KR20060110171A

KR20060110171A - The step on fame manufature method and the goods for stair that have non-slip

Info

Publication number: KR20060110171A
Application number: KR1020050032418A
Authority: KR
Inventors: 이수언
Original assignee: 주식회사 수리산업
Priority date: 2005-04-19
Filing date: 2005-04-19
Publication date: 2006-10-24

Abstract

A manufacturing method of a stepboard for stairs having non-slips is provided to make construction simple and easy by shaping a stepboard and a non-slip coupling plate separately and constructing concrete stairs, and to improve the efficiency of post management by replacing worn or damage non-slips. A manufacturing method of a stepboard for stairs having non-slips comprises the steps of: injection-molding a non-slip coupling plate, which has one or more non-slip couplers having a coupling groove and many fixing pieces, for forming on a concrete stepping plate in one using synthetic resins; preparing concrete materials by mixing 50~60 percent crushed stone, 20~30 percent white cement, 20~30 percent crushed stone powder and 20~30 percent water using a mixture; shaping a stepboard by installing and setting up the non-slip coupling plate to the inner front of a mold and pouring the prepared concrete materials; removing moisture contained in the mold by compressing the concrete materials in the mold using a presser at a pressure of 200 kg/cm and vibrating the mold; stripping off the stepboard from the mold and curing naturally or compulsively using steam or heat; grinding the exposed top and front of the stepboard after installing on stairs; and installing non-slips to the non-slip coupler of the stepboard through the coupling groove.

Description

The step on fame manufature method and the goods for stair that have non-slip}

도 1은 본 발명에 관한 계단용 콘크리트 디딤평판의 제조공정도1 is a manufacturing process diagram of the concrete stepping plate for stairs according to the present invention

도 2는 본 발명에 의해 시공된 계단의 단면구성도Figure 2 is a cross-sectional configuration diagram of the stairs constructed by the present invention

도 3은 본 발명에 의해 제조된 콘크리트 디딤평판의 사시도Figure 3 is a perspective view of the concrete stepping plate produced by the present invention

도 4는 도4의 일부측단면구성도4 is a partial side cross-sectional configuration of FIG.

도 5는 본 발명 디딤평판의 연마전 상태의 일부사시도Figure 5 is a partial perspective view of the pre-polishing state of the stepping plate of the present invention

도 6은 도5의 일부 측단면구성도6 is a partial side cross-sectional view of FIG.

도 7은 본 발명 논슬립체결판의 사시도7 is a perspective view of the non-slip fastening plate of the present invention

도 8은 도7의 측단면구성도8 is a side cross-sectional view of FIG.

도 9는 본 발명 디딤평판에 논슬립을 체결하는 상태도9 is a state diagram of fastening the non-slip to the tread plate of the present invention

도 10은 내지 도13은 본 발명 디딤평판의 제조과정도10 to 13 is a manufacturing process of the stepping plate of the present invention

도 14는 본 발명의 제조과정에서 연마전의 상태도14 is a state diagram before polishing in the manufacturing process of the present invention

도 15는 본 발명의 제조과정에서 연마되어 완성된 상태도15 is a state diagram polished and completed in the manufacturing process of the present invention

도 16은 본 발명의 다른 실시도16 is another embodiment of the present invention

도 17 내지 도 18은 본 발명 논슬립의 다른 실시도17 to 18 is another embodiment of the present invention non-slip

도 19는 본 발명 논슬립의 확대도19 is an enlarged view of the present invention non-slip

도 20은 본 발명 논슬립체결판의 다른 실시도.20 is another embodiment of the non-slip fastening plate of the present invention.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

100:콘크리트 디딤평판 200:챌판 100: concrete stepping plate 200: challenge plate

10:논슬립체결판 11:체결홈10: Non-Slip Fastener 11:

12:논슬립체결구 13,14:고정편12: Non-slip fasteners 13, 14: fixed

15:절취홈 20,20a,20b:논슬립15: cutting groove 20, 20a, 20b: non-slip

21:돌출편 M:금형21: protrusion piece M: mold

본 발명은 논슬립을 가지는 계단용 디딤평판의 제조방법 및 그 물품에 관한 것으로, 더욱 상세하게는 각종 건물의 계단을 시공시 사용되는 콘크리트 디딤평판을 종석, 백시멘트, 종석파우더 등으로 이루어지는 콘크리트 재료를 금형으로 성형토록 하면서도 이의 상면에는 별도의 논슬립이 체결되는 합성수지 재질의 논슬립체결구를 일체로 성형함으로써 제조를 자동화하여 생산성을 향상시키며 논슬립의 수리와 교체가 용이하여 유지관리가 편리한 논슬립을 가지는 계단용 디딤평판의 제조방법 및 그 물품에 관한 것이다.The present invention relates to a method for manufacturing a stepping plate for staircases having a non-slip, and more particularly, to a concrete stepping plate used when constructing a staircase of various buildings, including a concrete material comprising a stone, a back cement, a stone powder, or the like. Non-slip fasteners made of synthetic resin, which have a separate non-slip fastened to the upper surface thereof, are integrated into the mold to increase productivity by automating manufacturing, and easy to maintain and replace non-slip for staircases. A method for producing a stepping plate and an article thereof.

일반적으로 모든 건물에는 상,하층을 연락하는 복도의 연장으로서 중요한 역할을 하는 계단이 필연적으로 설치되어 있고, 이러한 계단은 외부계단과 내부계단으로 구분될 뿐만 아니라 그 형상이나 사용되는 재료 등에 따라 여러 가지로 분류되고 있다.In general, all buildings are inevitably provided with staircases that play an important role as an extension of the corridor that connects the upper and lower floors. These stairs are not only divided into external stairs and internal stairs, but also vary according to the shape and materials used. Are classified as

그 중에서도 철근콘크리트 계단은 콘크리트를 주재료로 타설되는 계단으로서 가장 보편적으로 널리 시공되고 있으며, 이 경우 계단의 디딤면에는 오르내리는 사용자의 미끄럼을 방지하기 위한 용도로 미끄름막이 즉, 논슬립(nonslip)이 설치되어 있다.Among them, reinforced concrete stairs are the most commonly used construction of concrete as the main material, and in this case, the sliding surface, or non-slip, is used to prevent the sliding of the user. It is installed.

상기 논슬립은 금속재, 타일, 합성수지재 등으로서 계단 디딤면의 끝단 모서리부분에 고정물로 설치되는 것이며, 주로 콘크리트 계단을 타설시 일체로 설치되 거나 또는 시공이 완료된 후 계단의 디딤면에 별도의 부착물로 부착되는 방식으로 설치되고 있다.The non-slip is a metal material, a tile, a synthetic resin material, etc., which is installed as a fixture at the end edge of the stepping surface of the staircase, and is mainly installed as a unit when pouring concrete stairs or as a separate attachment to the stepping surface of the stairs after construction is completed. It is installed in such a way that it is attached.

상기와 같이 사용되는 종래의 논슬립은 주로 금속(황동 등으로 이루어지는 금속)재질로 이루어지면서 표면에는 미끄럼을 방지하기 위하여 적어도 2줄 이상의 다수 줄로 미끄럼방지홈이 형성되는 구조를 가지고 있다.Conventional non-slip used as described above is mainly made of a metal (metal made of brass, etc.) and has a structure in which a non-slip groove is formed in a plurality of lines of at least two lines to prevent slipping on the surface.

그러나 이와 같은 종래의 대표적인 계단용 논슬립은 그 전체가 고가인 황동 등의 금속으로 제조되는 것이기 때문에 제조원가가 많이 소요될 뿐만 아니라 제조도 어려운 단점이 있었다.However, such a typical non-slip for the staircase of the prior art because it is made of a metal, such as brass, which is expensive as a whole, not only takes a lot of manufacturing cost but also had a disadvantage in manufacturing.

즉, 황동은 재질이 가지는 특성으로 인하여 금형에 고정할 수가 없고, 대부분의 제조공정이 수작업으로 이루어지는 것이기 때문에 자동화가 불가능하여 생산성이 저하되는 문제점이 있었을 뿐만 아니라, 그나마도 제조과정 중 연마공정에서 일부가 갈려 나가는 등 불량품도 많이 발생되는 문제점이 있었다.In other words, brass cannot be fixed to a mold due to the characteristics of the material, and since most manufacturing processes are made by hand, automation is impossible and productivity is reduced. There was a problem that a lot of defective products such as grinding.

이러한 문제점외에도 상기 논슬립은 장기간 사용시 녹이 발생되어 변색되거나 또는 마모되기 때문에 특수한 약품을 사용하여 수시로 청소 내지는 연마작업을 행하여야 하는 문제점이 있었다.In addition to these problems, the non-slip has a problem that the cleaning or polishing should be performed at any time using a special chemical because the rust is discolored or worn out during long-term use.

또한 오랜 사용으로 인하여 논슬립이 마모 및 파손되거나 또는 계단으로 부터 분리될 경우에는 논슬립만을 교체하기가 불가능하기 때문에 해당되는 계단을 재시공하여야 하는 등 사후관리에도 많은 문제점이 있었다.In addition, when the non-slip is worn and broken due to long use or separated from the stairs, it is impossible to replace only the non-slip, so there are many problems in post-management, such as the need to reconstruct the corresponding stairs.

한편, 상기와 같은 논슬립은 금속재 뿐만 아니라 경질도기재 타일이나 인조석 등의 석재로 형성되는 구조도 제안되어 실제로 사용되고 있다.On the other hand, the non-slip as described above has been proposed and actually used as a structure formed of a stone, such as hard ceramic tiles or artificial stone.

그러나 이 경우는 사용되는 재료로 인하여 외관상의 차이는 있었을 뿐 전술한 문제점은 여전히 남게 되는 것이고, 더욱이 논슬립이 쉽게 파손되는 등의 문제점이 있었다.However, in this case, there was a difference in appearance due to the materials used, but the above-described problems remain, and moreover, there were problems such as non-slip being easily broken.

그 밖에도 합성수지나 고무 등으로 이루어지는 논슬립을 얇은 판체형으로 성형하여 계단의 디딤면 전단에 부착하여 사용하는 구조도 있으나, 이 경우는 서로 다른 재질의 차이로 인하여 논슬립을 부착하기가 쉽지 않을 뿐만 아니라, 그 두께만큼 돌출되기 때문에 사고의 위험을 초래하는 문제점도 있었다.In addition, there is a structure in which a non-slip made of synthetic resin or rubber is formed into a thin plate shape and attached to the front of the stepping surface of the stairs, but in this case, it is not easy to attach the non-slip due to the difference in materials. Since it protrudes to the thickness, there is a problem that causes the risk of an accident.

본 발명은 상기와 같은 종래의 여러 가지 문제점을 고려하여 이루어진 것으로, 그 목적은 계단의 한 단에 해당되는 디딤단을 판체로 이루어지는 콘크리트 디딤평판과 챌판을 이용하여 시공토록 하면서도 상기 디딤평판에는 합성수지 재질의 논슬립체결구룰 일체로 성형하여 별도의 논슬립을 체결토록 함으로써 생산을 자동화할 수 있고, 논슬립의 마모나 파손시 교체사용이 가능토록 함으로써 사후관리성을 향상시키도록 하는 논슬립을 가지는 계단용 디딤평판의 제조방법 및 그 물품을 제공함에 있다.The present invention has been made in consideration of the various problems as described above, the purpose of which is to use a concrete stepping plate and a riser plate made of a plate stepping step corresponding to one step of the step while the synthetic resin material on the stepping plate It is possible to automate production by molding the non-slip fastening rule integrally and to make a separate non-slip, and to replace it in the case of wear or damage of the non-slip. To provide a method of manufacturing and the article.

이러한 목적을 달성하기 위한 본 발명은 건물의 계단을 시공함에 있어서, 합성수지 재질로 사출성형되는 논슬립체결구를 콘크리트 디딤평판과 일체로 성형함으로써 달성되는 것으로, 즉, 상기 콘크리트 디딤평판은 종석, 백시멘트, 종석파우더 등으로 이루어지는 콘크리트 재료를 이용하여 사각판체형으로 성형토록 함과 동시 에 그 상면의 전방위치에는 별도의 논슬립이 체결되는 합성수지 재질의 논슬립체결구를 일체로 성형토록 함을 특징으로 하는 것이다.In order to achieve the above object, the present invention is achieved by molding a non-slip fastener, which is injection molded from a synthetic resin material, with a concrete stepping plate integrally, that is, the concrete stepping plate is a keystone, a back cement. , By using a concrete material, such as a keystone powder, to form a rectangular plate body and simultaneously form a non-slip fastener made of a synthetic resin material in which a separate non-slip is fastened at a front position of the upper surface thereof. .

이하에서 본 발명의 제조방법을 포함하는 구성 및 작용을 첨부된 도면에 의하여 상세히 설명하면 다음과 같다.Hereinafter, the configuration and operation including the manufacturing method of the present invention will be described in detail by the accompanying drawings.

첨부된 도면의 도1에서는 본 발명의 제조공정도를 개략적으로 나타내고 있고, 도2는 본 발명에 의해 제조된 디딤평판을 이용하여 계단을 시공한 상태도를 나타내고 있으며, 도3 및 도4 이하에서는 본 발명의 제조방법에 의해 제조되는 제조과정이나 물품을 상세히 나타내고 있다.Figure 1 of the accompanying drawings schematically shows the manufacturing process diagram of the present invention, Figure 2 shows a state diagram of the construction of the stairs using the stepping plate manufactured by the present invention, Figures 3 and 4 below the present invention The manufacturing process or the article manufactured by the manufacturing method of this is shown in detail.

본 발명은 합성수지 재질로 이루어지면서 표면에는 다수 개의 미끄럼방지용 논슬립을 끼우거나 빼낼 수 있도록 하는 논슬립체결판을 사출성형하고, 이의 논슬립체결판을 금형에 셋팅한 후 종석, 백시멘트, 종석파우더 등으로 이루어지는 콘크리트 재료를 타설하며, 이어서 전면과 상면의 필요없는 부분을 연마하여 제거함으로써 상면에는 논슬립이 체결되는 논슬립체결구가 적어도 하나 이상 일체로 형성되는 콘크리트 디딤평판을 제조토록 하는 것이다.The present invention is made of a synthetic resin material injection molding non-slip fastening plate to insert or pull out a plurality of non-slip non-slip on the surface, and after setting the non-slip fastening plate in a mold made of a seedstone, back cement, stone powder, etc. The concrete material is poured, and then, by polishing and removing the unnecessary portions of the front surface and the upper surface, the upper surface is to produce a concrete stepping plate in which at least one non-slip fastener to which the non-slip is fastened is integrally formed.

이러한 콘크리트 디딤평판의 제조단계를 각 공정별로 상세히 설명하면 다음과 같다.The manufacturing steps of the concrete stepping plate will be described in detail for each process as follows.

제1공정(논슬립 체결판 성형공정)1st process (non slip fastening plate forming process)

합성수지 재질을 이용하여 콘크리트 디딤평판에 일체형으로 성형하기 위한 논슬립체결판(10)을 사출성형한다.Non-slip fastening plate 10 for molding integrally to the concrete stepping plate using a synthetic resin material is injection molded.

상기 논슬립체결판(10)은 합성수지로 사출성형되는 것으로, 직사각형의 판체로 형성되면서 횡방향을 따라 체결홈(11)을 가지는 논슬립체결구(12)가 적어도 하나 이상으로 형성되고, 또한 전단과 논슬립체결구(12)의 후면에는 다수 개의 고정편(13)(14)들이 일체로 형성된다.The non-slip fastening plate 10 is injection-molded with synthetic resin, and formed of at least one non-slip fastener 12 having a fastening groove 11 along the transverse direction while being formed of a rectangular plate body, and also having a shear and a non-slip. A plurality of fixing pieces 13 and 14 are integrally formed on the rear surface of the fastener 12.

이러한 논슬립체결판(10)은 콘크리트 디딤평판(100)에 일체로 성형되는 논슬립체결구(12)를 형성하기 위한 소재에 해당되는 것으로, 즉 후술하겠지만 후공정에 의하여 필요없는 일부분(L)은 연마되어 없어지고 논슬립체결구(12)만이 디딤평판(100)내에 매설되는 것과 같은 형태로 남게 되는 것이다.The non-slip fastening plate 10 corresponds to a material for forming the non-slip fastening hole 12 integrally formed on the concrete stepping flat plate 100, that is, as will be described later, a portion (L) which is not necessary by the post process is polished. Only the non-slip fasteners 12 are left in the same shape as buried in the stepping plate 100.

이와 같이 논슬립체결판(10)을 합성수지 재질의 사출물로 성형하는 이유는 논슬립체결구(12)만을 별도로 제조하여 금형(M)에 셋팅한다면, 이를 정확한 위치에 셋팅하기가 어려운 문제점이 있기 때문에 성형을 용이하게 하기 위함이고 성형후에는 필요없는 부분(L)을 연마하여 제거하는 것이다.The reason why the non-slip fastening plate 10 is formed of an injection molding material of synthetic resin is that if the non-slip fastening hole 12 is manufactured separately and set in the mold M, it is difficult to set it in the correct position. This is to facilitate the removal and to remove the unnecessary parts (L) after molding.

한편, 다른 실시예로서 첨부된 도20 에서 보는 바와 같이 논슬립체결판(10)의 연마되어 없어지는 부분(L)을 연마공정시 이를 제거하기 용이하도록 상단의 소정위치에 절취홈(15)을 형성할 수 있다.On the other hand, as shown in the accompanying Figure 20 as another embodiment to form a cutting groove (15) at a predetermined position of the upper end to facilitate the removal of the portion (L) of the grinding non-slip fastening plate 10 during the polishing process can do.

즉, 후술할 연마공정에서 논슬립체결판(10)의 상단 부분(L)은 연마되어 없어지는 부분에 해당되는 것이며, 이 경우 절취홈(15)을 이용하여 필요없는 부분(L)을 용이하게 제거할 수가 있는 것이다.That is, the upper portion L of the non-slip fastening plate 10 corresponds to a portion that is polished and disappeared in the polishing process to be described later. In this case, the unnecessary portion L is easily removed by using the cutting groove 15. You can do it.

한편, 다른 실시예로서 첨부된 도면의 도16에서 보는 바와 같이 상기 논슬립 체결판(10a)의 논슬립체결구(12)를 하나만 형성할 수도 있을 뿐만 아니라 두 개 이상의 다수개로 형성할 수도 있을 것이다.Meanwhile, as another embodiment, as shown in FIG. 16 of the accompanying drawings, not only one non-slip fastener 12 of the non-slip fastening plate 10a may be formed but also two or more.

제2공정(콘크리트 재료 배합공정)2nd process (concrete material mixing process)

본 공정에서는 계단용 콘크리트 디딤평판(100)을 제조하기 위한 재료를 준비하는 단계로서, 종석:50 ∼ 60%, 백시멘트:20 ∼ 30%, 종석파우더:20 ∼ 30%를 적정량의 물로서 믹서기로 충분히 배합한 콘크리트 재료를 준비한다.In the present step, as a step of preparing a material for manufacturing the concrete stepping plate 100 for stairs, a blender: 50 to 60%, back cement: 20 to 30%, stone powder: 20 to 30% as a suitable amount of water mixer Prepare concrete material mixed well with.

이러한 콘크리트 재료는 완성되는 디딤평판(100)의 몸체를 구성하는 것으로, 주로 대리석의 조각으로 이루어지는 종석과 종석파우더를 배합함으로써 제품의 강도보강과 더불어 이들이 외표면으로 표현되어 외관에 따른 제품성을 향상시키게 된다.This concrete material constitutes the body of the finished stepping plate 100, and by combining the keystone and the keystone powder mainly composed of pieces of marble, the strength of the product is expressed together with the external surface, thereby improving the productability according to the appearance. Let's go.

제3공정(성형 공정)3rd process (molding process)

금형(M)의 내부 전면에 사출성형된 논슬립체결판(10)을 설치하여 셋팅한 다음, 준비된 콘크리트 재료를 부어서 디딤평판(100)을 성형한다.After installing and setting the injection-molded non-slip fastening plate 10 on the inner front surface of the mold M, the prepared concrete material is poured to mold the stepping plate 100.

상기 논슬립체결판(10)은 그 전단의 고정편(13)이 전면 하부에 위치되는 형태로 설치하되, 성형후의 위치를 감안하여 역방향으로 설치하고, 이어서 준비되는 콘크리트 재료를 금형(M) 내부에 부어서 콘크리트 디딤평판(100)을 성형하는 것이다.The non-slip fastening plate 10 is installed in a shape in which the fixed piece 13 of the front end is located in the lower part of the front surface, and installed in the reverse direction in consideration of the position after molding, and then the concrete material prepared in the mold M Pour is to mold the concrete stepping plate (100).

상기 콘크리트 디딤평판(100)의 크기는 시공하고자 하는 계단의 형태 등에 따라 달리 할 수 있으며, 일예로서 일반적으로 많이 사용되는 제원은 길이 600-700mm 또는 1200-1400mm, 폭 280-320mm, 두께 28-32mm를 갖추어 구성된다.The size of the concrete stepping plate 100 may vary depending on the shape of the stairs to be constructed, etc. As an example, the specifications that are commonly used are 600-700mm or 1200-1400mm long, 280-320mm wide, and 28-32mm thick. It is equipped with.

또한, 상기 논슬립체결판(10)의 체결홈(11)에는 별도의 기본형 논슬립(20)을 미리 체결한 상태에서 성형하므로 성형과정에서 그 형태가 뒤틀리는 것을 최대한 방지할 수 있다.In addition, since the non-slip fastening plate 10 of the non-slip fastening plate 10 is molded in a state in which a separate basic non-slip 20 is fastened in advance, the shape of the non-slip fastening plate 10 can be prevented as much as possible.

제4공정(진동압축공정)4th process (vibration compression process)

금형(M)내의 콘크리트 재료를 200kg/㎠의 프레스로 압착함과 동시에 금형(M)을 진동시켜 콘크리트 재료속에 포함된 수분을 제거한다.While pressing the concrete material in the mold (M) with a press of 200 kg / cm 2, the mold (M) is vibrated to remove moisture contained in the concrete material.

상기와 같이 수분을 강제적으로 제거하는 것은 보다 빠른시간내에 양생이 이루어지게 하는 것으로, 금형(M)내에 여과포 등을 설치한 상태에서 프레스로 압착하여 수분을 제거하되, 콘크리트 재료 내에 수분이 약25 - 45% 정도 유지되도록 하는 것이 바람직하다.Forcibly removing the water as described above is to allow curing to occur within a faster time, by pressing in a state in which the filter cloth, etc. installed in the mold (M) by pressing to remove the water, the moisture in the concrete material It is desirable to maintain about 45%.

이때, 상기 제조하고자 하는 디딤평판(100)의 길이가 긴 경우에는 예를 들어 1200mm 이상인 경우에는 휨의 방지를 위하여 철근을 넣어야 하는 것이 요구되며, 이 경우에는 압축(프레스)과정을 생략할 수 있다.In this case, when the length of the stepping plate 100 to be manufactured is long, for example, 1200 mm or more, it is required to put reinforcing bars in order to prevent bending, and in this case, the compression (press) process may be omitted. .

제5공정(양생공정)5th process (cure process)

금형(M)내의 재료속에 포함된 수분을 강제적으로 제거한 후에는 금형(M)으로 부터 탈형하여 이를 양생한다.After forcibly removing the moisture contained in the material in the mold (M), it is demolded from the mold (M) to cure it.

이러한 양생방법은 여러 가지 조건에 따라 달리할 수 있는 것으로, 자연상태에서 약 3일정도 양생하는 자연양생방법이 가장 바람직하나, 스팀이나 열 등을 이용하여 강제적으로 양생하는 스팀(Steam)양생 방법을 택할 수도 있다.This curing method may vary according to various conditions. The natural curing method of curing for about three days in a natural state is most preferable, but the steam curing method of forcibly curing using steam or heat is used. You can also choose.

제6공정(연마공정)6th process (polishing process)

전술한 공정에서 금형(M)을 이용하여 성형되는 디딤평판(100)의 양생이 완료되면, 계단에 시공후 외부로 보이는 부분인 상면과 전면을 연마한다.When the curing of the stepping flat plate 100 formed by using the mold (M) in the above-described process is completed, the upper surface and the front surface, which is visible to the outside after the construction on the stairs are polished.

이러한 연마작업은 디딤평판(100)에 매설되는 형태로 성형된 논슬립체결판(10)의 논슬립체결구(12)를 제외한 나머지 필요없는 부분(L)은 연마하여 제거하는 것으로, 즉, 상기 상면과 전면의 제거부분(L)을 연마하고 나면 체결홈(11)을 가지는 논슬립체결구(12)만이 남게 되면서도 그 표면이 매끄러움과 동시에 종석이 부분적으로 나타나게 되어 아름다운 형태를 유지하게 되는 것이다.This polishing operation is to remove the unnecessary portion (L) except for the non-slip fasteners 12 of the non-slip fastening plate 10 formed in a form embedded in the tread flat plate 100, that is, the upper surface and After polishing the removal portion (L) of the front surface of the non-slip fastener (12) having a fastening groove 11 is left, while the surface is smooth and at the same time the part of the keystone appears to maintain a beautiful form.

이때, 상기 논슬립체결판(10)은 첨부된 도면의 도20 에서 보는 바와같이 절취홈(15)을 이용하여 제거되어야 할 부분(L)을 손쉽게 제거한 후 연마할 수 있다.At this time, the non-slip fastening plate 10 can be polished after easily removing the portion (L) to be removed using the cutting groove 15 as shown in Figure 20 of the accompanying drawings.

특히, 본 발명은 연마작업을 자동화된 기계를 이용하여 자동으로 행할 수 있음으로써 양산이 가능한 특징을 지니게 되는 것으로, 이에 따라 논슬립이 형성된 계단의 디딤평판(100)을 자동으로 제조할 수 있는 것이다.In particular, the present invention is to have a feature that can be mass-produced by the polishing operation can be automatically performed using an automated machine, it is possible to automatically manufacture the stepping plate 100 of the step is formed non-slip.

제7공정(논슬립 설치공정)7th process (non slip installation process)

콘크리트 디딤평판(100)의 성형이 모두 완료되면 디딤평판(100)의 상부에는 논슬립체결구(12)가 남게 됨으로써 이에 형성된 체결홈(11)을 통하여 별도로 제작되는 논슬립(20)을 끼워서 설치한다.When the molding of the concrete stepping plate 100 is completed, the non-slip fasteners 12 are left at the top of the stepping plate 100 so that the non-slip 20 is separately inserted through the fastening grooves 11 formed therein.

상기 논슬립(20)은 탄성이 매우 좋은 고무 또는 합성수지 등의 재질로 형성되면서도 단순한 형태의 기본형 논슬립(20)을 비롯하여, 몸체의 양측에 돌출편(21)을 가지는 둥근머리형 논슬립(20a)과 마름모머리형 논슬립(20b) 등을 선택하여 사용할 수 있다.The non-slip 20 is formed of a material such as rubber or synthetic resin having a very high elasticity, but also includes a basic non-slip 20 having a simple shape, and a round head non-slip 20a and a rhombus having protrusions 21 on both sides of the body. The head type non-slip 20b etc. can be selected and used.

이러한 경우 기본형의 논슬립(20)은 디딤평판(100)을 제조시에 논슬립체결구(12)의 체결홈(11)내에 끼워서 사용할 수 있음은 물론이고, 실제 사용시 논슬립체결구(12)에 설치하여 사용할 수 있다.In this case, the non-slip 20 of the basic type can be used in the fastening groove 11 of the non-slip fastening hole 12 when manufacturing the stepping flat plate 100, and of course, installed in the non-slip fastening hole 12 during actual use. Can be used.

더욱이 둥근머리형이나 마름모머리형의 논슬립(20a)(20b)들은 고무, 합성수지 등의 재질로 이루어지는 재질의 특성과 함께 돌출편(21)들에 의해 체결홈(11)내에 견고히 고정설치됨으로써 미끄럼을 최대한 방지하게 되는 것이다.Furthermore, the round slip or rhombus non-slips 20a and 20b are slidably installed in the fastening groove 11 by the protrusions 21 together with the characteristics of the material made of a material such as rubber or synthetic resin to slip. It will be prevented as much as possible.

따라서, 상기와 같은 제조공정을 순차적으로 행함으로써 계단에 사용되는 콘크리트 디딤평판(100)의 제조를 완료하게 되는 것이며, 이같이 제조되는 콘크리트 디딤평판(100)은 첨부된 도면의 도2 내지 도4에서와 같은 구조를 가지게 된다.Therefore, by sequentially performing the manufacturing process as described above is to complete the manufacturing of the concrete stepping plate 100 used for the stairs, the concrete stepping plate 100 is prepared in Figures 2 to 4 of the accompanying drawings. It will have the same structure as

상기 콘크리트 디딤평판(100)은 도2에서 보듯이 계단의 한 단에 해당되는 디딤단을 시공시 챌판(200)과 함께 사용되는 것으로, 즉 계단의 한 단을 디딤단(step)이라고 한다면 그 면을 디딤바닥 또는 디딤면(tread)이라고 하고, 그 널을 디딤평판(treadboard:100) 또는 단널이라고 하며, 상기 디딤평판(100)의 뒤쪽에 세로로 막아낸 널을 챌판(riser:200)이라고 할 수 있다. The concrete stepping plate 100 is used with the riser 200 when constructing a stepping step corresponding to one step of the stairs, that is, if one step of the step is a stepping step (step) as shown in FIG. Is called a stepping floor or a tread, and the board is called a treadboard (100) or a unit, and a board which is vertically blocked behind the treading plate (100) is called a riser (200). Can be.

상기와 같이 사용되는 콘크리트 디딤평판(100)은 종석:50 ∼ 60%, 백시멘트:20 ∼ 30%, 종석파우더:20 ∼ 30%를 적정량의 물로 혼합한 콘크리트 재료를 직사각형의 판체로 성형하여 구성되는 것이며, 이의 전면 상부에는 별도의 논슬립(20)이 체결되는 합성수지 재질의 논슬립체결구(12)가 일체로 성형된다.Concrete stepping plate 100 used as described above is formed by forming a rectangular plate body of a concrete material mixed with a suitable amount of water: 50 to 60%, back cement: 20 to 30%, back powder: 20 to 30% Non-slip fasteners 12 made of a synthetic resin material to which a separate non-slip 20 is fastened to an upper portion thereof is integrally molded.

상기 논슬립체결구(12)는 별도로 금형에 의해 사출성형된 후 디딤평판(100) 의 성형시 일체로 성형되는 것이고, 상면에는 횡방향으로 다수개의 체결홈(11)이 형성되어 별도의 논슬립(20)(20a)(20b)이 선택적으로 설치됨과 동시에, 논슬립체결구(12)의 후면에는 다수의 고정편(13)(14)이 돌출형성된다.The non-slip fasteners 12 are separately molded by injection molding and then integrally formed when the stepping flat plate 100 is formed, and a plurality of fastening grooves 11 are formed on the upper surface thereof to form a separate non-slip 20. 20a and 20b are selectively installed, and a plurality of fixing pieces 13 and 14 protrude from the rear surface of the non-slip fastener 12.

따라서, 합성수지 재질로 사출성형되는 논슬립체결구(12)는 콘크리트 재료로 성형되는 디딤평판(100)에 일체로 성형됨으로써 이의 상면에 형성되는 체결홈(11)을 통하여 별도의 논슬립(20)(20a)(20b)을 억지끼움식으로 설치하여 사용하게 되는 것이다.Therefore, the non-slip fastener 12 that is injection-molded with synthetic resin material is separately formed through the fastening groove 11 formed on the upper surface thereof by integrally molding the stepping plate 100 formed of concrete material. ) 20b is to be installed by using the interference fit method.

이때, 상기 디딤평판(100)은 통상에서와 같은 방법으로 챌판(200)과 함께 계단의 골격에 시공되는 것이며, 논슬립(20)(20a)(20b)은 첨부된 도면의 도17 내지 도19에서 더욱 상세히 나타낸 바와 같이 머리부분은 반원형 또는 마름모형으로 형성되면서도 하부의 양측에는 돌출편(21)이 형성되어 설치시 고정력을 제공하게 된다.At this time, the stepping plate 100 is to be constructed in the skeleton of the staircase with the riser 200 in the same manner as usual, non-slip 20, 20a, 20b is shown in Figures 17 to 19 of the accompanying drawings. As shown in more detail, while the head portion is formed in a semi-circular or rhombus, protruding pieces 21 are formed on both sides of the lower portion to provide a fixing force during installation.

특히, 상기 논슬립(20)(20a)(20b)은 사용자에 의해 선택적으로 설치하여 사용할 수 있을 뿐만 아니라 오랜 사용으로 인하여 마모되거나 파손될 경우에는 이를 디딤평판(100)로 부터 손쉽게 분리하여 교체사용할 수도 있는 것이다.In particular, the non-slip 20, 20a, 20b can be selectively installed and used by the user, and when it is worn or damaged due to long use, the non-slip 20, 20a, 20b can be easily separated from the stepping flat plate 100 and replaced. will be.

이상 상세히 설명한 바와 같이 본 발명은 계단의 디딤면에 해당되는 디딤평판과 챌판을 각각 별도로 성형하여 콘크리트 계단을 시공토록 함으로써 시공을 간편하고 손쉽게 할 수 있는 효과를 가지게 된다.As described in detail above, the present invention has an effect that the construction can be easily and easily by molding the stepping plate and the riser plate corresponding to the stepping surface of the stairs separately.

또한, 상기 콘크리트 디딤평판에는 별도의 논슬립이 체결되는 합성수지 재질의 논슬립체결구를 일체로 성형함으로써 제조의 단순화와 더불어 자동화를 기할 수 있어 생산성을 향상시키게 되는 효과를 가지게 된다.In addition, the concrete stepping plate has a non-slip fastener made of a synthetic resin material to which a separate non-slip is integrally molded, thereby simplifying manufacturing and making automation, thereby improving productivity.

특히, 상기 디딤평판의 논슬립체결구를 통하여 별도의 논슬립을 임의대로 끼우고 뺄수 있음으로서 마모나 파손시 손쉽게 교체사용할 수 있음은 물론이고 필요에 따라 다양한 형태의 논슬립을 선택적으로 사용할 수가 있는 효과도 가지게 되는 것이다.In particular, through the non-slip fasteners of the stepping plate can be inserted and pulled out of the separate non-slip arbitrarily, can be easily replaced and replaced when worn or damaged, as well as have the effect of selectively using a variety of non-slip as needed. Will be.

Claims

A non-slip fastening plate forming process of injection molding a non-slip fastening plate having a plurality of fastening grooves on the top surface of which is made of a synthetic material and having a separate non-slip installed thereon;

A concrete material blending step of preparing a mixture of 50 to 60% of a cement, 20 to 30% of a cement and 20 to 30% of a stone powder as an appropriate amount of water;

A molding step of forming a stepping plate by installing the injection-molded non-slip on the inside of the mold and then pouring the prepared concrete material;

Vibration compression process for pressing the concrete material in the mold by pressing and at the same time to vibrate to remove the moisture contained in the concrete material;

A curing process for curing after demolding from the mold;

A polishing step of polishing a top surface and an outer surface of the front surface of the stepping plate to form a smooth surface;

A non-slip installation step of fastening a separate non-slip to the non-slip fastener of the stepping plate: a method for manufacturing a stepping plate for a step with a non-slip comprising:

It is molded into mixed concrete material such as feldspar, back cement, and feldspar powder, and is formed into a plate shape for use as a step surface of the stepping step, which is one step of the stairs,

The upper part of the front is made of hard synthetic resin material, and the upper surface is integrally molded with non-slip fasteners in which the fastening groove is formed in the transverse direction.

A stepping plate for stairs having a non-slip, characterized in that a separate non-slip made of a material such as rubber having good elasticity is installed in the fastening groove of the non-slip fastener.

The method of claim 2,

The non-slip stepping flat plate having a non-slip comprising a plurality of protrusions to be easily fastened in the fastening grooves of the non-slip on both sides of the semi-circular round head on the upper surface.

The method of claim 2,

The non-slip stepping plate for a step having a non-slip comprising an upper surface having a rhombus head.

The method of claim 2,

The stepping step for the step has a stepping plate for the step having a non-slip comprising a non-slip fastener that can be installed at least two or more non-slip on the upper surface.