KR200401862Y1 - Functional accessories - Google Patents
Functional accessories Download PDFInfo
- Publication number
- KR200401862Y1 KR200401862Y1 KR20-2005-0022019U KR20050022019U KR200401862Y1 KR 200401862 Y1 KR200401862 Y1 KR 200401862Y1 KR 20050022019 U KR20050022019 U KR 20050022019U KR 200401862 Y1 KR200401862 Y1 KR 200401862Y1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- mixed
- fired
- mixture
- present
- Prior art date
Abstract
본 고안은 사용자에게 신진대사를 촉진시키거나 혈액의 약알칼리화, 혈관의 확장, 피로의 회복촉진, 면역력의 향상 등 신체적으로 유익한 효능을 얻을 수 있는 기능성 액세서리에 관한 것이다. The present invention relates to a functional accessory that promotes metabolism to the user or obtains physically beneficial effects such as weak alkaline of blood, expansion of blood vessels, recovery of fatigue, and improvement of immunity.
본 고안은 SiO2 11~12중량%, Al2O3 4~5중량%, Fe 25~30중량%, CaO 0.5~1중량%, MgO 4~5중량%, Na2O 2~3중량%, K2O 0.1~1중량%, TiO2 20~25중량%, Mn 0.1~0.5중량%, Cu 0.01~0.1중량%, S 0.01~0.1중량%, Zn 0.05~0.1중량% 및 토루말린 20~30중량%를 혼합한 1차 혼합물; 1차 혼합물 40∼60중량%에 장석, 토석, 백토, 고령토 및 도석을 미세입자로 분말화한 후 이를 1000∼1300℃에서 소성하여 1:1:1:1 중량비로 혼합한 세라믹 조성물 40∼60중량%를 혼합한 2차 혼합물; 2차 혼합물에 질소가스를 투입하면서 270~380℃의 온도에서 소성한 소성물; 소성물 40~60중량%에 고분자수지를 40~60중량% 혼합시킨 전자파 및 수맥파 흡수 중화 조성물을 실리콘에 혼합하고 170~180℃로 소성한 액상의 혼합물을 소정의 형상을 갖는 금형에 부어 성형한 성형물; 성형물을 인출하여 표면을 연마 가공하여 제조된다.The present invention is 11 to 12% by weight of SiO 2 , 4 to 5% by weight of Al 2 O 3 , 25 to 30% by weight of Fe, 0.5 to 1% by weight of CaO, 4 to 5% by weight of MgO, 2-3% by weight of Na 2 O 2 to , 0.1 to 1% by weight of K 2 O, 20 to 25% by weight of TiO 2 , 0.1 to 0.5% by weight of Mn, 0.01 to 0.1% by weight of Cu, 0.01 to 0.1% by weight of S, 0.05 to 0.1% by weight of Zn and 20 tom of tourmaline Primary mixture which mixed 30 weight%; 40 to 60 wt% of the first mixture of feldspar, earth, clay, kaolin and pottery powder into fine particles, and then fired at 1000 to 1300 ° C. and mixed in a 1: 1: 1: 1 weight ratio. Secondary mixtures mixed by weight; Calcined product calcined at a temperature of 270-380 ° C. while nitrogen gas was added to the secondary mixture; 40-60 wt% of the fired product was mixed with 40-60 wt% of the polymer resin and the water-wave absorbing neutralizing composition in silicon, and the liquid mixture fired at 170-180 ° C. was poured into a mold having a predetermined shape. Moldings; It is produced by taking out the molding and polishing the surface.
Description
본 고안은 사용자에게 신진대사를 촉진시키거나 혈액의 약알칼리화, 혈관의 확장, 피로의 회복촉진, 면역력의 향상 등 신체적으로 유익한 효능을 얻을 수 있는 기능성 액세서리에 관한 것이다.The present invention relates to a functional accessory that promotes metabolism to the user or obtains physically beneficial effects such as weak alkaline of blood, expansion of blood vessels, recovery of fatigue, and improvement of immunity.
일반적으로, 액세서리(Accessory)는 신체의 노출된 부위를 아름답게 가꾸기 위한 것으로 손목에 두르는 팔찌, 발목장식용 네크리스나 앵클릿, 목에 두르는 귀걸이, 귀걸이 등이 이에 포함된다.In general, the accessory (Accessory) to beautifully expose the exposed parts of the body includes a wrist bracelet, ankle necklace or anklet, neck earrings, earrings and the like.
이러한 액세서리의 기능은 전술한 용도 외에도 신앙심을 높이기 위하여 사용되기도 하는데, 이러한 것으로는 불교 신자들이 사용하는 염주 및 천주교신자들의 십자가 귀걸이 등이 있다.In addition to the above-mentioned uses, the function of these accessories may be used to increase faith, such as beads used by Buddhists and cross earrings of Catholics.
따라서, 이러한 액세서리들을 통하여 소속감을 높일 수 있으며, 자신이 속한 계층을 대변하는 데 용이하게 사용될 수 있다.Therefore, it is possible to increase the sense of belonging through these accessories, and can be easily used to represent the hierarchy to which they belong.
한편 음이온은 고원이나, 산림, 폭포와 같이 공기가 깨끗한 환경에 많이 분포하며, 양이온은 배기가스나 공장의 매연, 담배연기, 기계로부터 발생하는 전자파 등에 분포하게 된다.On the other hand, negative ions are widely distributed in clean air such as plateaus, forests, and waterfalls, and positive ions are distributed in exhaust gas, factory smoke, tobacco smoke, and electromagnetic waves generated from machinery.
따라서 인체에 양이온이 증가하게 되면, 혈액의 산성화, 혈관의 수축, 피로의 가중, 면역력의 저하 등이 발생할 수 있으며 이는 곧, 인체의 신진대사를 저하시켜 암의 발생률 등이 높아지게 된다.Therefore, when the cation is increased in the human body, blood acidification, blood vessel contraction, fatigue weighting, immunity may be lowered, and so on, which lowers the metabolism of the human body and increases the incidence of cancer.
결국, 이러한 양이온을 억제하기 위해서는 음이온의 섭취가 이루어져야 하며, 이러한 음이온의 섭취는 고원이나 해안, 전원지대서의 요양 등을 통해 가능하 다.Eventually, in order to suppress such cations, the intake of anions must be made, and the intake of these anions is possible through the plateau, coast, and rural areas.
그러나 현대인들의 생활 환경 등에 있어서 전술한 바와 같이 고원이나 해안, 전원지대를 쉽게 접할 수 없기 때문에 현대인들의 건강적인 측면을 고려하여 음이온 또는 원적외선이 방사되는 성분이 첨가된 액세서리가 제안되고 있으며, 이 외에도 다양한 효능을 갖는 첨가물이 부착된 액세서리가 소비자에게 제공되고 있는 추세인 것이다.However, in the living environment of the modern people, as mentioned above, the plateau, the coast, and the rural area are not easily accessible, and in consideration of the health aspects of modern people, an accessory to which anion or far-infrared radiation is added is proposed. Accessories with additives having efficacy are in the trend of being provided to consumers.
본 고안의 목적은, 사용자에게 신진대사를 촉진시키거나 혈액의 약알칼리화, 혈관의 확장, 피로의 회복촉진, 면역력의 향상 등 신체적으로 유익한 효능을 얻을 수 있는 기능성 액세서리를 제공하는 데 있다.It is an object of the present invention to provide a functional accessory that promotes metabolism or obtains physically beneficial effects such as weak alkaline of blood, expansion of blood vessels, recovery of fatigue, and improvement of immunity.
상기 목적을 달성하기 위한 본 고안에 따르면, SiO2 11~12중량%, Al2O3 4~5중량%, Fe 25~30중량%, CaO 0.5~1중량%, MgO 4~5중량%, Na2O 2~3중량%, K2O 0.1~1중량%, TiO2 20~25중량%, Mn 0.1~0.5중량%, Cu 0.01~0.1중량%, S 0.01~0.1중량%, Zn 0.05~0.1중량% 및 토루말린 20~30중량%를 혼합한 1차 혼합물; 상기 1차 혼합물 40∼60중량%에 장석, 토석, 백토, 고령토 및 도석을 미세입자로 분말화한 후 이를 1000∼1300℃에서 소성하여 1:1:1:1 중량비로 혼합한 세라믹 조성물 40∼60중량%를 혼합한 2차 혼합물; 상기 2차 혼합물에 질소가스를 투입하면서 270~380℃의 온도에서 소성한 소성물; 상기 소성물 40~60중량%에 고분자수지를 40~60중량% 혼합시킨 전자파 및 수맥파 흡수 중화 조성물을 실리콘에 혼합하고 170~180℃로 소성한 액상의 혼합물을 소정의 형상을 갖는 금형에 부어 성형한 성형물; 상기 성형물을 인출하여 표면을 연마 가공한 액세서리인 것을 특징으로 하는 기능성 액세서리를 제공한다.According to the present invention for achieving the above object, SiO 2 11-12% by weight, Al 2 O 3 4-5% by weight, Fe 25-30% by weight, CaO 0.5-1% by weight, MgO 4-5% by weight, Na 2 O 2-3%, K 2 O 0.1-1%, TiO 2 20-25%, Mn 0.1-0.5%, Cu 0.01-0.1%, S 0.01-0.1%, Zn 0.05 ~ Primary mixture of 0.1% by weight and 20-30% by weight of tourmaline; 40 to 60 wt% of the primary mixture, feldspar, earth, clay, kaolin and pottery were powdered into fine particles, and then fired at 1000 to 1300 ° C., and the ceramic composition 40 to mixed at a 1: 1: 1: 1 weight ratio. Secondary mixture mixed with 60% by weight; A fired product fired at a temperature of 270 to 380 ° C. while injecting nitrogen gas into the secondary mixture; 40-60 wt% of the fired product was mixed with 40-60 wt% of the polymer resin, and the water-wave absorbing neutralizing composition was mixed with silicone, and the liquid mixture fired at 170-180 ° C. was poured into a mold having a predetermined shape. One molding; Provided is a functional accessory, which is an accessory obtained by taking out the molding and polishing the surface.
이하 도면을 참조하여 상세히 설명한다. 그러나 이들 도면은 예시적인 목적일 뿐 본 고안이 이에 한정되는 것은 아니다.Hereinafter, with reference to the drawings will be described in detail. However, these drawings are for illustrative purposes only and the present invention is not limited thereto.
도 1은 본 고안의 제1 실시예에 따른 팔찌를 나타낸 사시도이며, 도 2는 본 고안의 제2 실시예에 따른 이동통신 단말기의 액세서리를 나타낸 사시도이다. 또한, 도 3은 본 고안의 제3 실시예에 따른 귀걸이를 나타낸 사시도이다.1 is a perspective view showing a bracelet according to a first embodiment of the present invention, Figure 2 is a perspective view showing an accessory of a mobile communication terminal according to a second embodiment of the present invention. 3 is a perspective view showing an earring according to a third embodiment of the present invention.
도 1 내지 도 3에 도시된 바와 같이 본 고안에 따른 기능성 액세서리는 제1 실시예인 팔찌(100), 제2 실시예인 이동통신 단말기의 액세서리(200), 제3 실시예인 귀걸이(300)와 같은 액세서리에 적용될 수 있다. 물론, 도시되지는 않았지만 반지나 목걸이 등의 액세서리에도 본 고안에서 사용되는 전자파 및 수맥파 흡수 중화 조성물(10)을 이용하여 액세서리를 제작할 수 있다.As shown in FIGS. 1 to 3, the functional accessory according to the present invention is an accessory such as a bracelet 100 as a first embodiment, an accessory 200 of a mobile communication terminal as a second embodiment, and an earring 300 as a third embodiment. Can be applied to Of course, although not shown, accessories such as rings and necklaces may be manufactured using the electromagnetic wave and water wave absorption neutralizing composition 10 used in the present invention.
한편, 본 고안에서 사용되는 전자파 및 수맥파 흡수 중화 조성물(10)은 SiO2 11~12중량%, Al2O3 4~5중량%, Fe 25~30중량%, CaO 0.5~1중량%, MgO 4~5중량%, Na2O 2~3중량%, K2O 0.1~1중량%, TiO2 20~25중량%, Mn 0.1~0.5중량%, Cu 0.01~0.1중량%, S 0.01~0.1중량%, Zn 0.05~0.1중량% 및 토루말린 20~30중량%를 1차 혼합하고, 1차 혼합된 혼합물 40∼60중량%에 장석, 토석, 백토, 고령토 및 도석을 미세입자로 분말화한 후 이를 1000∼1300℃에서 소성하여 1:1:1:1 중량비로 혼합한 세라믹 조성물 40∼60중량%를 2차로 혼합하며, 2차 혼합된 혼합물에 질소가스를 투입하면서 270~380℃의 온도에서 소성한 후, 소성된 혼합물 40~60중량%에 고분자수지를 40~60중량% 혼합하여 제조되게 된다.On the other hand, the electromagnetic wave and water-wave absorption neutralizing composition (10) used in the present invention is 11 to 12% by weight of SiO 2 , 4 to 5% by weight of Al 2 O 3 , Fe 25 to 30% by weight, CaO 0.5 to 1% by weight, MgO 4-5% by weight, Na 2 O 2-3%, K 2 O 0.1-1%, TiO 2 20-25%, Mn 0.1-0.5%, Cu 0.01-0.1%, S 0.01-0.1 First, a mixture of 0.05% to 0.1% by weight of Zn and 20% to 30% by weight of tourmaline, and powdered feldspar, earth, clay, kaolin and pottery stone into fine particles in 40 to 60% by weight of the first mixed mixture After firing it at 1000 to 1300 ° C., 40 to 60% by weight of the ceramic composition mixed at a weight ratio of 1: 1: 1: 1 was mixed in a second manner, and a temperature of 270 to 380 ° C. was added while adding nitrogen gas to the mixture. After calcining at 40 to 60% by weight of the calcined mixture is prepared by mixing the polymer resin 40 to 60% by weight.
여기서, 전술한 전자파 및 수맥파 흡수 중화 조성물(10)은 본원 발명인이 특허출원하여 등록받은 대한민국 특허등록 제491983호 "전자파 및 수맥파 흡수 중화 조성물 및 그 제조방법"에 상세히 설명되어 있다. 상술한 전자파 및 수맥파 흡수 중화 조성물(10)은 전자파와 수맥파에 의한 지자기 교란 현상을 흡수 중화시키는 것은 물론 높은 전자파 흡수율, 원적외선 방사율, 항균작용 및 탈취기능을 갖게 된다.Here, the above-mentioned electromagnetic wave and water-wave absorption neutralizing composition 10 is described in detail in Korean Patent Registration No. 491983, "Electromagnetic Wave and Water-wave Absorption Neutralizing Composition and Manufacturing Method thereof," which the inventors have applied for a patent application. The above-mentioned electromagnetic wave and water-wave absorption neutralizing composition 10 absorbs and neutralizes the geomagnetic disturbance phenomenon caused by the electromagnetic wave and water-wave, as well as having a high electromagnetic wave absorption rate, far-infrared emissivity, antibacterial action and deodorizing function.
이와 같이 본 고안에 따른 기능성 액세서리를 제조하기 위해서는 먼저 전자파 및 수맥파 흡수 중화 조성물(10)과 실리콘을 170~180℃로 소성하게 된다.As such, in order to manufacture the functional accessory according to the present invention, first, the electromagnetic wave and water wave absorption neutralizing composition 10 and silicon are fired at 170 to 180 ° C.
다음, 전자파 및 수맥파 흡수 중화 조성물(10)과 실리콘의 소성물을 액세서리 형상, 예를 들어 팔찌(100), 이동통신 단말기의 액세서리(200) 또는 귀걸이(300)와 같은 형상으로 제조된 금형(미도시)에 부어 액세서리 형상으로 성형하게 되며, 금형으로부터 팔찌(100), 이동통신 단말기의 액세서리(200) 또는 귀걸이(300) 형상으로 성형된 것을 인출하고 표면을 연마함으로써 본 고안에 따른 기능성 액세서리가 제조되는 것이다.Next, a mold made of an electromagnetic wave and water-wave absorption neutralizing composition 10 and a fired product of silicon in an accessory shape, for example, a bracelet 100, an accessory 200 of a mobile communication terminal, or an earring 300. Poured into the shape of the accessory, and the functional accessory according to the present invention is manufactured by drawing the molded part into the shape of the bracelet 100, the accessory 200 of the mobile communication terminal, or the earring 300 from the mold and polishing the surface. Will be.
이때, 전자파 및 수맥파 흡수 중화 조성물(10)과 실리콘의 소성물은 전자파 및 수맥파 흡수 중화 조성물(10) 40~60중량%와 실리콘 40~60중량%로 구성되게 된다.At this time, the firing material of the electromagnetic wave and water-wave absorption neutralizing composition 10 and the silicon is composed of 40 to 60% by weight of the electromagnetic wave and water-wave absorption neutralizing composition 10 and 40 to 60% by weight of silicon.
이는 전자파 및 수맥파 흡수 중화 조성물(10)의 배합비가 40중량% 미만이면 그 효과가 미미하기 때문이며, 60중량%를 초과하면 과량이 되어 실리콘과의 소성이 잘 이루어지지 않게 되기 때문이다.This is because the effect is insignificant when the compounding ratio of the electromagnetic wave and the water-wave absorption neutralizing composition 10 is less than 40% by weight, and when it exceeds 60% by weight, it is excessive and the baking with silicon is not easily performed.
본 고안에서는 전자파 및 수맥파 흡수 중화 조성물(10)과 실리콘을 소성하여 액세서리를 형성하는 것으로 설명하였으나 이외에도 금속 또는 합성수지와 전자파 및 수맥파 흡수 중화 조성물(10)을 소성하여 액세서리를 형성할 수도 있다.In the present invention, the electromagnetic and water-wave absorbing neutralizing composition 10 and silicon have been described as forming an accessory. In addition, the accessory may be formed by firing a metal or synthetic resin and the electromagnetic and water-wave absorbing neutralizing composition 10.
또한 금속, 합성수지 또는 실리콘을 이용하여 액세서리 형상을 성형한 후 이렇게 성형된 팔찌(100), 이동통신 단말기의 액세서리(200) 또는 귀걸이(300) 형상의 외면에 전자파 및 수맥파 흡수 중화 조성물(10)을 소성한 소성물을 코팅하여 액세서리를 제조할 수도 있다.In addition, after forming the accessory shape using a metal, synthetic resin or silicon, the electromagnetic wave and water wave absorption neutralizing composition 10 is formed on the outer surface of the bracelet 100, the accessory 200 of the mobile communication terminal, or the earring 300. The fired material may be coated to manufacture an accessory.
이와 같이, 본 고안이 속하는 기술분야의 종사자는 본 고안이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. As such, those skilled in the art to which the present invention pertains may understand that the present invention may be embodied in other specific forms without changing the technical spirit or essential features thereof.
그러므로 이상에서 기술한 실시 예들은 모든 면에서 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 하고, 본 고안의 범위는 상기 상세한 설명보다는 후술하는 실용신안등록청구범위에 의하여 나타내어지며, 실용신안등록청구범위의 의미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 고안의 범위에 포함되는 것으로 해석되어야 한다.Therefore, the above-described embodiments are to be understood as illustrative and not restrictive in all respects, and the scope of the present invention is represented by the utility model registration claims described below rather than the detailed description, and the scope of the utility model registration claims is as follows. All changes or modifications derived from the meaning and scope and equivalent concepts shall be construed as being included in the scope of the present invention.
이상에서 상세히 설명한 바와 같이 본 고안에 따른 기능성 액세서리에 의하면, 사용자에게 신진대사를 촉진시키거나 혈액의 약알칼리화, 혈관의 확장, 피로의 회복촉진, 면역력의 향상 등 신체적으로 유익한 효능을 얻을 수 있는 효과가 있다.As described in detail above, according to the functional accessory according to the present invention, it is possible to obtain a physically beneficial effect such as promoting metabolism to the user or weakly alkaline the blood, expanding blood vessels, promoting fatigue, and improving immunity. There is.
도 1은 본 고안의 제1 실시예에 따른 팔찌를 나타낸 사시도이다.1 is a perspective view showing a bracelet according to a first embodiment of the present invention.
도 2는 본 고안의 제2 실시예에 따른 이동통신 단말기의 액세서리를 나타낸 사시도이다.2 is a perspective view illustrating an accessory of a mobile communication terminal according to a second embodiment of the present invention.
도 3은 본 고안의 제3 실시예에 따른 귀걸이를 나타낸 사시도이다.3 is a perspective view showing an earring according to a third embodiment of the present invention.
*** 도면의 주요 부분에 대한 부호의 설명 *** *** Explanation of symbols for the main parts of the drawing ***
100; 팔찌 200; 이동통신 단말기의 액세서리100; Bracelet 200; Accessories of Mobile Phones
300; 귀걸이 10; 전자파 및 수맥파 흡수 중화 조성물300; Earrings 10; Electromagnetic and water wave absorption neutralizing composition
Claims (1)