KR102407983B1 - Multi-layered ceramic electronic component and method for manufacturing the same - Google Patents
Multi-layered ceramic electronic component and method for manufacturing the same Download PDFInfo
- Publication number
- KR102407983B1 KR102407983B1 KR1020200103334A KR20200103334A KR102407983B1 KR 102407983 B1 KR102407983 B1 KR 102407983B1 KR 1020200103334 A KR1020200103334 A KR 1020200103334A KR 20200103334 A KR20200103334 A KR 20200103334A KR 102407983 B1 KR102407983 B1 KR 102407983B1
- Authority
- KR
- South Korea
- Prior art keywords
- electronic component
- manufacturing
- multilayer ceramic
- ceramic electronic
- internal electrode
- Prior art date
Abstract
본 발명의 일 실시 형태에 따른 적층 세라믹 전자부품의 제조 방법은 세라믹 그린시트를 마련하는 단계; W, Mo, Cr 및 Co 중 1 이상을 그 합계로 1~20 wt% 포함하며 Sn을 포함하는 도전성 분말을 포함하는 내부 전극용 페이스트를 상기 세라믹 그린시트 상에 도포하여 내부 전극 패턴을 형성하는 단계; 상기 내부 전극 패턴이 형성된 세라믹 그린시트를 적층하여 세라믹 적층체를 형성하는 단계; 및 상기 세라믹 적층체를 소성하여 유전체층 및 내부 전극을 포함하는 바디를 형성하는 단계;를 포함한다. A method of manufacturing a multilayer ceramic electronic component according to an embodiment of the present invention includes: preparing a ceramic green sheet; Forming an internal electrode pattern by applying an internal electrode paste including a conductive powder containing Sn and containing 1 to 20 wt% of W, Mo, Cr, and Co in total on the ceramic green sheet. ; forming a ceramic laminate by stacking the ceramic green sheets on which the internal electrode patterns are formed; and forming a body including a dielectric layer and an internal electrode by firing the ceramic laminate.
Description
본 발명은 적층 세라믹 전자부품 및 그 제조방법에 관한 것이다.The present invention relates to a multilayer ceramic electronic component and a method for manufacturing the same.
일반적으로 커패시터, 인덕터, 압전 소자, 바리스터 또는 서미스터 등의 세라믹 재료를 사용하는 전자부품은 세라믹 재료로 이루어진 바디, 바디 내부에 형성된 내부 전극 및 상기 내부 전극과 접속되도록 바디 표면에 설치된 외부전극을 구비한다.In general, an electronic component using a ceramic material such as a capacitor, an inductor, a piezoelectric element, a varistor or thermistor includes a body made of a ceramic material, an internal electrode formed inside the body, and an external electrode installed on the body surface to be connected to the internal electrode. .
적층 세라믹 전자부품 중 적층 세라믹 커패시터는 적층된 복수의 유전체층, 일 유전체층을 사이에 두고 대향 배치되는 내부 전극, 상기 내부 전극에 전기적으로 접속된 외부전극을 포함한다.Among multilayer ceramic electronic components, a multilayer ceramic capacitor includes a plurality of stacked dielectric layers, internal electrodes disposed to face each other with one dielectric layer interposed therebetween, and external electrodes electrically connected to the internal electrodes.
적층 세라믹 커패시터는 소형이면서 고용량이 보장되고, 실장이 용이하다는 장점으로 인하여 컴퓨터, PDA, 휴대폰 등의 이동 통신장치의 부품으로서 널리 사용되고 있다.Multilayer ceramic capacitors are widely used as components of mobile communication devices, such as computers, PDAs, and mobile phones, due to their small size, high capacity, and easy mounting.
최근 전기, 전자기기 산업의 고성능화 및 경박단소화에 따라 전자부품에 있어서도 소형, 고성능 및 초고용량화가 요구되고 있다. Recently, in accordance with the high performance and light, thin and compact in the electrical and electronic device industries, small size, high performance, and ultra high capacity are required for electronic components as well.
특히, 적층 세라믹 커패시터의 고용량화 및 소형화에 따라 단위 부피당 정전 용량을 극대화 시키는 기술이 필요하다.In particular, there is a need for a technique for maximizing the capacitance per unit volume in accordance with the high-capacity and miniaturization of multilayer ceramic capacitors.
따라서, 내부 전극의 경우 면적은 최대로 구현하면서 부피를 최소화하여 적층수 증가를 통한 고용량을 구현하여야 한다.Therefore, in the case of the internal electrode, it is necessary to realize a high capacity by increasing the number of layers by minimizing the volume while maximizing the area.
그러나, 내부 전극이 박층화 될수록 면적 대비 두께의 비율이 낮아 소결 구동력이 증가하며, 이로 인하여 전극 끊김 및 뭉침의 증가가 심화하게 된다. However, as the internal electrode becomes thinner, the ratio of the thickness to the area is lowered, thereby increasing the sintering driving force, which intensifies the increase in electrode breakage and agglomeration.
따라서, 고용량 적층 세라믹 커패시터를 구현하기 위해, 박층의 내부 전극을 형성시 문제가 되는 전극 끊김 현상과 전극의 뭉침 현상을 억제하여 신뢰성 높은 소형, 고용량 적층 세라믹 커패시터를 구현할 수 있는 방법이 요구된다.Therefore, in order to realize a high-capacity multilayer ceramic capacitor, there is a need for a method capable of implementing a highly reliable small-sized, high-capacity multilayer ceramic capacitor by suppressing electrode breakage and electrode aggregation, which are problems when forming a thin-layered internal electrode.
본 발명의 목적 중 하나는 전극 끊김 현상과 전극의 뭉침 현상을 억제하여 신뢰성 높은 소형, 고용량 적층 세라믹 커패시터를 구현할 수 있는 적층 세라믹 전자부품의 제조방법을 제공하기 위함이다. One of the objects of the present invention is to provide a method of manufacturing a multilayer ceramic electronic component capable of realizing a highly reliable small and high-capacity multilayer ceramic capacitor by suppressing electrode breakage and electrode aggregation.
본 발명의 일 실시예에 따르면, 세라믹 그린시트를 마련하는 단계; W, Mo, Cr 및 Co 중 1 이상을 그 합계로 1~20 wt% 포함하며 Sn을 포함하는 도전성 분말을 포함하는 내부 전극용 페이스트를 상기 세라믹 그린시트 상에 도포하여 내부 전극 패턴을 형성하는 단계; 상기 내부 전극 패턴이 형성된 세라믹 그린시트를 적층하여 세라믹 적층체를 형성하는 단계; 및 상기 세라믹 적층체를 소성하여 유전체층 및 내부전극을 포함하는 바디를 형성하는 단계;를 포함하는 적층 세라믹 전자부품의 제조 방법을 제공한다.According to an embodiment of the present invention, the method comprising: preparing a ceramic green sheet; Forming an internal electrode pattern by applying an internal electrode paste including a conductive powder containing Sn and containing 1 to 20 wt% of W, Mo, Cr, and Co in total on the ceramic green sheet. ; forming a ceramic laminate by laminating the ceramic green sheets on which the internal electrode patterns are formed; and forming a body including a dielectric layer and an internal electrode by firing the ceramic multilayer body.
또한, 본 발명의 일 실시예에 따른 적층 세라믹 전자부품의 제조 방법에 의해 제조된 적층 세라믹 전자부품으로서, 유전체층 및 내부전극을 포함하는 세라믹 바디; 및 상기 세라믹 바디에 배치되는 외부 전극;을 포함하고, 상기 내부 전극은 금속 결정립과, 상기 금속 결정립을 둘러싸고 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층을 포함하는 적층 세라믹 전자부품을 제공한다. In addition, there is provided a multilayer ceramic electronic component manufactured by the method for manufacturing a multilayer ceramic electronic component according to an embodiment of the present invention, comprising: a ceramic body including a dielectric layer and an internal electrode; and an external electrode disposed on the ceramic body, wherein the internal electrode includes a metal crystal grain and a composite layer surrounding the metal crystal grain and containing at least one of W, Mo, Cr, and Co and Ni and Sn. Ceramic electronic components are provided.
본 발명에 따르면 W, Mo, Cr 및 Co 중 1 이상을 그 합계로 1~20 wt% 포함하며 Sn을 포함하는 도전성 분말을 포함하는 내부 전극용 페이스트를 이용함으로써 내부 전극 뭉침 현상 및 내부 전극 끊김 현상을 억제할 수 있는 효과가 있다. According to the present invention, the internal electrode aggregation phenomenon and internal electrode breakage phenomenon by using the internal electrode paste containing 1 to 20 wt% of W, Mo, Cr, and Co at least 1 to 20 wt% in total and containing Sn-containing conductive powder has a deterrent effect.
도 1은 Ni과 W의 합금(발명예 1), W가 포함되지 않은 Ni 분말(비교예 1), 및 S를 2000ppm 포함하는 Ni 분말(비교예 2)의 열수축 거동을 비교한 그래프이다.
도 2는 내부 전극 패턴이 형성된 세라믹 그린시트를 개략적으로 나타낸 도면이다.
도 3은 본 발명의 일 실시예에 따른 적층 세라믹 전자부품의 제조 방법에 의해 제조된 적층 세라믹 전자부품을 개략적으로 나타낸 사시도이다.
도 4는 도 3의 I-I`선을 따른 단면을 나타낸 도면이다.
도 5는 도 4의 A 부분을 확대하여 나타낸 도면이다. 1 is a graph comparing the thermal shrinkage behavior of an alloy of Ni and W (Invention Example 1), Ni powder without W (Comparative Example 1), and Ni powder containing 2000 ppm of S (Comparative Example 2).
2 is a view schematically illustrating a ceramic green sheet on which an internal electrode pattern is formed.
3 is a perspective view schematically illustrating a multilayer ceramic electronic component manufactured by the method of manufacturing a multilayer ceramic electronic component according to an exemplary embodiment of the present invention.
FIG. 4 is a view showing a cross-section taken along line II′ of FIG. 3 .
FIG. 5 is an enlarged view of part A of FIG. 4 .
이하, 구체적인 실시형태 및 첨부된 도면을 참조하여 본 발명의 실시형태를 설명한다. 그러나, 본 발명의 실시형태는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 이하 설명하는 실시형태로 한정되는 것은 아니다. 또한, 본 발명의 실시형태는 통상의 기술자에게 본 발명을 더욱 완전하게 설명하기 위해서 제공되는 것이다. 따라서, 도면에서의 요소들의 형상 및 크기 등은 보다 명확한 설명을 위해 과장될 수 있으며, 도면상의 동일한 부호로 표시되는 요소는 동일한 요소이다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described with reference to specific embodiments and the accompanying drawings. However, the embodiment of the present invention may be modified in various other forms, and the scope of the present invention is not limited to the embodiments described below. Further, the embodiments of the present invention are provided in order to more completely explain the present invention to those skilled in the art. Accordingly, the shapes and sizes of elements in the drawings may be exaggerated for clearer description, and elements indicated by the same reference numerals in the drawings are the same elements.
그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하고, 여러 층 및 영역을 명확하게 표현하기 위하여 두께를 확대하여 나타내었으며, 동일한 사상의 범위 내의 기능이 동일한 구성요소는 동일한 참조부호를 사용하여 설명한다. 나아가, 명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다.And in order to clearly explain the present invention in the drawings, parts irrelevant to the description are omitted, and the thickness is enlarged to clearly express various layers and regions, and components having the same function within the scope of the same idea are referred to as the same. It is explained using symbols. Furthermore, throughout the specification, when a part "includes" a certain element, it means that other elements may be further included, rather than excluding other elements, unless otherwise stated.
도면에서, X 방향은 제1 방향, L 방향 또는 길이 방향, Y 방향은 제2 방향, W 방향 또는 폭 방향, Z 방향은 제3 방향, T 방향 또는 두께 방향으로 정의될 수 있다.In the drawings, an X direction may be defined as a first direction, an L direction or a length direction, a Y direction may be defined as a second direction, a W direction or a width direction, and a Z direction may be defined as a third direction, a T direction, or a thickness direction.
도 1은 Ni과 W의 합금(발명예 1), W가 포함되지 않은 Ni 분말(비교예 1), 및 S를 2000ppm 포함하는 Ni 분말(비교예 2)의 열수축 거동을 비교한 그래프이다. 1 is a graph comparing the thermal shrinkage behavior of an alloy of Ni and W (Invention Example 1), Ni powder without W (Comparative Example 1), and Ni powder containing 2000 ppm of S (Comparative Example 2).
도 2는 내부 전극 패턴이 형성된 세라믹 그린시트를 개략적으로 나타낸 도면이다. 2 is a view schematically illustrating a ceramic green sheet on which an internal electrode pattern is formed.
도 3은 본 발명의 일 실시예에 따른 적층 세라믹 전자부품의 제조 방법에 의해 제조된 적층 세라믹 전자부품을 개략적으로 나타낸 사시도이다. 3 is a perspective view schematically illustrating a multilayer ceramic electronic component manufactured by the method for manufacturing a multilayer ceramic electronic component according to an exemplary embodiment of the present invention.
도 4는 도 3의 I-I`선을 따른 단면을 나타낸 도면이다. FIG. 4 is a view showing a cross-section taken along line I-I` of FIG. 3 .
도 5는 도 4의 A 부분을 확대하여 나타낸 도면이다. FIG. 5 is an enlarged view of part A of FIG. 4 .
이하, 도 1 내지 도 5를 참조하여, 본 발명의 일 측면에 따른 적층 세라믹 전자부품의 제조방법 및 그에 따라 제조된 적층 세라믹 전자부품에 대하여 상세히 설명한다. Hereinafter, a method of manufacturing a multilayer ceramic electronic component according to an aspect of the present invention and a multilayer ceramic electronic component manufactured according to the method will be described in detail with reference to FIGS. 1 to 5 .
적층 세라믹 전자부품의 제조방법Manufacturing method of multilayer ceramic electronic components
본 발명의 일 측면에 따른 적층 세라믹 전자부품의 제조방법은 세라믹 분말을 포함하는 세라믹 그린시트를 마련하는 단계; W, Mo, Cr 및 Co 중 1 이상을 그 합계로 1~20 wt% 포함하며 Sn을 포함하는 도전성 분말을 포함하는 내부 전극용 페이스트를 상기 세라믹 그린시트 상에 도포하여 내부 전극 패턴을 형성하는 단계; 상기 내부 전극 패턴이 형성된 세라믹 그린시트를 적층하여 세라믹 적층체를 형성하는 단계; 및 상기 세라믹 적층체를 소성하여 유전체층 및 내부 전극을 포함하는 바디를 형성하는 단계;를 포함한다. According to an aspect of the present invention, a method of manufacturing a multilayer ceramic electronic component includes: preparing a ceramic green sheet including ceramic powder; Forming an internal electrode pattern by applying an internal electrode paste including a conductive powder containing Sn and containing 1 to 20 wt% of W, Mo, Cr, and Co in total on the ceramic green sheet. ; forming a ceramic laminate by laminating the ceramic green sheets on which the internal electrode patterns are formed; and forming a body including a dielectric layer and an internal electrode by firing the ceramic laminate.
세라믹 그린시트를 마련하는 단계Steps to prepare a ceramic green sheet
세라믹 분말을 포함하는 세라믹 그린시트를 마련한다. A ceramic green sheet including ceramic powder is prepared.
상기 세라믹 그린시트는 세라믹 분말, 바인더, 용제 등을 혼합하여 슬러리를 제조하고, 상기 슬러리를 닥터 블레이드 법으로 수 ㎛의 두께를 갖는 시트(sheet)형으로 제작할 수 있다. 상기 세라믹 그린시트는 이후 소결되어 도 4에 도시된 바와 같이 일 유전체층(111)을 형성할 수 있다.The ceramic green sheet may be prepared by mixing ceramic powder, a binder, a solvent, etc. to prepare a slurry, and the slurry may be prepared in a sheet type having a thickness of several μm by a doctor blade method. The ceramic green sheet may then be sintered to form a
상기 세라믹 그린시트의 두께는 0.6 ㎛ 이하일 수 있으며, 이로 인하여 소성 후 유전체층의 두께는 0.4 ㎛ 이하일 수 있다. The thickness of the ceramic green sheet may be 0.6 μm or less, and for this reason, the thickness of the dielectric layer after firing may be 0.4 μm or less.
본 발명의 일 실시예에 따르면 유전체층 및 내부 전극이 매우 얇은 경우에도 효과적으로 전극 끊김 및 뭉침의 증가를 억제할 수 있기 때문에 0.4 ㎛ 이하의 두께를 가지는 유전체층을 형성할 수 있다. According to an embodiment of the present invention, even when the dielectric layer and the internal electrode are very thin, since the increase in electrode breakage and aggregation can be effectively suppressed, the dielectric layer having a thickness of 0.4 μm or less can be formed.
내부 전극 패턴을 형성하는 단계forming an inner electrode pattern
W, Mo, Cr 및 Co 중 1 이상을 그 합계로 1~20 wt% 포함하며 Sn을 포함하는 도전성 분말을 포함하는 내부 전극용 페이스트를 상기 세라믹 그린시트 상에 도포하여 내부 전극 패턴을 형성한다. An internal electrode pattern is formed by coating an internal electrode paste including a conductive powder containing Sn and containing 1 to 20 wt% of W, Mo, Cr, and Co in total on the ceramic green sheet.
상기 내부 전극 패턴은 스크린 인쇄법 또는 그라비아 인쇄법에 의하여 형성될 수 있다.The internal electrode pattern may be formed by a screen printing method or a gravure printing method.
내부 전극용 페이스트와 세라믹 그린시트와의 소결 온도 차이로 인해 전극 끊김 현상, 전극의 뭉침 현상 등 여러가지 문제점이 발생할 수 있다. 특히, 내부 전극의 두께가 얇아질수록 이러한 문제점이 발생할 확률이 점점 커진다. Due to the difference in sintering temperature between the internal electrode paste and the ceramic green sheet, various problems such as electrode breakage and electrode aggregation may occur. In particular, as the thickness of the internal electrode becomes thinner, the probability of occurrence of this problem gradually increases.
전극 끊김 현상, 전극의 뭉침 현상 등의 문제점을 해결하기 위하여, 공재를 분산시켜 도전성 분말의 소결을 지연시키는 방안이 개발되었으나, 공재는 세라믹 물질로 니켈 표면과 접촉성이 떨어져 소결 초기단계에서 제한적으로 소결을 지연시키는 역할을 하며, 소결 후 유전체 층으로 빠져 나가 유전체 특성을 변화시키는 원인이 된다. In order to solve problems such as electrode breakage and electrode aggregation, a method of delaying the sintering of the conductive powder by dispersing the common material has been developed. It plays a role in delaying sintering, and it leaks into the dielectric layer after sintering and causes changes in dielectric properties.
또한, 시트 강도를 구현하기 위해 사용한 유기물들의 일부가 가소 시 악성 잔탄(결정화된 carbon)으로 남아 전극 뭉침 현상, 유전체층의 불균일 소결 등의 문제점을 유발할 수 있다. 이러한 문제점은 공정 최적화로 일부 해결할 수는 있었으나, 내부 전극 및 유전체층의 박층화가 진행됨에 따라 공정 최적화만으로는 해결하기 어렵게 되었다. In addition, some of the organic materials used to implement the sheet strength remain as malignant xanthan (crystallized carbon) during calcination, which may cause problems such as electrode aggregation and non-uniform sintering of the dielectric layer. This problem could be partially solved by process optimization, but as the internal electrodes and dielectric layers became thinner, it became difficult to solve only by process optimization.
본 발명의 일 실시예에 따라 도전성 분말에 고융점 메탈(metal)인 W, Mo, Cr 및 Co 중 1 이상을 첨가 시, 소결 초기단계의 니켈 소결을 지연시킬 뿐 아니라 이후 높은 온도에도 동일하게 작용하여 효과적으로 전극의 열화를 막고, 소성 후에는 유전체 층으로 빠져나가지 않고 내부 전극에 존재하여 유전체의 특성 변화를 초래하지 않는다.According to an embodiment of the present invention, when one or more of W, Mo, Cr, and Co, which are high-melting-point metals, is added to the conductive powder, it not only delays the nickel sintering in the initial stage of sintering, but also acts the same at a high temperature thereafter. Thus, it effectively prevents the deterioration of the electrode, and after firing, it does not escape into the dielectric layer and is present in the internal electrode and does not cause a change in the properties of the dielectric.
또한, Sn을 포함하지 않는 도전성 분말을 이용하는 경우 전극 표면에 실타래처럼 관찰되는 악성 잔탄(결정화된 carbon)이 생성되어 전극 뭉침 현상, 유전체층의 불균일 소결 등의 문제점이 발생할 우려가 있으나, 본 발명의 일 실시예에 따라 Sn을 첨가하는 경우에는 가소 시 도전성 분말의 탈수소화 촉매 역할로 인한 악성 잔탄(결정화된 carbon)의 생성을 억제할 수 있다. In addition, when a conductive powder that does not contain Sn is used, malignant xanthan (crystallized carbon), which is observed like a skein of thread, is generated on the electrode surface, which may cause problems such as electrode aggregation and non-uniform sintering of the dielectric layer. According to an embodiment, when Sn is added, the generation of malignant xanthan (crystallized carbon) due to the role of a catalyst for dehydrogenation of the conductive powder during calcination may be suppressed.
또한, Sn은 도전성 분말에 고용은 잘 되지 않으나 도전성 분말과의 젖음성은 좋고, 융점이 낮기 때문에 소성 과정에서 내부 전극의 결정립의 표면에 농화되어 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층을 형성함으로써 결정립의 성장을 억제할 수 있으며, 고융점 메탈(metal)의 소결 지연 효과를 더욱 향상시키는 역할을 한다. In addition, Sn does not dissolve well in the conductive powder, but has good wettability with the conductive powder and has a low melting point. It is possible to suppress the growth of crystal grains by forming a composite layer containing
따라서, 본 발명의 일 실시예에 따르면 전극 끊김 및 뭉침의 증가를 억제할 수 있으며, 특히 유전체층 및 내부 전극이 매우 얇은 경우에도 효과적으로 전극 끊김 및 뭉침의 증가를 억제할 수 있다. Therefore, according to an embodiment of the present invention, it is possible to suppress the increase in electrode breakage and aggregation, and in particular, even when the dielectric layer and the internal electrode are very thin, it is possible to effectively suppress the increase in electrode breakage and aggregation.
또한, 도 5에 도시된 바와 같이 Sn이 소성 과정에서 내부 전극의 결정립(121a)의 표면에 농화되어 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)을 형성함으로써 결정립의 성장을 억제할 수 있다.In addition, as shown in FIG. 5, Sn is concentrated on the surface of the
도 1은 W를 첨가한 Ni 분말(발명예 1), W가 포함되지 않은 Ni 분말(비교예 1), 및 S를 2000ppm 포함하는 Ni 분말(비교예 2)의 열수축 거동을 비교한 그래프이다. 발명예 1의 W의 함량은 Ni 분말 대비 10 wt%이었다. 1 is a graph comparing the thermal shrinkage behavior of Ni powder with W added (Invention Example 1), Ni powder without W (Comparative Example 1), and Ni powder containing 2000 ppm S (Comparative Example 2). The content of W in Inventive Example 1 was 10 wt% compared to the Ni powder.
도 1을 참조하면, 비교예 1, 비교예 2 및 발명예 1의 -5% 수축 온도가 각각 271℃, 476℃ 및 525℃로 발명예 1의 열수축 거동이 제일 우수한 것을 확인할 수 있다. Referring to FIG. 1 , the -5% shrinkage temperatures of Comparative Examples 1, 2, and 1 were 271° C., 476° C., and 525° C., respectively, indicating that the heat shrinkage behavior of Inventive Example 1 was the best.
이때, W, Mo, Cr 및 Co 중 1 이상은 그 합계로 도전성 분말 대비 1~20 wt% 포함될 수 있다. In this case, at least one of W, Mo, Cr, and Co may be included in an amount of 1 to 20 wt% compared to the conductive powder in total.
W, Mo, Cr 및 Co 중 1 이상이 그 합계로 1 wt% 미만일 경우에는 전극의 연결성이 저하될 우려가 있고, 20 wt% 초과일 경우에는 내부 전극과 유전체층의 계면에 존재하는 산화물 형태의 금속의 양이 증가되어 정전용량을 저하시킬 우려가 있다. When at least one of W, Mo, Cr, and Co is less than 1 wt% in total, there is a risk of deterioration of electrode connectivity, and when it exceeds 20 wt%, an oxide-type metal present at the interface between the internal electrode and the dielectric layer is increased, and there is a risk of lowering the capacitance.
또한, 도전성 분말 대비 Sn 함량은 1.5 wt% 이상일 수 있다. In addition, the Sn content relative to the conductive powder may be 1.5 wt% or more.
Sn 함량이 1.5 wt% 미만인 경우에는 악성 잔탄(결정화된 carbon)을 억제하는 효과 또는 결정립의 성장을 억제하는 효과가 불충분할 수 있다. 한편, 도전성 분말 대비 Sn 함량의 상한은 특별히 제한할 필요는 없으나, 4.0 wt% 이하일 수 있다. If the Sn content is less than 1.5 wt%, the effect of inhibiting malignant xanthan (crystallized carbon) or the growth of crystal grains may be insufficient. Meanwhile, the upper limit of the Sn content relative to the conductive powder does not need to be particularly limited, but may be 4.0 wt% or less.
상기 도전성 분말은 상기 W, Mo, Cr 및 Co 중 1 이상과 상기 Sn을 합금 형태로 포함할 수 있다. The conductive powder may include at least one of W, Mo, Cr, and Co and the Sn in the form of an alloy.
W, Mo, Cr 및 Co 중 1 이상과 Sn이 합금 형태로 포함되는 경우에는, 도전성 분말의 분산성과 무관하게 소결을 지연시킬 수 있다. When at least one of W, Mo, Cr, and Co and Sn are included in the form of an alloy, sintering may be delayed regardless of dispersibility of the conductive powder.
또한, Cu, Ag, Pd, Pt, Rh, Ir 및 Ru 중 1 이상을 합금 형태로 더 포함할 수 있다. In addition, one or more of Cu, Ag, Pd, Pt, Rh, Ir, and Ru may be further included in the form of an alloy.
상기 도전성 분말은 상기 W, Mo, Cr 및 Co 중 1 이상과 상기 Sn을 상기 도전성 분말의 표면에 형성된 코팅층 형태로 포함할 수 있다. The conductive powder may include at least one of W, Mo, Cr, and Co and the Sn in the form of a coating layer formed on the surface of the conductive powder.
W, Mo, Cr 및 Co 중 1 이상과 Sn이 도전성 분말의 표면에 코팅층 형태로 포함되는 경우에는, 도전성 분말의 분산성과 무관하게 도전성 분말 간의 접촉을 막아 소결을 지연시킬 수 있다. When at least one of W, Mo, Cr, and Co and Sn are included in the form of a coating layer on the surface of the conductive powder, sintering may be delayed by preventing contact between the conductive powders regardless of dispersibility of the conductive powder.
또한, 상기 코팅층은 Cu, Ag, Pd, Pt, Rh, Ir 및 Ru 중 1 이상을 더 포함할 수 있다. In addition, the coating layer may further include one or more of Cu, Ag, Pd, Pt, Rh, Ir, and Ru.
또한, 상기 코팅층은 원자층 증착 공법에 의해 형성된 것일 수 있다. In addition, the coating layer may be formed by an atomic layer deposition method.
원자층 증착(Atomic Layer Deposition, ALD) 공법은 반도체공정 중 기판 표면에 박막이나 보호막을 증착시키는 기술로 화학적으로 박막을 입히는 기존 증착 기술과 달리 원자층을 한 층씩 쌓아 박막을 성장시키는 기술이다. 원자층 증착 공법은 단차 피복(Step-coverage)이 우수하며 박막 두께조절이 용이하고, 균일한 박막을 형성할 수 있는 장점이 있다. Atomic Layer Deposition (ALD) is a technology that deposits a thin film or a protective film on the surface of a substrate during semiconductor processing. Unlike the existing deposition technology that chemically coats a thin film, it is a technology that grows thin films by stacking atomic layers one by one. The atomic layer deposition method has advantages of excellent step-coverage, easy thin film thickness control, and uniform thin film formation.
코팅층을 원자층 증착 공법에 의해 형성함으로써 치밀하고 균일한 코팅층을 형성할 수 있다. By forming the coating layer by an atomic layer deposition method, a dense and uniform coating layer can be formed.
또한, 상기 내부 전극용 페이스트는 상기 도전성 분말 함량 대비 300 ppm 이하(0은 제외)의 S를 추가로 포함할 수 있다. In addition, the internal electrode paste may further include 300 ppm or less (excluding 0) S compared to the conductive powder content.
일반적으로 내부 전극을 형성을 위한 도전성 페이스트에는 수축 지연제인 황(S)을 포함할 수 있으나, 그 함량이 300 ppm 초과인 경우에는 소성 후 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층이 불균일하게 형성될 우려가 있다. In general, the conductive paste for forming the internal electrode may contain sulfur (S) as a shrinkage retardant, but if the content is more than 300 ppm, at least one of W, Mo, Cr, and Co and Ni and Sn after firing There is a fear that the composite layer including the non-uniform formation.
상기 내부 전극 패턴의 두께는 0.5 ㎛ 이하일 수 있으며, 이로 인하여 소성 후 내부 전극의 두께는 0.4 ㎛ 이하일 수 있다. 본 발명의 일 실시예에 따르면 유전체층 및 내부 전극이 매우 얇은 경우에도 효과적으로 전극 끊김 및 뭉침의 증가를 억제할 수 있기 때문에 0.4 ㎛ 이하의 두께를 가지는 내부 전극을 형성할 수 있다. The thickness of the internal electrode pattern may be 0.5 μm or less, and thus the thickness of the internal electrode after firing may be 0.4 μm or less. According to an embodiment of the present invention, even when the dielectric layer and the internal electrode are very thin, since the increase in electrode breakage and aggregation can be effectively suppressed, the internal electrode having a thickness of 0.4 μm or less can be formed.
한편, 상기 도전성 분말은 Sn보다 융점이 높은 Ni 분말일 수 있다. Meanwhile, the conductive powder may be a Ni powder having a higher melting point than Sn.
세라믹 적층체를 형성하는 단계forming a ceramic laminate
내부 전극 패턴이 형성된 세라믹 그린시트를 적층하여 세라믹 적층체를 형성한다. A ceramic laminate is formed by stacking ceramic green sheets on which internal electrode patterns are formed.
이때, 세라믹 적층체를 적층 방향으로부터 가압하여, 압착시킬 수 있다.At this time, the ceramic laminate can be pressed from the lamination direction to be crimped.
다음으로, 세라믹 적층체를 1개의 커패시터에 대응하는 영역마다 절단하여 칩화할 수 있다. Next, the ceramic multilayer body may be cut and chipped for each region corresponding to one capacitor.
이때, 내부 전극 패턴의 일단이 측면을 통하여 교대로 노출되도록 절단할 수 있다. 이에 따라, 도 2에 도시된 바와 같이, 세라믹 그린시트(S) 상에 소성 후 제1 내부 전극(121)이 되는 내부 전극 패턴(P1)이 형성된 세라믹 그린시트(a)와 세라믹 그린시트(S) 상에 소성 후 제2 내부 전극(122)이 되는 내부 전극 패턴(P2)이 형성된 세라믹 그린시트(b)가 번갈아 적층된 형태를 가질 수 있다. In this case, one end of the internal electrode pattern may be cut to be alternately exposed through the side surface. Accordingly, as shown in FIG. 2 , the ceramic green sheet (a) and the ceramic green sheet (S) in which the internal electrode pattern P1 which becomes the first
바디를 형성하는 단계Steps to form the body
세라믹 적층체를 소성하여 유전체층 및 내부 전극을 포함하는 바디를 형성한다. The ceramic laminate is fired to form a body including a dielectric layer and an internal electrode.
상기 소성 공정은 환원 분위기에서 수행될 수 있다. 또한, 소성 공정은 승온 속도를 조절하여 수행될 수 있으며, 이에 제한되는 것은 아니나, 상기 승온 속도는 700℃ 이하에서 30℃/60s 내지 50℃/60s일 수 있다.The firing process may be performed in a reducing atmosphere. In addition, the calcination process may be performed by controlling the temperature increase rate, but is not limited thereto, and the temperature increase rate may be 30°C/60s to 50°C/60s at 700°C or less.
다음으로, 바디의 측면을 덮으며, 바디의 측면으로 노출된 내부 전극과 전기적으로 연결되도록 외부전극을 형성할 수 있다. 이후, 외부 전극의 표면에 니켈, 주석 등의 도금층을 형성할 수 있다.Next, an external electrode may be formed to cover the side surface of the body and to be electrically connected to the internal electrode exposed to the side surface of the body. Thereafter, a plating layer such as nickel or tin may be formed on the surface of the external electrode.
바디의 사이즈는 특별히 한정할 필요는 없다. The size of the body does not need to be particularly limited.
다만, 소형화 및 고용량화를 동시에 달성하기 위해서는 유전체층 및 내부 전극의 두께를 얇게 하여 적층수를 증가시켜야 하기 때문에, 0402(0.4mm×0.2mm) 사이즈 이하의 적층 세라믹 전자부품에서 본 발명에 따른 전극 끊김 및 뭉침의 증가를 억제하는 효과가 보다 현저해질 수 있다. 따라서, 바디의 길이는 0.4 mm 이하일 수 있으며, 두께는 0.2 mm 이하일 수 있다. However, in order to achieve miniaturization and high capacity at the same time, since it is necessary to increase the number of stacks by making the thickness of the dielectric layer and the internal electrode thin, the electrode according to the present invention is broken and The effect of inhibiting the increase in agglomeration may be more pronounced. Accordingly, the length of the body may be 0.4 mm or less, and the thickness may be 0.2 mm or less.
적층 세라믹 전자부품Multilayer Ceramic Electronic Components
상술한 본 발명의 일 실시예에 따른 적층 세라믹 전자부품의 제조 방법에 의해 제조된 적층 세라믹 전자부품(100)은 유전체층(111) 및 내부 전극(121, 122)을 포함하는 바디(110); 및 상기 바디(110)에 배치되는 외부 전극(131, 132);을 포함하고, 상기 내부 전극(121, 122)은 금속 결정립(121a)과, 상기 금속 결정립(121a)을 둘러싸고 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)을 포함한다. The multilayer ceramic
바디(110)는 유전체층(111) 및 내부 전극(121, 122)이 교대로 적층되어 있다.In the
바디(110)의 구체적인 형상에 특별히 제한은 없지만, 도시된 바와 같이 바디(110)는 육면체 형상이나 이와 유사한 형상으로 이루어질 수 있다. 소성 과정에서 바디(110)에 포함된 세라믹 분말의 수축으로 인하여, 바디(110)는 완전한 직선을 가진 육면체 형상은 아니지만 실질적으로 육면체 형상을 가질 수 있다.Although the specific shape of the
바디(110)는 두께 방향(Z 방향)으로 서로 대향하는 제1 및 제2 면(1, 2), 상기 제1 및 제2 면(1, 2)과 연결되고 폭 방향(Y 방향)으로 서로 대향하는 제3 및 제4 면(3, 4), 제1 및 제2 면(1, 2)과 연결되고 제3 및 제4 면(3, 4)과 연결되며 길이 방향(X 방향)으로 서로 대향하는 제5 및 제6 면(5, 6)을 가질 수 있다. The
바디(110)를 형성하는 복수의 유전체층(111)은 소성된 상태로서, 인접하는 유전체층(111) 사이의 경계는 주사전자현미경(SEM: Scanning Electron Microscope)를 이용하지 않고 확인하기 곤란할 정도로 일체화될 수 있다. The plurality of
유전체층(111)을 형성하는 원료는 충분한 정전 용량을 얻을 수 있는 한 특별히 제한되지 않으며, 예를 들어, 티탄산바륨(BaTiO3) 분말일 수 있다. 유전체층(111)을 형성하는 재료는 티탄산바륨(BaTiO3) 등의 파우더에 본 발명의 목적에 따라 다양한 세라믹 첨가제, 유기용제, 가소제, 결합제, 분산제 등이 첨가될 수 있다.The raw material for forming the
바디(110)의 상부 및 하부, 즉 두께 방향(Z 방향) 양 단부에는 각각 내부 전극이 형성되지 않은 유전체층을 적층하여 형성되는 커버층(112)을 포함할 수 있다. 커버층(112)은 외부 충격에 대해 커패시터의 신뢰성을 유지하는 역할을 수행할 수 있다. The upper and lower portions of the
커버층(112)의 두께는 특별히 한정할 필요는 없다. 다만, 커패시터 부품의 소형화 및 고용량화를 보다 용이하게 달성하기 위하여 커버층(112)의 두께는 20㎛ 이하일 수 있다. The thickness of the
유전체층(111)의 두께는 특별히 한정할 필요는 없다. The thickness of the
다만, 본 발명에 따르면 유전체층 및 내부 전극이 매우 얇은 경우에도 효과적으로 전극 끊김 및 뭉침의 증가를 억제할 수 있으므로, 커패시터 부품의 소형화 및 고용량화를 보다 용이하게 달성하기 위하여 유전체층(111)의 두께는 0.4㎛ 이하일 수 있다. However, according to the present invention, since the increase in electrode breakage and aggregation can be effectively suppressed even when the dielectric layer and the internal electrode are very thin, the thickness of the
상기 유전체층(111)의 두께는 상기 제1 및 제2 내부 전극(121, 122) 사이에 배치되는 유전체층(111)의 평균 두께를 의미할 수 있다. The thickness of the
상기 유전체층(111)의 평균 두께는 바디(110)의 길이 및 두께 방향(L-T) 단면을 주사전자현미경(SEM, Scanning Eletron Microscope)으로 이미지를 스캔하여 측정할 수 있다. The average thickness of the
예를 들어, 바디(110)의 폭 방향의 중앙부에서 절단한 길이 및 두께 방향(L-T) 단면을 주사전자현미경(SEM, Scanning Eletron Microscope)으로 스캔한 이미지에서 추출된 임의의 유전체층에 대해서, 길이 방향으로 등간격인 30개의 지점에서 그 두께를 측정하여 평균값을 측정할 수 있다. For example, for an arbitrary dielectric layer extracted from an image scanned with a scanning electron microscope (SEM) of a length and thickness direction (L-T) cross section cut at the center of the width direction of the
상기 등간격인 30개의 지점은 제1 및 제2 내부 전극(121, 122)이 서로 중첩되는 영역을 의미하는 용량 형성부에서 측정될 수 있다.The 30 equally spaced points may be measured in the capacitor forming part, which means a region where the first and second
다음으로, 내부 전극(121, 122)은 유전체층과 교대로 적층되며, 제1 및 제2 내부 전극(121, 122)을 포함할 수 있다. 제1 및 제2 내부 전극(121, 122)은 바디(110)를 구성하는 유전체층(111)을 사이에 두고 서로 대향하도록 번갈아 배치되며, 바디(110)의 제3 및 제4면(3, 4)으로 각각 노출될 수 있다. Next, the
이때, 제1 및 제2 내부 전극(121, 122)은 중간에 배치된 유전체층(111)에 의해 서로 전기적으로 분리될 수 있다. In this case, the first and second
상기 도전성 페이스트의 인쇄 방법은 스크린 인쇄법 또는 그라비아 인쇄법 등을 사용할 수 있으며, 본 발명이 이에 한정되는 것은 아니다. The method for printing the conductive paste may use a screen printing method or a gravure printing method, but the present invention is not limited thereto.
이하, 제1 내부 전극(121)에 대한 도면인 도 5를 기준으로 설명하나, 제2 내부 전극(122)에도 동일하게 적용될 수 있다. Hereinafter, although description will be made with reference to FIG. 5 , which is a diagram of the first
내부 전극(121)은 금속 결정립(121a), 상기 금속 결정립(121a)을 둘러싸고 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)을 포함한다. The
금속 결정립(121a)은 금속 원자가 규칙적으로 배열해서 만들어진 다면체이다. W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)은 금속 결정립(121a)을 둘러싸고 있다. 즉, W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)은 금속 결정립계(Grain Boundary)에 존재한다. W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)은 금속 결정립(121a)이 외부로 성장하는 것을 억제함으로써 내부 전극 끊김 현상을 억제하고, 내부 전극 뭉침현상을 억제하는 역할을 한다. The
W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)은 적어도 하나의 금속 결정립(121a)을 거의 완전하게 둘러싸고 있는 형태일 수 있다. The
Sn은 융점이 낮기 때문에 소성 과정에서 내부 전극의 결정립의 표면에 농화되어 복합층(121b) 내 전체에 골고루 퍼져 있는 형태로 존재할 수 있으며, 고융점 메탈인 W, Mo, Cr 및 Co 중 1 이상은 복합층(121b) 내에서 분산되어 있는 형태로 존재할 수 있다. Since Sn has a low melting point, it is concentrated on the surface of the crystal grains of the internal electrode during the firing process and may exist in a form that is evenly spread throughout the
내부 전극(121)의 전체 길이에 대한 실제 내부 전극이 형성된 부분의 길이의 비를 내부 전극의 연결성(C)이라 정의할 때, W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)이 금속 결정립(121a)이 외부로 성장하는 것을 억제함으로써 내부 전극(121)이 85%≤C를 만족할 수 있다. When the ratio of the length of the portion where the internal electrode is actually formed to the total length of the
W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)의 두께는 1~15nm일 수 있다. The thickness of the
W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)의 두께가 1nm 미만인 경우에는 금속 결정립이 외부로 성장하는 것을 충분히 억제할 수 없을 수 있으며, 15nm 초과인 경우에는 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층(121b)의 두께가 균일하지 못하여 금속 결정립이 외부로 성장하는 것을 억제하는 효과가 떨어질 수 있다. When the thickness of the
상기 금속 결정립(121a)은 Ni 결정립일 수 있다. The
한편, 제1 및 제2 내부 전극(121, 122)의 두께는 특별히 한정할 필요는 없다. Meanwhile, the thicknesses of the first and second
다만, 본 발명에 따르면 유전체층 및 내부 전극이 매우 얇은 경우에도 효과적으로 전극 끊김 및 뭉침의 증가를 억제할 수 있으므로, 커패시터 부품의 소형화 및 고용량화를 보다 용이하게 달성하기 위하여 제1 및 제2 내부 전극(121, 122)의 두께는 0.4㎛ 이하일 수 있다. However, according to the present invention, since the increase in electrode breakage and aggregation can be effectively suppressed even when the dielectric layer and the internal electrode are very thin, the first and second
상기 제1 및 제2 내부 전극(121, 122)의 두께는 제1 및 제2 내부 전극(121, 122)의 평균 두께를 의미할 수 있다. The thickness of the first and second
상기 제1 및 제2 내부 전극(121, 122)의 평균 두께는 바디(110)의 길이 및 두께 방향(L-T) 단면을 주사전자현미경(SEM, Scanning Eletron Microscope)으로 이미지를 스캔하여 측정할 수 있다. The average thickness of the first and second
예를 들어, 바디(110)의 폭(W) 방향의 중앙부에서 절단한 길이 및 두께 방향(L-T) 단면을 주사전자현미경(SEM, Scanning Eletron Microscope)으로 스캔한 이미지에서 추출된 임의의 제1 및 제2 내부 전극(121, 122)에 대해서, 길이 방향으로 등간격인 30개의 지점에서 그 두께를 측정하여 평균값을 측정할 수 있다. For example, an arbitrary first and With respect to the second
상기 등간격인 30개의 지점은 제1 및 제2 내부 전극(121, 122)이 서로 중첩되는 영역을 의미하는 용량 형성부에서 측정될 수 있다.The 30 equally spaced points may be measured in the capacitor forming part, which means a region where the first and second
외부 전극(131, 132)은 바디(110)에 배치되고 내부 전극(121, 122)과 연결된다. 도 4에 도시된 형태와 같이 제1 및 제2 내부 전극(121, 122)과 각각 접속된 제1 및 제2 외부 전극(131, 132)을 포함할 수 있다. 본 실시 형태에서는 커패시터 부품(100)이 2개의 외부 전극(131, 132)을 갖는 구조를 설명하고 있지만, 외부 전극(131, 132)의 개수나 형상 등은 내부 전극(121, 122)의 형태나 기타 다른 목적에 따라 바뀔 수 있을 것이다. The
한편, 외부 전극(131, 132)은 금속 등과 같이 전기 전도성을 갖는 것이라면 어떠한 물질을 사용하여 형성될 수 있고, 전기적 특성, 구조적 안정성 등을 고려하여 구체적인 물질이 결정될 수 있으며, 나아가 다층 구조를 가질 수 있다. On the other hand, the
예를 들어, 외부 전극(131, 132)은 바디(110)에 배치되는 전극층(131a, 132a) 및 전극층(131a, 132a) 상에 형성된 도금층(131b, 132b)을 포함할 수 있다. For example, the
전극층(131a, 132a)에 대한 보다 구체적인 예를 들면, 전극층(131a, 132a)은 도전성 금속 및 글라스를 포함한 소성 전극일 수 있으며, 도전성 금속은 Cu일 수 있다. 또한, 전극층(131a, 132a)은 복수의 금속 입자 및 도전성 수지를 포함한 수지계 전극일 수 있다. As a more specific example of the
도금층(131b, 132b)에 대한 보다 구체적인 예를 들면, 도금층(131b, 132b)은 Ni 도금층 또는 Sn 도금층일 수 있으며, 전극층(131a, 132a) 상에 Ni 도금층 및 Sn 도금층이 순차적으로 형성된 형태일 수 있고, 복수의 Ni 도금층 및/또는 복수의 Sn 도금층을 포함할 수도 있다. As a more specific example of the plating layers 131b and 132b, the plating layers 131b and 132b may be a Ni plating layer or a Sn plating layer, and a Ni plating layer and a Sn plating layer may be sequentially formed on the
적층 세라믹 전자부품의 사이즈는 특별히 한정할 필요는 없다. The size of the multilayer ceramic electronic component does not need to be particularly limited.
다만, 소형화 및 고용량화를 동시에 달성하기 위해서는 유전체층 및 내부 전극의 두께를 얇게 하여 적층수를 증가시켜야 하기 때문에, 0402(0.4mm×0.2mm) 사이즈 이하의 적층 세라믹 전자부품에서 본 발명에 따른 전극 끊김 및 뭉침의 증가를 억제하는 효과가 보다 현저해질 수 있다. 따라서, 적층 세라믹 전자부품의 길이는 0.4 mm 이하이고, 두께는 0.2 mm 이하일 수 있다. However, in order to achieve miniaturization and high capacity at the same time, since it is necessary to increase the number of stacks by making the thickness of the dielectric layer and the internal electrode thin, the electrode according to the present invention is broken and The effect of inhibiting the increase in agglomeration may be more pronounced. Accordingly, the multilayer ceramic electronic component may have a length of 0.4 mm or less and a thickness of 0.2 mm or less.
이상에서 본 발명의 실시 형태에 대하여 상세하게 설명하였지만 본 발명은 상술한 실시형태 및 첨부된 도면에 의해 한정되는 것이 아니며, 첨부된 청구범위에 의해 한정하고자 한다. 따라서, 청구범위에 기재된 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 당 기술분야의 통상의 지식을 가진 자에 의해 다양한 형태의 치환, 변형 및 변경이 가능할 것이며, 이 또한 본 발명의 범위에 속한다고 할 것이다.Although the embodiment of the present invention has been described in detail above, the present invention is not limited by the above-described embodiment and the accompanying drawings, but is intended to be limited by the appended claims. Accordingly, various types of substitution, modification and change will be possible by those skilled in the art within the scope not departing from the technical spirit of the present invention described in the claims, and it is also said that it falls within the scope of the present invention. something to do.
100: 적층 세라믹 전자부품
110: 바디
111: 유전체층
112: 커버층
121, 122: 내부 전극
121a: 금속 결정립
121b: 복합층
131, 132: 외부 전극
131a: 전극층
132b: 도금층100: multilayer ceramic electronic component
110: body
111: dielectric layer
112: cover layer
121, 122: internal electrode
121a: metal grains
121b: composite layer
131, 132: external electrode
131a: electrode layer
132b: plating layer
Claims (17)
W, Mo, Cr 및 Co 중 1 이상을 그 합계로 1~20 wt% 포함하며 Sn을 1.5 wt% 이상 포함하는 도전성 분말을 포함하는 내부 전극용 페이스트를 상기 세라믹 그린시트 상에 도포하여 내부 전극 패턴을 형성하는 단계;
상기 내부 전극 패턴이 형성된 세라믹 그린시트를 적층하여 세라믹 적층체를 형성하는 단계; 및
상기 세라믹 적층체를 소성하여 유전체층 및 내부 전극을 포함하는 바디를 형성하는 단계;를 포함하고,
상기 내부 전극은 상기 유전체층과의 계면에 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층을 포함하는
적층 세라믹 전자부품의 제조 방법.
providing a ceramic green sheet;
An internal electrode pattern is formed by coating an internal electrode paste including a conductive powder containing 1 to 20 wt% of W, Mo, Cr, and Co at least 1 to 20 wt% in total and 1.5 wt% or more of Sn on the ceramic green sheet. forming a;
forming a ceramic laminate by laminating the ceramic green sheets on which the internal electrode patterns are formed; and
Firing the ceramic laminate to form a body including a dielectric layer and an internal electrode;
The internal electrode includes a composite layer comprising at least one of W, Mo, Cr, and Co and Ni and Sn at an interface with the dielectric layer
A method for manufacturing a multilayer ceramic electronic component.
상기 내부 전극 패턴의 두께는 0.5㎛ 이하인
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The thickness of the inner electrode pattern is 0.5㎛ or less
A method for manufacturing a multilayer ceramic electronic component.
상기 세라믹 그린시트의 두께는 0.6㎛ 이하인
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The thickness of the ceramic green sheet is 0.6㎛ or less.
A method for manufacturing a multilayer ceramic electronic component.
상기 도전성 분말은 상기 W, Mo, Cr 및 Co 중 1 이상과 상기 Sn을 합금 형태로 포함하는
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The conductive powder comprises at least one of W, Mo, Cr, and Co and the Sn in an alloy form.
A method for manufacturing a multilayer ceramic electronic component.
상기 도전성 분말은 Cu, Ag, Pd, Pt, Rh, Ir 및 Ru 중 1 이상을 합금 형태로 더 포함하는
적층 세라믹 전자부품의 제조 방법.
5. The method of claim 4,
The conductive powder further comprises at least one of Cu, Ag, Pd, Pt, Rh, Ir and Ru in the form of an alloy.
A method for manufacturing a multilayer ceramic electronic component.
상기 도전성 분말은 상기 W, Mo, Cr 및 Co 중 1 이상과 상기 Sn을 상기 도전성 분말의 표면에 형성된 코팅층 형태로 포함하는
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The conductive powder comprises at least one of W, Mo, Cr, and Co and the Sn in the form of a coating layer formed on the surface of the conductive powder
A method for manufacturing a multilayer ceramic electronic component.
상기 코팅층은 Cu, Ag, Pd, Pt, Rh, Ir 및 Ru 중 1 이상을 더 포함하는
적층 세라믹 전자부품의 제조 방법.
7. The method of claim 6,
The coating layer further comprises at least one of Cu, Ag, Pd, Pt, Rh, Ir and Ru
A method for manufacturing a multilayer ceramic electronic component.
상기 코팅층은 원자층 증착 공법에 의해 형성된 것인
적층 세라믹 전자부품의 제조 방법.
7. The method of claim 6,
The coating layer is formed by an atomic layer deposition method
A method for manufacturing a multilayer ceramic electronic component.
상기 도전성 분말은 상기 도전성 분말 함량 대비 300 ppm 이하(0은 제외)의 S를 추가로 포함하는
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The conductive powder further comprises S of 300 ppm or less (excluding 0) compared to the content of the conductive powder
A method for manufacturing a multilayer ceramic electronic component.
상기 도전성 분말은 Ni 분말인
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The conductive powder is Ni powder
A method for manufacturing a multilayer ceramic electronic component.
상기 바디는 길이가 0.4mm 이하이고, 두께가 0.2 mm 이하인
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The body has a length of 0.4 mm or less and a thickness of 0.2 mm or less
A method for manufacturing a multilayer ceramic electronic component.
상기 내부 전극은 복수의 금속 결정립을 포함하고,
상기 복수의 급속 결정립 간의 계면에도 상기 복합층이 추가로 배치되는
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The internal electrode includes a plurality of metal grains,
The composite layer is additionally disposed at the interface between the plurality of rapid crystal grains.
A method for manufacturing a multilayer ceramic electronic component.
상기 내부전극의 두께는 0.4㎛ 이하인
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The thickness of the inner electrode is 0.4 μm or less.
A method for manufacturing a multilayer ceramic electronic component.
상기 W, Mo, Cr 및 Co 중 1 이상과 Ni 및 Sn을 포함하는 복합층의 두께는 1~15nm인
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The thickness of the composite layer comprising at least one of W, Mo, Cr and Co and Ni and Sn is 1 to 15 nm.
A method for manufacturing a multilayer ceramic electronic component.
상기 금속 결정립은 Ni 결정립인
적층 세라믹 전자부품의 제조 방법.
13. The method of claim 12,
The metal grains are Ni grains
A method for manufacturing a multilayer ceramic electronic component.
상기 내부 전극은,
내부 전극의 전체 길이에 대한 실제 내부 전극이 형성된 부분의 길이의 비를 내부 전극의 연결성(C)이라 정의하면, 85%≤C를 만족하는
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The inner electrode is
If the ratio of the length of the portion where the internal electrode is actually formed to the total length of the internal electrode is defined as the interconnectivity (C) of the internal electrode, 85%≤C is satisfied.
A method for manufacturing a multilayer ceramic electronic component.
상기 유전체층의 두께는 0.4㎛ 이하인
적층 세라믹 전자부품의 제조 방법.
According to claim 1,
The thickness of the dielectric layer is 0.4 μm or less.
A method for manufacturing a multilayer ceramic electronic component.