KR20170022757A - Hydrogel Alginate Non-woven mask pack - Google Patents
Hydrogel Alginate Non-woven mask pack Download PDFInfo
- Publication number
- KR20170022757A KR20170022757A KR1020150118165A KR20150118165A KR20170022757A KR 20170022757 A KR20170022757 A KR 20170022757A KR 1020150118165 A KR1020150118165 A KR 1020150118165A KR 20150118165 A KR20150118165 A KR 20150118165A KR 20170022757 A KR20170022757 A KR 20170022757A
- Authority
- KR
- South Korea
- Prior art keywords
- mask pack
- alginate
- fibers
- hydrogel
- nonwoven
- Prior art date
Abstract
An alginate nonwoven mask pack produced by mixing calcium alginate polymer fibers and different types of fibers by a method comprising mixing the calcium alginate polymeric fibers with water soluble hydrogel alginate It is characterized by reforming.
Description
More particularly, the present invention relates to an alginate nonwoven mask pack produced by blending calcium alginate polymer fibers and a different kind of fibers in the form of a sheet, wherein the insoluble calcium alginate polymer in the calcium alginate polymer fiber is water- Wherein the hydrogel alginate nonwoven fabric is modified with hydrogel alginate.
In general, the cosmetic mask pack is made by adding water or lotion to a sheet such as a nonwoven fabric, or adding a cosmetic solution such as a natural or synthetic substance known to have a function. Such a cosmetic mask pack is a functional cosmetic product which is attached to the face and supplies the cosmetic ingredient contained in the mask pack to the skin, thereby moisturizing the skin and removing the waste matter of the keratin and pore to restore the skin physiological function It is a kind.
In such a mask pack, there are various kinds of sheets to which a cosmetic ingredient is applied, and among them, a nonwoven fabric type which can be made thin is widely used. The nonwoven mask pack is manufactured by cutting a thin nonwoven fabric into a face shape and immersing the cosmetic ingredient on one face thereof, which is advantageous in that it is inexpensive and easy to use.
However, even if the nonwoven mask pack is fixed to the skin, the nonwoven mask pack is not firmly adhered to a desired site, and a part of the pack is excited at the bending portion, so that the cosmetic ingredient of the mask pack is not effectively transferred to the skin. In addition, the synthetic polymer is often added to the nonwoven fabric in accordance with the manufacturing process, and when the cosmetic liquid is added, the resultant fiber becomes stiff, and the feeling of use is poor and the skin affinity is low. In addition, in the case of a formulation in which the nonwoven fabric is soaked in an additive such as a cosmetic liquid to induce continuous absorption of the cosmetic liquid, the skin adhesion is poor, and since too high a cosmetic ingredient comes into contact with the skin at an early stage, disadvantage And 10 to 15 minutes, the moisture is evaporated and dried, and the mask pack falls off the face.
In order to overcome the drawbacks of such a nonwoven mask pack, research and development on a hydrogel mask pack have been actively conducted. The hydrogel is a material having a three-dimensional hydrophilic polymer network structure using purified water as a dispersion medium. The hydrogel is capable of absorbing a large amount of water, and has the same flexibility as a natural tissue. The hydrogel has elasticity, skin adhesion, Is used as a mask pack substrate improved in moisturizing, nutritional supply or exfoliation effect.
However, when a mask pack is manufactured using only the hydrogel itself, the shape of the mask pack may be difficult to maintain due to its low mechanical strength. In order to maintain the shape of the mask pack, a synthetic resin, a nonwoven fabric, ), And the like. However, in this case, since the gel-like hydrogel may elute the chemical components of the synthetic resin, it is necessary to examine from the standpoint of biocompatibility and stability, as well as inconvenience due to the use of the support, insufficient cosmetic ingredients and relatively high There are disadvantages such as price.
In order to improve the disadvantages of the nonwoven mask pack and the hydrogel mask pack as described above, a hydrogel mask pack, a method for producing the same, and a composition used for the production thereof (hereinafter referred to as Patent Document 1 Discloses a hydrogel nonwoven fabric, a method for producing the nonwoven fabric, and a mask pack (hereinafter referred to as "Patent Document 2") using the same, which are disclosed in Japanese Patent Application Laid-Open No. 10-1296105.
However, in Patent Document 1, a hydrogel mask pack is manufactured by gelating a composition for a hydrogel mask pack. Rather, due to excessive adhesive force of the product itself, a phenomenon of aggregation occurs in the mask pack product itself, There is an inconvenience. Patent Document 2 discloses that a hydrogel is impregnated using a nonwoven fabric as a mask pack support, and there is a possibility that the gel-like hydrogel still elutes the chemical components of the synthetic resin, thereby causing skin trouble due to skin irritation There was a problem that could be.
Disclosure of the Invention The present invention has been conceived to solve the problems described above, and it is an object of the present invention to provide a calcium alginate polymer having excellent adhesion, feel and transparency by modifying an insoluble calcium alginate polymer with water-soluble hydrogel alginate, The hydrogel liquid cosmetic solution maintains the active ingredients of the hydrogel liquid for a long period of time through the formation of microcapsules and high water retention, thereby providing a sufficient supply of nutrients to the skin. The hydrogel alginate nonwoven mask pack having anti-whitening, moisturizing, skin barrier strengthening and anti- .
In order to solve the above-mentioned problems, the hydrogel alginate nonwoven mask pack according to the present invention is an alginate nonwoven mask pack prepared by mixing calcium alginate polymer fibers and different types of fibers and forming a sheet, wherein the insoluble calcium alginate polymer in the calcium alginate polymer fiber Is modified with water-soluble hydrogel alginate.
Further, the modification is characterized in that the calcium ion of the insoluble calcium alginate polymer is substituted with a metal salt.
The metal salt may include any one of potassium (K), magnesium (Mg), and sodium (Na).
In addition, the heterogeneous fibers include at least one selected from the group consisting of regenerated fibers and natural fibers.
Also, the aliphatic nonwoven mask pack may contain 10 to 99% by weight of the heterogeneous fibers.
As described above, according to the present invention, the insoluble calcium alginate polymer in the calcium alginate polymer fiber is modified with the water-soluble hydrogel alginate, so that the adhesion, feel and transparency are excellent, and the water- It is possible to maintain the activity of the active ingredient contained in the hydrogel cosmetic liquid for a long time to provide sufficient nutrition to the skin and to provide anti-whitening, moisturizing, skin barrier enhancement, and anti-inflammatory effects.
Hereinafter, the present invention will be described in detail.
An alginate nonwoven mask pack produced by mixing calcium alginate polymer fibers and different types of fibers by using calcium alginate polymer fibers made of alginate as a raw material, wherein the calcium alginate polymer fibers are mixed with calcium Characterized in that the alginate polymer is modified with water-soluble hydrogel alginate.
The alginate of the calcium alginate polymer fiber is a kind of seaweed polysaccharide which constitutes a cell membrane and intercellular material of brown algae which is one of the marine organisms and is often called alginic acid. It is a block of malonic acid (M) unit, a block of glutaric acid And the block of MG unit in the middle is a linear copolymer composed of 1,4-glycoside.
The physicochemical properties of the alginic acid are determined by viscosity, solubility, ion exchange capacity, and the like depending on the relative ratio of the block of malonic acid (M) unit, the block of gluronic acid (G) And its structure is shown in the following reference drawing 1.
[Reference drawing 1]
Structure of Alginate
These alginates are used in the form of sodium alginate, which is water-soluble rather than alginic acid itself, which is usually insoluble in water, because the alginic acid has a carboxyl group (-COOH) of uronic acid in the molecule. When the calcium chloride solution is spun in a coagulating bath, . Particularly, alginic acid has functions and effects such as water retention, stickiness, lubricity, gelation and emulsification stability, physiological activity, and is not toxic to human body, easy to process, Is widely used.
In general, the calcium alginate polymer fiber of the alginate nonwoven mask pack forms calcium insoluble calcium alginate which is insoluble in water through strong ionic bonding instead of hydrogen in the carboxyl group of the alginate. If the mask pack is manufactured by blending, the skin adhesion feeling and feel are deteriorated, and the cosmetic ingredient of the essence liquid is not effectively transferred to the facial skin.
Therefore, it is necessary to convert the calcium alginate polymer fibers of the nonwoven mask pack into water-soluble alginate fibers so as to improve the adhesion feeling, feel and transparency of the mask pack. This is achieved by modifying the insoluble calcium alginate polymer in the calcium alginate polymer fibers with water-soluble hydrogel alginate So that the calcium alginate polymer fiber has a water-soluble property.
In the present invention, the modification is carried out by replacing the calcium ion of the insoluble calcium alginate polymer with a metal salt.
The metal salt may be any one selected from the group consisting of sodium chloride, sodium lactate, sodium citrate, potassium chloride, potassium lactate, potassium citrate, , Magnesium sulfide and the like is used to modify the insoluble calcium alginate polymer with water-soluble hydrogel alginate.
In the calcium alginate polymer fiber, calcium is present as an insoluble calcium alginate polymer through ionic bonding with an alginate polymer. In this case, potassium (K), magnesium (Mg), and sodium Na), the calcium alginate polymer fibers are converted into water-soluble alginate fibers by modifying the insoluble calcium alginate polymer with water-soluble alginate by replacing the calcium ions with the metal alginate polymer.
[Reference drawing 2]
On the other hand, such modification by the substitution reaction can be carried out by combining the above metal salts with each other or in a predetermined ratio to prepare purified water, allantoin, adenosine, arginine, 1,3-butylene glycol, panthenol, glycerin, 60 hydrogenated castor oil or hydroxyethyl cellulose, and the calcium alginate polymer fiber and the heterogeneous fiber are blended with each other to form an alginate nonwoven mask pack, Is impregnated with the essence liquid.
Here, the metal salt concentration of the essence solution is preferably 0.01 to 50% by weight.
Meanwhile, in the present invention, the alginate nonwoven mask pack is prepared in a sheet form by blending calcium alginate polymer fibers and different types of fibers, and the different types of fibers include at least one kind selected from the group consisting of regenerated fibers and natural fibers to be.
In the alginate nonwoven mask pack, 10 to 99% by weight of heterogeneous fibers are preferably added, and 10 to 90% by weight of heterogeneous fibers are most preferably added.
In the present invention, the above different kind of fibers are composed of regenerated fibers such as cellulose fibers and rayon fibers, and natural fibers such as cotton fibers, hemp fibers, silk fibers and bamboo fibers instead of the fibers made of synthetic resin, The water soluble hydrogel alginate modified from the insoluble calcium alginate polymer in the alginate polymer fiber can prevent the elution of the chemical component of the synthetic resin, thereby minimizing troubles due to skin irritation.
As described above, the present invention can maintain the activity of the active ingredient contained in the hydrogel cosmetic liquid for a long period of time through the formation of the micro-film of the water-soluble alginate component and the high water retention, Moisturizing, strengthening skin barrier, and anti-inflammation.
Hereinafter, the present invention will be described in more detail with reference to the following Examples, Comparative Examples and Experimental Examples.
It should be understood, however, that the invention is not construed as being limited to the embodiments set forth herein, but is capable of modifications and equivalents within the spirit and scope of the invention. Will be apparent to those skilled in the art to which the present invention pertains.
[Example 1]
Calcium alginate polymer fibers and cellulose fibers were blended in a weight ratio of 50:50 to prepare an alginate nonwoven mask pack in sheet form.
The essence liquid impregnated in the alginate nonwoven mask pack was prepared by adding sodium lactate having a composition ratio of 0.5 in order to contain ingredients for cosmetic use as shown in Table 1 below.
Next, an essence solution prepared as described above was impregnated into the alginate nonwoven mask pack to prepare a hydrogel alginate nonwoven mask pack.
[Example 2]
A hydrogeled alginate nonwoven mask pack was prepared in the same manner as in Example 1 except that the component ratio of sodium lactate added to the essence solution was changed to 1.0.
[Comparative Example]
In Example 1, a hydrogeled alginate nonwoven mask pack was prepared in the same manner as in Example 1, except that no sodium lactate was added to the essence solution.
[Experimental Example 1] Whitening effect
The following experiment was conducted to examine the whitening effect on human skin.
First, in 12 healthy men, an opaque tape with a hole of 1.5 cm in diameter was attached to the upper part of the subject's neck, and then the skin was blackened by irradiating the subject with 1.5 to 2 times of the minimum erythema Respectively.
After irradiating the ultraviolet rays, the mask packs prepared in the above Examples and Comparative Examples were stuck for 15 minutes and then peeled off. Thereafter, the state changes were observed for 8 weeks, and the skin color was measured with a colorimeter CR2002 (Minolta Co., Japan) every 1 week.
Then, the difference (ΔL *) between the skin color and the skin color at the time of attaching and removing the mask pack prepared in the above Examples and Comparative Examples was calculated according to the following Equation 1, and the results are shown in Table 2 below. On the other hand, the whitening effect was determined by comparison of? L * between the mask pack attachment sites of Examples 1 and 2 and Comparative Example. When? L * value is about 2, whitening of the deposited pigment is noticeable. As shown in FIG.
As a result of the above Table 2, it can be confirmed that the whitening effect of Example 2 in which the essence liquid containing sodium lactate containing 1.0 component ratio is impregnated into the nonwoven mask pack shows the highest whitening effect, It can be confirmed that it has an excellent whitening effect.
It can be seen that the whitening effect can be improved by modifying the insoluble calcium alginate polymer with water-soluble hydrogel alginate.
[Experimental Example 2] Effect of moisturizing and skin barrier function improvement
30 healthy women were divided into three groups (A, B, and C) at a temperature of 25 ° C and a relative humidity of 45% in a room without air flow. The mask pack of Example 2 was applied to the group B, and the mask pack of the comparative example was applied to the upper arm of the subjects for the group C three times a day for 6 weeks, and then the TEWAMETER TM300 (C + K electronic Transepidermal Water Loss (TEWL) value was measured by the TEWL value change amount TEWL with time according to the change of the transdermal water loss by using a CORNEOMETER CM 820 PC (C + K electronic GmbH, Germany) The moisture content of the skin was quantified from 0 to 150 according to the change of the electric conductivity according to the moisture content of the skin. The results are shown in Table 3 below.
As can be seen from the results of Table 3, the hydrogel alginate nonwoven mask pack modified by the metal salt of the present invention shows a much higher moisture loss than that of the unmodified alginate nonwoven mask pack, . Also, it can be seen that Examples 1 and 2 show a higher increase in the corneometer value, which is a measure of the water content of the skin, as compared with the comparative example.
That is, the hydrogel alginate nonwoven mask pack according to the present invention can effectively transfer the cosmetic ingredient of the essence liquid to the skin by modifying the insoluble calcium alginate polymer with the water-soluble hydrogel alginate, Skin transdermal water loss is improved, and it is found to be very effective in improving moisturizing and skin barrier function.
[Experimental Example 3] Anti-inflammatory effect
First, 30 women were divided into 3 groups by applying a 5% solution of SDS (sodium dodecyl sulphate) for 4 hours to the cosmetic application area of the test subject, and then the mask pack of Example 1 was divided into three groups and the group B The mask pack of Example 2 was applied to the group and the mask pack of the comparative example was applied to the area of 2 x 2 (cm 2) of the arm on the left side of the arm for 6 weeks twice a day, The degree of inflammation due to stimulation induced by SDS application was observed by measuring the degree of skin erythema with a measuring device (Mexameter MX18, C + K Electronics GmbH Germany).
As can be seen from Table 4, the hydrogel alginate nonwoven mask pack modified with the metal salt of the present invention is superior to the alginate nonwoven mask pack which has not been modified.
As described above, the hydrogeled alginate nonwoven mask pack according to the present invention is excellent in adhesion, feel and transparency, and also has an effect component included in the hydrogel cosmetic liquid through the formation of a microfilm of a water-soluble alginate component and a high water- It is possible to prepare a hydrogel alginate nonwoven mask pack having the characteristics of anti-whitening, moisturizing, strengthening of skin barrier, and anti-inflammation while maintaining sufficient activity for skin for a long time.
Claims (5)
Wherein the insoluble calcium alginate polymer in the calcium alginate polymer fiber is modified with water-soluble hydrogel alginate.
Wherein the modification is carried out by replacing the calcium ion of the insoluble calcium alginate polymer with a metal salt.
Wherein the metal salt comprises any one of potassium (K), magnesium (Mg), and sodium (Na).
Wherein the heterogeneous fibers comprise at least one selected from the group consisting of regenerated fibers and natural fibers.
The alginate nonwoven mask pack according to any one of the preceding claims, wherein the aliphatic nonwoven fabric mask pack comprises 10 to 99% by weight of the heterogeneous fibers.