KR102650069B1 - 고내열성 마스킹 필름 - Google Patents
고내열성 마스킹 필름 Download PDFInfo
- Publication number
- KR102650069B1 KR102650069B1 KR1020210134651A KR20210134651A KR102650069B1 KR 102650069 B1 KR102650069 B1 KR 102650069B1 KR 1020210134651 A KR1020210134651 A KR 1020210134651A KR 20210134651 A KR20210134651 A KR 20210134651A KR 102650069 B1 KR102650069 B1 KR 102650069B1
- Authority
- KR
- South Korea
- Prior art keywords
- masking film
- heat
- polyamide
- layer
- core layer
- Prior art date
Abstract
본 발명은 고내열성 마스킹 필름에 관한 것으로, 코어층(10)의 양면에 무기물 및 폴리아마이드 혼합층이 도포되어 도료의 흘러내림을 방지하는 고내열성 마스킹 필름에 관한 것이다. 구체적으로, 본 발명의 마스킹 필름은 코어층 양면으로 무기물 및 폴리아마이드 혼합층이 도포되어 도료의 흘러내림을 방지하고, 내열성이 우수하여 고온 조건에서도 유용하게 사용될 수 있다.
Description
본 발명은 고내열성 마스킹 필름에 관한 것으로, 코어층(10)의 양면에 무기물 및 폴리아마이드 혼합층(30)이 도포되어 도료의 흘러내림을 방지하는 고내열성 마스킹 필름에 관한 것이다.
일반적으로, 선박 건조, 차량 제작 또는 건축물의 인테리어 작업 과정에 도장작업이 포함되는데, 페인트가 도포되지 않아야 할 부분에 마스킹 필름을 부착하고 작업을 한다. 마스킹 필름을 부착한 후, 페인트를 스프레이로 분사하거나 붓으로 칠하여 도장작업이 진행되고, 부착된 마스킹 필름은 페인트가 건조된 후 다른 작업을 위해 제거된다. 이런 이유로 마스킹 필름은 제거된 후에 부착 대상에 잔류물을 남기지 않아야 하며, 우수한 내열성을 가져 고온의 조건에서 도장작업을 수행하여도 이와 같은 문제가 발생하지 않아야 한다.
종래에는 이와 같은 용도를 위해 청테이프를 주로 사용하였으나, 청테이프 표면에 도포된 페인트가 시간이 경과함에 따라 표면으로부터 탈락하여 주변을 더럽혀 탈락된 페인트를 청소해야하는 별도의 작업이 필요하다. 또한, 청테이프 제거시 점착제가 잔류하여 잔류된 점착제를 제거하기 위한 별도의 작업이 필요한 문제가 있었다.
이와 관련하여, 대한민국 등록특허 제10-2188838호는 폴리에틸렌층과, 폴리에틸렌층의 상면에 폴리에틸렌이 함침된 부직포층과, 폴리에틸렌층의 하면에 폴리에틸렌이 함침된 면사층으로 이루어진 기재; 및 기재의 면사층의 하면에 점착제층을 포함하여, 테이프의 폭 방향으로의 말림을 개선하고, 기존의 저밀도폴리에틸렌용 압출기를 활용하여 경제적이며, 일괄공정으로 부직포, 폴리에틸렌 및 면사를 결합하여 테이프의 찢김성과 찢김 방향성을 개선하고, 부직포의 열압착에 의한 배면효능을 증진시키는 도장용 마스킹 테이프를 개시하고 있다.
본 발명의 목적은 도료의 흘러내림을 방지하는 고내열성 마스킹 필름을 제공하는 것이다.
상기 목적을 달성하기 위하여, 본 발명은 코어층(10), 및 상기 코어층(10) 양면에 도포된 무기물 및 폴리아마이드(polyamide) 혼합층(30)을 포함하는 고내열성 마스킹 필름을 제공한다.
본 발명의 마스킹 필름은 코어층 양면으로 무기물 및 폴리아마이드 혼합층이 도포되어 도료의 흘러내림을 방지하고, 내열성이 우수하여 고온 조건에서도 유용하게 사용될 수 있다.
도 1은 본 발명에 따른 고내열성 마스킹 필름의 구조를 나타내는 모식도이다.
도 2는 본 발명에 따른 마스킹 필름의 내열성을 확인한 결과 도면이다.
도 2는 본 발명에 따른 마스킹 필름의 내열성을 확인한 결과 도면이다.
이하, 본 발명을 상세히 설명한다.
본 발명은 코어층(10), 및 상기 코어층(10) 양면에 도포된 무기물 및 폴리아마이드(polyamide) 혼합층(30)을 포함하는 고내열성 마스킹 필름을 제공한다.
상기 코어층(10)은 통상의 기술분야에 필름의 제조에 사용되는 것으로 알려진 모든 종류를 사용할 수 있다. 구체적으로, 상기 코어층(10)은 폴리올레핀일 수 있다. 상기 용어, '폴리올레핀(polyolefine)'은 이중결합을 1개 갖는 사슬모양의 탄화수소 화합물인 올레핀의 중합으로 생기는 고분자 화합물을 의미한다. 일례로, 상기 올레핀은 에틸렌, 프로필렌, 부텐, 이소부텐, 펜텐, 메틸펜텐, 헥센, 헵텐, 옥텐 및 데센 등을 포함할 수 있다. 한편, 상기 폴리올레핀은 폴리에스테르, 폴리에틸렌 및 폴리프로필렌으로 구성된 군으로부터 선택되는 어느 하나 이상일 수 있다.
상기 폴리올레핀은 올레핀 단량체의 중합체일 수 있다. 또한, 상기 폴리올레핀은 코어층(10)으로서의 특성을 유지하는 한, 올레핀 단량체가 다른 종류의 단량체와 중합되어 생성된 공중합체 또는 삼중합체를 모두 포함할 수 있다. 상기 공중합체 또는 삼중합체는 랜덤 공중합체(random copolymer), 블록 공중합체(block copolymer), 교대 공중합체(alternating copolymer) 또는 그라프트 공중합체(graft copolymer)의 형태일 수 있다.
상기 코어층은 용융 강도가 0.05 N 이상, 0.05 내지 0.15 N 또는 0.05 내지 0.1 N일 수 있고, 용융 흐름 지수가 5 이하, 1 내지 5, 1 내지 3 또는 1 내지 2일 수 있다.
본 발명에 따른 고내열성 마스킹 필름은 상기 코어층(10) 양면에 무기물 및 폴리아마이드 혼합층(30)이 도포된 것일 수 있다. 상기 무기물은 칼슘계열 및 규산계열 무기물로 구성된 군으로부터 선택되는 어느 하나 이상일 수 있다. 일례로, 상기 무기물은 탄산칼슘, 실리카, 산화티탄, 알루미늄옥사이드, 산화칼슘, 하이드록시아파타이트, 벤토나이트, 산화아연, 마그네슘 수산화물 등을 포함할 수 있다. 본 발명의 일 실시예에서, 상기 무기물은 탄산칼슘 또는 실리카일 수 있다. 구체적으로, 상기 무기물은 분말의 형태로 첨가될 수 있고, 상기 분말은 1 내지 15 ㎛, 1 내지 12 ㎛, 1 내지 10 ㎛, 5 내지 15 ㎛, 5 내지 12 ㎛ 또는 5 내지 10 ㎛의 평균 입경을 가질 수 있다. 상기 무기물은 통상적인 방법으로 분쇄되어 분말의 형태로 수득될 수 있다.
상기 무기물은 폴리아마이드와 적절한 비율로 혼합될 수 있다. 이때, 혼합비는 통상의 기술자에 의해 적절히 선택될 수 있으나, 구체적으로, 상기 무기물은 전체 혼합층(30) 무게를 기준으로 1 내지 20%(w/w), 1 내지 15%(w/w) 또는 1 내지 10%(w/w)의 함량으로 포함될 수 있다.
본 명세서에 사용된 용어, '폴리아마이드(polyamide)'는 각각의 단량체가 아마이드 결합으로 반복되어 연결된 고분자 중합체 화합물을 의미한다. 구체적으로, 상기 폴리아마이드는 합성 폴리아마이드일 수 있고, 이는 통상적으로 축합 중합, 개환 중합 또는 첨가 중합 반응을 통해 제조될 수 있다. 상기 폴리아마이드는 이를 구성하는 단량체에 따라 지방족 폴리아마이드, 방향족 폴리아마이드 또는 지방족 고리 폴리아마이드로 나뉠 수 있다.
상기 폴리아마이드는 극성 또는 무극성 폴리아마이드를 모두 포함할 수 있고, 구체적으로 극성 폴리아마이드일 수 있다. 일례로, 상기 폴리아마이드는 표면접촉각이 78 내지 92 또는 78 내지 84도일 수 있다.
본 발명에 따른 고내열성 마스킹 필름은 코어층(10)과 무기물 및 폴리아마이드 혼합층(30) 사이에 접착층(20)을 더 포함할 수 있다. 상기 접착층(20)은 코어층(10)과 무기물 및 폴리아마이드 혼합층(30)을 접착시킬 수 있는 물질이라면 어떠한 물질을 사용하여도 무방하다. 구체적으로, 상기 접착층(20)은 그라프트 공중합체일 수 있다. 일례로, 상기 그라프트 공중합체는 폴리에틸렌-에틸렌비닐아세테이트 그라프트 공중합체, 무수말레인산 그라프트머(MAH-graftmer), 메타아크릴산(methacrylic acid) 공중합체 및 아이오노머(ionomer)로 구성된 군으로부터 선택되는 어느 하나 이상일 수 있다. 본 발명의 일 실시예에서 상기 접착층(20)은 폴리에틸렌-에틸렌비닐아세테이트 공중합체일 수 있다.
상기 용어, '폴리에틸렌(polyethylene)'은 에틸렌 단량체를 중합하여 수득되는 고분자를 의미하며, 금속 촉매 배위 중합법 또는 라디칼 중합법으로 제조될 수 있다. 상기 폴리에틸렌은 저밀도 폴리에틸렌(LDPE), 고밀도 폴리에틸렌(HDPE), 선형저밀도 폴리에틸렌(LLDPE), 초저밀도 폴리에틸렌(VLDPE), 초고분자량 폴리에틸렌(UHMWPE) 등을 포함할 수 있다.
또한, 상기 용어, '에틸렌비닐아세테이트(ethylene vinyl acetate, EVA)'는 에틸렌과 비닐아세테이트 모노머를 중합하여 수득되는 공중합체로, 발포성, 접착성 및 투명성이 우수하다. 상기 에틸렌비닐아세테이트는 폴리에틸렌과 함께 공중합체를 형성할 수 있으며, 이때, 에틸렌비닐아세테이트 단량체는 20 내지 80%(w/w)의 함량으로 포함될 수 있다.
본 발명에 따른 고내열성 마스킹 필름은 코어층(10)의 양면에 무기물 및 폴리아마이드 혼합층(30)이 도포된 것이나, 필요에 따라 코어층(10)의 일측면에 무기물 및 폴리아마이드 혼합물이 도포되고, 다른 일측면에는 마스킹 필름이 부착 부위에 부착될 수 있도록 점착층이 도포될 수 있다. 한편, 본 발명에 따른 고내열성 마스킹 필름은 코어층(10)의 양면에 무기물 및 폴리아마이드 혼합층(30)이 도포되고, 상기 혼합층(30)의 일측면에 마스킹 필름이 부착 부위에 부착될 수 있도록 점착층이 도포될 수 있다.
상기 점착층은 본 발명에 따른 마스킹 필름을 부착 부위에 부착시킬 수 있는 물질이라면 어떠한 물질로도 사용가능하다. 상기 점착층은 천연고무 또는 합성고무에 점착부여제인 석유수지 및 폴리부텐이 혼합되어 도포된 것일 수 있다. 상기 점착층은 필요에 따라 기타 충진제나 안정제가 더 첨가될 수 있다.
본 발명에 따른 고내열성 마스킹 필름은 도료의 흘러내림을 방지하고, 내열성이 우수하여 고온 조건에서도 유용하게 사용될 수 있다. 뿐만 아니라, 상기 마스킹 필름은 기계적 또는 물리학적 손상이나, 오염으로부터 대상을 보호하기 위해 사용될 수도 있다.
상기 마스킹 필름은 통상의 기술분야에 잘 알려진 방법에 따라 제조될 수 있다. 구체적으로, 상기 마스킹 필름은 캐스트 압출 또는 블로운 공정에 의해 제조될 수 있다. 이때, 본 발명에 따른 마스킹 필름을 구성하는 코어층(10), 혼합층(30) 및 접착층(20)은 동시에 공압출 공정에서 압출되거나, 각각을 별도로 형성한 후, 각각의 결합 또는 적층시킴으로써 제조될 수 있다.
또한, 상기 마스킹 필름은 본 발명에 따른 효과를 저해하지 않는 한 기타의 첨가제를 더 포함할 수 있다.
이하, 본 발명을 하기 실시예에 의해 상세히 설명한다, 단, 하기 실시예는 본 발명을 예시하기 위한 것일 뿐, 이들에 의해 본 발명이 제한되는 것은 아니다. 본 발명의 청구범위에 기재된 기술적 사상과 실질적으로 동일한 구성을 갖고 동일한 작용 효과를 이루는 것은 어떠한 것이라도 본 발명의 기술적 범위에 포함된다.
실시예
1. 무기물 분말 및
폴리아마이드를
포함하는
마스킹
필름의 제조-(1)
코어층으로 저밀도 폴리에틸렌(LDPE)를 포함하고, 이의 양면에 탄산칼슘 분말과 표면 접촉각 92도의 폴리아마이드의 혼합층이 코팅된 마스킹 필름을 압출-캐스팅 공정을 이용하여 통상적인 방법으로 제조하였다. 이때, 탄산칼슘 분말은 압출기의 주입구역(feeding zone)을 통해 공급되었다.
실시예
2. 무기물 분말 및
폴리아마이드를
포함하는
마스킹
필름의 제조-(2)
혼합층에 탄산칼슘 분말 및 표면 접촉각 92도의 폴리아마이드 대신, 다공성 실리카와 표면 접촉각 78도의 폴리아마이드가 사용된 것을 제외하고는 상기 실시예 1과 동일한 조건 및 방법으로 마스킹 필름을 제조하였다.
실시예
3. 무기물 분말 및
폴리아마이드를
포함하는
마스킹
필름의 제조-(3)
코어층 및 혼합층 사이에 에틸렌초산비닐 공중합체(EVA)로 구성된 접착층을 사용한 것을 제외하고는, 상기 실시예 2와 동일한 조건 및 방법으로 마스킹 필름을 제조하였다.
실시예
4. 무기물 분말 및
폴리아마이드를
포함하는
마스킹
필름의 제조-(4)
에틸렌초산비닐 공중합체 대신 비닐아세테이트(vinylacetate) 단량체의 함량이 70%인 폴리에틸렌-에틸렌비닐아세테이트 그라프트 공중합체를 사용한 것을 제외하고는, 상기 실시예 3과 동일한 조건 및 방법으로 마스킹 필름을 제조하였다.
비교예
1.
폴리아마이드
층을 포함하지 않는
마스킹
필름의 제조
코어층 및 혼합층을 모두 LDPE로 구성된 것을 제외하고는, 상기 실시예 2와 동일한 조건 및 방법으로 마스킹 필름을 제조하였다.
비교예
2. 탄산칼슘 분말을 포함하는
마스킹
필름의 제조
혼합층이 LDPE 및 탄산칼슘 분말로 구성된 것을 제외하고는, 상기 비교예 1과 동일한 조건 및 방법으로 마스킹 필름을 제조하였다.
비교예
3. 무극성
폴리아마이드를
포함하는
마스킹
필름의 제조
혼합층을 표면 접촉각이 92도인 무극성 폴리아마이드로 구성된 것을 제외하고는, 상기 비교예 1과 동일한 조건 및 방법으로 마스킹 필름을 제조하였다.
비교예
4. 극성
폴리아마이드를
포함하는
마스킹
필름의 제조
혼합층을 표면 접촉각이 78도인 극성 폴리아마이드로 구성된 것을 제외하고는, 상기 비교예 1과 동일한 조건 및 방법으로 마스킹 필름을 제조하였다.
비교예
5. 폴리에틸렌을 포함하는
마스킹
필름의 제조-(3)
코어층 및 혼합층 사이에 LDPE로 구성된 접착층을 더 포함하는 것을 제외하고는, 상기 비교예 1과 동일한 조건 및 방법으로 마스킹 필름을 제조하였다.
실험예
1.
마스킹
필름의
흐름저항성
확인
상기에서 제조된 마스킹 필름의 흐름저항성을 ISO 16862에 규정된 방법에 따라 실험을 수행하여 확인하고, 그 결과를 하기 표 1에 나타내었다.
| 마스킹 필름 | 흐름성(㎜) |
| 실시예 1 | 11 |
| 실시예 2 | 9 |
| 실시예 3 | 8 |
| 실시예 4 | 9 |
| 비교예 1 | 67 |
| 비교예 2 | 51 |
| 비교예 3 | 34 |
| 비교예 4 | 25 |
| 비교예 5 | 9 |
표 1에 나타난 바와 같이, 코어층의 양면에 무기물 및 폴리아마이드 혼합층이 위치한 실시예 1 내지 4의 마스킹 필름은 흐름성이 유의적으로 낮았다. 한편, 코어층으로만 구성되거나, 코어층 양면에 무기물 또는 폴리아마이드 층이 위치한 비교예 1 내지 4의 마스킹 필름은 25 내지 67 ㎜까지 도포된 도료가 흘러내렸다. 그러나, 코어층 및 혼합층 사이에 접착층으로서 폴리에틸렌을 포함하는 마스킹 필름(비교예 5)은 다른 비교예의 마스킹 필름과 달리 흐름성이 유의적으로 낮았다.
따라서, 상기 결과로부터 본 발명에 따른 마스킹 필름은 도료의 흘러내림을 방지하는 우수한 효과를 나타냄을 알 수 있었다.
실험예
2.
마스킹
필름의 내열성 확인
실시예 1, 2 및 비교예 1 내지 4에서 제조된 마스킹 필름의 내열성을 다음과 같은 방법으로 육안관찰을 통해 확인하였다.
구체적으로, 도장판 위에 상기 제조된 마스킹 필름을 깔고, 그 위에 약 500 g인 스테인레스 재질의 원통추를 올렸다. 이를 오븐에 넣고 200℃의 온도로 가열한 후, 마스킹 필름에 원통추의 자국이 남는지 육안으로 관찰하고, 그 결과를 도 2에 나타내었다.
도 2에 나타난 바와 같이, 무기물 분말을 폴리아마이드와 혼합하여 제조된 마스킹 필름은 원통추의 자국 및 잔여물 등이 남지 않았으나, 비교예 1 내지 4의 마스킹 필름은 고온에 의해 원통추의 자국 및 잔여물 등이 남았다.
따라서, 상기 결과로부터 본 발명에 따른 마스킹 필름이 내열성이 우수하여 고온 조건에서도 유용하게 사용될 수 있음을 알 수 있었다.
실험예
3.
마스킹
필름의 박리테스트
실시예 3 및 4와 비교예 5에서 제조된 마스킹 필름의 박리테스트를 ISO 11139에 규정된 방법, 및 육안으로 확인하여 품질을 판정한 결과를 하기 표 2에 나타내었다.
| 마스킹 필름 | Peel test 180° | 육안 관찰 | 품질 판정 |
| 실시예 3 | 8.7 N | 전이전사 없음 | 합격 |
| 실시예 4 | 13.9 N | 전이전사 없음 | 합격 |
| 비교예 5 | 0 N | 코어층으로 전사 | 불합격 |
표 2에 나타난 바와 같이, 실시예 3 및 4의 마스킹 필름은 전이전사가 없는 우수한 품질을 나타냈다.
실험예
4.
마스킹
필름의 가공 수율 확인
본 발명에 따른 마스킹 필름의 가공 수율을 다음과 같은 방법으로 확인하였다.
구체적으로, 코어층으로서 1.2의 용융흐름지수, 0.08 N의 용융강도를 갖는 LDPE를 준비하고, 상기 LDPE의 양면에 비닐아세테이트 단량체의 함량이 70%인 폴리에틸렌-에틸렌비닐아세테이트 그라프트 공중합체를 적용한 후, 최외각 양면에 다공성 실리카(7 ㎛의 평균입경) 및 표면접촉각 78도의 92% 폴리아미드를 적용하여 마스킹 필름을 제조하였다. 상기 마스킹 필름은 통상적으로 알려진 5층(5 layer) 공압출 방법으로 제조되었다. 제조된 마스킹 필름의 가공 수율 및 제조과정에서의 파단 발생 횟수를 확인하여 하기 표 3에 나타내었다.
| 항목 | 마스킹 필름 |
| 파단 발생 횟수(회) | 0 |
| 가공 수율(%) | 84 |
표 3에 나타난 바와 같이, 본 발명에 따른 마스킹 필름은 공압출 방법으로 제조하는 과정에서 파단이 발생하지 않았고, 84%의 높은 가공 수율을 나타내었다.
Claims (10)
- 코어층(10), 및
상기 코어층(10) 양면에 도포된 무기물 및 극성 폴리아마이드(polyamide) 혼합층(30)
을 포함하는 내열성 마스킹 필름으로서,
상기 무기물은 칼슘계열 및 규산계열 무기물로 구성된 군으로부터 선택되는 어느 하나 이상인 내열성 마스킹 필름.
- 제1항에 있어서, 코어층(10)과 혼합층(30) 사이에 접착층(20)을 더 포함하는, 내열성 마스킹 필름.
- 제2항에 있어서, 상기 접착층은 그라프트 공중합체인, 내열성 마스킹 필름.
- 제3항에 있어서, 상기 그라프트 공중합체는 폴리에틸렌-에틸렌비닐아세테이트 그라프트 공중합체 및 무수말레인산 그라프트머(MAH-graftmer)로 구성된 군으로부터 선택되는 어느 하나 이상을 포함하는, 내열성 마스킹 필름.
- 제1항에 있어서, 상기 코어층(10)은 폴리올레핀인, 내열성 마스킹 필름.
- 제5항에 있어서, 상기 폴리올레핀은 폴리에틸렌 및 폴리프로필렌으로 구성된 군으로부터 선택되는 어느 하나 이상인, 내열성 마스킹 필름.
- 삭제
- 제1항에 있어서, 상기 혼합층(30)은 무기물을 1 내지 20%(w/w)의 함량으로 포함하는, 내열성 마스킹 필름.
- 제8항에 있어서, 상기 무기물은 1 내지 15 ㎛의 평균 입경을 갖는 분말인, 내열성 마스킹 필름.
- 제1항에 있어서, 상기 내열성 마스킹 필름은 도료의 흘러내림을 방지하는, 내열성 마스킹 필름.