CN107234685A - Energy saving and environment friendly pure solid wood is without the thick core multi-layered board normal temperature pressing process of deformation - Google Patents
Energy saving and environment friendly pure solid wood is without the thick core multi-layered board normal temperature pressing process of deformation Download PDFInfo
- Publication number
- CN107234685A CN107234685A CN201710629938.3A CN201710629938A CN107234685A CN 107234685 A CN107234685 A CN 107234685A CN 201710629938 A CN201710629938 A CN 201710629938A CN 107234685 A CN107234685 A CN 107234685A
- Authority
- CN
- China
- Prior art keywords
- veneer
- blade
- disrumpent feelings
- deformation
- solid wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to energy saving and environment friendly pure solid wood without the thick core multi-layered board normal temperature pressing process of deformation, it is characterised by：Rounding is machined to the thick veneers of 3 5mm；Dry to aqueous uniform；Using the from top to bottom vertical punching press veneer of disrumpent feelings blade, the blade of blade is vertical with the grain direction of veneer, makes the growth fiber of the veneer after punching press disrumpent feelings；Scar knot dise knife correspondence will be gone to be positioned at the scar node of veneer surface, from top to bottom the scar knot punching press on veneer is removed using pressed sheet, falls to refill patch at hole in former scar knot afterwards；Compound one side is needed uniformly to coat glue-line in veneer；Veneer after gluing is carried out into interlayer to be combined, cold moudling after being combined.The present invention saves the energy, and nontoxic non-hazardous is environment friendly and pollution-free.Greatly improve the flatness of finished product sheet material.The resistance to deformation and flatness of finished product sheet material are ensured, sheet material wood effect, outward appearance class and application is improved.
Description
Technical field
It is particularly a kind of with the indeformable pure solid wood board of energy-conserving and environment-protective the present invention relates to a kind of plate processing technology
Normal temperature pressing process, belongs to plate processing technology technical field.
Background technology
At this stage, high-grade house ornamentation furniture solid wood composite board industry is very good in current market demand situation, especially
For the solid wood board of environment-friendly type, no matter domestic market or international market demand it is more powerful.
Traditional multi-layer solid wood sheet material has that technique is difficult to control to, wood effect is undesirable, yielding warpage, opened at present
Split, seriously polluted, inadequate environmental protection and energy saving, the technical barrier of Carving Machining can not be carried out on the basis of sheet material.
Conventional multilayer solid wood board is the veneer that log is first processed into 1-3mm or so, then by veneer by drying, applying
Glue, splice and combine, the process such as hot-forming is prepared from, and there is following main technological deficiency using such a technique：
1st, the veneer thickness used by this composite board is relatively thin, required when producing the composite board of same thickness
Veneer the number of plies it is also more, the glue-line quantity between veneer also just increases therewith, and which results in glue-line and glue consumption
Increase, finally increase the burst size of methanal of finished product sheet material, harm to the human body greatly, while take glue expense manually also result in into
This increase.
2nd, conventional drying processes are mainly based on Exposure to Sunlight and natural air drying, this mode the containing for sheet material for removing moisture
The equilibrium degree of water rate is difficult to control to, and dries naturally and there is the bad problems such as percentage of damage is high, sheet deformation is big, error is big.
3rd, it is main in splicing and combining that seamed split is spelled by Three kinds of hors d'oeuvres four using by multiple veneers, between layers according to list
Plate texture is combined by the way of crisscross, and this connecting method is easily caused spliced whole veneer and there is thickness
Inconsistent the problem of, it is combined again in this case, thickness difference of the whole sheet material after Multi-stacking compaction at each position
Amplification is accumulated by, the finished product density ultimately resulted in after being combined is uneven, and variable thickness more exacerbates the deformation of sheet material.
4th, do not handled effectively for veneer fiber and the scar knot itself existed in conventional panels processing technology, in sheet material
During internal stress release, the wood effect after easily having influence on pressing result and being compound.
5th, conventional thermocompression mode is, it is necessary to which firing to support, and needs to improve platen temperature to 120-200 using high temperature
It can just make there is aldehyde glue to play adhesive effect when spending, and high temperature more increases the release of aldehyde glue formaldehyde, and human body and environment are made
Into larger harm.
In view of the above-mentioned technical difficulty that traditional solid sawn sheet material heat pressing process is present, this application provides a kind of pure solid wood board
Normal temperature pressing process.
The content of the invention
Present invention seek to address that deformed present in existing practical sheet material pressing process warpage, consumption it is a large amount of using combustion can,
The technical problem underlying such as not environmental and ecological enough and wood effect is undesirable, has revolutionary innovation there is provided one kind in this application
Energy saving and environment friendly pure solid wood without the thick core multi-layered board normal temperature pressing process of deformation, the technique has relative to conventional thermocompression technique
Energy-conserving and environment-protective, technique is controllable, flatness is good, without the advantage such as deformation warpage, wood effect be excellent.
To solve the above problems, the technical solution adopted in the present invention is：
The pure indeformable wood plank normal temperature pressing process of reality, it is characterized in that, it can hot-forming be without any to change tradition combustion
The cold moudling of energy is fired, concrete technology step is as follows：
Step 1: Veneer Cutting
Rounding is machined to the thick log veneers of 3-5mm, the log board dimension specification is 1280mmX2520mm, rotation
Log veneer after cutting is the whole veneer without splicing；
Step 2: drying
Veneer after rotary-cut is sent into drying kiln, drying to Veneer moisture is 6%-8%, obtain aqueous uniform whole veneer；
Step 3: removing scar knot
Scar knot dise knife correspondence will be gone to be positioned at the scar node of veneer surface, from top to bottom the scar knot on veneer will be rushed using pressed sheet
Pressure is removed, and is fallen to refill patch at hole in former scar knot afterwards, is become one without whole high veneer of scar knot, flatness；
Step 4: disrumpent feelings fiber
Using disrumpent feelings blade vertical punching press veneer from top to bottom, the blade of disrumpent feelings blade is vertical with the grain direction of veneer lumber,
Make the growth fiber of the veneer after punching press disrumpent feelings, to remove the deformational stress of veneer；
In order that veneer fiber part after punching press rapid closing and can not influence single plate intensity, the present invention to disrumpent feelings blade with
And the design that punching press point is adapted；The cutter hub thickness of wherein described disrumpent feelings blade is 0.2-0.4mm, and bottom blade is whole
Body is arc structure, and edge length is 5mm, and thickness of knife edge is 0.1-0.2mm；In the grain direction of the veneer lumber, two
Spacing between adjacent punching press point is 15-30cm；
Step 5: using glue
Compound one side is needed uniformly to coat glue-line in veneer, glue used is the splicing adhesive of conventional commercial；
Step 6: cold moudling
According to different product thickness requirements, by whole veneer after gluing along it is forward unidirectional or replace in length and breadth both complex methods it
One carries out interlayer overlapping, by cold press cold moudling after being combined, and obtains good flatness, even density, without deformation warpage, height
The good pure solid wood board finished product of shelves environmental protection, wood effect；
In order to further reach the demand of industrialized production, production capacity is improved, curing agent can be added in interlayer compound tense, addition is
Conventional amount used.
Going in scar knot and disrumpent feelings fiber process in above-mentioned technical process, uses a kind of multifunctional plate processor
Tool equipment, its structure includes the lifting punching mechanism of dynamical system drive control, and is fixed on ground and is lifted with top
The corresponding plane operating mechanism of punching mechanism；The dynamical system uses hydraulic jack 1, and the hydraulic jack 1 is exported
The lifting punching mechanism is connected, the lifting punching mechanism is controlled by the output power of hydraulic jack 1 up and down reciprocatingly
Punching press is acted；The lifting punching mechanism includes lifting support 2 and the press work platform being fixedly connected by the lifting support 2
3, the lower surface of the press work platform 3 is planar structure；The plane operating mechanism includes ground riser 4 and is installed on ground
Pressure-bearing workbench 5 on face riser 4, for placing sheet material.
The sheet material processing plant equipment of said structure removes scar knot available for plate stamping, finds sheet material scar node, will go scar
Cutter placement positioning is tied at the scar node of plate surface, then can be by going scar by the downward punching press of top press work platform 3
Knot cutter washes out the scar node on sheet material.
Further, in order that the equipment has the function of broken fiber, the lower surface of the press work platform is detachably pacified
Equipped with broken fiber tool 6；The broken fiber tool 6 is by rectangle tool rest 6-1 and is uniformly fixed on the rectangle tool rest 6-1
Some disrumpent feelings blade 6-2 are constituted, and the blade direction of the disrumpent feelings blade 6-2 on the rectangle tool rest 6-1 is consistent, disrumpent feelings blade 6-2
Blade direction and sheet material growth grain direction it is vertical；The vertical or horizontal arrangements of rectangle tool rest 6-1 are laid in the punching press
The lower surface of workbench 3, uniformly arranges some disrumpent feelings blade 6-2 along rectangle tool rest 6-1 length wises, in the press work platform
3 lower surface formation dot matrix arrangement, in the grain direction of sheet material, staggered row between two adjacent rows are disrumpent feelings blade 6-2
Spacing between row, two adjacent rows are disrumpent feelings blade 6-2 is 15-30cm.
In order to obtain more punching press effect, the using effect and service life of cutter are ensured, the disrumpent feelings blade 6-2 is whole
Body is arc structure, and the impact failure itself brought to disrumpent feelings blade in punching course is reduced with this, the disrumpent feelings blade 6-2's
Cutter hub thickness is 0.2-0.4mm, and edge length is 5mm, and thickness of knife edge is 0.1-0.2mm.
The energy saving and environment friendly pure solid wood of the present invention is without the thick core multi-layered board normal temperature pressing process of deformation, and changing tradition combustion can hot pressing
The cold pressing forming process without any combustion energy is shaped to, relative to conventional thermocompression shaping, the energy is not only saved, more crucial is cold pressing
No aldehyde glue is directly used to can reach pressing result without there is aldehyde glue, or even more preferably so that pressing process and finished product are used
It is environment friendly and pollution-free to the nontoxic non-hazardous of human body.On joint technology, the present invention, which changes traditional Three kinds of hors d'oeuvres four and spells seamed splitting mode, is
Whole seamless veneer, it is to avoid because each part thickness is inconsistent, density is inconsistent, flat on a plate caused by seamed split
The defect of whole degree difference, greatly improves the flatness of finished product sheet material.In addition, in order to ensure that finished product sheet material is indeformable, the application is adopted
With broken fiber and scar knot technique is gone, make it that veneer fiber is disrumpent feelings by broken fiber, to reduce distortional stress, by going scar knot will
Veneer itself removes in the presence of some scar knots and fills up closure, maximized to remove the oneself factor for being easily caused veneer deformation warpage
Remove, to ensure the resistance to deformation and flatness of finished product sheet material, and can carry out chasing processing on its surface, greatly improve sheet material
Wood effect, outward appearance class and application.
Brief description of the drawings
Fig. 1：A kind of mechanical device structure schematic diagram of multifunctional plate processing；
Fig. 2：Broken fiber tool structural representation in Fig. 1；
Fig. 3：Plate surface structural representation after disrumpent feelings fiber；
In figure, 1, hydraulic jack, 2, lifting support, 3, press work platform, 4, ground riser, 5, pressure-bearing workbench, 6, broken fibre
Tie up cutter, 6-1, rectangle tool rest, 6-2, disrumpent feelings blade.
Embodiment
The energy saving and environment friendly pure solid wood of the present invention is made in detailed below without the thick core multi-layered board normal temperature pressing process of deformation below
Illustrate, following examples and must not be used as limiting the scope of the invention as just the explanation of technical solution of the present invention.
Embodiment 1
The finished product solid wood board specification that the present embodiment is suppressed is thickness 10mm, length 1220mm, width 2440mm, conventional lattice
Plate.
Energy saving and environment friendly pure solid wood is without the thick core multi-layered board normal temperature pressing process of deformation, and it can hot-forming be nothing to change tradition combustion
The cold moudling of any combustion energy is needed, concrete technology step is as follows：
Step 1: Veneer Cutting
Rounding is machined to 3.5mm thickness, 2440mm length, three wide 1220mm full wafer log veneers, wherein two veneers
Machine direction is longitudinal direction, and the machine direction of a veneer is laterally in addition；
Step 2: drying
Veneer after rotary-cut is sent into drying kiln, drying to Veneer moisture is 6%-7%, obtain aqueous uniform whole veneer；
Step 3: removing scar knot
Scar knot dise knife correspondence will be gone to be positioned at the scar node of veneer surface, from top to bottom the scar knot on veneer will be rushed using pressed sheet
Pressure is removed, and is fallen to refill patch at hole in former scar knot afterwards, is become one without whole high veneer of scar knot, flatness；
Step 4: disrumpent feelings fiber
Using the from top to bottom vertical punching press veneer of disrumpent feelings blade, the blade of blade is vertical with the fiber pattern direction of veneer lumber,
Make the growth fiber of the veneer after punching press disrumpent feelings, to remove the deformational stress of veneer；The cutter hub thickness of the disrumpent feelings blade is
0.2-0.4mm, bottom blade generally arc structure, edge length is 5mm, and thickness of knife edge is 0.1-0.2mm；In the veneer
In the grain direction of timber, the spacing between 2 adjacent punching press points is 15-30cm；
Step 5: using glue
Splicing adhesive is uniformly coated respectively in the veneer two sides as core plate, and another two veneers as top layer are without gluing；
Step 6: cold moudling
Three veneers after gluing are subjected to interlayer superimposion in longitudinal and transverse, vertical this mode alternate in length and breadth from bottom to top, it is multiple
By cold press cold moudling after conjunction, good flatness, even density are obtained, warpage, high-grade environmentally friendly, wood effect are good without deforming
Pure solid wood board finished product.
Embodiment 2
The finished product solid wood board specification that the present embodiment is suppressed is thickness 20mm, length 1800mm, width 1000mm.
Energy saving and environment friendly pure solid wood is without the thick core multi-layered board normal temperature pressing process of deformation, and it can hot-forming be nothing to change tradition combustion
The cold moudling of any combustion energy is needed, concrete technology step is as follows：
Step 1: Veneer Cutting
Rounding is machined to 4mm thickness, 1800mm length, five wide 1000mm log veneers（Three veneers of longitudinal fiber, it is horizontal
To two veneers of fiber）；
Step 2: drying
Veneer after rotary-cut is sent into drying kiln, drying to Veneer moisture is 7%-8%, obtain aqueous uniform whole veneer；
Step 3: removing scar knot
Scar knot dise knife correspondence will be gone to be positioned at the scar node of veneer surface, from top to bottom the scar knot on veneer will be rushed using pressed sheet
Pressure is removed, and is fallen to refill patch at hole in former scar knot afterwards, is become one without whole high veneer of scar knot, flatness；
Step 4: disrumpent feelings fiber
Using the from top to bottom vertical punching press veneer of disrumpent feelings blade, the blade of blade is vertical with the fiber pattern direction of veneer lumber,
Make the growth fiber of the veneer after punching press disrumpent feelings, to remove the deformational stress of veneer；The cutter hub thickness of the disrumpent feelings blade is
0.2-0.4mm, bottom blade generally arc structure, edge length is 5mm, and thickness of knife edge is 0.1-0.2mm；In the veneer
In the grain direction of timber, the spacing between 2 adjacent punching press points is 15-30cm；
Step 5: using glue
The two sides of two core plates uniform coating splicing adhesive respectively wherein, and bosom veneer and as top layer other two
Veneer is opened without gluing；
Step 6: cold moudling
Five veneers after gluing are combined with each other along alternate interlayer superimposion mode in length and breadth, pass through cold pressing after being combined
Machine cold moudling, obtain that flatness is good, even density, without the good pure solid wood board of deformation warpage, high-grade environmental protection, wood effect into
Product.
Embodiment 3
The finished product solid wood board specification that the present embodiment is suppressed is thickness 35mm, length 2000mm, width 1200mm.
Pure solid wood board normal temperature pressing process, it can hot-forming be the cold moudling without any combustion energy, tool to change traditional combustion
Body technology step is as follows：
Step 1: Veneer Cutting
Rounding is machined to 5mm thickness, 2000mm length, seven wide 1200mm log veneers（Four layers of veneer of longitudinal fiber, it is horizontal
To three layers of veneer of fiber）；
Step 2: drying
Veneer after rotary-cut is sent into drying kiln, drying to Veneer moisture is 6%-8%, obtain aqueous uniform whole veneer；
Step 3: removing scar knot
Scar knot dise knife correspondence will be gone to be positioned at the scar node of veneer surface, from top to bottom the scar knot on veneer will be rushed using pressed sheet
Pressure is removed, and is fallen to refill patch at hole in former scar knot afterwards, is become one without whole high veneer of scar knot, flatness；
Step 4: disrumpent feelings fiber
Using the from top to bottom vertical punching press veneer of disrumpent feelings blade, the blade of blade is vertical with the grain direction of veneer lumber, makes punching
The growth fiber of veneer after pressure is disrumpent feelings, to remove the deformational stress of veneer；The cutter hub thickness of the disrumpent feelings blade is 0.2-
0.4mm, bottom blade generally arc structure, edge length is 5mm, and thickness of knife edge is 0.1-0.2mm；In the veneer lumber
Grain direction on, spacing between 2 adjacent punching press points is 15-30cm；
Step 5: using glue
The two sides of three core plates uniform coating splicing adhesive respectively wherein, in addition two core plates and as top layer veneer without
Need gluing；
Step 6: cold moudling
Seven veneers after gluing are carried out into interlayer by alternate mode in length and breadth to be combined, it is ensured that there is glue to be glued between layers
Close, by cold press cold moudling after being combined, obtain good flatness, even density, without deformation warpage, high-grade environmental protection, solid wood
The good pure solid wood board finished product of effect.
Embodiment 4
The finished product solid wood board specification that the present embodiment is suppressed is thickness 10mm, length 2600mm, width 1300mm, conventional lattice
Plate.
Energy saving and environment friendly pure solid wood is without the thick core multi-layered board normal temperature pressing process of deformation, and it can hot-forming be nothing to change tradition combustion
The cold moudling of any combustion energy is needed, concrete technology step is as follows：
Step 1: Veneer Cutting
Rounding is machined to 3.5mm thickness, 2600mm length, three wide 1300mm full wafer log veneers, three log veneers
Fiber pattern direction it is consistent；
Step 2: drying
Veneer after rotary-cut is sent into drying kiln, drying to Veneer moisture is 6%-7%, obtain aqueous uniform whole veneer；
Step 3: removing scar knot
Scar knot dise knife correspondence will be gone to be positioned at the scar node of veneer surface, from top to bottom the scar knot on veneer will be rushed using pressed sheet
Pressure is removed, and is fallen to refill patch at hole in former scar knot afterwards, is become one without whole high veneer of scar knot, flatness；
Step 4: disrumpent feelings fiber
Using the from top to bottom vertical punching press veneer of disrumpent feelings blade, the blade of blade is vertical with the fiber pattern direction of veneer lumber,
Make the growth fiber of the veneer after punching press disrumpent feelings, to remove the deformational stress of veneer；The cutter hub thickness of the disrumpent feelings blade is
0.2-0.4mm, bottom blade generally arc structure, edge length is 5mm, and thickness of knife edge is 0.1-0.2mm；In the veneer
Grain direction on, spacing between 2 adjacent punching press points is 15-30cm；
Step 5: using glue
Splicing adhesive is uniformly coated respectively in the veneer two sides as core plate, and another two veneers as top layer are without gluing；
Step 6: cold moudling
By three veneers after gluing by unidirectionally forward in the way of carry out interlayer superimposion, it is compound after be cold-pressed by cold press
Shaping, obtains good flatness, even density, without the good pure solid wood board finished product of deformation warpage, high-grade environmental protection, wood effect.
The pure solid wood board normal temperature pressing process of above example, compares conventional thermocompression technique, there is following technical advantage：
1st, it is cold moudling to change tradition combustion energy hot-forming, starts making sheet energy-conserving and environment-protective new page, the existing national ring of high response
Guarantor's policy, with Prospects of Sustainable Development.
2nd, change traditional making sheet has aldehyde glue to be no aldehyde splicing adhesive with adhesive, to human body and the equal nontoxic pollution-free of environment, belongs to
Pure environmental and ecological plate.
3rd, it is thick core plate to change conventional thin core plate, and few with flaggy number during compacting same thickness sheet material, glue consumption is less, pure reality
Wood effect is more notable.
4th, it is that whole Zhang Houxin is seamless without edge-gluing veneer to change traditional Three kinds of hors d'oeuvres four to spell seamed match board, and the veneer of this mode rotary-cut exists
The uniformity, density on each point is consistent, so as to ensure the flatness of sheet material, smoothness and resistance to deformation crooking ability.
5th, by breaking fiber and going scar knot technique to solve the deformation effect that log oneself factor is caused to finished product sheet material, simultaneously
The scar knot that high-grade effect is influenceed in raw material is removed, production board non-deformability and high-grade degree is improved.
6th, traditional crisscross combination process is changed for forward unidirectional compound suppressing, technique simplifies, while production efficiency is improved,
Reduce deformation factor.
7th, the energy is saved, artificial, raising production capacity is saved, industrialized production can be achieved.
Through analysis, cause solid wood board deform principal element come from log own growth attribute, connecting method and
These three factors in the technical process of the present invention, have been carried out corresponding research and development and captured by these aspects of heat pressing process,
For log own growth attribute, the application employs brokenly fiber and goes scar knot technique, and for connecting method, the application is using whole
Piece veneer, for hot pressing power consumption and contamination hazard, the application uses cold pressing forming process.Pass through being directed to for above three broad aspect
Property effective means, solves the problem on deformation of existing solid wood board.
Claims (7)
1. energy saving and environment friendly pure solid wood is without the thick core multi-layered board normal temperature pressing process of deformation, it is characterised in that changing tradition combustion can heat
Molded is the cold moudling without any combustion energy, and concrete technology step is as follows：
Step 1: Veneer Cutting
Rounding is machined to the thick log veneers of 3-5mm；
Step 2: drying
Veneer after rotary-cut is sent into drying kiln, aqueous uniform whole veneer is obtained；
Step 3: removing scar knot
Scar knot dise knife correspondence will be gone to be positioned at the scar node of veneer surface, from top to bottom the scar knot on veneer will be rushed using pressed sheet
Pressure is removed, and is fallen to refill patch at hole in former scar knot afterwards, is become one without whole high veneer of scar knot, flatness；
Step 4: disrumpent feelings fiber
Using the from top to bottom vertical punching press veneer of disrumpent feelings blade, the blade of disrumpent feelings blade is vertical with the grain direction of veneer lumber,
Make the growth fiber of the veneer after punching press disrumpent feelings, to remove the deformational stress of veneer；
Step 5: using glue
Compound one side is needed uniformly to coat glue-line in veneer, glue used is splicing adhesive；
Step 6: cold moudling
According to different product thickness requirements, by whole veneer after gluing along it is forward unidirectional or replace in length and breadth both complex methods it
One carries out interlayer overlapping, by cold press cold moudling after being combined, and obtains good flatness, even density, without deformation warpage, height
The good pure solid wood board finished product of shelves environmental protection, wood effect.
2. energy saving and environment friendly pure solid wood as claimed in claim 1 exists without the thick core multi-layered board normal temperature pressing process of deformation, feature
In
In step one rotary-cut, the log veneer after rotary-cut is the whole veneer without splicing.
3. energy saving and environment friendly pure solid wood as claimed in claim 2 exists without the thick core multi-layered board normal temperature pressing process of deformation, feature
In,
In step 2 drying, drying to Veneer moisture is 6%-8%.
4. energy saving and environment friendly pure solid wood as claimed in claim 3 exists without the thick core multi-layered board normal temperature pressing process of deformation, feature
In,
In step 3 is disrumpent feelings fiber, the cutter hub thickness of the disrumpent feelings blade is 0.2-0.4mm, bottom blade generally arcuation knot
Structure, edge length is 5mm, and thickness of knife edge is 0.1-0.2mm；In the grain direction of the veneer lumber, two adjacent punching presses
Spacing between point is 15-30cm.
5. energy saving and environment friendly pure solid wood as claimed in claim 1 is without the thick core multi-layered board normal temperature pressing process of deformation, its feature
It is
Step 3 is gone in scar knot, uses a kind of multifunctional plate processing plant equipment, and it, which includes being driven by dynamical system, controls
The lifting punching mechanism of system, and it is fixed on plane operating mechanism on ground and corresponding with top lifting punching mechanism；Institute
State dynamical system and use hydraulic jack（1）, the hydraulic jack（1）The output connection lifting punching mechanism, passes through liquid
Compressing cylinder（1）Output power come control it is described lifting punching mechanism up and down reciprocatingly punching press action；The lifting punching mechanism
Including lifting support（2）And by the lifting support（2）The press work platform being fixedly connected（3）, the press work platform（3）
Lower surface be planar structure；The plane operating mechanism includes ground riser（4）And it is installed on ground riser（4）Upper, use
In the pressure-bearing workbench for placing sheet material（5）.
6. the energy saving and environment friendly pure solid wood as described in claim 1 or 5 is without the thick core multi-layered board normal temperature pressing process of deformation, it is special
Levy and be
In step 4 is disrumpent feelings fiber, a kind of multifunctional plate processing plant equipment is used, it includes being driven by dynamical system
The lifting punching mechanism of control, and it is fixed on plane operating mechanism on ground and corresponding with top lifting punching mechanism；
The dynamical system uses hydraulic jack（1）, the hydraulic jack（1）The output connection lifting punching mechanism, passes through
Hydraulic jack（1）Output power come control it is described lifting punching mechanism up and down reciprocatingly punching press action；The lifting stamping machine
Structure includes lifting support（2）And by the lifting support（2）The press work platform being fixedly connected（3）, the press work platform
（3）Lower surface be planar structure；The plane operating mechanism includes ground riser（4）And it is installed on ground riser（4）Upper,
Pressure-bearing workbench for placing sheet material（5）；The lower surface of the press work platform is detachably provided with brokenly fiber tool（6）；
The broken fiber tool（6）By rectangle tool rest（6-1）And uniformly it is fixed on the rectangle tool rest（6-1）On some disrumpent feelings knives
Piece（6-2）Constitute, the rectangle tool rest（6-1）On disrumpent feelings blade（6-2）Blade direction it is consistent, disrumpent feelings blade（6-2）'s
Blade direction is vertical with sheet material growth grain direction.
7. energy saving and environment friendly pure solid wood as claimed in claim 6 is without the thick core multi-layered board normal temperature pressing process of deformation, its feature
It is
The rectangle tool rest（6-1）Vertical or horizontal arrangement is laid in the press work platform（3）Lower surface, along rectangle tool rest
（6-1）Length wise is uniformly arranged some disrumpent feelings blades（6-2）, in the press work platform（3）Lower surface formation dot matrix row
Cloth structure, in the grain direction of sheet material, the adjacent disrumpent feelings blade of two rows（6-2）Between be staggered, two adjacent rows are disrumpent feelings
Blade（6-2）Between spacing be 15-30cm；The disrumpent feelings blade（6-2）Generally arc structure, cutter hub thickness is 0.2-
0.4mm, edge length is 5mm, and thickness of knife edge is 0.1-0.2mm.