KR20090011053A - 내피로균열 진전성이 우수한 강판 및 그 제조방법 - Google Patents
내피로균열 진전성이 우수한 강판 및 그 제조방법 Download PDFInfo
- Publication number
- KR20090011053A KR20090011053A KR1020097000477A KR20097000477A KR20090011053A KR 20090011053 A KR20090011053 A KR 20090011053A KR 1020097000477 A KR1020097000477 A KR 1020097000477A KR 20097000477 A KR20097000477 A KR 20097000477A KR 20090011053 A KR20090011053 A KR 20090011053A
- Authority
- KR
- South Korea
- Prior art keywords
- steel
- steel plate
- fatigue
- steel sheet
- fatigue crack
- Prior art date
Abstract
Description
Claims (17)
- 질량%로, C:0.01∼0.10%, Si:0.03∼0.6%, Mn:0.3∼2%, sol.Al:0.001∼0.1%, N:0.0005∼0.008%를 함유하고, 잔부는 Fe 및 불순물로 이루어지는 화학조성을 갖고, 또한 금속조직이 면적율로 60% 이상 85% 이하인 베이나이트 조직, 합계로 5%이하인 마르텐사이트 조직과 펄라이트 조직, 잔부가 페라이트 조직이며, 소성 변형률이 0.3~0.82인 형상 교정을 행한 것을 특징으로 하는 내피로균열 진전성이 우수한 강판.
- 청구항 1에 있어서,Fe의 일부 대신에, 질량%로, Cu:0.05∼1%, Ni:0.05∼1%, Cr:0.05∼1%, Mo:0.05∼0.8% 및 W:0.05∼0.5%의 1종 또는 2종 이상을 더 함유하는 것을 특징으로 하는 내피로균열 진전성이 우수한 강판.
- 청구항 1에 있어서, Fe의 일부 대신에, 질량%로, Nb:0.005∼0.08%, Ti: 0.005%∼0.03%, V:0.005∼0.08% 및 B:0.0005∼0.003%의 1종 또는 2종 이상을 더 함유하는 것을 특징으로 하는 내피로균열 진전성이 우수한 강판.
- 청구항 2에 있어서, Fe의 일부 대신에, 질량%로, Nb:0.005∼0.08%, Ti: 0.005%∼0.03%, V:0.005∼0.08% 및 B:0.0005∼0.003%의 1종 또는 2종 이상을 더 함 유하는 것을 특징으로 하는 내피로균열 진전성이 우수한 강판.
- 청구항 1에 있어서,Fe의 일부 대신에, 질량%로, Ca:0.0005∼0.007%, Mg:0.0005∼0.007% 및 REM:0.0005∼0.05%의 1종 또는 2종 이상을 더 포함하는 것을 특징으로 하는 내피로균열 진전성이 우수한 강판.
- 청구항 2에 있어서,Fe의 일부 대신에, 질량%로, Ca:0.0005∼0.007%, Mg:0.0005∼0.007% 및 REM:0.0005∼0.05%의 1종 또는 2종 이상을 더 포함하는 것을 특징으로 하는 내피로균열 진전성이 우수한 강판.
- 청구항 3에 있어서,Fe의 일부 대신에, 질량%로, Ca:0.0005∼0.007%, Mg:0.0005∼0.007% 및 REM:0.0005∼0.05%의 1종 또는 2종 이상을 더 포함하는 것을 특징으로 하는 내피로균열 진전성이 우수한 강판.
- 청구항 4에 있어서,Fe의 일부 대신에, 질량%로, Ca:0.0005∼0.007%, Mg:0.0005∼0.007% 및 REM:0.0005∼0.05%의 1종 또는 2종 이상을 더 포함하는 것을 특징으로 하는 내피로 균열 진전성이 우수한 강판.
- 청구항 1 내지 청구항 8 중 어느 한 항에 기재한 화학조성을 갖는 강편을, 1000℃∼1250℃의 온도 범위 내로 가열한 후, 열간 압연을 행하고 나서 냉각을 행하고, 냉각후에 강판의 소성 변형률을 0.3∼0.87로 하여 형상 교정을 행하는 강판의 제조방법으로서, 상기 냉각시에, 적어도 650℃∼500℃의 온도영역에서 평균 냉각속도 5℃/s 이상으로 가속냉각을 하는 것을 특징으로 하는 강판의 제조방법.
- 청구항 1 내지 청구항 8 중 어느 한 항에 기재한 화학조성을 갖는 강편을, 1000℃∼1250℃의 온도 범위내로 가열한 후, 열간 압연을 행하고, 이어서 열간 압연후 Ac1점 이상의 온도로 재가열하여 냉각을 행하고, 냉각후에 강판의 소성 변형률을 0.3∼0.87로 하여 형상 교정을 행하는 강판의 제조방법으로서, 상기 냉각시에, 적어도 650℃∼500℃의 온도영역에서 평균 냉각속도 5℃/s 이상으로 가속냉각을 하는 것을 특징으로 하는 강판의 제조방법.
- 청구항 9에 기재한 강판의 제조방법에 있어서, 가속 냉각후 450℃ 이하로 더 가열하여 템퍼링 처리를 실시하는 것을 특징으로 하는 강판의 제조방법.
- 청구항 10에 기재한 강판의 제조방법에 있어서, 가속 냉각후 450℃ 이하로 더 가열하여 템퍼링 처리를 실시하는 것을 특징으로 하는 강판의 제조방법.
- 청구항 1 내지 청구항 8 중 어느 한 항에 기재한 강판을 이용한 구조물.
- 청구항 9에 기재한 제조방법에 의해 제조된 강판을 이용한 구조물.
- 청구항 10에 기재한 제조방법에 의해 제조된 강판을 이용한 구조물.