세포를 순식간에 분해, 파괴할 수 있다. 이러한 효소가 존재하는 황토는 원적외선을 발생시켜 혈액의 흐름을 촉진시키고, 발한작용을 촉진시키며, 생체에 쌓인 노폐물을 배설시키고, 중금속을 방출하는 효과가 있으며, 향균 및 방충효과와 함께 곰팡이의 번식을 막고 제습효과가 탁월한 장점이 있다. 또한, 화학적, 전기적 방사성 물질들의 원인인 공기오염 정화기능이 있으며, 포르말린과 같은 유해물질을 정화시키고, 담배연기나 악취 제거가 가능하며, 유해전자파 차단, 여과 기능, 습도조절이 가능한 장점이 있다.
본 발명은 상기와 같은 다양한 효과를 내포하는 황토를 원료에 혼합하여 줌으로써 황토 고유의 장점을 살려 기능성을 극대화시킬 수 있으며, 이를 위해 상기 황토는 원료 100중량부에 대하여 1~30중량부가 혼합된다. 상기 황토가 1중량부 미만으로 혼합되면 성분 함량의 미달로 인하여 황토가 갖는 다양한 효과를 나타낼 수 없다.
상기에서 황토가 30 중량부 초과로 혼합되면 표면 다공성이 줄어 기능성이 저하되는 상황이 발생된다.
상기 바잘트섬유는 천연 현무암을 섬유화한 것으로 인장강도가 우수하고, 저밀도, 저열팽창성, 내열성, 화학적 안정성, 자기윤활성, 탄성, 흡음성의 특징을 갖고 있는 것으로, 화재에 강하고 인장도가 높아져 쉽게 깨지는 단점을 보완할 수 있다. 상기 바잘트섬유는 기존 유리섬유보다 성질이 우수하면서도 친환경적이므로 인테리어 마감재에 적합한 장점이 있다.
상기 바잘트섬유는 상기 원료 100중량부에 대하여 2~10중량부가 혼합되는데, 상기 바잘트섬유가 2중량부 미만으로 혼합되면 내열성, 강도가 저하되는 문제점이 있으며, 10중량부를 초과할 경우 과도한 뭉침현상으로 균일하게 성형이 되지 않고 제품생산이 어려운 문제점이 있다.
상기 닥섬유는 한지의 원료가 되는 재료로써 성형성과 친환경성이 우수하여 한지의 느낌을 살리는 인테리어 기능의 향상과 습도 조절능력을 향상시킬 수 있고, 아토피 등 환경성 피부질환의 저항력을 향상시킬 수 있다.
상기 닥섬유는 상기 원료 100중량부에 대하여 2~10중량부가 혼합된다. 상기 닥섬유가 2중량부 미만으로 혼합되면 습도 조절능력이 저하되는 문제점이 있으며, 10중량부를 초과할 경우 상기 바잘트섬유와 마찬가지로 과도한 뭉침현상으로 균일한 성형이 이루어지지 못하는 문제점이 발생할 수 있다.
또한, 본 발명은 상기 원료에 구문추 추출액과, 피톤치드 및 숯을 더 혼합하여 혼합물을 조성함으로써 더욱 다양한 기능(장점)을 갖는 타일을 제조할 수 있다.
구문초라 함은 펠라고늄(Pelargonium) 종에 속하며, 페니로얄민트 향과, 시트로넬라 향을 발산하며, 이 향이 지니고 있는 고유한 방향성질(INSECT REPELLENT PERFUME)을 통해 모기를 비롯한 각종의 해충들이 가까이 접근하지 못하도록 효과적으로 차단 및 퇴치하여 주는 효과가 있다. 상기 구문초 추출액은 다양한 방법을 통해 추출할 수 있으며, 예를 들어 구문초로부터 잎사귀를 분리하여 압착한 후 고형분을 분리, 제거함으로써 얻을 수 있다.
상기 구문초 추출액은 상기 원료 100중량부에 대하여 1~30중량부가 혼합된다. 상기 구문초 추출액이 1중량부 미만으로 혼합될 경우 성분 함량의 미달로 인하여 모기, 해충의 차단 및 퇴치효과가 저하될 수 있다. 또한, 상기 구문초 추출액은 장미향을 발산하는 특징이 있으므로 기준치 범위 내에서 다량의 구문초 추출액을 혼합할 경우 방향제로서의 효과를 얻을 수도 있다.
한편, 상기 구문초가 30 중량부 초과로 혼합되면 기능성은 증가하지 않으며 오히려 원재료가 경화되는 것을 방해하며 강도 저하가 발생된다.
상기 피톤치드는 식물 주위의 미생물이나 병원균에 저항하기 위하여 방사하는 천연향균물질로 항균뿐만 아니라 스트레스완화, 면역기능향상, 중추신경 안정, 탈취 등의 효과가 있어 방향제, 아토피 치료제와 새집증후군에 따른 유해가스제거제 등에 사용된다.
상기 피톤치드는 상기 원료 100중량부에 대하여 1~30중량부가 혼합된다. 상기 피톤치드가 1중량부 미만으로 혼합되면 항균성 저하, 스트레스완화 기능 저하, 면역기능저하, 탈취 기능 저하 등의 단점이 있다.
상기 피톤치드가 30 중량부 초과로 혼합되면 기능성은 증가하지 않으면서 오히려 원재료가 경화되는 것을 방해하며 강도 저하가 발생된다.
상기 숯은 공기를 정화시켜 주고, 많은 양의 음이온을 방출시켜 부교감신경에 영향을 주어서 기분을 안정시키고 몸 긴장을 이완시켜주는 효과가 있으며, 원적외선을 방출시켜 혈액순환을 촉진시켜준다. 또한, 상기 숯은 우수한 흡착력과 도전성, 축전성이 있어 전자파를 차단시켜주며, 악취를 흡착하는 효과가 있으며, 공기 정화 및 습도 조절이 가능하며, 항균 및 해독기능을 갖으며, 병충해의 침입을 방지해주고, 숙면과 피로회복에 도움을 주어 기력을 충전시켜주는 탁월한 효과가 있다.
상기 숯은 원료 100중량부에 대하여 1~30중량부가 혼합되며, 공기정화, 방향 및 탈취효과, 병충해 방지, 전자파 흡수, 항균, 숙면과 피로회복 기능, 기력 충전, 음이온 발산 및 습도조절과 같은 기능성을 더욱 극대화 시킬 수 있다. 상기 숯이 1중량부 미만으로 혼합되면 성분 함량의 미달로 인하여 숯이 갖는 다양한 효과를 나타낼 수 없다.
한편, 상기 숯이 30 중량부 초과로 혼합되면 표면의 다공성을 저하시키며 제품 표면에 숯이 묻어나는 현상 발생된다.
본 발명에서 사용된 각 섬유(바잘트섬유, 닥섬유)의 경우 2 중량부 미만시 섬유의 기능을 발현할 수 없으며, 10 중량부 초과시 기능성은 향상되지 않으며 섬유 뭉침 현상이 발생된다.
상기 기능성 이미지 타일에 원료 100중량부에 대하여 시트로넬라 에센스 및 로즈마리 에센스 중에서 적어도 하나이상이 각각 1-30 중량부가 더 혼합될 수 있다, 상기 에센스들은 방충기능 향상에 관계된다.
추가적으로 사용될 탄소섬유 역시 상기의 다른 섬유와 마찬가지로 중량부 함량을 벗어날 경우 상기의 문제가 발생된다.
상기 탄소섬유에 포함된 기능성 이미지 타일에 원료 100중량부에 대하여 시트로넬라 에센스 및 로즈마리 에센스 중에서 적어도 하나이상이 각각 1-30 중량부가 더 혼합될 수 있다.
상기 에센스는 1 중량부 미만시 방충기능이 미미하고, 30 중량부 초과시 너무 과한 효과와 함께 비용이 올라간다.
본 발명은 상기와 같이 조성된 혼합물을 성형틀 또는 금형 내부에 투입, 성형 후 탈형하여 타일을 제조하고, 상기 타일의 표면에 소망하는 이미지(예를 들어, 사진이나 캐릭터 또는 풍경)를 인쇄하여 제조된다.
도 1은 본 발명에 따른 기능성 이미지 타일의 제조공정도이다 (S 101-S 107)
석고 55~61중량%와 물39~45중량%을 혼합하여 원료를 형성하는 단계와; 상기 원료 100중량부에 황토 1~30중량부와, 바잘트섬유 2~10중량부와, 닥섬유 2~10중량부를 혼합하여 혼합물을 형성하는 단계와; 상기 혼합물을 성형틀 또는 금형 내부에 투입한 다음 탈형하여 타일을 제조하는 단계; 및 상기 타일의 표면에 소망하는 이미지를 인쇄하는 단계; 를 포함한다.
도 2는 본 발명에 따른 타일의 전자현미경 사진이다. 도 2에 나타난 바와 같이 본 발명에 따른 타일에는 수많은 기공(40)이 형성되어 있다는 것을 알 수 있다. 상기 타일의 표면에 형성된 기공은 공기의 유통 및 흡습 효과를 향상시켜주며, 실내의 온,습도 조절에 큰 영향을 미친다.
종래의 타일은 표면 기공이 작아 실내의 습도를 흡습하는 능력이 없었으며, 이에 따라 습기가 많은 공간에서는 타일의 표면 위에 이슬 맺힘이 일어나게 되고, 그에 따른 벽면에 곰팡이가 생기게 되면 거주자의 호흡기에 질환을 일으키거나 불결한 환경에서 생활하게 되어 불쾌감이 커지게 되는 문제점이 있었다. 또한, 종래의 타일은 공기를 유통시키지 못함으로써 통기가 불량하고 주거공간에 습도가 높아지며, 그에 따른 주거공간에 세균이나 곰팡이가 번식하는 원인이 되었으며, 원적외선 방사, 조습, 탈취효과 및 항균효과가 거의 없었다. 따라서, 오직 청소용이나 장식용일 뿐 건강 증진의 기능은 거의 없는 단순한 건축 내장재에 해당된다.
또한, 종래의 이미지 타일은 표면 기공이 작은 종래의 타일의 표면에 이미지를 인쇄하되, 인쇄된 이미지를 보호하기 위하여 이미지 위에 코팅작업(예를 들어 우레탄 수지를 코팅하는 작업)이 이루어져야만 했는데, 이와 같이 타일의 표면에 코팅층이 형성되면 타일의 표면에 형성된 기공을 모두 차단해버리기 때문에 공기의 유통을 완벽하게 차단하여 통기성이 더욱 떨어지는 문제점이 있었다.
이에 반하여, 본 발명에 따른 타일은 표면에 수많은 기공이 형성되어 있어서 공기정화성능이 탁월하여 실내의 습도조절이 원활하고, 그에 따른 주거공간에 세균이나 곰팡이가 번식하는 것을 방지할 수 있다.
또한, 상기 타일의 표면에 이미지를 인쇄하여 제조되는 이미지 타일은 흡수성이 우수한 석고와 황토를 혼합하여 제조되기 때문에 표면에 이미지 인쇄시 잉크를 원활하게 흡수할 수 있으며, 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있다. 이에 따라 이미지를 보호하기 위한 코팅층을 형성하는 코팅작업을 생략할 수 있고, 표면에 형성된 기공이 코팅층에 의해 막히는 것을 방지할 수 있으므로 상기 황토, 바잘트섬유, 닥섬유를 혼합하여 얻을 수 있는 효과가 저하되는 것을 방지할 수 있다.
한편, 이미지 타일은 시공하는 벽면의 가로, 세로방향을 따라 순차적으로 결합되며, 대부분 표면에 서로 다른 이미지가 인쇄된다. 여기에서 서로 다른 이미지들은 하나의 단일 이미지를 분할한 분할 이미지이다. 예를 들어, 도 3과 같이 꽃과 나비를 포함하는 단일 이미지에 대하여, 복수의 타일들 중에서 좌측 하단에 위치한 타일(20)은 나비(30)가 인쇄되어 있고, 상단 중앙에 위치하는 타일(20′)는 꽃의 이미지 중에서 꽃잎(30′)이 인쇄되어 있다. 상기 복수의 타일들 각각은 단독으로는 하나의 완성된 이미지를 표시할 수는 없지만 전체로서 적절히 배열되어 하나의 완성된 이미지를 표시할 수 있다.
물론, 복수의 타일들이 동일한 이미지를 갖도록 할 수도 있지만, 심미성이나 입체감을 살리기 위하여 복수의 타일들 각각에 분할 이미지를 표시하는 방법을 이용한다. 즉, 단일 타일의 표면 전체에 이미지가 인쇄되는 것이 아니므로 표면에 형성된 복수의 기공 전체가 차단되지 않으며, 도 3에 도시된 나비(30)가 인쇄되어 있는 타일(20)의 우측에 시공되는 타일과 같이 표면에 이미지가 전혀 인쇄되지 않을 수도 있으므로 본 발명에 따른 기능성 이미지 타일(10)을 복수개로 시공할 경우 황토, 바잘트섬유, 닥섬유를 비롯해 필요에 따라 더 혼합되는 구문초 추출액, 피톤치드 및 숯으로부터 얻을 수 있는 다양한 효과, 효능을 기대할 수 있다.
* 실시예 1
석고 60중량%와 물 40중량%를 혼합하여 원료를 조성한 다음, 상기 원료 100중량부에 대하여 황토 25중량부와, 바잘트섬유 9중량부와, 닥섬유 7중량부를 혼합하여 혼합물을 형성하였다.
상기 혼합물을 성형틀 내부에 투입하여 경화시킨 다음 성형틀에서 탈형하여 타일을 제조한 다음, 상기 타일의 표면에 이미지를 인쇄하여 본 발명에 따른 기능성 이미지 타일을 제조하였다.
* 실시예 2
석고 60중량%와 물 40중량%를 혼합하여 원료를 조성한 다음, 상기 원료 100중량부에 대하여 황토 5중량부와, 바잘트섬유 5중량부와, 닥섬유 5중량부를 혼합하여 혼합물을 형성하였다.
상기 혼합물을 성형틀 내부에 투입하여 경화시킨 다음 성형틀에서 탈형하여 타일을 제조한 다음, 상기 타일의 표면에 이미지를 인쇄하여 본 발명에 따른 기능성 이미지 타일을 제조하였다.
* 실시예 3
석고 60중량%와 물 40중량%를 혼합하여 원료를 조성한 다음, 상기 원료 100중량부에 대하여 황토 30중량부와, 바잘트섬유 10중량부와, 닥섬유 10중량부를 혼합하여 혼합물을 형성하였다.
상기 혼합물을 성형틀 내부에 투입하여 경화시킨 다음 성형틀에서 탈형하여 타일을 제조한 다음, 상기 타일의 표면에 이미지를 인쇄하여 본 발명에 따른 기능성 이미지 타일을 제조하였다.
* 실시예 4
석고 60중량%와 물 40중량%를 혼합하여 원료를 조성한 다음, 상기 원료 100중량부에 대하여 황토 25중량부와, 바잘트섬유 9중량부와, 닥섬유 7중량부와, 구문초추출액 20 중량부, 피톤치드 20중량부, 숯 중량부를 혼합하여 혼합물을 형성하였다.
상기 혼합물을 성형틀 내부에 투입하여 경화시킨 다음 성형틀에서 탈형하여 타일을 제조한 다음, 상기 타일의 표면에 이미지를 인쇄하여 본 발명에 따른 기능성 이미지 타일을 제조하였다.
* 비교예 1
석고 60중량%와 물 40중량%를 혼합하여 원료를 조성한 다음, 상기 원료 100중량부에 대하여 황토 40중량부와, 바잘트섬유 1중량부와, 닥섬유 20중량부를 혼합하여 혼합물을 형성하였다.
상기 혼합물을 성형틀 내부에 투입하여 경화시킨 다음 성형틀에서 탈형하여 타일을 제조한 다음, 상기 타일의 표면에 이미지를 인쇄하여 본 발명에 따른 기능성 이미지 타일을 제조하였다.
구 분 | 유해물질흡착/악취제거 | 습도조절 | 방음/내화성 | 면역력 향상 |
방충기능 |
실시 예 1 | 5 | 5 | 5 | 1 | 0 |
실시 예 2 | 5 | 5 | 3 | 0 | 0 |
실시 예 3 | 5 | 5 | 5 | 1 | 0 |
실시 예 4 | 5 | 5 | 5 | 5 | 5 |
비교 예 1 | 3 | 3 | 3 | 1 | 0 |
상기 결과에 나타난 바와 같이, 본 발명에서 기술되고 있는 모든 성분들이 적절한 함량으로 제조된 타일에서의 효과가 제일 우수하였다.
상기한 바와 같이 본 발명은, 기능성 이미지 타일 및 그 제조방법에 관한 것으로, 더욱 상세하게는 석고와 물을 혼합하여 조성된 원료에 황토와, 바잘트섬유(basalt fiber)와, 닥섬유(mulberry fiber)를 혼합한 혼합물을 통해 제조된 타일의 표면에 소망하는 이미지를 인쇄하여 제조되며, 흡수성이 우수한 석고와 황토가 혼합되어 이미지 인쇄시 잉크를 원활하게 흡수할 수 있고, 표면에 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있고, 바잘트섬유와 닥섬유가 혼합되어 내열성, 강도, 습도조절능력이 우수한 것을 특징으로 하는 기능성 이미지 타일 및 그 제조방법에 관한 것이다.
Claims (6)
- 석고와 물을 혼합하여 조성된 원료에 황토와, 바잘트섬유와, 닥섬유를 혼합한 혼합물을 통해 제조된 타일의 표면에 소망하는 이미지를 인쇄하여 제조되며,
흡수성이 우수한 석고와 황토가 혼합되어 이미지 인쇄시 잉크를 원활하게 흡수할 수 있고, 표면에 인쇄된 이미지가 벗겨지거나 수분에 의해 번지는 현상을 방지할 수 있고, 바잘트섬유와 닥섬유가 혼합되어 내열성, 강도, 습도조절능력이 우수한 것을 특징으로 하는 기능성 이미지 타일. - 제1항에 있어서, 상기 기능성 이미지 타일은 석고 55~61중량%와 물 39~45중량%를 혼합하여 조성된 원료 100중량부에 대하여 황토 1~30중량부와, 바잘트섬유 2~10중량부와, 닥섬유 2~10중량부가 혼합되는 것을 특징으로 하는 기능성 이미지 타일.
- 제2항에 있어서, 상기 기능성 이미지 타일은 원료 100중량부에 대하여 구문초 추출액 1~30중량부, 피톤치드 1~30중량부, 숯 1~30중량부가 더 혼합되는 것을 특징으로 하는 기능성 이미지 타일.
- 제 2항 또는 3에 있어서, 상기 기능성 이미지 타일은 원료 100중량부에 대하여 탄소섬유 2~10중량부가 더 혼합되는 것을 특징으로 하는 기능성 이미지 타일.
- 제 4항에 있어서, 상기 기능성 이미지 타일은 원료 100중량부에 대하여 시트로넬라 에센스 및 로즈마리 에센스 중에서 적어도 하나이상이 각각 1-30 중량부가 더 혼합되는 것을 특징으로 하는 기능성 이미지 타일.
- 석고 55~61중량%와 물39~45중량%을 혼합하여 원료를 형성하는 단계와;
상기 원료 100중량부에 황토 1~30중량부와, 바잘트섬유 2~10중량부와, 닥섬유 2~10중량부를 혼합하여 혼합물을 형성하는 단계와;
상기 혼합물을 성형틀 또는 금형 내부에 투입한 다음 탈형하여 타일을 제조하는 단계; 및
상기 타일의 표면에 소망하는 이미지를 인쇄하는 단계; 를 포함하여 이루어지는 것을 특징으로 하는 기능성 이미지 타일의 제조방법.