KR101076017B1 - Constructing Method of Color pattern floors - Google Patents

Constructing Method of Color pattern floors Download PDF

Info

Publication number
KR101076017B1
KR101076017B1 KR1020080098862A KR20080098862A KR101076017B1 KR 101076017 B1 KR101076017 B1 KR 101076017B1 KR 1020080098862 A KR1020080098862 A KR 1020080098862A KR 20080098862 A KR20080098862 A KR 20080098862A KR 101076017 B1 KR101076017 B1 KR 101076017B1
Authority
KR
South Korea
Prior art keywords
layer
color
pattern
weight
release agent
Prior art date
Application number
KR1020080098862A
Other languages
Korean (ko)
Other versions
KR20100039775A (en
Inventor
지성호
강성원
지상호
Original Assignee
삼중씨엠텍(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼중씨엠텍(주) filed Critical 삼중씨엠텍(주)
Priority to KR1020080098862A priority Critical patent/KR101076017B1/en
Publication of KR20100039775A publication Critical patent/KR20100039775A/en
Application granted granted Critical
Publication of KR101076017B1 publication Critical patent/KR101076017B1/en

Abstract

본 발명은 액상이형제를 이용한 칼라무늬 바닥재의 시공방법에 관한 것으로서, 콘크리트 또는 아스팔트 층 상부에 칼라하드너 층을 형성하는 단계; 상기 칼라 하드너층 상부에 용제 70~84중량%, 실리콘오일 14~26중량%, 소포제 0.3~0.7중량%, 분산제 0.3~0.7중량%, 계면활성제 0.4~0.6중량% 및, 무기안료 1~2 중량%로 이루어진 이형제층을 형성하는 단계; 상기 이형제층 상부에 스템프를 이용해 패턴무늬를 음각하는 단계; 상기 스템프가 제거된 후, 양생과정을 거쳐 이형제 성분이 칼라하드너층으로 완전 흡수되면서, 이형제의 안료 성분이 칼라하드너층에 투톤칼라의 무늬를 형성하는 단계; 및 상기 패턴무늬 상부에 코팅층을 형성하는 단계;를 포함한다.The present invention relates to a construction method of a color patterned flooring material using a liquid releasing agent, the method comprising: forming a color hardener layer on an concrete or asphalt layer; 70-84% by weight of solvent, 14-26% by weight of silicone oil, 0.3-0.7% by weight of antifoam, 0.3-0.7% by weight of dispersant, 0.4-0.6% by weight of surfactant, and inorganic pigment 1-2% Forming a release agent layer composed of%; Engraving a pattern pattern using a stamp on the release agent layer; After the stamp is removed, the curing agent is completely absorbed into the color hardener layer through the curing process, the pigment component of the release agent to form a two-tone color pattern on the color hardener layer; And forming a coating layer on the pattern pattern.

본 발명은 칼라하드너층 표면에 패턴무늬를 형성하는 스템프의 분리가 쉽게 이루어지도록 하고, 스템프 분리후 칼라하드너층 표면에 완전 흡수되도록 함으로써, 별도의 세척공정 없이 후속공정(코팅작업)의 진행이 가능하도록 함으로써, 작업시간을 단축할 수 있는 효과를 갖는다.The present invention is to facilitate the separation of the stamp forming a pattern on the surface of the color hardener layer, and to be completely absorbed on the surface of the color hardener layer after removing the stamp, it is possible to proceed to the subsequent process (coating operation) without a separate washing process By doing so, the work time can be shortened.

칼라무늬, 바닥재, 콘크리트, 이형제, 투톤칼라 Color pattern, flooring, concrete, release agent, two-tone color

Description

액상이형제를 이용한 칼라무늬 바닥재의 시공방법{Constructing Method of Color pattern floors}Construction method of color pattern flooring using liquid release agent

본 발명은 액상이형제를 이용한 칼라무늬 바닥재의 시공방법에 관한 것으로서, 보다 상세하게는 액상으로 제조되어 물청소 없이도 바로 코팅작업이 가능하고, 스템프 도장 후의 이형성이 뛰어나고, 자연 암석에 가까운 무늬를 갖는 투톤 칼라의 연출이 가능한 액상이형제를 이용한 칼라무늬 바닥재의 시공방법에 관한 것이다.The present invention relates to a construction method of a color patterned flooring material using a liquid releasing agent, and more particularly, it is manufactured in a liquid state, and thus coating can be performed immediately without cleaning with water, and has excellent releasability after stamping, and has a pattern close to natural rock. It relates to a construction method of a color patterned flooring using a liquid release agent capable of directing two-tone color.

도 1은 종래기술의 칼라무늬 콘크리트 습식 매트 공법의 시공과정을 개략적으로 도시한 흐름도로서, 종래기술을 도 1을 참조하여 설명하면, 시멘트, 모래, 물 등으로 구성되는 레미콘 콘크리트 조성물을 적정하게 포설한 후 면을 고르고, 물기가 없어지고 어느 정도 경화되면, 하드너(hardener)로 원하는 색상을 뿌려서 베이스 칼라를 넣게 된다. 그 후에, 종래의 파우더 이형제와 안료를 분사하여 습식 몰탈 작업 방식에서 후속공정의 우레탄 몰드(예를 들어, 고무매트)와 하드너와의 층 을 쉽게 이형시키고 안료의 첨가로 2차 착색의 효과를 부여하였다. 이형제의 분사 후, 고무매트 등의 몰드로 원하는 패턴을 압인한 후, 파우더 이형제를 제거하기 위해 물로 세척하는 단계를 거치게 된다. 파우더 이형제가 남아 있으면, 후속공정의 아크릴 또는 아크릴-우레탄을 코팅할 경우 이형제에 의해 접착이 형성되지 못하고, 쉽게 벗겨지는 문제가 있다.1 is a flow chart schematically showing the construction process of the prior art color patterned concrete wet mat method, when the prior art will be described with reference to FIG. 1, the concrete concrete composition composed of cement, sand, water, etc. is properly installed. Once you've picked the surface, drained and hardened to a certain extent, you can apply the base color by applying the desired color with a hardener. After that, the conventional powder release agent and the pigment are sprayed to easily release the layer of the urethane mold (for example, rubber mat) and hardener in the subsequent process in the wet mortar operation method, and the addition of the pigment gives the effect of secondary coloring. It was. After spraying the release agent, the desired pattern is stamped with a mold such as a rubber mat, and then washed with water to remove the powder release agent. If the powder release agent remains, when the acrylic or acrylic-urethane coating of the subsequent process, the adhesive is not formed by the release agent, there is a problem that peel off easily.

또한, 파우더 이형제를 수세할 때 파우더의 날림현상으로 주변의 오염문제가 심각하고, 또한 잔량의 처리문제가 매우 힘들다. 이와 함께, 환경오염의 심각한 우려가 되고 있는 실정이다.In addition, when washing the powder release agent, the problem of contamination of the surroundings due to the blowing of the powder is serious, and the problem of the remaining amount is very difficult. In addition, the situation is a serious concern of environmental pollution.

본 발명의 목적은 칼라하드너층 표면에 패턴무늬를 형성하는 스템프의 분리가 쉽게 이루어지도록 하고, 스템프 분리후 칼라하드너층 표면에 완전 흡수되도록 함으로써, 별도의 세척공정 없이 후속공정의 진행이 가능하도록 하고, 시공된 바닥재가 자연석 무늬와 흡사한 투톤칼라의 연출이 가능하도록 한 액상이형제를 이용한 칼라무늬 바닥재의 시공방법을 제공함에 있다.An object of the present invention is to facilitate the separation of the stamp to form a pattern on the surface of the color hardener layer, and to be completely absorbed on the surface of the color hardener layer after the separation of the stamp, to allow the progress of the subsequent process without a separate washing process In addition, the present invention provides a method of constructing a colored patterned flooring material using a liquid release agent that enables the production of a two-tone color similar to a natural stone pattern.

본 발명의 목적을 달성하기 위한 액상이형제를 이용한 칼라무늬 바닥재의 시공방법은 콘크리트 또는 아스팔트 층 상부에 칼라하드너 층을 형성하는 단계; 상기 칼라 하드너층 상부에 용제 70~84중량%, 실리콘오일 14~26중량%, 소포제 0.3~0.7중량%, 분산제 0.3~0.7중량%, 계면활성제 0.4~0.6중량% 및, 무기안료 1~2 중량%로 이루어진 이형제층을 형성하는 단계; 상기 이형제층 상부에 스템프를 이용해 패턴무늬를 음각하는 단계; 상기 스템프가 제거된 후, 양생과정을 거쳐 이형제 성분이 칼라하드너층으로 완전 흡수되면서, 이형제의 안료 성분이 칼라하드너층에 투톤칼라의 무늬를 형성하는 단계; 및 상기 패턴무늬 상부에 코팅층을 형성하는 단계;를 포함한다.The construction method of the color patterned flooring using a liquid release agent for achieving the object of the present invention comprises the steps of forming a color hardener layer on the concrete or asphalt layer; 70-84% by weight of solvent, 14-26% by weight of silicone oil, 0.3-0.7% by weight of antifoam, 0.3-0.7% by weight of dispersant, 0.4-0.6% by weight of surfactant, and inorganic pigment 1-2% Forming a release agent layer composed of%; Engraving a pattern pattern using a stamp on the release agent layer; After the stamp is removed, the curing agent is completely absorbed into the color hardener layer through the curing process, the pigment component of the release agent to form a two-tone color pattern on the color hardener layer; And forming a coating layer on the pattern pattern.

여기서, 상기 칼라하드너층은 2~10mm 두께로 형성하는 것이 바람직하다.Here, the color hardener layer is preferably formed to have a thickness of 2 ~ 10mm.

그리고, 상기 용제는 미네럴 스피릿일 수 있다.In addition, the solvent may be a mineral spirit.

또한, 상기 무기안료는 고형분 50%의 산화철 및 산화티탄, 유산바륨, 탄산바륨 중 어느 하나일 수 있다.In addition, the inorganic pigment may be any one of iron oxide and titanium oxide, barium lactate, barium carbonate having a solid content of 50%.

그리고, 상기 코팅층은 유성계 아크릴 합성고분자 수지 또는 수성계인 퓨어 아크릴 합성고분자 수지를 사용해 0.05~0.1mm 두께로 도포하는 것이 바람직하다.The coating layer is preferably coated with an oil-based acrylic synthetic polymer resin or a water-based pure acrylic synthetic polymer resin at a thickness of 0.05 to 0.1 mm.

본 발명은 칼라하드너층 표면에 패턴무늬를 형성하는 스템프의 분리가 쉽게 이루어지도록 하고, 스템프 분리후 칼라하드너층 표면에 완전 흡수되도록 함으로써, 별도의 세척공정 없이 후속공정(코팅작업)의 진행이 가능하도록 함으로써, 작업시간을 단축할 수 있는 효과를 갖는다.The present invention is to facilitate the separation of the stamp forming a pattern on the surface of the color hardener layer, and to be completely absorbed on the surface of the color hardener layer after removing the stamp, it is possible to proceed to the subsequent process (coating operation) without a separate washing process By doing so, the work time can be shortened.

또한, 본 발명은 이형제 세척에 따른 오염물질이 발생되지 않기 때문에 친환 경적인 시공이 가능한 효과를 갖는다.In addition, the present invention has an effect that can be eco-friendly construction because no contaminants are generated by the cleaning of the release agent.

또한, 본 발명은 이형제 내의 안료를 적절히 분산시킴으로써, 시공된 바닥재가 자연석 무늬와 흡사한 투톤칼라의 연출이 가능하고, 이로 인해, 칼라무늬 바닥재의 시공품질을 고급화시키는 효과를 갖는다.In addition, the present invention enables the production of a two-tone color in which the constructed flooring material resembles a natural stone pattern by appropriately dispersing the pigment in the release agent, and thus has the effect of enhancing the construction quality of the colored patterned flooring material.

이하, 본 발명의 바람직한 실시 예를 첨부된 도면을 참조하여 자세히 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 2a 내지 도 2e는 본 발명에 따른 칼라무늬 바닥재의 시공과정을 설명하기 위한 공정도이다.2a to 2e is a process chart for explaining the construction process of the collar pattern flooring according to the present invention.

동 도면에서 보는 바와 같은 본 발명은 먼저, 칼라무늬 바닥재 시공을 위해 콘크리트층(10) 상부에 칼라하드너층(20)을 형성한다.(도 2a)The present invention as shown in the drawing, first, to form a collar hardener layer 20 on the concrete layer 10 for the construction of the collar pattern flooring (FIG. 2a).

이때, 상기 콘크리트층(10)은 포설 후, 수분이 완전 건조되지 않은 상태이다.At this time, after the concrete layer 10 is installed, the moisture is not completely dried.

또한, 상기 칼라하드너(20)는 파우더 상태로 도포되어 콘크리트(10) 에 배어 있는 수분과 접촉하여 반응이 이루어지게 된다.In addition, the color hardener 20 is applied in a powder state is in contact with the moisture soaked in the concrete 10 is made to react.

이때, 상기 칼라하드너(20)가 수분 반응에 의해 페이스트 상태가 되면, 흙손 등을 이용해 균일한 두께로 미장하게 된다.At this time, when the color hardener 20 is in the paste state by the water reaction, it is plastered to a uniform thickness using a trowel or the like.

이와 같은 칼라하드너층(20)은 2~10mm 두께로 형성할 수 있다.The color hardener layer 20 may be formed to a thickness of 2 ~ 10mm.

상기 칼라하드너층(20)은 바닥재의 강도를 증진시키는 역할을 하는 동시에 무늬도장에 의한 입체감을 제공할 수 있고, 시공 바닥의 베이스 칼라를 형성하게 되는데, 시중에 판매되고 있는 제품명 AC 102 아트콘(제조사:삼중건설화학), 제품명 AC 103 아트콘(제조사:삼중건설화학)이 사용될 수 있다.The color hardener layer 20 serves to enhance the strength of the flooring and at the same time provide a three-dimensional effect by the pattern coating, and form a base collar of the construction floor, commercially available product name AC 102 artcon ( Manufacturer: triple construction chemical), product name AC 103 Artcon (manufacturer: triple construction chemical) can be used.

이후, 상기 칼라하드너층(20) 상부에 본 발명에 따른 이형제 조성물을 이용한 이형제층(30)을 형성한다.(도 2b)Thereafter, the release agent layer 30 using the release agent composition according to the present invention is formed on the color hardener layer 20. (FIG. 2B)

이때, 상기 이형제(30)는 스프레이 장비 등을 이용하여 골고루 분사시켜 도포하게 된다.At this time, the release agent 30 is applied by spraying evenly using a spray equipment or the like.

이와 같은 이형제의 조성은 용제 70~84중량%, 실리콘오일 14~26중량%, 소포제 0.3~0.7중량%, 분산제 0.3~0.7중량%, 계면활성제 0.4~0.6중량% 및, 무기안료 1~2 중량%로 이루어진다.The composition of the release agent is 70 to 84% by weight of solvent, 14 to 26% by weight of silicone oil, 0.3 to 0.7% by weight of antifoaming agent, 0.3 to 0.7% by weight of dispersant, 0.4 to 0.6% by weight of surfactant, and 1 to 2 weight of inorganic pigment. In percent.

여기서, 상기 용제는 일종의 희석제로서, 중합체를 용해하여 도료의 유동성을 조절하고, 도장할 때의 건조속도를 조절할 수 있고, 작업성을 좋게 하거나 또는 도막에 평활성(유동성)을 부여하는 역할을 한다.Here, the solvent is a kind of diluent, it is possible to control the fluidity of the coating by dissolving the polymer, and to control the drying rate when coating, improve the workability or impart smoothness (fluidity) to the coating film.

이러한 용제로는 미네럴 스피릿을 사용할 수 있다. 이때, 상기 미네럴 스피릿은 일종의 희석제로서, 중합체를 용해하여 도료의 유동성을 조절하고, 도장할 때의 건조속도를 조절할 수 있고, 작업성을 좋게 하거나 또는 도막에 평활성(유동성)을 부여하는 역할을 한다.As such a solvent, mineral spirits can be used. At this time, the mineral spirit is a kind of diluent, and it dissolves the polymer to control the fluidity of the paint, and to control the drying speed when painting, and to improve the workability or to provide a smoothness (fluidity) to the coating film .

그리고, 상기 실리콘 오일은 이형효과를 높이기 위한 이형보조제로서 사용되 는데, 실리콘 오일의 함량이 14 중량% 미만이면 이형효과에 큰 영향이 없으며, 26 중량%를 초과하면 후속공정인 코팅공정에서 코팅제와의 접착력을 저하시키게 된다.In addition, the silicone oil is used as a release aid to increase the release effect, if the content of the silicone oil is less than 14% by weight does not have a significant effect on the release effect, if it exceeds 26% by weight of the coating agent in the coating process and subsequent steps The adhesion of the will be lowered.

또한, 상기 소포제는 기포가 발생되는 것을 억제시키거나 제거하는 역할을 하고, 상기 분산제는 안료의 미립자를 액체 속에 분산시키는 역할을 하며, 상기 계면활성제는 표면활성제로서, 이형제 내의 안료를 균일하게 분산시키는 역할을 한다.In addition, the antifoaming agent serves to suppress or eliminate the generation of bubbles, the dispersing agent serves to disperse the fine particles of the pigment in the liquid, the surfactant is a surface active agent, to uniformly disperse the pigment in the release agent Play a role.

또한, 본 발명의 이형제는 고형분 50% 무기계 안료를 사용하게 되는데, 산화철, 산화티탄, 유산바륨, 탄산바륨 등이 사용될 수 있다.In addition, the release agent of the present invention is to use a solid 50% inorganic pigment, iron oxide, titanium oxide, barium lactate, barium carbonate may be used.

상기한 바와 같은 이형제(30)를 분사시켜 도막을 형성한 후에는 스템프(40)를 이용해 이형제층(30) 상부에 패턴무늬를 압인시키게 된다.(도 2c)After forming the coating film by spraying the release agent 30 as described above, the stamp pattern 40 is pressed into the upper part of the release agent layer 30 by using a stamp 40 (FIG. 2C).

이때, 상기 스템프(40)는 특정한 형태의 패턴무늬가 양각된 우레탄 몰드, 고무매트 및 롤러 등이 이용될 수 있는데, 이와 같은 스템프(40)를 이형제층(30) 상부에 올려놓고 힘을 가해 압인시키게 되면, 이형제층(30) 및 칼라하드너층(20)에 음각의 패턴무늬를 전사시킬 수 있게 된다.In this case, the stamp 40 may be a urethane mold, a rubber mat, a roller, and the like, in which a pattern of a certain pattern is embossed, and the stamp 40 is placed on the release agent layer 30 and pressed in by force. In this case, the intaglio pattern may be transferred to the release agent layer 30 and the color hardener layer 20.

상기와 같은 패턴무늬를 형성한 후에는, 스템프(40)를 제거하게 되는데, 이때 이형제층(30)은 분리층으로서의 역할을 수행함으로써, 칼라하드너층(20)으로부터 손쉽게 스템프(40)를 분리시킬 수 있도록 한다.After forming the pattern pattern as described above, the stamp 40 is removed, wherein the release agent layer 30 serves as a separation layer, so that the stamp 40 can be easily separated from the color hardware layer 20. To help.

상기한 바와 같이 스템프(40)가 제거되고 나면, 양생과정을 거치게 되는데, 이 과정에서 이형제(30) 성분이 칼라하드너층(20)으로 잔여물 없이 완전 흡수된 다.(도 2d)As described above, after the stamp 40 is removed, a curing process is performed, in which the release agent 30 is completely absorbed into the color hardener layer 20 without residue (FIG. 2D).

이때, 상기 이형제(30)에 포함된 안료 성분이 칼라하드너층(20)에 흡수되면서, 투톤칼라의 무늬를 연출하게 된다.At this time, the pigment component contained in the release agent 30 is absorbed in the color hardener layer 20, thereby producing a two-tone color pattern.

이때 연출되는 무늬는 자연 암석에서 볼 수 있는 불규칙 얼룩무늬 패턴을 갖도록 하는 것이 중요한데, 이를 위해 이형제(30) 내에 분포하는 안료(31)는 소단위의 얼룩으로 뭉쳐져 있고, 이러한 소단위 얼룩들은 이형제 내에서 균일한 분포를 이루도록 이형제를 배합한다.At this time, it is important to produce a pattern having an irregular speckle pattern found in natural rocks. For this purpose, the pigment 31 distributed in the release agent 30 is aggregated into subunit stains, and the subunit stains are uniform in the release agent. The release agent is blended to form a distribution.

이와 같은 본 발명은 기존의 이형제 제거작업으로 인한 불편함이 없고, 오염물질을 배출하지 않기 때문에 친환경적인 이점이 있다.Such the present invention has no inconvenience due to the existing release agent removal operation, there is an environmentally friendly advantage because it does not discharge the pollutants.

상기와 같은 과정을 통해 패턴무늬를 형성하고 나면, 이를 보호하기 위한 코팅층(50)을 형성한다.(도 2e)After the pattern is formed through the same process as described above, a coating layer 50 is formed to protect it (FIG. 2E).

상기 코팅층(50)은 유성계 아크릴 합성고분자 수지 또는 수성계인 퓨어 아크릴 합성고분자 수지를 롤러나 스프레이건을 이용해 1~2회 정도 도포하게 된다.The coating layer 50 is applied to the oil-based acrylic synthetic polymer resin or a water-based pure acrylic synthetic polymer resin 1-2 times using a roller or a spray gun.

이때, 도포하는 두께는 0.05~0.1mm 가 되도록 하는 것이 바람직하다.At this time, it is preferable that the thickness to apply | coat becomes 0.05-0.1 mm.

이와 같은 코팅층(50)은 칼라무늬 바닥재를 기름이나 먼지, 물 등의 영향으로부터 보호하기 위한 것으로서, 내열성과 표면 광택도가 우수하고 표면의 끈적임이 적어 먼지오염이 적은 이점을 갖는다.Such a coating layer 50 is to protect the colored pattern flooring from the effects of oil, dust, water, etc., has excellent heat resistance and surface glossiness and less stickiness of the surface, thereby having less dust pollution.

도 1은 종래기술의 칼라무늬 콘크리트 습식 매트 공법의 시공과정을 개략적으로 도시한 흐름도.1 is a flow chart schematically showing the construction process of the prior art colored concrete wet mat method.

도 2a 내지 도 2e는 본 발명에 따른 칼라무늬 바닥재의 시공과정을 설명하기 위한 공정도.Figure 2a to 2e is a process chart for explaining the construction process of the collar pattern flooring according to the present invention.

<도면중 주요 부분에 대한 부호의 설명><Explanation of symbols for main parts of the drawings>

10: 콘크리트층 20: 칼라하드너층10: concrete layer 20: color harder layer

30: 이형제층 40: 스템프30: release agent layer 40: stamp

50: 코팅층50: coating layer

Claims (5)

삭제delete 삭제delete 콘크리트 또는 아스팔트 층 상부에 2~10mm 두께로 칼라하드너층을 형성하는 단계; 상기 칼라 하드너층 상부에 용제인 미네럴 스피릿 70~84중량%과 실리콘오일 14~26중량%과 소포제 0.3~0.7중량%과 분산제 0.3~0.7중량%과 계면활성제 0.4~0.6중량% 및 고형분 50%의 산화철, 산화티탄, 유산바륨, 탄산바륨 중 선택된 어느 하나인 무기안료 1~2 중량%로 이루어진 이형제층을 형성하는 단계; 상기 이형제층 상부에 스템프를 이용해 패턴무늬를 음각하는 단계; 상기 스템프가 제거된 후, 양생과정을 거쳐 이형제 성분이 칼라하드너층으로 완전 흡수되면서, 이형제의 안료 성분이 칼라하드너층에 투톤칼라의 무늬를 형성하는 단계; 및 상기 패턴무늬 상부에 유성계 아크릴 합성고분자 수지 또는 수성계인 퓨어 아크릴 합성고분자 수지를 사용해 0.05~0.1mm 두께로 도포하여 코팅층을 형성하는 단계;로 이루어지는 것을 특징으로 하는 액상이형제를 이용한 칼라무늬 바닥재의 시공방법.Forming a color hardener layer on the concrete or asphalt layer to a thickness of 2 to 10 mm; 70-84% by weight of mineral spirit, 14-26% by weight of silicone oil, 0.3-0.7% by weight of defoaming agent, 0.3-0.7% by weight of dispersant, 0.4-0.6% by weight of surfactant, and 50% of solid content on the color hardner layer Forming a release agent layer composed of 1 to 2% by weight of an inorganic pigment, which is any one selected from iron oxide, titanium oxide, barium lactate, and barium carbonate; Engraving a pattern pattern using a stamp on the release agent layer; After the stamp is removed, the curing agent is completely absorbed into the color hardener layer through the curing process, the pigment component of the release agent to form a two-tone color pattern on the color hardener layer; And forming a coating layer by applying an oil-based acrylic synthetic polymer resin or an aqueous pure acrylic synthetic polymer resin to a thickness of 0.05 to 0.1 mm on the patterned pattern; forming a coating layer using a liquid releasing agent. Construction method. 삭제delete 삭제delete
KR1020080098862A 2008-10-08 2008-10-08 Constructing Method of Color pattern floors KR101076017B1 (en)