Abstract

(과제)
튀김의 과잉 유분의 흡수 용도에 적합한 키친 페이퍼를 제공한다.
(해결 수단)
엠보스가 부여되어 있지 않은 2 장의 크레이프지가 산재적으로 배치된 접착제를 개재하여 적층 일체화되고, 상기 접착제 중에, 열에 의해 발포하여 팽창되는 발포 잉크가 미발포 상태로 함유되어 있는 키친 페이퍼에 의해 해결된다.(assignment)
Provides kitchen paper suitable for absorbing excess oil in frying.
(Solution)
Two sheets of crepe paper to which no embossment is imparted are laminated and integrated via an adhesive disposed in a scattered manner and the adhesive paper is solved by a kitchen paper in which a foamed ink which is expanded and expanded by heat is contained in an unfoamed state.

Description

Kitchen paper {KITCHEN PAPER}

본 발명은 키친 페이퍼에 관한 것이다.The present invention relates to kitchen paper.

키친 페이퍼의 용도는, 식품의 포장, 조림 음식의 작은 뚜껑, 선어 (鮮魚) 등의 드립 흡수재, 물기 제거, 기름기 여과, 부엌 주변의 걸레질 등 다방면에 걸쳐 사용되는데, 그 하나로, 접시나 트레이 위에 키친 페이퍼를 깔아, 그 위에 튀긴 튀김이나 데친 것을 두고, 튀김 등의 과잉 유분이나 수분을 흡수하기 위한 용도가 있다. 이 튀김 등의 과잉 유분 등의 흡수 용도에 있어서는, 튀김옷 등을 손상시키지 않고, 튀김 등으로부터의 증기나 기름에 의해 튀김 등이 달라붙지 않도록 빠르게 기름이나 물기를 흡수하고, 또한 그 일단 흡수된 기름 등이 튀김 등으로 돌아가지 않도록 하는 기능이 요구된다.The use of kitchen paper is used for various aspects such as packing of food, small lid of stewed food, drip absorber such as fresh fish, dewatering, oil filtration, mopping around kitchen, There is a use for laying up paper, fried deep-fried food or batter, and for absorbing excess oil or moisture such as deep-fried food. In the absorption application such as the excessive oil such as the deep-fried food, the oil or moisture is quickly absorbed so that the deep-fried food does not adhere due to steam or oil from the deep-fried food or the like without damaging the deep- It is required to have a function of preventing the user from returning to the deep-fried food or the like.

종래의 키친 페이퍼는, 엠보스 가공한 위생 박엽지를 적당한 장수 적층한 것이 잘 알려져 있는데, 이 종래의 키친 페이퍼는, 엠보스의 요철에 의해 지면과 튀김 등의 접촉 면적이 작고, 또 시트 섬유 사이의 공극에 의한 모세관 현상을 주된 흡액 기구로 하여 각 시트의 엠보스 사이의 공극에 수분, 유분 등을 받아들여 유지하도록 함으로써, 튀김 등의 과잉 유분 등의 흡수 용도에 있어서의 기능성이 확보되고 있다.In the conventional kitchen paper, it is well known that an embossed sanitary papermaking paper is laminated with a suitable long lap. In this conventional kitchen paper, the contact area of the ground and the frying is small due to the embossing and embossing of the emboss, The capillary phenomenon by the gap is used as a main liquid absorbing mechanism and water and oil are received and held in the space between the embosses of each sheet to secure the functionality in absorbing applications such as excessive oil such as frying.

그러나, 상기 서술한 엠보스 가공한 종래 키친 페이퍼는, 튀김을 놓았을 때, 그 하중이나 유분, 수분의 흡액에 의한 섬유의 풀림에 의해, 엠보스가 찌부러지는 경우가 있어, 엠보스에 의한 흡액성을 충분히 발휘할 수 없는 경우가 있었다.However, in the above-described embossed conventional kitchen paper, the emboss may be distorted by loosening of the fibers due to the absorption of the load, oil, and moisture when the fry is placed, and the emboss- Can not be fully demonstrated.

이 문제는, 엠보스 부여시의 엠보스압을 높이고, 엠보스를 종이에 확실하게 부여함으로써 어느 정도는 개선되지만, 과도한 엠보스압은 종이의 파단 원인이 되고, 또 확실하게 부여된 엠보스는 종이를 뻣뻣하게 하는 경우가 있어, 제조상 혹은 닦아내는 용도 등 키친 페이퍼가 필요로 하는 부드러움이나 유연성을 저하시킨다는 다른 문제를 일으킨다.This problem is somewhat improved by increasing the embossing pressure at the time of embossing and reliably applying the embossing to the paper, but excessive embossing pressure causes the paper to be broken, Which may cause stiffness, which may cause problems such as softness and flexibility required for kitchen paper such as manufacturing or wiping.

그래서, 본 발명자들은, 키친 페이퍼의 닦는 기능 등의 주요 기능을 저하시키지 않고, 튀김의 과잉 유분의 흡수 성능을 높이기 위해, 하기 특허문헌 1 및 2 에 개시되는 발포 잉크에 주목하였다. 이들 발포 잉크는, 주로 장식성, 의장성을 높이기 위해 사용되는 것인데, 그 발포성의 메커니즘을 키친 페이퍼에 유용하게 이용할 수 있는 것을 지견하여 본 발명을 완성하기에 이르렀다.Therefore, the present inventors paid attention to the foaming inks disclosed in the following Patent Documents 1 and 2 in order to enhance the absorption performance of the excessive oil of the fry without deteriorating the main function such as the function of wiping the kitchen paper. These foaming inks are mainly used for enhancing ornamentality and designability, and it has been found that the mechanism of the foaming property can be effectively utilized for kitchen paper, and thus the present invention has been accomplished.

일본 공개특허공보 2002-254588호Japanese Patent Application Laid-Open No. 2002-254588 일본 공개특허공보 평9-41296호Japanese Patent Application Laid-Open No. 9-41296

본 발명의 주된 과제는, 통상적인 키친 페이퍼로서의 기능을 가지면서도, 특히 튀김의 과잉 유분을 흡수하는 용도에 있어서 특히 적합한 키친 페이퍼를 제공하는 것에 있다.The main object of the present invention is to provide a kitchen paper which is particularly suitable for use in absorbing excess oil of frying while having a function as a normal kitchen paper.

상기 과제를 해결한 본 발명 및 작용 효과는 다음과 같다.The present invention, which has solved the above problems, and its effects are as follows.

<청구항 1 에 기재된 발명><Invention according to Claim 1>

엠보스가 부여되어 있지 않은 2 장의 크레이프지가 선 형상으로 배치된 접착제를 개재하여 적층 일체화되고, 그 선 형상으로 배치된 접착제에 의해 둘러싸인 구획을 복수 갖고, 또한 상기 접착제에 열에 의해 발포하여 팽창되고 팽창 후에 경화되는 발포성 경화 물질이 미발포 상태로 함유되어 있는 것을 특징으로 하는 키친 페이퍼.Two crepe fabrics not provided with embosses are laminated and integrated via an adhesive disposed in a line shape, and a plurality of compartments surrounded by the linearly arranged adhesive agent are provided, and the adhesive agent is foamed by heat, expanded, Wherein the foamable curing material to be cured is contained in an unfoamed state.

(작용 효과)(Action effect)

본 발명은, 2 장의 크레이프지끼리를 접착하는 접착제 중에 열을 가함으로써 발포하여 팽창되고 팽창 후에 경화되는 발포 경화 물질을 함유시켰기 때문에, 트레이, 배트 (vat), 접시 등에 깔고, 그 위에 튀김 등을 놓았을 때, 그 튀김이 갖는 열에 의해 상기 발포성 경화 물질이 발포된다. 그리고, 발포성 경화 물질은, 발포 후에 그 발포 상태가 유지되고, 탄성, 강성, 혹은 강탄성이 있는 경화된 상태로 변화되므로, 발포성 경화 물질의 발포에 의해, 본 발명의 키친 페이퍼는, 크레이프지 사이의 간격이 넓어짐과 함께, 2 장의 크레이프지 사이에 튀김 등으로부터의 유분 등을 흡수 유지하는 공극이 형성되어 그것이 유지된다.In the present invention, since an adhesive for bonding two sheets of crepe paper contains a foamed hardening substance which is foamed, expanded, and cured after expansion by applying heat, it is spread on a tray, a vat, a plate, The foamable curing substance is foamed by the heat of the frying. Since the foamable cured material is maintained in its foamed state after foaming and is changed into a cured state having elasticity, rigidity or strong elasticity, the foam paper of the present invention is foamed by foaming of the foamy curable material, And a space for absorbing and retaining oil or the like from the deep-fried food or the like is formed between the two sheets of crepe paper and is retained.

특히, 본 발명에서는, 접착제를 선 형상으로 배치하고, 그 선 형상으로 배치된 접착제에 의해 둘러싸인 구획을 복수 갖도록 되어 있다. 따라서, 선 형상으로 배치된 접착제 부분에 포함되는 발포성 경화 물질이 발포됨으로써, 당해 접착제 부여 부분이 다수의 벽주 (壁柱) 가 되어 튀김을 지지하도록 작용한다.Particularly, in the present invention, the adhesives are arranged in a linear shape, and a plurality of sections surrounded by the linearly arranged adhesive are provided. Therefore, the foamable hardening material contained in the linearly arranged adhesive portion is foamed, so that the adhesive-applied portion functions as a plurality of wall posts to support the frying.

또, 발포성 경화 물질을 함유하는 접착제는, 크레이프지에 대한 도포, 인쇄 등의 부여시, 크레이프지의 지층 (紙層) (2 장의 크레이프지의 간격이 아니라 크레이프지의 내부) 에도 침투하기 때문에, 당해 접착제 부여 부분은, 발포 후에 종이만으로 형성되는 엠보스 볼록부와 비교하면 매우 높은 형상 유지성을 갖고, 당해 공극이 튀김 등에 의한 하중으로도 찌부러지지 않고 유지된다.Further, since the adhesive containing the foamable curing substance infiltrates into the crepe paper layer (the inside of the crepe paper instead of the interval between the two crepe paper sheets) of the crepe paper when the crepe paper is applied or printed, Has a very high shape-retaining property as compared with the emboss convex portion formed only of paper after foaming, and the porosity is retained without being crushed by a load caused by frying or the like.

또, 본 발명에서는, 선 형상으로 배치된 접착제에 의해 둘러싸인 구획을 복수 갖도록 되어 있기 때문에, 2 장의 크레이프지 사이에 형성되는 공극이 구획되어 있고, 충분한 공극이 확보되어 있음과 함께, 1 구획에 흡액된 기름 등이 다른 공극으로 이동하지 않는다. 따라서, 기름 등을 흡액한 하나의 구획은, 다른 구획에 대한 흡액성의 영향이 없다. 이것은, 지면을 넓게 사용할 수 있고, 이로써 복수의 튀김을 놓았을 때의 편리성이 높아진다.Further, according to the present invention, since a plurality of compartments surrounded by the linearly arranged adhesive are provided, voids formed between the two sheets of crepe paper are partitioned, sufficient voids are ensured, The oil does not move to other pores. Therefore, one compartment in which oil or the like is absorbed has no influence on the liquid-absorbing properties of the other compartments. This makes it possible to use a wider ground, thereby enhancing the convenience of placing a plurality of fries.

또한, 본 발명에서는 크레이프를 갖는 크레이프지를 이용하고, 또한 접착제를 선 형상으로 배치하고, 그 선 형상으로 배치된 접착제에 의해 둘러싸인 구획을 복수 갖도록 되어 있고, 인접하는 선 형상의 접착제 부여 부분 사이에 접착제 비부여 부분이 존재한다. 이로써, 튀김 등에 닿은 일부분의 발포성 경화 물질이 발포되었다고 해도, 접착제가 부여되어 있지 않은 부분의 크레이프가 신장되므로, 발포성 경화 물질이 지면의 일부분에서 발포되었다고 해도 키친 페이퍼가 찢어지지 않는다.Further, in the present invention, crepe paper having a crepe is used, and the adhesive is linearly arranged, and a plurality of sections surrounded by the linearly arranged adhesive are provided, and an adhesive There is a non-imparted portion. Thereby, even if a part of the foamable hardened material touching the fry or the like is foamed, the crepe of the portion to which the adhesive is not applied is stretched, so that even if the foamed hardened material is foamed at a part of the ground, the kitchen paper is not torn.

한편, 키친 페이퍼는, 일반적으로 롤 형상, 다발 형상으로 판매되기 때문에 과도하게 부피가 크면 수송상의 문제가 있지만, 본 발명에서는, 접착제 중에 발포성 경화 물질을 미발포 상태로 함유시키는 것으로 되어 있기 때문에, 수송시 등의 미사용시에 있어서의 취급에 대해 종래의 키친 페이퍼에 비해 열등하지도 않다.On the other hand, since the kitchen paper is generally sold in the form of a roll or a bundle, there is a transportation problem if the volume is excessively large. In the present invention, since the foamable curing substance is contained in an unfoamed state in the adhesive, It is not inferior to the conventional kitchen paper in terms of handling in the unused state of the city or the like.

또, 본 발명에서는, 크레이프지에 엠보스를 부여하지 않는다. 따라서, 엠보스 부여시의 가압에 의한 크레이프지의 종이 두께 저하, 섬유의 고밀도화 등이 없고, 따라서, 섬유간 공극이 충분히 확보되고, 흡액 속도에 있어서 우수하다. 또, 부피감, 유연성, 부드러움 면에서도 우수하다.In the present invention, no emboss is given to the crepe paper. Therefore, there is no reduction in the paper thickness of the crepe paper due to the pressing at the time of embossing and a high density of the fibers. Therefore, the inter-fiber voids are sufficiently ensured and the absorption speed is excellent. Also, it is excellent in terms of volume, flexibility and softness.

또한, 접착제를 산재적으로 배치함과 함께, 발포성 경화 물질을 미발포 상태로 접착제 중에 함유시키는 것으로 했기 때문에, 물, 오염, 먼지 등을 닦아내는 용도 등의 키친 페이퍼의 다른 사용시에 있어서는, 그 사용을 저해하지 않는다.In addition, since the adhesive is arranged in an acidic manner and the foamable curing substance is contained in the adhesive in an unfoamed state, when the kitchen paper is used for other purposes such as wiping off water, dirt, dust, etc., Lt; / RTI >

<청구항 2 에 기재된 발명><Invention according to Claim 2>

상기 발포성 경화 물질은 90∼200 ℃ 에서 발포되고, 그 발포에 의해 종이 두께가 발포 전과 비교하여 100 ㎛ 이상 증가하는 청구항 1 에 기재된 키친 페이퍼.The kitchen paper according to claim 1, wherein the foamable curable material is foamed at 90 to 200 캜, and the paper thickness is increased by 100 탆 or more as compared with that before foaming.

(작용 효과)(Action effect)

튀김을 튀길 때의 일반적인 기름의 온도는 180 ℃ 전후이며, 본 발명자들은, 이 온도의 기름으로부터 튀김을 꺼낸 경우, 튀김의 온도가 100∼120 ℃ 정도로 저하되는 것으로 지견하고 있다. 따라서, 본 발명과 같이 발포성 경화 물질이 90∼200 ℃ 에서 발포되는 것으로 하면, 튀김의 과잉 유분의 흡수 용도에 있어서 특히 적합한 것이 된다.The general oil temperature at the time of frying the deep fry is about 180 DEG C and the present inventors believe that when the deep frying oil is taken out from the oil at this temperature, the temperature of the deep frying is lowered to about 100 to 120 DEG C. Therefore, when the foamable curable material is foamed at 90 to 200 캜 as in the present invention, it is particularly suitable for the purpose of absorbing excess oil of the fry.

한편, 키친 페이퍼는, 튀김의 과잉 유분의 흡수 용도 이외에는 90 ℃ 이상의 기름·물에 접할 기회가 매우 적어, 이 범위로 하면, 그 밖의 용도에 사용할 때 발포성 경화 물질이 의도하지 않게 발포되지 않아, 닦아낼 때 등에 있어서는 종래 키친 페이퍼와 전혀 변함 없이 취급할 수 있다.On the other hand, the kitchen paper has a very small chance of coming into contact with oil and water of 90 ° C or more, except for the purpose of absorbing excessive oil of frying. In this range, foaming hardening material is not inadvertently foamed when used for other purposes, And the like can be treated with the conventional kitchen paper at all times.

<청구항 3 에 기재된 발명><Invention according to Claim 3>

키친 페이퍼 전체로서의 종이 두께가 700 ㎛ 이하이고, 각 크레이프지의 평량이 10∼42 g/㎡, 밀도는 2.5 × 10⁴∼4.2 × 10⁵ g/㎥ 인 청구항 1 또는 2 에 기재된 키친 페이퍼.The kitchen paper according to claim 1 or 2, wherein the paper thickness of the entire kitchen paper is 700 μm or less, the basis weight of each crepe paper is 10 to 42 g / m 2, and the density is 2.5 × 10 ^{4 to} 4.2 × 10 ⁵ g / m 3.

(작용 효과)(Action effect)

상기 키친 페이퍼의 종이 두께의 범위에서, 각 크레이프지의 평량, 밀도를 상기 범위로 하면, 발포성 경화 물질의 발포에 의해 공극이 형성되었을 때의 흡액 속도에 있어서 더욱 우수하고, 또 유연하고 부드러우며, 또한 확실하게 닦아낼 수 있게 된다.When the basis weight and density of each crepe paper in the range of the paper thickness of the kitchen paper are within the above range, it is possible to provide a paper material which is superior in the liquid-absorbing speed when the void is formed by foaming of the foamable curing material, So that it can be wiped cleanly.

<청구항 4 에 기재된 발명><Invention according to Claim 4>

선 형상으로 배치된 접착제의 선폭이 0.25∼2.00 ㎜ 이고, 선 형상으로 배치된 접착제에 의해 둘러싸인 1 구획의 면적이 25∼100 ㎟ 인 청구항 1∼3 중 어느 1 항에 기재된 키친 페이퍼.The kitchen paper according to any one of claims 1 to 3, wherein the line width of the linearly arranged adhesive is 0.25 to 2.00 mm and the area of one compartment surrounded by the linearly arranged adhesive is 25 to 100 mm 2.

(작용 효과)(Action effect)

본 발명의 범위로 하면, 발포성 경화 물질이 발포되었을 때 크레이프지 사이에 공극이 충분히 확보된다. 또, 튀김을 놓았을 때, 이것에 접하여 발포된 발포성 경화 물질에 의해 형성되는 발포 접착 부분이 충분한 산재 밀도가 된다. 이로써 튀김을 충분히 지지할 수 있고, 따라서 공극이 확실하게 찌부러지지 않게 된다.In the scope of the present invention, when the foamable curable material is foamed, a sufficient gap is secured between the crepe paper. In addition, when the fry is placed, the foamed adhesive portion formed by the foamed hardening material bubbled in contact therewith has sufficient scattering density. As a result, the fry can be sufficiently supported, so that the gap can not be reliably collapsed.

또한, 상기 범위로 하면, 키친 페이퍼 전체로서의 부드러움이나 유연성을 충분히 확보할 수 있다.In the above range, softness and flexibility as a whole of the kitchen paper can be sufficiently secured.

또한, 구획의 면적이 본 발명의 범위이면, 흡수량과 기름 등의 퍼짐이 억제되는 범위와의 밸런스가 양호하다.When the area of the compartment is within the range of the present invention, the balance between the amount of absorption and the range in which the spread of oil and the like is suppressed is good.

<청구항 5 에 기재된 발명><Invention according to Claim 5>

일방 (一方) 지면에 대한 접착제 부여 부분의 총 면적의 비율이 5∼30 % 인 청구항 1∼4 중 어느 1 항에 기재된 키친 페이퍼.The kitchen paper according to any one of claims 1 to 4, wherein the ratio of the total area of the adhesive application portion to one surface is from 5 to 30%.

(작용 효과)(Action effect)

청구항 3 과 동일한 효과를 발휘한다.The same effects as those of claim 3 are exhibited.

<청구항 6 에 기재된 발명><Invention according to Claim 6>

2 장의 각 크레이프지 중 어느 면에 친유성 기제가 담지되어 있는 청구항 1∼5 중 어느 1 항에 기재된 키친 페이퍼.The kitchen paper according to any one of claims 1 to 5, wherein a lipophilic base material is supported on either side of each of the two crepe paper sheets.

(작용 효과)(Action effect)

친유성 기제를 담지시킴으로써, 기름과 크레이프지의 친화성이 향상되고, 따라서, 흡유 속도가 향상된다.By carrying the lipophilic base agent, the affinity between the oil and the crepe paper is improved, and therefore the rate of oil absorption is improved.

<청구항 7 에 기재된 발명><Invention according to Claim 7>

상기 크레이프지가 띠 형상이고, 또한 길이 방향으로 소정 간격으로 폭 방향에 걸친 절취용 절취선이 배치된 띠 형상의 상기 크레이프지가 롤 형상으로 감겨 있는 청구항 1∼6 중 어느 1 항에 기재된 키친 페이퍼.The kitchen paper according to any one of claims 1 to 6, wherein the crepe paper is in the shape of a strip and the strip-shaped crepe paper in which stripping lines for cutting are arranged in the width direction at predetermined intervals in the longitudinal direction is wound in a roll shape.

(작용 효과)(Action effect)

크레이프지가 롤 형상으로 감겨 있는 키친 페이퍼는 제조가 용이하다. 또, 롤 형상의 키친 페이퍼는, 동일한 롤 직경인 경우 시트의 부피가 커짐에 비례하여 감는 길이 (사용 가능한 길이) 가 짧아지는데, 본 발명은 크레이프지에 엠보스가 부여되어 있지 않기 때문에, 엠보스에서 기인되는 부피 커짐이 없고, 또 발포성 경화 물질도 미발포 상태로 함유되어 있으므로, 감는 길이를 길게 할 수 있는 이점이 있어, 이러한 롤 형상 형태의 키친 페이퍼에 있어서 효과가 높다. 또, 절취선을 배치함으로써, 편리성이 높아진다.The kitchen paper in which the crepe paper is rolled is easy to manufacture. Further, in the roll-shaped kitchen paper, when the same roll diameter is used, the length (usable length) wound in proportion to the volume of the sheet becomes short. However, since embosses are not given to the crepe paper in the present invention, And the foaming curing material is also contained in an unfoamed state. Therefore, there is an advantage in that the winding length can be lengthened, and the effect is great in such a roll paper form kitchen paper. By arranging the perforated lines, convenience is improved.

이상과 같이 본 발명에 의하면, 통상적인 키친 페이퍼로서의 기능을 가지면서도, 특히 튀김의 과잉 유분을 흡수하는 용도에 있어서 특히 적합한 키친 페이퍼가 제공된다.INDUSTRIAL APPLICABILITY As described above, the present invention provides a kitchen paper particularly suitable for use in absorbing excess oil of frying while having a function as a normal kitchen paper.

도 1 은 본 발명의 키친 페이퍼 (X1) 를 설명하기 위한 사시도이다.
도 2 는 본 발명의 키친 페이퍼 (X1) 의 단면도이다.
도 3 은 본 발명의 키친 페이퍼 (X1) 의 다른 단면도이다.
도 4 는 본 발명의 키친 페이퍼 (X1) 의 롤 형태의 사시도이다.1 is a perspective view for explaining a kitchen paper X1 of the present invention.
2 is a sectional view of the kitchen paper X1 of the present invention.
3 is another sectional view of the kitchen paper X1 of the present invention.
4 is a perspective view of the roll of the kitchen paper X1 of the present invention.

발명을 실시하기 위한 형태DETAILED DESCRIPTION OF THE INVENTION

다음으로, 본 발명의 키친 페이퍼의 실시형태를 설명한다. 도 1∼4 에, 본 실시형태의 키친 페이퍼 (X1) 를 나타낸다.Next, an embodiment of the kitchen paper of the present invention will be described. Figs. 1 to 4 show a kitchen paper X1 of the present embodiment. Fig.

이 키친 페이퍼 (X1) 는, 도 1∼도 3 에 나타내는 바와 같이 2 장의 크레이프지 (1, 2) 가 선 형상으로 배치된 접착제 (3, 3) 를 개재하여 적층 일체화되어 있고, 그 선 형상으로 배치된 접착제에 의해 둘러싸인 구획을 복수 갖고, 그 접착제 중에는 열에 의해 발포하여 팽창되고, 팽창 후에 경화되는 발포성 경화 물질이 미발포 상태로 함유되어 있다.As shown in Figs. 1 to 3, the kitchen paper X1 is formed by laminating and integrating two sheets of crepe paper 1, 2 via linearly arranged adhesives 3, 3, And a plurality of compartments surrounded by the disposed adhesive, wherein the adhesive contains an expandable cured material which is expanded by foaming by heat and cured after expansion, in an unfoamed state.

본 발명에 있어서의 접착제 (3, 3) 의 부여 양태는, 상기 서술한 바와 같이 접착제 (3, 3 ) 를 선 형상으로 배치하고 있다. 이로써, 발포성 경화 물질의 발포에 의한 크레이프지 사이의 공극 형성을 가능하게 하면서, 또한 그 형성된 공극이 구획되게 되어 흡액량을 충분한 것으로 할 수 있음과 함께, 하나의 구획에 흡액된 기름 등이 다른 구획으로 이행되지 않는다. 여기서, 구획은, 도 1 에 나타내는 격자 형상과 같이 반드시 규칙성을 가지고 배치되어 있을 필요는 없고, 랜덤하게 배치되어 있어도 된다. 구획의 형상은, 육각형이나 삼각형 등 도시된 격자에 한정되지 않는다.In the embodiment of the present invention, the adhesives 3 and 3 are arranged linearly as described above. This makes it possible to form voids between the crepe paper due to foaming of the foamable curing material and to partition the formed voids so that the amount of absorbed liquid can be made sufficient and the oil or the like absorbed in one compartment, . Here, the division does not necessarily have to be arranged regularly like the lattice shape shown in Fig. 1, but may be arranged at random. The shape of the section is not limited to a lattice shown by hexagons, triangles, or the like.

여기서, 접착제 (3) 의 선폭 L1 은 0.25∼2.00 ㎜ 인 것이 바람직하다. 이 경우에 있어서, 선 형상으로 배치된 접착제 (3, 3) 에 의해 둘러싸이는 1 구획 P 의 면적이 25∼100 ㎟ 인 것이 바람직하다. 선폭 L1 이 0.25 ㎜ 미만이면, 크레이프지 (1, 2) 끼리의 접착이 불충분해짐과 함께 발포성 경화 물질을 충분히 함유하지 못하여 발포성 경화 물질의 발포에 의한 효과가 불충분해짐과 함께, 튀김 등을 지지하기에 충분하지 않게 되어 공극 유지성이 악화된다. 또, 2.00 ㎜ 를 초과하면, 접착제에 의한 종이의 강성이 높아져 부드러움, 유연성이 저하됨과 함께, 접착제 부분이 지나치게 많아 흡액성이 열등하게 된다.Here, the line width L1 of the adhesive 3 is preferably 0.25 to 2.00 mm. In this case, it is preferable that the area of one compartment P surrounded by the linearly arranged adhesives 3, 3 is 25 to 100 mm < 2 >. If the line width L1 is less than 0.25 mm, adhesion between the crepe paper 1 and the crepe paper 1 becomes insufficient, and the foamed curing material is not sufficiently contained, so that the effect of foaming the foamed curing material becomes insufficient, And the air gap retention deteriorates. On the other hand, if it exceeds 2.00 mm, the rigidity of the paper caused by the adhesive increases, resulting in a decrease in softness and flexibility, and an excessively large amount of the adhesive portion leads to inferior liquid absorbency.

또한, 접착제의 부여 양태는, 키친 페이퍼 (X1) 의 일방 지면에 대한 접착제 부여 부분의 총 면적의 비율이 5∼30 % 인 것이 바람직하다. 5 % 미만이면, 크레이프지끼리의 접착이 불충분해지고, 30 % 를 초과하면 접착 부분이 지나치게 넓어, 키친 페이퍼가 뻣뻣해짐과 함께, 흡액성이 불충분해진다.It is preferable that the ratio of the total area of the adhesive application portion to one surface of the kitchen paper X1 is 5 to 30%. If it is less than 5%, the adhesion between the crepe paper becomes insufficient, and if it exceeds 30%, the adhesive portion becomes too wide, and the kitchen paper becomes stiff and the liquid absorbency becomes insufficient.

한편, 접착제 중에 함유되는 발포성 경화 물질은 90∼200 ℃ 에서 발포되는 것이 바람직하고, 본 발명에서는, 그 발포에 의해 종이 두께 L2 가 발포 전과 비교하여 100 ㎛ 이상 증가되는 것으로 하는 것이 바람직하다.On the other hand, it is preferable that the foamable curing substance contained in the adhesive is foamed at 90 to 200 DEG C, and in the present invention, it is preferable that the foamed foam increases the paper thickness L2 by 100 mu m or more as compared with that before foaming.

여기서, 본 발명의 키친 페이퍼 (X1) 는, 종이 두께 L2 가 700 ㎛ 이하, 바람직하게는 500 ㎛ 이하인 것이 바람직하다. 700 ㎛ 를 초과하면 종이 두께가 지나치게 두꺼워, 수송시에 있어서는 컴팩트하고 사용시에 있어서 발포성 경화 물질의 발포에 의해 종이 두께가 두꺼워진다는 본 발명의 효과를 얻기가 어려워진다.Here, in the kitchen paper X1 of the present invention, it is preferable that the paper thickness L2 is 700 mu m or less, preferably 500 mu m or less. When the thickness exceeds 700 mu m, the thickness of the paper is too thick, and it is difficult to obtain the effect of the present invention that the paper is compact when transported and the thickness of paper becomes thick due to foaming of the foamable curing material at the time of use.

상기 점을 정리하면, 본 발명의 키친 페이퍼 (X1) 에 있어서의 발포성 경화 물질과 종이 두께의 관계는, 발포 전에 있어서 700 ㎛ 이하, 바람직하게는 500 ㎛ 이하이고, 발포성 경화 물질의 발포에 의해, 종이 두께 L3 이 700 ㎛ 를 초과하게 되는 것이 특히 바람직한 형태이다.In summary, the relationship between the foamable curing substance and the paper thickness in the kitchen paper X1 of the present invention is 700 占 퐉 or less, preferably 500 占 퐉 or less, before foaming. By foaming of the foamable curing substance, It is a particularly preferable form that the paper thickness L3 exceeds 700 mu m.

종이 두께의 측정 방법으로는, JIS P 8111 의 조건하에서, 다이얼 시크니스 게이지 (두께 측정기) 예를 들어 「PEACOCK G 형」(오자키 제작소 제조) 을 이용하여 측정한다. 구체적으로는, 플런저와 측정대 사이에 티끌, 먼지 등이 없는 것을 확인하여 플런저를 측정대 위에 내려놓고, 상기 다이얼 시크니스 게이지의 메모리를 이동시켜 제로점을 맞추고, 이어서, 플런저를 올려 시료를 시험대 위에 두고, 플런저를 천천히 내려 그 때의 게이지를 판독한다. 여기서, 시료를 시험대 위에 놓기 전에, 75 g (저면 평탄하고 또한 저면적 30 ㎠) 의 추를 60 초간 얹어 가중시켜 두기로 한다. 이 때, 플런저를 놓는 것만으로 한다. 또한, 두께는 측정을 10 회 실시하여 얻어지는 평균값으로 한다.As a method for measuring the paper thickness, a measurement is made using a dialingness gauge (thickness measuring instrument), for example, "PEACOCK G type" (manufactured by Ozaki Manufacturing Co., Ltd.) under the conditions of JIS P 8111. Specifically, it is confirmed that there is no dust or dirt between the plunger and the measurement table, the plunger is placed on the measurement table, the memory of the dial seeking gauge is moved to set the zero point, then the plunger is raised, And the plunger is slowly lowered to read the gauge at that time. Before putting the sample on the test stand, weigh 75 g (flat bottom surface and 30 cm2 of low surface area) for 60 seconds before placing the sample on the test stand. At this time, it is only necessary to dispose the plunger. The thickness is an average value obtained by performing measurement ten times.

여기서, 발포성 경화 물질이 90∼200 ℃ 에서 발포되는 것에 대해서는, 키친 페이퍼로 한 상태에서 접착제 부분의 외부 환경이 90∼200 ℃ 에 도달했을 때, 보다 구체적으로는, 지면의 접착제 부분에 90∼200 ℃ 의 물체가 접촉되었을 때, 혹은, 키친 페이퍼 자체가 90∼120 ℃ 의 환경하에 놓여졌을 때 발포성 경화 물질이 발포되는 것을 의미한다. 단, 이것은 발포성 경화 물질 자체의 발포 온도에 의존하므로 발포성 경화 물질이 90∼200 ℃ 에서 발포되는 것이면 충분히 달성된다.When the foamed cured material is foamed at 90 to 200 DEG C, when the external environment of the adhesive portion reaches 90 to 200 DEG C in the state of the kitchen paper, more specifically, 90 to 200 Or when the kitchen paper itself is placed under an environment of 90 to 120 DEG C, it means that the foamable hardening material is foamed. However, since this depends on the foaming temperature of the foamable curing substance itself, it is sufficiently achieved that the foamable curing substance is foamed at 90 to 200 占 폚.

또한, 본 발명의 키친 페이퍼 (X1) 의 보다 바람직한 발포성 경화 물질의 발포에 의한 종이 두께의 증가는, 적어도 2.5 g/㎠ 의 가중하에서 종이 두께가 100 ㎛ 증가하는 것이다. 정리하면, 본 발명에 있어서의 키친 페이퍼의 가장 바람직한 예는, 종이 두께가 700 ㎛ 이하, 바람직하게는 500 ㎛ 이하이고, 2.5 g/㎠ 의 가중하에서 90∼200 ℃ 에서 발포성 경화 물질이 발포되어, 그 종이 두께가 700 ㎛ 를 초과하게 되는 것이다.Further, an increase in the paper thickness due to the foaming of the foamable hardening material of the kitchen paper (X1) of the present invention is such that the paper thickness is increased by 100 占 퐉 under a weight of at least 2.5 g / cm2. In summary, the most preferred example of the kitchen paper in the present invention is a paper sheet having a paper thickness of 700 μm or less, preferably 500 μm or less, foamed at 90 to 200 ° C. under a weight of 2.5 g / The paper thickness exceeds 700 mu m.

여기서, 2.5 g/㎠ 의 가중하에 있어서의 종이 두께의 증가는, 구체적으로는, 튀김을 놓았을 때를 상정하여, 도 3 에 나타내는 바와 같이 키친 페이퍼를 수평대 G 위에 놓고, 그 위에 90∼200 ℃ 의 75 g (저면 평탄하고 또한 저면적 30 ㎠) 의 추 (10) 를 놓고, 60 초 후에 추를 떼어냈을 때의 종이 두께의 증가, 또는 75 g (저면 평탄하고 또한 저면적 30 ㎠) 의 추를 놓고, 그대로 항온조에서 90∼200 ℃ 의 환경하에서 60 초 방치하고, 그 후에 항온조로부터 꺼내어, 추를 떼어내고 측정했을 때의 종이 두께의 증가 중 어느 것을 만족하면 된다고 정의할 수 있다.The increase in paper thickness under the weighting of 2.5 g / cm < 2 >, specifically, assuming that the fried paper is laid, is determined by placing the kitchen paper on the horizontal belt G as shown in Fig. 3, Of 75 g (bottom flatness and low area of 30 cm 2) of 75 g (when the weight is removed after 60 seconds), or 75 g It can be defined that the weight is left to stand for 60 seconds in an environment of 90 to 200 deg. C in a thermostatic bath and then removed from the thermostatic chamber to satisfy any of the increase in paper thickness when the weight is removed and measured.

<크레이프지><Crepe paper>

본 발명의 크레이프지 (1, 2) 는, 이미 알려진 키친 페이퍼와 마찬가지로 원료 펄프를 주성분으로 하는 초지 원료를, 와이어 파트, 프레스 파트, 드라이어 파트, 크레이프 가공 파트 등을 거치는 공지된 크레이프지의 초지 기술에 의해 제조할 수 있다. 단, 본 발명의 크레이프지 (1, 2) 는, 엠보스가 부여되어 있지 않은 것으로 한다. 엠보스가 부여되어 있지 않아도 본 발명의 효과를 충분히 발휘할 수 있기 때문에, 엠보스의 부여는 본 발명에서는 제조상의 번잡함의 증가, 비용 상승의 요인이 되고, 또 크레이프지 (1, 2) 에 엠보스가 부여되어 있으면 종이 두께가 두꺼워지기 때문에 수송성도 저하된다.The crepe paper (1, 2) of the present invention can be produced by using a known paper material, such as a known paper paper, as a paper material, . &Lt; / RTI > It should be noted that the crepe paper 1, 2 of the present invention is not embossed. The effect of the present invention can be sufficiently exerted even if the emboss is not imparted. Therefore, embossing is added in the present invention to increase the manufacturing complexity and increase the cost, and the embossing is given to the crepe paper 1, 2 The thickness of the paper becomes thick, so that the transportability is lowered.

또한, 본 발명의 크레이프지 (1, 2) 는 드라이 크레이프지이어도 되고, 웨트 크레이프지이어도 되는데, 바람직하게 드라이 크레이프법에 의한 크레이프지이다.Further, the crepe paper 1, 2 of the present invention may be a dry crepe paper or a wet crepe paper, preferably a crepe paper by a dry crepe method.

크레이프지 (1, 2) 는, 바람직하게는 섬유 원료가 100 % 펄프 원료이고, 그 원료 펄프종으로는, 이미 알려진 크레이프지 제조에 사용되는 펄프종이 사용된다. 또, 원료 펄프가 표백인지, 미표백인지는 상관 없다. 단, 블리치드 펄프로 불리는 표백 펄프가 바람직하다. 펄프 원료 중에서도, LBKP (활엽수 크래프트 펄프), NBKP (침엽수 크래프트 펄프) 를 적당한 비율로 배합한 것이 바람직하다. LBKP 와 NBKP 를 사용하는 경우에는, 그 배합 비율로는, LBKP : NBKP 가 0 : 100∼50 : 50 인 것이 바람직하다.The crepe paper (1, 2) is preferably a 100% pulp raw material for the fiber raw material, and pulp paper used for producing a known crepe paper is used as the raw pulp type. Whether the raw pulp is bleached or unbleached is not relevant. However, bleached pulp called bleached pulp is preferable. Among pulp raw materials, it is preferable that LBKP (hardwood kraft pulp) and NBKP (softwood kraft pulp) are blended in an appropriate ratio. When LBKP and NBKP are used, it is preferable that LBKP: NBKP is 0: 100 to 50: 50 as the blending ratio.

또, 본 발명의 크레이프지 (1, 2) 는, 평량이 10∼42 g/㎡ 이고, 밀도는 2.5 × 10⁴∼4.2 × 10⁵ g/㎥ 인 것이 바람직하다. 두께는, 100∼350 ㎛ 의 범위에 있는 것이 바람직하다. 또한, 본 발명 및 명세서 중에 있어서의 평량 및 단위 면적당 중량이란, JIS P 8113 에 기초하여 측정한 값을 말한다. 또, 밀도는, 평량을 두께로 나눈 수치이다. 크레이프지의 종이 두께의 측정 방법도, 상기 서술한 키친 페이퍼의 측정 방법과 동일하고, JIS P 8111 의 조건하에서, 다이얼 시크니스 게이지 (두께 측정기), 예를 들어 「PEACOCK G 형」(오자키 제작소 제조) 을 이용하여 측정한다.The crepe paper 1, 2 of the present invention preferably has a basis weight of 10 to 42 g / m 2 and a density of 2.5 × 10 ^{4 to} 4.2 × 10 ⁵ g / m 3. The thickness is preferably in the range of 100 to 350 mu m. In the present invention, the basis weight and the weight per unit area in the specification are values measured based on JIS P 8113. The density is a value obtained by dividing the basis weight by the thickness. The method for measuring the paper thickness of crepe paper is the same as that for the measurement of the kitchen paper described above. Under the conditions of JIS P 8111, a dialingness gauge (thickness measuring instrument) such as "PEACOCK G type" .

평량이 10 g/㎡ 미만이면, 키친 페이퍼로서의 최저한의 지력 (紙力) 이나 흡수량을 유지하는 것이 곤란해지고, 42 g/㎡ 를 초과하면 뻣뻣해져 사용감이 저하되게 된다. 또, 밀도가 2.5 × 10⁴ g/㎥ 미만이면, 물, 기름의 흡수 속도 및 흡수량이 충분하지 않게 되고, 4.2 × 10⁵ g/㎥ 를 초과하면 뻣뻣해지고, 닦는 기능의 악화, 트레이, 접시, 배트 등에 깔 때의 취급성도 악화된다.If the basis weight is less than 10 g / m 2, it is difficult to maintain the minimum paper force or water absorption amount as the kitchen paper, and if it exceeds 42 g / m 2, the paper becomes stiff and the feeling of use is lowered. If the density is less than 2.5 × 10 ⁴ g / m ³ , the absorption rate and the absorption amount of water and oil become insufficient. If the density exceeds 4.2 × 10 ⁵ g / m 3, the stiffness becomes worsened, The handling of the bat and the like is also deteriorated.

또한, 본 발명의 키친 페이퍼 (X1) 에서는, 크레이프지 (1, 2) 의 크레이프율이 13∼35 % 인 것이 좋다. 또한, 본 발명에 있어서의 크레이프율이란, (((제지시의 드라이어의 주속) - (릴 주속))/(제지시의 드라이어의 주속) × 100) 에 의해 산출할 수 있다.In the kitchen paper X1 of the present invention, the crepe ratio of the crepe paper 1, 2 is preferably 13 to 35%. The crepe ratio in the present invention can be calculated by (((the peripheral speed of the dryer at the time of papermaking) - (the peripheral speed of the reel) / (the peripheral speed of the dryer at the time of papermaking) × 100).

또한, 본 발명에 있어서는 2 장의 크레이프지는 동일한 구성일 필요는 없다. 본 발명의 범위에서 적당히 상이한 구성이어도 된다.Further, in the present invention, the two crepe fabrics do not need to have the same configuration. But may be appropriately different in the scope of the present invention.

<접착제><Adhesive>

크레이프지 (1, 2) 를 접착하는 접착제 (3) 는 발포성 경화 물질을 미발포 상태로 함유한다. 발포성 경화 물질 이외의 접착제의 주체는, 이미 알려진 접착 기재를 사용할 수 있고, 구체예로는, 아크릴계 수지, 아세트산비닐계 수지, 아세트산비닐-에틸렌 공중합 수지, 우레탄계 수지, 염화비닐계 수지 등을 들 수 있다.The adhesive 3 for bonding the crepe paper 1, 2 contains the foamable curing material in an unfoamed state. Examples of the adhesive agent other than the foamable curing agent may include an acrylic resin, a vinyl acetate resin, a vinyl acetate-ethylene copolymer resin, a urethane resin, a vinyl chloride resin, etc. have.

크레이프지에 대한 접착제의 부여는, 이미 알려진 패턴 인쇄 기술, 패턴 도포 기술을 이용할 수 있고, 구체적으로는, 그라비아 인쇄, 플렉소 인쇄 등에 의해 부여할 수 있다.The application of the adhesive to the crepe paper can be carried out by a known pattern printing technique or pattern application technique, and specifically, gravure printing, flexographic printing or the like.

<발포성 경화 물질>&Lt; Foamable hardening substance &

발포성 경화 물질은, 이미 알려진 발포 잉크 등에 사용되고 있는 것을 이용할 수 있다. 또한, 미리 조제된 발포 잉크 그 자체를 접착 기재에 혼합하여 함유시켜도 되고, 접착 기재를 사용하지 않고, 발포 잉크 중의 바인더 성분을 접착 기재로서 기능시키고, 발포 잉크 그 자체를 발포성 경화 물질을 함유하는 접착제로서 사용해도 된다.As the foamable curing substance, those which have been already known, such as foaming ink, etc., can be used. In addition, the previously prepared foamed ink itself may be mixed with the adhesive base material, or the binder component in the foamed ink may function as an adhesive base material without using an adhesive base material, and the foamed ink itself may be mixed with an adhesive containing a foamable curing material .

발포성 경화 물질은, 구체적으로는, 열에 의해 팽창되는 특성을 갖는 심 (芯) 물질을 열가소성 고분자 재료의 피막 혹은 외피에 내포시킨 마이크로 캡슐을 예시할 수 있다. 마이크로 캡슐의 입자경 등은, 마이크로 캡슐의 발포성, 사용하는 인쇄기 등에 따라 적절히 선택할 수 있고, 특별히 한정되지 않지만, 대체로 10∼50 ㎛ 의 입경이다.Specifically, the foamable curing substance may be exemplified by a microcapsule in which a core material having a property of being swollen by heat is contained in a film or shell of a thermoplastic polymer material. The particle size and the like of the microcapsule can be appropriately selected depending on the foamability of the microcapsule, the printing machine to be used, and the like, and is not particularly limited, but is generally about 10 to 50 mu m in particle diameter.

이 종류의 발포성 경화 물질은, 적당한 온도가 되면 심물질이 팽창됨과 함께 피막 또는 외피가 확장됨으로써 팽창 상태가 유지된다. 또한, 본 발명에서는, 이 팽창 상태, 즉 경화 상태가 적어도 1 시간 정도 유지되면 된다. 바람직하게는 경화된 상태가 영구적으로 유지되는 것이다. 또한, 본 발명에 있어서의 경화란 탄성, 강성, 강탄성 상태를 포함하는 의미이다.In this type of expandable curing material, when the temperature becomes appropriate, the core material is expanded and the film or the envelope is expanded, thereby maintaining the expanded state. In the present invention, the expanded state, that is, the cured state, may be maintained for at least one hour. Preferably, the cured state is maintained permanently. The curing in the present invention includes the elasticity, rigidity, and rigid elasticity.

여기서, 본 발명의 발포성 경화 물질은, 90∼120 ℃ 에서 발포되는 것이 바람직하다. 이것은, 상기 서술한 바와 같이, 튀김을 튀길 때의 일반적인 기름의 온도는 180 ℃ 전후이며, 이 온도의 기름으로부터 튀김을 꺼낸 경우, 튀김의 온도가 100∼120 ℃ 정도로 저하되기 때문에, 튀김의 과잉 유분의 흡수 용도에 있어서 특히 적합하기 때문이다.Here, the foamable curing material of the present invention is preferably foamed at 90 to 120 캜. This is because, as described above, when the frying temperature is about 180 deg. C at the time of frying the frying pan, and the frying temperature is lowered to about 100 to 120 deg. C when the frying pan is taken out from the oil at this temperature, Especially for absorption applications of the < / RTI >

또한, 마이크로 캡슐의 피막 혹은 외피를 형성하는 열가소성 고분자 재료의 구체예로는, 메타크릴산메틸, 아크릴로니트릴 등의 아크릴계 수지, 염화비닐리덴, 폴리아미드, 폴리부타디엔, 우레탄계 수지, 스티렌계 수지 등에서 선택되는 열가소성 고분자 재료, 혹은 이들을 혼합한 열가소성 고분자 재료 등을 들 수 있고, 또 열에 의해 팽창 경화되는 특성을 갖는 심물질의 구체예로는, 부탄이나 이소부탄 등의 탄화수소계 화합물, 그 밖의 유기 용제나 중탄산나트륨, 탄산나트륨, 탄산암모늄, 아지드 화합물, 히드라지드 화합물 등의 탄산 가스, 질소 가스 등의 분해 가스를 발생시키는 유기 물질, 무기 물질을 들 수 있다.Specific examples of the thermoplastic polymer material forming the film or shell of the microcapsules include acrylic resins such as methyl methacrylate and acrylonitrile, vinylidene chloride, polyamide, polybutadiene, urethane resin, styrene resin and the like Specific examples of the core material having the property of expanding and curing by heat include hydrocarbon-based compounds such as butane and isobutane, and other organic solvents Organic substances and inorganic substances which generate decomposition gases such as carbonic acid gas and nitrogen gas, such as sodium bicarbonate, sodium carbonate, ammonium carbonate, azide compounds and hydrazide compounds.

보다 구체적인 발포성 경화 물질을 예시하면, Expancel 사 제조의 Expancel 시리즈, 마츠모토 유지 제약 주식회사 제조의 마이크로스페어 등을 예시할 수 있다.More specific examples of the foamable curing material include Expancel series manufactured by Expancel, microsphere manufactured by Matsumoto Yushi Pharmaceutical Co., Ltd., and the like.

또한, 발포성 경화 물질의 배합 비율은, 발포성 경화 물질의 발포성, 접착 기재의 접착성을 고려하여 적절히 조정할 수 있다. 대체로 접착제 기재 20∼60 중량부에 대해 3∼20 중량부이다.The compounding ratio of the foamable curing substance can be appropriately adjusted in consideration of the foaming property of the foamable curing substance and the adhesiveness of the adhesive base. It is generally 3 to 20 parts by weight per 20 to 60 parts by weight of the adhesive base material.

<친유성 기제><Lipophilic base>

한편, 키친 페이퍼 (X1) 는, 흡유 속도의 향상을 위해, 크레이프지 (1, 2) 에 친유성 기제가 담지되어 있는 것이 바람직하다. 2 장의 각 크레이프지 (1, 2) 중 어느 쪽에 담지시키는지, 또 어느 면에 친유성 기제가 담지되는지는 한정되지 않는다. 2 장의 쌍방에 담지시켜도 되고, 1 장에만 담지시켜도 된다. 또, 각 크레이프지 (1, 2) 의 일방면에만 담지시켜도 되고, 쌍방의 면에 담지시켜도 된다. 단, 바람직하게는, 2 장의 크레이프지 (1, 2) 의 대향면에 도포 등에 의해 부분적으로 혹은 전면적으로 담지시키는 것이 좋다. 기름이 크레이프지로 이행되기 쉽고, 또 일단 흡수된 유분이 유지되기 쉬워짐과 함께, 공극 내에 기름이 유지되기 쉬워진다.On the other hand, in the kitchen paper X1, it is desirable that the lipophilic base material is carried on the crepe paper 1 or 2 in order to improve the oil-absorbing speed. It is not limited to which of the two crepe sheets 1 and 2 the two sheets are supported, and on which side the lipophilic base material is carried. They may be carried on both of two sheets, or may be carried on only one sheet. It may be carried on only one side of each crepe paper 1 or 2, or on both sides. Preferably, however, it is preferable to partially or entirely support the two sheets of crepe paper 1 and 2 on opposite sides thereof by coating or the like. The oil is easily transferred to the crepe paper, the once absorbed oil is easily retained, and the oil is easily retained in the gap.

친유성 기제의 구체예로는, 탄화수소, 유동 파라핀, 트리글리세리드, 지방산 아마이드, 아크릴산에스테르 공중합체, 자당 에스테르, 이소스테아르산에스테르를 들 수 있다. 그 중에서도 유동 파라핀, 트리글리세리드가 적합하다. 유동 파라핀은, 산화 안정성 면에서 우수하여, 특히 바람직하게 사용된다. 또, 트리글리세리드 중에서도 탄소수 6∼12 의 포화 지방산으로 이루어지는 것, 특히는 중사슬 지방산이 특히 바람직하다. 포화인 것에 의해 산화 안정성이 우수하고, 탄소수를 6∼12 로 함으로써 적당한 분자량으로 시트지에 대한 침투성이 양호해진다. 또, 단순한 직사슬 지방산보다 트리글리세리드 형태가 기름의 확산·침투성을 높이는 효과가 우수하다.Specific examples of the lipophilic base include hydrocarbons, liquid paraffin, triglycerides, fatty acid amides, acrylic acid ester copolymers, sucrose esters and isostearic acid esters. Among them, liquid paraffin and triglyceride are suitable. Liquid paraffin is excellent in oxidation stability and is particularly preferably used. Among the triglycerides, saturated fatty acids having 6 to 12 carbon atoms, particularly fatty acids with a heavy chain length are particularly preferred. Saturation is excellent in oxidation stability. When the number of carbon atoms is 6 to 12, permeability to a sheet becomes good with an appropriate molecular weight. Further, the triglyceride form is more effective than the simple linear fatty acid in enhancing the diffusion and penetration of oil.

친유성 기제의 함유량은, 크레이프지 (1, 2) 장당 그 중량의 1∼20 중량% 가 바람직하다. 1 중량% 미만에서는 충분한 효과가 발현되지 않는 경우가 있고, 20 중량% 를 초과하면 친화성이 양호해지고, 크레이프지 (1, 2) 의 표리면에서 기름이 머물러, 2 장의 크레이프지 사이의 공극으로의 기름의 이동이 늦어지는 경우가 있다.The content of the lipophilic base agent is preferably 1 to 20% by weight of the weight per one crepe paper (1, 2). If it is less than 1% by weight, a sufficient effect may not be exhibited. If it is more than 20% by weight, the affinity is improved and the oil remains on the front and back surfaces of the crepe paper 1 and 2, There is a case where the movement of oil of the oil is delayed.

친유성 기제를 크레이프지 (1, 2) 에 담지시키는 방법은, 내첨, 외첨 중 어느 방법에 의해도 된다. 예를 들어, 내첨하는 것이면, 원료 펄프, 또는 원료 펄프 슬러리에 친유성 기제를 첨가한 것을 초지하는 방법을 채택할 수 있고, 외첨하는 것이면, 크레이프지 원지의 형성 후, 친유성 기제를 산포, 도포, 도공하는 방법을 채택할 수 있다. 산포하는 경우에는, 크레이프지 원지에 대해 약제를 산포하는 이미 알려진 스프레이 장치를 사용할 수 있고, 도공하는 것이면, 이미 알려진 도공기 또는 인쇄기를 사용할 수 있다.The method of supporting the lipophilic base material on the crepe paper (1, 2) can be carried out by any method of internal addition and external addition. For example, in the case of using a raw material pulp or a raw pulp slurry, a method in which a lipophilic base agent is added to the raw pulp slurry can be adopted, and if the raw material pulp is extruded, a lipophilic base can be dispersed and applied , A coating method can be adopted. In the case of spreading, a known spraying device for dispensing a medicament against a crepe paper can be used, and if it is a coating, a known coating machine or a printing machine can be used.

<롤 형태><Roll form>

이어서, 롤 형태의 본 발명의 키친 페이퍼에 대해 도 4 를 참조하면서 설명한다 (또한, 도 4 중에서 접착제 부여 부분은 생략한다).Next, the kitchen paper of the present invention in the form of a roll will be described with reference to Fig. 4 (further, the adhesive imparting portion is omitted in Fig. 4).

본 발명의 키친 페이퍼는, 띠 형상의 2 장의 크레이프지 (1, 2) 를 상기 접착제에 의해 적층 일체화하고, 이것을 크레이프지 (1, 2) 의 짧은 길이 방향의 종이 폭과 실질적으로 동일 폭의 관심 (管芯) (5) 에 감는 등 롤 형태인 것이 바람직하다 (이하, 띠 형상의 2 장의 크레이프지 (1, 2) 를 접착제에 의해 적층 일체화한 상태의 키친 페이퍼는 간단히 시트 (12) 라고 한다).In the kitchen paper of the present invention, two belt-shaped crepe paper sheets 1 and 2 are laminated and integrated by the adhesive agent, and this is fed to the paper sheets of the crepe paper sheets 1 and 2 of interest (Hereinafter, the two sheets of crepe paper 1 and 2 in the form of strips are laminated and integrated by an adhesive), the kitchen paper is simply referred to as sheet 12 ).

관심 (5) 은, 이 종류의 키친 페이퍼에 사용되고 있는 이미 알려진 것을 이용할 수 있다. 일반예를 나타내면, 그 외경 (감는 직경) L4 는 30∼50 ㎜, 폭 H 는 100∼250 ㎜ 정도이다.The attention (5) can use known already used in this kind of kitchen paper. As a general example, the outer diameter (winding diameter) L4 is about 30 to 50 mm, and the width H is about 100 to 250 mm.

시트 (12) 의 감는 길이는 8.8∼30 m 로 할 수 있고, 상기 관심 (5) 을 사용한 경우에는, 키친 페이퍼 (X2) 의 외경은 90∼130 ㎜ 가 된다. 이것은, 시판되는 키친 페이퍼보다 길다.The winding length of the sheet 12 may be 8.8 to 30 m, and when the above-mentioned interest (5) is used, the outside diameter of the kitchen paper X2 is 90 to 130 mm. This is longer than commercially available kitchen paper.

한편, 특히 도 4 에 나타내는 바와 같이, 본 형태의 시트 (12) 는, 시트 길이 방향의 소정 간격 L5 마다 시트 폭 방향에 걸친 절취선 (6) 을 형성하는 것이 바람직하다. 이 절취선 (6, 6…) 에 의해, 시트 (12) 가 절단되기 쉬워진다. 소정 간격 L5 는, 48∼250 ㎜ 정도로 하는 것이 좋다. 48 ㎜ 미만이면, 실제로 사용하기에 지나치게 작아지게 되고, 250 ㎜ 를 초과하면 식기 등과 비교하여 커지므로 사용감이 나빠진다.On the other hand, as shown in Fig. 4 in particular, it is preferable that the sheet 12 of this embodiment forms a perforated line 6 extending in the sheet width direction at predetermined intervals L5 in the sheet longitudinal direction. The sheet 12 is easily cut by the perforations 6, 6, .... The predetermined interval L5 is preferably set to about 48 to 250 mm. If it is less than 48 mm, it becomes too small for practical use, and if it exceeds 250 mm, it becomes larger than that of a tableware or the like, resulting in poor feeling of use.

상기 절취선 (6) 은, 이미 알려진 퍼포레이션 롤 (절취날 롤) 설비에 의해 형성할 수 있다. 즉, 관심 (5) 에 권취하는 전단 (前段) 에 있어서, 시트 (12) 의 폭보다 폭이 넓은 롤 상에, 다수의 날을 폭 방향을 따라 배치하여 날열을 형성하고, 이 날열을 소정 간격 L5 와 동일한 피치로 롤의 원주 방향으로 복수 형성한 퍼포레이션 롤을 회전시키면서, 주행하는 시트 (12) 에 맞닿게 함으로써, 시트 (12) 의 폭 방향에 걸친 절취선 (6) 을, 길이 방향의 소정 간격 L5 마다 형성할 수 있다.The perforated line 6 can be formed by a known perforation roll (cut-off blade) facility. That is, a plurality of blades are arranged along the width direction on a roll having a width wider than the width of the sheet 12 at the front stage where the blades are wound on the target 5, The perforated line 6 extending in the width direction of the sheet 12 is pressed against the sheet 12 to be driven while the perforation roll formed in the circumferential direction of the roll at the same pitch as L5 is rotated while rotating the perforation roll, Can be formed every interval L5.

또한, 본 형태의 키친 페이퍼 (X2) 는, 도시예와 같이 절취선 (6) 이 이중선 이상인 것이 바람직하다. 복수 겹의 절취선을 형성하는 데에 있어서는, 복수 겹의 적당한 날열의 퍼포레이션 롤을 구비하는 퍼포레이션 롤 설비에 의해 형성하면 된다. 또한, 이 경우의 절취선 (6) 은, 시트 폭 방향 전체에 걸쳐 이중으로 형성되어 있을 필요는 없고, 예를 들어 시트 (12) 의 폭 방향 측부만이 이중으로 형성되어 있어도 된다.In the kitchen paper X2 of this embodiment, it is preferable that the perforated line 6 is double or more lines as shown in the drawing. In forming a plurality of perforated lines, it may be formed by a perforation roll facility having perforation rolls of a suitable number of rows and a suitable number of blades. In this case, the perforated lines 6 need not be formed double over the entire width of the sheet. For example, only the widthwise side portions of the sheet 12 may be formed in a double manner.

또한, 절취선 (12) 을 이중으로 하는 경우에 있어서, 일본 공개특허공보 2003-276936호 등을 참고로, 예를 들어 컷 부분을 지그재그 형상으로 하거나, 혹은 일방의 절취선의 컷 부분의 단부 (端部) 와, 이 컷 부분의 단부에 가장 근접한 타방의 절취선의 컷 부분의 단부를 연결하는 직선에 대한, 절취선이 이루는 각을 직각 또는 예각으로 하거나 하여, 절단의 용이화 등을 도모할 수도 있다.When the perforated line 12 is doubled, for example, the cut portion may be formed in a staggered shape, or the end portion of the cut portion of one of the perforated lines And the angle formed by the perforated line with respect to a straight line connecting the end of the cut portion of the other perforated line closest to the end of the cut portion may be a right angle or an acute angle so as to facilitate cutting.

여기서, 본 형태의 키친 페이퍼 (X2) 는, 바람직하게는 절취선 (6) 에 있어서의 시트 길이 방향의 인장 강도가 100∼500 cN 인 것이 좋다. 절취선 (6) 에 있어서의 시트 길이 방향의 인장 강도가 100 cN 이상이면, 시트를 풀어낼 때의 절취선 (6) 에서의 원하지 않은 분단이 확실하게 방지된다. 한편, 절취선 (6) 에 있어서의 시트 길이 방향의 인장 강도가 500 cN 이하이면, 절단하고자 하는 원하는 절취선 (6) 에서 확실하고 또한 용이하게 시트 (12) 를 절단할 수 있다.Here, the kitchen paper X2 of this embodiment preferably has a tensile strength in the sheet longitudinal direction of the perforated line 6 of 100 to 500 cN. If the tensile strength of the perforated line 6 in the longitudinal direction of the sheet is 100 cN or more, undesired division at the perforated line 6 when the sheet is unwound is reliably prevented. On the other hand, if the tensile strength of the perforated line 6 in the longitudinal direction of the sheet is 500 cN or less, the sheet 12 can be reliably and easily cut at the desired perforation line 6 to be cut.

여기서 「인장 강도」란, JIS P 8113 에 규정되는 인장 특성 시험 방법에 준거하여 측정되는 건조시 인장 강도를 의미한다. 시트 (12) 자체, 요컨대 절취선 (6) 이 없는 시트 (12) 의 인장 강도가 아니고, 절취선 (6) 이 있는 시트 (12) 를 대상으로 하고, 절취선 (6) 을 걸쳐 측정한 인장 강도를 의미한다.Here, the "tensile strength" means the tensile strength at the time of drying measured in accordance with the tensile property test method specified in JIS P 8113. Refers to the tensile strength measured over the perforated line 6 with the sheet 12 having the perforated line 6 as an object and not the tensile strength of the sheet 12 itself, that is, the sheet 12 without the perforated line 6. [ do.

이 절취선 (6) 에 있어서의 길이 방향의 인장 강도의 조절은, 절취선 (6) 에 있어서의 접속부인 타이 길이와, 동일 분단부인 컷 길이를 조절함으로써, 혹은 이 타이 길이와 컷 길이의 비인 타이 컷비를 조절함으로써 실시할 수 있다. 보다 구체적으로는, 원하는 타이 컷 길이 및 타이 컷비의 날열을 구비하는 퍼포레이션 롤로 교환함으로써 조절할 수 있다. 또, 이 인장 강도의 조절은, 퍼포레이션 롤의 시트 (12) 에 대한 가압 선압 (시트 단위 폭당 시트 (12) 에 대한 가압력 (kgf/㎝)) 의 조절이나, 와인더 속도 (시트 (12) 의 권취 속도) 의 조절에 의해서도 조절할 수 있다.The adjustment of the tensile strength in the longitudinal direction of the perforated line 6 can be performed by adjusting the length of the tie, which is the connecting portion in the perforated line 6, and the cut length, which is the same partial length, . &Lt; / RTI > More specifically, it can be adjusted by exchanging with a perforation roll having a desired cut length and a blade cut-off ratio. The adjustment of the tensile strength can be performed by adjusting the pressure applied to the sheet 12 of the perforation roll 12 (pressing force (kgf / cm) against the sheet 12 per sheet width) The winding speed of the recording medium).

한편, 본 형태의 키친 페이퍼 (X2) 는, 시트 (12) 자체의 시트 길이 방향의 인장 강도에 대한, 절취선 (6) 에 있어서의 시트 길이 방향의 인장 강도의 비율이 1.0∼50 % (바람직하게는 2.0∼10 %) 이면 바람직하다. 인장 강도의 비율이 50 % 이하이면, 절취선 (6) 이 없는 시트 부분의 인장 강도가 상대적으로 높아지므로, 시트 (12) 의 절단시에, 절취선 (6) 이외의 시트 부분에서 시트 (12) 가 분단되는 것이 억제되어, 절취선 (6) 에서 확실하게 절단할 수 있다. 한편, 인장 강도의 비율이 1.0 % 이상이면, 상대적으로 절취선 (6) 의 인장 강도가 높아지므로, 절취선 (6) 의 간격을 짧게 함으로써, 절취선 (6) 이 증가되었다고 해도, 시트를 풀어낼 때의 절취선 (6) 에서의 원하지 않은 분단을 확실하게 방지할 수 있다.On the other hand, in the kitchen paper X2 of the present embodiment, the ratio of the tensile strength in the sheet longitudinal direction of the perforated line 6 to the tensile strength in the sheet longitudinal direction of the sheet 12 itself is 1.0 to 50% Is 2.0 to 10%). When the ratio of the tensile strength is 50% or less, the tensile strength of the sheet portion without the perforated line 6 becomes relatively high. Therefore, at the time of cutting the sheet 12, So that it is possible to reliably cut off the perforated line 6. On the other hand, when the ratio of the tensile strength is 1.0% or more, the tensile strength of the perforated line 6 is relatively increased. Therefore, even if the perforated line 6 is increased by shortening the interval of the perforated line 6, Undesired division in the perforated line 6 can be surely prevented.

여기서 시트 (12) 자체의 길이 방향의 인장 강도도, 전술한 JIS P 8113 에 규정되는 인장 특성 시험 방법에 준거하여 측정되는 것이다. 물론 절취선 (6) 이 없는 시트 부분의 건조시 인장 강도이다.The tensile strength in the longitudinal direction of the sheet 12 itself is also measured in accordance with the tensile property test method specified in JIS P 8113 mentioned above. Of course, it is the tensile strength at the time of drying the sheet portion without the perforated line 6. [

또한, 절취선 (6) 에 있어서의 시트 길이 방향의 인장 강도를 10∼200 cN 으로 설정하고, 인장 강도의 비율을 1.0∼50 % 로 설정하기 위해서는, 절취선 (6) 의 타이 길이를 0.9∼2.5 ㎜ 로, 컷 길이를 0.9∼37.5 ㎜ 로 함과 함께, 타이 컷비 (타이 : 컷) 를 1 : 15∼1 : 1 로 설정하면 된다.In order to set the tensile strength of the perforated line 6 in the sheet longitudinal direction to 10 to 200 cN and to set the ratio of the tensile strength to 1.0 to 50%, the tie length of the perforated line 6 is set to 0.9 to 2.5 mm , The cut length may be 0.9 to 37.5 mm and the tie cut ratio (tie: cut) may be set at 1: 15 to 1: 1.

<시험예><Test Example>

이어서, 본 발명의 키친 페이퍼에 관련된 특히 바람직한 형태에 관한 시험예를 이하에 나타낸다.Next, test examples relating to a particularly preferable form relating to the kitchen paper of the present invention are shown below.

먼저, 하기 표 1 에 롤 형태의 키친 페이퍼에 있어서의 종이 두께와 감는 직경, 감는 길이의 관계를 나타낸다. 또한, 일반적으로 시판되고 있는 엠보스를 부여한 키친 페이퍼 2 장에서의 종이 두께는 약 700 ㎛ 이다. 이 시험에서 사용한 시료의 평량은 28 g/㎡ 인 것을 사용하였다. 또, 친유성 기제를 도포한 경우, 기름의 확산 속도가 빨라지지만, 감는 길이나 종이 두께, 절대 흡유량에는 영향을 주지 않기 때문에, 본 시험예에서는 친유성 기제의 도포는 실시하지 않았다.First, Table 1 shows the relationship between the paper thickness, the winding diameter, and the winding length in a rolled kitchen paper. In addition, the thickness of the paper on two kitchen papers which are generally embossed on the market is about 700 mu m. The basis weight of the sample used in this test was 28 g / m 2. Further, when the lipophilic base material is applied, the diffusion rate of the oil is increased, but the application of the lipophilic base material is not carried out in this test example because it does not affect the winding length, paper thickness and absolute oil absorption.

다음으로 본 발명의 키친 페이퍼에 있어서의 접착 면적률과 흡유량의 관계를 하기 표 2 에 나타낸다. 또한, 이 시험에서 사용한 시료 (키친 페이퍼 ; 크레이프지 2 장 접착) 의 종이 두께는 초기가 440 ㎛ 이고, 발포성 경화 물질의 발포에 의해 300 ㎛ 종이 두께가 증가하도록 조정한 것을 사용하였다. 또, 크레이프지는, 표 2 중에도 나타내는 바와 같이, 21 g/㎡, 28 g/㎡ 인 것을 사용하였다.Next, the relationship between the adhesive area ratio and the oil absorption amount in the kitchen paper of the present invention is shown in Table 2 below. The paper thickness of the sample (kitchen paper; two sheets of crepe paper) used in this test was 440 占 퐉 in the initial stage and adjusted to increase the paper thickness by 300 占 퐉 by foaming of the foamable curing material. As shown in Table 2, the crepe paper had a basis weight of 21 g / m 2 and 28 g / m 2.

흡유량은, 사방 100 ㎜ 로 재단한 건조 시료의 중량을 측정한 후, 당해 시료를 샐러드유 (닛신 오일리오 그룹 주식회사 제조) 중에 15 초간 침지시키고, 그 후에 끌어 올려 25 초 후의 중량을 측정하고, 그 측정값으로부터 상기 건조 시료의 중량을 공제한 값으로 하였다.The oil absorption amount was determined by measuring the weight of a dry sample cut into 100 mm square, immersing the sample in salad oil (manufactured by Nissin Oil Group Co., Ltd.) for 15 seconds and then raising it to measure the weight after 25 seconds, And the value obtained by subtracting the weight of the dry sample from the measured value.

또한, 2 장의 각 크레이프지에 엠보스가 부여된 종이 두께가 720 ㎛ 인 시판품 (종래 제품) 에 있어서의 흡유량은 대체로 680 g/㎡ 이다.In addition, the oil absorption amount in a commercial product (conventional product) having a paper thickness of 720 mu m embossed on each of the two crepe paper is generally 680 g / m < 2 >.

표 2 로부터, 본 발명의 키친 페이퍼에서는, 발포 전에 있어서는 접착 면적률의 차이에 따른 흡유량의 차이는 볼 수 없지만, 발포 후에 있어서는, 접착 면적률이 3∼35 %, 특히 5∼25 % 에 있어서 현저하게 흡유량에 대해 양호해지는 경향이 있다. 따라서, 본 발명에 있어서의 바람직한 접착 면적률은 3∼35 %, 특히 바람직한 접착 면적률은 5∼25 % 라고 할 수 있다.From Table 2, it can be seen from Table 2 that in the kitchen paper of the present invention, there is no difference in the amount of oil absorption due to the difference in the bonding area ratio before foaming, but after foaming, the bonding area ratio is remarkably in the range of 3 to 35% So that it tends to be improved with respect to the oil absorption amount. Therefore, the preferable adhesive area ratio in the present invention is 3 to 35%, and a particularly preferable adhesive area ratio is 5 to 25%.

또, 이 표 2 의 결과와 표 1 의 종이 두께와 감는 직경의 관계로부터, 본 발명의 키친 페이퍼는, 종래 제품과 동등한 기름의 흡수량을 확보하면서, 감는 길이를 길게 할 수 있다는 것도 확인할 수 있다. 예를 들어, 종이 두께가 2 장으로 440 ㎛, 평량 28 g/㎡, 접착 면적률 7 %, 발포 후의 종이 두께가 740 ㎛ 인 경우, 대응하는 엠보스를 갖는 키친 페이퍼는, 11 m 의 감는 길이인 것에 대해, 본 실시예에서는, 동일한 감는 직경으로 약 2 배인 20 m 감는 것이 가능해져 수송, 보관 면에서 매우 우수하다.It can also be seen from the relationship between the results of Table 2 and the paper thickness and the winding diameter in Table 1 that the kitchen paper of the present invention can increase the winding length while securing the amount of oil equivalent to that of the conventional product. For example, when the paper thickness is 440 占 퐉, the basis weight is 28 g / m2, the adhesive area ratio is 7%, and the paper thickness after foaming is 740 占 퐉, the kitchen paper having the corresponding emboss has a winding length of 11 m In the present embodiment, it is possible to wind about 20 m at the same winding diameter twice, which is excellent in terms of transportation and storage.

다음으로, 본 발명의 키친 페이퍼에 있어서의 미터평량, 밀도, 크레이프지의 종이 두께와의 관계에 대한 시험 결과를 하기 표 3 에 나타낸다. 또한, 여기서 사용한 크레이프지는, 키친 페이퍼로 한 후, 접착된 각 크레이프지를 강제적으로 박리하여 얻은 것이다. 따라서, 크레이프지에는 접착제가 도포되어 있다. 또, 종이 밀도는 (당해 평량/종이 두께) 에 의해 산출하였다. 또, 표 중의 흡수 속도는, 지면에 1 ㏄ 의 기름을 적하한 후, 그 광택이 소멸될 때까지의 시간이다. 소멸되었는지의 여부는 육안으로 판단하였다. 평가로는 60 초 이하이면 바람직하다고 할 수 있다.Next, the test results of the relation between the meter basis weight, the density, and the paper thickness of the crepe paper in the kitchen paper of the present invention are shown in Table 3 below. Also, the crepe paper used here was obtained by forcibly peeling each of the bonded crepe paper after making it into kitchen paper. Therefore, the crepe paper is coated with an adhesive. The paper density was calculated based on the (basis weight / paper thickness). The rate of absorption in the table is the time from dropping 1 cc of oil to the paper to the time when the gloss disappears. Whether or not they were extinct was judged by the naked eye. An evaluation time of 60 seconds or less is preferable.

찢어지기 쉬운 정도는, 20 명의 피험자에게, 시료를 이용하여 실제로 닦아내는 용도로 사용하게 하고, 그 때 찢어지기 쉬운 것으로 느꼈는지의 여부로 판단하였다. 평가는, 10 명 이상이 찢어질 것 같다고 느낀 것을 △ 로 하였다.To the extent that it was easy to tear, 20 subjects were allowed to use the sample for actual wiping, and judged whether or not they felt tearable at that time. In the evaluation, △ indicates that more than ten people felt likely to tear.

평량이 10 g/㎡, 17 g/㎡ 인 것은, 사용시에 찢어질 것 같다는 피험자가 많았고, 밀도가 2.17 × 10⁵ g/㎥, 2.67 × 10⁵ g/㎥ 인 것은 흡액 속도가 늦어지는 경향이 있다. 따라서, 접착제 도포에 의한 흡액성의 저하를 고려하면, 적어도 본 발명의 키친 페이퍼에 있어서의 평량은 바람직하게는 21∼32 g/㎡ 이고, 밀도는 바람직하게는 0.83 × 10⁵∼1.94 × 10⁵ g/㎥ 이다.Many subjects were found to have a basis weight of 10 g / m 2 and 17 g / m 2, which tended to be torn at the time of use. The density of 2.17 × 10 ⁵ g / m 3 and 2.67 × 10 ⁵ g / have. Therefore, considering the lowering of the liquid-absorbing property by the application of the adhesive, the basis weight of the kitchen paper of the present invention is preferably 21 to 32 g / m 2, and the density is preferably 0.83 × 10 ^{5 to} 1.94 × 10 ⁵ g / m < 3 >.

표 3 으로부터, 본 발명의 키친 페이퍼에 있어서의 특히 바람직한 평량 및 밀도는, 이들 쌍방을 만족하는 평량이 21∼32 g/㎡ 이고, 또한 밀도가 1.22 × 10⁵∼1.94 × 10⁵g/㎥ 이다.From Table 3, particularly preferred weights and densities in the kitchen paper of the present invention are those in which the basis weight and the density satisfying both of them are 21 to 32 g / m 2 and the density is 1.22 × 10 ^{5 to} 1.94 × 10 ⁵ g / m 3 .

1, 2 : 크레이프지
3 : 접착제 부여 부분 (접착제)
4 : 공극
5 : 관심
6 : 절취선
10 : 추 (식재 등)
12 : 시트
P : 구획
L1 : 선폭
L2 : 발포성 경화 물질 미발포 상태의 종이 두께
L3 : 발포성 경화 물질 발포 상태의 종이 두께
L4 : 외경 (감는 직경)
L5 : 절취선 간격
G : 수평대
X1, X2 : 키친 페이퍼1, 2: Crepe paper
3: Adhesive application part (adhesive)
4: Pore
5: Interest
6: perforated line
10: Chu (planting)
12: Sheet
P: compartment
L1: Line width
L2: Paper thickness of foamed hardened material unfoamed
L3: Paper thickness of foamed curing material foamed
L4: Outer diameter (winding diameter)
L5: Perforation line spacing
G: Horizontal
X1, X2: Kitchen paper

Claims

Two crepe fabrics not provided with embosses are laminated and integrated via an adhesive disposed in a line shape, and a plurality of compartments surrounded by the linearly arranged adhesive agent are provided, and the adhesive agent is foamed by heat, expanded, Wherein the foamable curing material to be cured is contained in an unfoamed state.

The method according to claim 1,
Wherein the foamable curable material is foamed at 90 to 200 캜 and the paper thickness is increased by 100 탆 or more as compared with that before foamed by foaming.

3. The method according to claim 1 or 2,
Wherein the paper thickness of the entire kitchen paper is 700 占 퐉 or less, the basis weight of each crepe paper is 10 to 42 g / m2, and the density is 2.5 占^{04 to} 4.2 占⁰⁵ g / m3.

3. The method according to claim 1 or 2,
Wherein the line width of the linearly arranged adhesive is 0.25 to 2.00 mm and the area of one compartment surrounded by the linearly arranged adhesive is 25 to 100 mm 2.

3. The method according to claim 1 or 2,
Wherein the ratio of the total area of the adhesive-imparting portion to the one-side paper surface is 5 to 30%.

3. The method according to claim 1 or 2,
A kitchen paper in which a lipophilic base material is carried on one of the two crepe paper sheets.

3. The method according to claim 1 or 2,
Wherein said crepe paper is wound in a roll shape in a strip shape in which said crepe paper is in the shape of a band and in which a cutout line extending in the width direction at a predetermined interval in the longitudinal direction is disposed.