KR100880368B1 - Manufacturing method of artificial cubic stone united with protruding lining mark - Google Patents

Manufacturing method of artificial cubic stone united with protruding lining mark Download PDF

Info

Publication number
KR100880368B1
KR100880368B1 KR1020070076679A KR20070076679A KR100880368B1 KR 100880368 B1 KR100880368 B1 KR 100880368B1 KR 1020070076679 A KR1020070076679 A KR 1020070076679A KR 20070076679 A KR20070076679 A KR 20070076679A KR 100880368 B1 KR100880368 B1 KR 100880368B1
Authority
KR
South Korea
Prior art keywords
joint
artificial stone
stone
mold
manufacturing
Prior art date
Application number
KR1020070076679A
Other languages
Korean (ko)
Inventor
한영찬
Original Assignee
한영찬
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한영찬 filed Critical 한영찬
Priority to KR1020070076679A priority Critical patent/KR100880368B1/en
Application granted granted Critical
Publication of KR100880368B1 publication Critical patent/KR100880368B1/en

Abstract

A method for preparing the artificial stone integrated with the projected lining mark is provided to allow the lining mark to be formed automatically together with construction, thereby reducing the construction period. A method for preparing the artificial stone integrated with the projected lining mark comprises the steps of making a PVC-based artificial stone mold(13) having a lining mark molding part(12) by using the rod-shaped gypsum lining mark(11); and making the mortar-based artificial stone(15) integrated with a projected lining mark(21) by using the artificial stone mold.

Description

돌출 줄눈 일체형 인조석의 제조방법{Manufacturing method of artificial cubic stone united with protruding lining mark}Manufacturing method of artificial cubic stone united with protruding lining mark

본 발명은 돌출 줄눈 일체형 인조석 및 그 제조방법에 관한 것으로서, 더욱 상세하게는 전통 한식 건물 등의 시공 시 사용되는 사고석, 전돌 등과 같은 인조석과 이것에 돌출 줄눈을 일체로 성형하는 제조방법에 관한 것이다. The present invention relates to a protruding joint-integrated artificial stone and a manufacturing method thereof, and more particularly, to a manufacturing method of integrally forming a protruding joint to artificial stone, such as accident stone, stone, and the like used in the construction of a traditional Korean building. .

우리나라에서는 예부터 전통 한식 건물이나 궁궐의 벽체나 담장에 여러 가지 무늬를 놓아 독특한 치례를 하였다.Since ancient times, various patterns have been placed on traditional Korean buildings, palace walls, and fences, making it unique.

그렇게 치례한 벽체나 담장을 꽃담이라고 하며, 지금도 볼 수 있는 옛 궁궐 꽃담은 화려하되 야하지 않고 은근한 멋을 풍긴다.Such a disrespectful wall or fence is called a flower wall, and the old palace flower wall, which can still be seen, does not have to be glamorous but has a subtle style.

두메산골 토담집 주인이 투박한 솜씨로 토담에 꾹꾹박아 놓은 기왓조각의 질박한 무늬에 구수한 한국인의 심성이 그대로 배어 있어 그윽한 정취를 느끼게 한다.The owner of Dumesangol's Todam House, who is clunked with clunky craftsmanship, is immersed in the immaculate pattern of the gilded sculptures.

일반적으로 꽃담은 바닥에 1~3단의 사고석을 쌓고 그 위에 일정 높이의 전돌을 구축하는 형태로 시공을 하고, 현대에 와서도 건물의 외벽이나 축벽을 쌓는데에 사고석과 전돌이 많이 사용되고 있으며, 사고석이나 전돌의 이음매 부분은 돌출 형태의 줄눈으로 마감한다.In general, the wall is constructed in the form of 1 ~ 3 steps of accident seats on the floor, and a certain height stone on the floor, and even in modern times, accident stones and stones are used to build the exterior walls and shaft walls of buildings. The joints of accident seats or masonry are finished with a projecting joint.

여기서, 상기 줄눈은 사고석 및 전돌을 시공할 때 각 단위 블록 사이를 모르타르, 실리콘 등으로 메우는 긴 줄 모양의 마감재로서, 소정의 외관을 조성하는 역할도 하게 된다. Here, the joint is a long string-like finishing material filling the mortar, silicon, etc. between the unit blocks when constructing accident stone and stone, and also serves to create a predetermined appearance.

전통 한식 건물이나 궁궐의 꽃담을 시공하는 경우, 화강석 사고석이나 전돌을 담장에 붙여 놓고, 연결되는 이음새 부분에 돌출되는 줄눈을 현장에서 만들어가는 것이 일반적이다. When constructing a traditional Korean-style building or a flower wall of a palace, it is common to place granite stone or stone on a fence and to make joints projecting on the connecting seams.

이때, 줄눈을 만들기 위해서는 합판이나 얇은 판자에 만들고자 하는 넓이나 모양으로 홈을 파서 빈 공간을 만든 후, 이것을 시공된 사고석이나 전돌 이음새에 대고 빈 공간에 흰색 회나 백 시멘트를 채워 넣고 꼭꼭 누른 다음, 합판을 치우고 다듬으면서 마무리 해 나가는 방법으로 줄눈을 만들고 있다. At this time, in order to make joints, dig a groove into a plywood or a thin board to make an empty space. Then, put it on the constructed accident stone or stone seam, fill it with white ash or white cement and press it tightly. I'm making a joint by removing and trimming.

그러나, 위의 줄눈 시공의 경우 여러 명의 작업자들이 줄눈 한줄 한줄을 담장 전체 면적에 걸쳐 작업을 수행해야 하는 등 전적으로 작업자의 수작업에 의존해야 하므로, 작업이 비효율적일 뿐 아니라 많은 인력과 시간을 필요로 하는 단점이 있다. However, in the case of the joint construction above, it is not only inefficient but also requires a lot of manpower and time since several workers have to rely solely on the manual work of the worker, such as having to work on the entire line of the joint line. There are disadvantages.

특히, 최근의 사극 드라마 제작이 활발해지면서 옛 담장 등을 구현한 세트장의 건축이 많이 이루어지고 있는 상황에서 영구구조물이 아닌 임시 가건물 성격의 세트장에 실제 줄눈 등을 수작업에 의존하여 일일이 시공한다는 것은 효율성 측면에서도 많은 불리한 점이 있다. In particular, with the recent production of historical dramas, the construction of set rooms that embody old fences is being made a lot. There are also many disadvantages.

또한, 사고석 등의 경우 실제 화강석을 그대로 사용함에 따라 사고석에 적합한 형태로 다듬어야 하거나, 재료 수급에 어려움이 있는 등 취급성 측면이나 경제적인 측면에서 불리한 점이 있다. In addition, in the case of accident stone, such as using the actual granite as it is, it is disadvantageous in terms of handling or economic aspects, such as need to be trimmed in a form suitable for accident stone, or difficult to supply materials.

따라서, 본 발명은 이와 같은 점을 감안하여 안출한 것으로서, 화강석 사고석이나 전돌 등을 인조로 만들고, 이때 돌출된 줄눈도 일체형으로 만들어 줌으로써, 사고석 또는 전돌 시공 시 시공과 동시에 자동으로 줄눈이 형성되게 할 수 있고, 이에 따라 경제적으로나 공사기간을 절감 및 단축할 수 있는 돌출 줄눈 일체형 인조석과 이것을 제조하는 방법을 제공하는데 그 목적이 있다. Therefore, the present invention has been devised in view of such a point, by making artificial granite or stone of granite, and at this time, by making the projecting joint integrally, so that joints are automatically formed at the same time of construction of accident stone or stone construction. The purpose of the present invention is to provide a protruding joint-integrated artificial stone and a method of manufacturing the same, which can be economically possible and thus reduce and shorten the construction period.

상기 목적을 달성하기 위한 본 발명의 일 실시예에 따른 돌출 줄눈 일체형 인조석의 제조방법은 실제 사고석으로 사용되는 화강석 사고석 또는 실제 전벽돌과 그 위에 일체 형성되는 돌출 줄눈 성형용 막대형의 석고 줄눈을 이용하여 줄눈성형요부를 갖는 PVC 재질의 인조석 몰드를 제조하는 단계와, 상기 인조석 몰드를 이용하여 돌출 줄눈이 일체형으로 성형된 모르타르 재질의 인조석을 제조하는 단계를 포함하는 것을 특징으로 한다. Method for producing a protruding joint integral artificial stone according to an embodiment of the present invention for achieving the above object is a gypsum joint of the granular granite or actual front brick used as a real accident stone and a bar-shaped gypsum joint formed integrally thereon By using the artificial stone mold of the PVC material having a joint forming recess, and using the artificial stone mold, characterized in that it comprises a step of manufacturing a mortar artificial stone molded protrusion molded integrally.

여기서, 상기 인조석 몰드를 제조하는 단계는 화강석 사고석 또는 전벽돌의 윗면 가장자리에 판재를 이용하여 막대형의 석고 줄눈을 성형한 후 석고 줄눈을 가지는 화강석 사고석 또는 전벽돌의 둘레를 일정높이의 틀 부재로 마감하는 과정과, 상기 틀 부재 내에 실리콘을 투입하여 음각의 줄눈성형요부를 가지면서 한 면이 화강석 또는 전벽돌의 질감을 나타내는 1차 실리콘 몰드를 제조하는 과정과, 상기 1 차 실리콘 몰드를 일정 높이의 틀 부재로 마감한 후 틀 부재 내에 실리콘을 투입하여 양각의 줄눈성형철부를 가지면서 한 면이 화강석 또는 전벽돌의 질감을 나타내는 2차 실리콘 몰드를 제조하는 과정과, 상기 2차 실리콘 몰드를 일정 높이의 틀 부재로 마감한 후 틀 부재 내에 연질 PVC를 투입하여 음각의 줄눈성형요부를 가지면서 한 면이 화강석 또는 전벽돌의 질감을 나타내는 연질 PVC 재질의 인조석 몰드를 제조하는 과정 등을 포함할 수 있다. Here, the step of manufacturing the artificial stone mold is a frame of a certain height around the granite accident stone or front brick having a plaster joint after forming a bar-shaped gypsum joint using a plate on the upper edge of the granite accident stone or front brick The process of finishing with a member, the process of manufacturing a primary silicon mold having a concave joint forming portion by injecting silicon into the frame member, the surface of the granite or the front brick, the surface of the primary silicon mold, and the primary silicon mold After finishing with a frame member of a certain height, the process of producing a secondary silicone mold having a relief of the granite or the front brick with one side having a relief-shaped joint formed by injecting silicon into the frame member, and the secondary silicon mold After finishing with a frame member of a certain height, the soft PVC is injected into the frame member to have a concave joint forming recess. It may include a process for producing the artificial stone molded of a flexible PVC material that represents the texture around the brick.

또한, 상기 인조석 몰드 제조 시 형성되는 막대형의 석고 줄눈은 화강석 사고석 또는 전벽돌의 가장자리 2변에 걸쳐 배치되는 "ㄱ"자 형태나, 화강석 사고석 또는 전벽돌의 가장자리 4변에 걸쳐 배치되는 "ㅁ"자 형태로 성형할 수 있다. In addition, the bar-shaped gypsum joint formed during the manufacture of the artificial stone mold is a "b" shape disposed over two edges of granite accident stone or front brick, or disposed over four edges of granite accident stone or front brick. It may be molded in the form of "ㅁ".

상기 인조석 몰드 제조 시 다수 개의 2차 실리콘 몰드를 하나의 판 위에 배치하는 동시에 각각 일정간격을 유지하도록 하고, 이렇게 배치한 2차 실리콘 몰드들을 일정거리를 두고 일정 높이의 틀 부재로 마감한 후 틀 부재 내에 연질 PVC를 투입하여 각각의 음각의 줄눈성형요부를 갖는 동시에 한 면이 화강석 또는 전벽돌의 질감을 나타내는 다수 개의 독립된 성형부가 있는 연질 PVC 재질의 인조석 몰드를 제조하는 과정을 포함할 수 있다. When the artificial mold is manufactured, a plurality of secondary silicon molds are placed on one plate and maintained at a predetermined interval, respectively, and the secondary silicon molds thus disposed are finished with a frame member having a predetermined height at a predetermined distance and then a frame member. Injecting a soft PVC in the inside may include a process of manufacturing a synthetic PVC mold of a soft PVC material having a plurality of independent molding parts each having a concave forming portion of each intaglio and at one side representing the texture of granite or front brick.

상기 돌출 줄눈을 일체형으로 가지는 인조석을 제조하는 단계는 인조석 몰드의 줄눈성형요부에만 소정의 색상을 갖는 모르타르를 먼저 투입하여 건조시키는 과정과, 줄눈 성형을 위한 모르타르 건조 후 인조석 블럭 몸체를 성형하기 위하여 틀 부재 내에 소정의 색상을 갖는 모르타르를 투입하여 건조시키는 과정을 포함할 수 있다. The step of manufacturing the artificial stone having the protruding joint as a unit is a process for first adding a mortar having a predetermined color to only the joint molding portion of the artificial mold, and drying the mortar for molding the artificial stone block body after drying the mortar for forming the joint. It may include the step of drying by adding a mortar having a predetermined color in the member.

상기 돌출 줄눈을 일체형으로 가지는 인조석을 제조하는 단계는 사고석 질감을 갖는 인조석 블럭 몸체 성형을 위한 모르타르 투입 전 몰드 표면에 흑색소가 혼합된 모르타르를 일정 두께로 분사하여 점박이 효과를 낼 수 있도록 하는 과정을 더 포함할 수 있다. The step of manufacturing the artificial stone having the protruding joints integrally is a process of spraying the mortar mixed with black pigment to a predetermined thickness before applying the mortar for forming the artificial stone block body having the accidental stone texture to a certain thickness. It may further include.

다른 실시예로서 상기 돌출 줄눈을 일체형으로 가지는 인조석을 제조하는 단계는 인조석 몰드의 각 줄눈성형요부에만 소정의 색상을 갖는 모르타르를 먼저 투입하여 건조시키는 과정과, 줄눈 성형을 위한 모르타르 건조 후 인조석 블럭 몸체를 성형하기 위하여 각각의 성형부 내에 소정의 색상을 갖는 모르타르를 투입하여 건조시키는 과정을 포함할 수 있다. In another embodiment, the step of manufacturing the artificial stone having the protruding joint as an integral step may include first drying the mortar having a predetermined color only in each joint molding portion of the artificial mold, and drying the mortar for the joint molding. In order to mold the mortar having a predetermined color in each of the molding portion may include the process of drying.

한편, 상기 목적을 달성하기 위한 본 발명의 일 실시예에 따른 돌출 줄눈 일체형 인조석은 화강석의 질감 또는 전벽돌의 질감을 표면을 나타내면서 그 가장자리에 돌출된 띠 모양의 줄눈을 일체형으로 갖는 모르타르 재질의 직사각형 블럭 형태로 이루어질 수 있다. On the other hand, protruding joint integral artificial stone according to an embodiment of the present invention for achieving the above object is a mortar-shaped rectangle having a strip-shaped joint protruding at the edge of the granite or the front brick texture as a surface integrally It may be made in the form of blocks.

여기서, 상기 돌출된 띠 모양의 줄눈은 직사각형 블럭의 가장자리 2변에 걸쳐 배치되는 "ㄱ"자 형태 또는 직사각형 블럭의 가장자리 4변에 걸쳐 배치되는 "ㅁ"자 형태가 될 수 있다. Here, the protruding band-shaped joint may have a "-" shape arranged over two edges of the rectangular block or a "ㅁ" shape arranged over four edges of the rectangular block.

이상에서 설명한 바와 같이 본 발명은 사고석이나 전돌을 인조석으로 제조하면서 돌출 줄눈도 함께 성형되도록 하는 인조석 제조방식을 제공함으로써, 사고석 이나 전돌 축조 시 별도로 줄눈을 시공하는 작업을 삭제할 수 있고, 이에 따라 작업시간을 단축할 수 있고 인력과 비용을 절감할 수 있는 효과가 있다. As described above, the present invention provides an artificial stone manufacturing method for forming an accident stone or a stone with an artificial stone while also forming a projecting joint, thereby eliminating the task of constructing a joint separately during the construction of the accident stone or a stone, and thus working This can save time and save manpower and money.

특히, 가 건축물 성격을 가지는 드라마 세트장 시공 시나 현대식 건물이지만 한옥전통양식의 이미지를 연출하고자 하는 건축물 내 외장 외관 장식부재로서 유용하게 활용할 수 있는 효과가 있다. In particular, the construction of a drama set or a modern building that has the characteristics of a temporary building, but can be usefully used as an exterior exterior decorative member in a building to produce a traditional Korean-style image.

또한, 사고석이나 전돌을 다수 개의 성형부를 갖는 인조석 몰드로 대량 제조가 가능함으로써, 제조비용을 절감할 수 있는 등 경제적으로 인조 사고석 또는 전돌을 제조할 수 있는 장점이 있다. In addition, it is possible to manufacture a large number of accident stone or stone artificial stone mold having a plurality of molding parts, there is an advantage that can be manufactured economically artificial stone or stone such as to reduce the manufacturing cost.

이하, 첨부한 도면을 참조하여 본 발명의 일 실시예에 따른 돌출 줄눈 일체형 인조석과 이것을 제조하는 방법에 대해 상세히 설명하면 다음과 같다.Hereinafter, with reference to the accompanying drawings will be described in detail with respect to the protruding joint-integrated artificial stone according to an embodiment of the present invention and a method of manufacturing the same.

도 1은 본 발명의 일 실시예에 따른 돌출 줄눈 일체형 인조석의 제조과정을 나타내는 개략도이다. Figure 1 is a schematic diagram showing the manufacturing process of the protruding joint integral artificial stone according to an embodiment of the present invention.

도 1에 도시한 바와 같이, 상기 돌출 줄눈 일체형 인조석은 전통 한식 건물이나 궁궐의 벽체나 담장 등의 재현을 위해 사용되는 것으로서, 돌출된 줄눈을 일체형으로 가지는 모르타르 재질의 직사각형 블럭으로 제조됨에 따라 담장 등의 시공 시 별도의 줄눈 시공 작업을 배제할 수 있는 등 시간이나 노력, 비용 등을 절감하는 측면에서 유용하게 사용될 수 있다. As shown in FIG. 1, the protruding joint-integrated artificial stone is used for reproducing a wall or a fence of a traditional Korean building or a palace, and is manufactured as a rectangular block made of a mortar material having the protruding joint as an integral wall. It can be useful in terms of saving time, effort, and cost, such as eliminating the extra joint construction work.

이를 위하여, 상기 돌출 줄눈 일체형 인조석을 제조하는 방법은 크게 연질 PVC 재질의 인조석 몰드를 제조하는 단계와, 이 인조석 몰드를 사용하여 돌출된 줄눈을 갖는 인조석 제품, 예를 들면 인조 사고석이나 인조 전돌을 제조하는 단계로 이루어져 있다. To this end, the method of manufacturing the protruding joint integral artificial stone largely comprises the step of manufacturing an artificial stone mold made of soft PVC material, the artificial stone product having a projecting joint using the artificial stone mold, for example, artificial accident stone or artificial stone Consists of steps.

먼저, 실제 사고석 또는 전돌로 사용되는 화강석 사고석(10a), 또는 전벽돌(10b)을 준비한다. First, prepare granite accident stone 10a, or front brick 10b used as an actual accident stone or stone.

이때의 화강석 사고석(10a) 또는 전벽돌(10b)은 화강석 질감이나 전벽돌 질감을 얻기 위한 한 면을 제외하고, 나머지 사각 둘레면과 밑면은 편평하게 다듬는 것이 바람직하다. At this time, the granite accident stone 10a or the front brick 10b is preferably flattened with the remaining rectangular circumferential surface and the bottom surface except for one surface to obtain the granite texture or the front brick texture.

다음, 돌출 줄눈 부위를 성형하기 위하여 화강석 사고석(10a)의 화강석 질감이 살아있는 윗면, 또는 전벽돌(10b)의 질감이 살아있는 윗면에 그 가장자리 일부 면적이 남도록 판재(16)를 배치한다. Next, in order to mold the protruding joint, the plate 16 is disposed so that a portion of the edge remains on the upper surface of the granite texture of the granite accident stone 10a, or the upper surface of the texture of the front brick 10b.

상기 돌출 줄눈은 다양한 형태로 성형할 수 있으며, 이에 상응하여 판재(16)의 크기를 적절히 선택하여 여러 크기로 배치할 수 있다. The protruding joint may be molded in various forms, and accordingly, the size of the plate 16 may be appropriately selected and arranged in various sizes.

예를 들면, 화강석 사고석(10a) 또는 전벽돌(10b)의 가장자리 2변에 걸쳐 "ㄱ"자 형태로 배치하거나, 또는 4변에 걸쳐 "ㅁ"자 형태로 배치할 수 있으며, 이에 따라 인조석에 일체로 성형되는 돌출 줄눈도 "ㄱ"자 형태나 "ㅁ"자 형태가 될 수 있다. For example, the granite accident stone 10a or the front brick 10b may be arranged in the shape of “a” on the two sides, or in the form of “ㅁ” on the four sides, and thus the artificial stone The protruding joint formed integrally with the can also be in the form of "a" or "ㅁ".

이렇게 화강석 사고석(10a) 또는 전벽돌(10b) 위에 줄눈성형을 위한 판재(16)의 배치까지 완료되면, 틀 부재(14)로 외곽을 마감한 다음, 판재(16)가 차지하고 있는 면적을 제외한 화강석 사고석(10a) 또는 전벽돌(10b)의 가장자리 면적에 석고를 부어 석고 줄눈(11)을 성형한다. When the plate 16 for joint formation is completed on the granite accident stone 10a or the front brick 10b in this way, the outer surface is finished with the frame member 14, and then the board 16 is excluded. Gypsum is poured into the edge area of the granite accident stone 10a or the front brick 10b to form a plaster joint 11.

위의 과정을 모두 마치면 석고 줄눈(11)을 일체로 갖는 화강석 사고석(10a) 또는 전벽돌(10b)이 만들어진다. After completing the above process, the granite accident stone (10a) or the front brick (10b) having a gypsum joint (11) integrally.

이와 같이 만들어진 화강석 사고석(10a) 또는 전벽돌(10b) 둘레를 일정높이를 갖는, 예를 들면 화강석 사고석(10a) 또는 전벽돌(10b) 보다 높은 틀 부재(14)로 마감한 다음, 틀 부재(14) 내에 실리콘을 투입하여 음각의 줄눈성형요부(12)를 갖는 1차 실리콘 몰드(17)를 제조한다. The granite accident stone 10a or the front brick 10b made in this way is finished with a frame member 14 having a predetermined height, for example, higher than the granite accident stone 10a or the front brick 10b, and then The silicon is injected into the member 14 to produce a primary silicon mold 17 having a negative joint recess 12.

이렇게 제조된 1차 실리콘 몰드(17)에 실리콘 이형제를 골고루 도포한 후, 틀 부재(14)로 마감한 다음, 재차 실리콘을 투입하여 양각의 줄눈성형철부(18)를 갖는 2차 실리콘 몰드(19)를 제조한다. After applying the silicone releasing agent evenly to the primary silicone mold 17 thus prepared, and finished with a frame member 14, and then again the silicon is added to the secondary silicone mold (19) having an embossed joint portion (18) ).

이렇게 만들어진 2차 실리콘 몰드(19)의 둘레를 틀 부재(14)로 마감한 후, 연질의 PVC를 투입하여 음각의 줄눈성형요부(12)를 갖는 인조석 몰드(13)를 제조한다. After the circumference of the secondary silicon mold 19 made in this way with the frame member 14, soft PVC is added to prepare the artificial stone mold 13 having the intaglio joint recess 12.

여기서, 연질 PVC 재질은 통상의 가열방식으로 용융시킨 상태로 틀 부재에 투입할 수 있다. Herein, the soft PVC material may be introduced into the mold member in a state in which the soft PVC material is melted by a normal heating method.

이때의 인조석 몰드(13)가 인조석 제품 제조를 위한 생산용 금형이 된다.At this time, the artificial stone mold 13 becomes a production die for manufacturing artificial stone products.

한편, 다른 실시예로서, 도 2에서는 연질의 PVC 재질로 이루어진 인조석 몰드(13)을 제조하는 다른 예를 보여준다. Meanwhile, as another embodiment, FIG. 2 shows another example of manufacturing the artificial stone mold 13 made of a soft PVC material.

예를 들면, 위의 2차 실리콘 몰드(19)를 다수를 제조하여 일정한 간격을 두고 하나의 철판에 배열한 후, 접착제 등으로 고정시킨다. For example, a plurality of the above-described secondary silicon mold 19 is manufactured and arranged on one iron plate at regular intervals, and then fixed with an adhesive or the like.

이때, 사고석 제조의 경우 4개를 상하 2개씩 1~2센티미터 간격으로 배열 고정하는 것이 바람직하고, 전돌 제조의 경우 10개를 2열로 5개씩 1~2센티미터 간격으로 배열 고정하는 것이 바람직하다. At this time, it is preferable to arrange and fix four pieces at an interval of 1 to 2 centimeters by two at the top and bottom in case of accident stone manufacturing, and it is preferable to arrange and fix the ten at intervals of 1 to 2 centimeters by five in two rows in the case of preparing the projection.

다음, 철판에 배열된 넓이보다 4면이 3센티미터 정도 더 넓고, 실리콘 몰드보다 1센티미터 정도 더 높은 사각의 철판 틀 부재를 둘레에 설치 고정한다.Next, four sides are three centimeters wider than the width arranged on the iron plate, and a square iron plate frame member about one centimeter higher than the silicon mold is installed and fixed around.

즉, 다수 개의 2차 실리콘 몰드(19)를 하나의 판 위에 배치하되, 서로 간은 1센티미터의 간격을 유지하도록 하고, 이렇게 배치한 2차 실리콘 몰드(19)들을 사방 외곽쪽으로 3센티미터의 거리를 두고 틀 부재(14)로 마감한다. That is, a plurality of secondary silicon molds 19 are arranged on one plate, and the distance between each other is maintained by 1 centimeter, and the secondary silicon molds 19 thus arranged are spaced three centimeters outwards. The frame member 14 is finished.

틀 부재의 설치 고정을 완료한 후, 연질의 PVC 재질을 투입하여 굳은 다음 틀 부재를 해체하면, 각각의 줄눈성형요부(12)를 포함하는 다수 개의 성형부(20)를 갖는 인조석 몰드(13)를 구할 수 있다. After the installation and fixing of the frame member is completed, a soft PVC material is added and solidified, and then the frame member is dismantled, and the artificial stone mold 13 having a plurality of molded parts 20 including respective joint molding recesses 12 is formed. Can be obtained.

이때의 인조석 몰드(13)에 있는 각각의 성형부(20)는 하나하나 독립된 형태가 되면서 외곽틀을 자연스럽게 갖게 되므로서, 제품 생산시 별도의 틀 부재 등을 사용하지 않고 직접 성형부 내에 모르타르를 투입하는 방식으로 제품을 생산할 수 있다. At this time, each molded part 20 in the artificial stone mold 13 becomes an independent form one by one, thereby naturally having an outer frame, so that mortar is directly injected into the molded part without using a separate frame member or the like when producing a product. Can be produced in such a way.

위와 같이 제조된 연질 PVC 재질의 인조석 몰드(13)는 인조사고석 제품을 대량 제조하기 위한 생산용 몰드로서, 이 몰드의 가장자리에는 제품의 줄눈 성형을 위한 음각의 줄눈성형요부(12)가 갖추어져 있다. The artificial PVC mold 13 manufactured as described above is a production mold for mass production of irradiated stone products, and an intaglio joint forming recess 12 for joint forming of the product is provided at the edge of the mold. .

다음, 상기 인조석 몰드(13)를 이용하여 돌출된 줄눈이 일체로 형성되어 있는 인조석을 제조하는 단계를 수행한다. Next, a step of manufacturing an artificial stone in which the protruding joint is integrally formed using the artificial stone mold 13 is performed.

이를 위하여, 음각의 줄눈성형요부(12)를 가지는 인조석 몰드(13)에 줄눈성형요부(12) 내에만 얻고자 하는 줄눈의 색상으로 배합된 모르타르를 투입하여 건조시킨다. To this end, a mortar blended with the color of the joint to be obtained only in the joint molding recess 12 is added to the artificial stone mold 13 having the intaglio joint recess 12.

계속해서, 줄눈성형요부(12)에 투입된 모르타르가 건조되면, 틀 부재(14) 또는 성형부(20) 내에 얻고자 하는 색상의 색소가 배합된 모르타르를 투입하여 양생시킨 후, 몰드에서 분리하여 건조시키면, 돌출된 줄눈(21)이 일체로 형성되어 있는 인조석(15)을 제조할 수 있다. Subsequently, when the mortar put into the joint molding recess 12 is dried, the mortar in which the pigment of the color desired to be obtained is put into the mold member 14 or the molding unit 20 is cured, and then separated from the mold and dried. In this case, the artificial stone 15 protruding joint 21 is integrally formed.

즉, 표면은 화강석의 질감 또는 전벽돌의 질감을 나타내고 가장자리에는 돌출된 띠 모양의 줄눈을 일체형으로 갖는 모르타르 재질의 직사각형 블럭 형태의 인조석을 제조할 수 있다. That is, the surface of the granite, or the texture of the front brick, and the edge can be manufactured in the form of a rectangular block-shaped artificial stone of mortar material having a strip-like joint projecting.

특히, 사고석을 제조하는 경우 인조석에 보다 더 효과적인 화강석의 질감을 나타내기 위하여 화강석 특유의 표면 질감을 나타내는 점박이 무늬를 표현하는 과정을 더 수행할 수 있다. In particular, when manufacturing accident stone, in order to represent the texture of granite more effective than artificial stone, the process of expressing a spot pattern representing the surface texture peculiar to granite may be further performed.

예를 들면, 줄눈 성형을 위한 모르타르 건조 후, 인조석 블럭 몸체 성형을 위한 모르타르를 투입하게 되는데, 그 전에 몰드 표면에 흑색소가 혼합된 모르타르혹은 화강석스톤코트를 일정 두께로 분사함으로써, 인조석의 표면에 화강석의 거친 질감과 함께 점박이 효과를 표현할 수 있다. For example, after drying the mortar for forming the joint, the mortar for molding the artificial stone block body is introduced, and before the mortar or granite stone coat mixed with black pigment is sprayed to a predetermined thickness, the surface of the artificial stone Along with the rough texture of the granite, the spotting effect can be expressed.

이때, 흑색소가 혼합된 모르타르는 대략 시멘트 대비 20% 정도의 흑색소가 혼합된 모르타르를 본타일 분사기에 넣고 콤프레서를 이용하여 분사하는 방식을 적용할 수 있다. In this case, the mortar mixed with the black pigment may be applied to the mortar mixed with about 20% of the black pigment into the bone tile injector and sprayed using a compressor.

즉, 흑색소가 혼합된 모르타르혹은 화강석스톤코트를 선(先) 분사한 다음, 인조사고석 몸체가 되는 모르타르를 투입함으로써, 화강석 특유의 질감이 잘 나타나는 표면을 갖는 인조 사고석을 얻을 수 있다. That is, by pre-injecting the mortar or granite stone coat mixed with the black pigment, and then by adding the mortar to the artificial stone body, it is possible to obtain an artificial accident stone having a surface showing the unique texture of granite.

여기서, 모르타르를 적절한 비율로 배합하는 방법, 색소를 적당하게 배합하는 방법 등은 인조석 제조와 관련한 당해 기술 분야에서 통상적으로 사용하는 방법이라면 특별히 제한되지 않고 채택될 수 있다. Herein, a method of blending mortar in an appropriate ratio, a method of blending a pigment suitably, and the like may be adopted without particular limitation as long as it is a method commonly used in the art related to artificial stone production.

도 3은 본 발명의 일 실시예에 따른 돌출 줄눈 일체형 인조석을 이용하여 담장을 시공한 형태를 개략도이다. Figure 3 is a schematic view of the construction of the fence using a protruding joint integral artificial stone according to an embodiment of the present invention.

도 3에 도시한 바와 같이, 전통 한식 건물이나 궁궐의 벽체나 담장 등의 구축 시 사고석이나 전돌은 기존 벽체(100)에 사고석과 전돌을 부착하는 방법으로 시공할 수 있다. As shown in Figure 3, when building a traditional Korean building or palace wall or fence, accident stone or stone can be constructed by attaching the accident stone and stone to the existing wall (100).

예를 들면, 아래쪽으로 1~3단의 인조석(15)을 쌓은 다음, 그 윗쪽으로 일정 높이의 전돌을 쌓는 방법으로 전통 한식 건물의 담장 등을 구축할 수 있다. For example, a wall of a traditional Korean building can be constructed by stacking artificial stone 15 of one to three steps downward, and then stacking stones of a certain height upward.

이때, 인조 사고석 또는 인조 전돌에 일체형의 돌출된 줄눈이 성형되어 있기 때문에 인조 사구석이나 인조 전돌을 그대로 쌓는 방식으로 부착하기만 하면, 시공 작업을 마칠 수 있고, 결국 종전과 같이 돌출된 줄눈을 별도로 시공해야 하는 수고나 시간, 번거로움 등을 배제할 수 있으므로, 그 만큼 작업을 수월하고 신속하게 할 수 있고, 비용도 크게 절감할 수 있다. At this time, since an integral projecting joint is formed on the artificial accident stone or artificial stone, simply attaching the artificial sand dune or artificial stone in such a manner as to be stacked as it is, the construction work can be completed, and finally, the projecting joint is separated separately as before. Since labor, time, and trouble that need to be constructed can be eliminated, the work can be easily and quickly performed, and the cost can be greatly reduced.

또한, 실제 화강석 사고석 또는 전벽돌을 사용하는 것이 아니라, 제조가 간단하고 경제적인 화강석 질감을 갖는 인조 모르타르 제품을 사용함으로써, 현대식 건물이지만 한옥전통양식이미지를 연출할 수 있는 건축물 내외장재로서나 드라마 등의 세트장의 건축 등에 전통양식에 대한 수요가 늘어나더라도 그 자재의 수급을 원활히 할 수 있고, 또 세트장 건축을 저렴한 비용으로 수행할 수 있다. In addition, by using artificial mortar products with simple and economical granite texture, instead of using real granite accident stone or front brick, it is a modern building, but it is a building interior or exterior material that can produce traditional style image of Hanok. Even if the demand for traditional styles increases, such as the construction of the set, the supply and demand of the materials can be smoothly achieved, and the set construction can be performed at low cost.

도 1은 본 발명의 일 실시 예에 따른 돌출 줄눈 일체형 인조석의 제조과정을 나타내는 개략도Figure 1 is a schematic diagram showing the manufacturing process of the protruding joint integral artificial stone according to an embodiment of the present invention

도 2는 본 발명의 다른 실시 예에 따른 돌출 줄눈 일체형 인조석의 제조과정을 나타내는 개략도Figure 2 is a schematic diagram showing the manufacturing process of the protruding joint integral artificial stone according to another embodiment of the present invention

도 3은 본 발명의 일 실시 예에 따른 돌출 줄눈 일체형 인조석을 이용하여 담장을 시공한 형태를 개략도Figure 3 is a schematic diagram of the construction of the fence using a protruding joint integral artificial stone according to an embodiment of the present invention

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

10a : 화강석 사고석 10b : 전벽돌10a: granite accident stone 10b: front brick

11 : 석고 줄눈 12 : 줄눈성형요부11: plaster joint 12: joint molding

13 : 인조석 몰드 14 : 틀 부재13: artificial stone mold 14: frame member

15 : 인조석 16 : 판재15: artificial stone 16: plate

17 : 1차 실리콘 몰드 18 : 줄눈성형철부17: 1st silicon mold 18: joint molding part

19 : 2차 실리콘 몰드 20 : 성형부19: secondary silicon mold 20: molding part

21 : 돌출 줄눈21: extrude joint

Claims (9)

실제 사고석으로 사용되는 화강석 사고석(10a) 또는 실제 전벽돌(10b)과 그 위에 일체 형성되는 돌출 줄눈 성형용 막대형의 석고 줄눈(11)을 이용하여 줄눈성형요부(12)를 갖는 PVC 재질의 인조석 몰드(13)를 제조하는 단계와, 상기 인조석 몰드(13)를 이용하여 돌출 줄눈(21)이 일체형으로 성형된 모르타르 재질의 인조석(15)을 제조하는 단계를 포함하는 것을 특징으로 하는 돌출 줄눈 일체형 인조석의 제조방법. PVC material having joint forming recesses 12 using granite accident stone 10a or actual front brick 10b used as an actual accident stone and a plaster joint 11 of a protrusion-shaped stick joint formed on it. Producing an artificial stone (13) of the projections, characterized in that it comprises a step of manufacturing the artificial stone 15 of the mortar material in which the protruding joint 21 is integrally molded using the artificial stone mold (13) Method of manufacturing joint integral artificial stone. 청구항 1에 있어서, 상기 인조석 몰드(13)를 제조하는 단계는 화강석 사고석(10a) 또는 전벽돌(10b)의 윗면 가장자리에 판재(16)를 이용하여 막대형의 석고 줄눈(11)을 성형한 후 석고 줄눈(11)을 가지는 화강석 사고석(10a) 또는 전벽돌(10b)의 둘레를 일정높이의 틀 부재(14)로 마감하는 과정과, 상기 틀 부재(14) 내에 실리콘을 투입하여 음각의 줄눈성형요부(12)를 가지면서 한 면이 화강석 또는 전벽돌의 질감을 나타내는 1차 실리콘 몰드(17)를 제조하는 과정과, 상기 1차 실리콘 몰드(17)를 일정 높이의 틀 부재(14)로 마감한 후 틀 부재(14) 내에 실리콘을 투입하여 양각의 줄눈성형철부(18)를 가지면서 한 면이 화강석 또는 전벽돌의 질감을 나타내는 2차 실리콘 몰드(19)를 제조하는 과정과, 상기 2차 실리콘 몰드(19)를 일정 높이의 틀 부재(14)로 마감한 후 틀 부재(14) 내에 연질 PVC를 투입하여 음각 의 줄눈성형요부(12)를 가지면서 한 면이 화강석 또는 전벽돌의 질감을 나타내는 연질 PVC 재질의 인조석 몰드(13)를 제조하는 과정을 포함하는 것을 특징으로 하는 돌출 줄눈 일체형 인조석의 제조방법. The method of claim 1, wherein the step of manufacturing the artificial stone mold 13 is formed by forming a bar-shaped gypsum joint 11 using the plate 16 on the upper edge of the granite accident stone (10a) or the front brick (10b) After finishing the granite accident stone (10a) or the front brick (10b) having a gypsum joint (11) with a frame member 14 of a predetermined height, and the silicon in the mold member 14 A process of manufacturing a primary silicon mold (17) having a joint molding recess (12), the surface of which has a granite or a front brick texture, and a frame member (14) of the primary silicon mold (17) having a predetermined height After the process of manufacturing a secondary silicon mold 19 having the embossed joint portion 18 by embossing the silicon into the frame member 14 and the one surface showing the texture of granite or front brick, After finishing the secondary silicone mold 19 with a frame member 14 of a certain height, Protruding joint, comprising the step of manufacturing a soft PVC artificial stone mold 13 having a concave joint forming portion 12 of the intaglio by injecting soft PVC into the granite or the front brick Method of manufacturing integral artificial stone. 청구항 1 또는 청구항 2에 있어서, 상기 인조석 몰드(13) 제조 시 형성되는 막대형의 석고 줄눈(11)은 화강석 사고석 또는 전벽돌의 가장자리 2변에 걸쳐 배치되는 "ㄱ"자 형태나, 화강석 사고석 또는 전벽돌의 가장자리 4변에 걸쳐 배치되는 "ㅁ"자 형태로 성형하는 것을 특징으로 하는 돌출 줄눈 일체형 인조석의 제조방법. The method according to claim 1 or 2, wherein the rod-shaped gypsum joint 11 formed during the manufacture of the artificial stone mold 13 is a "b" shape or granite accident that is disposed over the two sides of the granite accident stone or front brick A method of manufacturing a protruding joint-integrated artificial stone, characterized in that it is molded in the form of "ㅁ" is arranged over the four sides of the stone or front brick. 청구항 1 또는 청구항 2에 있어서, 상기 인조석 몰드(13) 제조 시 다수 개의 2차 실리콘 몰드(19)를 하나의 판 위에 배치하는 동시에 각각 일정간격을 유지하도록 하고, 이렇게 배치한 2차 실리콘 몰드(19)들을 일정거리를 두고 일정 높이의 틀 부재(14)로 마감한 후 틀 부재(14) 내에 연질 PVC를 투입하여 각각의 음각의 줄눈성형요부(12)를 갖는 동시에 한 면이 화강석 또는 전벽돌의 질감을 나타내는 다수 개의 독립된 성형부(20)가 있는 연질 PVC 재질의 인조석 몰드(13)를 제조하는 과정을 포함하는 것을 특징으로 하는 돌출 줄눈 일체형 인조석의 제조방법. The method according to claim 1 or 2, when the artificial stone mold 13 is manufactured to arrange a plurality of secondary silicon mold 19 on one plate while maintaining a predetermined interval, respectively, the secondary silicon mold (19) ) With a certain distance to finish the frame member 14 of a certain height, and then put a soft PVC in the frame member 14, each having a concave forming recess 12 of each intaglio at the same time one side of the granite or front brick A method of manufacturing a protruding joint-integrated artificial stone, characterized in that it comprises the step of manufacturing a soft PVC artificial stone mold (13) having a plurality of independent molded parts 20 showing the texture. 청구항 1에 있어서, 상기 돌출 줄눈을 일체형으로 가지는 인조석을 제조하는 단계는 인조석 몰드(13)의 줄눈성형요부(12)에만 소정의 색상을 갖는 모르타르를 먼저 투입하여 건조시키는 과정과, 줄눈 성형을 위한 모르타르 건조 후 인조석 블럭 몸체를 성형하기 위하여 틀 부재(14) 내에 소정의 색상을 갖는 모르타르를 투입하여 건조시키는 과정을 포함하는 것을 특징으로 하는 돌출 줄눈 일체형 인조석의 제조방법. The method of claim 1, wherein the manufacturing of the artificial stone having the protruding joint as an integral part comprises first drying the mortar having a predetermined color only in the joint molding recess 12 of the artificial mold 13, and forming the joint. Method of manufacturing a protruding joint integral artificial stone, characterized in that it comprises the step of drying the mortar having a predetermined color into the mold member 14 to form the artificial stone block body after drying the mortar. 청구항 1 또는 청구항 5에 있어서, 상기 돌출 줄눈을 일체형으로 가지는 인조석을 제조하는 단계는 사고석 질감을 갖는 인조석 블럭 몸체 성형을 위한 모르타르 투입 전 몰드 표면에 흑색소가 혼합된 모르타르를 일정 두께로 분사하여 점박이 효과를 낼 수 있도록 하는 과정을 더 포함하는 것을 특징으로 하는 돌출 줄눈 일체형 인조석의 제조방법. The method according to claim 1 or 5, wherein the step of manufacturing the artificial stone having the protruding joints integrally by spraying a mortar mixed with black pigment to a predetermined thickness before adding the mortar for molding the artificial stone block body having an accidental stone texture Method of producing a protruding joint integral artificial stone, characterized in that it further comprises a process to make the spot effect. 청구항 1에 있어서, 상기 돌출 줄눈을 일체형으로 가지는 인조석을 제조하는 단계는 인조석 몰드(13)의 각 줄눈성형요부(12)에만 소정의 색상을 갖는 모르타르를 먼저 투입하여 건조시키는 과정과, 줄눈 성형을 위한 모르타르 건조 후 인조석 블럭 몸체를 성형하기 위하여 각각의 성형부(20) 내에 소정의 색상을 갖는 모르타르를 투입하여 건조시키는 과정을 포함하는 것을 특징으로 하는 돌출 줄눈 일체형 인조석의 제조방법. The method of claim 1, wherein the step of manufacturing the artificial stone having the protruding joints integrally comprises the step of first drying the mortar having a predetermined color only in each of the joint forming recesses 12 of the artificial stone mold 13, and joint molding. Method for producing a protruding joint integral artificial stone, characterized in that it comprises the step of drying by adding a mortar having a predetermined color in each of the forming portion 20 to mold the artificial stone block body after drying the mortar. 삭제delete 삭제delete
KR1020070076679A 2007-07-31 2007-07-31 Manufacturing method of artificial cubic stone united with protruding lining mark KR100880368B1 (en)