KR102474553B1 - Uninterruptible live wire cleaning agent composition for fire prevention of electrical equipment - Google Patents
Uninterruptible live wire cleaning agent composition for fire prevention of electrical equipment Download PDFInfo
- Publication number
- KR102474553B1 KR102474553B1 KR1020220107687A KR20220107687A KR102474553B1 KR 102474553 B1 KR102474553 B1 KR 102474553B1 KR 1020220107687 A KR1020220107687 A KR 1020220107687A KR 20220107687 A KR20220107687 A KR 20220107687A KR 102474553 B1 KR102474553 B1 KR 102474553B1
- Authority
- KR
- South Korea
- Prior art keywords
- electrical equipment
- weight
- fire prevention
- limonene
- cleaning composition
- Prior art date
Abstract
Description
본 발명은 세정제 조성물에 관한 것으로, 보다 구체적으로 전기화재 예방용 산업전기설비 세정제 조성물에 관한 것이다.The present invention relates to a cleaning composition, and more particularly, to a cleaning composition for industrial electrical equipment for preventing electrical fires.
자가발전 수배전반, 옥내 수배전반, 옥외 수배전반, 지하철 스크린도어, 분전반 등의 저·고압 전기설비 또는 지하철 운용설비, 대형 복합건물 통제시설, 무정전 전원 장치(UPS), 전산실, 이동통신시설, 승강기 인쇄 배선회로 기판(PCB) 등의 전기·전자통신장비는 미세한 회로와 반도체 등 전자소자의 복합적인 통전기기로 구성되어 있다.Self-powered power switchboard, indoor switchboard, outdoor switchboard, subway screen door, distribution board, etc., low/high voltage electrical equipment or subway operating facilities, control facilities for large complex buildings, uninterruptible power supply (UPS), computer rooms, mobile communication facilities, elevator printed wiring circuits Electrical/electronic communication equipment such as a board (PCB) is composed of a complex energizer of electronic elements such as fine circuits and semiconductors.
특히, 상술한 산업전기설비는 24시간 가동되면서 지속적으로 외부오염에 노출됨에 따라 통전기기 내·외부에 미세먼지, 그리스, 레진 등의 오염물질이 축적되며, 이러한 오염물질에 대한 정밀세척이 이루어지지 않은 상태로 유지 및 운영될 경우, 오염물질에 의해 트래킹(tracking)이 발생한다. 이러한 트래킹이 지속될 경우, 트래킹에 의한 화제, 감전 등의 사고, 오작동 및 설비 성능 저하 등의 문제점이 발생할 수 있다. 한편, 전압이 인가된 도체 간의 고체절연물 표면에 습기, 수분, 먼지, 오존, 또는 전해질을 함유하는 액체 증기 또는 금속가루 등의 도체가 부착될 경우, 오염된 곳의 표면을 따라 줄 발열(Joule heating)이 발생하며, 상기 줄 발열에 의해 표면이 국부적으로 발열되어 표면의 부착물 간에 미소방전이 발생하게 된다. 여기서 트래킹이란 이러한 미소방전이 반복될 경우 절연물 표면의 일부가 분해되어 탄화되거나 침식되어 도전성의 통로(track)가 형성되는 현상이다.In particular, as the above-mentioned industrial electrical equipment is operated 24 hours a day and is continuously exposed to external contamination, contaminants such as fine dust, grease, and resin accumulate inside and outside the electrical equipment, and precise cleaning of these contaminants is not performed. If maintained and operated in an unregulated state, tracking by contaminants occurs. If such tracking continues, problems such as accidents such as fire and electric shock due to tracking, malfunctions, and degradation of facility performance may occur. On the other hand, when a conductor such as moisture, moisture, dust, ozone, liquid vapor or metal powder containing an electrolyte is attached to the surface of a solid insulator between conductors to which voltage is applied, Joule heating along the surface of the contaminated area ) occurs, and the surface is locally heated by the Joule heating, so that microdischarges occur between the attachments on the surface. Here, tracking is a phenomenon in which, when such micro-discharges are repeated, a part of the surface of the insulator is decomposed and carbonized or eroded to form a conductive track.
따라서, 전기가 흐르는 다양한 산업전기설비들의 수명, 내구성 향상 및 안전사고 예방을 위해서 산업전기설비 내부의 오염원(미세먼지, 그리스, 레진 등)을 제거하는 주기적인 관리가 필요하다.Therefore, periodic management to remove pollutants (fine dust, grease, resin, etc.) inside industrial electrical equipment is required to improve the lifespan, durability, and prevent safety accidents of various industrial electrical equipment through which electricity flows.
일반적인 세척방법으로 정전을 시킨 상태에서 붓이나 솔을 이용하여 먼지 등의 오염원을 이탈시키는 방법(1); 두번째로 컴프레서(Compressor) 등을 이용한 강한 바람을 이용하여 오염원을 제거하는 방법(2); 세번째로 세정제 조성물을 이용하여 이물질을 분해 및 제거하는 방법(3)이 주로 이용되었다. 이들 중 물리적인 세척 방법(1, 2)의 경우, 물리적인 힘에 의해 통전기기가 손상될 위험이 높고, 세척 시 발생되는 정전기에 의해 오염원이 발화될 위험이 있으며, 특히, 그리스, 레진 등의 기름때 오염원을 완전하게 제거할 수 없는 문제점이 있었다.As a general cleaning method, using a brush or a brush in a state of power failure to remove contaminants such as dust (1); Second, a method of removing pollutants by using strong wind using a compressor (2); Thirdly, the method (3) of decomposing and removing foreign substances using a detergent composition was mainly used. Among them, in the case of physical cleaning methods (1, 2), there is a high risk of damage to the electrical current due to physical force, and there is a risk of ignition of contaminants due to static electricity generated during cleaning. In particular, grease, resin, etc. There was a problem of not being able to completely remove the oil stain contamination source.
이에, 세정제 조성물을 이용하는 화학적인 방법(3)이 유용하게 이용되어 왔다. 그러나, 종래의 화학 세정제에 포함되는 석유 용제는 대부분 큰 탄소 수를 가져 점도가 높아 스프레이 분사와 같은 분사를 위해 점도 조절을 위한 별도의 첨가제가 요구되는 문제점이 있었다. 이러한 첨가제는 오존 파괴물질 또는 탄소 수 3 이하의 저급 알코올 화합물 등과 같은 휘발성이 매우 높은 물질로 구성되어, 휘발성 물질의 낮은 인화점으로 인하여 폭발사고의 위험이 존재하였다.Thus, the chemical method (3) using a detergent composition has been usefully used. However, most of the petroleum solvents included in conventional chemical cleaners have a high carbon number and high viscosity, so there is a problem in that a separate additive for viscosity control is required for spraying such as spraying. These additives are composed of highly volatile substances such as ozone depleting substances or lower alcohol compounds having 3 or less carbon atoms, and there is a risk of explosion due to the low flash point of the volatile substances.
또한, 높은 휘발성을 가진 세정제 조성물이 통전기기의 표면에 닿게 되면 기화열로 인한 경화작용을 일으켜 전선이나 플라스틱과 같은 연성장비의 취성화로 인해 끊어지는 등 오작동을 일으켜 고장 발생률이 높아지는 문제가 있었다.In addition, when the detergent composition with high volatility comes into contact with the surface of the electrical device, it causes a hardening action due to heat of vaporization, resulting in malfunctions such as brittleness of soft equipment such as wires or plastics, resulting in a high failure rate.
또한, 세정제 조성물에 디클로로에탄, 트리클로로에탄, 펜타클로로에탄 등의 클로로알칸 화합물이 포함될 경우, 세정력이 우수한 장점을 갖고 있지만, 피부, 목, 폐, 또는 신장에 유해하며 심지어는 암을 유발하는 문제점도 갖고 있었다.In addition, when a chloroalkane compound such as dichloroethane, trichloroethane, pentachloroethane, etc. is included in the detergent composition, it has an excellent detergency, but is harmful to the skin, neck, lungs, or kidneys, and even causes cancer also had
본 발명의 목적은, 공급 중인 전력의 차단 없이 전기 및 전자통신장비 내에 오염된 미세먼지 또는 분진을 효과적으로 제거하여 전기화재를 예방할 수 있는 산업전기설비 세정제 조성물을 제공하는 것이다.An object of the present invention is to provide an industrial electrical equipment cleaning composition capable of preventing electrical fires by effectively removing fine dust or dust contaminated in electrical and electronic communication equipment without interruption of power being supplied.
본 발명의 다른 목적은, 인체에 무해하고 친환경적인 산업전기설비 세정제 조성물을 제공하는 것이다.Another object of the present invention is to provide a detergent composition for industrial electrical equipment that is harmless to the human body and environmentally friendly.
본 발명의 목적들은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 본 발명의 다른 목적 및 장점들은 하기의 설명에 의해서 이해될 수 있고, 본 발명의 실시예에 의해 보다 분명하게 이해될 것이다. 또한, 본 발명의 목적 및 장점들은 청구범위에 나타낸 수단 및 그 조합에 의해 실현될 수 있음을 쉽게 알 수 있을 것이다.The objects of the present invention are not limited to the above-mentioned objects, and other objects and advantages of the present invention not mentioned above can be understood by the following description and will be more clearly understood by the examples of the present invention. It will also be readily apparent that the objects and advantages of the present invention may be realized by means of the instrumentalities and combinations indicated in the claims.
상기 목적을 달성하기 위한 본 발명의 일 실시예는, 수소처리된 경질 정제유 30 내지 40 중량%; 수소처리된 중질 나프타(hydrotreated heavy naphtha) 25 내지 35 중량%; 및 D-리모넨(D-limonene) 1 내지 10 중량%;를 포함하는 전기화재 예방용 산업전기설비 세정제 조성물을 제공한다.One embodiment of the present invention for achieving the above object, 30 to 40% by weight of hydrotreated light refined oil; 25 to 35% by weight of hydrotreated heavy naphtha; And D- limonene (D-limonene) 1 to 10% by weight; provides an industrial electrical equipment cleaning composition for preventing electrical fires containing.
구체적으로 상기 수소처리된 경질 정제유는, 탄소 수 13 내지 14의 이소파라핀을 포함할 수 있다.Specifically, the hydrogen-treated light refined oil may include isoparaffins having 13 to 14 carbon atoms.
구체적으로 상기 수소처리된 중질 나프타는 끓는점이 150 내지 200℃이고 인화점이 60 내지 65℃일 수 있다.Specifically, the hydrotreated heavy naphtha may have a boiling point of 150 to 200 °C and a flash point of 60 to 65 °C.
상기 목적을 달성하기 위한 본 발명의 또 다른 실시예에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 개질 폴리디메틸실록산 1 내지 5 중량%;를 더 포함할 수 있다. 구체적으로, 상기 D-리모넨과 상기 개질 폴리디메틸실록산의 중량비(D-리모넨:개질 폴리디메틸실록산)는 1:0.5 내지 1:1일 수 있다.Industrial electrical equipment cleaner composition for preventing electrical fires according to another embodiment of the present invention for achieving the above object may further include 1 to 5% by weight of modified polydimethylsiloxane. Specifically, the weight ratio between the D-limonene and the modified polydimethylsiloxane (D-limonene:modified polydimethylsiloxane) may be 1:0.5 to 1:1.
구체적으로 상기 개질 폴리디메틸실록산은, 말단기가 히드록시기로 개질된 폴리디메틸실록산일 수 있다.Specifically, the modified polydimethylsiloxane may be a polydimethylsiloxane having a terminal group modified with a hydroxyl group.
상기 목적을 달성하기 위한 본 발명의 또 다른 실시예에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 염화나트륨 수용액 0.1 내지 1.0 중량%를 더 포함할 수 있다.Industrial electrical equipment cleaner composition for preventing electrical fires according to another embodiment of the present invention for achieving the above object may further include 0.1 to 1.0% by weight of an aqueous sodium chloride solution.
구체적으로,상기 염화나트륨 수용액은, 염화나트륨과 물이 8:2 내지 9:1의 중량비로 혼합된 혼합물일 수 있다. Specifically, the aqueous sodium chloride solution may be a mixture of sodium chloride and water in a weight ratio of 8:2 to 9:1.
상기 목적을 달성하기 위한 본 발명의 또 다른 실시예에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 용매 20 내지 30 중량%를 더 포함할 수 있다.Industrial electrical equipment cleaner composition for preventing electrical fires according to another embodiment of the present invention for achieving the above object may further include 20 to 30% by weight of a solvent.
구체적으로, 상기 용매는, 말단에 할로겐원자를 갖는 탄소 수 6 내지 8의 에스테르계 화합물을 포함할 수 있다.Specifically, the solvent may include an ester-based compound having 6 to 8 carbon atoms having a halogen atom at the terminal.
상기 과제의 해결 수단은, 본 발명의 특징을 모두 열거한 것은 아니다. 본 발명의 다양한 특징과 그에 따른 장점과 효과는 아래의 구체적인 실시예를 참조하여 보다 상세하게 이해될 수 있을 것이다.The solution to the above problems does not enumerate all the features of the present invention. Various features of the present invention and the advantages and effects thereof will be understood in more detail with reference to the following specific examples.
본 발명의 일 실시예에 따르면, 공급 중인 전력의 차단 없이 전기 및 전자통신장비 내에 오염된 미세먼지 또는 분진을 효과적으로 제거할 수 있고, 정밀 회로 및 전자소자에 손상을 주지 않으면서 스파크, 아크, 코로나 발생과 연계되는 인화성 화재의 위험을 예방할 수 있는 세정제 조성물을 제공할 수 있다.According to an embodiment of the present invention, it is possible to effectively remove fine dust or dust contaminated in electrical and electronic communication equipment without interruption of power being supplied, and sparks, arcs, and corona without damaging precision circuits and electronic devices. It is possible to provide a cleaning composition capable of preventing the risk of inflammable fire associated with occurrence.
상술한 효과와 더불어 본 발명의 구체적인 효과는 이하 발명을 실시하기 위한 구체적인 내용을 설명하면서 함께 기술한다.In addition to the above effects, specific effects of the present invention will be described together while explaining specific details for carrying out the present invention.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 각 구성을 보다 상세히 설명하나, 이는 하나의 예시에 불과할 뿐, 본 발명의 권리범위가 다음 내용에 의해 제한되지 아니한다.Hereinafter, each configuration of the present invention will be described in more detail so that those skilled in the art can easily practice it, but this is only one example, and the scope of the present invention is Not limited.
본 발명의 일 실시예에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 수소처리된 경질 정제유 30 내지 40 중량%; 수소처리된 중질 나프타(hydrotreated heavy naphtha) 25 내지 35 중량% 및 D-리모넨(D-limonene) 1 내지 10 중량%를 포함한다. 본 발명의 일 실시예에 따르면, 공급 중인 전력의 차단 없이 전기 및 전자통신장비 내에 오염된 미세먼지 또는 분진을 효과적으로 제거할 수 있고, 정밀 회로 및 전자소자에 손상을 주지 않으면서 스파크, 아크, 코로나 발생과 연계되는 인화성 화재의 위험을 예방할 수 있는 세정제 조성물을 제공할 수 있다.An industrial electrical equipment cleaner composition for preventing electrical fires according to an embodiment of the present invention includes 30 to 40% by weight of hydrogenated light refined oil; 25 to 35% by weight of hydrotreated heavy naphtha and 1 to 10% by weight of D-limonene. According to an embodiment of the present invention, it is possible to effectively remove fine dust or dust contaminated in electrical and electronic communication equipment without interruption of power being supplied, and sparks, arcs, and corona without damaging precision circuits and electronic devices. It is possible to provide a cleaning composition capable of preventing the risk of inflammable fire associated with occurrence.
이하에서는, 본 발명의 구성을 보다 상세히 설명한다.Hereinafter, the configuration of the present invention will be described in more detail.
본 발명에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 독성이 낮으며 세척력이 우수한 수소처리된 경질 정제유 30 내지 40 중량%를 포함한다. 구체적으로, 상기 수소처리된 경질 정제유는, 탄소 수 13 내지 14의 이소파라핀(isoparaffin)을 포함할 수 있다. 예를 들어, 상기 수소처리된 경질 정제유의 녹는점은 -60 내지 -50℃일 수 있고, 끓는점은 200 내지 250℃일 수 있고, 인화점은 200 내지 250℃일 수 있다.The industrial electrical equipment cleaner composition for preventing electrical fires according to the present invention includes 30 to 40% by weight of hydrotreated light refined oil having low toxicity and excellent cleaning power. Specifically, the hydrogen-treated light refined oil may include isoparaffin having 13 to 14 carbon atoms. For example, the hydrotreated light refined oil may have a melting point of -60 to -50 °C, a boiling point of 200 to 250 °C, and a flash point of 200 to 250 °C.
구체적으로 상기 수소처리된 경질 정제유의 함량은 상기 전기화재 예방용 산업전기설비 세정제 조성물의 전체 중량을 기준으로 32 내지 38 중량%, 더욱 구체적으로 33 내지 36 중량%, 더욱 구체적으로 34 내지 36 중량%일 수 있다. 상기 수소처리된 경질 정제유의 함량이 상기 수치 범위 미만일 경우 세정제 조성물의 세척력이 충분히 달성되지 못할 수 있고 상기 수치 범위를 초과할 경우 세정제 조성물의 균일성이 저하되어 세정 후 잔류물질이 발생하는 문제가 존재할 수 있다.Specifically, the content of the hydrotreated light refined oil is 32 to 38% by weight, more specifically 33 to 36% by weight, more specifically 34 to 36% by weight based on the total weight of the industrial electrical equipment cleaner composition for preventing electrical fires. can be If the content of the hydrogenated light refined oil is less than the above numerical range, the cleaning power of the detergent composition may not be sufficiently achieved, and if it exceeds the above numerical range, the uniformity of the detergent composition is lowered and there is a problem that residual substances are generated after cleaning. can
본 발명에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 수소처리된 중질 나프타(hydrotreated heavy naphtha) 25 내지 35 중량%를 포함한다. 구체적으로 상기 수소처리된 중질 나프타는, 나프타를 촉매 하에 수소 첨가된 나프타로서 미세먼지 또는 분진 등의 오염에 대한 세정력이 우수할 수 있다. 예를 들어, 상기 수소처리된 중질 나프타는 끓는점이 150 내지 200℃이고 인화점이 60 내지 65℃일 수 있다.The industrial electrical equipment cleaner composition for preventing electrical fires according to the present invention includes 25 to 35% by weight of hydrotreated heavy naphtha. Specifically, the hydrotreated heavy naphtha is naphtha obtained by hydrogenating naphtha under a catalyst, and may have excellent detergency against contamination such as fine dust or dust. For example, the hydrotreated heavy naphtha may have a boiling point of 150 to 200 °C and a flash point of 60 to 65 °C.
구체적으로 상기 수소처리된 중질 나프타의 함량은 상기 전기화재 예방용 산업전기설비 세정제 조성물의 전체 중량을 기준으로 27 내지 32 중량%, 더욱 구체적으로 28 내지 32 중량%, 더욱 구체적으로 29 내지 31 중량%일 수 있다. 상기 수소처리된 중질 나프타의 함량이 상기 수치 범위 미만일 경우 점도가 높아져 취급성이 떨어지고, 세정력이 저하될 뿐만 아니라, 세정제 조성물의 혼화성이 저하되어 세정제 조성물의 균일성에 문제가 생길 수 있고 상기 수치 범위를 초과할 경우 취급성은 양호해지나 휘발성이 높아지고 인화점이 낮아지는 위험성이 발생할 수 있다.Specifically, the content of the hydrotreated heavy naphtha is 27 to 32% by weight, more specifically 28 to 32% by weight, more specifically 29 to 31% by weight based on the total weight of the industrial electrical equipment cleaner composition for preventing electrical fires. can be When the content of the hydrotreated heavy naphtha is less than the above numerical range, the viscosity is increased and the handleability is deteriorated, and the cleaning power is lowered, and the miscibility of the detergent composition is lowered, which may cause a problem in the uniformity of the detergent composition. If it exceeds , handling becomes good, but the risk of high volatility and low flash point may occur.
본 발명에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 D-리모넨(D-limonene) 1 내지 10 중량%를 포함한다. 상기 D-리모넨은 과일의 껍질로부터 추출된 화합물로 인체에 무해하며 친환경적인 장점을 가짐과 동시에 미세먼지 또는 분진에 대한 세척력이 우수한 특징을 가질 수 있다. 종래 D-리모넨을 배합하지 않은 세정제 조성물은 석유 유래 화합물의 함량이 과도하게 높아 환경을 해하며 인체에 유해한 문제점이 있었다. 본 발명의 일 실시예에 따르면 친환경적이면서 인체에 무해한 D-리모넨을 세척력 조성물에 배합함으로써 세척력을 더욱 개선할 수 있다.The industrial electrical equipment cleaner composition for preventing electrical fires according to the present invention includes 1 to 10% by weight of D-limonene. The D-limonene is a compound extracted from the skin of a fruit, which is harmless to the human body and is environmentally friendly, and at the same time has excellent cleaning power against fine dust or dust. Conventional detergent compositions that do not contain D-limonene have a problem in that the content of petroleum-derived compounds is excessively high, which harms the environment and is harmful to the human body. According to one embodiment of the present invention, the detergency can be further improved by mixing D-limonene, which is environmentally friendly and harmless to the human body, into the detergency composition.
구체적으로 상기 D-리모넨은 하기 화학식 1로 표시되는 화합물일 수 있다.Specifically, the D-limonene may be a compound represented by Formula 1 below.
[화학식 1][Formula 1]
본 발명에 따른 D-리모넨은 예를 들어 감귤류 껍질로부터 추출된 화합물 또는 해당 기술분야의 통상의 기술자가 쉽게 구입할 수 있는 화합물일 수 있다.D-limonene according to the present invention may be, for example, a compound extracted from citrus peel or a compound readily available to a person skilled in the art.
구체적으로, 본 발명에 따른 D-리모넨의 함량은 상기 전기화재 예방용 산업전기설비 세정제 조성물의 전체 중량을 기준으로 2 내지 8 중량%, 더욱 구체적으로 3 내지 7 중량%, 더욱 구체적으로 4 내지 6 중량% 또는 5 내지 6 중량%일 수 있다. 상기 D-리모넨의 함량이 상기 수치 범위 미만일 경우 석유 유래 화합물의 함량이 상대적으로 높아져 환경을 해함과 동시에 인체에 유해할 수 있고, 상기 수치 범위를 초과할 경우 세정제 조성물의 균일성이 저하되어 세척력이 낮아지거나 안정성이 저하되는 문제가 발생할 수 있다.Specifically, the content of D-limonene according to the present invention is 2 to 8% by weight, more specifically 3 to 7% by weight, more specifically 4 to 6% by weight based on the total weight of the industrial electrical equipment cleaner composition for preventing electrical fires. weight percent or 5 to 6 weight percent. When the content of D-limonene is less than the above numerical range, the content of petroleum-derived compounds is relatively high, harming the environment and harming the human body. There may be a problem of lowering or deteriorating stability.
본 발명의 또 다른 실시예에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 개질 폴리디메틸실록산 1 내지 5 중량%를 더 포함할 수 있다. 구체적으로 상기 개질 폴리디메틸실록산의 중량평균분자량은 3,000 내지 5,000g/mol일 수 있고, 더욱 구체적으로 4,000 내지 4,500g/mol일 수 있고, 더욱 구체적으로 4,100 내지 4,300g/mol일 수 있고, 더욱 구체적으로 4,200 내지 4,300g/mol일 수 있다. 상기 개질 폴리디메틸실록산의 중량평균분자량이 상기 수치 범위 내를 만족할 때 취급성이 용이해질 뿐만 아니라 세정제 조성물의 균일성이 우수해질 수 있다.The industrial electrical equipment cleaner composition for preventing electrical fires according to another embodiment of the present invention may further include 1 to 5% by weight of modified polydimethylsiloxane. Specifically, the modified polydimethylsiloxane may have a weight average molecular weight of 3,000 to 5,000 g/mol, more specifically 4,000 to 4,500 g/mol, more specifically 4,100 to 4,300 g/mol, and more specifically It may be 4,200 to 4,300 g / mol. When the weight average molecular weight of the modified polydimethylsiloxane is within the above numerical range, not only easy handling but also excellent uniformity of the detergent composition can be obtained.
본 발명에 따른 개질 폴리디메틸실록산은 말단기가 히드록시기로 개질된 폴리디메틸실록산일 수 있다. 상기 개질 폴리디메틸실록산의 말단기가 히드록시기로 개질됨으로써 공급 중인 전력의 차단 없이 전기 및 전자통신장비 내에 오염된 미세먼지 또는 분진을 효과적으로 제거할 수 있다.The modified polydimethylsiloxane according to the present invention may be a polydimethylsiloxane having a terminal group modified with a hydroxyl group. By modifying the terminal group of the modified polydimethylsiloxane with a hydroxyl group, it is possible to effectively remove fine dust or dust contaminated in electrical and electronic communication equipment without interruption of power being supplied.
본 발명의 또 다른 실시예에 따르면, 상기 D-리모넨과 상기 개질 폴리디메틸실록산의 중량비(D-리모넨:개질 폴리디메틸실록산)는 1:0.5 내지 1:1일 수 있고 구체적으로 1:0.6 내지 1:1일 수 있고, 더욱 구체적으로 1:0.8 내지 1:1일 수 있다. 상기 D-리모넨과 상기 개질 폴리디메틸실록산의 중량비가 상기 수치 범위 내를 만족할 때 공급 중인 전력의 차단 없이 전기 및 전자통신장비 내에 오염된 미세먼지 또는 분진을 효과적으로 제거할 수 있고, 정밀 회로 및 전자소자에 손상을 주지 않으면서 스파크, 아크, 코로나 발생과 연계되는 인화성 화재의 위험을 예방할 수 있는 세정제 조성물을 제공할 수 있다.According to another embodiment of the present invention, the weight ratio of the D-limonene and the modified polydimethylsiloxane (D-limonene:modified polydimethylsiloxane) may be 1:0.5 to 1:1, specifically 1:0.6 to 1 :1, and more specifically, 1:0.8 to 1:1. When the weight ratio of the D-limonene to the modified polydimethylsiloxane is within the above numerical range, it is possible to effectively remove fine dust or dust polluted in electrical and electronic communication equipment without interruption of power being supplied, and precision circuits and electronic devices It is possible to provide a cleaning composition capable of preventing the risk of inflammable fire associated with sparks, arcs, and corona occurrence without damaging it.
본 발명의 또 다른 실시예에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 염화나트륨 수용액 0.1 내지 1.0 중량%를 더 포함할 수 있다. 상기 염화나트륨 수용액은 인체에 무해하며 고압 판넬 등의 산업전기설비에 있는 미세먼지 또는 분진 등을 효과적으로 제거할 수 있다.The industrial electrical equipment cleaner composition for preventing electrical fires according to another embodiment of the present invention may further include 0.1 to 1.0% by weight of an aqueous sodium chloride solution. The sodium chloride aqueous solution is harmless to the human body and can effectively remove fine dust or dust from industrial electrical equipment such as high-voltage panels.
상기 염화나트륨 수용액의 함량은 상기 전기화재 예방용 산업전기설비 세정제 조성물의 전체 중량을 기준으로 0.5 내지 1.0 중량%, 더욱 구체적으로 0.8 내지 1.0 중량%일 수 있다. 상기 염화나트륨 수용액의 함량이 상기 수치 범위 내를 만족할 때, 공급 중인 전력의 차단 없이 미세먼지 또는 분진을 효과적으로 제거할 수 있다.The content of the sodium chloride aqueous solution may be 0.5 to 1.0% by weight, more specifically 0.8 to 1.0% by weight based on the total weight of the industrial electrical equipment cleaner composition for preventing electrical fires. When the content of the sodium chloride aqueous solution satisfies the above numerical range, fine dust or dust can be effectively removed without interruption of power being supplied.
본 발명의 또 다른 실시예에 따르면, 상기 염화나트륨 수용액은 염화나트륨(NaCl)과 물이 8:2 내지 9:1의 중량비(NaCl:물)로 혼합된 혼합물일 수 있다. 상기 염화나트륨과 물이 상기 수치 범위 내로 혼합됨으로써, 미세먼지 또는 분진을 더욱 효과적으로 제거할 수 있다.According to another embodiment of the present invention, the aqueous sodium chloride solution may be a mixture of sodium chloride (NaCl) and water in a weight ratio (NaCl:water) of 8:2 to 9:1. By mixing the sodium chloride and water within the above numerical range, fine dust or dust can be more effectively removed.
본 발명의 또 다른 실시예에 따른 전기화재 예방용 산업전기설비 세정제 조성물은 용매 20 내지 30 중량%를 더 포함할 수 있다. 상기 용매는 예를 들어, 말단에 할로겐원자를 갖는 탄소 수 6 내지 8의 에스테르계 화합물을 포함할 수 있다. 상기 에스테르계 화합물은 포화 에스테르계 화합물로 탄소-탄소 다중결합을 포함하지 않는 화합물일 수 있다. 상기 용매의 함량이 상기 수치 범위 내를 만족할 때, 세정제 조성물의 균일성 및 세척력이 우수해질 수 있다.The industrial electrical equipment cleaner composition for preventing electrical fires according to another embodiment of the present invention may further include 20 to 30% by weight of a solvent. The solvent may include, for example, an ester-based compound having 6 to 8 carbon atoms having a halogen atom at the terminal. The ester-based compound is a saturated ester-based compound and may be a compound that does not contain a carbon-carbon multiple bond. When the content of the solvent is within the above numerical range, uniformity and detergency of the detergent composition may be improved.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 상세히 설명하나, 이는 하나의 예시에 불과할 뿐, 본 발명의 권리범위가 다음 내용에 의해 제한되지 아니한다.Hereinafter, an embodiment of the present invention will be described in detail so that those skilled in the art can easily practice it, but this is only one example, and the scope of the present invention is Not limited.
[제조예 1: 산업전기설비 세정제 조성물의 제조][Preparation Example 1: Preparation of industrial electrical equipment cleaning composition]
하기 표 1에 따른 산업전기설비 세정제 조성물을 제조하였다.An industrial electrical equipment cleaning composition according to Table 1 was prepared.
중량%unit:
weight%
수용액6) sodium chloride
aqueous solution 6)
2) CAS No. 64742-48-9
3) D-(+)-리모넨
4) 말단에 히드록시기가 형성되지 않은 상용 폴리디메틸실록산 Mw=4,200g/mol
5) 말단에 히드록시기가 형성된 폴리디메틸실록산(CAS No. 70131-67-8; Mw=4,200g/mol)
6) NaCl과 물이 8:2의 중량비로 혼합된 NaCl(aq)
7) 스토다드 용제(CAS No.8052-41-3)1) CAS No. 64742-47-8
2) CAS No. 64742-48-9
3) D-(+)-Limonene
4) Commercially available polydimethylsiloxane with no terminal hydroxy group Mw = 4,200 g/mol
5) Polydimethylsiloxane having a hydroxyl group at the end (CAS No. 70131-67-8; Mw = 4,200 g/mol)
6) NaCl (aq) mixed with NaCl and water in a weight ratio of 8:2
7) Stoddard Solvent (CAS No.8052-41-3)
[실험예: 세정제 조성물의 인화성 여부 및 세척력 평가][Experimental Example: Evaluation of Flammability and Detergency of Detergent Composition]
1) 세정제 조성물의 안정성 평가1) Evaluation of stability of detergent composition
미세먼지 및 분진이 흡착된 솜(1.5g)을 상기 실시예 및 비교예에 따른 세정제 조성물에 충분히 침지한 후, 시험판에 꺼내 놓았다. 순서대로 점화기에 불을 붙여 약 20 내지 30초간 점화 작업을 실시하였고, 전기 스파크와 유사한 환경의 실험을 위해 2 내지 3초 간격으로 점화 및 소화 작업을 반복하였다. 그 후 마지막에 세정제 조성물이 연소한 후에 솜의 성분만 남아서 연소하는 현상까지 확인한 후 인화성 여부를 ○(우수), △(보통) 및 ×(미흡)로 구분하여 하기 표 2에 평가하였다.Fine dust and dust-adsorbed cotton (1.5 g) was sufficiently immersed in the detergent composition according to Examples and Comparative Examples, and then taken out on a test plate. The igniter was lit in order and ignition was performed for about 20 to 30 seconds, and ignition and extinguishing were repeated at intervals of 2 to 3 seconds for an experiment in an environment similar to an electric spark. After that, after the detergent composition was finally burned, only the components of the cotton remained to check the burning phenomenon, and then the flammability was classified into ○ (excellent), △ (normal), and × (insufficient), and evaluated in Table 2 below.
2)세정제 조성물의 세척력 평가2) Evaluation of cleaning power of cleaning composition
고압 분사기를 이용하여, 고압 판넬에 붙어있는 미세먼지를 향해 5.2kg/cm2의 분사압력과 10초 동안 상기 실시예 및 비교예에 따른 세정제 조성물을 분사하였다. 그 후 10년 이상의 해당 기술분야의 전문가가 세척 후의 만족도를 1 내지 10점으로 평가한 후, 그 결과를 하기 표 2에 표시하였다.Using a high-pressure sprayer, the detergent compositions according to Examples and Comparative Examples were sprayed at a spray pressure of 5.2 kg/cm 2 for 10 seconds toward the fine dust attached to the high-pressure panel. After that, experts in the relevant technical field for more than 10 years evaluated the satisfaction after washing on a scale of 1 to 10, and the results are shown in Table 2 below.
상기 표 2에서 비교예 1과 실시예 1을 비교하면 D-리모넨의 첨가로 인해 고압 판넬에 있는 미세먼지를 효과적으로 제거할 수 있을 뿐만 아니라 전기화재를 효과적으로 예방할 수 있음을 확인할 수 있다.Comparing Comparative Example 1 and Example 1 in Table 2, it can be seen that fine dust in the high-pressure panel can be effectively removed due to the addition of D-limonene, as well as electrical fire can be effectively prevented.
비교예 2와 실시예 1을 비교하면 D-리모넨의 함량이 1 내지 10 중량%일 때 세척력과 안정성을 동시에 달성할 수 있음을 확인할 수 있다.Comparing Comparative Example 2 and Example 1, it can be seen that detergency and stability can be simultaneously achieved when the content of D-limonene is 1 to 10% by weight.
또한, 실시예 2와 3을 비교하면, 말단에 히드록시기가 형성된 개질 폴리디메틸실록산과 D-리모넨의 조합으로 인해 세척력이 더욱 개선됨을 확인할 수 있다.In addition, when comparing Examples 2 and 3, it can be seen that the detergency is further improved due to the combination of modified polydimethylsiloxane having a hydroxyl group at the terminal and D-limonene.
실시예 1과 실시예 4를 비교하면 NaCl(aq)의 추가적인 첨가로 인해 세척력이 더욱 개선됨을 확인할 수 있고, 실시예 4 및 5를 비교하면 개질 폴리디메틸실록산과 NaCl(aq)의 조합으로 인해 세척력과 안정성을 동시에 달성할 수 있음을 확인할 수 있다.Comparing Example 1 and Example 4, it can be seen that the cleaning power is further improved due to the additional addition of NaCl (aq), and comparing Examples 4 and 5, cleaning power is due to the combination of modified polydimethylsiloxane and NaCl (aq). and stability can be achieved simultaneously.
상기 실험결과를 종합적으로 해석할 때, 본 발명의 일 실시예에 따르면, 공급 중인 전력의 차단 없이 전기 및 전자통신장비 내에 오염된 미세먼지 또는 분진을 효과적으로 제거할 수 있고, 정밀 회로 및 전자소자에 손상을 주지 않으면서 스파크, 아크, 코로나 발생과 연계되는 인화성 화재의 위험을 예방할 수 있는 세정제 조성물을 제공할 수 있다.When comprehensively interpreting the above experimental results, according to an embodiment of the present invention, it is possible to effectively remove fine dust or dust contaminated in electrical and electronic communication equipment without interruption of power being supplied, and to precision circuits and electronic devices. It is possible to provide a cleaning composition capable of preventing the risk of inflammable fire associated with sparks, arcs, and corona without causing damage.
이상에서 본 발명의 바람직한 실시예들에 대하여 상세하게 설명하였지만 본 발명의 권리 범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리 범위에 속하는 것이다.Although the preferred embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improvements of those skilled in the art using the basic concept of the present invention defined in the following claims are also present. It falls within the scope of the right of invention.
Claims (9)
수소처리된 중질 나프타(hydrotreated heavy naphtha) 25 내지 35 중량%;
D-리모넨(D-limonene) 1 내지 10 중량%; 및
용매 20 내지 30 중량% ;를 포함하고,
상기 용매는,
말단에 할로겐원자를 갖는 탄소 수 6 내지 8의 에스테르계 화합물을 포함하는
전기화재 예방용 산업전기설비 세정제 조성물.
30 to 40% by weight of a hydrotreated light refined oil;
25 to 35% by weight of hydrotreated heavy naphtha;
1 to 10% by weight of D-limonene; and
20 to 30% by weight of a solvent;
The solvent is
containing an ester-based compound having 6 to 8 carbon atoms having a halogen atom at the terminal
Industrial electrical equipment cleaning composition for electrical fire prevention.
상기 수소처리된 경질 정제유는,
탄소 수 13 내지 14의 이소파라핀을 포함하는,
전기화재 예방용 산업전기설비 세정제 조성물.
According to claim 1,
The hydrotreated light refined oil,
Containing isoparaffins having 13 to 14 carbon atoms,
Industrial electrical equipment cleaning composition for electrical fire prevention.
상기 수소처리된 중질 나프타는 끓는점이 150 내지 200℃이고 인화점이 60 내지 65℃인,
전기화재 예방용 산업전기설비 세정제 조성물.
According to claim 1,
The hydrotreated heavy naphtha has a boiling point of 150 to 200 ° C and a flash point of 60 to 65 ° C,
Industrial electrical equipment cleaning composition for electrical fire prevention.
개질 폴리디메틸실록산 1 내지 5 중량%;를 더 포함하고,
상기 D-리모넨과 상기 개질 폴리디메틸실록산의 중량비(D-리모넨:개질 폴리디메틸실록산)는 1:0.5 내지 1:1인,
전기화재 예방용 산업전기설비 세정제 조성물.
According to claim 1,
1 to 5% by weight of modified polydimethylsiloxane; further comprising,
The weight ratio of the D-limonene to the modified polydimethylsiloxane (D-limonene: modified polydimethylsiloxane) is 1:0.5 to 1:1,
Industrial electrical equipment cleaning composition for electrical fire prevention.
상기 개질 폴리디메틸실록산은,
말단기가 히드록시기로 개질된 폴리디메틸실록산인,
전기화재 예방용 산업전기설비 세정제 조성물.
According to claim 4,
The modified polydimethylsiloxane,
The terminal group is a polydimethylsiloxane modified with a hydroxyl group,
Industrial electrical equipment cleaning composition for electrical fire prevention.
염화나트륨 수용액 0.1 내지 1.0 중량%;를 더 포함하는
전기화재 예방용 산업전기설비 세정제 조성물.
According to claim 1,
0.1 to 1.0% by weight of sodium chloride aqueous solution; further comprising
Industrial electrical equipment cleaning composition for electrical fire prevention.
상기 염화나트륨 수용액은,
염화나트륨과 물이 8:2 내지 9:1의 중량비로 혼합된 혼합물인,
전기화재 예방용 산업전기설비 세정제 조성물.
According to claim 6,
The sodium chloride aqueous solution,
A mixture of sodium chloride and water in a weight ratio of 8:2 to 9:1,
Industrial electrical equipment cleaning composition for electrical fire prevention.