KR20040110242A - Ability barren land brick and the manufacture method for interior finishing material - Google Patents
Ability barren land brick and the manufacture method for interior finishing material Download PDFInfo
- Publication number
- KR20040110242A KR20040110242A KR1020030039459A KR20030039459A KR20040110242A KR 20040110242 A KR20040110242 A KR 20040110242A KR 1020030039459 A KR1020030039459 A KR 1020030039459A KR 20030039459 A KR20030039459 A KR 20030039459A KR 20040110242 A KR20040110242 A KR 20040110242A
- Authority
- KR
- South Korea
- Prior art keywords
- ocher
- pulp
- rosin
- silicon solution
- palm fiber
- Prior art date
Abstract
Description
본 발명은 내장재용 벽돌 및 그 제조방법에 관한 것으로서, 보다 상세하게는 건축물 내장재로 사용되는 벽돌을 제조함에 있어, 황토 및 송진 분말체를 이용하여 벽돌을 제조함에 따라, 항균, 살균, 습도조절 및 원적외선 방출 등의 기능성을 갖는 내장재용 벽돌 및 그 제조방법에 관한 것이다.The present invention relates to a brick for interior materials and a method of manufacturing the same, and more particularly, in the manufacture of bricks used as building interior materials, by manufacturing brick using ocher and rosin powder, antibacterial, sterilization, humidity control and The present invention relates to a brick for interior materials having functionality such as far-infrared emission and a method of manufacturing the same.
일반적으로, 내장재라 함은 내부공간의 기능과 요구되는 각 성능을 충족시키며, 쾌적한 실내환경을 얻기 위한 소재로서, 풍우(風雨) ·한서 ·일사(日射) ·불 ·열 ·소음의 차단구실을 한다. 내장은 그 공법과 사용재료에 따라 구조체 자체로서 내장을 겸하게 하는 경우도 있으나, 주로, 구조체와는 별도로 붙이거나 발라 마무리한다. 대부분 각종 소재로 된 판형재료(板形材料)가 주가 되어 면을 이루게 하는 것이 많으며, 이들의 내구성 ·질감(質感) ·촉감 등 각종 요구성능을 충족시키는 것이어야 한다.In general, interior materials are materials for satisfying the functions of the interior space and required performances, and for obtaining a comfortable indoor environment, and are used as a barrier for wind, rain, heat, fire, heat, and noise. do. Depending on the method of construction and materials used, the interior may also serve as the interior itself, but is usually attached or applied separately from the structure. Mostly, plate-shaped materials made of various materials are mainly used to form cotton, and they must satisfy various performance requirements such as durability, texture, and touch.
이러한, 건축물을 축조함에 있어, 벽체 등의 내장재로 사용되고 있는 벽돌은 일정량의 모래와 시멘트로 이루어져 있으며, 모래와 시멘트를 물과 함께 일정한 비율로 혼합하여 소정의 모양을 갖는 성형틀을 이용하여 육면체 형상을 갖도록 제조된다.In constructing such a building, a brick used as an interior material such as a wall is made of a certain amount of sand and cement, and a sand cube is formed by using a molding mold having a predetermined shape by mixing sand and cement with water at a predetermined ratio. It is manufactured to have.
현재, 황토가 인체에 좋은 영향을 미친다는 것이 알려지면서, 황토방, 황토매트 등의 황토를 이용한 다양한 제품들이 개발되어져 사용되고 있으며, 이는 황토의 특성 즉, 황토에는 마그네슘, 칼륨, 알류미늄, 게르마늄, 칼슘 등이 함유되어 있고, 인체에 유익한 5∼20㎛의 원적외선 파장이 90%이상 방사되는 특성을 갖기 때문이다.Nowadays, it is known that ocher has a good effect on the human body, and various products using ocher such as ocher, and ocher mat have been developed and used, which is characteristic of ocher, that is, magnesium, potassium, aluminum, germanium, calcium, etc. It is because it has the characteristic that the far-infrared wavelength of 5-20 micrometers which is beneficial to a human body is emitted more than 90%.
그러나, 상기와 같이, 황토가 인체에 많은 유익함은 제공함에도 불구하고, 지금까지 건축물을 축조하기 위해 사용되고 있는 벽돌, 즉, 모래와 시멘트로 이루어진 벽돌은 비교적 강도가 높고 생산성이 우수하며 가격이 저렴하다는 장점을 갖고 있으나, 종래의 벽돌에서는 인체에 유해한 성분이 방출되며, 인체에 좋은 영향을 미치는 각종 파동을 차단하여 생체리듬을 파괴하므로서, 건강을 헤치게 되는 등의 폐단을 안고 있다.However, as mentioned above, although the loess provides many benefits to the human body, the bricks that have been used to construct buildings, ie, bricks made of sand and cement, are relatively high in strength, high in productivity, and low in price. However, in the conventional brick, harmful components are emitted to the human body, and by breaking various rhythms that have a good effect on the human body, destroying biological rhythms, such as endangering health.
또한, 종래의 벽돌을 이용하여 건물을 축조함에 있어서는 위에서와 같은 폐단을 해소하기 위해서는 인체에 유익한 황토, 맥반석, 바이오 세라믹 등의 재질로 이루어진 내장재를 별도로 구비하여 이를 시공해야 되므로, 별도의 내장재 구입에 따른 비용부담과, 내장재 시공에 따른 작업의 번거로움과 많은 인력 및 추가적인작업 공기(工期)가 요구되므로 비효율적이고 경제적이지 못한 문제점이 발생하였다.In addition, in the construction of a building using a conventional brick, in order to eliminate the above-mentioned waste, it is necessary to separately install interior materials made of materials such as loess, elvan, bio ceramics, etc., which are beneficial to the human body. Due to the cost burden, cumbersome work due to the construction of interior materials and a lot of manpower and additional working air (industrial work) was required, inefficient and economical problems occurred.
본 발명은 상기와 같은 종래의 폐단 및 문제점을 해결하기 위한 것으로서, 그 목적은 건축물을 축조하기 위한 벽돌을 제조함에 있어서, 인체에 유익한 기능성 물질의 황토 및 송진 등을 이용하여 벽돌을 제조하므로서, 황토에 의한 항균, 살균, 탈취기능 및 습도 조절과 대기 정화기능을 부여하여 건축 내장재로 활용할 수 있도록 된 새로운 형태의 내장재용 기능성 황토 벽돌 및 그 제조방법을 제공하고자 하는 것이다.The present invention is to solve the problems and problems of the prior art as described above, the purpose of the manufacture of bricks for building the building, by manufacturing the bricks using the loess and rosin of the functional material beneficial to the human body, By providing antimicrobial, sterilization, deodorizing function and humidity control and air purification function by using the new type of functional ocher bricks for interior materials that can be utilized as architectural interior materials and its manufacturing method.
본 발명의 다른 목적은 기능성을 갖는 황토 및 송진을 이용하여 벽돌을 제조하므로서, 건축물 축조시 벽돌을 이용하여 벽체를 형성함은 물론, 벽돌을 내장재로 활용할 수 있도록 함과 동시에, 1000℃ 이상의 직열을 가하여도 연소성이 없는 불연, 방화기능이 향상되며, 또한, 송진이 혼합되고 프레스에 의해 압착·성형됨에 따라, 보다 더 높은 강성을 갖는 황토 벽돌을 제공하고자 하는 것이다.Another object of the present invention is to manufacture a brick using the ocher and rosin having a functional, as well as to form a wall using the brick when building, as well as to utilize the brick as interior materials, and at the same time direct heat of 1000 ℃ It is intended to provide an ocher brick having higher rigidity as the non-combustible and fire-proof functions which are not combustible even if added, and the rosin are mixed and pressed and molded by a press.
이와 같은 목적을 달성하기 위하여, 본 발명은 기능성의 황토 벽돌을 제조함에 있어서, 일정량의 황토, 송진, 규소용액, 펄프, 야자섬유실을 구비한 상태에서, 황토와 송진을 분말화하는 단계; 분말화된 황토 및 송진을 혼합·교반하는 단계; 규소용액을 물에 용융시켜 수용성 규소용액화 하는 단계; 수용성 규소용액에 펄프와 야자섬유실을 혼합·교반하는 단계; 펄프와 야자 섬유실이 혼합된 수용성 규소용액에 분말체로 혼합된 황토와 송진을 투입하는 단계; 분말체로 혼합된 황토, 송진과 펄프, 야자 섬유실을 성형기를 이용한 교반·반죽하는 단계; 프레스 압착에 의해 소정 모양의 고형물이 성형되는 단계; 프레스를 이용하여 절단하는 단계; 절단된 고형물을 자연 건조시키는 단계로 이루어진 특징을 갖는다.In order to achieve the above object, the present invention in the manufacture of the functional ocher bricks, in the state having a certain amount of loess, rosin, silicon solution, pulp, palm fiber yarn, powdering the loess and rosin; Mixing and stirring the powdered loess and rosin; Melting the silicon solution into water to form a water-soluble silicon solution; Mixing and stirring the pulp and palm fiber yarn in a water-soluble silicon solution; Injecting ocher and rosin mixed in powder to a water-soluble silicon solution in which pulp and palm fiber yarn are mixed; Stirring and kneading the loess mixed with powder, rosin and pulp, and palm fiber yarn using a molding machine; Forming a solid having a predetermined shape by press pressing; Cutting using a press; And a step of naturally drying the cut solids.
이와 같은 본 발명에서, 기능성 황토 벽돌은 분말체의 황토와 송진을 펄프와 야자 섬유실이 혼합·교반된 수용성 규소액에 투입시키고, 이를 교반 및 프레스 압착시켜 자연건조시킨 특징을 갖는다.In the present invention as described above, the functional ocher brick is characterized in that the ocher and rosin of the powder is added to the water-soluble silicon solution mixed and stirred with the pulp and palm fiber yarn, and stirred and pressed to spontaneously dry.
도 1은 본 발명에 따른 벽돌 제조방법을 나타내는 플로우 차트,1 is a flow chart showing a brick manufacturing method according to the present invention,
도 2는 본 발명에 따른 벽돌의 제조공정을 나타내는 개략도이다.Figure 2 is a schematic diagram showing a manufacturing process of a brick according to the present invention.
이하, 본 발명을 첨부된 도면에 의해 보다 상세하게 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.
도 1 및 도 2에 도시된 바와 같이, 본 발명의 황토 벽돌은 일정량의 황토, 송진, 규소용액, 펄프, 야자섬유실을 구비한 상태에서, 황토와 송진을 분말화하는 단계(S10)와; 분말화된 황토 및 송진을 혼합·교반하는 단계(S20)와; 규소용액을 물에 용융시켜 수용성 규소용액화 하는 단계(S30)와; 수용성 규소용액에 펄프와 야자섬유실을 혼합·교반하는 단계(S40)와; 펄프와 야자 섬유실이 혼합된 수용성 규소용액에 분말체로 혼합된 황토와 송진을 투입하는 단계(S50)와; 분말체로 혼합된 황토, 송진과 펄프, 야자 섬유실을 성형기를 이용한 교반·반죽하는 단계(S60)와; 프레스 압착에 의해 소정 모양의 고형물이 성형되는 단계(S70)와; 프레스를 이용하여 절단하는 단계(S80)와; 절단된 고형물을 자연 건조시키는 단계(S90)에 의해 황토 벽돌이 제조되는 것이다.As shown in Fig. 1 and 2, the ocher brick of the present invention is a state of having a certain amount of loess, rosin, silicon solution, pulp, palm fiber yarn, powdering the loess and rosin (S10); Mixing and stirring the powdered ocher and rosin (S20); Melting the silicon solution into water to form a water-soluble silicon solution (S30); Mixing and stirring the pulp and palm fiber yarn in a water-soluble silicon solution (S40); Putting ocher and rosin mixed in powder into a water-soluble silicon solution in which pulp and palm fiber yarn are mixed (S50); Stirring and kneading the loess mixed with powder, rosin and pulp, and palm fiber yarn using a molding machine (S60); Forming a solid having a predetermined shape by press pressing (S70); Cutting using a press (S80); The ocher brick is manufactured by the step S90 of naturally drying the cut solids.
따라서, 분말체의 황토와 송진을 펄프와 야자 섬유실이 혼합·교반된 수용성 규소액에 투입시키고, 이를 교반 및 프레스 압착시킨 후, 자연건조시켜 황토 벽돌을 제조하게 되는 것이며, 이때, 황토 90%, 송진 4%, 펄프 3%, 야자섬유실 3%의 혼합비율을 가지며, 수용성 규소용액은 규소용액과 물을 1:1의 비율로 혼합한 것이다.Therefore, the ocher and rosin of the powder is added to the water-soluble silicon solution in which the pulp and the palm fiber yarn are mixed and stirred, and after stirring and pressing, it is naturally dried to prepare the ocher brick. , 4% rosin, pulp 3%, palm fiber yarn 3% mixing ratio, the water-soluble silicon solution is a mixture of silicon solution and water in a ratio of 1: 1.
그리고, 상기 고형물이 성형되는 단계(S80)에서는 규소용액에 송진의 향과 성분이 용융되면서, 황토, 규소, 펄프, 야자섬유실에 송진의 점도가 경화되어 견고하게 융착되며, 물과 반응하여 조화되는 황토분말체, 펄프, 야자섬유실, 송진은 수분이 증발되면서 경화 결합되는 것이다.Then, in the step of forming the solid (S80) while the fragrance and components of the rosin in the silicon solution is melted, the viscosity of the rosin in the ocher, silicon, pulp, palm fiber chamber is hardened by fusion and firmly fused, react with water Being ocher powder, pulp, palm fiber yarn, rosin is hardened by the evaporation of moisture.
이와 같은, 본 발명에 따른 황토 벽돌의 건축용 내장재로 사용되는 실시예를 설명하면 다음과 같다.Such, when explaining the embodiment used as a building material for the construction of the ocher brick according to the present invention.
도 1 및 도 2에 도시된 바와 같이, 단계(S10)에서 황토와 송진을 분말화된 후, 단계(S20)에서 황토 및 송진이 혼합·교반되며, 단계(S30)에서 규소용액과 물이 1;1의 비울로 혼합되어 수용성 규소용액화 되고, 단계(S40)에서 수용성 규소용액에 펄프와 야자섬유실을 혼합·교반되며, 단계(S50)를 통하여 펄프와 야자 섬유실이 혼합된 수용성 규소용액에 분말체로 혼합된 황토와 송진을 투입되어 성형기에 의해 혼합·반죽(S60)된 후, 단계(S70)에 의해 프레스 압착에 의해 소정 모양의 고형물이 성형되고, 단계(S80)에서 프레스에 의해 절단되며, 단계(S90)를 거치면서 성형된 고형물이 자연 건조되어 황토 벽돌이 완성되는 것이다.1 and 2, after the ocher and rosin are powdered in step S10, the ocher and rosin are mixed and stirred in step S20, and the silicon solution and water are added in step S30. 1 is mixed with a droplet of water-soluble silicon solution, the pulp and palm fiber yarns are mixed and stirred in the water-soluble silicon solution in step S40, and the pulp and palm fiber yarns are mixed through the step (S50). After the ocher mixed with the powder and rosin were mixed and mixed and kneaded by a molding machine (S60), solids having a predetermined shape were formed by press pressing in step S70, and cut by pressing in step S80. And, through the step (S90), the molded solid is naturally dried to complete the ocher bricks.
이때, 상기 단계(70)에서는 성형기에 설치되는 형틀의 모양에 따라, 원형이나 사각형태의 고형물이 성형되는 것으로서, 사용자가 원하는 다양한 형태의 고형물 성형이 가능한 것이다.At this time, in the step 70, according to the shape of the mold installed in the molding machine, the solid of the round or square shape is molded, it is possible to form a solid of various forms desired by the user.
이러한, 황토 벽돌은 황토 분말체를 원하는 형상으로 성형하여 단단한 결합체로 치밀화 현상을 이용하여 만든 것으로, 야자 섬유실은 균열방지를 위한 목적으로 사용되는 것이고, 물에 풀은 펄프는 미세균열을 방지하기 위한 것이다.Such, ocher brick is made by using the densification phenomenon of the solid powder by molding the ocher powder into a desired shape, the palm fiber yarn is used for the purpose of crack prevention, the pulp in the water to prevent microcracks will be.
또한, 본 발명에 따른 황토 벽돌은 화학성분이나 독성이 없는 인체에 무해한 천연재료를 사용하였으며, 황토에 의한 살균 및 정화 작용을 갖는 환경친화적이고, 담배와 니코틴 냄새, 곰팡이, 세균등에 의한 악취 등을 분해하여 실내공기를 정화하는 탈취기능과, 물질표면에 부착되는 오염 요소를 분해하여 늘 쾌적한 실내를 유지할 수 있는 방오(防汚)기능이 부여되며, 대기중의 습기를 흡수하고, 건조시에는 습기를 배출하여 상시 인체리듬에 최적의 상태로 실내 습도를 유지할 수 있는 습도조절기능을 갖게 된다.In addition, the ocher brick according to the present invention is a natural material that is harmless to the human body without chemical composition or toxicity, and is environmentally friendly with sterilization and purification action by ocher, and smells like cigarettes and nicotine, mold, and bacteria. Deodorization function to decompose and purify indoor air and antifouling function to decompose contaminants attached to the surface of the material to maintain a comfortable room at all times. Absorb moisture in the air. It has a humidity control function that can maintain the indoor humidity in an optimal state for the human body rhythm at all times.
본 발명에 따른 황토 벽돌은 대기 정화기능, 원적외선 기능 및 불연, 방화기능을 갖게 되며, 특히, 원적외선의 6대 작용인 온열작용, 숙성작용, 자성작용, 건습작용, 중화작용, 공명작용으로 황토에서 방출작용하는 인체친환경 물질로 실내의 최적합 조건이 인류의 건강 생활 추구의 최상이라 할 수 있고, 약 1000℃이상의 직열을 가하여도 연소되지 않는 불연이며 가연성 가스도 전혀 발생하지 않으므로 화재발생시 유해가스에 의한 인명피해가 전무한 것이다.Ocher brick according to the present invention will have the air purification function, far infrared function and non-combustible, fire-retardant function, in particular, the six major actions of far-infrared heat, aging, magnetic action, wet and dry action, neutralization, resonance in the loess It is a human-friendly material that emits and acts as the best condition for the health of human beings, and it is a non-combustible and non-combustible gas that does not burn even when direct heat above 1000 ℃ is applied. There is no damage to human life.
그리고, 본 발명에 따른 황토 벽돌은 3%의 비율로 혼합된 송진에 의해 자연의 향을 발산하게 되므로, 마치, 자연속에서의 산림욕(솔밭)을 느끼게 하는 쾌적한 실내 환경을 유지하게 된다.In addition, the ocher brick according to the present invention emits the natural aroma by the rosin mixed at a rate of 3%, so as to maintain a comfortable indoor environment to feel the forest bath (pine field) in nature.
또한, 황토벽돌의 황토, 송진, 펄프, 야자섬유실의 혼합비율은 사용자가 임의 조절이 가능한 것으로서, 각각의 혼합 비율 범위는 황토:85∼95%, 송진:2∼5%, 펄프3∼5%, 야자섬유실:2∼5% 정도에서 이루어진다.In addition, the mixing ratio of ocher, rosin, pulp, and palm fiber yarn of the ocher brick can be arbitrarily adjusted by the user. The mixing ratio range is ocher: 85 to 95%, rosin: 2 to 5%, and pulp 3 to 5 %, Palm fiber yarn: 2 to 5%.
이와 같이, 본 고안에 따른 황토 벽돌을 이용함에 따라, 황토 벽돌을 건축용 내장재로 활용할 수 있음은 물론, 황토에 의한 항균, 살균, 탈취기능 및 습도 조절과 대기 정화기능에 대한 효과를 얻을 수 있으며, 또한, 혼합된 송진에 의해 발산되는 자연향에 의한 산림욕효과와 쾌적한 실내환경을 조성할 수 있는 효과를 얻을 수 있는 것이다.As such, by using the ocher brick according to the present invention, it can be used as the interior material for the ocher brick, as well as to obtain the effect on the antibacterial, sterilization, deodorization function and humidity control and air purification function by the ocher, In addition, it is possible to obtain a forest bathing effect due to the natural flavor emitted by the mixed rosin and to create a comfortable indoor environment.
Claims (4)