KR100481953B1 - A making method of glaze for ceramics - Google Patents
A making method of glaze for ceramics Download PDFInfo
- Publication number
- KR100481953B1 KR100481953B1 KR10-2000-0027224A KR20000027224A KR100481953B1 KR 100481953 B1 KR100481953 B1 KR 100481953B1 KR 20000027224 A KR20000027224 A KR 20000027224A KR 100481953 B1 KR100481953 B1 KR 100481953B1
- Authority
- KR
- South Korea
- Prior art keywords
- porcelain
- producing
- latex
- oak
- ceramics
- Prior art date
Abstract
본 발명은 도자기용 유액의 제조방법에 관한 것으로, 그 목적은 중금속이나 발암물질과 같은 인체에 해로운 성분이 베어 나옴이 없고, 도자기의 통기를 원활히 하여 수납된 내용물을 장기간 신선하게 보관할 수 있을 뿐만 아니라 질감이 따뜻하고 외관이 매우 미려하고 세련됨은 물론 다량의 원적외선을 방사시킬 수 있는 도자기를 제작할 수 있는 도자기용 유액의 제조방법을 제공하는 것이며, 그 구성은 도자기용 유액의 제조방법에 있어서, 상기 방법은 소나무, 참나무 또는 떡갈나무중 어느 하나의 나무를 연소시켜 얻은 재 45 내지 50%와, 낙엽발효물 35 내지 45%와, 장석분말 5 내지 20%를 혼합하여 제조되는 것을 특징으로 한다. The present invention relates to a method for producing a porcelain emulsion, the object of which is not harmful to the human body such as heavy metals or carcinogens, and the aeration of the porcelain to facilitate the storage of the stored contents as well as fresh The present invention provides a method for producing a latex for porcelain, which is capable of producing a porcelain that is warm in texture, very beautiful and refined as well as capable of radiating a large amount of far-infrared rays. 45 to 50% of the ash obtained by burning any wood of pine, oak or oak tree, 35 to 45% of the deciduous fermentation, and is characterized in that it is prepared by mixing 5 to 20% of feldspar powder.
Description
본 발명은 도자기용 유액의 제조방법에 관한 것으로, 더욱 상세하게는 중금속이나 발암물질과 같은 인체에 해로운 성분이 베어 나옴이 없고, 도자기의 통기를 원활히 하여 수납된 내용물을 장기간 신선하게 보관할 수 있을 뿐만 아니라 질감이 따뜻하고 외관이 매우 미려하고 세련됨은 물론 다량의 원적외선을 방사시킬 수 있는 도자기를 제작할 수 있도록 한 도자기용 유액의 제조방법에 관한 것이다. The present invention relates to a method for producing an emulsion for ceramics, and more particularly, no harmful components such as heavy metals or carcinogens are cut out, and the contents stored by the aeration of the ceramics can be kept fresh for a long time. It also relates to a process for producing a latex for porcelain, which makes it possible to produce porcelain which is warm in texture, very beautiful in appearance and refined as well as capable of emitting a large amount of far infrared rays.
일반적으로, 도자기는 원료인 점토를 성형한 후 성형물을 가마에 넣고 초벌소성하고, 초벌소성된 소태에 유액을 입혀 재벌소성하여 완성된다. In general, pottery is completed by molding the clay as a raw material, putting the molded product in a kiln and firing the first, and applying the latex to the firing of the firing.
상기와 같은 도자기는 표면이 수분이 침투되지 않도록 매끄럽고, 광택이나는데 이는 초벌소성된 소태의 표면에 유액을 입혀 재벌소성하였기 때문이며, 이러한 유액은 도자기의 품질과 외관의 미려함과 예술성에 큰 영향을 미치게된다. The porcelain as described above is smooth and glossy to prevent moisture from penetrating the surface of the porcelain, which is caused by the application of latex to the surface of the prebaked calcined conglomerate, and this latex has a great influence on the quality and beauty of the porcelain and the artistry. do.
상기와 같은 종래의 유액은 화학유액으로서 규소, 석회석, 장석 카우린 등을 소정배합율로 배합하여 제조하는데 도자기가 완성되었을 때 광택이 많이 나도록 인체에 매우 해로운 납성분을 첨가하여 제작하는 경우도 종종 있다. The conventional latex is prepared by blending silicon, limestone, feldspar cowin and the like at a predetermined blending rate as a chemical latex, which is often produced by adding a lead component which is very harmful to the human body so that the porcelain is polished. .
그러나, 상기와 같이 제작된 종래의 도자기용 유액은 유리질이 도자기의 통공을 모두 차단하여 통기가 원활하게 이루어지지 않아 도자기내의 수납물을 장기간 신선하게 보관하지 못하고 쉽게 부패시킬 뿐만 아니라 발암물질 및 납성분과 같은 중금속성분이 베어 나오기 때문에 인체에 매우 해롭고, 도자기의 외표면에 윤기를 심하게 일으며, 질감이 차갑고 도자기의 품격도 저하시킨다는 문제점이 있었다. However, the conventional porcelain latex produced as described above is not easy to keep the contents in the porcelain because the glass is not blocking all the pores of the porcelain smoothly and not easily decayed as well as carcinogens and lead components Since heavy metal components such as cut outs are very harmful to the human body, the surface of the porcelain is heavily polished, there is a problem that the texture is cold and the quality of the porcelain is also reduced.
본 발명은 상기와 같은 종래의 문제점을 고려하여 안출한 것으로서, 그 목적은 중금속이나 발암물질과 같은 인체에 해로운 성분이 베어 나옴이 없고, 도자기의 통기를 원활히 하여 수납된 내용물을 장기간 신선하게 보관할 수 있을 뿐만 질감이 따뜻하고 외관이 매우 미려하고 세련됨은 물론 다량의 원적외선을 방사시킬 수 있는 도자기를 제작할 수 있는 도자기용 유액의 제조방법을 제공하는 것이다. The present invention has been made in view of the conventional problems as described above, the object is that harmful components such as heavy metals or carcinogens are not cut out, and the contents of the stored contents can be kept fresh for a long time by smoothly ventilating porcelain In addition to the warm texture, the appearance is very beautiful and refined, as well as to provide a method for producing a ceramic latex that can produce a ceramic that can emit a large amount of far infrared rays.
상기 본 발명의 목적은 도자기용 유액의 제조방법에 있어서, 상기 방법은 소나무, 참나무 또는 떡갈나무중 어느 하나의 나무를 연소시켜 얻은 재 45 내지 50%와, 낙엽발효물 35 내지 45%와, 장석분말 5 내지 20%를 혼합하여 제조되는 것을 특징으로 하는 도자기용 유액의 제조방법에 의해 달성될 수 있는 것이다. An object of the present invention is a method for producing a latex for ceramics, the method is 45 to 50% ash obtained by burning any wood of pine, oak or oak, 35 to 45% deciduous fermentation, feldspar It can be achieved by the method for producing a ceramic latex, characterized in that the powder is prepared by mixing 5 to 20%.
이하, 첨부한 도면을 참조하여 본 발명의 바람직한 실시예에 따른 도자기용 유액의 제조방법에 대하여 설명하기로 한다. Hereinafter, with reference to the accompanying drawings will be described a method for producing a ceramic latex according to a preferred embodiment of the present invention.
본 발명에 따른 도자기용 유액은 소나무, 참나무 또는 떡갈나무중 어느 하나의 나무를 연소시켜 얻은 재 45 내지 50%와, 낙엽의 발효시킨 납엽발효물35 내지 45%와, 고운 분말로 분쇄시킨 장석분말 5 내지 20%를 혼합시킴으로서 제조된다. Pottery milk according to the present invention is 45 to 50% ash obtained by burning any one of pine, oak or oak tree, 35 to 45% fermented lead leaf fermentation of deciduous leaves, feldspar powder pulverized into fine powder Prepared by mixing 5-20%.
또한, 본 발명에 따른 도자기용 유액의 제조방법의 다른 실시예로서, 완성된 도자기로부터 보다 많은 량의 원적외선이 방사될 수 있도록 하기 위하여 고운 분말로 분쇄시킨 장석분말 15 내지 25%와, 소나무, 참나무 또는 떡갈나무중 어느 하나의 나무를 연소시켜 얻은 재 25 내지 35%와, 고운 분말로 분쇄시킨 맥반석 분말 또는 게르마늄 분말 40 내지 60%를 혼합시킴으로서 제조된다. In addition, as another embodiment of the manufacturing method of the ceramic latex according to the present invention, 15 to 25% feldspar powder pulverized into fine powder in order to allow a greater amount of far-infrared radiation from the finished porcelain, pine, oak Or by mixing 25 to 35% of the ash obtained by burning one of the oak trees with 40 to 60% of the ganbanite powder or germanium powder pulverized into fine powder.
상기와 같은 본 발명의 제조방법에 의해 제조된 도자기용 유액은 도자기의 통공을 차단하지 않고 도가기의 통기를 원활하게 유지시키기 때문에 도자기내에 보관된 수납물을 신선한 상태로 오랫동안 보관할 수 있을 뿐만 아니라 인체에 해로운 성분이 전혀 베어 나오지 않고, 도자기 표면에 은은한 광택을 발생시킴으로서 도자기가 따뜻한 질감을 갖도록 함은 물론 미려하고 세련된 외관을 갖도록 함으로서 도자기의 품질은 물론 예술적인 품격까지 크게 향상시킬 수 있는 것이다. The porcelain latex prepared by the manufacturing method of the present invention as described above can keep the contents stored in the porcelain in a fresh state for a long time as well as keep the aeration of the pottery smoothly without blocking the pores of the porcelain The harmful ingredients are not cut out at all, and by creating a gentle luster on the surface of the porcelain, the porcelain can not only have a warm texture but also have a beautiful and refined appearance, thereby greatly improving the quality of the porcelain and the artistic dignity.
이상으로 설명한 본 발명에 의하면, 중금속이나 발암물질과 같은 인체에 해로운 성분이 베어 나옴이 없고, 도자기의 통기를 원활히 하여 수납된 내용물을 장기간 신선하게 보관할 수 있을 뿐만 질감이 따뜻하고 외관이 매우 미려하고 세련됨은 물론 다량의 원적외선을 방사시킬 수 있는 도자기를 제작할 수 있는 효과를 갖는다. According to the present invention described above, harmful ingredients such as heavy metals and carcinogens are not cut out, and the aerated contents of the porcelain can be smoothly stored for a long time, and the texture is warm and the appearance is very beautiful and refined. Of course, it has the effect of producing a ceramic that can emit a large amount of far infrared rays.
Claims (2)