KR101118079B1 - Method of manufacturing nanofiber web - Google Patents
Method of manufacturing nanofiber web Download PDFInfo
- Publication number
- KR101118079B1 KR101118079B1 KR1020080078061A KR20080078061A KR101118079B1 KR 101118079 B1 KR101118079 B1 KR 101118079B1 KR 1020080078061 A KR1020080078061 A KR 1020080078061A KR 20080078061 A KR20080078061 A KR 20080078061A KR 101118079 B1 KR101118079 B1 KR 101118079B1
- Authority
- KR
- South Korea
- Prior art keywords
- polymer solution
- resin
- collector
- spinning needle
- nanofiber web
- Prior art date
Abstract
본 발명은 전기방사방식을 이용한 나노섬유 웹의 제조방법에 관한 것으로서, (ⅰ) 전압발생장치(60)에 의해 고전압이 걸려 있으며, 하단부는 고분자 용액 욕조(30)의 바닥에 고정되어 있고, 상단부는 고분자 용액 욕조(30)의 상부면에 천공된 구멍(31)을 통해 고분자 용액 욕조(30)의 상부면 위로 돌출되어 있는 방사니들(40)의 상단부로 전기력을 이용하여 상기 고분자 용액 욕조(30) 내에 담겨진 고분자 용액(80)을 공급한 다음, (ⅱ) 전압발생장치(60)에 의해 고전압이 걸려 있으며, 상기 방사니들(40)의 상부에 위치하는 컬렉터(50)를 향하여 방사니들(40)의 상단부에 공급된 고분자 용액(80)을 전기방사하여 나노섬유(70)를 휘산시킨 다음, (ⅲ) 휘산되는 나노섬유(70)를 상기 컬렉터(50) 상에 적층하는 것을 특징으로 한다.The present invention relates to a method of manufacturing a nanofiber web using the electrospinning method, (i) high voltage is applied by the voltage generator 60, the lower end is fixed to the bottom of the polymer solution bath 30, the upper end The polymer solution bath 30 uses an electric force to the upper end of the spinning needle 40 protruding over the top surface of the polymer solution bath 30 through a hole 31 drilled in the upper surface of the polymer solution bath 30. After supplying the polymer solution 80 contained in the (), (ii) high voltage is applied by the voltage generator 60, the spinning needle 40 toward the collector 50 located on the top of the spinning needle (40) The nanofiber 70 is volatilized by electrospinning the polymer solution 80 supplied to the upper end of the c), and (i) the nanofibers 70 volatilized are laminated on the collector 50.
본 발명은 상향식 전기방사시에 전기방사용 노즐 대신에 방사니들을 사용하기 때문에 나노섬유 웹의 균일성이 향상되고, 제조비용이 절감되고, 방사노즐의 막힘 현상등이 없어 설비의 유지 보수가 용이하고, 설비가 간소화되는 장점이 있다.In the present invention, since the spinning needle is used instead of the electrospinning nozzle during the bottom-up electrospinning, the uniformity of the nanofiber web is improved, the manufacturing cost is reduced, and there is no clogging phenomenon of the spinning nozzle. And there is an advantage that the equipment is simplified.
전기방사, 상향식, 웹, 나노섬유, 방사니들, 균일성, 컬렉터 Electrospinning, Bottom Up, Web, Nanofiber, Spinning Needle, Uniformity, Collector
Description
본 발명은 전기방사방식을 이용한 나노섬유 웹의 제조방법에 관한 것으로서, 보다 구체적으로는 종래의 노즐 대신에 바늘 형태의 방사니들(Spining Needle)로 고분자 용액을 전기방사함으로서 제조비용이 절감되고, 제조 공정의 관리가 용이하고, 설비의 유지 보수도 간편하게 되는 나노섬유 웹의 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a nanofiber web using an electrospinning method, and more specifically, manufacturing cost is reduced by electrospinning a polymer solution with a needle in the form of a spinning needle instead of a conventional nozzle. The present invention relates to a method for producing a nanofiber web, in which the process can be easily managed and the equipment can be easily maintained.
전기방사는 직경이 수십 내지 수백 ㎚인 초극세 섬유(이하"나노섬유"라고 한다.)를 제조할 수 있는 비교적 간단한 방법으로 이미 1930년대에 독일에서 첫 선을 보였다. 그러나, 당시의 기술로는 이를 상품화하는 데에 한계가 있어 관심을 받지 못하다가 1970년대에 이르러서야 연구가 다시 시작되었다가 2000년대 이후에서야 본격적인 연구가 시작되었다.Electrospinning was first introduced in Germany in the 1930s as a relatively simple way to produce ultrafine fibers (hereinafter referred to as "nano fibers") with diameters of tens to hundreds of nm. However, the technology of the time was limited to commercialization of this technology, so it was not received attention, and research began again until the 1970s, and full-scale research began only after the 2000s.
전기방사는 고분자용액에 수천 내지 수만 볼트의 높은 전압을 가하여 고분자 용액으로부터 용매의 표면장력을 넘는 접선벡터의 힘이 가해져서 고분자용액으로부터 미세한 폴리머 제트가 형성되어 고분자용액에 가해진 전하와 반대의 전하를 띠는 물체를 향해 빠른 속도로 진행하게 된다. 분사된 고분자 제트는 이어 수많은 미세 섬유로 다시 분산되어 뿌려지게 되는데 이때의 미세 섬유의 직경은 수십내지 수 백 나노미터의 굵기를 가진다.Electrospinning applied a high voltage of several thousand to tens of thousands of volts to the polymer solution, and the force of the tangential vector exceeding the surface tension of the solvent was applied from the polymer solution to form a fine polymer jet from the polymer solution. The band advances rapidly toward the object. The jets of polymer jets are then dispersed and scattered back into a number of fine fibers, which have a diameter of tens to hundreds of nanometers.
전기방사를 이용하면 고분자용액으로부터 수십 내지 수백 나노미터의 굵기를 가지는 나노섬유로 이루어진 도 4와 같은 나노섬유 웹을 제조할 수 있으며, 이를 이용하여 고기능성 의류, 초정밀 필터, 세포배양용 소재(scaffold) 등의 고성능 제품을 얻을 수 있다.Electrospinning can be used to produce a nanofiber web as shown in Figure 4 consisting of nanofibers having a thickness of several tens to hundreds of nanometers from a polymer solution, using the high-performance clothing, ultra-precision filter, cell culture material (scaffold) High performance products, such as) can be obtained.
도 4는 나노섬유 웹의 전자현미경사진이다.4 is an electron micrograph of a nanofiber web.
상업적으로 나노섬유 웹을 제조하기 위해서 한국등록특허 제0412241호, 한국등록특허 제0422459호 및 한국공개특허 제2005-15610호 고분자 용액을 다수의 노즐을 통해 전기방사하는 방법을 제안하고 있다.In order to commercially manufacture a nanofiber web, Korean Patent No. 0412241, Korean Patent No. 0422459 and Korean Patent Application No. 2005-15610 propose a method of electrospinning a plurality of nozzles through a plurality of nozzles.
구체적으로, 상기의 종래 방법은 도 3에 도시된 바와 같이 고분자 용액을 계량펌프(2)를 통해 고전압이 걸려있는 다수의 노즐(3)에 공급한 다음, 이를 노즐과 반대 전하를 띠는 고전압이 걸려있는 컬렉터(4)상에 위치하는 섬유기재상에 전기방사하여 나노섬유 웹을 제조하였다.Specifically, in the conventional method, as shown in FIG. 3, the polymer solution is supplied to the plurality of
도 3은 종래 전기방사 공정 개략도이다.3 is a schematic diagram of a conventional electrospinning process.
상기의 종래 방법은 하나의 노즐을 사용하는 것에 비하여 생산성이 매우 우수하고 균일성이 우수하여졌다. 그러나, 상기 종래 기술은 다수의 노즐을 사용함에 따라 노즐에서의 막힘 등으로 인한 결점 발생의 가능성이 매우 높고, 노즐을 수시로 탈거하여 일일이 세정하여야하는 번거로움이 따른다. 또, 노즐마다 수천 내지 수만볼트의 고전압을 가하게 되므로 각 노즐에서의 전기장에 의해 노즐에서 발생하는 고분자 제트의 방향에 상호 영향을 미쳐 균일한 나노섬유 웹을 얻기가 어렵다.The conventional method described above has excellent productivity and excellent uniformity compared to using one nozzle. However, the prior art has a very high possibility of defects due to clogging in the nozzle, and the need for removing the nozzles from time to time causes a hassle. In addition, since a high voltage of thousands to tens of thousands of volts is applied to each nozzle, it is difficult to obtain a uniform nanofiber web because the electric field in each nozzle affects the direction of the polymer jet generated in the nozzle.
게다가 고분자의 종류, 고분자의 분자량, 용매의 점도, 온도 등에 따라서 노즐 끝에서의 고분자 용액 방울의 형성이 모두 상이하므로 고분자 종류 변경, 고분자 용액의 변경, 생산속도의 변경 시 안정적인 방사성을 얻기 위해서 노즐의 규격을 그에 맞도록 변경하여야하는 번거로움이 따른다. 노즐의 규격을 최적화하기 위해서는 별도의 시험을 통해 적합한 노즐의 내경, 길이 등을 조사하고 이에 맞는 노즐을 준비하여 설치해야 하므로 다양한 품종의 나노섬유 웹을 생산하는 데에 있어 준비기간이 매우 길어지게 된다.In addition, the formation of polymer solution droplets at the nozzle tip is different depending on the type of polymer, molecular weight of polymer, viscosity of solvent, temperature, etc. This is a hassle to change the specification to conform. In order to optimize the size of the nozzle, it is necessary to investigate the inner diameter and length of a suitable nozzle through separate tests, and to prepare and install a nozzle suitable for the nozzle. Therefore, the preparation period for producing various kinds of nanofiber webs becomes very long. .
이를 해결하기 위해 실제 상업적 형태의 전기방사 설비에 있어서는 노즐을 기재의 대각선 방향으로 배열하거나 혹은 여러 개의 층으로 나누어 배열하되 서로 교호의 위치가 되도록 배열하는 등의 기술이 적용되고 있으나 다수의 노즐을 일일이 세정해야하며 노즐에서의 전기장에 의한 고분자 제트의 상호 영향의 문제를 근본적으로 해결하기 어렵다.In order to solve this problem, in actual commercial-type electrospinning equipment, a technique of arranging nozzles in a diagonal direction of the substrate or dividing into several layers and arranging them alternately with each other has been applied. It must be cleaned and it is difficult to fundamentally solve the problem of the mutual influence of the polymer jets by the electric field in the nozzle.
또한, 종래방법은 제조비용이 상승되고 설비가 복잡한 문제도 있었다.In addition, the conventional method has a problem that the manufacturing cost is increased and the equipment is complicated.
본 발명의 목적은 이와 같은 종래 문제점을 해결함으로써 나노섬유 웹의 균일성을 크게 향상시키기 위한 것이다.An object of the present invention is to significantly improve the uniformity of the nanofiber web by solving such a conventional problem.
본 발명의 또다른 목적은 나노섬유 웹 제조시 제조원가를 절감하고 공정관리가 용이하며 설비의 보수 및 유지도 용이하게 하기 위한 것이다.Another object of the present invention is to reduce the manufacturing cost, easy process management, and easy maintenance and maintenance of the fabric when manufacturing the nanofiber web.
이와 같은 과제를 달성하기 위한 본 발명에 따른 나노섬유 웹의 제조방법은, (ⅰ) 전압발생장치(60)에 의해 고전압이 걸려 있으며, 하단부는 고분자 용액 욕조(30)의 바닥에 고정되어 있고, 상단부는 고분자 용액 욕조(30)의 상부면에 천공된 구멍(31)을 통해 고분자 용액 욕조(30)의 상부면 위로 돌출되어 있는 방사니들(40)의 상단부로 전기력을 이용하여 상기 고분자 용액 욕조(30) 내에 담겨진 고분자 용액(80)을 공급한 다음, (ⅱ) 전압발생장치(60)에 의해 고전압이 걸려 있으며, 상기 방사니들(40)의 상부에 위치하는 컬렉터(50)를 향하여 방사니들(40)의 상단부에 공급된 고분자 용액(80)을 전기방사하여 나노섬유(70)를 휘산시킨 다음, (ⅲ) 휘산되는 나노섬유(70)를 상기 컬렉터(50) 상에 적층하는 것을 특징으로 한다.In the method of manufacturing a nanofiber web according to the present invention for achieving such a problem, (i) a high voltage is applied by the
이하, 첨부한 도면 등을 통하여 본 발명을 상세하게 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
먼저, 본 발명은 도 1에 도시된 바와 같이 고분자 용액 주탱크(10)내에 보관중인 고분자 용액을 고분자 용액 공급 펌프(20)를 통해 고분자 용액 욕조(30)로 공급하여 저장한다.First, as shown in FIG. 1, the polymer solution stored in the polymer solution
다음으로는, 고분자 용액 욕조(30) 내에 저장된 고분자 방사용액을 고전압이 걸려 있는 상태로 하단부는 상기 고분자 용액 욕조(30)의 바닥에 고정되어 있고 상단부는 고분자 용액 욕조의 상부면에 천공된 구멍(31)을 통해 고분자 용액 욕조의 상부면 위로 돌출되어 있는 방사니들(40)의 상단부로 공급한다. Next, the lower end portion is fixed to the bottom of the
다음으로는, 방시니들(40)의 상단부에 공급된 고분자 용액(80)을 고전압이 걸려 있는 상태로 방사니들(40)의 상부에 위치하는 컬렉터(50)를 향해 전기방사시켜 나노섬유(70)를 휘산시킨 다음, 휘산되는 나노섬유(70)를 상기 컬렉터(50) 상에 적층하여 나노섬유 웹을 제조한다.Next, the
도 1은 본 발명의 공정 개략도이다.1 is a process schematic diagram of the present invention.
상기 방사니들(40)과 컬렉터(50) 각각에는 전기방사를 위해 서로 다른 전하를 띄는 고전압이 걸려진다.Each of the
상기 방사니들(40)의 하단부는 고분자 용액 욕조(30)의 바닥면에 고정되어 있고, 상단부는 고분자 용액 욕조의 상부면에 천공된 구멍(31)을 통해 고분자 용액 욕조의 상부면 위로 돌출되어 있다.The lower end of the
고분자 용액 욕조(30) 내에 저장된 고분자 용액은 방사니들(40)에 가해지는 고전압에 의해 발생되는 전기에 의해 방사니들(40)의 상단부로 올라오게 되고, 상기와 같이 방사니들(40)의 상단부로 위로 올라온 고분자 용액은 방사니들(40)과 컬렉터(50)에 걸려있는 고전압에 의해 고분자 용액의 표면장력보다 법선벡터 방향으로 응력이 커져서 고분자 제트(Jet)를 형성하게 된다.The polymer solution stored in the
상기 고분자 제트는 반대 전하를 띄는 컬렉터(50)를 향하게 되며, 방사니들(40)으로부터 일정구간까지는 제트(Jet) 상태를 유지하다가 그 이후에는 나노섬유(70)로 변하면서 휘산되어 컬렉터(50) 상에 집적된다.The polymer jet is directed toward the
도 2는 방사니들 상단부로 고분자 용액 욕조(30)에 저장된 고분자 용액이 올 라오는 상태를 나타내는 모식도이다.Figure 2 is a schematic diagram showing a state in which the polymer solution stored in the polymer solution bath 30 to the upper end of the spinning needle.
상기 고분자 용액은 폴리아미드 수지, 폴리우레탄 수지, 폴리에스테르 수지, 폴리스티렌 수지, 셀룰로오스, 폴리비닐아세테이트, 폴리비닐클로라이드, 폴리비닐알코올 수지, 폴리설폰 수지, 폴리아크릴로니트릴 수지, 폴리메틸메타 아크릴에이트 수지, 폴리스티렌 수지, 폴리아크릴산 수지, 폴리올레핀 수지, 전방향족폴리아미드 수지 또는 폴리비닐리덴 플루오라이드 수지 등과 같이 용해 가능한 모든 섬유형성능 고분자를 사용할 수 있다.The polymer solution may be polyamide resin, polyurethane resin, polyester resin, polystyrene resin, cellulose, polyvinylacetate, polyvinylchloride, polyvinyl alcohol resin, polysulfone resin, polyacrylonitrile resin, polymethylmethacrylate resin All soluble fiber-forming polymers such as polystyrene resin, polyacrylic acid resin, polyolefin resin, wholly aromatic polyamide resin or polyvinylidene fluoride resin can be used.
또, 고분자 물질을 용해하기 위한 용매의 종류에도 제한이 없다. 용매는 고분자에 따라 한정이 되는 것이며 나노섬유 웹을 제조하는 데에 사용되는 고분자에 따라 용매를 자유로이 할 수 있다. 또, 고분자 용액의 제조방법에 대해서도 제한이 없다. Moreover, there is no restriction | limiting also in the kind of solvent for melt | dissolving a high molecular substance. The solvent is limited depending on the polymer, and the solvent can be freely determined depending on the polymer used to prepare the nanofiber web. Moreover, there is no restriction also about the manufacturing method of a polymer solution.
고분자 용액의 농도는 1% 이하의 낮은 농도부터 50% 이하의 높은 농도에 까지 이른다.The concentration of the polymer solution can range from as low as 1% or less to as high as 50% or less.
또한, 두 종류 이상의 고분자를 동시에 사용할 수 있다. 두 종류 이상의 상이한 고분자를 용매에 녹여 사용하는 것도 가능하며, 동종의 고분자에 있어 분자량 등의 특성이 상이한 고분자를 용매에 녹여 사용하는 것도 가능하다.In addition, two or more kinds of polymers may be used simultaneously. It is also possible to dissolve two or more kinds of different polymers in a solvent, or to dissolve and use polymers having different properties such as molecular weight in solvents.
컬렉터(50) 위에는 섬유기재 또는 필름이 위치할 수도 있다.The fibrous substrate or film may be positioned on the
상기 컬렉터(50)는 방사니들(40)의 상부에 위치하고, 일정한 선속도로 운동한다.The
방사니들(40)과 컬렉터(50) 각각의 표면은 금, 은, 텅스텐, 구리, 스테인레 스 강 또는 이들의 합금 등이고, 보다 바람직 하기로는 스테인레스 강에 백금이 코팅된 것이 좋다.The surface of each of the
이와 같이 본 발명에서는 다수의 노즐을 사용하는 대신에 방사니들(40)을 사용함으로써, 다수의 노즐을 일일이 세정하고 관리하여야 하는 번거로움이 없으며 다수의 노즐의 배열에 따라 나노섬유 웹의 균일성이 좌우되는 단점이 없다. 또, 고분자의 종류, 점도 등에 따라 노즐의 내경, 길이 등을 변경하여 설치하여야 하는 번거로움이 없어 품종의 교체 등이 매우 용이하며 노즐을 사용함에 따른 노즐간의 정전기적 반발력으로 인한 나노섬유 웹의 불균일성이 없는 장점이 있다. 또, 하향식 노즐을 사용하는 종래의 전기방사 장치에 비하여서는 미용해 고분자 등의 결점이 기재 상에 분산되지 않으므로 결점이 거의 없는 나노섬유 웹을 얻을 수 있다.Thus, in the present invention, by using the
본 발명은 제조비용이 저렴하고, 나노섬유 웹의 균일성을 크게 향상시키고 품종 변경 및 공정관리가 용이하다The present invention is low in manufacturing cost, greatly improves the uniformity of the nanofiber web, easy to change the variety and process management
아울러, 본 발명은 설비의 보수 및 유지가 용이하고 설비도 간소화할 수 있다.In addition, the present invention is easy to repair and maintain the equipment and can simplify the equipment.
그 결과 본 발명으로 제조된 나노섬유 웹은 고성능 필터, 광학소재 등으로 유용하다.As a result, the nanofiber web produced by the present invention is useful as a high performance filter, optical material and the like.
이하 실시예 및 비교실시예를 통하여 본 발명을 보다 구체적으로 살펴본다. 그러나 본 발명이 하기 실시예에만 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. However, the present invention is not limited only to the following examples.
실시예Example 1 One
폴리아미드를 개미산에 농도가 8%가 되도록 용해하여 25℃의 폴리아미드 용액을 제조하여 고분자 용액으로 사용하였다.Polyamide was dissolved in formic acid at a concentration of 8% to prepare a polyamide solution at 25 ° C. and used as a polymer solution.
도 1에 도시된 공정에 따라 고분자 용액 주탱크(10)내에 저장된 폴리아미드 용액을 고분자 용액 공급 펌프(20)를 통해 고분자 용액 욕조(30)로 공급, 저장한 다음, 상기 고분자 용액 욕조(30) 상에 음극의 고전압이 걸려 있는 상태로 하단부는 상기 고분자 용액 욕조(30)의 바닥에 고정되어 있고 상단부는 고분자 용액 욕조의 상부면 위로 돌출되어 있는 방사니들(40)이 상단부로 공급한 다음, 방사니들(40)의 상단부에 공급된 고분자 용액(80)을 양극의 고전압이 걸려있는 상태로 방사니들(40)의 상부에 위치하는 컬렉터(50)를 향해 분사시켜 나노섬유를 휘산시킨 다음, 휘산되는 나노섬유(70)를 컬렉터(50) 위에 적층하여 폴리아미드 나노섬유 웹을 제조하였다.According to the process shown in FIG. 1, the polyamide solution stored in the polymer solution
이때, 방사니들(40)과 컬렉터(50)에는 220볼트, 60Hz의 교류전원이 연결된 전압 발생장치(60)를 이용하여 55,000볼트의 전압을 걸었다.At this time, a voltage of 55,000 volts was applied to the
상기 방사니들(40)과 컬렉터(50) 각각의 표면은 스테인레스 백금이 코팅된 재질로 구성되며, 방사니들(40)에 천공된 미세구멍(41)의 직경은 0.5㎜로 하였다.The surface of each of the spinning
또한 방사니들(40)과 컬렉터(50)의 간격은 30㎝로 설정하였다.In addition, the interval between the spinning
제조된 나노섬유 웹의 각종 물성을 평가한 결과는 표 3과 같다.The results of evaluating various physical properties of the prepared nanofiber webs are shown in Table 3.
실시예Example 2 ~ 2 ~ 실시예Example 6 6
고분자 용액을 구성하는 고분자 및 용매 종류, 컬렉터 및 방사니들에 가해지는 전압 및 방사니들과 컬렉터간의 간격을 표 1과 같이 변경한 것을 제외하고는 실시예 1과 동일한 조건으로 나노섬유 웹을 제조하였다.The nanofiber web was manufactured under the same conditions as in Example 1 except that the polymer and solvent type constituting the polymer solution, the voltage applied to the collector and the spinning needle, and the interval between the spinning needle and the collector were changed as shown in Table 1.
제조한 나노섬유 웹의 각종 물성을 평가한 결과는 표 3과 같다.The results of evaluating various physical properties of the prepared nanofiber webs are shown in Table 3.
장치Electrospinning
Device
종류Polymer
Kinds
(볼트)Voltage
(volt)
(㎝)Spinning needle-collector spacing
(Cm)
비교실시예Comparative Example 1 One
폴리아미드를 개미산에 농도가 8%가 되도록 용해하여 25℃의 폴리아미드 용액을 제조하여 고분자 용액으로 사용하였다.Polyamide was dissolved in formic acid at a concentration of 8% to prepare a polyamide solution at 25 ° C. and used as a polymer solution.
도 3에 도시된 공정에 따라 고분자 용액 주탱크(1)내에 저장된 폴리아미드 용액을 고분자 용액 공급 펌프(2)를 통해 양극의 고전압이 걸려있는 다수의 노즐에 공급한 다음, 이를 음극의 고전압이 걸려 있는 금속판의 컬렉터(4)를 향해 분사시켜 나노섬유를 휘산시킨 다음, 휘산되는 나노섬유를 컬렉터 상에 적층하여 나노섬유 웹을 제조하였다.According to the process shown in FIG. 3, the polyamide solution stored in the polymer solution
이때, 다수의 노즐과 컬렉터(4)에는 220볼트, 60Hz의 교류전원이 연결된 전압발생장치(6)를 이용하여 55,000 볼트의 전압을 걸어 주었고, 노즐 토출량은 0.5ml/분으로 하였다.At this time, a voltage of 55,000 volts was applied to the plurality of nozzles and the
또한 노즐과 컬렉터(4)의 간격은 30㎝로 설정하였다.In addition, the space | interval of the nozzle and the
제조된 나노섬유 웹의 각종 물성을 평가한 결과는 표 3과 같다.The results of evaluating various physical properties of the prepared nanofiber webs are shown in Table 3.
비교실시예Comparative Example 2 ~ 2 ~ 비교실시예Comparative Example 6 6
고분자 용액을 구성하는 고분자 및 용매종류, 컬렉터 및 노즐들에 가해지는 전압, 노즐의 토출량 및 노즐과 컬렉터간의 간격을 표 2와 같이 변경한 것을 제외하고는 비교실시예 1과 동일한 조건으로 나노섬유 웹을 제조하였다.Nanofiber web under the same conditions as in Comparative Example 1 except for changing the polymer and solvent constituting the polymer solution, the voltage applied to the collector and the nozzles, the discharge amount of the nozzle and the interval between the nozzle and the collector as shown in Table 2 Was prepared.
제조한 나노섬유 웹의 각종 물성을 평가한 결과는 표 3과 같다.The results of evaluating various physical properties of the prepared nanofiber webs are shown in Table 3.
장치Electrospinning
Device
(볼트)Voltage
(volt)
토출량
(ml/min)Nozzle
Discharge
(ml / min)
(㎝)Nozzle-Collector Spacing
(Cm)
(g/㎡/day)Breathable average
(g / ㎡ / day)
(g/㎡/day)Permeability Standard Deviation
(g / ㎡ / day)
(개)fault
(dog)
상기의 평가 결과에서 보는 바와 같이 실시예 1 내지 실시예 6으로 제조된 나노섬유 웹의 투습도 표준편차는 500g/㎡/day 이하로 매우 균일하다. 또, 나노 섬유 웹 상의 결점도 없는 매우 우수한 품질의 나노섬유 웹을 얻을 수 있었다.As can be seen from the above evaluation results, the standard deviation of the water vapor transmission rate of the nanofiber webs prepared in Examples 1 to 6 is very uniform, not more than 500 g /
그러나, 비교실시예 1 내지 비교실시예 6으로 제조된 나노섬유 웹은 실시예 1 내지 실시예 6과 거의 동일한 투습도를 나타내는 가운데 표준편차가 2,000g/㎡/day 이상으로 매우 높게 나타났다. 또, 결점도 6개 내지 12개 수준으로 실시예 1 내지 실시예 6으로 제조한 나노섬유 웹에 비교하여 매우 많다. 결점은 대부분 노즐에서 떨어진 고분자용액이며 품종 교체에 따른 노즐의 막힘의 영향도 발생하였다.However, the nanofiber webs prepared in Comparative Examples 1 to 6 exhibited substantially the same moisture permeability as Examples 1 to 6, but showed a very high standard deviation of 2,000 g /
표 3의 물성들은 아래와 같은 방법으로 평가하였다.Properties of Table 3 were evaluated by the following method.
?나노섬유 웹의 ? Of nanofiber web 투습도Moisture permeability
나노섬유 웹의 투습도를 측정 부위를 달리하여 각 10회 평가하고 그 평균 값과 표준편차를 구하였다. 투습도 평가 방법은 원단에 일정한 압력으로 습기를 가하고 24시간 경과 후 통과한 수분의 g 수를 평가하는 것으로 한국공업규격 KS K 0594를 따른다.The water vapor permeability of the nanofiber web was evaluated 10 times with different measurement sites, and the average value and standard deviation were calculated. The method of evaluating moisture permeability is to evaluate the number of grams of moisture passed after 24 hours of application of moisture to a fabric under a certain pressure, according to Korean Industrial Standard KS K 0594.
?나노섬유 웹의 결점Drawbacks of Nanofiber Web
나노섬유 웹에 대해 폭 45cm, 길이 5m 내에서의 결점의 수를 육안검사를 통해 파악한다. 결점은 고분자 용액이 낙하한 지점의 수와 나노섬유가 도포되지 않은 지점의 수로 평가하였다.The number of defects within 45 cm wide and 5 m long for the nanofiber web is visually determined. The defects were evaluated by the number of points where the polymer solution fell and the number of points where no nanofibers were applied.
도 1은 본 발명의 공정 개략도.1 is a process schematic diagram of the present invention.
도 2는 본 발명에서 방사니들에 고분자 용액이 공급되는 상태를 나타내는 모식도.Figure 2 is a schematic diagram showing a state in which the polymer solution is supplied to the spinning needle in the present invention.
도 3은 종래 전기방사 공정 개략도.3 is a schematic diagram of a conventional electrospinning process.
도 4는 나노섬유 웹의 전자현미경 사진.4 is an electron micrograph of the nanofiber web.
* 도면 중 주요 부분 설명* Description of the main parts of the drawings
1, 10 : 고분자 용액 주탱크 2, 20 : 고분자 용액 공급펌프1, 10: polymer solution
30 : 고분자 용액 욕조 40 : 방사니들30: polymer solution bath 40: spinning needle
31 : 고분자 용액 욕조 상부면에 천공된 구멍 4, 50 : 컬렉터31 hole punched in the upper surface of the
6, 60 : 전압발생장치 70 : 나노섬유6, 60: voltage generator 70: nanofibers
80 : 방사니들에 공급된 고분자 용액80: polymer solution supplied to the spinning needle
3 : 노즐블록 5 : 전압전달로드.3: nozzle block 5: voltage transfer rod.
Claims (5)