KR20070001822A - A construction plate and method for manufacturing the same - Google Patents
A construction plate and method for manufacturing the same Download PDFInfo
- Publication number
- KR20070001822A KR20070001822A KR1020060058615A KR20060058615A KR20070001822A KR 20070001822 A KR20070001822 A KR 20070001822A KR 1020060058615 A KR1020060058615 A KR 1020060058615A KR 20060058615 A KR20060058615 A KR 20060058615A KR 20070001822 A KR20070001822 A KR 20070001822A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- clear
- bright
- building
- paint
- Prior art date
Abstract
Description
도 1은 실시예에 있어서의 건축판의 표면을 부분적으로 확대하여 도시된 단면 설명도. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a cross-sectional explanatory view showing a partially enlarged surface of a building plate in an embodiment;
도 2는 실시예에 있어서의 건축 원판을 도시된 사시도. Fig. 2 is a perspective view showing a building disc in the embodiment.
도 3은 실시예에 있어서의 건축 원판의 표면을 부분적으로 확대하여 도시된 단면 설명도. 3 is an explanatory cross-sectional view showing a partially enlarged surface of a building disc in an embodiment.
도 4는 실시예에 있어서의 건축 원판의 표면에 하도층을 형성한 상태를 부분적으로 확대하여 도시된 단면 설명도. Fig. 4 is a cross-sectional explanatory view showing a partially enlarged state in which a undercoat layer is formed on the surface of a building disc in the embodiment.
도 5는 실시예에 있어서의 하도층의 표면에 중도층을 형성한 상태를 부분적으로 확대하여 도시된 단면 설명도. Fig. 5 is an explanatory cross-sectional view showing a partially enlarged state in which a middle layer is formed on the surface of the undercoat layer in the embodiment.
도 6은 실시예에 있어서의 중도층의 요철 표면에서의 볼록부에 광휘 클리어층을 형성한 상태를 부분적으로 확대하여 도시된 단면 설명도. Fig. 6 is a cross-sectional explanatory view showing a partially enlarged state in which a bright clear layer is formed in the convex portion on the uneven surface of the intermediate layer in the embodiment.
도 7은 실시예에 있어서의 건축판의 표면을 부분적으로 확대하여 도시된 평면도. 7 is a partially enlarged plan view of the surface of the building plate in the embodiment;
도 8은 실시예에 있어서의 건축판의 표면을 부분적으로 확대하여 도시된 단면 설명도. 8 is a cross-sectional explanatory view showing a partially enlarged surface of a building plate in the embodiment;
* 도면의 주요 부분에 대한 부호의 간단한 설명 *Brief description of symbols for the main parts of the drawings
1 : 건축판 1: building plate
2 : 건축 원판2: architectural disc
3 : 하도층3: undercoat
4 : 중도층 4: middle layer
5 : 광휘 클리어층5: bright clear layer
6 : 표면 클리어층 6: surface clear layer
31 : 하도 도료31: undercoat
41 : 중도 도료41: intermediate paint
51 : 제 1 클리어 도료51: the first clear paint
52 : 박편형 광휘재 52: flaky bright material
61: 제 2 클리어 도료 61: second clear paint
201 : 표면201: surface
211 : 요철 모양211: irregularities
212 : 볼록부 212: convex portion
213 : 오목부213: recess
[특허문헌1] 일본 공개특허공보 제(평)10-305546 [Patent Document 1] Japanese Patent Application Laid-Open No. 10-305546
[특허문헌2] 일본 공개특허공보 제(소)58-20786호[Patent Document 2] Japanese Patent Application Laid-Open No. 58-20786
본 발명은 건축 원판의 요철 표면에 박편형(薄片狀) 광휘재를 함유하는 클리어층을 형성하여 이루어지는 건축판 및 그 제조방법에 관한 것이다. BACKGROUND OF THE
건축물의 외벽으로서 시공하는 건축판에 있어서는 건축 원판의 표면에 착색 도료로 이루어지는 도료층을 형성한 후, 이 도료층의 표면에 클리어 도료로 이루어지는 클리어층을 형성하고, 도료층을 보호하여 건축판의 내구성을 향상시키고 있다. In a building plate constructed as an outer wall of a building, after forming a paint layer made of colored paint on the surface of the building disc, a clear layer made of clear paint is formed on the surface of the paint layer, and the paint layer is protected to I improve durability.
그리고, 상기 클리어층의 내부 또는 상기 도료층의 표면에, 운모(mica) 박편 또는 금속가루 등으로 이루어지는 광휘재를 배치함으로써, 건축판의 의장 표면에 광휘성을 갖는(광택이 있는) 외관을 형성하고 있다. Then, by placing a bright material made of mica flakes, metal powder or the like on the inside of the clear layer or on the surface of the paint layer, an appearance having a glossiness (gloss) on the design surface of the building plate is formed. Doing.
예를 들면, 특허문헌1에 있어서는 섬유판으로 이루어지는 기재(基材)의 표면에 요철 모양을 형성하고, 이 요철 모양의 전체면에 하지(下地) 도막층 및 상도 도막층을 순차 형성하고, 그 후, 요철 모양의 볼록부면에만 광휘성 물질이 첨가된 클리어 도료를 도포하여 클리어 도막층을 형성하고 있다. 이것에 의해, 기재의 표면에 요철 모양이 형성되어 있어도, 소량의 광휘성 물질로 높은 광휘 효과를 얻을 수 있도록 하고 있다. For example, in
또한, 특허문헌2에 있어서는 기판상에 도포한 에나멜 도료의 표면에, 광물가루 또는 금속가루를 살포 또는 분출하고, 그 후, 클리어 도료를 도포하여, 장기간에 걸쳐 금속광택을 유지할 수 있는 시멘트판을 제조하였다. Moreover, in
그렇지만, 상기 특허문헌1에 있어서는 기재의 표면에 형성한 클리어층에 있어서, 광휘성 물질의 배치상태에 관해서는 아무런 연구가 이루어져 있지 않다. However, in the said
또한, 상기 특허문헌2에 있어서도, 에나멜 도료의 표면에 배치된 광물가루 또는 금속가루는 클리어 도료의 아래로 침강하고 있고, 광물가루 또는 금속가루의 배치상태에 관해서는 아무런 연구가 이루어져 있지 않다. Moreover, also in the said
그 때문에, 상기 특허문헌1, 2에 의해서는 광휘성 물질 또는 광물가루 등에 의한 충분한 광휘성(광택)을 얻는 것이 곤란하다. Therefore, according to the said
과제를 해결하기 위한 수단Means to solve the problem
본 발명은 이러한 종래의 문제점을 감안하여 이루어진 것으로, 대부분의 경사방향에서 보아도 광휘감을 나타낼 수 있고, 복잡한 반사의 간섭색을 나타낼 수 있는 건축판 및 그 제조방법을 제공하고자 하는 것이다. SUMMARY OF THE INVENTION The present invention has been made in view of such a conventional problem, and it is an object of the present invention to provide a building plate and a method of manufacturing the same, which can show brightness even in most oblique directions, and can exhibit interference colors of complex reflections.
제 1 발명은, 요철 모양을 갖는 표면을 구비한 건축 원판과;The first invention includes a building disc having a surface having an uneven shape;
상기 건축 원판의 상기 표면에 하도(下塗) 도료를 도포하여 이루어지는 하도층과;An undercoat layer formed by applying a undercoat paint to the surface of the building disc;
상기 하도층의 표면에 중도(中塗) 도료를 도포하여 이루어지고, 상기 요철 모양에 따른 요철 표면을 형성하여 이루어지는 중도층과; A middle layer formed by applying a middle coating material to the surface of the undercoat layer and forming a concave-convex surface according to the concave-convex shape;
상기 중도층의 요철 표면에서의 볼록부에, 복수의 박편형 광휘재를 함유하는 제 1 클리어 도료를 도포하여 이루어지는 광휘 클리어층; 및A bright clear layer formed by applying a first clear paint containing a plurality of flaky bright materials to the convex portions on the uneven surface of the intermediate layer; And
상기 광휘 클리어층의 표면을 포함한 상기 중도층의 표면의 전체에, 제 2 클리어 도료를 도포하여 이루어지는 표면 클리어층을 포함하며, A surface clear layer formed by applying a second clear paint to the entire surface of the intermediate layer including the surface of the bright clear layer,
상기 광휘 클리어층에서 상기 복수의 박편형 광휘재를, 침강시키지 않고, 상기 건축 원판의 면방향과 대략 평행하게 배치하는 것을 특징으로 하는 건축판에 관한 것이다(청구항 1). The plurality of flake shaped bright materials are disposed in the bright clear layer without being settled, and are arranged substantially parallel to the plane direction of the building disc (claim 1).
본 발명의 건축판에 있어서는 특히, 상기 복수의 박편형 광휘재를 함유하는 광휘 클리어층에 대해 연구를 하고 있다. In the building plate of this invention, the bright clear layer containing the said some flaky bright material is especially studied.
즉, 본 발명의 건축판에 있어서는 건축 원판의 표면에 형성한 중도층의 요철 표면에서의 볼록부에, 복수의 박편형 광휘재를 함유하는 제 1 클리어 도료를 도포하여, 광휘 클리어층을 형성하고 있다. 그리고, 이 광휘 클리어층에 있어서의 복수의 박편형 광휘재의 대부분은 광휘 클리어층에 있어서의 바닥부에 침강하지 않고, 광휘 클리어층에 있어서의 내부에 위치하고 있다. 또, 복수의 박편형 광휘재의 대부분은 건축 원판의 면방향과 대략 평행하게 배치되어 있다. That is, in the building plate of the present invention, a first clear paint containing a plurality of flake-shaped bright materials is applied to the convex portions of the uneven surface of the intermediate layer formed on the surface of the building disc, thereby forming a bright clear layer. have. And most of the flake-shaped bright materials in this bright clear layer do not settle in the bottom part in a bright clear layer, but are located inside the bright clear layer. In addition, most of the plurality of flaky bright materials are disposed substantially parallel to the plane direction of the building disc.
그리고, 건축판의 표면에 조사되는 광은 표면 클리어층을 통과하여, 광휘 클리어층에 있어서의 박편형 광휘재에 의해서 반사되어, 광휘감을 나타낼 수 있다. 또한, 건축판의 표면에 조사되는 광은 광휘 클리어층에 있어서의 박편형 광휘재에 의해서 반사되지 않아도, 표면 클리어층을 통과하여, 중도층에 의해서 반사되어, 광휘감을 나타낼 수 있다.And the light irradiated to the surface of a building plate passes through a surface clear layer, and is reflected by the flaky bright material in a brightness clear layer, and can show a glossiness. In addition, even if the light irradiated to the surface of the building plate is not reflected by the flaky bright material in the bright clear layer, the light passes through the surface clear layer and is reflected by the intermediate layer, thereby exhibiting a bright feeling.
이것에 의해, 건축판의 표면은 그에 대한 입사광의 각도에 그 만큼 영향을 받지 않고, 대부분의 경사방향에서 보아도 광휘감을 나타낼 수 있다. As a result, the surface of the building plate is not affected by the angle of incident light thereto, so that the surface of the building plate can exhibit brightness even when viewed in most oblique directions.
또한, 박편형 광휘재가 광휘 클리어층에 있어서 침강하지 않고, 건축 원판의 면방향과 대략 평행하게 배치됨으로써, 중도층에 의해서 반사된 광은 박편형 광휘재를 통과하여 표면 클리어층으로부터 출사되는 경우도 있다. In addition, since the flaky bright material does not settle in the bright clear layer and is disposed substantially parallel to the plane direction of the building disc, the light reflected by the intermediate layer passes through the flaky bright material and is emitted from the surface clear layer. have.
이것에 의해, 박편형 광휘재에 의해서 반사된 광과 중도층에 의해서 반사된 광이 간섭하여, 복잡한 반사의 간섭색을 나타낼 수 있다. Thereby, the light reflected by the flaky bright material and the light reflected by the intermediate | middle layer interfere, and the interference color of a complex reflection can be shown.
그 때문에, 본 발명의 건축판의 표면은 대부분의 경사방향에서 보아도 광휘감을 나타낼 수 있고, 복잡한 반사의 간섭색을 나타낼 수 있다. Therefore, the surface of the building plate of the present invention can exhibit a feeling of brightness even when viewed from most inclined directions, and can exhibit an interference color of complex reflection.
제 2 발명은, 요철 모양을 갖는 표면을 구비한 건축 원판을 성형하는 원판 성형 공정과;2nd invention is a disk shaping | molding process of shape | molding the building disc provided with the surface which has an uneven | corrugated shape;
상기 건축 원판의 상기 표면에 하도 도료를 도포하여 하도층을 형성하는 하도층 형성 공정과;A undercoat layer forming step of applying a undercoat to the surface of the building disc to form a undercoat;
상기 하도층의 표면에 중도 도료를 도포하여, 상기 요철 모양에 따른 요철 표면을 구비한 중도층을 형성하는 중도층 형성 공정과;A middle layer forming step of applying a middle paint to the surface of the undercoat layer to form a middle layer having a concave-convex surface according to the concave-convex shape;
상기 중도층의 요철 표면에서의 볼록부에 복수의 박편형 광휘재를 함유하고, 점도가 95 내지 120KU인 제 1 클리어 도료를 도포하여 광휘 클리어층을 형성하는 광휘 클리어층 형성 공정; 및A bright clear layer forming step of forming a bright clear layer by applying a first clear paint having a viscosity of 95 to 120 KU and containing a plurality of flaky bright materials in the convex portions on the uneven surface of the intermediate layer; And
상기 광휘 클리어층의 표면을 포함한 상기 중도층의 표면의 전체에, 제 2 클리어 도료를 도포하여 표면 클리어층을 형성하는 표면 클리어층 형성 공정을 포함하며, A surface clear layer forming step of applying a second clear paint to the entire surface of the intermediate layer including the surface of the clear clear layer to form a surface clear layer,
상기 광휘 클리어층 형성 공정에서는, 상기 제 1 클리어 도료를 롤 도장함으 로써, 상기 광휘 클리어층에서 상기 복수의 박편형 광휘재를 침강시키지 않고 상기 건축 원판의 면방향과 대략 평행하게 배치하는 것을 특징으로 하는 건축판의 제조방법에 관한 것이다(청구항 4). In the bright clear layer forming step, the first clear paint is roll-coated, so that the plurality of flaky bright materials are disposed in the bright clear layer to be substantially parallel to the plane direction of the building disc. It relates to a method of manufacturing a building plate to claim (claim 4).
본 발명의 건축판의 제조방법에 있어서는 상기 원판 성형 공정, 하도층 형성 공정 및 중도층 형성 공정을 행하여, 건축 원판의 표면에, 하도층 및 중도층을 형성한다. 이 때, 중도층에는 건축판의 표면에서의 요철 모양에 따른 요철 표면이 형성된다. In the manufacturing method of the building board of this invention, the said disk shaping | molding process, the undercoat layer forming process, and the middle layer forming process are performed, and the undercoat layer and the intermediate layer are formed in the surface of a building original board. At this time, the uneven surface corresponding to the uneven shape on the surface of the building plate is formed in the intermediate layer.
이어서, 상기 광휘 클리어층 형성 공정을 행하여, 중도층의 요철 표면에서의 볼록부에 광휘 클리어층을 형성한다. 그리고, 이 광휘 클리어층은 박편형 광휘재를 함유하고, 점도가 95 내지 120KU인 제 1 클리어 도료를 중도층의 요철 표면에서의 볼록부에 롤 도장함으로써 형성한다. Subsequently, the bright clear layer forming step is performed to form a bright clear layer on the convex portion on the uneven surface of the intermediate layer. And this bright clear layer contains flaky bright material, and is formed by roll-coating the 1st clear paint whose viscosity is 95-120 KU in the convex part in the uneven surface of an intermediate | middle layer.
그 때문에, 광휘 클리어층에 있어서는 제 1 클리어 도료 중에 존재하는 복수의 박편형 광휘재의 대부분이 바닥부에 침강하지 않고, 광휘 클리어층에 있어서의 내부에 배치된다. 또한, 복수의 박편형 광휘재의 대부분은 건축 원판의 면방향과 대략 평행하게 배치된다. For this reason, in the bright clear layer, most of the plurality of flaky bright materials present in the first clear paint do not settle to the bottom portion, and are disposed inside the bright clear layer. In addition, most of the plurality of flaky bright materials are disposed substantially parallel to the plane direction of the building disc.
그 후, 상기 표면 클리어층 형성 공정을 행하여, 광휘 클리어층의 표면을 포함한 중도층의 표면의 전체에 표면 클리어층을 형성한다. Thereafter, the surface clear layer forming step is performed to form a surface clear layer on the entire surface of the intermediate layer including the surface of the bright clear layer.
이렇게 해서 제조한 건축판의 표면은 상기 제 1 발명과 같이, 이 건축판의 표면에 대한 입사광의 각도에 그다지 영향을 받지 않고, 대부분의 경사방향에서 보아도 광휘감을 나타낼 수 있고, 복잡한 반사의 간섭색을 나타낼 수 있다. The surface of the building plate manufactured in this way is not affected by the angle of incident light with respect to the surface of the building plate as in the first invention, and can exhibit brightness even when viewed in most oblique directions, and exhibits complex reflection interference colors. Can be represented.
그 때문에, 본 발명의 건축판의 제조방법에 의하면, 대부분의 경사방향에서 보아도 광휘감을 나타낼 수 있고, 복잡한 반사의 간섭색을 나타낼 수 있는 건축판을 용이하게 제조할 수 있다. Therefore, according to the manufacturing method of the building board of this invention, even if it sees in the most inclination direction, it can show a brightness and can manufacture the building board which can show the interference color of a complex reflection easily.
발명을 실시하기 위한 최선의 형태Best Mode for Carrying Out the Invention
상술한 제 1, 제 2 발명에 있어서의 바람직한 실시 형태에 관하여 설명한다. Preferred embodiment in above-mentioned 1st, 2nd invention is demonstrated.
상기 제 1 발명에 있어서, 상기 제 1 클리어 도료의 점도의 값(KU)은 스토마 점도계{패들(paddle) 점도계}에 의해서 도료를 휘저을 때의 교반저항의 값으로 할 수 있다. KU는 KU치 또는 Krebs 단위라고 부르는 경우도 있다. 상기 제 2 발명에 있어서도 동일하다. In the said 1st invention, the value KU of the viscosity of a said 1st clear paint can be made into the value of the agitation resistance at the time of stirring the paint with a stoma viscometer (paddle viscometer). KU is sometimes called KU value or Krebs unit. The same applies to the second invention.
상기 제 1, 제 2 발명에 있어서, 상기 건축판으로서는 예를 들면, 양산을 하는 무기질 건축판이 있다. 또한, 무기질 건축판으로서는 예를 들면, 요업계(窯業界) 건축판이 있다. In the said 1st, 2nd invention, the said building board includes the inorganic building board which mass-produces, for example. In addition, as an inorganic building board, there exists a ceramic building board, for example.
또한, 상기 박편형 광휘재로서는 예를 들면, 운모(마이카)의 표면에 이산화티타늄의 피막을 형성하여 이루어지는 펄(pearl) 안료를 사용할 수 있다. 이산화티타늄은 높은 굴절율을 갖는 동시에 광의 확산성이 크고, 또한 반투명하기 때문에, 다중 평행광을 형성하기 쉬운 성질을 갖고 있다. As the flaky bright material, for example, a pearl pigment formed by forming a film of titanium dioxide on the surface of mica (mica) can be used. Titanium dioxide has a high refractive index, high light diffusivity, and translucency, and therefore has a property of easily forming multiple parallel lights.
또한, 그 외에도, 박편형 광휘재로서는 박편형의 유리인 유리 후레이크에 알루미늄을 증착하여 이루어지는 것, 운모, 티타늄 코팅 운모(은색), 백운모, 합성운모, 간섭운모, 산화 티타늄을 첨가한 운모 등이 있다. 이러한 박편형 광휘재는 비중 4 내지 5정도의 고비중이며, 침강하기 쉬운 경향이 있다. In addition, as the flaky bright material, aluminum is deposited on glass flakes, which are flaky glass, mica, titanium coated mica (silver), white mica, synthetic mica, interference mica, titanium oxide added mica, and the like. have. Such flaky bright materials have a high specific gravity of about 4 to 5 specific gravity and tend to settle easily.
또한, 박편형 광휘재는 그 입자직경이 30 내지 50㎛이고, 그 두께가 1 내지 2㎛인 것을 사용할 수 있다. Moreover, the flaky bright material can be used whose particle diameter is 30-50 micrometers, and whose thickness is 1-2 micrometers.
또한, 제 1 클리어 도료 전량에 대한 박편형 광휘재의 함유량은 예를 들면, 3 내지 7질량%로 할 수 있다. In addition, content of the flaky bright material with respect to 1st clear paint whole quantity can be 3-7 mass%, for example.
또, 상기 제 1 발명에 있어서, 상기 건축 원판에 있어서의 요철 모양은 복수의 미세한 볼록부를 형성하여 이루어지고, 상기 광휘 클리어층은 상기 중도층의 요철 표면에서의 미세한 볼록부에 도포하는 것이 바람직하다(청구항 2). Moreover, in the said 1st invention, it is preferable that the uneven | corrugated shape in the said building disc forms a some fine convex part, and the said bright clear layer is apply | coated to the fine convex part in the uneven surface of the said intermediate | middle layer. (Claim 2).
이 경우에는 요철 표면에서의 미세한 볼록부에 박편형 광휘재를 정착시킴으로써, 박편형 광휘재의 사용량을 적게 하여, 광휘감이 우수하고, 복잡한 반사의 간섭색을 나타낼 수 있는 건축판을 제조할 수 있다. 또, 비싼 박편형 광휘재의 사용량을 가능한 한 적게 함으로써, 건축판의 비용 상승을 억제할 수 있다. In this case, by fixing the flaky bright material to fine convex portions on the uneven surface, the amount of use of the flaky bright material can be reduced, and a building plate can be produced which is excellent in the brightness and can exhibit a complex reflection interference color. Moreover, the cost increase of a building plate can be suppressed by making the usage-amount of an expensive flaky bright material as small as possible.
또한, 상기 제 1 클리어 도료의 점도는 95 내지 120KU이고, 상기 광휘 클리어층은 상기 제 1 클리어 도료를 롤 도장함으로써 형성하는 것이 바람직하다(청구항 3). Moreover, it is preferable that the viscosity of the said 1st clearing paint is 95-120 KU, and the said glossiness clear layer is formed by roll-coating the said 1st clearing paint (claim 3).
이 경우에는 상기 광휘감이 우수하고, 복잡한 반사의 간섭색을 나타낼 수 있는 건축판을 용이하게 제조할 수 있다. In this case, the building plate which is excellent in the said brightness | luminance and can exhibit the interference color of a complex reflection can be manufactured easily.
또, 상기 제 1, 제 2 발명에 있어서, 상기 제 1 클리어 도료의 점도가 95KU 미만인 경우에는 제 1 클리어층의 점도가 지나치게 낮아져, 박편형 광휘재가 그 비중에 의해 침강하여 버려, 광휘 클리어층에 있어서의 내부에 배치시키는 것이 곤란하게 된다. 한편, 제 1 클리어 도료의 점도가 120KU를 초과하는 경우에는 제 1 클 리어층의 점도가 지나치게 높아져, 제 1 클리어층을 중도층의 요철 표면에 도포하는 것이 곤란하게 된다. Moreover, in the said 1st, 2nd invention, when the viscosity of the said 1st clearing paint is less than 95 KU, the viscosity of a 1st clear layer will become low too much, and a flaky bright material will settle by the specific gravity, and to a bright clear layer It becomes difficult to arrange | position inside. On the other hand, when the viscosity of the first clear paint exceeds 120 KU, the viscosity of the first clear layer becomes too high, making it difficult to apply the first clear layer to the uneven surface of the intermediate layer.
실시예Example
이하에, 본 발명의 건축판 및 그 제조방법에 관계되는 실시예에 관하여, 도면과 함께 설명한다.EMBODIMENT OF THE INVENTION Below, the Example which concerns on the building plate of this invention and its manufacturing method is demonstrated with drawing.
본 예의 건축판(1)은 도 1에 도시된 바와 같이, 요철 모양(211)을 갖는 건축 원판(2)의 표면에, 하도층(3), 중도층(4), 광휘 클리어층(5) 및 표면 클리어층(6)을 순차 형성하여 이루어진다. As shown in FIG. 1, the
상기 하도층(3)은 도 4에 도시된 바와 같이, 건축 원판(2)의 표면에, 하도 도료(31)를 도포하여 이루어진다. 상기 중도층(4)은 도 5에 도시된 바와 같이, 하도층(3)의 표면에 중도 도료(41)를 도포하여 이루어지고, 건축 원판(2)의 표면에서의 요철 모양(211)에 따른 요철 표면을 형성하여 이루어진다.As shown in FIG. 4, the
상기 광휘 클리어층(5)은 도 6에 도시된 바와 같이, 중도층(4)의 요철 표면에서의 볼록부(411)에, 복수의 박편형 광휘재(52)를 함유하는 제 1 클리어 도료(51)를 도포하여 이루어진다. 그리고, 광휘 클리어층(5)에 있어서의 복수의 박편형 광휘재(52)는 침강시키지 않고, 건축 원판(2)의 면방향에 대략 평행하게 배치되어 있다. As shown in FIG. 6, the bright
상기 표면 클리어층(6)은 도 1에 도시된 바와 같이, 광휘 클리어층(5)의 표면을 포함한 중도층(4)의 표면의 전체에, 제 2 클리어 도료(61)를 도포하여 이루어진다. As shown in FIG. 1, the surface
이하에, 본 예의 건축판(1) 및 그 제조방법에 관하여, 도 1 내지 도 8과 함께 상세하게 설명한다. Below, the
도 2에 도시된 바와 같이, 상기 건축 원판(2)은 요업계 건축판(1)이고, 시멘트질 원료(시멘트, 규산 원료 등)에, 목질 원료(목섬유, 목칩 등), 첨가제 및 물 등을 혼합하여 혼합 원료를 만들고, 이 혼합 원료를 성형형의 성형면상에 살포하여 건조 경화시켜 성형한 것이다. As shown in Fig. 2, the
그리고, 건축 원판(2)의 표면은 복수의 미세한 볼록부(212)에 의한 요철 모양(211)을 형성하여 이루어지는 의장 볼록면(21)과, 이 의장 볼록면(21)으로부터 함몰하여 의장 볼록면(21)을 구획하는 줄눈 오목부(22)로 이루어진다. And the surface of the building
또한, 건축 원판(2)에 있어서의 요철 모양(211)은 복수의 미세한 볼록부(212)와 오목부(213)를 혼재 형성하여 이루어진다. 그리고, 오목부(213)에 대한 볼록부(212)의 돌출 높이는 0.1 내지 1mm으로 되어 있다. In addition, the uneven |
상기 하도 도료(31)는 점도가 70 내지 75KU인 도료로 이루어진다. 그리고, 상기 하도층(3)은 하도 도료(31)를 스프레이 도장에 의해, 10 내지 12g/척(尺)2(109 내지 131g/㎡)의 도포량으로 도포하여 이루어지고, 건축판(1)의 줄눈색(줄눈 오목부(22)의 색)으로서 형성된다. The
상기 중도 도료(41)는 점도가 80 내지 85KU인 도료로 이루어진다. 그리고, 상기 중도층(4)은 중도 도료(41)를 롤 코터 도장에 의해, 4 내지 6g/척2(43 내지 65g/㎡)의 도포량으로 도포하여 이루어지고, 건축 원판(2)의 의장 볼록면(21)에서 의 요철 모양(211)의 전체에 형성된다. The
상기 제 1 클리어 도료(51)는 점도가 95 내지 120KU인 클리어 도료로 이루어지고, 그 전체량에 대하여 박편형 광휘재(52)를 5질량% 함유하여 이루어진다. 그리고, 상기 광휘 클리어층(5)은 제 1 클리어 도료(51)를 롤 코터 도장에 의해, 4 내지 6g/척2(43 내지 65g/㎡)의 도포량으로 도포하여 이루어지고, 요철 모양(211)에 있어서의 볼록부(212)에 형성된다 The said 1st
상기 제 2 클리어 도료(61)는 점도가 20 내지 25초(이와타컵 NK2, 25℃)인 클리어 도료로 이루어진다. 그리고, 상기 표면 클리어층(6)은 제 2 클리어 도료(61)를 에어 스프레이 도장에 의해, 4 내지 8g/척2(43 내지 87g/㎡)의 도포량으로 도포하여 이루어지고, 건축 원판(2)의 표면의 전체(의장 볼록면(21) 및 줄눈 오목부(22))에 형성된다. The second
본 예의 박편형 광휘재(52)로서는 운모(마이카)의 표면에 이산화티타늄의 피막을 형성하여 이루어지는 펄 안료이다. 이 펄 안료는 그 막 두께를 변화시킴으로써, 여러가지의 색의 발색이 가능하다. 그리고, 본 예의 복수의 박편형 광휘재(52)는 그 막 두께가 복수 종류로 변화하고 있는 것에 의해, 광이 조사되었을 때에 복수 종류의 색을 발색할 수 있다. The flaky
또한, 중도층(4)을 형성하기 위해서 중도 도료(41)는 바니시와 안료를 혼합하여 이루어지고, 불투명색을 갖고 있다. 제 1 클리어 도료(51)는 경화 후에 투명한 외관을 나타내는 클리어 수지, 복수의 박편형 광휘재(52) 및 각종 첨가제를 함 유하여 이루어진다. 제 2 클리어 도료(61)는 경화 후에 투명한 외관을 나타내는 클리어 수지 및 각종 첨가제를 함유하여 이루어진다. In addition, in order to form the intermediate |
또한, 중도 도료(41) 및 클리어 도료(51, 61)는 윤 제거제를 거의 함유하고 있지 않아, 윤기가 있는 도막을 형성할 수 있다. In addition, the
다음에, 상기 건축판(1)의 제조방법에 관하여 상세하게 설명한다. Next, the manufacturing method of the said
건축판(1)을 제조할 때는 우선, 도 2, 도 3에 도시된 바와 같이, 원판 성형 공정으로서, 건축 원판(2)을 성형한다. 그리고, 이 건축 원판(2)에는 의장 볼록면(21)과 줄눈 오목부(22)를 형성하고, 의장 볼록면(21)의 표면에는 복수의 미세한 볼록부(212)와 오목부(213)를 구비한 요철 모양(211)을 형성한다. When manufacturing the
이어서, 도시는 생략하지만, 실러 공정으로서, 하도층 형성 공정 전에, 건축 원판(2)과 하도층(3)을 밀착시키기 위해서, 건축 원판(2)의 표면의 전체에 실러처리를 실시한다. Next, although illustration is abbreviate | omitted, as a sealer process, in order to make the building
이어서, 도 4에 도시된 바와 같이, 하도층 형성 공정으로서, 건축 원판(2)의 표면의 전체(상기 의장 볼록면(21) 및 줄눈 오목부(22))에, 스프레이 도장에 의해 하도 도료(31)를 도포한다. 이 때, 하도 도료(31)에는 점도가 70 내지 75KU인 도료를 사용한다. 그리고, 건축 원판(2)의 표면에, 하도 도료(31)를 10 내지 12g/척2의 도포량으로 도포하여, 하도층(3)을 형성한다. Subsequently, as shown in FIG. 4, as the undercoat layer forming step, the entire undercoat (the design
또한, 하도층(3)은 80 내지 110℃의 온풍을 약 3분간 분출하여, 제트 건조시키는 동시에 경화를 시킬 수 있다. In addition, the
이어서, 도 5에 도시된 바와 같이, 중도층 형성 공정으로서, 상기 의장 볼록면(21)에 있어서의 하도층(3)의 표면에, 롤 코터 도장에 의해 중도 도료(41)를 도포한다. 이 때, 중도 도료(41)에는 점도가 80 내지 85KU인 도료를 사용한다. 그리고, 중도층(4)의 표면에, 중도 도료(41)를 4 내지 6g/척2의 도포량으로 도포하여, 건축 원판(2)의 표면에서의 요철 모양(211)에 따른 요철 표면을 구비한 중도층(4)을 형성한다. Next, as shown in FIG. 5, the intermediate |
또, 중도층(4)은 80 내지 110에서의 온풍을 대략 3분간 분출하여, 제트 건조시키는 동시에 경화를 시킬 수 있다. Moreover, the intermediate |
이어서, 도 6에 도시된 바와 같이, 광휘 클리어층 형성 공정으로서, 중도층(4)의 요철 표면에서의 볼록부(411)에, 롤 코터 도장에 의해 제 1 클리어 도료(51)를 도포한다. 이 때, 제 1 클리어 도료(51)에는 복수의 박편형 광휘재(52)를 5질량% 함유하고, 점도가 105 내지 110KU인 도료를 사용한다. 그리고, 중도층(4)의 요철 표면에서의 볼록부(411)에, 제 1 클리어 도료(51)를 4 내지 6g/척2의 도포량으로 도포하여, 광휘 클리어층(5)을 형성한다. Next, as shown in FIG. 6, as a bright clear layer formation process, the 1st
또한, 건축 원판(2)의 표면에 접촉시키는 롤 코터의 롤 표면의 고무 경도는 35 내지 45도로 높게 하고, 롤 표면이, 중도층(4)의 요철 표면에서의 볼록부(411)에만 접촉하도록 하였다. In addition, the rubber hardness of the roll surface of the roll coater which contacts the surface of the building
상기 제 1 클리어 도료(51)의 점도가 105 내지 110으로 높은 것에 의해, 광휘 클리어층(5)에 있어서는 제 1 클리어 도료(51) 중에 존재하는 복수의 박편형 광 휘재(52)의 대부분이 바닥부에 침강하지 않고, 광휘 클리어층(5)에 있어서의 내부에 배치된다. 또한, 복수의 박편형 광휘재(52)의 대부분은 건축 원판(2)의 면방향에 대략 평행하게 배치된다. Since the viscosity of the said
이와 같이 박편형 광휘재(52)의 대부분이 건축 원판(2)의 면방향에 대략 평행하게 배치되는 이유로서는 아래와 같이 생각된다. 즉, 제 1 클리어 도료(51)가 고점도이기 때문에, 박편형 광휘재(52)는 제 1 클리어 도료(51)의 중간부분에 유리(遊離)한다. 그리고, 롤 코터의 롤 표면의 고무경도가 높은 것에 의해, 제 1 클리어 도료(51) 중의 박편형 광휘재(52)가 롤 코터의 압력을 받아 평행형이 되고, 박편형 광휘재(52)의 대부분이 건축 원판(2)의 면방향에 대략 평행하게 배치된다고 생각한다. Thus, the reason why most of the flaky
그 후, 도 1에 도시된 바와 같이, 표면 클리어층 형성 공정으로서, 광휘 클리어층(5)의 표면을 포함한 중도층(4)의 표면의 전체(상기 의장 볼록면(21) 및 줄눈 오목부(22))에, 스프레이 도장에 의해 제 2 클리어 도료(61)를 도포한다. 이 때, 제 2 클리어 도료(61)에는 점도가 20 내지 25초(이와타컵 NK2, 25℃)인 클리어 도료를 사용한다. 그리고, 중도층(4)의 표면의 전체에, 제 2 클리어 도료(61)를 4 내지 8g/척2의 도포량으로 도포하여, 표면 클리어층(6)을 형성한다. Thereafter, as shown in FIG. 1, as a surface clear layer forming process, the entire surface of the
그리고, 광휘 클리어층(5) 및 표면 클리어층(6)을, 80 내지 110℃의 온풍을 대략 3분간 분출하여, 제트 건조시키는 동시에 경화를 시킬 수 있다. 이렇게 해서, 건축 원판(2)의 표면에 도료층을 형성하여 이루어지는 건축판(1)을 제조할 수 있다. Then, the bright
이와 같이 제조한 건축판(1)은 복수의 박편형 광휘재(52)의 대부분을 광휘 클리어층(5)에 있어서 침강시키지 않고, 건축 원판(2)의 면방향에 대략 평행하게 배치시켜 이루어진다. The
도 7은 건축판(1)의 표면을 확대하여 모식적으로 도시된 도면이다. 동 도면에 있어서, 복수의 박편형 광휘재(52)가 배치된 부분은 건축판(1)의 표면의 요철 모양(111)에 있어서의 볼록부(112)를 나타내고, 박편형 광휘재(52)가 거의 배치되어 있지 않은 부분은 건축판(1)의 표면의 요철 모양(111)에 있어서의 오목부(113)를 나타낸다. 7 is a diagram schematically showing an enlarged surface of the
그리고, 도 8에 도시된 바와 같이, 건축판(1)의 표면에 조사되는 광(L1)은 표면 클리어층(6)을 통과하여, 광휘 클리어층(5)에 있어서의 박편형 광휘재(52)에 의해서 반사되어, 광휘감을 나타낼 수 있다. 또, 건축판(1)의 표면에 조사되는 광(L2)은 광휘 클리어층(5)에 있어서의 박편형 광휘재(52)에 의해서 반사되지 않아도, 표면 클리어층(6)을 통과하여, 중도층(4)에 의해서 반사되고, 다시 표면 클리어층(6)을 통과함으로써, 광휘감을 나타낼 수도 있다. And, as shown in FIG. 8, light L1 irradiated to the surface of the
이것에 의해, 건축판(1)의 표면은 이것에 대한 입사광의 각도에 그다지 영향을 받지 않고, 대부분의 경사방향에서 보아도 광휘감을 나타낼 수 있다. Thereby, the surface of the
또, 도 8에 도시된 바와 같이, 박편형 광휘재(52)가 광휘 클리어층(5)에 있어서 침강하지 않고, 건축 원판(2)의 면방향에 대략 평행하게 배치되어 있는 것에 의해, 중도층(4)에 의해서 반사된 광(L3)은 박편형 광휘재(52)를 통과하여 표면 클 리어층(6)으로부터 출사되는 경우도 있다. 이 광(L3)은 중도층(4)의 색채를 반영하여 발색할 수 있다. In addition, as shown in FIG. 8, the flaky
이것에 의해, 박편형 광휘재(52)에 의해서 반사된 광과, 중도층(4)에 의해서 반사된 광이 간섭하여, 건축판(1)은 복잡한 반사의 간섭색으로서, 여러가지의 색채를 나타낼 수 있다. As a result, the light reflected by the flaky
이와 같이, 박편형 광휘재(52)에 의해서 복잡한 반사의 간섭색을 나타낼 수 있기 때문에, 광휘 클리어층(5)을 형성하는 제 1 클리어 도료(51)에 착색 안료를 함유시킬 필요가 없다. 그 때문에, 박편형 광휘재(52)가 착색 안료의 아래로 잠입하여 들어가지 않아, 한층 더 효과적으로 광휘감을 나타낼 수 있다. Thus, since the interference | reflection color of a complex reflection can be exhibited by the flaky
그런데, 광휘감을 나타내는 박편형 광휘재(52)는 이것에 대하여 직각에 가까운 각도로부터 입사하는 광은 효과적으로 반사시킬 수 있지만, 예를 들면, 10 내지 20°정도의 입사각으로 입사하는 광은 거의 반사시킬 수 없다는 결점을 갖고 있다. By the way, the flake-shaped
그 때문에, 이 박편형 광휘재(52)의 결점을 보충하기 위해서, 본 예의 건축판(1)에 있어서는 클리어 도막을, 박편형 광휘재(52)를 함유하는 광휘 클리어층(5)과 표면 클리어층(6)의 2층의 클리어층에 의해 형성하였다. 이것에 의해, 박편형 광휘재(52)가 광휘성을 발휘하지 않는 입사각의 광에 대해서는 중도층(4) 및 표면 클리어층(6)에 의한 반사를 이용하여, 중도층(4)의 색을 반영한 색채의 광휘감을 발휘시키도록 하고 있다. Therefore, in order to compensate for the drawback of this flaky
또한, 종래의 건축판에 있어서, 박편형 광휘재에 의해 광휘감이 있는 색채를 발색시키기 위해서는 박편형 광휘재에 대하여 여러가지의 색채를 나타내는 안료를 사용하였다. 그 때문에, 종래의 건축판에 있어서는 박편형 광휘재는 안료의 색채를 반영한 색채를 나타내었다. In addition, in the conventional building board, in order to develop the color with a bright feeling with a flaky bright material, the pigment which shows various colors with respect to a flaky bright material was used. Therefore, in the conventional building board, the flaky bright material exhibited the color reflecting the color of the pigment.
이것에 대하여, 본 예의 건축판(1)에 있어서는 안료를 사용하지 않고, 중도층(4)의 색채를 이용하여, 박편형 광휘재(52)에 광휘감이 있는 색채를 발색시키고 있다. 즉, 중도층(4)에 의해서 반사되어, 박편형 광휘재(52)를 통과하여 출사하는 광은 중도층(4)의 색채를 반영하여 발색할 수 있다. On the other hand, in the
그 때문에, 본 예의 건축판(1)에 있어서는 안료가 불필요해지고, 중도층(4)의 색채를 필요에 따라서 적절하게 변경함으로써, 변경한 중도층(4)의 색채에 따른 색채를 나타낼 수 있다. Therefore, in the
그 때문에, 본 예의 건축판(1)의 표면은 대부분의 경사방향에서 보아도 광휘감을 나타낼 수 있고, 복잡한 반사의 간섭색을 나타낼 수 있다. 그리고, 상기 건축판(1)의 제조방법에 의하면, 이와 같이 우수한 작용 효과를 나타내는 건축판(1)을 용이하게 제조할 수 있다. Therefore, the surface of the
또한, 광휘 클리어층(5)은 중도층(4)의 요철 표면에서의 볼록부(411)에 형성하고 있고, 오목부(213)에는 거의 형성하지 않았다. 그 때문에, 고가의 박편형 광휘재(52)의 사용량을 줄일 수 있다. In addition, the bright
또한, 건축판(1)의 표면의 전체는 표면 클리어층(6)에 의해서 덮여 있어, 이 표면 클리어층(6)에 의해, 건축판(1)의 표면의 열화를 효과적으로 억제할 수 있다. In addition, the whole surface of the
본 발명에 따른 건축판에 의하면, 대부분의 경사방향에서 보아도 광휘감을 나타낼 수 있고, 복잡한 반사의 간섭색을 나타낼 수 있다는 효과를 제공한다. According to the building plate according to the present invention, even when viewed in the most inclined direction, it can exhibit a bright feeling, it can provide the effect of the interference color of a complex reflection.
Claims (4)