KR20100103431A - Constructing method of non-slip color pattern floors - Google Patents
Constructing method of non-slip color pattern floors Download PDFInfo
- Publication number
- KR20100103431A KR20100103431A KR1020100022540A KR20100022540A KR20100103431A KR 20100103431 A KR20100103431 A KR 20100103431A KR 1020100022540 A KR1020100022540 A KR 1020100022540A KR 20100022540 A KR20100022540 A KR 20100022540A KR 20100103431 A KR20100103431 A KR 20100103431A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- pattern
- slip
- stencil
- asphalt
- Prior art date
Abstract
Description
The present invention relates to a method for constructing a non-slip color patterned flooring that is excellent in visibility and suitable for use in public places requiring public attention, such as pedestrian roads, bicycle residual roads, school zones, green zones, and the like.
Conventional anti-slip floor is generally used to apply a resin to the road, spray the aggregate (steelmaking sleeve), and then use a method of compacting and finishing the surface using a compaction compactor roller.
In this method, the visibility of the color is insufficient, the visibility is reduced, the dropping of aggregates impregnated in the resin due to the continuous impact caused by the traveling vehicle, and the wear and slip resistance of the product is remarkably lowered. This weak, if used for a long time there was a problem that the falling off from the base material asphalt.
In addition, since the durability of the coating film is rapidly discolored, the color of the product is changed to a white phenomenon occurs, which caused a problem that the visibility of the product is sharply lowered.
Another conventional non-slip bottom is coated with a thermoplastic resin.
Since this method uses a separate melting machine to work, the workability is good, but the variety of product colors falls, and there is a problem that the visibility of the product is lowered due to color discoloration. In addition, thick aggregates such as bauxite or steelmaking slug are used as anti-skid aggregates so that the aggregates contained in the products sink when the molten product is applied. There was a problem in which the phenomenon of losing the anti-slip function appeared.
The present invention has been made to improve the conventional problems, the object of the present invention is excellent workability by spray coating a non-slip paint, and can easily and elaborately express various pattern patterns by using a pattern pattern stencil, showing the aesthetic appearance It can be beautifully decorated and can produce various colors and patterns, and it has excellent visibility, so it is suitable for use in public places that require public attention, such as pedestrian roads, bicycle paths, school zones, green zones, etc. It provides a method of constructing a non-slip collar-patterned flooring that is excellent in its anti-slip effect and lifespan due to its excellent adhesion.
Construction method of the non-slip collar pattern flooring material for achieving the object of the present invention as a first embodiment
A cleaning operation step of removing foreign matter from the asphalt surface;
Installing a patterned stencil on the cleaned asphalt;
25 to 55% by weight of acrylic resin, 5 to 20% by weight of solvent, 0.3 to 5% by weight of defoaming agent, 0.3 to 5% by weight of dispersant, 0.8 to 5% by weight of middle agent, 2.5 to 10% of titanium dioxane on the pattern pattern stencil Spray coating a non-slip paint composed of%, and 30 to 55% by weight of aggregate;
Removing the pattern pattern stencil and drying the non-slip paint;
Forming a coating layer on the dried working surface.
In addition, the construction method of the non-slip collar pattern flooring material for achieving the object of the present invention as a second embodiment, the cleaning operation step of removing foreign matter on the asphalt surface;
A pretreatment step of applying a primer or a base coat on the cleaned asphalt;
Installing a patterned stencil on the cleaned asphalt;
25 to 55% by weight of acrylic resin, 5 to 20% by weight of solvent, 0.3 to 5% by weight of defoaming agent, 0.3 to 5% by weight of dispersant, 0.8 to 5% by weight of middle agent, 2.5 to 10% of titanium dioxane on the pattern pattern stencil Spray coating a non-slip paint composed of%, and 30 to 55% by weight of aggregate;
Removing the pattern pattern stencil and drying the non-slip paint;
Forming a coating layer on the dried working surface.
Here, the solvent is characterized in that any one selected from water or minor spirits.
In addition, the aggregate is characterized in that it comprises 8 to 70% by weight of silica sand 5, 15 to 80% by weight of silica sand 6 and 15 to 75% by weight of silica sand 7.
In addition, the aggregate is characterized in that it comprises calcium carbonate 15 to 80% by weight, silica sand No. 7 20 to 85% by weight.
In addition, the non-slip paint is characterized in that formed to a thickness of 1 ~ 2mm.
In addition, the coating layer is characterized in that formed to a thickness of 0.05 ~ 0.1mm.
The present invention has an effect excellent in workability by spray coating a non-slip paint.
In addition, the present invention can be easily and elaborately expressed a variety of pattern patterns using a pattern pattern stencil, has the effect of helping to beautify the beauty of the city.
In addition, the present invention can produce a variety of colors and a variety of patterns, excellent visibility has an effect that is suitable for use in public places that require the attention of the public, such as pedestrian road and bicycle road, school zone, green zone and the like.
In addition, the present invention has no change in color and has excellent adhesion to prevent slippage and extend life.
1 is a flow chart for explaining the construction process of the non-slip collar pattern flooring according to the present invention.
Figure 2 is a flow chart for explaining the construction process of the non-slip collar pattern flooring according to another embodiment of the present invention
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
≪ Example 1 >
1 is a flow chart for explaining the construction process of the non-slip collar pattern flooring according to the present invention.
According to the construction method of the non-slip collar pattern flooring according to the present invention as shown in the drawing, the surface of the asphalt first performs a refining operation step to remove foreign matters. (S10)
The asphalt surface cleaning operation is to clean various contaminants such as dust, dirt, grease, rust, stains and other oily products on the construction surface by using a dedicated cleaner or a weak acid and remove the contaminants with a high pressure cleaner. Can be.
Next, a step of installing a pattern pattern stencil on the cleaned asphalt is performed.
At this time, the pattern pattern stencil is provided in the form of a paper to form a blue hole region and a non-perforated region to produce a variety of patterns.
Next, 25 to 55% by weight of acrylic resin, 5 to 20% by weight of solvent, 0.3 to 5% by weight of antifoaming agent, 0.3 to 5% by weight of dispersant, 0.8 to 5% by weight of thickener, titanium on the working surface on which the patterned pattern stencil is installed Spray coating the non-slip paint consisting of 2.5 to 10% by weight of dioxane, and 30 to 55% by weight of aggregates.
Here, the acrylic resin is a clear, colorless, transparent, colorless resin that is made by polymerizing various acrylic monomers, and is tough and excellent in weather resistance, and has good water resistance, acid resistance, alkali resistance, and pollution resistance, and is a petroleum solvent, plant fiber, and grease. It has a large resistance to back and is widely used as a building paint.
In addition, the solvent may be any one selected from water or minor spirits, the solvent is a kind of diluent, can dissolve the polymer to control the fluidity of the paint, can control the drying rate when painting, workability It acts to improve or improve the smoothness (fluidity) in the coating.
In addition, the antifoaming agent serves to suppress or eliminate the generation of bubbles, the dispersing agent serves to separate the fine particles of the pigment into the liquid, the surfactant serves to uniformly disperse the pigment in the release agent as a surfactant. do.
And the aggregate may be made of a mixture of silica sand No. 5 8-70% by weight, silica sand No. 6 15-80% by weight and quartz sand No. 7 15-75% by weight, and also calcium carbonate 15-80% by weight, silica sand No. 7 20 It may be made of a formulation of ~ 85% by weight.
At this time, the non-slip paint is preferably applied to a thickness of 1 ~ 2mm.
Then, after removing the pattern pattern stencil, a step of drying the non-slip paint is performed.
In this case, when the pattern pattern stencil is removed, only the non-slip paint applied to the perforated area remains on the asphalt surface, and the non-slip paint applied to the non-perforated region is removed together with the pattern pattern stencil, thereby making the asphalt to be constructed. Various patterns can be produced on the floor.
After the non-slip paint is dried, a step of forming a bottom protective coating layer on an upper working surface is performed.
At this time, the coating layer is preferably formed to a thickness of 0.05 ~ 0.1mm.
<Example 2>
Figure 2 is a flow chart for explaining the construction process of the non-slip collar pattern flooring according to another embodiment of the present invention, according to the construction method of the non-slip collar pattern flooring according to the present invention as shown in the same drawing, first of the asphalt Carry out a cleaning operation step to remove foreign substances on the surface. (S10)
The asphalt surface cleaning operation is to clean various contaminants such as dust, dirt, grease, rust, stains and other oily products on the construction surface by using a dedicated cleaner or a weak acid and remove the contaminants with a high pressure cleaner. Can be.
Next, a pretreatment step using a primer or a base coat is performed on the asphalt after the cleaning operation. (S15)
At this time, the primer and the base coat can be formed in a thickness of 1 ~ 2mm, respectively, the primer and the base coat can be installed together in turn.
Next, a step of installing a patterned stencil on the pretreated working surface is performed. (S20)
At this time, the pattern pattern stencil is provided in the form of a paper to form a perforated region and a non-perforated region to produce a variety of patterns.
Next, 32 to 48% by weight of acrylic resin, 8 to 12% by weight of solvent, 0.3 to 0,5% by weight of antifoaming agent, 0,3 to 0,5% by weight of dispersant 0 Spray coating the non-slip paint, consisting of 8 to 1.5% by weight, 2.5 to 3.5% by weight of titanium dioxide, and 40 to 50% by weight of aggregate.
Here, the acrylic resin is a clear, colorless, transparent, non-chromic resin made by polymerizing various acrylic monomers, which is tough and excellent in weather resistance, and has good water resistance, acid resistance, alkali resistance, and fouling resistance, petroleum solvent, plant fiber, It has a large resistance to grease and is widely used as a building paint.
In addition, the solvent may be any one selected from water or minor spirits, the solvent is a kind of diluent, can dissolve the polymer to control the fluidity of the paint, can control the drying rate when painting, workability It acts to improve or improve the smoothness (fluidity) in the coating.
In addition, the antifoaming agent serves to suppress or eliminate the generation of bubbles, the dispersing agent serves to separate the fine particles of the pigment into the liquid, the surfactant serves to uniformly disperse the pigment in the release agent as a surfactant. do.
And the aggregate may be made of a mixture of silica sand No. 5 8-70% by weight, silica sand No. 6 15-80% by weight and quartz sand No. 7 15-75% by weight, and also calcium carbonate 15-80% by weight, silica sand No. 7 20 It may be made of a formulation of ~ 85% by weight.
At this time, the non-slip paint is preferably applied to a thickness of 1 ~ 2mm.
Then, after removing the pattern pattern stencil, a step of drying the non-slip paint is performed.
In this case, when the pattern pattern stencil is removed, only the non-slip paint applied to the perforated area remains on the asphalt surface, and the non-slip paint applied to the non-perforated region is removed together with the pattern pattern stencil, thereby making the asphalt to be constructed. Various patterns can be produced on the floor.
After the non-slip paint is dried, a step of forming a bottom protective coating layer on an upper working surface is performed.
At this time, the coating layer is preferably formed to a thickness of 0.05 ~ 0.1mm.
Claims (7)
Installing a patterned stencil on the cleaned asphalt;
25 to 55% by weight of acrylic resin, 5 to 20% by weight of solvent, 0.3 to 5% by weight of defoaming agent, 0.3 to 5% by weight of dispersant, 0.8 to 5% by weight of middle agent, 2.5 to 10% of titanium dioxane on the pattern pattern stencil Spray coating a non-slip paint composed of%, and 30 to 55% by weight of aggregate;
Removing the pattern pattern stencil and drying the non-slip paint;
Forming a coating layer on the dried working surface; Construction method of a non-slip collar pattern flooring comprising a.
A pretreatment step of applying a primer or a base coat on the cleaned asphalt;
Installing a patterned stencil on the cleaned asphalt;
25 to 55% by weight of acrylic resin, 5 to 20% by weight of solvent, 0.3 to 5% by weight of defoaming agent, 0.3 to 5% by weight of dispersant, 0.8 to 5% by weight of middle agent, 2.5 to 10% of titanium dioxane on the pattern pattern stencil Spray coating a non-slip paint composed of%, and 30 to 55% by weight of aggregate;
Removing the pattern pattern stencil and drying the non-slip paint;
Forming a coating layer on the dried working surface; Construction method of a non-slip collar pattern flooring comprising a.
The solvent is a construction method of the non-slip collar pattern flooring, characterized in that any one selected from water or minor spirit.
The aggregate is a method of constructing a non-slip collar pattern flooring, characterized in that it comprises 8 to 70% by weight of silica sand No. 5, 15 to 80% by weight of silica sand No. 7 and 15 to 75% by weight.
The aggregate is a method of constructing a non-slip collar pattern flooring, characterized in that it comprises 15 to 80% by weight of calcium carbonate, 20 to 85% by weight of silica sand.
The non-slip paint is a construction method of the non-slip collar pattern flooring, characterized in that formed to a thickness of 1 ~ 2mm.
Construction method of the non-slip collar pattern flooring, characterized in that the coating layer is formed to a thickness of 0.05 ~ 0.1mm.