KR102140152B1 - 노란색 빛을 차단하는 디스플레이용 투명부재 - Google Patents

노란색 빛을 차단하는 디스플레이용 투명부재 Download PDF

Info

Publication number
KR102140152B1
KR102140152B1 KR1020170034761A KR20170034761A KR102140152B1 KR 102140152 B1 KR102140152 B1 KR 102140152B1 KR 1020170034761 A KR1020170034761 A KR 1020170034761A KR 20170034761 A KR20170034761 A KR 20170034761A KR 102140152 B1 KR102140152 B1 KR 102140152B1
Authority
KR
South Korea
Prior art keywords
display
transparent
transparent member
delete delete
yellow light
Prior art date
Application number
KR1020170034761A
Other languages
English (en)
Other versions
KR20180106434A (ko
Inventor
유영철
권오성
조병옥
한승택
임형섭
Original Assignee
(주)석경에이티
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)석경에이티 filed Critical (주)석경에이티
Priority to KR1020170034761A priority Critical patent/KR102140152B1/ko
Publication of KR20180106434A publication Critical patent/KR20180106434A/ko
Application granted granted Critical
Publication of KR102140152B1 publication Critical patent/KR102140152B1/ko

Abstract

본 발명은 노란색 빛을 흡수하는 두께가 10Å~10000Å 이내인 디스플레이용 투명부재를 제공하며, Nd(OCH3)3, Nd(OC2H5)3 등의 Nd의 유기금속화합물을 원료로 하여 노란색 광만 선택적으로 흡수시키는 색재현성을 높인 투명 디스플레이용 부재를 제조할 수 있다. 따라서 이러한 투명 디스플레이용 부재를 사용하여 내열성, 신뢰성에서 차별화되는 투명 디스플레이 장치를 얻을 수 있다.

Description

노란색 빛을 차단하는 디스플레이용 투명부재{TRANSPARENT SUBSTANCE HAVING ABSORBING YELLOW LIGHT FOR DISPLAY}
본 발명은 고온 신뢰성 및 내열성이 우수한 디스플레이용 투명부재에 관한 것이다.
전자 기술의 발전에 따라 다양한 디스플레이 장치가 개발되고 있다. CRT, LCD, PDP, OLED 등과 같이 다양한 디스플레이 부품을 포함하는 디스플레이 장치들이 사용되었거나 사용되고 있다. 그러나, 기존의 디스플레이 장치들은 디스플레이부가 배치된 일 방향에서 시청할 수 밖에 없는 한계를 가지고 있었다. 이러한 한계를 극복하기 위해 투명 디스플레이 장치에 대한 연구가 진행되고 있다.
투명 디스플레이 장치는 디스플레이부가 투명하기 때문에 사용자가 디스플레이부에 표시되는 컨텐츠와 함께 디스플레이부 뒷면의 피사체를 함께 볼 수 있는 장점이 있다. 이러한 LED 등의 디스플레이용 투명부재의 기존 재료는 Yellow 파장대를 흡수하는 재료는 많으나 입자 Size가 커 휘도 저하가 크게 발생하고 또한 유기 안료를 사용하여 고온 신뢰성 및 색순도 유지가 어려운 단점이 있었다. 또한 투명 기판을 PC, PVC, PET를 사용하는 경우에도, 이와 같은 필름은 그 내열특성이 COB 공정의 섭씨 100 내지 160도의 1 내지 3시간의 공정온도를 견디지 못하는 내열특성을 가지고 있는바, 제품의 생산에 있어서 휨, 비틀림, 변색, 수축 등의 다양한 불량요인으로 인해 제품양산이 불가능하다는 단점이 있고, 더 나아가 발광 다이오드 상에 전극을 적층하여 기판과 전극 사이에 발광 다이오드가 형성되어 있어 전극이 외부로 노출되어 외력에 취약하다는 구조적 불안정성을 가지면서도 이를 해결하기 위한 마땅한 수단을 제시하지 못하고 있는 상황이다.
본 발명의 목적은 노란색 빛을 차단하는 디스플레이용 투명부재를 제공하는 것을 목적으로 한다.
또한 본 발명은 본 발명의 목적은 내열성, 신뢰성에서 차별화되는 투명 디스플레이용 부재를 제조하는 것이다.
본 발명은 노란색 빛을 흡수하는 디스플레이용 투명부재를 제공한다. 또한 상기 상기 투명부재의 두께가 10Å~10000Å 이내인 것을 특징으로 하며 투명부재의 가시광선 투과율이 50% 이상인 것을 특징으로 한다.
상기 투명부재는 기재에 노란빛을 흡수하는 Nd계 화합물 층이 코팅된 것을 특징으로 한다. 상기 투명부재 내에는 Nd계 화합물이 10ppm 이상 함유된 것을 특징으로 한다.
또한 상기 노란빛을 흡수하는 투명부재는 Nd(OCH3)3, Nd(OC2H5)3 등의 Nd의 유기금속화합물을 원료로 하여 코팅하여 건조하거나 CVD 법으로 만들어진 것을 특징으로 한다.
상기 Nd2O3 층은 Nd2O3 Sol을 이용하여 만들어질 수 있고, Nd2O3 타겟을 이용하여 만들어질 수 있다.
한편, 상기 투명부재는 Neodium Metal 타겟을 이용하여 만들어질 수 있다.
그리고 상기 투명부재는 Nd2O3과 디스플레이용 광학부재를 컴파운드하여 만들어질 수도 있다. 이와 같은 디스플레이용 투명기재는 투명 플라스틱 필름, 시트, 유리, 석영(Quartz)으로부터 선택되는 것을 특징으로 한다.
본 발명의 목적은 Nd(OCH3)3, Nd(OC2H5)3 등의 Nd의 유기금속화합물을 원료로 하여 노란색 광만 선택적으로 흡수시키는 색재현성을 높인 투명 디스플레이용 부재를 제조할 수 있다. 따라서 이러한 투명 디스플레이용 부재를 사용하여 내열성, 신뢰성에서 차별화되는 투명 디스플레이 장치를 얻을 수 있다.
도 1 및 도 2는 광 특성 평가 결과를 나타낸 그래프이다.
도 3은 Green 형광체 자체 색차값을 나타낸 그래프이다.
도 4는 흡광체 코팅 후 색차값을 나타낸 그래프이다.
이하에서는 실시예를 통하여 본 발명의 노란색 빛을 흡수하는 디스플레이용 투명부재를 보다 상세하게 설명한다.
1. 고투명 Nd 2 O 3 Sol 제조
Nd-Acetate + Acetic acid + pure water 혼합액을 수열(Hydro thermal, 120 ~ 250℃)처리하여 Purple색의 10nm이하의 고투명 Nd2O3 Sol 제조하였다.
상기 액을 기재에 코팅하여 건조하거나 CVD법으로 코팅하여 투명 부재를 제조하였다.
즉, 노란빛을 흡수하는 투명부재는 Nd(OCH3)3, Nd(OC2H5)3 등의 Nd의 유기금속화합물을 원료로 하여 코팅하여 건조하거나 CVD 법으로 제조하였다.
또한 Neodium Metal 타겟을 이용하여 만들어질 수 있고, Nd2O3과 디스플레이용 광학부재를 컴파운드하여 만들어질 수도 있다.
2. 코팅 함량
상기 투명부재는 기재에 노란빛을 흡수하는 Nd2O3 층이 코팅된 것을 특징으로 한다. Nd2O3 함량은 0.1wt% 함유하였다.
투명기재로는 투명 플라스틱 필름, 시트, 유리, 석영(Quartz)으로부터 선택될 수 있다.
3. 코팅 및 건조
고투명 Nd2O3 Sol을 함량별로 균일 혼합 후 Evaporator를 이용하여 H2O 를 제거하면서 80~300℃ 에서 균일 코팅 건조하였다.
투명부재의 코팅 두께가 10Å~10000Å 이내인 것이 바람직하다.
4. 흡수 영역 : 560~600nm ( Yellow 광 흡수)
도 1 및 도 2에서는 광 특성 평가 결과를 나타내었다.
투명부재의 가시광선 투과율이 50% 이상이다. 즉, 560~600nme대의 불필요한 광을 흡수하여 고색재현이 가능하고, NTSC 100%이상의 색재현율 및 DTI 중첩비 100% 가능함을 알 수 있다.

Claims (12)

  1. Nd계 화합물이 10 ppm 이상 함유되어 있는 Nd계 화합물 층이 10 ~ 10,000Å 의 두께로 코팅되어, 노란색 빛을 흡수하고 가시광선 투과율이 50% 이상이며, TSC 100% 이상의 색재현율 및 DTI 중첩비 100% 를 가지는 디스플레이용 투명부재로서,
    상기 Nd계 화합물 층은 Nd의 유기금속화합물인 Nd(OCH3)3 및 Nd(OC2H5)3 원료를 코팅하여 건조하거나 CVD 법으로 만들어지며, 상기 투명부재는 Nd2O3 타겟 또는 Neodium Metal 타겟을 이용하여 만들어진 것을 특징으로 하는 디스플레이용 투명부재.
  2. 삭제
  3. 삭제
  4. 삭제
  5. 삭제
  6. 삭제
  7. 삭제
  8. 삭제
  9. 제1항에 있어서, 상기 투명부재는 Nd2O3과 디스플레이용 광학부재를 컴파운드하여 만들어진 것을 특징으로 하는 디스플레이용 투명부재.
  10. 삭제
  11. 삭제
  12. 제1항, 또는 제9항에 있어서, 상기 디스플레이용 투명부재는 투명 플라스틱 필름, 시트, 유리, 석영(Quartz)으로부터 선택되는 것을 특징으로 하는 디스플레이용 투명부재.
KR1020170034761A 2017-03-20 2017-03-20 노란색 빛을 차단하는 디스플레이용 투명부재 KR102140152B1 (ko)