KR100730340B1

KR100730340B1 - The step on fame manufature method for stair that have non-slip

Info

Publication number: KR100730340B1
Application number: KR1020060030632A
Authority: KR
Inventors: 이수언
Original assignee: 주식회사 수리산업
Priority date: 2006-04-04
Filing date: 2006-04-04
Publication date: 2007-06-20

Abstract

A manufacturing method of a step plate for stairs having a non-slip is provided to increase manufacturability and productivity by shaping a step plate with concrete materials and attaching a synthetic resin non-slip on the concrete step plate to be separable and to increase maintenance efficiency by repairing and replacing a non-slip easily. The manufacturing method of a step plate for stairs having a non-slip comprises the steps of shaping a non-slip fastener provided with a rectangular fastening groove and fixed blades on a concrete step plate using synthetic resins, manufacturing concrete materials by mixing 50-60 weight percent keystone, 20-30 weight percent white cement and 20-30 weight percent keystone powder with the optimum quantity of water in a mixer, shaping a step plate by marking an installation site of a non-slip fastener in a mold, fixing a separate fastening rail by screws or adhesives, fastening the non-slip fastener using the fastening rail and pouring the manufactured concrete materials, removing moisture contained in the concrete materials compulsively by compressing the concrete materials in the mold with a press of 200kg/cm and vibrating the mold, and stripping off the mold and curing the step plate naturally for 3 days or compulsively using steam or heat, grinding the top and the front of the step plate, and inserting a non-slip in the fastening groove of the non-slip fastener unified on the step plate.

Description

The step on fame manufature method for stair that have non-slip}

도 1은 본 발명에 관한 계단용 콘크리트 디딤평판의 제조공정도1 is a manufacturing process diagram of the concrete stepping plate for stairs according to the present invention

도 2는 본 발명에 의해 시공된 계단의 일부구성도2 is a partial configuration of the stairs constructed by the present invention

도 3은 본 발명에 의해 제조되는 콘크리트 디딤평판의 일부사시도Figure 3 is a partial perspective view of the concrete stepping plate produced by the present invention

도 4(a)(b)는 도3의 일부 측단면구성도Figure 4 (a) (b) is a partial side cross-sectional view of Figure 3

도 5는 본 발명의 다른 실시예를 보인 구성도5 is a configuration diagram showing another embodiment of the present invention

도 6은 본 발명의 또다른 실시예를 보인 구성도Figure 6 is a block diagram showing another embodiment of the present invention

도 7은 본 발명 디딤평판의 다른 제조과정도7 is another manufacturing process of the stepping plate of the present invention

도 8은 본 발명 디딤평판의 제조과정도8 is a manufacturing process of the stepping plate of the present invention

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

100:디딤평판 10:논슬립체결구100: stepping plate 10: non-slip fastener

11:체결홈 12:고정날개11: Tightening Home 12: Fixed Wings

20,20a:논슬립 21:바디20,20a: Non-Slip 21: Body

22:중공부 23:가이드면22: hollow part 23: guide surface

24:걸림돌기 25,25a:미끄럼방지면24: Jamming 25,25a: Non-slip surface

25b:요철 25b: unevenness

본 발명은 논슬립을 가지는 계단용 디딤평판의 제조방법에 관한 것으로, 더욱 상세하게는 각종 건물의 계단을 시공시 사용되는 콘크리트 디딤평판을 종석, 백시멘트, 종석파우더로 이루어지는 콘크리트 재료로 성형토록 하면서도 이의 상면에는 논슬립체결구를 일체로 성형하여 별도의 논슬립을 착탈가능토록 구성함으로써 제조성 및 생산성을 향상시키고 논슬립의 수리와 교체가 용이하여 유지관리성을 향상시키도록 한 것이다.The present invention relates to a method for manufacturing a stepping plate for staircases having a non-slip, and more particularly, to form a concrete stepping plate used in the construction of the stairs of various buildings to a concrete material consisting of a stone, a back cement, a stone powder The non-slip fasteners are integrally molded on the upper surface so that a separate non-slip is detachable, thereby improving productivity and productivity, and easy maintenance and replacement of the non-slip to improve maintenance.

일반적으로 모든 건물에는 상,하층을 연락하는 복도의 연장으로서 중요한 역할을 하는 계단이 필연적으로 설치되어 있고, 이러한 계단은 외부계단과 내부계단으로 구분될 뿐만 아니라 그 형상이나 사용되는 재료 등에 따라 여러 가지로 분류되고 있다.In general, all buildings are inevitably provided with staircases that play an important role as an extension of the corridor that connects the upper and lower floors. These stairs are not only divided into external stairs and internal stairs, but also vary according to the shape and materials used. Are classified as

그 중에서도 철근콘크리트 계단은 콘크리트를 주재료로 타설되는 계단으로서 가장 보편적으로 널리 시공되고 있으며, 이 경우 계단의 디딤면에는 오르내리는 사용자의 미끄럼을 방지하기 위한 용도로 미끄름막이 즉, 논슬립(nonslip)이 설치되어 있다.Among them, reinforced concrete stairs are the most commonly used construction of concrete as the main material, and in this case, the sliding surface, or non-slip, is used to prevent the sliding of the user. It is installed.

상기 논슬립은 금속재, 타일, 합성수지재 등으로 형성되어 계단 디딤면의 끝단 모서리부분에 고정물로 설치되는 것이며, 주로 콘크리트 계단을 타설시 일체로 설치되거나 또는 시공이 완료된 후 계단의 디딤면에 별도의 부착물로 부착되는 방식으로 설치되고 있다.The non-slip is formed of a metal material, a tile, a synthetic resin, etc. and is installed as a fixture at the end edge of the stepping surface of the staircase, and is mainly installed integrally when placing the concrete stairs or a separate attachment to the stepping surface of the stairs after construction is completed. It is installed in such a way that it is attached.

상기와 같이 사용되는 종래의 논슬립은 주로 금속(황동 등으로 이루어지는 금속)재질로 이루어지면서 표면에는 미끄럼을 방지하기 위하여 여러 줄의 미끄럼방지홈이 형성되는 구조를 가지고 있다.Conventional non-slip used as described above is mainly made of a metal (metal made of brass, etc.) and has a structure in which a plurality of non-slip grooves are formed on the surface to prevent slipping.

그러나 이와 같은 종래의 대표적인 계단용 논슬립은 그 전체가 고가인 황동 등의 금속으로 제조되는 것이기 때문에 제조원가가 많이 소요될 뿐만 아니라 제조도 어려운 단점이 있었다.However, such a typical non-slip for the staircase of the prior art because it is made of a metal, such as brass, which is expensive as a whole, not only takes a lot of manufacturing cost but also had a disadvantage in manufacturing.

즉, 황동은 재질이 가지는 특성으로 인하여 금형에 고정할 수가 없고, 대부분의 제조공정이 수작업으로 이루어지는 것이기 때문에 자동화가 불가능하여 생산성이 저하되는 문제점이 있었을 뿐만 아니라, 그나마도 제조과정 중 연마공정에서 일부가 갈려 나가는 등 불량품도 많이 발생되는 문제점이 있었다.In other words, brass cannot be fixed to a mold due to the characteristics of the material, and since most manufacturing processes are made by hand, automation is impossible and productivity is reduced. There was a problem that a lot of defective products such as grinding.

이러한 문제점외에도 상기 논슬립은 장기간 사용시 녹이 발생되어 변색되거나 또는 마모되기 때문에 특수한 약품을 사용하여 수시로 청소 내지는 연마작업을 행하여야 하는 문제점이 있었다.In addition to these problems, the non-slip has a problem that the cleaning or polishing should be performed at any time using a special chemical because the rust is discolored or worn out during long-term use.

또한 오랜 사용으로 인하여 논슬립이 마모 및 파손되거나 또는 계단으로 부터 분리될 경우에는 논슬립만을 교체하기가 불가능하기 때문에 해당되는 계단을 재시공하여야 하는 등 사후관리에도 많은 문제점이 있었다.In addition, when the non-slip is worn and broken due to long use or separated from the stairs, it is impossible to replace only the non-slip, so there are many problems in post-management, such as the need to reconstruct the corresponding stairs.

그리고, 상기와 같은 논슬립은 금속재 뿐만 아니라 경질의 도기재 타일이나 인조석 등의 석재로 형성되는 구조도 제안되어 실제로 사용되고 있다.In addition, the non-slip as described above has been proposed and actually used as a structure formed of a stone such as hard ceramic tiles or artificial stone.

그러나 이 경우는 사용되는 재료로 인하여 외관상의 차이는 있었을 뿐 전술한 문제점은 여전히 남게 되는 것이고, 더욱이 논슬립이 쉽게 마모되거나 파손되는 등의 문제점이 있었다.However, in this case, there was a difference in appearance due to the materials used, but the above-described problems remain, and moreover, there were problems such as non-slip wear or breakage.

그 밖에도 합성수지나 고무 등으로 이루어지는 논슬립을 얇은 판체형으로 성형하여 계단의 디딤면 전단에 부착하여 사용하는 구조도 있으나, 이 경우는 서로 다른 재질의 차이로 인하여 논슬립을 부착하기가 쉽지 않을 뿐만 아니라 쉽게 떨어지는 문제점도 있었다.In addition, there is a structure in which a non-slip made of synthetic resin or rubber is formed into a thin plate shape and attached to the front of the stepping surface of the stairs, but in this case, it is not only easy to attach the non-slip due to the difference in materials. There was also a problem falling.

한편, 상기와 같은 종래의 여러 가지 문제점을 고려하여 새로운 개념의 논슬립구조를 가지는 계단용 디딤평판이 제안된 바 있다. On the other hand, in view of the various problems as described above, a stepping plate for a step having a new concept of non-slip structure has been proposed.

이는 특허출원 제10-2005-0032418호로서 계단의 디딤평판을 종석, 백시멘트, 종석파우더로 이루어지는 콘크리트 재료를 금형으로 성형토록 함과동시에 이의 상면에는 합성수지 재질의 논슬립을 착탈가능토록 형성하는 것으로, 합성수지 재질로 사출성형되는 논슬립체결구를 콘크리트 재료와 함께 성형틀에 넣고 성형한 후, 상면과 전면의 일부를 연마기로 연마하여 필요없는 부분을 제거함으로써 디딤평판을 제조하는 것이며, 이같이 제조된 디딤평판을 계단에 시공하여 그 상면에 위치하는 논슬립체결구에 별도의 논슬립을 체결하여 사용토록 하는 것이다.This is a patent application No. 10-2005-0032418, which forms a stepping plate of stairs to form a concrete material consisting of a keystone, a back cement and a keystone powder into a mold, and simultaneously forms a non-slip of a synthetic resin material on the upper surface thereof. The non-slip fastener, which is injection molded from synthetic resin, is put together with a concrete material into a molding mold and molded, and then a part of the top and front surfaces is polished by a polishing machine to remove unnecessary parts. To be used on the staircase and fasten a separate non-slip to the non-slip fastener located on the upper surface.

그러나 이와 같은 종래의 구성은 제조과정에서 다음과 같은 여러 가지 문제점이 야기되고 있다.However, such a conventional configuration has caused a number of problems in the manufacturing process as follows.

즉, 디딤평판의 논슬립체결구는 합성수지 재질로 사출성형되면서도 논슬립이 체결되는 체결홈을 정확한 위치에 셋팅시키기 위한 구조를 가짐에 따라서 사출성형에 따른 작업성은 물론이고 재료가 많이 소요되어 원가상승의 요인이 되는 문제점이 있다. In other words, the non-slip fastener of the stepping plate has a structure to set the fastening groove to which the non-slip is fastened even though the injection molding is made of synthetic resin, so that the material cost is increased as well as the workability due to the injection molding. There is a problem.

또한 연마작업시에도 상기 논슬립체결구의 체결홈을 제외한 다른 부분을 전부 연마하여 제거하여야 함에 따라 연마작업이 어려운 문제점이 있고, 실제로 연마작업시 합성수지 재질의 논슬립체결구와 디딤평판의 콘크리트 부분을 동시에 연마하여야 함으로써 고성능의 연마기가 필연적으로 요구됨은 물론이고 많은 쓰레기도 배출되는 등의 문제점이 있다.In addition, the polishing operation is difficult because the other parts except the fastening grooves of the non-slip fasteners are polished and removed, and the non-slip fasteners made of synthetic resin and the concrete part of the stepping plate must be polished at the same time. As a result, a high-performance grinder is inevitably required, and there is a problem that a lot of waste is discharged.

본 발명은 상기와 같은 종래의 여러 가지 문제점을 개선하기 위하여 이루어진 것으로, 그 목적은 계단의 디딤평판을 콘크리트 재료를 이용하여 성형토록 하면서도 상기 디딤평판에는 합성수지 재질의 논슬립체결구룰 일체로 성형하여 별도의 논슬립을 착탈가능토록 구성함으로써 논슬립의 마모나 파손시 교체사용이 가능토록 하는 논슬립을 가지는 계단용 디딤평판의 제조방법을 제공함에 있다.The present invention has been made to improve the various problems as described above, the purpose of which is to form a stepping plate of the step using a concrete material, while the stepping plate is formed by molding a non-slip fastening rule of a synthetic resin material separately By providing a non-slip detachable to provide a method for manufacturing a stepping plate for a step having a non-slip so that the replacement can be used when the non-slip wear or breakage.

이러한 목적을 달성하기 위한 본 발명은 계단의 디딤평판을 종석, 백시멘트, 종석파우더로 이루어지는 콘크리트 재료를 이용하여 사각판체형으로 성형토록 함과 동시에 그 상면의 전방위치에는 별도의 논슬립이 착탈가능토록 체결되는 합성수지 재질의 논슬립체결구를 일체로 성형토록 함으로써 논슬립을 교체 사용할 수 있도록 함을 특징으로 하는 것이다.The present invention for achieving this object is to form a stepping plate of the staircase to form a square plate using a concrete material consisting of a stone, a back cement, a stone powder, and at the same time a separate non-slip is detachable in the front position of the upper surface. The non-slip fastener made of a synthetic resin material is integrally molded so that the non-slip can be replaced.

이하에서 본 발명에 관한 계단의 디딤평판에 따른 실시예를 첨부된 도면에 의하여 상세히 설명하면 다음과 같다.Hereinafter, an embodiment according to the stepping plate of the stairs according to the present invention will be described in detail by the accompanying drawings.

첨부된 도면의 도1에서는 본 발명의 제조공정도를 개략적으로 나타내고 있고, 도2에서는 본 발명이 적용되는 계단의 일부를 사시도로 나타내고 있으며, 도3이하에서는 본 발명 디딤평판의 상세한 구조 및 이의 제조과정 등을 나타내고 있다, Figure 1 of the accompanying drawings schematically show the manufacturing process of the present invention, Figure 2 shows a part of the stairs to which the present invention is applied in a perspective view, and in Figure 3 or less the detailed structure of the stepping plate of the present invention and its manufacturing process Etc.,

상기 도면의 도2에서 부호 100은 계단에 사용되는 디딤평판의 본체를 표시하고 있고, 부호 200은 챌판을 표시하고 있다.In FIG. 2 of the figure, reference numeral 100 denotes a main body of a stepping plate used for stairs, and reference numeral 200 denotes a riser.

상기 디딤평판(100)과 챌판(200)은 판체형으로 형성되어 계단의 외형을 이루게 되고, 종석, 백시멘트, 종석파우더의 콘크리트 재료를 이용하여 견고한 강도를 지니는 인조석으로 성형된다.The stepping flat plate 100 and the riser plate 200 are formed in a plate shape to form an outer shape of the staircase, and are formed of artificial stone having solid strength by using concrete materials such as feldspar, back cement, and feldspar powder.

또 상기 디딤평판(100)은 도면의 도3 및 도4에서 더욱 상세히 나타낸 바와 같이 상부의 표면에는 합성수지 재질로 사출성형되는 적어도 하나 이상의 논슬립체결구(10)가 일체로 매몰되게 형성된다.In addition, the stepping plate 100 is formed to be integrally buried at least one or more non-slip fasteners 10 injection-molded with a synthetic resin material on the upper surface as shown in more detail in Figures 3 and 4 of the drawings.

상기 논슬립체결구(10)는 합성수지 재질로 사출성형되면서도 상부가 개구되는 사각형의 체결홈(11)을 갖추어 구성되고, 양측면에는 디딤평판(100)의 성형시 결합력을 향상시키기 위한 고정날개(12)가 외향 돌출되게 각각 형성된다.The non-slip fastener 10 has a rectangular fastening groove 11 that is open at the top while being injection molded from a synthetic resin material, and fixing blades 12 for improving the bonding force when forming the stepping flat plate 100 on both sides. Are each formed to protrude outwards.

이때, 상기 논슬립체결구(10)는 전술한 바와 같이 계단의 크기나 형태 등을 감안하여 적어도 하나 이상이 일정한 간격으로 설치되며, 이는 디딤평판(100)을 성형시 일체로 성형된다.At this time, the non-slip fastener 10 is installed at least one or more at regular intervals in consideration of the size and shape of the stairs as described above, which is integrally formed when the stepping flat plate 100 is formed.

또한 상기 논슬립체결구(10)의 체결홈(11)에는 유연한 합성수지 또는 고무 등의 재질로 성형되는 별도의 논슬립(20)이 착탈가능토록 설치된다.In addition, the non-slip fastening groove 10 of the non-slip fastener 10 is provided with a separate non-slip 20 that is formed of a material such as flexible synthetic resin or rubber.

상기 논슬립(20)은 논슬립체결구(10)의 체결홈(11)내에 억지끼움식으로 삽입체결되는 바디(21)의 내부에 신축 및 팽창을 용이하게 하는 중공부(22)를 갖추어 구성된다.The non-slip 20 is provided with a hollow portion 22 to facilitate the expansion and expansion in the interior of the body 21 to be inserted into the fastening groove 11 of the non-slip fastener 10 is fitted.

상기 바디(21)는 논슬립체결구(10)의 체결홈(11)내에 완전히 삽입되는 형태로 체결되는 것이며, 이의 내부에 형성되는 중공부(22)는 논슬립(20)이 유연한 합성수지 또는 고무 등의 재질로 형성됨에 따라 신축 및 팽창을 용이하게 이루어지도록 하기 위한 것이다.The body 21 is fastened in a form that is completely inserted into the fastening groove 11 of the non-slip fastener 10, the hollow portion 22 formed therein is made of a non-slip 20 flexible synthetic resin or rubber As it is formed of a material to facilitate the expansion and expansion.

즉, 논슬립(20)을 논슬립체결구(10)의 체결홈(11)내에 삽입 및 분리시에는 중공부(22)로 인하여 바디(21)가 수축되면서 삽입 및 분리가 용이하게 이루어지게 되는 것이며, 이와는 반대로 체결후에는 자체가 가지는 탄성에 의해 원상으로 복귀되어 체결력을 증대시키게 된다.That is, when the non-slip 20 is inserted into and detached from the fastening groove 11 of the non-slip fastener 10, the body 21 is contracted due to the hollow portion 22, and thus the non-slip 20 is easily inserted and separated. On the contrary, after fastening, the fastening force is increased by returning to the original shape by the elasticity of the fastening itself.

또 바디(21)의 하단은 체결을 용이하게 하도록 하는 뽀족한 가이드면(23)이 형성됨과 동시에 양측면에는 체결력을 향상시키도록 하는 걸림돌기(24)가 적어도 하나 이상 다수 개로 돌출되게 형성되고, 상부에는 반원형의 미끄럼방지면(25)이 디딤평판(100)의 상부로 돌출되게 설치된다.In addition, the lower end of the body 21 is formed with a protruding guide surface 23 to facilitate the fastening and at the same time formed on both sides of the engaging projection 24 to improve the fastening force at least one or more protruded, The semicircular anti-slip surface 25 is installed to protrude to the top of the stepping flat plate 100.

상기 가이드면(23)은 뽀족하게 형성됨에 따라 체결이 용이한 것이며, 걸림돌기(24)는 외향으로 돌출되게 형성됨에 따라 논슬립체결구(10)의 체결홈(11)내에 체결시 긴밀하게 밀착되어 그 체결력을 증대시키게 된다.The guide surface 23 is easy to fasten as it is sharply formed, and the locking protrusion 24 is formed to protrude outward so that the guide surface 23 is closely adhered to the fastening groove 11 of the non-slip fastener 10. The tightening force is increased.

또, 상기 미끄럼방지면(25)은 디딤평판(100)의 외부로 노출되는 부분으로서 대략 반원형으로 형성되어 실제적인 논슬립의 기능을 제공하게 되는 것이며, 즉 계단을 오르내리는 사람들에 의해 신발과 접촉되어 미끄럼을 방지하게 된다.In addition, the non-slip surface 25 is a portion exposed to the outside of the stepping plate 100 is formed in a substantially semi-circular shape to provide a function of the actual non-slip, that is, in contact with the shoes by people climbing up and down the stairs It prevents slipping.

한편, 상기와 같은 논슬립(20)은 그 형태에 따라 다른 실시예를 가지게 되는 것으로, 즉 첨부된 도면의 도5 및 도6에서 보듯이 논슬립(20a)은 상면을 마름모 형태의 미끄럼방지면(25a)으로 형성할 수도 있을 뿐만 아니라 이의 상면을 요철(25b)로 형성할 수도 있을 것이고, 또한 도면에서는 상세히 도시하지 않았지만 다른 형태로 구성할 수도 있을 것이다.On the other hand, the non-slip 20 as described above will have a different embodiment according to its shape, that is, as shown in Figures 5 and 6 of the accompanying drawings, the non-slip 20a is a non-slip surface 25a of the rhombus shape It may be formed not only) but also its upper surface may be formed of the unevenness 25b, and may be configured in other forms although not shown in detail in the drawings.

따라서, 상기와 같이 구성되는 본 발명의 디딤평판(100)은 다음과 같은 제조공정에 의해 제조되는 것으로 이의 제조방법을 첨부된 도면에 의하여 상세히 설명하면 다음과 같다.Therefore, the stepping flat plate 100 of the present invention constituted as described above is manufactured by the following manufacturing process and the manufacturing method thereof will be described in detail with reference to the accompanying drawings.

제1공정(논슬립체결구 성형공정)Step 1 (non-slip fastener molding process)

합성수지 재질을 이용하여 콘크리트 디딤평판(100)에 일체형으로 성형하기 위한 논슬립체결구(10)를 성형한다.The non-slip fastener 10 for integrally molding the concrete stepping flat plate 100 is molded using a synthetic resin material.

상기 논슬립체결구(10)는 합성수지로 사출성형되는 것으로, 상부가 개구되는 대략 사각형의 체결홈(11)과 양측면에는 고정날개(12)가 각각 돌출되게 형성된다.The non-slip fastener 10 is injection molded from a synthetic resin, and the fixing blades 12 are formed to protrude on both sides of the fastening groove 11 and the sides of the substantially rectangular upper opening.

제2공정(콘크리트 재료 배합공정)2nd process (concrete material mixing process)

본 공정에서는 계단용 콘크리트 디딤평판(100)을 제조하기 위한 재료를 준비하는 단계로서, 종석:50 ∼ 60중량%, 백시멘트:20 ∼ 30중량%, 종석파우더:20 ∼ 30중량%를 적정량의 물로서 믹서기로 충분히 배합한 콘크리트 재료를 준비한다.In the present step, as a step of preparing a material for manufacturing the concrete stepping plate 100 for stairs, the keystone: 50 to 60% by weight, the back cement: 20 to 30% by weight, the keystone powder: 20 to 30% by weight of the appropriate amount Prepare concrete material mixed well with a blender as water.

이러한 콘크리트 재료는 완성되는 디딤평판(100)의 몸체를 구성하는 것으로, 주로 대리석의 조각으로 이루어지는 종석과 종석파우더를 배합함으로써 제품의 강도보강과 더불어 이들이 외표면으로 표현되어 외관에 따른 제품성을 향상시키게 된다.This concrete material constitutes the body of the finished stepping plate 100, and by combining the keystone and the keystone powder mainly composed of pieces of marble, the strength of the product is expressed together with the external surface, thereby improving the productability according to the appearance. Let's go.

제3공정(성형 공정)3rd process (molding process)

금형(M)의 내부에 논슬립체결구(10)의 설치위치를 표시한 다음, 별도의 체결레일(40)을 스크류나 접착제로 고정설치하고, 이의 체결레일(40)을 이용하여 논슬립체결구(10)를 체결하며, 이어서 준비된 콘크리트 재료를 부어서 디딤평판(100)을 성형한다.Mark the installation position of the non-slip fastener 10 in the mold (M), and then install a separate fastening rail 40 fixed with a screw or an adhesive, and using the fastening rail 40 of the non-slip fastener ( 10) is fastened, and then the prepared concrete material is poured to form the stepping plate 100.

상기 논슬립체결구(10)는 성형후의 위치를 감안하여 체결레일(40)에 역방향으로 설치하게 되는 것이고, 상기 체결레일(40)은 금형(M)의 내부에서 스크류, 접착제 등으로서 고정설치되는 것이다.
이때 상기 논슬립체결구(10)를 금형(M)의 내부에 설치하는 방법은 체결레일(40)을 사용하는 것이나, 이와는 다른 실시예로서 양면테이프(30)를 이용하여 설치할 수도 있다.
또한, 상기 콘크리트 디딤평판(100)의 크기는 시공하고자 하는 계단의 형태 등에 따라 달리 할수 있으며, 일예로서 일반적으로 많이 사용되는 제원은 길이 600-700mm 또는 1200-1400mm, 폭 280-320mm, 두께 28-32mm를 갖추어 구성된다.The non-slip fastener 10 is to be installed in the reverse direction to the fastening rail 40 in consideration of the position after the molding, the fastening rail 40 is fixed to the inside of the mold (M) as a screw, adhesive or the like. .
At this time, the method for installing the non-slip fastener 10 in the mold M is to use the fastening rail 40, but may be installed using the double-sided tape 30 as another embodiment.
In addition, the size of the concrete stepping plate 100 may vary depending on the shape of the stairs to be constructed, etc. As an example, the specifications generally used are 600-700mm or 1200-1400mm long, 280-320mm wide, and 28-thick. It is equipped with 32mm.

삭제delete

제4공정(진동압축공정)4th process (vibration compression process)

금형(M)내의 콘크리트 재료를 200kg/㎠의 프레스로 압착함과 동시에 금형(M)을 진동시켜 콘크리트 재료속에 포함된 수분을 제거한다.While pressing the concrete material in the mold (M) with a press of 200 kg / cm 2, the mold (M) is vibrated to remove moisture contained in the concrete material.

상기와 같이 수분을 강제적으로 제거하는 것은 보다 빠른시간내에 양생이 이루어지게 하는 것으로, 금형(M)내에 여과포 등을 설치한 상태에서 프레스로 압착하여 수분을 제거하되, 콘크리트 재료 내에 수분이 약25 - 45% 정도 유지되도록 하는 것이 바람직하다.Forcibly removing the water as described above is to allow curing to occur within a faster time, by pressing in a state in which the filter cloth, etc. installed in the mold (M) by pressing to remove the water, the moisture in the concrete material It is desirable to maintain about 45%.

이때, 상기 제조하고자 하는 디딤평판(100)의 길이가 긴 경우에는 예를 들어 1200mm 이상인 경우에는 휨의 방지를 위하여 철근을 넣어야 하는 것이 요구되며, 이 경우에는 압축(프레스)과정을 생략할 수 있다.In this case, when the length of the stepping plate 100 to be manufactured is long, for example, 1200 mm or more, it is required to put reinforcing bars in order to prevent bending, and in this case, the compression (press) process may be omitted. .

제5공정(양생공정)5th process (cure process)

금형(M)내의 재료속에 포함된 수분을 강제적으로 제거한 후에는 금형(M)으로 부터 탈형하여 이를 양생한다.After forcibly removing the moisture contained in the material in the mold (M), it is demolded from the mold (M) to cure it.

이러한 양생방법은 여러 가지 조건에 따라 달리할 수 있는 것으로, 자연상태에서 약 3일정도 양생하는 자연양생방법이 가장 바람직하나, 스팀이나 열 등을 이 용하여 강제적으로 양생하는 스팀(Steam)양생 방법을 택할 수도 있다.This curing method may vary according to various conditions. The natural curing method of curing for about 3 days in a natural state is most preferable, but the steam curing method of forcibly curing using steam or heat is used. You can also choose.

제6공정(연마공정)6th process (polishing process)

전술한 공정에서 금형(M)을 이용하여 성형되는 디딤평판(100)의 양생이 완료되면, 계단에 시공후 외부로 보이는 부분인 상면과 전면을 연마한다.When the curing of the stepping flat plate 100 formed by using the mold (M) in the above-described process is completed, the upper surface and the front surface, which is visible to the outside after the construction on the stairs are polished.

이러한 연마작업은 디딤평판(100)을 제조하는 마무리공정으로서 자동화된 기계를 이용하여 자동으로 행할 수 있으며, 연마가 이루어지고 나면 표면이 매끄럽게 형성됨과 동시에 종석이 부분적으로 나타나게 되어 아름다운 형태를 유지하게 되는 것이다.This polishing operation can be performed automatically by using an automated machine as a finishing process for manufacturing the stepping plate 100, and after polishing is performed, the surface is smoothly formed, and at the same time, the part of the stone appears to maintain a beautiful shape. will be.

제7공정(논슬립 설치공정)7th process (non slip installation process)

콘크리트 디딤평판(100)의 성형이 모두 완료되면 디딤평판(100)에 일체로 형성되는 논슬립체결구(10)의 체결홈(11)내에 별도로 제작되는 논슬립(20)을 끼워서 설치한다.When the molding of the concrete stepping plate 100 is completed, the non-slip 20 is separately inserted into the fastening groove 11 of the non-slip fastener 10 formed integrally with the stepping plate 100.

상기 논슬립(20)은 탄성이 매우 좋은 합성수지 또는 고무 등의 재질로 형성되면서도 반원형의 미끄럼방지면(25)을 가지는 것이며, 이러한 형태는 물론이고, 마름모형의 미끄럼방지면(25a)을 가지거나 그 상면에 요철을 가지는 형태 등을 사용할 수 있는 것이다.The non-slip 20 is formed of a material such as a synthetic resin or rubber having a very high elasticity and has a semi-circular anti-slip surface 25, and of course, has a non-slip surface 25a of a rhombus or the like. The form etc. which have an unevenness | corrugation on an upper surface can be used.

상기와 같은 제조공정을 순차적으로 행하여 성형되는 콘크리트 디딤평판(100)은 첨부된 도면의 도2에서 보듯이 계단을 시공시 챌판(200)과 함께 시공되는 것이며, 이때 디딤평판(100)의 상면에는 논슬립(20)이 체결되므로써 계단을 오르내리는 사용자의 미끄러짐을 방지하게 되는 것이다.Concrete stepping plate 100 is formed by sequentially performing the manufacturing process as shown in Figure 2 of the accompanying drawings is to be constructed with the construction plate 200 when the stairs are constructed, the upper surface of the stepping plate 100 The non-slip 20 is fastened to prevent the user from slipping up and down the stairs.

이러한 논슬립(20)은 사용자에 의해 선택적으로 설치하여 사용할 수 있을 뿐만 아니라 오랜 사용으로 인하여 마모되거나 파손될 경우에는 이를 디딤평판(100)으로 부터 손쉽게 분리한 후 다른 것으로 교체사용할 수도 있는 것이다.Such a non-slip 20 can be installed and used selectively by the user, and when it is worn or damaged due to long use, it can be easily separated from the stepping flat plate 100 and then replaced with another one.

이상 상세히 설명한 바와 같이 본 발명은 계단에 사용되는 디딤평판을 종석, 백시멘트, 종석파우더로 이루어지는 콘크리트 재료를 금형으로 성형토록 하면서도 이의 상면에는 합성수지 재질의 논슬립체결구를 일체로 형성함과 동시에 별도의 논슬립을 착탈가능토록 형성함으로써 제조를 자동화하여 생산성을 향상시키게 되는 효과를 가지게 되고, 이와 더불어 논슬립의 수리와 교체 사용이 가능하여 유지관리성을 향상시키게 되는 효과를 가지게 된다.As described in detail above, the present invention allows the stepping plate used for the staircase to form a concrete material consisting of a keystone, a back cement, and a keystone powder into a mold, but simultaneously forms a non-slip fastener made of synthetic resin on the upper surface thereof. By forming the non-slip to be detachable has the effect of improving the productivity by automating the manufacturing, and also has the effect of improving the maintainability by enabling the repair and replacement of the non-slip.

특히, 논슬립이 체결되는 합성수지 재질의 논슬립체결구를 콘크리트 디딤평판에 간편하게 성형할 수 있도록 구성함으로써 제조성의 향상과 더불어 생산성을 향상시키게 되는 효과를 가지게 되는 것이다.In particular, the non-slip fastener made of synthetic resin material to which the non-slip is fastened can be easily formed on the concrete stepping plate, thereby improving productivity and productivity.

Claims

Forming a non-slip fastener formed of a synthetic resin material and having fastening grooves open at the same time, wherein fixed blades are formed on both sides;

A concrete material mixing step of preparing a mixture of the seedstone, the back cement and the seed powder as an appropriate amount of water;

A molding process in which a fastening rail is installed in the longitudinal direction of the mold, the fastening non-slip fastener is fastened therein, and then the prepared concrete material is poured to form a stepping flat plate;

Vibration compression process for pressing the concrete material in the mold by pressing and at the same time to vibrate to remove the moisture contained in the concrete material;

A curing process for curing after demolding from the mold;

A polishing step of smoothly polishing the outer surface of the stepping plate;

A non-slip installation step of fastening a separate non-slip to the non-slip fastener of the stepping plate: a method for manufacturing a stepping plate for a step with a non-slip comprising:

delete