KR102381676B1 - 접착력 가변 폴더블 디스플레이용 보호 필름 및 이를 포함하는 폴더블 디스플레이 장치 - Google Patents

접착력 가변 폴더블 디스플레이용 보호 필름 및 이를 포함하는 폴더블 디스플레이 장치 Download PDF

Info

Publication number
KR102381676B1
KR102381676B1 KR1020200149871A KR20200149871A KR102381676B1 KR 102381676 B1 KR102381676 B1 KR 102381676B1 KR 1020200149871 A KR1020200149871 A KR 1020200149871A KR 20200149871 A KR20200149871 A KR 20200149871A KR 102381676 B1 KR102381676 B1 KR 102381676B1
Authority
KR
South Korea
Prior art keywords
foldable display
meth
acrylate
protective film
sensitive adhesive
Prior art date
Application number
KR1020200149871A
Other languages
English (en)
Other versions
KR20210059629A (ko
Inventor
유한솔
김현철
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Publication of KR20210059629A publication Critical patent/KR20210059629A/ko
Application granted granted Critical
Publication of KR102381676B1 publication Critical patent/KR102381676B1/ko

Abstract

본 발명은 가변적인 접착력을 가지는 폴더블 디스플레이용 보호 필름 및 이를 포함하는 폴더블 디스플레이 장치를 제공한다.

Description

접착력 가변 폴더블 디스플레이용 보호 필름 및 이를 포함하는 폴더블 디스플레이 장치 {PROTECTION FILM FOR FOLDABLE DISPLAY HAVING VARIABLE ADHESIVENESS AND FOLDABLE DISPLAY DEVICE COMPRISING THE SAME}
본 명세서는 2019년 11월 15일에 한국특허청에 제출된 한국 특허 출원 제10-2019-0146812호의 출원일의 이익을 주장하며, 그 내용 전부는 본 발명에 포함된다.
본 발명은 접착력 가변 폴더블 디스플레이용 보호 필름 및 이를 포함하는 폴더블 디스플레이 장치에 관한 것이다.
최근 디스플레이 관련 기술의 발달과 함께, 접거나, 롤(Roll) 형상으로 말거나, 고무줄처럼 늘리는 등, 사용 단계에서 변형 가능한 디스플레이 장치들이 연구 및 개발되고 있다. 이들 디스플레이는 다양한 형태로 변형 가능하기 때문에, 사용 단계에서의 디스플레이의 대형화 요구와 휴대를 위한 디스플레이의 소형화의 요구를 모두 만족시킬 수 있다.
또한 최근 이동통신 단말기(wireless terminal), PDA(Personal Digital Assistant), PMP(Portable Multimedia Player), 전자수첩 등과 같은 휴대 단말기는 휴대성을 위하여 크기가 소형화되는 추세이다.
하지만, 사용자는 휴대 단말기의 화면을 통하여 문자 정보, 동영상, 게임 등 과 같은 각종 컨텐츠로부터 정보를 제공 받기를 원하기 때문에, 디스플레이 화면의 크기에 대해서는 대형화 또는 와이드(Wide) 화를 요구하고 있다. 그러나 휴대 단말기의 소형화는 디스플레이 화면의 크기 축소를 불러오기 때문에, 두 가지 요구사항을 모두 충족시키는데 한계가 있다.
종래 디스플레이 장치는 변형이 되지 않는 디스플레이(unbreakable display)를 사용하였으나, 상기와 같은 한계점을 극복하기 위하여, 변형 가능한 디스플레이 즉, 곡면을 가지는 디스플레이(Curved display), 구부러진 디스플레이(bended display), 접을 수 있는 디스플레이(foldable display) 및 감을 수 있는 디스플레이(rollable display) 등이 개발되어 왔다.
변형 가능한 디스플레이 장치는 미리 설정된 형태로 변형될 수 있을 뿐 아니라, 사용자의 요구에 상응하여 또는 디스플레이 장치가 사용되는 상황의 필요에 맞추어 다양한 형태로 변형될 수 있다. 따라서, 디스플레이의 변형된 형태를 인식하고, 인식한 형태에 대응하여 디스플레이 장치를 제어할 필요가 있다.
한편, 변형 가능한 디스플레이가 적용되는 태블릿 PC 또는 스마트폰 사용시 패널의 손상을 막고자 커버윈도우를 적용하게 되며 커버윈도우 표면의 스크래치 및 오염을 방지하기 위하여 보호 필름을 커버 윈도우에 부착하여 사용하고 있다.
이러한 보호필름은 폴더블 디스플레이를 접었다 폈다 하는 사용 도중 이탈을 방지해야 하므로 커버윈도우와의 접착력이 충분히 높게 설계될 필요가 있다. 하지만 접착력이 적당한 수준일 경우 사용자가 임의로 보호필름의 박리를 시도하다가 커버윈도우의 손상 내지는 내부 패널의 파손 등의 문제가 발생할 여지가 있다.
따라서 이와 같은 문제를 해결하기 위해서 사용중에는 디스플레이 장치와 충분히 강하게 붙어있다가 교체를 원할 때 광조사를 통하여 접착력을 낮추어 보호필름을 제거할 때의 디스플레이 장치의 손상을 방지하고자 한다. 하지만 접착력이 과하게 낮아질 경우 디스플레이를 접었다 펴는 과정에서 보호필름이 이탈하는 문제가 발생할 수 있다. 따라서 광조사 후 일정 수준의 접착력이 유지하여야 할 필요가 있다.
본 발명이 이루고자 하는 기술적 과제는 가변적인 접착력을 가지는 점착제층을 포함하는 폴더블 디스플레이용 보호 필름 및 이를 포함하는 폴더블 디스플레이 장치를 제공하는 것이다.
본 발명의 일 측면에 따르면, 알킬(메트)아크릴레이트 모노머; 가교성 관능기 함유 모노머; 및 광개시형 모노머;를 포함하는 혼합물이 공중합되어 제조된 (메트)아크릴레이트 수지를 포함하는 점착제 조성물을 포함하는 점착제층; 및 상기 점착제층의 일면에 구비된 보호기재;를 포함하는 폴더블 디스플레이용 보호 필름으로서, 상기 광개시형 모노머는 상기 혼합물의 0.2 내지 4.5 중량% 로 포함되고, 반경 4mm 폴딩 테스트 결과, 상기 보호 기재가 손상 또는 탈리되지 않고 유지되고,
하기 식 1을 만족하는 것인 폴더블 디스플레이용 보호 필름:
[식 1]
1 ≤ 100 * B / A ≤ 30
상기 식 1에서, A는 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 광 조사 전 23℃, 50 RH%에서 측정한 접착력이고, B는 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 380nm 이하의 파장을 갖는 광 조사 후 23℃, 50 RH%에서 측정한 접착력이다.
본 발명의 다른 측면에 따르면, 폴더블 디스플레이; 및 상기 폴더블 디스플레이의 일면에 구비된 상기 폴더블 디스플레이용 보호 필름;을 포함하고, 상기 폴더블 디스플레이용 보호 필름의 상기 점착제층과 상기 폴더블 디스플레이의 일면이 접하는 것인 폴더블 디스플레이 장치가 제공된다.
본 발명의 일 구현예에 따른 폴더블 디스플레이용 보호 필름은 자외선에 노출되는 경우 점착제층이 천천히 경화됨으로써 서서히 접착력이 감소하여 추후 박리시 커버 윈도우의 손상 없이 제거할 수 있는 효과가 있다.
도 1은 자외선 광량에 따른 실시예 1에서 제조한 폴더블 디스플레이용 보호 필름의 접착력 변화 그래프이다.
본 명세서에서 어떤 부분이 어떤 구성요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다.
이하, 본 발명에 대하여 더욱 상세하게 설명한다.
본 발명의 일 구현예에 따르면, 알킬(메트)아크릴레이트 모노머; 가교성 관능기 함유 모노머; 및 광개시형 모노머;를 포함하는 혼합물이 공중합되어 제조된 (메트)아크릴레이트 수지를 포함하는 점착제 조성물을 포함하는 점착제층; 및 상기 점착제층의 일면에 구비된 보호기재;를 포함하는 폴더블 디스플레이용 보호 필름으로서, 상기 광개시형 모노머는 상기 혼합물의 0.2 내지 4.5 중량% 로 포함되고, 반경 4mm 폴딩 테스트 결과, 상기 보호 기재가 손상 또는 탈리되지 않고 유지되고, 하기 식 1을 만족하는 것인 폴더블 디스플레이용 보호 필름이 제공된다:
[식 1]
1 ≤ 100 * B / A ≤ 30
상기 식 1에서, A는 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 광 조사 전 23℃, 50 RH%에서 측정한 접착력이고, B는 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 380nm 이하의 파장을 갖는 광 조사 후 23℃, 50 RH%에서 측정한 접착력이다.
본 발명의 일 구현예에 따르면, 상기 혼합물은 알킬(메트)아크릴레이트 모노머; 가교성 관능기 함유 모노머; 및 광개시형 모노머;를 포함한다. 상기 혼합물은 공중합되어 (메트)아크릴레이트 수지를 제조할 수 있다. 구체적으로, 상기 혼합물은 벌크중합 또는 용액중합의 방법으로 공중합되어 (메트)아크릴레이트 수지를 제조할 수 있다.
본 발명의 일 구현예에 따르면, 상기 광개시형 모노머는 (메트)아크릴레이트기를 갖는 벤조페논(Benzophenone)계 화합물일 수 있다. 구체적으로, 상기 광개시형 모노머는 4-벤조일페닐 (메트)아크릴레이트 또는 N-(2-벤조일페닐) 아크릴아미드일 수 있다.
상기 광개시형 모노머가 (메트)아크릴레이트기를 갖는 벤조페논(Benzophenone)계 화합물인 경우, (메트)아크릴레이트 관능기를 포함함으로써 광 조사시 가교 반응이 원활하게 일어날 수 있으며, 모노머 및 경화제로서의 역할도 수행할 수 있다.
본 발명의 일 구현예에 따르면, 상기 광개시형 모노머는 상기 혼합물의 0.2 내지 4.5 중량%, 0.5 내지 4.5 중량% 또는 0.5 내지 2.9 중량%로 포함되는 것일 수 있다. 본 발명의 일 구현예에 따른 점착제 조성물이 상기 수치 범위 내의 함량으로 광개시형 모노머를 포함하는 경우, 자외선을 조사하였을 때 상기 점착제 조성물은 서서히 경화되어 접착력이 낮아지게 되고, 폴더블 디스플레이로부터 박리하더라도 커버 윈도우의 손상을 방지할 수 있다.
본 발명의 일 구현예에 따르면, 상기 알킬 (메트)아크릴레이트 모노머는 특별히 한정되지 않으나, 예를 들면 상기 알킬 (메트)아크릴레이트는 탄소수 1 내지 12의 알킬기를 가지는 단량체로서, 펜틸 (메트)아크릴레이트, n-부틸 (메트)아크릴레이트, 에틸 (메트)아크릴레이트, 메틸 (메트)아크릴레이트, 헥실 (메트)아크릴레이트, n-옥틸 (메트)아크릴레이트, 이소옥틸 (메트)아크릴레이트, 2-에틸헥실 (메트)아크릴레이트, 도데실 (메트)아크릴레이트 및 데실 (메트)아크릴레이트 중 1종 이상을 포함하는 것일 수 있다. 바람직하게는 상기 알킬 (메트)아크릴레이트 모노머는 2-에틸헥실아크릴레이트일 수 있다.
본 명세서에서, (메트)아크릴레이트는 아크릴레이트 및 메타크릴레이트를 모두 포함하는 의미이다.
본 발명의 일 구현예에 따르면, 상기 가교성 관능기 함유 모노머는 카르복시기 함유 모노머 및 히드록시기 함유 모노머 중 1종 이상을 포함할 수 있다. 카르복시기 및 히드록시기의 경우 가교성 관능기로서, 카르복시기 함유 모노머 및 히드록시기 함유 모노머는 (메트)아크릴레이트 수지 제조시에 공중합 성분으로 사용될 수 있다.
상기 가교성 관능기 함유 모노머는 상기 혼합물의 0 초과 20 중량% 이하로 포함될 수 있고, 상기 카르복시기 함유 모노머는 상기 혼합물의 0 초과 10 중량% 이하로 포함될 수 있고, 상기 히드록시기 함유 모노머는 상기 혼합물의 0 초과 20 중량% 이하로 포함될 수 있다. 상기 혼합물이 상기 수치 범위 내로 가교성 관능기 함유 모노머를 포함하는 경우, 우수한 접착력을 발현하며 폴딩 성능도 우수한 효과가 있을 수 있다.
본 발명의 일 구현예에 따르면, 상기 카르복시기를 포함하는 모노머는 (메트)아크릴산, 2-(메트)아크릴로일옥시아세트산, 3-(메트)아크릴로일옥시프로필산, 4-(메트)아크릴로일옥시부틸산, 아크릴산 이량체, 이타콘산, 말레산 및 말레산 무수물 중 1종 이상을 포함하는 것일 수 있고, 바람직하게는 상기 카르복시기를 포함하는 모노머가 아크릴산일 수 있다.
상기 히드록시기 함유 모노머는 2-히드록시에틸 (메트)아크릴레이트, 2-히드록시프로필 (메트)아크릴레이트 및 4-히드록시부틸 (메트)아크릴레이트 중 1종 이상을 포함할 수 있다.
본 발명의 일 구현예에 따르면, 상기 혼합물은 공중합되어 (메트)아크릴레이트 수지를 제조할 수 있다. 구체적으로, 상기 혼합물은 벌크중합 또는 용액중합되어 (메트)아크릴레이트 수지를 제조할 수 있다.
본 발명의 일 구현예에 따르면, 상기 (메트)아크릴레이트 수지는 중량 평균 분자량이 10만g/mol 내지 300만g/mol일 수 있다. 상기 중량 평균 분자량이란 분자량이 균일하지 않고 어떤 고분자 물질의 분자량이 기준으로 사용되는 평균 분자량 중의 하나로, 분자량 분포가 있는 고분자 화합물의 성분 분자종의 분자량을 중량 분율로 평균하여 얻어지는 값이다. 상기 중량 평균 분자량은 겔 투과 크로마토그래피(GPC) 분석을 통하여 측정될 수 있다.
본 발명의 일 구현예에 따르면, 상기 점착제 조성물의 유리 전이 온도(Tg, Glass Transition Temperature) 값이 -30℃ 이하, -120℃ 이상 -30℃ 이하 또는 -110 ℃ 이상 -30℃ 이하일 수 있다. 상기 점착제 조성물의 유리전이온도가 상기 수치 범위를 만족하는 경우, 저온에서 폴딩시 내구성이 우수한 효과가 있을 수 있다.
본 발명의 일 구현예에 따른 점착제 조성물의 유리 전이 온도 값이 상기 범위를 만족함에 따라, 폴딩 특성이 특히 우수한 특징을 갖게 된다. 즉, 본 출원에 따른 점착제 조성물의 경우 점착제 조성물에 포함되는 (메트)아크릴레이트 수지의 원료인 혼합물에 포함되는 (메트)아크릴레이트 모노머, 카르복시기를 포함하는 모노머 및 광개시제의 함량을 특정 범위로 조절하여, 전체 점착제 조성물의 유리 전이 온도를 -30℃ 이하의 범위로 조절할 수 있으며, 이에 따라 폴딩 특성이 특히 우수한 점착시트를 형성할 수 있다.
본 명세서에서 유리 전이 온도는 시차주사형 열량계(DSC, Mettler 社)를 이용하여, 약 10mg의 시료를 전용 펜(pan)에 필봉하고 일정 승온 환경으로 가열 할 때 상 변이가 일어남에 따른 물질의 흡열 및 발열량을 온도에 따라 그려 측정한 값이다.
구체적으로, 유리 전이 온도는 문헌, 카탈로그 등에 기재된 공칭값이거나 또는 하기 일반식 (1)(Fox식)에 기초하여 계산된 값이다.
[일반식 (1)]
1/Tg=W1/Tg1+W2/Tg2+ … +Wn/Tgn
상기 일반식 (1)에 있어서, Tg는 중합체 A의 유리 전이 온도(단위: K), Tgi(i=1, 2, … n)는 단량체 i가 단독 중합체를 형성하였을 때의 유리 전이 온도(단위: K), Wi(i=1, 2, … n)는 단량체 i의 전체 단량체 성분 중의 질량 분율을 나타낸다.
상기 일반식 (1)은 중합체 A가 단량체 1, 단량체 2, …, 단량체 n의 n종류의 단량체 성분을 포함하는 경우의 계산식을 의미한다. 본 출원의 일 실시상태에 있어서, 상기 점착제 조성물의 유리 전이 온도는 성분 분석을 통해 각각의 모노머의 함량을 추정할 수 있으며, 이에 따라 상기 fox 식에 기초하여 유리 전이 온도를 계산할 수 있다.
본 발명의 일 구현예에 따르면, 상기 점착제 조성물은 용매, 경화제, 분산제, 열개시제, 실란커플링제, 가소제, 점착 부여제, 광개시제, 산화방지제 및 자외선 안정제 중 1종 이상을 더 포함할 수 있다.
상기 점착제 조성물이 경화제를 포함하는 경우, 경화제의 함량이 과다하면 초기 접착력이 작아 폴더블 디스플레이에 폴더블 디스플레이용 보호 필름의 부착 자체가 불가능할 수 있으므로, 경화제는 1 중량% 이하의 함량으로 포함되는 것이 바람직하다.
상기 점착제 조성물이 산화방지제 또는 자외선 안정제를 포함할 경우, 폴더블 디스플레이용 보호 필름의 접착력의 약화 속도가 작을 수 있다. 즉, 보다 천천히 접착력이 하락하게 되어, 사용자가 폴더블 디스플레이용 보호 필름을 사용하는 도중에 떨어져버리는 문제점이 발생하지 않을 수 있다.
상기 점착제 조성물이 광개시제를 포함하고, 상기 (메트)아크릴레이트 수지가 탄소 이중 결합을 포함하는 경우, 추가적인 가교를 유도할 수 있어 자외선 조사시 점착제층의 가교가 더 진행되어 접착력을 감소시킬 수 있다.
본 출원의 일 실시상태에 있어서, 상기 가교제는 가교성 화합물을 포함할 수 있으며, 상기 가교제는 이소시아네이트계 가교제를 사용할 수 있으며, 당업계에 알려진 것을 이용할 수 있다.
본 명세서의 일 실시상태에 따르면, 상기 가교성 화합물은 헥산디올디(메타)아크릴레이트, 에틸렌글리콜 디(메타)아크릴레이트, 에틸렌 기의 수가 2 내지 14인 폴리에틸렌 글리콜 디(메타)아크릴레이트, 트리메틸올프로판 디(메타)아크릴레이트, 트리메틸올프로판 트리(메타)아크릴레이트, 펜타에리스리톨 트리(메타)아크릴레이트, 펜타에리스리톨 테트라(메타)아크릴레이트, 2-트리스아크릴로일옥시메틸에틸프탈산, 프로필렌기의 수가 2 내지 14인 프로필렌 글리콜 디(메타)아크릴레이트, 디펜타에리스리톨 펜타(메타)아크릴레이트, 디펜타에리스리톨 헥사(메타)아크릴레이트, 디펜타에리스리톨 펜타(메타)아크릴레이트의 산성 변형물과 디펜타에리스리톨 헥사(메타)아크릴레이트의 혼합물(상품명으로 일본 동아합성사의 TO-2348, TO-2349) 등의 다가 알코올을 α,β-불포화 카르복실산으로 에스테르화하여 얻어지는 화합물; 트리메틸올프로판 트리글리시딜에테르아크릴산 부가물, 비스페놀 A 디글리시딜에테르아크릴산 부가물 등의 글리시딜기를 함유하는 화합물에 (메타)아크릴산을 부가하여 얻어지는 화합물; β-히드록시에틸(메타)아크릴레이트의 프탈산디에스테르, β-히드록시에틸 (메타)아크릴레이트의 톨루엔 디이소시아네이트 부가물 등의 수산기 또는 에틸렌성 불포화 결합을 갖는 화합물과 다가 카르복실산과의 에스테르 화합물, 또는 폴리이소시아네이트와의 부가물; 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 부틸(메타)아크릴레이트, 2-에틸헥실(메타)아크릴레이트 등의 (메타)아크릴산 알킬에스테르; 및 9,9'-비스[4-(2-아크릴로일옥시에톡시)페닐]플루오렌으로 이루어지는 군으로부터 선택되는 1종 이상을 포함할 수 있으며, 이들로만 한정되지 않고 당 기술분야에 알려져 있는 일반적인 것들을 사용할 수 있다.
상기 열개시제는 당업계에 알려진 것을 이용할 수 있다.
상기 용매로는 톨루엔(Toluene), 메틸에틸케톤(MEK, Methyl Ethyl Ketone), 메틸이소뷰틸케톤(MIBK, Methyl isobutyl ketone), 에틸아세테이트(EAc, Ethyl Acetate)가 사용될 수 있으나, 특정 물질을 용해시킬 수 있으면 이에 제한되지 않으며, 이에 따른 일반적 유기 용매가 사용될 수 있다.
본 발명의 일 구현예에 따르면, 상기 점착제층은 점착제 조성물을 그대로 포함할 수도 있고, 상기 점착제 조성물을 건조 또는 경화하여 포함하는 것일 수 있다. 구체적으로, 상기 점착제층은 점착제 조성물에 포함된 (메트)아크릴레이트 수지의 열경화 또는 광경화로 가교되어 우수한 초기 접착력을 구현할 수 있다.
본 발명의 일 구현예에 따르면, 상기 점착제층의 두께는 10 ㎛ 내지 100 ㎛, 12 ㎛ 내지 75 ㎛ 또는 15 ㎛ 내지 50 ㎛ 일 수 있다. 상기 점착제층이 상기 수치 범위의 두께를 갖는 경우, 점착 시트 내부에 기포의 발생 비율이 낮아질 수 있으며, 이에 따라 추후 커버 윈도우와의 접착시 접착력이 우수하며 들뜸 현상이 발생하지 않는 특징을 갖게 되고, 덴트(dent)의 문제가 발생하지 않는 특징을 갖게 된다.
본 발명의 일 구현예에 따르면, 상기 보호기재의 두께는 25 ㎛ 내지 150 ㎛, 38 ㎛ 내지 130 ㎛ 또는 50 ㎛ 내지 125 ㎛일 수 있다. 상기 보호기재가 상기 수치 범위의 두께를 갖는 경우, 적층된 보호 필름이 박막화가 가능한 특성을 갖게 되며, 폴더블 디스플레이에 적용시 폴딩 자국이 발생하지 않으며, 외부의 충격으로부터 충분히 폴더블 디스플레이의 커버 윈도우를 보호할 수 있는 특징을 갖게 된다.
상기 보호기재는 투명할 수 있으며, 여기서 투명하다는 것은 가시광(400~700nm)의 광투과율이 80% 이상인 것을 의미할 수 있다.
본 발명의 일 구현예에 따르면, 상기 보호기재는 PET(polyethylene terephthalate), 폴리에스테르(polyester), PC(polycarbonate), PI(polyimide), PEN(polyethylene naphthalate), PEEK(polyether ether ketone), PAR(polyarylate), PCO(polycylicolefin), 폴리노보넨(polynorbornene), PES(polyethersulphone), 유리(glass) 및 COP(cycloolefin polymer)로 이루어진 군으로부터 선택되는 것일 수 있다.
본 발명의 일 구현예에 따른 폴더블 디스플레이용 보호 필름의 두께는 35 ㎛ 내지 250 ㎛, 50 ㎛ 내지 200 ㎛ 또는 60 ㎛ 이상 150㎛ 일 수 있다. 상기 폴더블 디스플레이용 보호 필름이 상기 수치 범위의 두께를 가짐으로써, 추후 폴더블 디스플레이에 적용시 두께가 적합하며, 또한 디스플레이에 적용시 접착력 저하가 발생하지 않으며, 수회 폴딩/언폴딩을 반복하여도 신뢰성이 우수한 보호 필름을 제공할 수 있는 특징을 갖게 된다.
본 발명의 일 구현예에 따르면, 상기 점착제층의 상기 보호기재와 접하는 면의 반대 면에 이형 필름을 더 포함하는 것일 수 있다.
상기 이형 필름은 소수성 필름이 사용될 수 있으며, 두께가 매우 얇은 점착 시트를 보호하기 위한 층으로서, 점착 시트의 일면에 부착하는 투명층을 말하는 것이며, 기계적 강도, 열안정성, 수분차폐성, 등방성 등이 우수한 필름을 사용할 수 있다. 예를들면, 트리아세틸셀룰로오즈(TAC)와 같은 아세테이트계, 폴리에스테르계, 폴리에테르술폰계, 폴리카보네이트계, 폴리아미드계, 폴리이미드계, 폴리올레핀계, 시클로 올레핀계, 폴리우레탄계 및 아크릴계 수지 필름 등을 사용 할 수 있으나, 시판되는 실리콘 처리 이형 필름이라면 이에 한정되지 않는다.
상기 이형 필름은 디스플레이에 적용시 모두 제거될 수 있다.
본 발명의 일 구현예에 따른 폴더블 디스플레이용 보호 필름은, 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 광 조사 전 23℃, 50 RH%에서 측정한 접착력이 800gf/in 이상, 842gf/in 이상, 900 gf/in 이상, 930gf/in 이상, 1000gf/in 이상, 1021gf/in 이상, 1351gf/in 이상 또는 1585gf/in 이상일 수 있고, 380nm 이하의 파장을 갖는 광 조사 후 23℃, 50 RH%에서 측정한 접착력이 10gf/in 내지 300gf/in, 60gf/in 내지 300 gf/in, 60gf/in 내지 258gf/in, 75 gf/in 내지 258 gf/in, 75gf/in 내지 163gf/in, 157gf/in 내지 163 gf/in, 163 gf/in 내지 258gf/in 또는 258gf/in 내지 300gf/in 일 수 있다.
본 발명의 일 구현예에 따른 폴더블 디스플레이용 보호 필름은, 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 광 조사 전 23℃, 50 RH%에서 측정한 접착력과, 380nm 이하의 파장을 갖는 광 조사 후 23℃, 50 RH%에서 측정한 접착력의 차이가 500 gf/in 이상 또는 600 gf/in 이상일 수 있다.
상기 점착제층은 폴더블 디스플레이용 보호 필름이 폴더블 디스플레이에 적용되는 경우, 사용자의 사용 과정에서 자외선에 노출될 수 있고, 점착제층에 포함된 광개시형 모노머 또는 광개시제에 의해 광 가교 반응이 더 진행될 수 있고, 경화도가 상승함에 따라 상기와 같이 접착력이 감소할 수 있다.
상기와 같이 광 조사 전 및 후의 접착력 차이가 클 경우, 초기 접착력은 우수하여 사용자가 폴더블 디스플레이에 폴더블 디스플레이용 보호 필름을 부착하여 사용하는 동안에는 안정적으로 부착되어 있고, 사용 과정에서 자외선 등에 노출되어 점차 접착력이 감소하게 되며, 교체 등이 필요하여 상기 폴더블 디스플레이용 보호 필름을 박리해야 하는 경우 원활하게 제거될 수 있다.
본 발명의 일 구현예에 따르면, 반경 4mm 폴딩 테스트 결과 보호 기재가 손상 또는 탈리되지 않고 유지될 수 있고, 이에 따라 박형 폴더블 디스플레이에도 본 발명에 따른 폴더블 디스플레이용 보호 필름이 적용될 수 있다.
“반경 4mm 폴딩 테스트”란, 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI 기재와 접합한 다음, 외면이 보호 기재가 되고, 곡률이 4R(보호 필름간 간격이 8mm)이 되도록 접은 후, 1 일간 방치하고 다시 펼쳐 외관을 확인하는 시험을 의미할 수 있다. 반경 4mm 폴딩 테스트 결과, 상기 PI 기재 및 점착제층 간의 밀착성이 유지되고 외관 변화가 없는 경우, 즉 보호 기재가 손상되거나 탈리되지 않는 경우 폴더블 디스플레이용 보호 필름의 폴딩성이 우수한 것일 수 있다.
본 발명의 일 구현예에 따른 폴더블 디스플레이용 보호 필름은, 헤이즈(haze)가 0% 초과 2% 이하, 0% 초과 1.5% 이하 또는 0% 초과 1.35% 이하이고, 황색도(Yellow index)가 0 초과 3 이하, 0 초과 2 이하, 0 초과 1 이하 또는 0 초과 0.95 이하이며, 파장 550nm의 광 투과율이 85% 이상, 90% 이상 또는 92% 이상일 수 있다. 헤이즈, 황색도 및 광 투과율이 상기 수치 범위를 만족하는 경우, 투명성이 우수하고 광학 특성이 우수하여 폴더블 디스플레이용 보호 필름은 폴더블 디스플레이에 부착되더라도 사용자가 디스플레이에 표시되는 내용을 시각적 왜곡 없이 볼 수 있다.
본 발명의 다른 구현예에 따르면, 폴더블 디스플레이; 및 상기 폴더블 디스플레이의 일면에 구비된 본 발명에 따른 폴더블 디스플레이용 보호 필름;을 포함하고, 상기 폴더블 디스플레이용 보호 필름의 상기 점착제층과 상기 폴더블 디스플레이의 일면이 접하는 것인 폴더블 디스플레이 장치가 제공된다.
본 발명의 일 실시상태에 있어서, 상기 폴더블 디스플레이는 플렉서블 기재; 유기 발광층; 편광판; 및 커버 윈도우가 순차적으로 적층된 구조일 수 있고, 상기 커버 윈도우의 상기 편광판과 접하는 면의 반대면에 상기 폴더블 디스플레이용 보호 필름의 상기 점착제층이 구비될 수 있다.
본 발명에 따른 폴더블 디스플레이용 보호 필름의 경우, 폴더블 디스플레이의 상기 커버 윈도우의 스크래치 및 보호를 위한 것으로, 상기 커버 윈도우의 일면에 점착제층을 통하여 상기 보호 기재가 부착될 수 있다.
즉, 본 발명의 일 실시상태에 따른 폴더블 디스플레이용 보호 필름은 폴더블 디스플레이 장치의 커버 윈도우를 보호하기 위한 용도로 사용될 수 있다.
본 발명의 일 실시상태에 있어서, 상기 플렉서블 기재는 TPU(thermoplastic polyurethane), PDMS(polydimethylsiloxane), GLASS, PET(polyethylene terephthalate), 폴리에스테르(polyester), PC(Polycarbonate), PI(polyimide), PEN(polyethylene naphthalate), PEEK(polyether ether ketone), PAR(polyarylate), PCO(polycylicolefin), 폴리노보넨(polynorbornene), PES(polyethersulphone) 및 COP(cycloolefin polymer)로 이루어진 군으로부터 선택될 수 있고, 상기 플렉서블 기재는 PI(polyimide)일 수 있으며, 상기 PI(Polyimide)는 투명 PI(Polyimide)일 수 있다.
이하, 본 발명을 구체적으로 설명하기 위해 구현예를 들어 상세하게 설명하기로 한다. 그러나, 본 발명에 따른 구현예들은 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 기술하는 구현예들에 한정되는 것으로 해석되지 않는다. 본 명세서의 구현예들은 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해 제공되는 것이다.
(메트)아크릴레이트 수지의 제조
제조예 1 내지 8
하기 표 1에 기재된 함량으로 각 성분을 혼합하여 용액중합으로 (메트)아크릴레이트 수지를 제조하였다.
알킬(메트)아크릴레이트 모노머 광개시형 모노머 가교성 관능기 함유 모노머
제조예1 2-EHA 97 중량% BPMA 1 중량% AA 2.0 중량%
제조예2 2-EHA 97.5 중량% BPMA 0.5 중량% AA 2 중량%
제조예3 2-EHA 98 중량% BPMA 0.5 중량% AA 1.5 중량%
제조예4 2-EHA 98.9 중량% BPMA 0.1 중량% AA 1.0 중량%
제조예5 2-EHA 59 중량%, LA 20 중량% BPMAm 1.0 중량% 4-HBA 20.0 중량%
제조예6 2-EHA 58.3 중량%, LA 19.4 중량% BPMAm 2.9 중량% 4-HBA 19.4 중량%
제조예7 2-EHA 57.2 중량%, LA 19.0 중량% BPMAm 4.8 중량% 4-HBA 19.0 중량%
제조예8 2-EHA 54.6 중량%, LA 18.2 중량% BPMAm 9.0 중량% 4-HBA 18.2 중량%
상기 표 1에서, 2-EHA 는 2-에틸헥실아크릴레이트이고, LA 는 라우릴 아크릴레이트이고, MA는 메틸아크릴레이트이다. 또한, BPMA는 4-벤조일페닐 (메트)아크릴레이트이고, BPMAm 는 또는 N-(2-벤조일페닐) 아크릴아미드이고, AA는 아크릴산이고, 4-HBA는 4-히드록시부틸아크릴레이트이고, 2-HEA는 2-히드록시에틸아크릴레이트이다.
제조예 9
2-에틸헥실아크릴레이트 20 중량부, 메틸 아크릴레이트 55 중량부 및 2-히드록시에틸아크릴레이트 25 중량부를 혼합하여 용액중합으로 프리폴리머를 제조한 후, 쇼와덴코 社의 이소시아네이트기 및 아크릴레이트기를 포함하는 모노머인 Karenz MOI 20 중량부를 첨가하여 2차 중합하고 (메트)아크릴레이트 수지를 제조하였다.
폴더블 디스플레이용 보호 필름의 제조
실시예 1
상기 제조예 1에서 제조한 (메트)아크릴레이트 수지에 에폭시계 경화제 BXX-5240을 0.03부를 투입한 후 분산하여 점착제 조성물을 제조하였다. 이후 Toray사의 U483 50um PET필름 상에 도포한 후 건조, 경화시켜 최종 두께 25um가 되도록 하여 폴더블 디스플레이용 보호 필름을 제조하였다.
실시예 2 내지 5 및 비교예 1 내지 4
하기 표 2에 기재된 바와 같이 (메트)아크릴레이트 수지에 경화제 및/또는 광개시제를 투입하여 분산한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 폴더블 디스플레이용 보호 필름을 제조하였다.
(메트)아크릴레이트 수지 경화제 광개시제
실시예 1 제조예1 BXX-5240 0.03 중량부 -
실시예 2 제조예2 BXX-5240 0.03 중량부 -
실시예 3 제조예3 BXX-5240 0.03 중량부 -
비교예 1 제조예4 BXX-5240 0.03 중량부 -
실시예 4 제조예5 TKA-100 0.07 중량부 -
실시예 5 제조예6 TKA-100 0.07 중량부 -
비교예 2 제조예7 TKA-100 0.07 중량부 -
비교예 3 제조예8 TKA-100 0.07 중량부 -
비교예 4 제조예9 MHG-80B 2 중량부 IRG184 20 중량부
상기 표 2에서, BXX-5240 은 에폭시계 경화제이고, TKA-100 및 MHG-80B는 이소시아네이트계 경화제이고, IRG 184는 Irgacure 184이다.
물성 평가
초기 접착력 측정
상기 실시예 1 내지 5 및 비교예 1 내지 4에서 제조한 폴더블 디스플레이용 보호 필름을 투명 PI 기재에 부착하고, 23℃, 50 RH%에서 300 mm/min의 박리 속도로 180° 박리 테스트를 하여 광 조사 전 초기 접착력을 측정하였다.
광 조사 후 접착력 측정
상기 실시예 1 내지 5 및 비교예 1 내지 4에서 제조한 폴더블 디스플레이용 보호 필름을 투명 PI 기재에 부착하고, 메탈할라이드 램프를 이용하여 UVA 기준 3000 mJ/cm2 이상의 에너지(320~390 nm 파장, EIT 社의 UV power puck 2로 측정)를 갖는 광을 조사하였다. 이후 23℃, 50 RH%에서 300 mm/min의 박리 속도로 180° 박리 테스트를 하여 광 조사 후 접착력을 측정하였다.
광특성 측정
상기 실시예 1 내지 5 및 비교예 1 내지 4에서 제조한 폴더블 디스플레이용 보호 필름을 색차계 기기에 장착하고, 헤이즈, 황색도 및 광 투과율을 측정하였다.
색차계 기기는 Nippon Denshoku사의 COH-400 제품을 이용하였다,
4R 폴딩평가
상기 실시예 1 내지 5 및 비교예 1 내지 4에서 제조한 폴더블 디스플레이용 보호 필름을 투명 PI 기재에 부착하고, 메탈할라이드 램프를 이용하여 UVA 기준 3000 mJ/cm2 이상의 에너지(320~390 nm 파장, EIT 社의 UV power puck 2로 측정)를 갖는 광을 조사하였다. 이후 곡률이 4R(보호 필름간 간격이 8mm)이 되고, 외면이 보호 기재가 되도록 접은 후 1일간 방치한 후 다시 펼쳐 외관을 확인하였다.
상기에서 측정한 접착력, 헤이즈, 황색도 및 광 투과율을 하기 표 3에 나타내었다.
초기접착력
(gf/in)		 최종접착력
(gf/in)		 헤이즈
(%)		 황색도 광투과율
(%)		 자외선 3000mJ/cm2 조사후4R 폴딩평가
실시예1 1021 75 1.00 0.14 92.06 유지
실시예2 930 157 1.15 0.24 91.89 유지
실시예3 842 163 1.34 0.19 92.13 유지
비교예1 691 475 1.12 0.20 91.98 유지
실시예4 1585 60 1.11 0.88 92.29 유지
실시예5 1351 258 1.12 0.93 92.32 유지
비교예2 1293 435 1.04 0.89 92.27 유지
비교예3 1371 939 1.22 1.75 91.89 유지
비교예4 1265 4 0.67 0.52 91.47 탈리
상기 표 3을 참조하면, 실시예 1 내지 5의 폴더블 디스플레이용 보호 필름은 초기 접착력이 842 gf/in 이상으로 매우 높으나, 광 조사 후 접착력이 75 내지 258 gf/in로 현저히 낮아진 것을 확인할 수 있다. 즉, 자외선에 노출되는 경우 접착력이 낮아져 커버윈도우의 손상 없이 박리가 가능한 것을 확인할 수 있다. 반면, 비교예 1의 경우 초기 접착력은 너무 낮고 최종 접착력이 너무 높으며, 비교예 2 내지 4는 초기 접착력은 우수하나 최종 접착력이 너무 낮거나 너무 높은 것을 확인할 수 있다.
자외선 광량별 접착력 변화 측정
실시예 1에서 제조한 폴더블 디스플레이용 보호 필름을 투명 PI 기재에 부착하고, 자외선의 광량을 변화시켜가며 접착력을 측정하였다.
도 1에 자외선 광량에 따른 실시예 1에서 제조한 폴더블 디스플레이용 보호 필름의 접착력 그래프를 나타내었다.
도 1을 참조하면, 광량이 증가할수록 접착력이 낮아지는 것을 확인할 수 있고, 도 1에 삽입된 표를 참조하면 자외선 광량이 0 mJ/cm2인 경우, 즉 초기의 접착력은 1021 gf/in으로 매우 높은 것을 확인할 수 있다. 그러나 자외선 광량이 약 562 mJ/cm2인 경우, 접착력이 약 300 gf/in으로 매우 낮아진 것을 확인할 수 있다. 또한 3000 mJ/cm2 이상의 광량에 도달하는 경우, 접착력 수준은 더 이상 떨어지지 않고 유지되는 것을 확인할 수 있다. 이는 점착제층의 가교가 최대 수준으로 충분히 진행되었으며 더 이상의 접착력 변동이 없어짐을 의미한다.

Claims (17)

  1. 알킬(메트)아크릴레이트 모노머; 가교성 관능기 함유 모노머; 및 광개시형 모노머;를 포함하는 혼합물이 공중합되어 제조된 (메트)아크릴레이트 수지를 포함하는 점착제 조성물을 포함하는 점착제층; 및
    상기 점착제층의 일면에 구비된 보호기재;를 포함하는 폴더블 디스플레이용 보호 필름으로서,
    상기 광개시형 모노머는 상기 혼합물의 0.2 내지 4.5 중량% 로 포함되고,
    반경 4mm 폴딩 테스트 결과, 상기 보호 기재가 손상 또는 탈리되지 않고 유지되고,
    하기 식 1을 만족하는 것인 폴더블 디스플레이용 보호 필름:
    [식 1]
    1 ≤ 100 * B / A ≤ 30
    상기 식 1에서,
    A는 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 광 조사 전 23℃, 50 RH%에서 측정한 접착력이고,
    B는 상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 380nm 이하의 파장을 갖는 광 조사 후 23℃, 50 RH%에서 측정한 접착력이다.
  2. 제1항에 있어서,
    상기 점착제층의 상기 보호 기재와 접하는 면의 반대면을 PI기재에 대하여 접합 후 광 조사 전 23℃, 50 RH%에서 측정한 접착력이 800gf/in 이상이고, 380nm 이하의 파장을 갖는 광 조사 후 23℃, 50 RH%에서 측정한 접착력이 10gf/in 내지 300gf/in인 것인 폴더블 디스플레이용 보호 필름.
  3. 제1항에 있어서,
    상기 광개시형 모노머는 (메트)아크릴레이트기를 갖는 벤조페논(Benzophenone)계 화합물인 폴더블 디스플레이용 보호 필름.
  4. 제1항에 있어서,
    상기 알킬 (메트)아크릴레이트 모노머는 펜틸 (메트)아크릴레이트, n-부틸 (메트)아크릴레이트, 에틸 (메트)아크릴레이트, 메틸 (메트)아크릴레이트, 헥실 (메트)아크릴레이트, n-옥틸 (메트)아크릴레이트, 이소옥틸 (메트)아크릴레이트, 2-에틸헥실 (메트)아크릴레이트, 도데실 (메트)아크릴레이트 및 데실 (메트)아크릴레이트 중 1종 이상을 포함하는 것인 폴더블 디스플레이용 보호 필름.
  5. 제1항에 있어서,
    상기 가교성 관능기 함유 모노머는 카르복실기 함유 모노머 및 히드록시기 함유 모노머 중 1종 이상을 포함하는 것인 폴더블 디스플레이용 보호 필름.
  6. 제5항에 있어서,
    상기 카르복실기 함유 모노머는 (메트)아크릴산, 2-(메트)아크릴로일옥시아세트산, 3-(메트)아크릴로일옥시프로필산, 4-(메트)아크릴로일옥시부틸산, 아크릴산 이량체, 이타콘산, 말레산 및 말레산 무수물 중 1종 이상을 포함하는 것인 폴더블 디스플레이용 보호 필름.
  7. 제5항에 있어서,
    상기 히드록시기 함유 모노머는 2-히드록시에틸 (메트)아크릴레이트, 2-히드록시프로필 (메트)아크릴레이트 및 4-히드록시부틸 (메트)아크릴레이트 중 1종 이상을 포함하는 것인 폴더블 디스플레이용 보호 필름.
  8. 제1항에 있어서,
    상기 가교성 관능기 함유 모노머는 상기 혼합물의 0 초과 20 중량% 이하로 포함되는 것인 폴더블 디스플레이용 보호 필름.
  9. 제1항에 있어서,
    상기 점착제 조성물은 용매, 경화제, 분산제, 열개시제, 실란커플링제, 가소제, 점착 부여제, 광개시제, 산화방지제 및 자외선 안정제 중 1종 이상을 더 포함하는 것인 폴더블 디스플레이용 보호 필름.
  10. 제1항에 있어서,
    상기 점착제층의 두께는 10 ㎛ 이상 100 ㎛ 이하인 것인 폴더블 디스플레이용 보호 필름.
  11. 제1항에 있어서,
    상기 보호기재의 두께는 25 ㎛ 이상 150 ㎛ 이하인 것인 폴더블 디스플레이용 보호 필름.
  12. 제1항에 있어서,
    상기 보호기재는 PET(polyethylene terephthalate), 폴리에스테르(polyester), PC(polycarbonate), PI(polyimide), PEN(polyethylene naphthalate), PEEK(polyether ether ketone), PAR(polyarylate), PCO(polycylicolefin), 폴리노보넨(polynorbornene), PES(polyethersulphone), 유리(glass) 및 COP(cycloolefin polymer)로 이루어진 군으로부터 선택되는 것인 폴더블 디스플레이용 보호 필름.
  13. 제1항에 있어서,
    상기 점착제층의 상기 보호기재와 접하는 면의 반대 면에 이형 필름을 더 포함하는 것인 폴더블 디스플레이용 보호 필름.
  14. 제1항에 있어서,
    상기 폴더블 디스플레이용 보호 필름의 헤이즈(haze)가 0% 초과 2% 이하이며,
    상기 폴더블 디스플레이용 보호 필름의 황색도(Yellow index)가 0 초과 3 이하이고,
    상기 폴더블 디스플레이용 보호 필름의 파장 550nm의 광 투과율이 85% 이상인 것인 폴더블 디스플레이용 보호 필름.
  15. 폴더블 디스플레이; 및
    상기 폴더블 디스플레이의 일면에 구비된 제1항에 따른 폴더블 디스플레이용 보호 필름;을 포함하고,
    상기 폴더블 디스플레이용 보호 필름의 상기 점착제층과 상기 폴더블 디스플레이의 일면이 접하는 것인 폴더블 디스플레이 장치.
  16. 제15항에 있어서,
    상기 폴더블 디스플레이는, 플렉서블 기재;
    유기 발광층;
    편광판; 및
    커버 윈도우;가 순차적으로 적층된 구조로,
    상기 커버 윈도우의 상기 편광판과 접하는 면의 반대면에 상기 폴더블 디스플레이용 보호 필름의 상기 점착제층이 구비되는 폴더블 디스플레이 장치.
  17. 제16항에 있어서,
    상기 플렉서블 기재는 TPU(thermoplastic polyurethane), PDMS(polydimethylsiloxane), GLASS, PET(polyethylene terephthalate), 폴리에스테르(polyester), PC(Polycarbonate), PI(polyimide), PEN(polyethylenenaphthalate), PEEK(polyether ether ketone), PAR(polyarylate), PCO(polycylicolefin), 폴리노보넨(polynorbornene), PES(polyethersulphone) 및 COP(cycloolefin polymer) 중 1종 이상인 것인 폴더블 디스플레이 장치.
KR1020200149871A 2019-11-15 2020-11-11 접착력 가변 폴더블 디스플레이용 보호 필름 및 이를 포함하는 폴더블 디스플레이 장치 KR102381676B1 (ko)