KR20170012073A - Manufacturing method of veneer, piece of veneer, veneer and decorative sheet of veneer - Google Patents
Manufacturing method of veneer, piece of veneer, veneer and decorative sheet of veneer Download PDFInfo
- Publication number
- KR20170012073A KR20170012073A KR1020160091635A KR20160091635A KR20170012073A KR 20170012073 A KR20170012073 A KR 20170012073A KR 1020160091635 A KR1020160091635 A KR 1020160091635A KR 20160091635 A KR20160091635 A KR 20160091635A KR 20170012073 A KR20170012073 A KR 20170012073A
- Authority
- KR
- South Korea
- Prior art keywords
- veneer
- wood
- piece
- width
- pieces
- Prior art date
Abstract
Description
본 발명은 베니어의 제조 방법, 베니어편, 베니어 및 베니어 화장판에 관한 것이다. 자세하게는, 제조 비용을 최소화하면서 천연 나무의 안정감과 따뜻한 나무 질감을 구비하고, 나뭇결무늬와 색상이 통일된 베니어의 제조 방법, 베니어편, 베니어 및 베니어 화장판에 관한 것이다.The present invention relates to a method of manufacturing a veneer, a veneer piece, a veneer and a veneer veneer. More specifically, the present invention relates to a method for manufacturing a veneer having a natural wood feeling of stability and a warm wood texture while minimizing a manufacturing cost and having a uniform grain pattern and color, a veneer flake, a veneer and a veneer flake.
종래부터, 인테리어 가구의 재료, 또는 바닥이나 벽의 내장 자재로 베니어 화장판 또는 프린트 합판이 널리 사용되고 있다.Background Art [0002] Conventionally, veneer sheets or printed plywood have been widely used as materials for interior furniture, or as an integral material of floor or wall.
여기서, 베니어 화장판은, 공지된 바와 같이, 천연 나무의 각목을 얇게 슬라이스(절단)한 판을 합판 등의 기재 표면에 붙인 것이다.Here, as is well known, a veneer sheet is obtained by slicing (slicing) a piece of natural wood thinly on the surface of a substrate such as a plywood.
이 같은 베니어 화장판에 부착되는 베니어의 제조 방법은, 예를 들면 특허 문헌 1에 개시되어 있다. 구체적으로는 그림 3에 도시된 바와 같이, 먼저 원목으로부터 제재한 물건 가공에 적합한 형상의 목재편을 취하고, 취한 목재소편을 그 절삭 가공성을 높이기 위해, 소정 시간 끓인다.A manufacturing method of a veneer to be attached to such a veneer board is disclosed in, for example,
그리고, 자비한 목재소편을 슬라이스 기계 등으로 얇게 절단하여, 적당한 함수율이 될 때까지 건조시킴으로써, 천연 나무의 베니어를 얻을 수 있다.The veneer of a natural wood can be obtained by cutting a small piece of wood with a thin slice machine or the like and drying it until the moisture content becomes appropriate.
상기의 방법으로 제조된 베니어는 합판 등의 기재에 붙여, 베니어 화장판으로하여, 예를 들어 인테리어 가구의 재료, 또는 바닥이나 벽 등의 내장 자재로 사용하면, 천연 나무가 갖는 독특한 나뭇결무늬를 실현함과 동시에 전체적으로 안정정이고 따스한 나무 질감을 느낄 수 있다.The veneer produced by the above method is attached to a base material such as plywood and used as a veneer to realize a unique grain pattern of natural wood, for example, as a material for interior furniture, or as an interior material for a floor or a wall. At the same time, it is totally stable and can feel warm wood texture.
이에 대응하여, 프린트 합판은, 나뭇결무늬 등을 그라비아 인쇄 한 종이, 또는 필름을 기 재료에 붙인 것이며, 베니어 화장판에 비해 원재료비 및 제조 비용이 억제되기 때문에 저렴하게 제작할 수 있는 동시에 각 프린트 합판의 모양이나 색상을 균일하게 할 수 한다. 따라서, 예를 들어, 특정 모양으로 통일 한 나뭇결무늬의 프린트 합판을 인테리어 가구 재료, 또는 바닥이나 벽 등 내장 자재로 사용하면, 제품 간의 편차가 없이, 동일한 모양이나 색채를 갖는 인테리어 가구, 또는 내장 디자인을 실현할 수 있다.In response to this, the printed plywood is made by gravure printing paper or film of wood grain or the like on a base material. Since the raw material cost and manufacturing cost are suppressed as compared with the veneer, And the color can be made uniform. Therefore, for example, when a wood-printed plywood of a certain shape is used as an interior furniture material, or as an interior material such as a floor or a wall, it is possible to produce interior furniture having the same shape or color, Can be realized.
그런데, 천연 나무는 종류와 생육 환경 등에 따라, 그 나뭇결 모양, 및 색상이 개별 천연 나무에서 다르고, 그것이 천연 나무의 장점이자 개성으로 평가하고, 일물품 상품으로 상품 가치를 높일 수 있다.By the way, the natural wood is different from the natural wood according to the kind and the growing environment, the grain shape and the color of the natural wood, and it is evaluated as the advantage and the characteristic of the natural wood, and the value of the commodity can be increased.
한편, 제품 간의 디자인의 편차를 최소화해야 하는 대량 생산품인 인테리어 가구나, 각 방에서 동일한 내장 디자인이 요구되는 오피스 빌딩 또는 맨션에서는, 천연 나무 소재의 베니어를 사용하면, 각각의 베니어 화장판에서 천연 나무가 가지고 있는 나뭇결무늬와 색상의 개성이 드러나 버려, 제품 간의 디자인 편차 또는 객실 마다 내장 디자인의 편차가 생겨 버린다.On the other hand, in an office building or a mansion where large-scale production of interior furniture that requires minimal variation in design between products and which requires the same interior design in each room, using natural wood veneer, The distinctive grain pattern and color personality are revealed, and there is a deviation of the design among the products or a deviation of the interior design of each room.
한편, 프린트 합판을 사용하면, 특정 모양으로 통일할 수 있기 때문에 제품 간의 디자인 편차, 또는 방마다 디자인의 편차를 해소할 수 있는 반면, 인공적인 인상이 강하고, 베니어 화장판을 사용하는 경우와 같은 천연 나무의 안정함과 따스함이 있는 나무 질감을 느낄 수 없다.On the other hand, when the printed plywood is used, it is possible to unify the product in a specific shape, so that the design deviation between the products or the deviation of the design in each room can be solved, while the artificial impression is strong. I can not feel the wood texture with warmth and stability.
본 발명은, 이상의 점을 감안하여 창안된 것으로, 제조 비용을 줄이면서, 천연 나무의 안정함과 온기 있는 나무 질감을 구비하고, 나뭇결무늬와 색상이 통일 된 베니어의 제조 방법, 베니어편, 베니어 및 베니어 화장재를 제공하는 것을 목적으로 한다.The present invention has been made in view of the above points, and it is an object of the present invention to provide a method of manufacturing a veneer having a stable natural wood and a warm wood texture and having a uniform grain pattern and color, It is intended to provide a veneer cosmetic.
상기의 목적을 달성하기 위하여, 본 발명의 베니어의 제조 방법은, 원목에서 소정 크기의 목재편을 제재하는 제재 공정과, 상기 목재편을 5mm ~ 30mm 폭으로 목취하여 목재소편을 형성하는 목취 공정과, 상기 목재소편의 나뭇결무늬가 소정 방향으로 갖추어 지도록, 복수의 상기 목재소편을 폭 방향으로 붙여서 집성재를 형성하는 집성 공정과, 상기 집성재의 접착면에 대략 직교시켜 0.15mm ~ 0.60mm 두께로 절단하는 절단 공정을 구비한다.In order to achieve the above object, a method of manufacturing a veneer according to the present invention includes: a manufacturing process for manufacturing a wooden piece having a predetermined size from a raw wood; a necking process for shaping the wooden piece to a width of 5 mm to 30 mm; A collecting step of forming a collecting material by adhering a plurality of the pieces of wood in a width direction so that the grain patterns of the pieces of wood are aligned in a predetermined direction; .
여기에서 목재편을 제재하는 제재 공정에 의해, 예를 들어 정목 제거, 또는 이음매 잡기 등으로 원목으로부터 목적에 맞는 크기의 목재편을 제재 할 수 있다.Here, it is possible to remove the wooden piece of the size suitable for the purpose from the log, for example, by the removal of the root, or by the joining process, by the process of manufacturing the wooden piece.
또한, 목재편이 5mm ~ 30mm 폭으로 목취 됨으로써 천연 나무가 갖는 개성적인 나뭇결무늬나 색상이 눈에 띄지 않고, 각 건조 목재소편의 나뭇결무늬와 색상 을 통일한 것으로 할 수 있다.In addition, since the wooden pieces are woven in a width of 5 mm to 30 mm, the unique wood grain patterns and colors of the natural wood are not conspicuous, and the grain patterns and colors of the respective dry wood pieces can be unified.
또한 목재소편의 폭은 최대 30mm의 세폭으로 절단되기 때문에, 그 과정에서 목재의 섬유도 세세하게 분단되어 있다. 따라서, 목재소편을 얇게 절단하여 베니어 을 제작해도, 베니어의 컬을 방지하기 때문에, 기존, 절삭 가공성을 높이기 위해 실시하는 목재소편의 자비 공정을 생략 할 수 있어, 제조 비용 을 줄일 수 있다.In addition, since the width of wood pieces is cut to a width of 30 mm at maximum, the wood fibers are finely divided in the process. Therefore, even if the veneer is manufactured by cutting the piece of wood thinly, the curling of the veneer can be prevented. Therefore, it is possible to omit the self-expense process of the piece of wood for the purpose of improving the cutting workability and reduce the manufacturing cost.
또한, 자비 공정을 생략함으로써, 기존, 자비 공정 후에 푸른 곰팡이의 발생 등을 방지하기 위해 행해지는 건조 공정을 생략할 수 있어, 제조 비용을 줄일 수 있다.Also, by omitting the mercury process, the drying process performed to prevent the occurrence of the blue mold after the conventional mercury process can be omitted, and the manufacturing cost can be reduced.
또한, 목재소편을 5mm 폭 보다 좁은 폭으로 목취하면, 나뭇결무늬가 나타나고 않고, 천연 나무의 안정성과 따뜻한 나무 질감을 느낄 수 없다. 한편, 목재소편을 30mm 폭 보다 넓게 목취하면, 천연 나무가 갖는 특징적인 나뭇결무늬와 색상이 눈에 띄고, 목재소편의 표면이 전체적으로 통일감이 없는 디자인인 된다.In addition, if a piece of wood is woven with a width narrower than 5mm width, the grain pattern does not appear, and the stability of the natural wood and the warm wood texture can not be felt. On the other hand, when wood pieces are wider than a width of 30 mm, the characteristic wood grain pattern and color of the natural wood are conspicuous, and the surface of the wood frame is unified in design as a whole.
또한 목취된 목재소편의 나뭇결무늬가 소정 방향으로 갖추어 지면, 복수의 목재소편을 폭 방향으로 집성시켜 집성재를 제작하는 집성 공정에 의해, 집성재의 폭 방향으로 통일된 나뭇결무늬를 연속하여 형성할 수 있다.In addition, when the wood grain pieces of the woodworking pieces are aligned in a predetermined direction, the wood grain pieces unified in the width direction of the gathering material can be continuously formed by the collecting step of collecting the plurality of pieces of wood in the width direction to produce the collecting material have.
또한, 5mm ~ 30mm 의 폭이 좁은 목재소편을 집성하여, 기존 폐기된 목재소편도 유효하게 활용할 수 있기 때문에, 원목의 수율을 높일 수 있다.In addition, it is possible to increase the yield of logwood because it is possible to effectively utilize one of the existing discarded wood products by collecting the narrow wood pieces with a width of 5 mm to 30 mm.
또한, 집성재의 접착면에 대략 직교하여 0.15mm ~ 0.60mm 두께로 절단하는 절단 공정에 의해, 폭 방향으로 연속한 나뭇결무늬가 형성된 베니어를 쉽게 제작할 수 있다.In addition, a veneer having a grain pattern continuous in the width direction can be easily manufactured by a cutting step of cutting the steel sheet to a thickness of 0.15 mm to 0.60 mm substantially perpendicular to the bonding surface of the binder.
또한, 베니어를 0.15mm 두께보다 얇게 절단하면, 베니어가 컬이 쉬움과 동시에, 베니어를 기재에 부착한 때, 베니어에서 기재의 나뭇결이 비쳐 보이기 때문에 보기에 손상된다. 또한, 기재와 베니어를 접착한 후에, 접착제가 베니어 표면에 침투해 버려, 베니어 표면에 도장을 한 때 얼룩 등의 원인이 된다.In addition, when the veneer is cut thinner than 0.15 mm in thickness, the veneer is easily curled, and when the veneer is attached to the base material, the grain of the base material is seen through the veneer and is damaged. Further, after the base material and the veneer are adhered, the adhesive penetrates the surface of the veneer, which may cause unevenness when the surface of the veneer is coated.
한편, 베니어를 0.60mm 두께보다 두껍게 하면 베니어의 함수율을 일정하게 유지하지 못하고, 환경, 및 기후 변화에 따른 베니어의 신축에 의한 균열, 변형 등이 발생하기 쉬워진다. 또한, 베니어를 커터 등으로 소정의 형상으로 가공 시 절삭 가공성도 악화된다.On the other hand, if the veneer is thicker than 0.60 mm in thickness, the water content of the veneer can not be kept constant, and cracks and deformation due to expansion and contraction of the veneer due to the environment and the climate change are likely to occur. In addition, when the veneer is cut into a predetermined shape with a cutter or the like, cutting workability is also deteriorated.
상기의 목적을 달성하기 위하여, 본 발명의 베니어의 제조 방법은, 원목으로부터 소정 크기의 목재편을 제재하는 제재 공정과, 상기 목재편을 소정 기간 건조하는 건조 공정과, 상기 목재편을 5mm ~ 30mm 폭으로 목취하여 목재소편을 형성하는 목취 공정과, 상기 목재소편의 나뭇결무늬가 소정 방향으로 갖추어 지면, 복수의 상기 목재소편을 폭 방향으로 붙여서 집성재를 형성하는 집성 공정과, 상기 집성재의 접착면에 대략 직교시켜 0.15mm ~ 0.60mm 두께로 절단하는 절단 공정을 구비한다.In order to achieve the above object, a method of manufacturing a veneer according to the present invention comprises: a step of manufacturing a wooden piece having a predetermined size from a raw wood; a drying step of drying the wooden piece for a predetermined period; A collecting step of collecting a plurality of the pieces of wood in a width direction to form a collecting material when the wood grain pieces are aligned in a predetermined direction; To a thickness of 0.15 mm to 0.60 mm.
여기에서, 목재편을 제재하는 제재 공정에 의해, 예를 들어 정목 제거, 또는 이음매 잡기 등으로 원목에서 목적에 맞는 크기의 목재편을 제재 할 수 있다.Here, it is possible to apply a wooden piece of a size suitable for a purpose in the wood by, for example, removing the wooden block or seaming by the process of manufacturing the wooden block.
또한, 목재편이 5mm ~ 30mm 폭으로 목취 됨으로써 천연 나무가 갖는 개성적인 나뭇결무늬나 색상이 눈에 띄지 않고, 각 건조 목재소편의 나뭇결무늬와 색상을 통일한 것으로 할 수 있다.In addition, since the wooden pieces are woven in a width of 5 mm to 30 mm, the unique wood grain patterns and colors of the natural wood are not conspicuous, and the grain patterns and colors of the respective dry wood pieces can be unified.
또한, 목재소편을 소정 기간 건조하는 건조 공정에 의해, 목재소편의 함수율 을 일정하게 하여, 푸른 곰팡이의 발생을 억제할 수 있다.In addition, it is possible to suppress the occurrence of blue mold by making the moisture content of the wood pieces constant by the drying step of drying the wood pieces for a predetermined period.
또한, 목재소편의 폭은 최대로 30mm의 세폭으로 절단되어 있기 때문에, 그 과정에서 목재의 섬유도 세세하게 분단되어 있다. 따라서 목재소편을 얇게 절단하여 베니어를 제작해도, 베니어의 컬을 방지하기 때문에, 기존, 절삭 가공성을 높이기 위해 실시하고 있던, 목재소편의 자비공정을 생략할 수 있어, 제조 비용을 줄일 수 있다.In addition, since the width of the wood pieces is cut to a maximum width of 30 mm, the wood fibers are finely divided in the process. Therefore, even if the veneer is manufactured by cutting the piece of the wood slice thinly, curling of the veneer is prevented, so that it is possible to omit the self-expense process of the piece of wood, which has been carried out in order to increase the cutting workability, and the manufacturing cost can be reduced.
또한, 자비 공정을 생략함으로써, 기존, 자비공정 후에 푸른 곰팡이의 발생 등을 방지하기 위해 행해졌든 건조 공정을 생략할 수 있어, 제조 비용을 억제할 수 있다.Also, by omitting the mercury process, it is possible to omit the drying process, which has been carried out in order to prevent the occurrence of blue mold after the mercury process, and thus the production cost can be suppressed.
또한, 목재소편을 5mm 폭 보다 좁은 폭으로 목취하면, 나뭇결무늬가 나타나지 않고, 천연 나무의 안정성과 따뜻한 나무 질감을 느낄 수 없다. 한편, 목재소편을 30mm 보다 넓은 폭으로 목취 하면, 천연 나무가 갖는 특징적인 나뭇결무늬와 색상이 눈에 띄고, 목재편의 표면이 전체적으로 통일감이 없는 디자인이 된다.In addition, if a piece of wood is woven with a width narrower than 5mm width, the grain pattern does not appear, and the stability of the natural wood and the warm wood texture can not be felt. On the other hand, when wood pieces are woven with a width greater than 30 mm, the characteristic wood grain pattern and color of natural wood are conspicuous, and the surface of the wooden piece becomes a design having unity in the whole.
또한, 목취된 목재소편의 나뭇결무늬가 소정 방향으로 갖추어 지면 복수의 목재소편을 폭 방향으로 집성하고 집성재를 제작하는 집성 공정에 의해, 집성재의 폭 방향으로 통일된 나뭇결무늬를 연속 하여 형성 할 수있다.In addition, if the wood grain pieces of the woodworked pieces are aligned in a predetermined direction, a wood grain pattern unified in the width direction of the gathering material can be continuously formed by an aggregation step of collecting a plurality of pieces of wood pieces in the width direction and producing a collective material have.
또한, 5mm ~ 30mm의 폭이 좁은 목재소편을 집성하여, 기존 폐기된 목재소편도 유효하게 활용할 수 있기 때문에, 원목의 수율을 높일 수 있다.In addition, it is possible to increase the yield of logwood because it is possible to effectively utilize one of the existing discarded wood products by collecting the narrow wood pieces with a width of 5 mm to 30 mm.
또한, 집성재의 접착면에 대략 직교되게 0.15mm ~ 0.60mm 두께로 절단하는 절단 공정에 의해, 폭 방향으로 연속한 나뭇결무늬가 형성된 베니어를 쉽게 제작할 수 있다.In addition, a veneer having a grain pattern continuous in the width direction can be easily manufactured by a cutting step of cutting the adhesive material to a thickness of approximately 0.15 mm to 0.60 mm substantially perpendicular to the adhesive surface.
또한, 베니어를 0.15mm 두께 보다 얇게 절단하면, 베니어에 컬이 생김과 동시에, 베니어를 기재에 부착한 때, 베니어에서 기재의 나뭇결이 비쳐 보이기 때문에 보기에 손해이다. 또한, 기재와 베니어를 접착한 후에 접착제가 베니어 표면에 침투해 버려, 베니어 표면에 도장을 한 때 얼룩 등의 원인이 된다.In addition, when the veneer is cut thinner than 0.15 mm in thickness, curling of the veneer is caused, and at the same time, when the veneer is attached to the base material, the grain of the base material is visible in the veneer. Further, after the base material and the veneer are adhered, the adhesive penetrates the surface of the veneer, resulting in unevenness when the surface of the veneer is coated.
한편, 베니어를 0.60mm 두께 보다 두껍게 하면 베니어의 함수율을 일정하게 유지하지 못하고, 환경, 및 기후 변화에 따른 베니어의 신축에 의한 균열, 변형 등이 발생하기 쉬워진다. 또한, 베니어를 커터 등으로 소정의 형상으로 가공 시 절삭 가공성도 악화된다.On the other hand, if the veneer is thicker than 0.60 mm in thickness, the water content of the veneer can not be kept constant, and cracks and deformation due to expansion and contraction of the veneer due to the environment and the climate change are likely to occur. In addition, when the veneer is cut into a predetermined shape with a cutter or the like, cutting workability is also deteriorated.
상기의 목적을 달성하기 위하여, 본 발명의 베니어편은, 표면이 소정 방향의 나뭇결무늬가 있고, 적어도 5mm ~ 30mm 폭, 또한 0.15mm ~ 0.60mm 두께로 형성되어 있다.In order to achieve the above object, the veneer piece of the present invention has a grain pattern with a surface in a predetermined direction, and is formed to have a width of at least 5 mm to 30 mm and a thickness of 0.15 mm to 0.60 mm.
여기서, 베니어편이 5mm ~ 30mm 폭으로 형성되어 있는 것으로, 천연 나무가 가진 개성인 나뭇결무늬와 색상이 눈에 띄지 않고, 베니어편의 나뭇결무늬와 색상을 통일 한 것으로 할 수 잇다.Here, the veneer pieces are formed to have a width of 5 mm to 30 mm, so that the wood grain patterns and colors of the natural woods are not conspicuous and the veneer pieces can be made uniform in grain pattern and color.
또한, 베니어편의 폭은 최대 30mm로 세폭 절단되어 있기 때문에, 그 과정에서 목재도 세세하게 분단되어 있다. 따라서, 베니어편을 얇은 두께로 형성하여도 베니어편의 컬을 방지하기 때문에, 기존, 목재소편에서 베니어편을 절삭할 때 절삭 가공성을 높이기 위해 행해진, 목재소편의 자비공정을 생략하는 것이 가능하여, 제조 비용을 줄일 수 있다.In addition, since the width of the veneer piece is cut to a maximum of 30 mm, the wood is also finely divided in the process. Therefore, since the curling of the veneer piece is prevented even when the veneer piece is formed to have a thin thickness, it is possible to omit the self-piercing process of the piece of wood, which has been carried out in order to increase the cutting workability when cutting the veneer piece from the existing wooden piece, .
또한, 자비 공정을 생략함으로써, 기존, 자비공정 후에 푸른 곰팡이의 발생 등을 방지하기 위해 행해지는 건조 공정을 생략할 수 있어 제조 비용을 억제할 수 있다.Further, by omitting the mercury process, it is possible to omit the drying process, which is carried out in order to prevent the occurrence of the blue mold after the mercury process, and thus the manufacturing cost can be suppressed.
또한, 베니어편을 5mm 폭 보다 좁은 폭으로 형성하면, 나뭇결무늬가 나타나고 않고, 천연 나무의 안정성과 따뜻한 나무 질감을 느낄 수 없다. 한편, 베니어편을 30mm 폭 보다 넓게 형성하면, 천연 나무가 갖는 특징적인 나뭇결무늬와 색상이 눈에 띄고, 목재소편의 표면이 전체적으로 통일감이 없는 디자인인 된다.Further, when the veneer pieces are formed to have a width narrower than the width of 5 mm, the grain pattern does not appear, and the stability of the natural wood and the warm wood texture can not be felt. On the other hand, when the veneer pieces are formed wider than the width of 30 mm, the characteristic wood grain patterns and colors of the natural wood are conspicuous, and the surfaces of the wood panel pieces are unified in design as a whole.
또한, 베니어편이 0.15mm ~ 0.60mm 두께의 얇은 두께로 절단되는 것으로, 이것을 기재에 부착했을 때의 베니어편의 모양을 개선하고, 베니어편의 함수율을 일정하게 유지할 수 있어, 환경, 및 기후 변화에 따른 베니어편의 신축에 의한 균열, 변형 등을 방지할 수 있다.In addition, since the veneer pieces are cut to a thin thickness of 0.15 mm to 0.60 mm in thickness, it is possible to improve the appearance of the veneer pieces when they are attached to the base material, to maintain the moisture content of veneer pieces constant, It is possible to prevent cracks, deformation, and the like due to expansion and contraction of the sides.
또한, 베니어편을 0.15mm 두께 보다 얇게 절단하면 베니어편의 컬이 쉽게됨과 동시에, 베니어편을 기재에 부착한 때 베니어편에서 기재의 나뭇결이 비쳐 보이기 때문에 볼품이 손상된다. 또한, 기재와 베니어편을 접착한 후 접착제가 베니어편 표면에 침투하여, 베니어편 표면에 도장을 한 때 얼룩 등의 원인이 된다.In addition, when the veneer pieces are cut to a thickness smaller than 0.15 mm, the curling of the veneer pieces is facilitated and the grain of the base material is visually seen from the veneer pieces when the veneer pieces are attached to the base material. Further, after the base material and the veneer piece are bonded, the adhesive penetrates the surface of the veneer piece, and when the surface of the veneer piece is coated, it becomes a cause of unevenness and the like.
한편, 베니어편을 0.60mm 두께 보다 두껍게 하면 베니어편의 함수율을 일정하게 유지할 수 있어, 환경, 및 기후 변화에 따른 베니어 조각의 신축에 의한 균열, 변형등이 발생하기 쉬워진다. 또한, 베니어편을 커터 등으로 소정의 형상으로 가공 시 절삭 가공성도 악화된다.On the other hand, if the veneer pieces are thicker than 0.60 mm in thickness, the moisture content of the veneer pieces can be kept constant, and cracks and deformation due to expansion and contraction of the veneer pieces due to environmental and climate changes are likely to occur. In addition, when the veneer pieces are processed into a predetermined shape with a cutter or the like, cutting workability is also deteriorated.
또한, 베니어편의 표면이 곧은 경우에는 심플하고 모던한 인상을 줄 수 있으며, 엇결에 비해 목재의 섬유 방향이 일정한 방향으로 갖추어 지기 때문에, 베니어편의 왜곡 이 적고, 베니어편의 가공성이 향상된다.In addition, when the surface of the veneer piece is straight, it can give a simple and modern impression, and since the fiber direction of the wood is arranged in a certain direction as compared with the veneer piece, distortion of the veneer piece is small and workability of the veneer piece is improved.
상기의 목적을 달성하기 위하여, 본 발명의 베니어는, 표면이 소정 방향으로 나뭇결무늬가 있고, 1편이 적어도 5mm ~ 30mm 폭, 또한 0.15mm ~ 0.60mm 두께의 복수의 베니어편이 폭 방향으로 배열 되어 있다.In order to achieve the above object, a veneer of the present invention has a plurality of veneer pieces each having a grain pattern in a predetermined direction, one side having a width of at least 5 mm to 30 mm and a thickness of 0.15 mm to 0.60 mm, .
여기서, 베니어를 구성하는 각 베니어편이 5mm ~ 30mm 폭으로 형성되어 있는 것으로, 천연 나무가 갖는 개성적인 나뭇결무늬와 색상이 눈에 띄지 않고, 베니어의 나뭇결무늬와 색상을 통일 한 것으로 할 수 있다.Here, each veneer constituting the veneer is formed to have a width of 5 mm to 30 mm, so that the unique wood grain pattern and color of the natural wood are not conspicuous and the wood grain pattern and color of the veneer can be unified.
또한, 베니어를 구성하는 각 베니어편의 폭은 최대 30mm로 세폭 절단되어 있기 때문에, 그 과정에서 목재의 섬유도 세세하게 분단되어 있다. 따라서, 베니어를 얇은 두께로 형성하여도, 베니어판의 컬을 방지하기 때문에, 기존, 목재소편에서 베니어편을 절삭할 때 절삭 가공성을 높이기 위해 행해지는 자비공정을 생략할 수 있어, 제조 비용을 억제할 수 있다.Further, since the width of each veneer constituting the veneer is cut to a maximum of 30 mm, the fibers of the wood are finely divided in the process. Therefore, even when the veneer is formed to have a thin thickness, the curling of the veneer can be prevented. Therefore, it is possible to omit the complicated process for increasing the cutting workability when cutting the veneer piece from the wooden piece, .
또한, 자비 공정을 생략함으로써, 기존, 자비공정 후에 푸른 곰팡이의 발생 등을 방지하기 위해 행해지는 건조 공정을 생략할 수 있어, 제조 비용을 줄일 수 있다.Also, by omitting the mercury process, the drying process performed to prevent the occurrence of the blue mold after the conventional mercury process can be omitted, and the manufacturing cost can be reduced.
또한, 베니어를 구성하는 각 베니어편을 5mm 폭 보다 좁은 폭으로 형성하면 나뭇결무늬가 나타나지 않고, 천연 나무의 안정성과 따뜻한 나무 질감을 느낄 수 없다. 한편, 각 베니어편을 30mm 폭보다 넓은 폭으로 형성하면, 천연 나무가 갖는 특징적인 나뭇결무늬와 색상이 눈에 띄기 때문에, 베니어가 전체적으로 통일감이 없는 디자인이 된다.Further, if each veneer constituting the veneer is formed to have a narrower width than a width of 5 mm, no grain pattern appears, and the stability of the natural wood and the warm wood texture can not be felt. On the other hand, when each veneer piece is formed to have a width larger than a width of 30 mm, the distinctive grain pattern and color of the natural wood are conspicuous, so that the veneer becomes a design having no unity over the whole.
또한, 베니어를 구성하는 각 베니어편이 0.15mm ~ 0.60mm 두께의 얇은 두께 로 절단된 것으로, 이를 기재에 부착했을 때의 베니어의 모양을 개선하고, 베니어의 함수율을 일정하게 유지할 수 있어, 환경, 및 기후 변화에 따른 베니어의 신축에 의한 균열, 휘어짐 등을 방지 할 수 있다.Further, each of the veneer pieces constituting the veneer is cut into a thin thickness of 0.15 mm to 0.60 mm in thickness, which improves the appearance of the veneer when it is attached to the base material and maintains the water content of the veneer constant, It is possible to prevent cracking and warping due to expansion and contraction of veneer due to climate change.
또한, 베니어를 0.15mm 두께 보다 얇게 절단하면 베니어에 컬이 쉽게 생김과 동시에, 베니어를 기재에 부착한 때 베니어에서 기재의 나뭇결이 비쳐 보이기 때문에 보기에 손해다. 또한, 기재와 베니어를 접착한 후 접착제가 베니어 표면에 침투해 버려, 베니어 표면에 도장을 한 때 얼룩 등의 원인이 된다.In addition, if the veneer is cut thinner than 0.15mm in thickness, curling of the veneer is easy, and at the same time, when the veneer is attached to the base material, the grain of the base material is visibly seen from the veneer. Further, after the base material and the veneer are bonded, the adhesive penetrates the surface of the veneer, which may cause unevenness when the surface of the veneer is coated.
한편, 베니어를 0.60mm 두께 보다 두껍게 하면 베니어의 함수율을 일정하게 유지하지 못하고, 환경, 및 기후 변화에 따른 베니어의 신축에 의한 균열, 변형 등이 발생하기 쉬워진다. 또한, 베니어를 커터 등으로 소정의 형상으로 가공 시 절삭 가공성도 악화된다.On the other hand, if the veneer is thicker than 0.60 mm in thickness, the water content of the veneer can not be kept constant, and cracks and deformation due to expansion and contraction of the veneer due to the environment and the climate change are likely to occur. In addition, when the veneer is cut into a predetermined shape with a cutter or the like, cutting workability is also deteriorated.
상기의 목적을 달성하기 위하여, 본 발명의 베니어 화장판은, 표면이 소정 방향의 나뭇결무늬를 유지하고, 1 조각이 적어도 5mm ~ 30mm의 폭, 또한 0.15mm ~ 0.60mm 두께의 복수의 베니어편이 폭 방향으로 배열된 베니어를 기재에 접합 되어 있다.In order to achieve the above object, the veneer sheet of the present invention is characterized in that the surface of the veneer sheet has a grain pattern in a predetermined direction, and one piece has a width of at least 5 mm to 30 mm and a plurality of veneer pieces having a width of 0.15 mm to 0.60 mm And the veneer arranged in the direction of the base is joined to the base.
여기에서, 각 베니어편이 5mm ~ 30mm 폭으로 형성되어 있는 것으로, 천연 나무가 가진 개성적 나뭇결무늬와 색상이 눈에 띄지 않고, 이러한 베니어편을 기재에 붙여서 형성 한 베니어 화장판의 나뭇결무늬와 색상을 통일한 것으로 할 수있다.Here, each veneer piece is formed to have a width of 5 mm to 30 mm, and the wood grain pattern and color of the veneer veneer formed by attaching such a veneer piece to the substrate are unified Can be made.
또한, 각 베니어편의 폭은 최대 30mm로 세폭 절단되어 있기 때문에, 그 과정에서 목재의 섬유도 세세하게 분단되어 있다. 따라서, 베니어편 또는 베니어를 얇은 두께로 형성하여도 베니어의 컬을 방지하기 때문에 기존 절삭 가공성을 높이기 위해 행해진 목재소편의 자비공정을 생략하는 것이 가능하여, 제조 비용을 줄일 수 있다.In addition, since the width of each veneer piece is cut to a maximum of 30 mm, the fibers of the wood are finely divided in the process. Therefore, even if the veneer piece or the veneer is formed to have a thin thickness, curling of the veneer can be prevented, so that it is possible to omit the self-piercing process of the piece of wood made to increase the cutting workability, and the manufacturing cost can be reduced.
또한, 자비 공정을 생략함으로써, 기존, 자비공정 후에 푸른 곰팡이의 발생 등을 방지하기 위해 행해진 건조 공정을 생략할 수 있어 제조 비용을 줄일 수 있다.Further, by omitting the mercury process, the drying process performed to prevent the occurrence of blue mold after the conventional mercury process can be omitted, and the manufacturing cost can be reduced.
또한, 베니어를 구성하는 각 베니어편을 5mm 폭 보다 좁은 폭으로 형성하면 나뭇결무늬가 나타나 않고 천연 나무의 안정성과 따뜻한 나무 질감을 느낄 수 없다. 한편, 각 베니어편을 30mm 폭보다 넓은 폭으로 형성하면 천연 나무가 갖는 특징적인 나뭇결무늬와 색상이 눈에 띄기 때문에, 베니어가 전체적으로 통일감이 없는 디자인이 된다.Further, when each veneer constituting the veneer is formed to have a narrower width than the width of 5 mm, the grain pattern does not appear and the stability of the natural wood and the warm wood texture can not be felt. On the other hand, if each veneer piece is formed to have a width greater than 30 mm wide, the characteristic wood grain pattern and color of the natural wood are conspicuous, so that the veneer has a unified design as a whole.
또한, 각 베니어편이 0.15mm ~ 0.60mm 두께의 얇은 두께로 절단되는 것으로, 이를 기재에 부착했을 때의 베니어의 모양을 개선하고, 베니어의 함수율을 일정하게 유지 할 수 있어, 환경, 및 기후 변화에 따른 베니어의 신축에 의한 균열, 변형 등을 방지하기 수 있다.Further, since each veneer piece is cut into a thin thickness of 0.15 mm to 0.60 mm in thickness, it is possible to improve the shape of the veneer when it is attached to the base material, maintain the water content of the veneer constant, It is possible to prevent cracking, deformation, and the like caused by expansion and contraction of the veneer.
또한, 베니어를 0.15mm 두께 보다 얇게 절단하면 베니어가 컬이 생김과 동시에, 베니어를 기재에 부착한 때, 베니어에서 기재의 나뭇결이 비쳐 보이기 때문에 보기에 손해다. 또한 기재와 베니어를 접착한 후 접착제가 베니어 표면에 침투해 버려, 베니어 표면에 도장을 한 때 얼룩 등의 원인이 된다.In addition, when the veneer is cut thinner than 0.15 mm in thickness, the veneer is curled and, at the same time, when the veneer is attached to the base material, the grain of the base material is visibly seen from the veneer. Furthermore, after the base material and the veneer are adhered, the adhesive penetrates the surface of the veneer, which may cause unevenness when the surface of the veneer is coated.
한편, 베니어를 0.60mm 두께 보다 두껍게 하면 베니어의 함수율을 일정하게 유지하지 못하고, 환경, 및 기후 변화에 따른 베니어의 신축에 의한 균열, 변형 등이 발생하기 쉬워진다. 또한, 베니어를 커터 등으로 소정의 형상으로 가공 시 절삭 가공성도 악화된다.On the other hand, if the veneer is thicker than 0.60 mm in thickness, the water content of the veneer can not be kept constant, and cracks and deformation due to expansion and contraction of the veneer due to the environment and the climate change are likely to occur. In addition, when the veneer is cut into a predetermined shape with a cutter or the like, cutting workability is also deteriorated.
본 발명에 따른 베니어의 제조 방법, 베니어편, 베니어 및 베니어 화장재는 제조 비용을 억제 하고, 천연 나무의 안정성 있는 나무 질감을 구비하고, 나뭇결무늬와 색상을 통일 한 것으로 할 수 있다.The method for manufacturing a veneer, the veneer piece, the veneer, and the veneer cosmetic material according to the present invention can suppress the manufacturing cost, provide a stable wood texture of natural wood, and unify the grain pattern and color.
도 1은 본 발명의 실시 예에 따른 베니어 화장판의 사시도이다.
도 2는 본 발명에 따른 베니어의 제조 방법을 나타내는 도면이다.
도 3은 종래 기술에 따른 베니어의 제조 방법을 도시 한 블록도이다.1 is a perspective view of a veneer board according to an embodiment of the present invention.
2 is a view showing a method of manufacturing a veneer according to the present invention.
3 is a block diagram illustrating a method of manufacturing a veneer according to the prior art.
이하, 베니어의 제조 방법, 베니어편, 베니어 및 베니어 화장판에 관한 본 발명의 실시 예에 대해서, 도면을 참조하면서 설명하고, 본 발명의 이해에 제공한다.Hereinafter, embodiments of the present invention relating to a veneer manufacturing method, a veneer piece, a veneer and a veneer plate will be described with reference to the drawings, and are provided for an understanding of the present invention.
먼저, 도 1 은 본 발명에 따른 제조 방법에 의해 제조 한 베니어(1)을, 기재(3)의 표면에 붙여 마련한 베니어 화장판(2)의 사시도이다.First, FIG. 1 is a perspective view of a
기재(3), 예를 들어, 합판, 섬유판, 파티클 보드, 불연 보드 등이며, 소정 의 크기의 약 사각형상의 평판 형상으로 형성 되어 있다.The
베니어 화장판(2)은, 천연 나무로 노송 나무의 집성재를 얇게 절단한 것이며, 5mm ~30mm 폭의 베니어편(1a)이 폭 방향으로 복수 배열된 베니어(1)가 기재(2) 에 부착되어 있다. 베니어(1)은 그 두께에 따라 주로 얇은 베니어와 두꺼운 베니어로 분류되지만, 본 발명에 사용되는 베니어(1)의 두께는 0.15mm ~ 0.60mm 이다.The
여기서, 반드시, 천연 나무는 노송 나무가 아니라, 삼나무, 나라, 월넛 등 천연 나무를 사용 해도 좋다.Here, natural wood is not cypress, natural wood such as cedar, country, walnut may be used.
다음으로, 본 발명에 따른 베니어의 제조 공정에 대하여, 도 2를 이용하여 설명한다.Next, a manufacturing process of a veneer according to the present invention will be described with reference to FIG.
< 1. 목재 공정 ><1. Wood process>
입목을 베어 쓰러트린 원목(4)으로부터, 목적으로 하는 나뭇결의 베니어(1)가 되도록 제재를 실시한다. 나뭇결은, 연륜이 세로 줄무늬 모양으로 나타나는 정목과, 연륜이 산 형상과 물결 모양의 무늬로 나타나는 반목으로 크게 분류되지만, 본 발명에서는 정목을 갖는 목재편(5)을 자르는 정목 잡기로 제재한다. 정목 잡기 는, 도 2(a)에 나타낸 바와 같이, 원목 4의 연륜과 직교하는 길이 방향(원목(4)생육 방향)에, 1 편이 소정의 세폭이 되도록 잘라 목재편(5)을 얻는다.From the raw wood (4) that has been knocked down, it is made to be a veneer (1) of the desired grain. The wood grain is largely classified into a rootstock having a ring-shaped longitudinal stripes and a ring-shaped ring-shaped rootstock and a wavy pattern. In the present invention, the
여기서, 반드시, 정목 잡기에 제재하는 방법은, 원목(4)의 연륜과 직교하는 길이 방향으로 소정 폭으로 절단할 필요는 없다. 예를 들어, 공지된 방법으로 원목(4)의 길이 방향으로 십자로 4 등분 잘라, 그 하나를 바깥, 좌우, 심측을 절단하도록 목재편(5)을 제재해도 좋다. 단, 원목(4)의 연륜과 직교하는 길이 방향으로 1 편이 소정의 세폭이 되도록 절단하여, 원목(4)이 소경도 쉽게 정목 잡기에 제재하는 것이 가능해진다. 그 때문에, 종래, 정목 잡기에 제재 하려면 충분히 생육 한 대경목의 원목을 사용하고 있었지만, 소경 나무의 원목이라도 정목 잡기에 제재하는 것이 가능하기 때문에 자원을 활용 할 수 있다.Here, it is not always necessary to cut a predetermined width in the lengthwise direction orthogonal to the
또한, 반드시, 정목을 갖는 목재편(5)를 자르는 정목 잡기에 제재할 필요는 없다.In addition, it is not always necessary to apply the
예를 들어, 정목을 갖는 목재편을 절단하는 정목 잡기에 제재하여도 좋다. 단, 정목 잡기에 제재하는 것으로, 정목을 갖는 베니어, 및 베니어 화장판을 얻을 수 있다. 즉, 정목에 비례하여 목재의 섬유 방향이 일정한 방향으로 갖추어 지기 때문에, 베니어편의 왜곡이 적고, 베니어편의 가공성이 향상된다. 또한, 정목을 갖는 베니어, 및 베니어 화장재를 사용한 인테리어 가구, 및 방 인테리어 디자인은, 심플하고 모던한 인상을 줄 수 있으며, 의장적인 효과가 높아진다.For example, it is also possible to apply a wooden piece for cutting a wooden piece having a root. However, it is possible to obtain a veneer and a veneer board having a beech wood by performing the squeezing process. In other words, since the fiber direction of the wood is aligned in a predetermined direction in proportion to the natural wood, the distortion of the veneer piece is small and the workability of the veneer piece is improved. In addition, the interior furniture and the interior design using veneer and veneer cosmetic material having a natural wood can give a simple and modern impression, and the design effect is enhanced.
< 2. 건조 공정 ><2. Drying process>
제재 공정에서 얻은 목재편(5)은, 자연 건조, 또는 열풍 등을 이용하여 인공 건조하고, 목재편(5)이 일정한 함수율이 될 때까지 건조시킨다. 건조 기간은 사용하는 천연 나무의 종류, 용도, 및 시기에 따라 변동하지만, 자연 건조의 경우 약 1 개월 ~ 3 개월의 기간을 기준으로 한다.The
< 3. 목취 공정 ><3. Stitching process>
건조 공정에서 건조시켜, 일정한 함수율이 된 목재편(5)은, 그림 2 ( b ) 와 같이 폭(W) 5mm ~ 30mm, 길이(L) 1.8m ~ 4.0m, 두께( T )가 임의의 목재소편(6)에 목취한다. 또한, 본 발명에서 사용하는 목재서편(6)의 폭은 5mm ~ 30mm 이며, 특히, 5mm ~ 15mm가 더 바람직하다.The
즉, 천연 나무는, 그 나뭇결무늬와 색상이 나무의 종류와 생육 환경 등에 따라 크게 다르지만, 예를 들어, 목재편(5)의 폭을 소정 이상의 폭으로 목취 하면, 천연 나무가 갖는 개성적인 나뭇결무늬와 색상이 눈에 띄게 된다. 따라서, 이와 같이 목취 된 목재편을 절단 한 베니어를 베니어 화장판으로 하여 인테리어 가구, 및 객실 내외장으로 사용하면, 제품 간에 모양이나 색상에 편차가 생겨 버린다.For example, when the width of the
여기에서, 5mm ~ 50mm 폭의 범위 내에서 5mm 마다 폭을 변화시킨 베니어편(1a)을 준비하고, 이러한 베니어편(1a)을 폭 방향으로 복수(예를 들면 5 장) 배열 한 베니어(1)에 대하여 20명의 패널리스트에 대해 "좋은" "보통" "나쁜"의 3 단계에서의 의장성 평가를 한 결과를 표 1에 나타낸다.Here, a
또한, 여기서의 의장성이 '좋은'은, 패널리스트의 외관 재량에 따라 같은 폭 의 베니어편(1a)을 폭 방향으로 복수 배열한 경우에, 천연 나무가 갖는 특징적인 나뭇결무늬와 색상이 눈에 띄지 않고, 베니어(1)가 전체적으로 통일감 있는 디자인인 것을 말하며, 의장성이 "나쁜" 것은, 천연 나무가 가지는 특징적인 나뭇결무늬와 색상이 눈에 띄고, 베니어(1)가 전체적으로 통일감이 없는 디자인인 것을 말한다.In the case where the
표 1과 같이, 베니어편(1a)이 30mm 폭보다 넓게 되면, 의장성이 "나쁜" 것으로 느낀 패널이 많고, 천연 나무의 가지 나뭇결무늬와 색상이 눈에 띄기 시작하는 것으로 이해할 수 있다.As shown in Table 1, when the
한편, 베니어편(1a)이 30mm 폭 이하로 되면, 의장성이 "나쁜" 것으로 대답 하는 패널은 없어져, 특히 5mm ~ 15mm로 한 경우에는 천연 나무가 갖는 개성적인 나뭇결무늬나 색조가 억제되어 통일감 있는 디자인이 되는 것을 확인할 수 있었다.On the other hand, when the
< 4. 집성 공정 ><Aggregation Process>
목취 공정에서 목취 한 목재편(6)은, 도 2 (c)에 나타낸 바와 같이, 그 내측에 접착제를 도포하여, 폭 방향으로 소정 매수(도면에서는 5 장)을 붙여서 적층하고, 집성재(7)을 형성한다.As shown in Fig. 2 (c), the
여기서 반드시 목재편(6)의 적층 매수는 5 장 일 필요는 없다. 완제품인 베니어 화장판(2)의 폭에 맞게 적층하는 목재편(6)의 매수는 적절하게 선택될 수 있다.Here, the number of
< 5. 절삭 공정 ><5. Cutting process>
집성 공정에서 형성 한 집성재(7)는, 도 2(d)에 나타낸 바와 같이, 슬라이스 기계 등의 절삭기를 이용하여, 집성재(7)의 접합 면과 대략 직교하는 방향으로 0.15mm ~ 0.60mm 두께로 얇게 절삭하여, 도 2(e) 에 나타낸 베니어(1) 을 얻는다.As shown in Fig. 2 (d), the
여기에, 기존의 베니어의 제조 공정에서, 목재편을 얇게 절단하면 베니어가 말려 버리는 문제가 있었다. 따라서 절삭 전에 목취한 목재편을 끓여 목재편에 수분을 포함 시켜 일정한 부드러움이 생기면 절삭면을 절단했다.In the conventional manufacturing process of the veneer, there is a problem that the veneer is curled when the wood piece is cut to a small thickness. Therefore, the wood pieces that had been chopped before cutting were boiled, and the cutting surface was cut when the softness of the wood part was included by including water.
이 점, 본 발명에 따른 목재소편(6)은, 상술 한 바와 같이, 그 폭이 5mm ~ 30mm 의 내용폭으로 절단되어 있기 때문에, 그 과정에서 목재소편(6)의 섬유도 분단된다. 따라서, 자비 공정을 거치지 않아도 얇은 두께로 절단 한 베니어(1)의 컬을 방지 할 수 있다.In this respect, since the
또한, 베니어 두께는 가능한 한 얇은 것이, 함수율을 일정하게 유지할 수 있기 때문에, 환경, 및 미세 기후 변화에 따른 베니어의 신축에 의한 균열, 변형 등을 방지할 수 있다. 한편, 베니어 두께를 얇게 하면 베니어(1)가 말리기 쉽고, 후술하는 붙여 넣기 공정에서 베니어(1)가 기재(3)에 붙여 베니어 화장판(2)을 형성할 때의 작업 효율이 악화된다.Further, the veneer thickness is as thin as possible, and the water content can be kept constant, so that it is possible to prevent cracks, deformation, and the like caused by expansion and contraction of the veneer due to environment and micro climate change. On the other hand, if the thickness of the veneer is made thinner, the
그래서, 5mm ~ 35mm 폭의 범위 내에서 5mm 마다 폭을 변화시킨 목재소편(6)을 준비하고, 각 폭의 목재소편(6)을, 함수율을 비교적 일정하게 유지하는 것이 가능한 0.10mm ~ 0.60mm 두께의 범위에서 절단했을 때의, 베니어편(1a)의 컬의 유무를 확인한 결과를 표 2에 나타낸다.Thus, the
표 2에 나타낸 바와 같이, 상술한 의장적인 효과가 높아진다. 5mm ~ 30mm 폭의 범위에서는, 30mm 폭, 0.10mm 두께의 베니어판(1a)에서 컬 현상이 확인되었다. 또한, 베니어편(1a)이 35mm 폭 되면, 목재의 섬유가 분단되지 않고 남아 있기 때문에, 절삭 두께가 0.10mm ~ 0.20mm 두께의 범위에서 컬 현상이 확인되었다. 이 컬 현상은 목재편(6)을 여러 집성 한 집성재(7)을 절단한 경우에도 비슷한 범위에서 확인할 수 있었다. 한편, 기타의 경우에는 베니어편(1a) 및 베니어(1)의 컬은 확인할 수 없었다.As shown in Table 2, the above-mentioned decorative effect is enhanced. In the range of 5 mm to 30 mm width, a curling phenomenon was confirmed in the
따라서, 의장적인 효과가 높아진다. 5mm ~ 30mm 폭의 베니어편(1a)에서는 0.15mm ~ 0.60mm 두께로 절단하면, 이러한 베니어편(1a)을 폭 방향으로 배열 한 베니어(1)는 컬 없이, 베니어(1)를 기재(3)에 붙여 베니어 화장판(2)을 제작할 때의 작업 효율을 높일 수 있다.Therefore, the design effect is enhanced. The
즉, 베니어편(1a)이 5mm ~ 30mm 폭 이면서, 0.15mm ~ 0.60mm 두께의 경우 에는, 천연 나무가 갖는 개성적인 나뭇결무늬와 색상이 억제되어, 이 베니어편(1a) 을 폭 방향으로 배열 한 베니어(1)의 디자인이 통일될 수 있으며, 함수율을 일정하게 유지하면서, 환경, 및 기후 변화에 따른 베니어(1)의 신축에 의한 균열, 변형 등을 방지할 수 있다. 또한 베니어(1)에 컬이 없기 때문에, 기재(3)에 베니어(1) 을 붙여 베니어 화장판(2)를 제작할 때의 작업성도 향상된다.That is, when the
< 6. 붙여 넣기 공정 ><6. Paste Process>
상술 한 바와 같이, 0.15mm ~ 0.60mm 두께로 절단 한 베니어(1)는, 도 2(f)에 나타난 바와 같이, 예를 들어 합판 등으로 구성된 기재(3)에 붙여 면에 접착제 를 도포하여 기재 표면(8)에 붙여진다. 이렇게 제작된 베니어 화장판(2)의 표면은, 폭 방향으로 정목이 연속적으로 형성된, 무구재로 마무리 된다.As shown in Fig. 2 (f), the
또한, 각 베니어 화장판(2)의 나뭇결무늬 및 색상이 통일되어 있기 때문에, 이 베니어 화장판(2)을 인테리어 가구와 사무실 건물, 또는 맨션의 내장 자재로 사용하는 경우에, 천연 나무의 안정성 있고 따뜻한 나무 질감을 제공하면서, 천연 나무의 가지는 개성적인 나뭇결무늬와 색상이 눈에 띄지 않고, 각 제품의 디자인의 편차 또는 각 방 인테리어 디자인의 편차를 억제해, 통일된 디자인으로 할 수 있다.Further, since the
이상과 같이 본 발명을 적용한 베니어의 제조 방법, 베니어편, 베니어 및 베니어 화장재는 제조 비용을 줄이면서, 천연 나무의 안정성과 따뜻한 나무 질감을 갖춘 나뭇결무늬와 색상를 통일할 수 있는 것으로 되어 있다.As described above, the manufacturing method, the veneer piece, the veneer, and the veneer cosmetic material to which the present invention is applied are capable of unifying the grain pattern and color having the stability of the natural wood and the warm wood texture while reducing the manufacturing cost.
1 : 베니어
1a : 베니어편
2 : 베니어 화장판
3 : 기재
4 : 원목
5 : 목재편
6 : 목재소편
7 : 집성재
8 : 기재 표면1: veneer
1a: Veneer piece
2: veneer veneer
3: substrate
4: Wood
5: wooden piece
6: Woodwork
7: laminated wood
8: substrate surface
Claims (6)
상기 목재편을 5mm ~ 30mm 폭으로 목취하여 목재소편을 형성하는 목취 공정과,
상기 목재소편의 나뭇결무늬가 소정 방향으로 갖추어 지도록, 복수의 상기 목재소편을 폭 방향으로 붙여 집성재를 형성하는 집성 공정과,
상기 집성재의 접착 면에 직교시켜 0.15mm ~ 0.60mm 두께로 절단하는 절단 공정을 구비하는 베니어의 제조 방법.A material processing step of cutting a predetermined size of wood pieces from the wood,
A necking process for chopping the wooden piece with a width of 5 mm to 30 mm to form a piece of wood,
An aggregating step of forming a laminated material by pasting a plurality of the pieces of wood in a width direction so that grain patterns of the pieces of wood are aligned in a predetermined direction,
And a cutting step of cutting at a thickness of 0.15 mm to 0.60 mm orthogonally to the bonding surface of the builder.
상기 목재편을 소정 기간 건조하는 건조 공정과,
상기 목재편을 5mm ~ 30mm 폭으로 목취시켜 목재소편을 형성하는 목취 공정과,
상기 목재소편의 나뭇결무늬가 소정 방향으로 갖추어 지고, 복수의 상기 목재소편을 폭 방향으로 겹쳐서 붙여 집성재를 형성하는 집성 공정과,
상기 집성재의 접착면에 직교시켜 0.15mm ~ 0.60mm 두께로 절단하는 절단 공정을 구비하는 베니어의 제조 방법.A material processing step of cutting a predetermined size of wood pieces from the wood,
A drying step of drying the wood piece for a predetermined period,
A necking step of chopping the wooden piece with a width of 5 mm to 30 mm to form a piece of wood,
An aggregating step of forming a laminated material by arranging a plurality of the wood pieces in a widthwise direction and stacking the wood pieces in a predetermined direction,
And a cutting step of cutting at a thickness of 0.15 mm to 0.60 mm orthogonally to the bonding surface of the builder.
상기 표면은 정목을 갖는 베니어편.The method of claim 3,
Wherein the surface is a veneer.