KR20040064351A - 은분말을 함유한 합성수지 조성물 및 그 제조방법 및 용도 - Google Patents
은분말을 함유한 합성수지 조성물 및 그 제조방법 및 용도 Download PDFInfo
- Publication number
- KR20040064351A KR20040064351A KR1020030001881A KR20030001881A KR20040064351A KR 20040064351 A KR20040064351 A KR 20040064351A KR 1020030001881 A KR1020030001881 A KR 1020030001881A KR 20030001881 A KR20030001881 A KR 20030001881A KR 20040064351 A KR20040064351 A KR 20040064351A
- Authority
- KR
- South Korea
- Prior art keywords
- silver powder
- resin
- weight
- synthetic resin
- resin composition
- Prior art date
Abstract
본 발명은 특정한 조건으로 합성수지와 은분말을 혼합하여 항균, 탈취, 살균성능을 양호하게 유지하며, 원적외선 방사효율을 높혀 인체에 이로운 영향을 미칠 수 있도록 한 합성수지 조성물 및 그 제조방법에 관한 것으로서, 5 내지 10중량%의 은분말 95-90중량% 을 폴리 프로필렌(PP), 폴리에칠렌(PE), 폴리스타닌(PS), 아크로니트릴 부타디엔 스티렌(ABS) 수지로 이루어진 군으로부터 선택된 범용수지 95 내지 90중량%에 함침시켜 1차 숙성가공하고, 1차 숙성가공된 혼합물을 180내지 230℃의 조건에서 용융혼합한 은분말을 함유한 합성수지 조성물을 제공하여 합성수지 조성물의 항균력 및 탈취력 그리고 살균력을 향상 시킬 수 있으며, 식품용기 등으로 이용할 경우에는 내용물을 양호한 상태로 보관할 수 있는 효과를 갖는 것이다.
Description
본 발명은 은분말을 함유한 합성수지 조성물 및 그 제조방법에 관한 것으로서, 더욱 상세하게는 특정한 조건으로 합성수지와 은분말을 혼합하여 항균, 탈취, 살균성능을 양호하게 유지하며, 원적외선 방사효율을 높혀 인체에 이로운 영향을 미칠 수 있도록 한 합성수지 조성물 및 그 제조방법에 관한 것이다.
일반적으로 은(銀)은 여러형태로 사용되어 왔다. 특히 은은 아주 적은 량을 가지고도 살균효과가 탁월한 것으로 되어있다. 한방에서는 은침(銀針)과 독을 반지하는 물건으로 은수저를 귀중하게 여겼다. 현재도 의학에서는 소위 은 솜, 은 붕대라고 하는 것들이 고치기 힘든 상처, 수술후 상처보호 등의 치료와 침구 지료에 많이 쓰이고 있으며, 의약적으로 광범위하게 쓰이고 있다.
대한민국 특허공개 2002-0073912호에는 맥반석을 주재료로하여 이에 다른 혼합물을 첨가하여 매트리스나 베게, 방석등에 부착하거나 매설하여 사용할 수 있게한 원적외선 방사용 조성물 및 그 제조방법이 개시되어 있다.
이에 따르면, 맥반석분말 25중량%, 수정분말 10중량%, 알루미나 10중량%, 규석분말 10중량%, 가성소다 10중량%, 금분말 5중량%, 은분말5중량%를 혼합하고, 이 혼합물의 0.1 ~ 0.3 중량%에 해당하는 안료를 혼합하여 가열하여 용융한 후 일정한 형상으로 경화시켜 형성하고 있다.
이러한 종래의 원적외선 방사용 조성물은 경화된 최종 혼합물을 적정 온도에서 녹여 이를 매트리스나 베게, 방석등에 부착하여 사용할 수 있도록 하여 원적외선을 방사시키는 등의 신체에 이로운 작용에 의해 건강증진에 효과를 갖고 있는 것이다.
그러나 상기와 같은 종래의 원적외선 방사용 조성물은 맥반석을 주원료로 하고 있어 혼합시 형상화 하는데에 어려움이 있고, 특히, 식품용기등으로의 사용이 제한되는등 적용범위가 제한적인 문제를 갖고 있는 것이다.
이에 본 발명은 상기의 문제점들을 개선하기 위하여 안출된 것으로서, 그 목적은 항균, 탈취, 살균력이 향상된 은분말을 함유한 합성수지 조성물 및 그 제조방법을 제공함에 있다.
본 발명의 다른 목적은 은분말을 함유한 합성수지를 이용한 성형품을 제공함에 있다.
.
이러한 본 발명의 목적은 은분말을 오토미제이션 메소드 공법으로 5㎛~10㎛크기의 은분말 5 내지 10중량%을 범용수지 95 내지 90중량%를 용융혼합한 은분말을 함유한 합성수지 조성물에 의해 달성될 수 있다.
상기 범용수지는 PP, PE, PS, ABS 수지로 이루어진 군으로부터 선택된다.
본 발명의 제조방법은 5 내지 10중량%의 은분말을 PP, PE, PS, ABS 수지로 이루어진 군으로부터 선택된 범용수지 95 내지 90중량%에 함침시켜 1차 숙성가공하고, 1차 숙성가공된 혼합물을 180내지 230℃의 조건에서 용융혼합하는 것을 특징으로 한다.
본 발명의 제조방법은 용융혼합된 조성물을 압출하는 단계와, 압출된 제품을 적당한 크기로 절단하는 절단하는 단계와, 절달된 제품을 냉각시켜 펠릿을 형성하는 단계를 추가로 포함한다.
본 발명은 상기와 같은 제조방법에 의해 제조된 조성물을 원료로 사용한 식품용기로서의 용도에 특징을 갖는다.
이하, 본 발명의 바람직한 실시예를 첨부한 도면을 참고하여 구체적으로 설명하면 다음과 같다.
본 발명은 범용수지에 일정량의 은분말이 함침되어 구성된다.
범용수지는 폴리프로필렌(PP), 폴리에틸렌(PE), 폴리스타닌(PS), 아크로니트릴 부타디엔 스티렌(ABS)수지등의 범용수지의 군으로부터 선택되어진다. 범용수지와 은분말을 각각 95내지 90중량% 및 10 내지 15중량%의 혼합비를 갖는다. 바람직하게는 범용수지와 은분말은 90:10의 중량비를 갖는 것이 좋다.
은분말은 오토미제이션 메소드(atomization method)공법에 의해 제조되는 것으로 약 5㎛~10㎛의 크기를 갖는다.
합성수지와 은분말을 혼합한후 180내지 230℃에서 용융한다. 용융이 진행됨과 동시에 소정의 교반장치에 의해 교반하는 것에 의해 은분말은 합섭수지와 고르게 혼합되어 진다. 이때 은분말은 용융되지 않고 합성수지만이 용융되어 유동하게 되므로 분말상태의 은분말이 그대로 합성수지내로 함침되어지게 된다.
본 발명은 따르면, 이러한 상태 즉, 혼합완료된 조성물은 용융상태로부터 응용제품의 용도에 따라 후속공정을 다르게 하여 적절한 형태로의 응용이 가능하게 된다. 즉, 용융상태의 혼합물을 특정형태의 금형틀에 주입하여 냉각시키는 것에 의해 소망하는 형태로의 경화가 가능하게 된다.
또한, 본 발명은 용융혼합된 조성물을 압출공정을 거쳐 압출함과 동시에 적당한 크기로 절단하고, 절달된 제품을 냉각시켜 펠릿을 형성하여 반제품상태에서 보관 및 취급이 가능하다.
따라서, 합성수지에 함침된 은분말은 고유의 효능 즉 항균, 탈취 및 살균능력을 그대로 유지하게 된다.
이러한 본 발명은 특히 식품용기등을 이용하여 내용물의 신선도를 양호하게 유지하는 등의 효과를 볼 수 있고, 특히, 포장용백, 코팅재, 반도체장비부품 및 벽지등 다양한 분야에서의 이용이 가능하게 된다.
이상에서 설명한 본 발명에 따른 그 분말을 함유한 합성수지 조성물은 합성수지와 은분말을 적절히 용융혼합함으로써 합성수지 조성물의 항균력 및 탈취력 그리고 살균력을 향상 시킬 수 있으며, 식품용기 등으로 이용할 경우에는 내용물을 양호한 상태로 보관할 수 있는 효과를 갖는 것이다.
Claims (5)
- 5㎛~10㎛크기의 은분말 5 내지 10중량%을 범용수지 95 내지 90중량%를 용융혼합한 것을 특징으로 하는 은분말을 함유한 합성수지 조성물.
- 제 1항에 있어서, 상기 범용수지는 폴리 프로필렌(PP), 폴리에칠렌(PE), 폴리스타닌(PS), 아크로니트릴 부타디엔 스티렌(ABS) 수지로 이루어진 군으로부터 선택된 것을 특징으로 하는 조성물.
- 5 내지 10중량%의 은분말을 폴리 프로필렌(PP), 폴리에칠렌(PE), 폴리스타닌(PS), 아크로니트릴 부타디엔 스티렌(ABS) 수지로 이루어진 군으로부터 선택된 범용수지 95 내지 90중량%에 함침시켜 1차 숙성가공하고, 1차 숙성가공된 혼합물을 180내지 230℃의 조건에서 용융혼합하는 것을 특징으로 하는 은분말을 함유한 합성수지 조성물 제조방법.
- 제 2항에 있어서, 용융혼합된 조성물을 압출하는 단계와, 압출된 제품을 적당한 크기로 절단하는 절단하는 단계와, 절달된 제품을 냉각시켜 펠릿을 형성하는 단계를 추가로 포함하는 것을 특징으로 하는 은분말을 함유한 합성수지 조성물 제조방법.
- 제 3항 및 제 4항에 따른 제조방법에 의해 제조된 조성물을 원료로 사용한 식품용기의 용도.